AU2004290683A1 - Pultrusion systems and process - Google Patents

Description

WO 2005/049301 PCT/US2004/038118 PULTRUSION SYSTEMS AND PROCESS Cross Reference to Related Applications This application claims priority to U.S. Provisional Application, serial no. 5 60/520,765, which was filed on November 17, 2003, and U.S. Provisional Application, serial no. 60/560,295, which was filed on April 7, 2004. Field of the Invention The invention relates to polyisocyanate-based reaction systems, pultrusion of 10 those systems to produce reinforced matrix composites, and to composites produced thereby. Background of the Invention Pultrusion is a highly cost effective method for making fiber reinforced resin 15 matrix composites. The primary raw materials used in pultrusion are resin and reinforcement. Fillers and additives, such as, but not limited to, calcium carbonate, clay, mica, pigments, and UV stabilizers, may be added to the resin to enhance the physical, chemical, and mechanical properties of the pultruded product. Pultrusion is typically done by the injection die or open bath process. The open 20 bath process is the most common. The injection die process, however, is gaining importance due to environmental concerns about the large amounts of volatile contaminants released in the open bath process. In a typical open bath process, reinforcement material in the form of fibers, mat or roving is pulled continuously through an open bath of resin to produce an impregnated reinforcement. The impregnated 25 reinforcement is pulled through form plates to remove excess resin, and then through a curing die to cure the resin and yield a finished product. In the injection die pultrusion process, reinforcement material is passed through a closed injection die that has resin injection ports. The resin is injected under pressure through the ports to impregnate the reinforcement material. The impregnated reinforcement is pulled through the injection die 30 to produce a shaped product. Resins that have been used in the open bath and injection die methods of pultrusion include thermoset resins, such as unsaturated polyesters, epoxies, phenolics, WO 2005/049301 PCT/US2004/038118 methacrylates and the like, as well as thermoplastic resins such as PPS, ABS, Nylon 6. Blocked polyurethane prepolymers also have been used. Polyester and epoxy resins are generally slower reacting than polyisocyanate-based thermosets, such as polyurethanes and polyisocyanurates. In addition, the use of blocked polyurethane resins in pultrusion 5 has the disadvantage of requiring deblocking of the isocyanate to form a volatile by product. This creates environmental concerns and may cause unwanted plasticization of the cured resin. One component resin systems that are used in pultrusion include thermoset resins, which cure through ethylenic unsaturation, such as unsaturated polyesters, vinyl esters, 10 (meth)acrylics, and the like. These types of resins generally require the use of volatile unsaturated monomers, such styrene and/or methyl methacrylate. As such, resins of this type emit volatile organic compounds (VOC's) during processing. Engineering solutions to the VOC issue, such as the use of closed injection dies, have had only limited success in controlling these emissions and the intense odors that they produce. The monomers 15 used in the production of isocyanate-based resins are usually much less volatile than the unsaturated monomers. Accordingly, polyisocyanate-based resin systems have some inherent advantages. However, isocyanate-based formulations have had difficulties due to their relatively high reactivity at ambient temperatures. Direct mixing activation has also been used to form polyisocyanate-based matrix 20 polymers in the pultrusion process. Mixing activated systems of this type generally consist of a polyisocyanate component and an isocyanate reactive component (see e.g. WO 00/29459). The mixing activated systems disclosed in the prior art generally have a limited range of processability. This is due to the highly reactive nature of the mixing activated free isocyanate based chemistry. A careful balance needs to be struck between 25 the demands of adequate mixing and fiber wetting, the achievement of economically effective line speeds, and the physical properties required in the final pultruded composite article. The ideal mixing activated resin system has a long open time (or pot life) during (and after) mixing at relatively low temperature, but is characterized by rapid and even cure at the higher temperatures used for resin curing in the pultrusion curing die. 30 The ideal mixing activated resin system further provides for pultrusion processing at high line speeds. A significant drawback of prior art mixing activated isocyanate-based resin systems for use in pultrusion processing has been limited line speeds. Prior art systems of this type show surface defects and fouling of the processing apparatus when 2 WO 2005/049301 PCT/US2004/038118 processed at line speeds that are economically most interesting. The defects that are observed at these higher line speeds are sometimes referred to in the art as "powdering" or "sloughing". The onset of these phenomena, as a function of line speed, vary with the geometrical complexity of the pultruded profiles being made. It is not possible to cite any 5 particular line speed at which these undesirable phenomena always appear. However, it is noted that more complex profiles are usually more challenging to process at high line speeds than simple (flat) profiles. For any given profile, the ability to process at higher line speed without surface defects or fouling is an advantage in terms of the overall process economics. 10 A need therefore exists for mixing activated isocyanate-based resin systems, such as polyisocyanurate and polyurethane resin systems, that may be used in pultrusion, especially injection die pultrusion, which provide for a better combination of long pot life and fast cure and which can be processed at higher line speeds than prior art systems without powdering or sloughing. 15 Summary of the Invention The invention provides a reaction system for the preparation of a fiber-reinforced composite according to the pultrusion process comprising: (a) a reaction mixture formed by combining an isocyanate reactive composition 20 and a polyisocyanate composition, (b) a continuous fiber reinforcing material, and (c) a catalyst composition; wherein the catalyst composition contains a combination of at least two different metals in effective amounts, and wherein the combination of the reaction mixture and the 25 catalyst composition (henceforth the "catalyzed reaction mixture") initially contains both free isocyanate groups and free alcoholic -OH groups, has a gel time of greater than 768 seconds at 25 0 C, and a gel time of not greater than 120 seconds at 175'C. The invention further provides an improved pultrusion process for preparing a cured fiber reinforced polymer composite comprising the steps of: 30 (a) pulling continuous fibers through an impregnation die, (b) supplying an isocyanate reactive composition, a catalyst composition, and a polyisocyanate composition to produce a catalyzed reaction mixture and feeding the catalyzed reaction mixture to the impregnation die, 3 WO 2005/049301 PCT/US2004/038118 (c) contacting the continuous fibers with the catalyzed reaction mixture in the impregnation die for a time period and at a temperature sufficient to cause substantial polymerization of the catalyzed reaction mixture within the impregnation die to produce a composite of fibers coated by the reaction 5 mixture, (d) directing the composite of fibers coated by the reaction mixture through a heated curing die to at least partially advance the cure of the catalyzed reaction mixture so as to produce a solid fiber reinforced polymer matrix, and (e) drawing said solid composite from the curing die 10 wherein the catalyst composition contains a combination of at least two different metals in effective amounts, and wherein the mixture of the catalyst composition with the polyisocyanate composition and isocyanate reactive composition (henceforth the "catalyzed reaction mixture") initially contains both free alcoholic -OH groups and free isocyanate (-NCO) groups, has a gel time of greater than 768 seconds at 25 0 C, and a gel 15 time of not greater than 120 seconds at 175C. The pultrusion reaction system and process according to the invention are suitable for operation at higher line speeds, without powdering or sloughing, than are similar systems/processes that do not employ the metal based catalyst composition containing a combination of at least two different metals in effective amounts. When the comparison 20 is made on the same pultrusion line and with the same profile geometry (curing die geometry), the pultrusion reaction system and process disclosed herein surprisingly provides for operation at higher line speeds (prior to the onset of noticeably increased part surface defects or line fouling problems) than shown in the prior art. The invention further provides a fiber reinforced solid composite prepared 25 according to the improved pultrusion process. In preferred embodiments, the catalyzed reaction mixture has a gel time at 25 0 C of greater than 900 seconds. In more preferred embodiments, the catalyzed reaction mixture has a gel time at 25 0 C of 1000 seconds or more. In still more highly preferred embodiments, the catalyzed reaction mixture has a gel time at 25 0 C in the range of from 30 1000 seconds to 4000 seconds. In yet more highly preferred embodiments, the catalyzed reaction mixture has a gel time at 25 0 C in the range of from 1000 seconds to 3900 seconds, and a gel time at 175 0 C of less than 120 seconds. 4 WO 2005/049301 PCT/US2004/038118 In other preferred embodiments, the catalyzed reaction mixture is always substantially free of styrene or methyl methacrylate. In still other preferred embodiments, the catalyzed reaction mixture is substantially free of organic species, other than carbon dioxide, boiling lower than 200 0 C at 1 atmosphere pressure. In highly preferred 5 embodiments, the catalyzed reaction mixture remains in a liquid and flowable state, even though partial reaction has occurred, after it has been applied to the reinforcing fibers until it reaches the curing die. In a particularly preferred embodiment, the improved reaction system is free of tertiary amine catalysts. 10 The preferred metal-based catalyst compositions comprise effective amounts of at least two different metals in organically bound form. The different metals may be present in the catalyzed reaction mixture together within a single organometallic compound, in separate organometallic compounds, or both. The metals themselves may be present in any or all of their available oxidation states, provided that they are effective for the 15 catalysis of the cure of the reaction system under the conditions employed for pultrusion processing. The individual metals may be present as coordination complexes, as covalent compounds, as ionic compounds, or any combination thereof, provided that they are effective for the catalysis of the cure of the reaction system. The preferred organometallic compounds are those that have sufficient solubility in the polymer 20 forming reaction mixture, under the conditions employed for pultrusion processing, to be effective in catalyzing the cure of the reaction system. In the preferred embodiments, at least two of the metals present in the metal based catalyst composition are selected from the group consisting of any of the metals of Groups IIIB, IVB, VB, VIB, VIIB, VIIIB, IB, IA, IIA, liA, IVA, VA, VIA, the 25 Lanthanide series, and the Actinide series of the Periodic Table of the Elements. In still more preferred embodiments, at least two of the metals used in the catalyst composition are selected from among the group consisting of the metals of Groups IIA, IVA, and VA. In even more preferred embodiments, at least two of the metals used in the catalyst composition are selected from the group consisting of Al, Ga, In, Ge, Sn, Sb, and Bi. In 30 the most preferred embodiments, at least two of the metals used in the catalyst composition are selected from the group consisting of Al, Sn, and Bi. 5 WO 2005/049301 PCT/US2004/038118 Detailed Description of the Invention The invention provides a reaction system for the preparation of a fiber-reinforced composite according to the pultrusion process comprising: (a) a reaction mixture comprising an isocyanate reactive composition and a 5 polyisocyanate composition, (b) a continuous fiber reinforcing material, and (c) a catalyst composition; wherein the catalyst composition contains a combination of at least two different metals in effective amounts, and wherein the combination of the reaction mixture and the 10 catalyst composition (henceforth "catalyzed reaction mixture") initially contains both free isocyanate groups and free alcoholic -OH groups, has a gel time of greater than 768 seconds at 25oC, and a gel time of less than 120 seconds at 175°C. The invention further provides an improved pultrusion process for preparing a cured fiber reinforced polymer composite comprising the steps of: 15 (a) pulling continuous fibers through an impregnation die while contacting the fibers with a catalyzed reaction mixture comprising an isocyanate reactive composition, a polyisocyanate composition, and a catalyst composition sufficient to cause substantial polymerization of the catalyzed reaction mixture within the impregnation die to produce a composite of fibers coated by the 20 catalyzed reaction mixture, which is not,fully cured, (b) directing the composite of fibers coated by the catalyzed reaction mixture through a heated curing 'die to further advance the cure of the catalyzed reaction mixture so as to produce a solid fiber reinforced composite, and (c) withdrawing the solid fiber reinforced composite from the curing die; 25 wherein the catalyst composition contains a combination of at least two different metals in effective amounts, and wherein the catalyzed reaction mixture initially contains both free alcoholic -OH groups and free isocyanate (-NCO) groups, has a gel time of greater than 768 seconds at 25 0 C, and a gel time of less than 120 sec at 175 0 C. The expressions "impregnation die", "injection die", "impregnation box", and 30 "injection box" are synonymous within the context of the specification. The invention further provides an improved fiber reinforced solid composite prepared according to the pultrusion process. 6 WO 2005/049301 PCT/US2004/038118 In preferred embodiments, the catalyzed reaction mixture has a gel time at 25 0 C of greater than 900 seconds. In more preferred embodiments, the catalyzed reaction mixture has a gel time at 25'C of 1000 seconds or more. In still more highly preferred embodiments, the catalyzed reaction mixture has a gel time at 25 0 C in the range of from 5 1000 seconds to 4000 seconds. In yet more highly preferred embodiments, the catalyzed reaction mixture has a gel time at 25°C in the range of from 1000 seconds to 3900 seconds, and a gel time at 175 0 C of less than 120 seconds. In other preferred embodiments, the catalyzed reaction mixture is always substantially free of styrene or methyl methacrylate. In still other preferred embodiments, 10 the catalyzed reaction mixture is substantially free of organic species, other than carbon dioxide, boiling lower than 180oC, more preferably free of species boiling lower than 200oC, at 1 atmosphere pressure (760 mmHg). In highly preferred embodiments, the catalyzed reaction mixture remains in a liquid and flowable state, even though partial reaction has occurred, after it has been applied to the reinforcing fibers until it reaches the 15 curing die. WO 00/29459 provides background information on pultrusion processing with closed impregnation dies, and is incorporated herein fully by reference. Co-pending U.S. application serial number 10/626,983, filed July 25, 2003, provides further information and working examples of prior art reactive isocyanate-based pultrusion reaction systems 20 and of processes using these systems. This co-pending application is also incorporated herein fully by reference. Suitable isocyanate reactive compositions include compositions containing a plurality of active hydrogen groups that are reactive towards organic isocyanate groups under the conditions of processing. The most preferred isocyanate reactive compositions 25 are organic compounds, organic liquid polymers, or mixtures of such species that each individually contain a plurality of primary and/or secondary organically bound alcoholic hydroxyl groups. These polyhydroxy functional organic species (polyols) may optionally be used in combination with other kinds of organic polyfunctional isocyanate-reactive species in formulating the isocyanate reactive composition. Preferred examples of the 30 latter are polyamines, which contain primary and/or secondary amine groups. It is within the scope of the invention, however, to use isocyanate-reactive polyfunctional organic active hydrogen species other than polyols if these provide the desired reaction profile in derived mixing activated polymer-forming reaction systems. It is also within the scope of 7 WO 2005/049301 PCT/US2004/038118 the invention to employ active hydrogen species, which contain more than one kind of isocyanate-reactive active-hydrogen functional group. Preferred examples of the latter include aminoalcohols, which contain both isocyanate-reactive hydroxyl groups and isocyanate-reactive amino groups. Mixtures of different kinds of polyfunctional 5 isocyanate-reactive molecular species may, of course, be used in the formulation of the isocyanate reactive composition if desired. The isocyanate reactive functional groups present are preferably of the active hydrogen type. The isocyanate reactive compositions are all preferably liquids at 25 0 C. All polyfunctional isocyanate-reactive molecular species present in the reaction system (that are reactive towards organic isocyanate groups 10 under the conditions of processing and are not themselves isocyanates) are, by definition, part of the isocyanate reactive composition. The term "polyfunctional" is understood to encompass molecular species bearing two or more isocyanate reactive functional groups (that are reactive towards organic isocyanates under the conditions of processing and are not themselves isocyanate groups). The isocyanate reactive composition consists 15 essentially of one or a combination of these polyfunctional isocyanate reactive molecular species. The isocyanate reactive composition preferably contains less than 10% by weight, more preferably less than 5% by weight, still more preferably less than 2% by weight, and most preferably less than 1% by weight (of the total weight of the isocyanate reactive composition) of monofunctional isocyanate reactive molecular species, present as 20 impurities. It is, ideally, devoid of such monofunctional species. Monofunctional isocyanate reactive species may be added to the reaction system deliberately, as optional additives. However, such additives (added intentionally) are, by definition, outside the definition of the isocyanate reactive composition (and within the definition of optional additives, as defined further hereinbelow). 25 This isocyanate reactive composition preferably comprises at least one organic polyol, wherein said organic polyol has a number averaged functionality of organically bound primary or secondary alcohol groups of at least 1.8. The number averaged functionality of said polyol is preferably from 1.8 to 10, more preferably from 1.9 to 8, still more preferably from 2 to 6, and most preferably from 2.3 to 4. More preferably, the 30 isocyanate reactive composition consists predominantly, on a weight basis, of a polyol or mixture of polyols. Most preferably, the isocyanate reactive composition consists essentially of one or more polyols. 8 WO 2005/049301 PCT/US2004/038118 In certain embodiments, the isocyanate reactive composition will preferably comprise a mixture of two or more organic polyols. The individual polyols in the mixture will differ principally in regard to hydroxyl group functionality and molecular weight. In an embodiment of the invention, the organic polyols used in the isocyanate reactive 5 composition are selected from the group consisting of softblock polyols, rigid polyols, chain extenders, crosslinkers, and combinations of these different types of polyols. Polyols, which furnish softblock segments, are known to those skilled in the art as softblock polyols or as flexible polyols. Such polyols generally have a number averaged molecular weight of at least about 1500 (preferably from about 1750 to about 8000), a 10 number averaged equivalent weight of from about 400 to about 4000 (preferably from about 750 to 2500), and number averaged functionality of isocyanate reactive organic OH groups of about 1.8 to about 10 (preferably from about 2 to about 4). Such compounds include, for example, aliphatic polyether or aliphatic polyester polyols comprising primary and/or secondary hydroxyl groups. It is preferred that these softblock 15 polyols comprise from about 0 to about 30% by weight, and more preferably, from about 0 to about 20% by weight of the isocyanate reactive species present in the active hydrogen composition. Preferred softblock polyols are liquid at 25 0 C. Polyols that provide structural rigidity in the derived polymer are referred to in the art as rigid polyols, and are a preferred class of polyols. Such polyols generally have 20 number averaged molecular weights of from 250 to about 3000, preferably from 250 to less than 1500; number averaged equivalent weights of from 80 to about 750, preferably from 85 to about 300; and number averaged isocyanate reactive group functionalities of from 2 to 10, preferably 2 to 4, and more preferably 2 to 3. Such compounds include, for example, polyether or polyester polyols comprising primary and/or secondary hydroxyl 25 groups. Preferred rigid polyols are liquid at 25 0 C. Polyols that are referred to the in the art as chain extenders and/or crosslinkers are another preferred class of poyols. These have molecular weights between 60 to less than 250 (preferably from 60 to about 150), equivalent weights from 30 to less than 100 (preferably 30 to 70), and isocyanate-reactive group functionalities of from 2 to 4 30 (preferably from 2 to 3). Examples of suitable chain-extenders/crosslinkers are simple glycols and triols, such as ethylene glycol, propylene glycol, dipropylene glycol, 1,4-butanediol, 1,3 butanediol, triethanolamine, triisopropanolamine, tripropylene glycol, diethylene glycol, 9 WO 2005/049301 PCT/US2004/038118 triethylene glycol, glycerol, mixtures of these, and the like. The most preferred chain extenders/crosslinkers are liquids at 25 0 C. Although aliphatic -OH functional compounds, such as those just listed, are the most preferred as chain extenders/crosslinkers, it is accetpable to employ certain isocyanate-reactive polyamines, 5 polyamine derivatives, and/or polyphenols. Examples of suitable isocyanate-reactive amines known in the art include diisopropanolamine, diethanolamine, and 3,5-diethyl 2,4-diaminotoluene, 3 ,5-diethyl-2,6-diaminotoluene, mixtures of these, and the like. Examples of suitable isocyanate reactive amine derivatives include certain imino functional compounds such as those described in European Patent Application Nos. 10 284,253 and 359,456 and certain enamino-functional compounds such as those described in European Patent Application No. 359,456 having 2 or more isocyanate-reactive groups per molecule. Reactive amines, especially aliphatic primary amines, are less preferred due to their extremely high reactivity with polyisocyanates, but may optionally be used if desired in minor amounts. 15 It is also acceptable, albeit less preferred, to include within the polyol composition minor amounts of other types of isocyanate reactive species that may not conform to the types described hereinabove. The term "chain extender" is used in the art to refer to difunctional low molecular weight isocyanate reactive species, whereas the term "crosslinker" is limited to low 20 molecular weight isocyanate reactive species having a functionality of 3 or more. In one embodiment, a preferred isocyanate reactive composition comprises a mixture of (a) about 0 to 20% by weight of at least one polyol having a molecular weight of 1500 or greater and a functionality of 2 to 4, (b) about 60 to 100% by weight of at least one polyol having a molecular weight between 250 and 750 and a functionality of about 3 25 to about 4, most preferably about 3, and (c) about 2 to about 30% by weight of a least one polyol having a functionality of about 2 to about 3 and a molecular weight of less than 200, more preferably less than 150. The weights of (a) + (b) + (c) total 100% of the isocyanate reactive composition in this preferred isocyanate reactive composition for two component mixing activated pultrusion. All the polyol species in this preferred mixed 30 isocyanate reactive composition contain essentially all primary and/or secondary aliphatically bound organic -OH groups. In another embodiment, the isocyanate reactive composition comprises a total of at least 10% by weight, relative to the total weight of the isocyanate reactive composition, 10 WO 2005/049301 PCT/US2004/038118 of at least one hydrophobic polyol selected from the group consisting of hydrocarbon backbone polyols of number averaged molecular weight greater than 500, fatty ester polyols of number averaged molecular weight greater than 500, and fatty polyester polyols of number averaged molecular weight greater than 500. A particularly preferred 5 class of the fatty polyester polyols are those having number averaged functionalities of organically bound isocyanate-reactive hydroxyl groups of greater than 2. An especially preferred, but non-limiting, example of this class of fatty polyester polyols is castor oil. All the polyol species in these preferred isocyanate reactive compositions, according to this embodiment, contain essentially all primary and/or secondary aliphatically bound 10 organic -OH groups. Fatty ester (and fatty polyester) polyols are defined further, in greater detail, herein. In yet another embodiment, the polyisocyanate composition may contain isodyanate-terminated prepolymers of one or more of the hydrophobic polyols cited hereinabove. In the more preferred modes of this embodiment, the polyisocyanate 15 composition comprises a total of at least 5% by weight, relative to the total weight of said polyisocyanate composition, of the at least one isocyanate terminated prepolymer of a hydrophobic polyol. In the most preferred modes of this prepolymer embodiment, the polyisocyanate composition additionally contains some unreacted monomeric polyisocyanate species. Polyisocyanate compositions comprising isocyanate terminated 20 prepolymers of castor oil are especially preferred in this embodiment. The incorporation of hydrophobic polyols, as listed above, into either the isocyanate reactive composition, the polyisocyanate composition (as isocyanate terminated prepolymers), or both has the effect of reducing or eliminating unwanted foaming during processing of the reaction system into composite articles. This provides 25 one, although not the only, means for reducing foaming during processing. Another technique for inhibiting foaming during processing is to eliminate the use of tertiary amine species from the reaction system. Aliphatic tertiary amines are particularly problematic in this regard. It is to be understood unless otherwise stated that all functionalities, molecular 30 weights, and equivalent weights described herein with respect to polymeric materials are number averaged, and that all functionalities, molecular weights, and equivalent weights described with respect to pure compounds are absolute. 11 WO 2005/049301 PCT/US2004/038118 Some preferred types of polyols include the polyether polyols and the polyester polyols. Suitable polyether polyols that can be employed in the reaction systems of the invention include those that are prepared by reacting an alkylene oxide, a halogen substituted or aromatic substituted alkylene oxide or mixtures thereof, with an active 5 hydrogen containing initiator compound. Suitable oxides include for example ethylene oxide, propylene oxide, 1,2-butylene oxide, styrene oxide, epichlorohydrin, epibromohydrin, mixtures thereof, and the like. Propylene oxide and ethylene oxide are particularly preferred alkylene oxides. Suitable initiator compounds include water, ethylene glycol, propylene glycol, 10 butane diols, hexanediols, glycerine, trimethylolpropane, trimethylolethane, pentaerythritol, hexanetriols, sucrose, hydroquinone, resorcinol, catechol, bisphenols, novolac resins, phosphoric acid, and mixtures of these. Further examples of suitable initiators include ammonia, ethylenediamine, diaminopropanes, diaminobutanes, diaminopentanes, diaminohexanes, 15 diethylenetriamine, triethylenetetramine, tetraethylenepentamine, pentamethylenehexamine, ethanolamine, aminoethylethanolamine, aniline, 2,4 toluenediamine, 2,6-toluenediamine, 2,4'-diaminodiphenylmethane, 4,4' diaminodiphenylmethane, 1,3-phenylenediamine, 1,4-phenylenediamine, naphthylene 1,5-diamine, triphenylmethane-4,4',4"-tramine, 4,4'-di-(methylamino)-diphenylmethane, 20 1,3-diethyl-2,4-diaminobenzene, 2,4-diaminomesitylene, 1-methyl-3,5-diethyl-2,4 diaminobenzene, 1-methyl-3,5-diethyl-2,6-diaminobenzene, 1,3,5-triethyl-2,6 diaminobenzene, 3,5,3',5'-tetraethyl-4,4'-diamiodiphenylmethane, and amine aldehyde condensation products such as the crude polyphenylpolymethylene polyamine mixtures produced from aniline and formaldehyde, and mixtures thereof 25 Suitable polyester polyols include, for example, those prepared by reacting a polycarboxylic acid or anhydride with a polyhydric alcohol. The polycarboxylic acids may be aliphatic, cycloaliphatic, araliphatic, aromatic, and/or heterocyclic and may be substituted (e.g. with halogen atoms) and/or unsaturated: Examples of suitable carboxylic acids and anhydrides include succinic acid; adipic acid; suberic acid; azelaic acid; sebacic 30 acid; pthtalic acid; isophthalic acid; terephthalic acid; trimellitic acid; phthalic anhydride; tetrahydrophthalic anhydride; hexahydrophthalic anhydride; tetrachlorophthalic anhydride; endomethylene tetrahydrophthalic anhydride; glutaric acid anhydride; maleic acid; maleic anhydride; fumaric acid; dimeric and trimeric fatty acids, such as those 12 WO 2005/049301 PCT/US2004/038118 obtained from oleic acid, which may be in admixture with monomeric fatty acids. Simple esters of polycarboxylic acids may also be used in preparing polyester polyols. For example, terephthalic acid dimethyl ester, terephthalic acid bis glycol esters, and mixtures of these. Examples of polyhydric alcohols suitable for use in preparing polyester polyols 5 include ethylene glycol; 1,3-, 1,4-, 1,2-, and 2,3-butanediols; 1,6-hexanediol; 1,8 octanediol; neopentyl glycol; cyclohexane dimethanol (1,4-bis-hydroxymethyl cyclohexane); 2-methyl- 1,3-propanediol; glycerol; mannitiol; sorbitol; methylglucoside; diethylene glycol; trimethylolpropane; 1,2,6-hexanetriol; 1,2,4-butanetriol; trimethylolethane; pentaerythritol; triethylene glycol; tetraethylene glycol; polyethylene o10 glycols; dipropylene glycol; tripropylene glycol; polypropylene glycols; dibutylene glycol; polybutylene glycols; mixtures of these; and the like. The polyester polyols may optionally contain some terminal carboxy groups although preferably they are fully hydroxyl terminated. It is also possible to use polyesters derived from lactones such as caprolactone; or from hydroxy carboxylic acids such as hydroxy caproic acid or 15 hydroxyacetic acid. A particularly preferred class of polyester polyols are the fatty polyester polyols derived from natural sources, such as castor oil and the like. A non-limiting example of a preferred isocyanate reactive polyol suitable for use in the invention is a propylene oxide adduct of glycerol having a nominal functionality of 3 and a number-averaged hydroxyl equivalent weight of 86. This predominantly 20 secondary-OH functional triol is an example of a rigid polyol, as per the description provided hereinabove. It is commercially available from Huntsman Petrochemical Corporation as JEFFOL® G 30-650 polyol. Another preferred isocyanate reactive polyol suitable for use in the invention is a propylene oxide adduct of glycerol having a nominal functionality of 3 and a number-averaged hydroxyl equivalent weight of about 234. This 25 predominantly secondary-OH functional triol is another example of a rigid polyol, as per the description hereinabove. This polyol is also available from Huntsman Petrochemical Corporation as JEFFOL® G 30-240 polyol. Blends of JEFFOL® G 30-650 polyol with JEFFOL® G 30-240 polyol are examples of a preferred polyol mixture. The preferred weight ratios of these two polyols in these preferred blends are from about 1:2 to about 30 2:1. Examples of particularly preferred crosslinkers suitable for use in the isocyanate reactive composition include glycerol, trimethylolpropane, and mixtures of these. Glycerol is especially preferred. 13 WO 2005/049301 PCT/US2004/038118 Examples of particularly preferred chain extenders suitable for use in the isocyanate reactive composition include ethylene glycol, diethylene glycol, triethylene glycol, propylene glycol, dipropylene glycol, tripropylene glycol, and mixtures of these. Dipropylene glycol, diethylene glycol, and mixtures of these two glycols are especially 5 preferred. Combinations of both chain extenders and crosslinkers may, if desired, be used in the same isocyanate reactive composition. Examples of preferred optional flexible polyols that may be used in the isocyanate reactive compositions include polyether polyols of molecular weight 2000 or greater. An example of a preferred flexible polyether polyol suitable for use is JEFFOL@ G 31-55 10 polyol, which is a nominal polyether triol commercially available from Huntsman Petrochemical Corporation. JEFFOL® G 31-55 polyol has an hydroxyl equivalent weight of about 1000, and is prepared from a combination of propylene oxide and ethylene oxide. An example of another preferred flexible polyol that may be used in the polyol compositions suitable for the invention is JEFFOL® G 31-35 polyol. This polyol, 15 which is also prepared from propylene oxide and ethylene oxide, is a nominal polyether triol commercially available from Huntsman Petrochemical Corporation. JEFFOL® G 31-35 polyol has a hydroxyl equivalent weight of about 1600. A preferred class of flexible polyols contain predominantly primary -OH groups. The flexible polyols are preferably used at levels of 20% by weight or less of the total isocyanate reactive 20 composition, but may be used at higher levels if desired. It is within the scope hereof to produce relatively flexible pultruded composites by using predominantly flexible polyols in the isocyanate reactive composition. However, it is much more typical to produce rigid pultruded composites by using predominantly or exclusively rigid polyols, or combinations of rigid polyols with chain extenders and/or crosslinkers, in the isocyanate 25 reactive composition. Other examples of rigid polyols suitable for use include rigid polyether polyols produced from an initiator composition that comprises one or more sugars. A specific example of a suitable rigid polyol of this type is JEFFOL® SD-441 polyol, which is commercially available from Huntsman Petrochemical Corporation. JEFFOL® SD-441 30 polyol is prepared by propoxylation of a mixture of sucrose and a glycol, and has a number averaged equivalent weight of about 128. The term "nominal functionality" applied to polyols, as used in the context of this invention, denotes the expected functionality of the polyol based upon the raw materials 14 WO 2005/049301 PCT/US2004/038118 used in its synthesis. The nominal 'functionality may differ slightly form actual functionality, but the difference may usually be ignored in the context of this invention. The nominal functionality of a polyoxyalkylene polyether polyol is the functionality of the initiator. This is particularly true for polyether polyols, which are based 5 predominantly on EO and/or PO (such as, for example, the JEFFOL® G 30-650 polyol, described above). The nominal functionality of a pure compound is, of course, the same as its absolute functionality. If a mixed initiator is used, then the nominal functionality of the polyol is the number averaged functionality of the mixed initiator. A class of ester-group-containing polyols suitable for use in the isocyanate 10 reactive composition are the fatty ester (and fatty polyester) polyols. Fatty ester (and fatty polyester) polyols comprise at least one alkyl or alkenyl (hydrocarbon) side chain of from 4 to about 50 carbon atoms, preferably 5 to 25 carbon atoms, more preferably 6 to 20 carbon atoms, and most preferably 6 to less than 15 carbon atoms. The alkyl side chains are the more preferred. The fatty ester (and fatty polyester) polyols also comprise 15 at least two primary or secondary aliphatic -OH groups per molecule and preferably greater than 2 up to 4 such -OH groups. The fatty ester polyols contain one carboxylic ester linkages per molecule. The fatty polyester polyols contain at least two carboxylic ester linkages per molecule. The fatty polyester polyols are more preferred. Preferred examples of fatty polyester polyols are those that contain at least one triglyceride 20 structure and are liquid at 25 0 C. The fatty ester (and fatty polyester) polyols should preferably be free of aromatic rings, although it would be within the scope of the invention to use fatty ester (and fatty polyester) polyols that contain such rings. The fatty (poly)ester polyol may optionally contain ether linkages. A particularly preferred but non-limiting example of a triglyceride based fatty polyester polyol is castor oil. Mixtures 25 of different fatty (poly)ester polyols may be used if desired. The fatty (poly)ester polyol may be used by itself, but is preferably used in combination with at least one other type of polyol. The fatty (poly)ester polyol is most preferably used in combination with one or more polyether polyols. A preferred range of weight ratios of fatty (poly)ester polyols to polyether polyols, in the isocyanate reactive composition, is from about 1:9 to about 9:1, 30 and more preferably from 1:4 to 4:1. The fatty (poly)ester polyols have the desired effect of reducing foaming of the catalyzed reaction mixture during processing and curing, although this is not the only means for reducing foaming. The fatty (poly)ester polyols, and castor oil in particular, appear surprisingly more effective at reducing foaming than 15 WO 2005/049301 PCT/US2004/038118 conventional drying agents (such as molecular sieves) or conventional defoaming agents (such as silicone based antifoam additives). Although not wishing to be bound by theory, it is believed that the beneficial effects of the fatty (poly)ester polyols in reducing unwanted foaming (when foaming is present) is due to their hydrophobic nature. Other 5 hydrophobic polyols, and/or optional additives, that might be exploited for this beneficial (antifoaming) effect, when needed, include hydrocarbon backbone polyols such as the polybutadiene-based polyols, polyisoprene based polyols; hydrogenation products thereof; as well as simple aromatic or aliphatic oils. The optional, but preferred, hydrophobic polyols may also be incorporated into the polyisocyanate composition. It is, 10 for example, possible to include prepolymers of fatty (poly)ester or polybutadiene polyols into the polyisocyanate composition. The isocyanate reactive composition is the predominant isocyanate reactive material (other than the organic polyisocyanate itself) in the mixing activated chemical formulation used in the invention. This isocyanate reactive composition is, most 15 preferably, a polyol or a blend of polyols. Preferably, this isocyanate reactive composition constitutes at least 90% by weight, more preferably at least 95% by weight, and most preferably at least 98% by weight of the combined isocyanate reactive species (other than the organic polyisocyanate itself) present in the chemical formulation used in the present invention. Preferably, non-active hydrogen functional isocyanate-reactive 20 resins, such as epoxy resins, are substantially absent from the chemical formulation. By "substantially free" it is meant that the reaction mixture contains less than 10% by weight of all such non-active-hydrogen functional isocyanate-reactive resins combined, relative to the total weight of the catalyzed reaction mixture (including all catalysts, and optional additives that may be present). More preferably, the catalyzed reaction mixture contains 25 less than 5% by weight of all such species combined, relative to the total weight of the catalyzed reaction system. Still more preferably, the catalyzed reaction mixture contains less than 2% by weight of such species, even more preferably less than 1%, most preferably less than 0.5%, and ideally less than 0.1%, relative to the total weight of the catalyzed reaction mixture. 30 In an alternate embodiment, the isocyanate reactive composition may be admixed with minor amounts of water by weight. The water, when used, functions as a foaming agent. In the more preferred embodiments, the chemical formulation used in the process (including the isocyanate reactive composition, polyisocyanate composition, catalysts, 16 WO 2005/049301 PCT/US2004/038118 and any optional additives that may be present) is essentially free of water, or any other foam generating species. Preferably, the chemical formulation (including the isocyanate reactive composition, polyisocyanate composition, the required catalyst composition, and any optional additives that may be present) contains less than 0.2% by weight of water or 5 other foam generating species, relative to the total formulation weight. Still more preferably, this chemical formulation contains less than 0.1% by weight, and yet more preferably less than 0.05% by weight of water or other foam generating species, relative to the total formulation weight. Ideally, both the chemical formulation used to form the catalyzed reaction mixture and the entire reaction system (including the fibrous 10 reinforcing material) should be devoid of water and other foam generating species. The phrase "foam generating species" is understood to encompass both chemical blowing agents, which produce a volatile blowing agent under the conditions of processing by means of a chemical reaction, as well as physical blowing agents (i.e. entrained atmospheric gases, or volatile organic or inorganic compounds that simply boil under the 15 conditions of processing). The fiber reinforced pultruded composite articles made from the reaction system and according to the process of the invention are most preferably solid, and not foamed or cellular. The polyisocyanate composition preferably consists of organic polyisocyanates having a number averaged isocyanate (-NCO) functionality of from at least 1.8 to about 20 4.0. In the more preferred embodiments, the number averaged isocyanate functionality of the polyisocyanate composition is preferably from 2.0 to about 3.0, more preferably from 2.3 to 2.9. The polyisocyanate composition preferably has a free isocyanate group content ( NCO content) in the range of from 5% to 50% by weight, but more preferably in the 25 range of from 7% to 45%, still more preferably in the range of from 8% to 40%, yet more preferably in the range of from 9% to 35%, and most preferably in the range of from 10% to 33.6% by weight. The expression "organic polyisocyanate" will be understood to encompass isocyanate molecular species having a plurality of organically bound free isocyanate ( 30 NCO) groups. This definition includes organic diisocyanates, triisocyanates, higher functionality polyisocyanates, and mixtures thereof The polyisocyanates that may be used in the polyisocyanate composition in the preferred embodiments of present invention include any of the aliphatic, cycloaliphatic, 17 WO 2005/049301 PCT/US2004/038118 araliphatic, or aromatic polyisocyanates known to those skilled in the art. Especially preferred are those polyisocyanates that are liquid at 25 0 C. Examples of suitable polyisocyanates include 1,6-hexamethylenediisocyanate, isophorone diisocyanate, 1,4 cyclohexane diisocyanate, 4,4'-dicyclohexylmethane diisocyanate, 1,4-xylylene 5 diisocyanate, 1,4-phenylene diisocyanate, 2,4-toluene diisocyanate, 2,6-toluene diisocyanate, 4,4'-diphenylmethane diisocyanate (4,4'-MDI), 2,4'-diphenylmethane diisocyanate (2,4'-MDI), polymethylene polyphenylene polyisocyanates (crude, or polymeric, MDI), and 1,5-naphthalene diisocyanate. Mixtures of these polyisocyanates can also be used. Moreover, isocyanate-functional polyisocyanate variants, for example, 10 polyisocyanates that have been modified by the introduction of urethane, allophanate, urea, biuret, carbodiimide, uretonimine, isocyanurate, and/or oxazolidone residues can also be used. In general, aromatic polyisocyanates are more preferred. The most preferred aromatic polyisocyanates are 4,4'-MDI, 2,4'-MDI, polymeric MDI, MDI variants 15 (defined to encompass isocyanate terminated prepolymers), and mixtures of these. This most preferred class of aromatic polyisocyanates will be collectively referred to as the "MDI series" of polyisocyanates. Isocyanate terminated prepolymers may optionally be employed. Such prepolymers are generally prepared by reacting a molar excess of polymeric or pure 20 polyisocyanate with one or more polyols. The polyols may include aminated polyols, imine or enamine modified polyols, polyether polyols, polyester polyols or polyamines. Pseudoprepolymers (also known as semiprepolymers or quasiprepolymers), that are mixtures of an isocyanate terminated prepolymer and one or more monomeric polyisocyanates, may also be used. The use of prepolymers and especially 25 pseudoprepolymers is one preferred optional method for modifying the mechanical properties of the matrix resin. The use of prepolymers and pseudoprepolymers is also a useful technique for control of the weight ratios of the reactive components during mixing activated two-component pultrusion processing. Although it is within the scope of the invention to incorporate polyisocyanates that 3o are fully or partially blocked, it is much more preferable not to use any blocked isocyanate species. Free isocyanate (-NCO) groups are strongly preferred. Consequently, the polyisocyanate should be essentially free of blocked isocyanate groups. 18 WO 2005/049301 PCT/US2004/038118 Commercially available polyisocyanates useful in the preferred two-component isocyanate-based pultrusion process include the RUBINATE® and SUPRASEC@ brand polymeric isocyanates available from Huntsman International LLC. A specific example of a preferred polyisocyanate composition particularly suitable for use in the invention is 5 SUPRASEC@ 9700 polyisocyanate. This liquid isocyanate is of the polymeric MDI type and has a free isocyanate (-NCO) group content of 31.5% by weight and a number averaged isocyanate group functionality of 2.7. This polyisocyanate is commercially available from Huntsman International LLC. Another specific example of a preferred polyisocyanate composition suitable for use in certain embodiments of the invention is 10 RUBINATE® 1790 polyisocyanate. This product, which is commercially available from Huntsman International LLC, is a urethane modified pure 4,4'-VIDI product that has a number averaged isocyanate group functionality of about 2.00 and has a free isocyanate (-NCO) group content of about 23% by weight. The catalyzed reaction mixture contains a catalyst composition for catalyzing one 15 or more of the polymer forming reactions of polyisocyanates. The catalyst(s) are preferably introduced into the reaction mixture by pre-mixing with the isocyanate reactive composition (i.e. the polyol blend). The catalyzed reaction mixture, in this preferred embodiment, results when the pre-formed mixture of the isocyanate reactive composition with the catalyst composition is combined with the polyisocyanate composition. 20 It is a defining feature of the invention that the reaction system must contain a catalyst composition that comprises at least two different metals in catalytically effective amounts. The metals are preferably incorporated into one or more organometallic compounds that are sufficiently soluble in the reaction mixture to provide for effective catalytic activity under the conditions of pultrusion processing. The catalyst composition 25 preferably contains at least two different metals selected from the group consisting of the metals of Groups IIIA, IVA, and VA of the Periodic Table of the Elements. In the most preferred embodiments of the invention, the catalyst composition contains at least two different metals selected from the group consisting of aluminum, tin, and bismuth. Although not essential, it is acceptable to include additional metals in the catalyst 30 composition. It is also possible to include non-metal catalysts in the catalyst composition. Examples of non-metallic catalysts, suitable for promoting polymer-forming reactions of polyisocyanates, are tertiary amines. It is within the broader scope of the invention to use tertiary amines as optional additional catalysts. However, in a highly preferred 19 WO 2005/049301 PCT/US2004/038118 embodiment of the invention, no aliphatic tertiary amine catalysts or salts thereof are used in the reaction system. In this preferred embodiment, it is possible to employ aromatic tertiary amines, such as aromatic amine initiated polyols. However, it is most preferable to exclude aliphatic tertiary amine species from the reaction system. In another highly 5 preferred embodiment, the reaction system is free of both aliphatic and aromatic tertiary amine species or salts thereof. For the purposes of this specification, an aliphatic tertiary amine is a tertiary amine in which the tertiary nitrogen atom is bonded only to aliphatic carbon atoms. An aromatic tertiary amine is a tertiary amine in which the tertiary nitrogen atom is bonded to at least one aromatic carbon atom. 10 Optional additional catalysts for the polymer forming reactions of organic polyisocyanates are well known. The optional additional catalyst package may consist of a single catalyst, or a mixture of two or more catalysts, which are different from those required herein. 'Some examples of optional additional catalysts are selected from the group consisting of tertiary amines and tertiary amine acid salts. Examples of tertiary 15 amine catalysts that may optionally be used in the reaction system include triethylenediamine, N,N-dimethyl cyclohexylamine, bis-(dimethylamino)-diethyl ether, N-ethyl morpholine, N,N,N',N',N"-pentamethyl diethylenetriamine, N,N-dimethyl aminopropylamine, N-benzyl dimethylamine, and aliphatic tertiary amine-containing amides of carboxylic acids, such as the amides of N,N-dimethyl aminopropylamine with 20 stearic acid, oleic acid, hydroxystearic acid, and dihydroxylstearic acid. Commercially available tertiary amine catalysts include the JEFFCAT® brand catalysts from Huntsman Petrochemical Corporation and the POLYCAT® and the DABCO® amine catalysts, both available form Air Products and Chemicals Inc. Examples of suitable tertiary amine acid salt catalysts which may optionally be 25 used include those prepared by the at least partial neutralization of formic acid, acetic acid, 2-ethyl hexanoic acid, oleic acid, or oligomerized oleic acid with a tertiary amine such as triethylenediamine, triethanolamine, triisopropanolamine, N-methyl diethanolamine, N,N-dimethyl ethanolamine, mixtures of these amines, or the like. These amine salt catalysts are sometimes referred to as "blocked amine catalysts", owing to 30 delayed onset of catalytic activity that provides for improved convenience of resin application. The catalyst composition must contain at least two different catalytically active metals in effective amounts. These metals should preferably be selected from the group 20 WO 2005/049301 PCT/US2004/038118 consisting of the metals of Groups IIIB, IVB, VB, VIB, VIIB, VITIB, B13, IA, IIA, IIIA, IVA, VA, VIA, the Lanthanide series, and the Actinide series of the Periodic Table of the Elements. Optional additional metal catalysts containing metals from outside these groups may be used in the catalyst composition if desired, but only in addition to the 5 required metal catalyst(s) according to the invention. The most preferred catalyst compositions according to the invention comprise catalytically effective amounts of at least two metals selected from the group consisting of aluminum, tin, and bismuth. Examples of some optional additional organometal compounds for possible use as supplementary (optional) catalysts within the catalyst composition of the reaction system 10 include potassium 2-ethyl hexanoate (potassium "octoate"), potassium oleate, potassium acetate, calcium oleate, potassium hydroxide, zinc neodecanoate, zinc laurate, zinc oleate, and zinc stearate. Further examples of optional additional catalysts suitable for use within the catalyst composition of the reaction system include amido amine compounds derived 15 from the amidization reaction of N,N-dimethyl propanedimine with fatty carboxylic acids. A specific example of such a catalyst is BUSPERSE 47 catalyst from Buckman Laboratories. Mixtures of optional tertiary amine, optional amine acid salt, and optional additional organo-metal catalysts may possibly be used within the catalyst composition. 20 It is sometimes desirable to include in the mixing activated chemical formulation one or more optional additional catalysts for the trimerization of isocyanate groups. Preferred examples of these optional additional catalysts include the alkali metal salts'of carboxylic acids. Some specific examples of optional isocyanate trimerization (isocyanurate) catalysts include potassium 2-ethyl hexanoate, potassium oleate, potassium 25 acetate, and potassium hydroxide. These compounds are also effective as optional additional catalysts for the reaction of polyisocyanates with active hydrogen compositions such as polyols. The organo-metal compounds used in the catalyst composition, and any optional catalysts that might also be used in the catalyst composition, regardless of their specific 30 structure or function in the formulation, should preferably be non-volatile species. The more preferred catalysts therefore are those having boiling points above 200'C (at 1 atmosphere pressure), still more preferably above 250 0 C, and most preferably above 260 0 C (at 1 atmosphere pressure). 21 WO 2005/049301 PCT/US2004/038118 The most preferred catalyst compositions contain at least two separate organometallic compounds, based on at least two different metals selected from the group consisting of aluminum, tin, and bismuth. The organometallic compounds are preferably soluble in the isocyanate-reactive composition at the levels required for effective use in 5 pultrusion processing. Examples of suitable classes of organometallic compounds include metal carboxylates of the three metals mentioned above, and acetoacetates of these metals. These examples are not to be construed as limiting. The levels of the preferred catalysts required to achieve the needed reactivity profile for pultrusion processing will vary with the composition of the reaction system 10 and must be optimized for each reaction system. Such optimization would be well understood by persons of ordinary skill in the art of polyisocyanate-based polymer chemistry. The catalysts preferably have at least some degree of solubility in the isocyanate-reactive compositions (polyol blends) used, and are most preferably fully soluble in the polyol blend at the use levels required. 15 In the preferred embodiments, each of the at least two required metals is present in the catalyzed reaction mixture as a soluble organometallic compound and each of these organometallic compounds is present at a concentration of greater than 0.0001% by weight, more preferably at least 0.001%, and still more preferably at least 0.005% by weight, relative to the total weight of the catalyzed reaction mixture. 20 In the preferred embodiments each of the at least two required metals is present in the form of a separate organometallic compound. The required metals may be present in any available oxidation state(s), or any desired combination of oxidation states, provided that the oxidation states chosen offer effective catalytic activity for the cure of the reaction system under the conditions 25 selected for pultrusion processing. Each of the at least two required metals my optionally be present together in a single organometallic compound. In this unusual situation the mixed metal compound should be present in the catalyzed reaction mixture at a concentration of greater than 0.0001%, preferably at least 0.001%, and more preferably at least 0.005% by weight, 30 relative to the total weight of the catalyzed reaction mixture., The chemical precursors used to form the catalyzed reaction mixture may contain other optional additives if desired. 22 WO 2005/049301 PCT/US2004/038118 The catalyst composition and the optional additives are typically added to the isocyanate reactive composition (typically, this is a polyol blend) prior to processing, although it is within the scope of the invention to premix all or any part of the catalysts and the optional additives package with the polyisocyanate composition under the proviso 5 that it does cause the polyisocyanate to self-react or otherwise interfere with pultrusion processing of the reaction system. Non limiting examples of additional optional additives include particulate or short fiber fillers, internal mold release agents, fire retardants, smoke suppressants, dyes, pigments, antistatic agents, antioxidants, UV stabilizers, minor amounts of viscosity 10 reducing inert diluents (preferably those boiling above 180 0 C at 760 mmHg pressure, most preferably those boiling above 260 0 C at 760 mmHg pressure), combinations of these, and any other known additives from the art of polyisocyanate based polymer chemistry. In an alternative embodiment, the additives or portions thereof may be provided to the reinforcing fibers of the reaction system, such as by coating the fibrous 15 reinforcing material with the additive. Suitable fillers can include, for example, calcium carbonate, barium sulfate, clays, aluminium trihydrate, antimony oxide, milled glass fibers, wollastonite, talc, mica, flaked glass, silica, titanium dioxide, molecular sieves, micronized polyethylene, combinations of these, and the like. 20 Internal mold release additives are highly preferred in pultrusion of mixing activated isocyanate based reaction systems in order to prevent sticking or buildup in the die. Suitable internal mold release agents may include, for example, fatty amides such as erucamide or stearamide, fatty acids such a oleic acid, oleic acid amides, fatty esters such as LOXIOL G71S inert polyester (from Henkel), carnuba wax, beeswax (natural esters), 25 butyl stearate, octyl stearate, ethylene glycol monostearate, ethylene glycol distearate, glycerin di-oleate, glycerin tri-oleate, and esters of polycarboxylic acids with long chain aliphatic monovalent alcohols such as dioctyl sebacate, mixtures of (a) mixed esters of aliphatic polyols, dicarboxylic acids and long-chained aliphatic monocarboxylic acids, and (b) esters of the groups: (1) esters of dicarboxylic acids and long-chained aliphatic 30 monofunctional alcohols, (2) esters of long-chained aliphatic monofunctional alcohols and long-chained aliphatic monofunctional carboxylic acids, (3) complete or partial esters of aliphatic polyols and long-chained aliphatic monocarboxylic acids, silicones such as TEGO® IMR 412T silicone (from Goldschmidt), KEMESTER® 5721 ester (a fatty acid 23 WO 2005/049301 PCT/US2004/038118 ester product from Witco Corporation), fatty acid metal carboxylates such as zinc stearate and calcium stearate, waxes such as montan wax and chlorinated waxes, fluorine containing compounds such as polytetrafluoroethylene, fatty alkyl phosphates (both acidic and non acidic types) which are known in the art, chlorinated-alkyl phosphates; 5 hydrocarbon oils, combinations of these, and the like. Other preferred optional additives for use in pultrusion processing of mixing activated isocyanate-based polymer systems include moisture scavengers, such as molecular sieves; defoamers, such as polydimethylsiloxanes; coupling agents, such as the mono-oxirane or organo-amine functional trialkoxysilanes; combinations of these and the 10 like. The coupling agents are particularly preferred for improving the bonding of the matrix resin to the fiber reinforcement in the final pultruded composite. Fine particulate fillers, such as clays and fine silicas, are often used at thixotropic additives. Such particulate fillers may also serve as extenders to reduce resin usage. Fire retardants are sometimes used as additives in pultruded composites. 15 Examples of preferred optional fire retardant categories include but are not limited to triaryl phosphates; trialkyl phophates, especially those bearing halogens; melamine (as filler); melamine resins (in minor amounts); halogenated paraffins; combinations of these; and the like. Other optional additives that may be used will be apparent to those skilled in the art. 20 In preferred embodiments, the ratio of the combined weight of all the optional additives in the entire chemical formulation, precursor to the catalyzed reaction mixture, to the combined weights of the isocyanate reactive composition (in isolation from any additives) and polyisocyanate composition (in isolation from any additives) is less than 1, more preferably less than 0.5, still more preferably less than 0.25, yet more preferably 25 less than 0.1, and most preferably less than 0.07. The stoichiometry of mixing activated isocyanate-based polymer forming formulations, containing an organic polyisocyanate composition and a polyfunctional isocyanate reactive composition is often expressed by a quantity known in the art as the Index. The Index of such a mixing activated formulation is simply the ratio of the total 3o number of reactive isocyanate (-NCO) groups present to the total number of isocyanate reactive groups (that can react with the isocyanate under the conditions employed in the process). This quantity is often multiplied by 100 and expressed as a percent. Typical index values in the mixing activated formulations, which are suitable for use in the 24 WO 2005/049301 PCT/US2004/038118 invention range from about 70 to about 150%, but may extend as high as about 1500% if an optional catalyst for the trimerization of isocyanate groups is included in the catalyzed reaction mixture. A preferred range of Index values is from 90 to 110%. A still more preferred index range is from 100 to 110%. A yet more preferred index range is from 100 5 to 105%. Another preferred range of Index values is from 200 to 700%, when an optional catalyst for the trimerization of isocyanate groups is included in the catalyzed reaction mixture. A long fiber based reinforcing material provides both mechanical strength to the pultruded composite and as the means for transmitting the pulling force in the process. 10 The fibers should be at least long enough to pass though both the impregnation and curing dies and attach to a source of tension. The fibrous reinforcing structure may be made of any fibrous material or materials that can provide long fibers, which are capable of being at least partially wetted by the catalyzed reaction mixture during impregnation. The fibrous reinforcing structure may consist of single strands, braided strands, woven or non 15 woven mat structures, combinations of these, or the like. Mats or veils made of long fibers may be used, in single ply or multi-ply structures. Suitable fibrous materials are those known in the pultrusion art, including, but not limited to, glass fibers, glass mats, carbon fibers, polyester fibers, natural fibers, aramid fibers, nylon fibers, combinations of these, and the like. The fibrous reinforcing materials should preferably be dry. 20 Particularly preferred reinforcing structures are those made from long glass fibers. In preferred embodiments, the fibers and/or fibrous reinforcing structures are formed continuously from one or more reels feeding into the pultrusion apparatus and attached to a source of pulling force at the outlet side of the curing die. The reinforcing fibers may optionally be pre-treated with sizing agents or adhesion promoters known in the art. 25 The weight percentage of the long fiber reinforcement in the final pultruded composite articles may vary considerably, depending on the end use application intended for the composite articles. Typical reinforcement loadings are from about 30 to 95% by weight, but more typically from 40 to 90% by weight of the final composite. Preferred reinforcement loadings are in the range of 60 to 90% by weight, more preferably 70 to 30 90% by weight of the final composite. It is within the broader scope of the invention to use mixing activated reaction systems comprising more than two components. However, two component mixing activated systems are most preferred. 25 WO 2005/049301 PCT/US2004/038118 In the most preferred embodiments, a polyisocyanate component [A-Component] and an isocyanate reactive component [B-Component] are the only components that are fed into the impregnation die of the pultrusion process. The polyisocyanate component contains the polyisocyanate composition and any additives that have been premixed 5 therewith. The isocyanate reactive component contains the isocyanate reactive composition and any additives that have been premixed therewith. The term "additives" is understood to encompass both the required catalysts and any optional additives. The impregnation die must provide for adequate mixing of the reactive components and adequate impregnation of the fibrous reinforcing material. The 10 impregnation die may preferably be fitted with a mixing apparatus, such as a static mixer, which provides for mixing of the reactive components before the resulting catalyzed reaction mixture is used to impregnate the fibrous reinforcing structure. Other types of optional mixing devices may be used. They may include, but are not limited to, high pressure impingement mixing devices or low pressure dynamic mixers such as rotating 15 paddles. In some cases, adequate mixing is provided in the impregnation die itself, without any additional mixing apparatus. In the most preferred embodiments, the additives, including the required catalyst composition and any optional additional catalysts, are pre-mixed with the isocyanate reactive composition prior to mixing of the latter with the polyisocyanate composition. 20 However, it is to be understood that those additives that are not themselves polyfunctional isocyanate reactive materials are to be considered (counted) as entities separate from the isocyanate reactive composition, even when mixed therewith. Likewise, if the additives, or any part thereof, are premixed with the polyisocyanate composition, these are to be considered as entities separate from the polyisocyanate composition, except in the rare 25 case where they are themselves polyfunctional isocyanate species. In an especially preferred embodiment of the process, the two component mixing activated chemical formulation (that is precursor to the catalyzed reaction mixture) is formulated to provide for mixing at a component weight ratio of about 1:1. The pultrusion apparatus preferably contains at least one impregnation die and at 30 least one curing die. The curing die operates at a higher temperature than the impregnation die. The pultrusion apparatus may optionally contain a plurality of curing dies, or zones. Different curing zones may be set at different temperatures, if desired, but all the zones of the curing die should be higher in temperature than the impregnation die. 26 WO 2005/049301 PCT/US2004/038118 The pultrusion apparatus may optionally contain a plurality of impregnation dies. Preferably, there is just one impregnation die, and this preferably is situated immediately prior to the first curing die (or zone). The impregnation die is set at a temperature that provides for some degree of reaction (polymerization) between the polyisocyanate and 5 the polyisocyanate-reactive ingredients in the catalyzed reaction mixture before the fibrous reinforcing structure, which has been at least partially impregnated with said reaction mixture, enters the first curing die (or zone). It is highly preferable that the catalyzed reaction mixture retains some degree of flowability (liquidity) until it enters the first curing die (or zone). 10 It is highly preferred that the wetting of the fibrous reinforcing structure of the reaction system be complete and that there be no dry spots, which would lead to surface defects or voids in the cured composite. Further details about preferred mixing activated isocyanate-based pultrusion processing methods and apparatus are provided in WO 00/29459. 15 In a highly preferred embodiment, the chemical precursors (used to prepare the catalyzed reaction mixture) is substantially free of organic species, other than carbon dioxide, boiling less than 200'C at 1 atmosphere pressure. In a still more highly preferred embodiment, the catalyzed reaction mixture is substantially free of organic species, other than carbon dioxide, boiling less than 250 0 C at 1 atmosphere pressure. In an even more 20 highly preferred embodiment, the catalyzed reaction mixture is substantially free of organic species, other than carbon dioxide, boiling less than 260'C at 1 atmosphere pressure. In yet another highly preferred embodiment, the catalyzed reaction mixture is substantially free of organic species, other than carbon dioxide, having a vapor pressure 25 greater than or equal to 0.1 mmHg at 25 0 C. In yet another highly preferred embodiment, the catalyzed reaction mixture is substantially free of any organic species having a vapor pressure greater than or equal to 0.1 mmHg at 25'C. By "substantially free" it is meant that the catalyzed reaction mixture contains less than 10% by weight of all such organic species combined, relative to the total weight of the catalyzed reaction mixture (including 30 all optional additives that may be present therein). More preferably, the catalyzed reaction mixture contains less than 5% by weight of all such organic species combined, relative to the total weight of the catalyzed reaction mixture. Still more preferably, the catalyzed reaction mixture contains less than 2% by weight of such organic species, even 27 WO 2005/049301 PCT/US2004/038118 more preferably less than 1%, most preferably less than 0.5%, and ideally less than 0.1%, relative to the total weight of the catalyzed reaction mixture. The catalyzed reaction mixture contains less than 0.1% by weight, more preferably less than 0.01% by weight, and most preferably 0%, of styrene or methyl methacrylate. 5 It has surprisingly been found that a new class of mixing activated isocyanate based two component liquid precursors containing the required combination of metal based catalysts for pultrusion have resulted in substantially improved processing. Substantially higher line speeds, better processing efficiency, and improved part quality have been achieved. The catalyzed reaction mixtures used in the reaction systems and 10 process of the invention exhibit certain gel time ranges under a dry atmosphere. The reaction systems are thermosetting systems, which preferably cure by forming a covalently crosslinked organic network polymer structure as the matrix resin of a fiber reinforced composite. The catalyzed reaction mixture (that is, the chemical precursor mixture that forms the matrix resin), which initially contains both free alcoholic -OH 15 groups and free isocyanate (-NCO) groups, has a gel time of greater than 768 seconds at 25 0 C and a gel time of not greater than 120 seconds at 175 0 C. It is to be understood that the catalyzed reaction mixture is the (mixed) reaction system (as defined above) without the reinforcing fibers. In preferred embodiments, the catalyzed reaction mixture has a gel time at 25 0 C of 20 greater than 900 seconds. In more preferred embodiments, the catalyzed reaction mixture has a gel time at 25 0 C of 1000 seconds or more. In still more highly preferred embodiments, the catalyzed reaction mixture has a gel time at 25 0 C in the range of from 1000 seconds to 4000 seconds. In yet more highly preferred embodiments, the catalyzed reaction mixture has a gel time at 25°C in the range of from 1000 seconds to 3900 25 seconds, and a gel time at 175 0 C of less than 120 seconds. In another preferred embodiment, the catalyzed reaction mixture has a gel time at 25 0 C of greater than 1000 seconds but less than 1200 seconds, and a gel time at 175 0 C of less than 60 seconds. In yet another preferred embodiment, the catalyzed reaction mixture has a gel time at 25 0 C of from 2400 seconds to 2700 seconds, and a gel time at 30 175 0 C of from 60 seconds to 120 seconds. In still another preferred embodiment, the catalyzed reaction mixture has a gel time at 25C of from 3000 seconds to 3300 seconds, and a gel time at 175'C of from 60 seconds to 120 seconds. In still another preferred 28 WO 2005/049301 PCT/US2004/038118 embodiment, the catalyzed reaction mixture has a gel time at 25°C of from 3600 seconds to 3900 seconds, and a gel time at 175 oC of from 60 seconds to 120 seconds. These gel time ranges are all determined on the complete formulation (with any optional additives that may be present), but without the reinforcing fibers present, under 5 mixing conditions similar to those employed in the actual pultrusion apparatus. They are measured according to the following general procedure (in the absence of the reinforcing fibers): Procedure for determining reactivity parameters (at 25 0 C): 10 * Add required weights of the fully formulated Isocyanate component (A-component) and the fully formulated Polyol component (B-component), including all additives, to the container used for mixing in a DAC 400 FV lab mixer. This mixer is known as a Speed Mixer and is manufactured by Hauschild Engineering. The use of this particular type of mixer minimizes entrainment of air into the liquid resin sample. 15 The chemical components and apparatus are initially all at 25'C. Make sure there is at least 100g of material for the mixer to function properly, but not greater than 200 g of material. The target scale of the reaction should be 120 g of material. Mixing should be performed under a dry atmosphere (i.e. dry air or dry nitrogen). The B component is first weighed into the mixing container, followed by the A-component, 20 at the appropriate weight ratio of the components. The mixing container is then immediately closed and inserted into the mixer. * Mix material for 25 seconds @ 2250 rpm. Start the timer as soon as you begin the mixer. * Once mixer stops, pour material into a small (approximately 125 ml) cup to obtain the 25 reactivity. * The material is usually thick, creamy beige in color, and turns a clear brown as the mixture reacts. * To check for the gel time, lightly touch a wood tongue depressor (or, alternatively, a stainless steel spatula) to the surface of the material. The material has gelled when a 30 string is pulled from the top surface. A string resembles a fine, spun web. Keep in mind that touching a wood stick to the surface may cause foaming. 29 WO 2005/049301 PCT/US2004/038118 * A hard time may then be obtained. A hard time can be noted when the tongue depressor hits a hard, or cured, spot on the surface of the material. Procedure for determining reactivity parameters on a hot plate (175oQ: 5 * As mentioned above, after the material has been poured into the -125 ml cup, the reactivity can be checked on a hot plate while the reaction is taking place. The procedure, to this point, is exactly as described above (for 25 0 C). * The reactivity should be taken at 175 0 C. Using a temperature probe, find a spot on the plate that is 175 0 C. 10 * Use a flat steel washer and a syringe to get consistent results. The washer should have an external diameter of 2.25 in., and internal diameter (inner ring diameter) of 15/16 in., and a thickness of 1/8 in. Place the center of the washer ring over the spot that is 175 0 C. Leave it there for 5 min., and then check that the temperature of the center (hole) is 1750 C. This should be sufficient time for the temperature of the washer to 15 equilibrate to that of the hot plate (175oC). Have a second stop watch ready to note the reactivity. * Draw 2cc of the catalyzed reaction mixture from the cup into the syringe. When the timer that is being used to get the 25'C gel time shows 3 minutes, simultaneously start the second stop watch as the material is dispensed into the middle of the ring. The 20 material should fill the circle right to the rim. * There are three times that should be noted: 1. Cream time- when the full circle of material has turned from opaque to clear. 2. Gel time- when the material produces a fine string from the surface when the wooden tongue depressor is pulled away. Take the gel time from the center of the 25 circle. 3. Hard time- when the material has fully cured. * The material, once cured, should pop right out of the circle so that the washer may be reused. Scrape off any remaining residue so that the washer will continue to lie flat on the hot plate. 30 The preferred two-component mixing activated chemical formulations disclosed herein provide a surprising combination of long open time at relatively low temperature with fast cure at relatively high temperature. The catalyzed reaction mixtures formed 30 WO 2005/049301 PCT/US2004/038118 from these compositions generally cure homogeneously and do not form separated solids prior to entering the first curing zone of the pultrusion line. This homogeneity of cure (without solids separation) is highly desirable. The catalyst compositions disclosed herein, particularly those having the preferred 5 combination of catalytic metals, have unexpectedly provided reaction systems that are processable at much higher pultrusion line speeds than comparable systems of the prior art. The higher pultrusion processing rates are achieved without unacceptable increases in processing problems, such as powdering and sloughing. The invention is further illustrated by the following non-limiting Examples. 10 Examples In the Examples that follow, all percentages given are percentages by weight unless indicated otherwise. All component (A/B) ratios are weight ratios unless indicated otherwise. The B-component composition is defined for each Example. The isocyanate used in each Example is the A-component. 15 Glossary: 1) JEFFOL® G 30-650 polyol: Is an oxypropylated glycerol, nominal triol having an hydroxyl number of about 650, available from Huntsman. 2) JEFFOL@ G 30-240 polyol: Is an oxypropylated glycerol, nominal triol having an 20 hydroxyl number of 240, available from Huntsman. 3) JEFFOL® G 31-55 polyol: Is an oxypropylated and oxyethylated glycerol, a nominal flexible triol having an hydroxyl number of about 55. It is available from Huntsman. 4) JEFFOL® G 31-35 polyol: Is an oxypropylated and oxyethylated glycerol, a nominal flexible triol having an hydroxyl number of about 35. It is available from Huntsman. 25 5) JEFFOL® SD-441 polyol: Is a polyol composition obtained by oxypropylation of a mixture of sucrose and a glycol. This polyol has a number averaged hydroxyl functionality of greater than 3, and an hydroxyl value of about 440. It is available from Huntsman. 6) SUPRASEC® 9700 polyisocyanate: Is a liquid polymeric MDI product having a free 30 isocyanate group content of about 31.5% by weight and a number averaged isocyanate group functionality of about 2.7. This product is available from Huntsman. 31 WO 2005/049301 PCT/US2004/038118 7) RUBINATE® 1790 polyisocyanate: Is a liquid derivative of pure 4,4'-MDI that contains urethane groups, has a number averaged functionality of isocyanate groups of about 2.00 and an isocyanate group content of about 23% by weight. This derivative is commercially available from Huntsman. 5 8) Molecular Sieve 3: Alternatively BAYLITH® 3A sieve, BAYLITH® 4A sieve, or any mixture thereof Both of these molecular sieve moisture scavenger products are available from Bayer Corporation. 9) TECHLUBE® BR 550 lubricant: Is a proprietary internal mold release agent containing complex complex condensation polymer of synthetic resins, glyceride and 10 organic esters manufactured by Technick Products, Rahway NJ. 10)Molecular Sieve 4: Is a molecular sieve moisture scavenger product having a pore size of 4 Angstroms, such as BAYLITH® 4A sieve available from Bayer Corporation. 11) COSCAT® BiZn catalyst: Is a proprietary organometallic catalyst composition 15 believed to comprise bismuth and zinc, commercially available from Caschem Chemical Corporation. 12)K-KAT® 5218 catalyst: Is an aluminum chelate catalyst believed to be aluminum acetlylacetonate. This catalyst product is commercially available from King Industries. 20 13) Mold Wiz® INT1938MCH: Is an internal mold release additive (IlR) available from Axel Industries. It detailed composition is proprietary. 14) FOMREZ® UL29 catalyst: Is an organotin catalyst from Witco Corp. Pultrusion of Polyurethane and Polyisocyanurate Systems 25 Generally, pultrusion of polyurethane and polyisocyanurate systems with fiber reinforced composites is performed by supplying the formulated isocyanate and polyol components to a mix/metering machine for delivery in a desired ratio to a mixing apparatus, preferably a static mixer, to produce a reaction mixture. The catalyzed 30 reaction mixture is supplied to an injection die where it can be used to impregnate fibers being pulled concurrently into the injection die where partial polymerization and impregnation of the fibrous reinforcing materials occurs. The resulting incompletely cured composite is pulled through a zoned heating die, attached directly to the injection 32 WO 2005/049301 PCT/US2004/038118 die, having a desired cross-section where it is shaped and fully cured. The dynamic forces needed to pull the composite through the forming die is supplied by the pulling machine. This machine typically consists of gripping devices that contact the cured composite profile (or the glass fibers therein) and give the traction necessary to pull the 5 composite profile through the die. The machine also consists of a device that develops a force in the desired direction of pull that gives the impetus necessary to pull the composite profile continuously through the die. The resulting composite profile upon exiting the pulling machine is then cut to the desired length 'typically by an abrasive cut off saw. 10 The Examples outlined below have been processed on a lab pultrusion line. The meter/mix machine used to supply the catalyzed reaction mixture to the injection die was Liquid Control Corp., North Canton, OH, Model RPV. It supplies the liquid reaction components at the desired ratio to a static mixer at a rate of approximately 2 g/s. The static mixer is equipped with two static mixing tubes in series with 30 polypropylene 15 elements each which combines the reactants to form a homogeneous mixture. The inside diameter of this static mixer is 8 mm and the overall length of each unit is 32.26 cm. The static mixer is attached to an injection box that combines the catalyzed reaction mixture with the reinforcement that is being pulled concurrently through the injection box. The injection box internal dimensions are 8 in. long by 1.5 in. wide by 0.6 20 in. tapering to 0.1 in. high. The injection box is attached to the curing die that has internal measurements of 26 in. long by 1.5 in. wide by 0.120 in. high. The curing die has two'12 in. long heated zones equipped with electrical heating coils individually controlled to maintain the desired temperatures. Curing dies with three zones may also be used. The reinforcement used in the preparation of the pultruded composite were in the 25 form of 45 fiberglass rovings supplied by Owens Corning Fiberglass Co., 366AD Type 30, 4400 Tex. A pulling machine manufactured by Huntsman International LLC pulled the rovings and composite. It is a caterpillar type machine in which the grippers provide the propulsion that drives the process. 30 Example 1 and Comparative Example A: Evaluated in laboratory and on pultrusion line. 33 WO 2005/049301 PCT/US2004/038118 The mixing activated formulation shown in Example 1 (according to the invention) uses a commercial organo-aluminum based catalyst (an aluminum acetylacetonate catalyst) obtained from King Industries, in combination with an organotin based catalyst. The formulation provides unexpected and surprising improvements in pultrusion -processing, 5 facilitating the achievement of higher practical line speeds than prior art formulations. The improvements stem from the use of the mixed metal catalyst composition. The catalyst composition contains two different metals, aluminum and tin, in effective amounts. The formulation and a description of the observed improvements resulting from 10 its use in pultrusion are provided in detail below in Example 1. The formulation is a two component mixing activated reactive formulation. A comparative example, Example A, is shown to illustrate the benefits of the invention. The formulation shown below for Example 1 is not to be construed as limiting on the scope of the invention. 15 The pultrusion formulation of Example 1 consists of a polyol blend component (below) and a polyisocyanate component (below). The ratio of the polyol blend and polyisocyanate components, used in Example 1, is uniquely defined by its Isocyanate Index (which is 105%). The numbers corresponding to the amounts of the individual ingredients in the B-component below are expressed in parts by weight (PBW). The filler 20 (CaCO3), the internal mold release, and the molecular sieves are optional additive ingredients. However, the use of the internal mold release (IMR) and the molecular sieves are highly preferred. B-Component: 25 JEFFOL® G30-650 polyol 85 JEFFFOL® G31-35 polyol 7.75 SILOSIV® A3 molecular sieves 2.5 Mold-Wiz® INT1938MCH mold release 5 30 K-KAT® 5218 catalyst 0.75 FOMREZ® UL29 catalyst 0.25 CaCO3 40 34 WO 2005/049301 PCT/US2004/038118 The polyisocyanate component (A-Component) is SUPRASEC® 9700 isocyanate, from Huntsman. The two component mixing activated system is processed at an Isocyanate Index of 105%. This corresponds to a weight ratio of the two components on 5 an unfilled basis of 1.4/1 A/B (i.e., without the calcium carbonate filler shown). With said filler (as shown above) the weight ratio of the components, which satisfies the 105% Index, is 1:1. The polyol blend, with the additives, is the B-component. The polyisocyanate is the A-component. The composition of the B-Component blend (above) is by weight 10 (expressed as PBW). The component ratios are by weight and correspond to the quoted Isocyanate Index. The following reactivity observations were made on the catalyzed reaction system (without the fibrous reinforcement structure): 15 Room Temp 250 F Hot Plate Gel Hard Time Hard Time 21 min 22 min 52 sec Pultrusion Run: The system shown above, with 0.75 pbw of K-KAT® 5218 catalyst and 0.25 pbw 20 of FOMREZ® UL29 tin catalyst, was run on a pultrusion line to produce a glass fiber reinforced flat profile. The following observations were made: Die EXAMPLE 1: Line Speed where Comparative Example A: Line Speed Temp* powdering starts with K-KAT 5218 where powdering starts with 1.5 PBW catalyst / FOMREZ UL29 catalyst COSCAT® BiZn catalyst only as shown above 250 F 50"/min < 24"/ in 275 F 60"/min (very very slight powdering) 300 F 86"/min (very very slight powdering) 48"/min (heavier powdering) *The "Die Temp" is the surface temperature of the curing die. 25 A step change in line speed in production of 3 mm thick flat profiles is shown. The purges (i.e., surfaces of the composite during line stoppages) look better with the 35 WO 2005/049301 PCT/US2004/038118 catalyst package according to the invention. The powdering that is eventually observed with the catalyst package according to the invention is much less than with the BiZn catalyst package (which is not according to the invention). The pultruded parts made by the process of the invention cured up very well and 5 no glass read-through was observed. No problems with achieving complete fiber wetout were seen, even at 86"/min. The line speed of 86"/min was the maximum speed which could be achieved on the pultrusion line used. The use of the combination of the organoaluminum catalyst (i.e., Al-ac-ac) with 10 the organotin catalyst is a preferred embodiment of the invention. Comparative Example B and Examples 2 and 3: The following is a list of formulations for pultrusion systems, and some pultrusion trial results. Some of these systems (Ex-2 and Ex-3, which are both according to the 15 invention) showed an unexpected and surprising improvement in processability. Specifically, it was possible to process the inventive formulations consistently at higher than expected line speeds in a reactive pultrusion process using long glass fiber reinforcement. The principle factor that limits line speed in pultrusion, for these reactive polyurethane formulations, is the sloughing off of partially cured resin particles. This 20 phenomenon, known as "powdering", occurs at higher line speeds with the inventive formulations, relative to the others. The improvement appears to be related to the use of a combination of at least two different metal catalysts. The preferred formulations shown below contain an organotin catalyst (UL 29) in combination with an organobismuth catalyst (BiZn). The best performing system additionally contained an organoaluminum 25 catalyst (K-KAT 5218). The two inventive formulations are the last two on the right hand side of the Table I below. The organobismuth catalyst (BiZn) is believed to contain an organozinc compound as well as an organobismuth compund. The enhanced line speed performance may conceivably be due to an interaction of one organometal catalyst with organic species (such as ligands) from one or more of the other organometal catalysts. 30 However, it is currently believed that at least two different metals are required in the catalyst composition for the best results. 36 WO 2005/049301 PCT/US2004/038118 The formulations shown in Table I were run with SUPRASEC® 9700 isocyanate as the polyisocyanate. The glass fiber loading was about 80% by weight of the final pultruded part weight. Comparative Example B (shown in the Table below) is outside the invention. The 5 basic details of the pultrusion process, the glossary of formulation ingredients, and other relevant details may be found above. TABLE I: 10 Comp-B Ex-2 Ex-3 JEFFOL G30-650 polyol 85 85 85 JEFFOL G31-35 polyol 7.75 7.75 7.75 Techlube BR 550 product 0 0 0 INT 1938 MCH 7.5 7.5 7.5 Silosiv A3 sieve* 2.5 2.5 2.5 Fomrez UL 29 catalyst 0 0.1 0.1 Coscat BiZn product 1 1 1 Al-ac-ac [K-KAT 5218 catalyst**] 0 0 0.05 CaCO3 20 20 20 Iso/Polyol weight ratio 1.17 1.17 1.17 Iso/Polyol weight ratio 1 1 1 Line speed where powdering started 60"/min 78"/min 86"/min * From Grace Davison Co. ** From King Industries. 37

Claims (5)

1. A reaction system for the preparation of a fiber reinforced composite according to the pultrusion process comprising: (a) a reaction mixture comprising an isocyanate reactive composition and a polyisocyanate composition; 10 (b) a continuous fiber reinforcing material; and (c) a catalyst composition, wherein the catalyst composition contains a combination of at least two different metals selected from the group consisting of any of the metals of Groups IIIB, 15 IVB, VB, VIB, VIIB, VIIIB, IB, IA, IIA, IIA, IVA, VA, VIA, the Lanthanide series, and the Actinide series of the Periodic Table of the Elements in effective amounts, and wherein the combination of the reaction mixture and the catalyst composition 20 initially contains both free isocyanate groups and free alcoholic -OH groups, has a gel time greater than 768 seconds at 25oC, and a gel time less than 120 seconds at 175 0 C.

2. A reaction system for the preparation of a fiber reinforced composite according to 25 the pultrusion process comprising: (a) a reaction mixture comprising an isocyanate reactive composition and a polyisocyanate composition; (b) a continuous fiber reinforcing material; and (c) a catalyst composition, 30 wherein the catalyst composition contains a combination of at least two different metals selected from the group consisting of any of the metals of Groups IIIB, IVB, VB, VIB, VIIB, VIIIB, IB, IIIA, IVA, VA, VIA, the Lanthanide series, & the Actinide series of the Periodic Table of the Elements in effective amounts, and 38 WO 2005/049301 PCT/US2004/038118 wherein the combination of the reaction mixture and the catalyst composition initially contains both free isocyanate groups and free alcoholic -OH groups, has a gel time greater than 768 seconds at 25oC, and a gel time less than 120 seconds at 5 175 0 C.

3. The reaction system according to claim 2, wherein the reaction system is a mixing activated thermosetting system that cures by forming a covalently crosslinked organic polymer network structure, the organic polymer network structure 10 providing the matrix resin phase of a fiber reinforced composite.

4. The reaction system according to claim 2, wherein the polyisocyanate composition comprises one or more polyisocyanates of the MDI series, has a number averaged functionality of isocyanate groups in the range of from 2.3 to 15 2.9, and a free isocyanate group content in the range of from 10% by weight to

33.6% by weight. 5. The reaction system according to claim 2, wherein the isocyanate reactive composition comprises a mixture of (i) from 0 to 20% by weight of at least one 20 polyol having a number averaged molecular weight of 1500 or greater and a number averaged functionality of 2 to 4, (ii) 60 to 100% by weight of at least one polyol having a number averaged molecular weight between 250 and 750 and a number averaged functionality of 3 to 4, and (iii) 2 to about 30% by weight of at least one polyol having a number averaged functionality of 2 to 3 and a number 25 averaged molecular weight of less than 200; wherein the weights of (i) + (ii) + (iii) total 100% of the isocyanate reactive composition. 6. The reaction system according to claim 2, wherein the isocyanate reactive composition comprises a total of at least 10% by weight, relative to the total 30 weight of the isocyanate reactive composition, of at least one hydrophobic polyol selected from the group consisting of hydrocarbon backbone polyols of number averaged molecular weight greater than 500, fatty ester polyols of number 39 WO 2005/049301 PCT/US2004/038118 averaged molecular weight greater than 500, and fatty polyester polyols of number averaged molecular weight greater than 500. 7. The reaction system according to claim 6, wherein the at least one hydrophobic 5 polyol is a fatty polyester polyol having a number averaged functionality of organically bound isocyanate-reactive hydroxyl groups of greater than 2. 8. The reaction system according to claim 2, wherein the catalyst composition comprises an organobismuth catalyst and an organotin catalyst. 10 9. The reaction system according to claim 2, wherein the catalyst composition comprises an organotin catalyst and an organoaluminum catalyst. 10. The reaction system according to claim 2, wherein the catalyst composition 15 comprises an organobismuth catalyst and an organoaluminum catalyst. 11. The reaction system according to claim 2, wherein the catalyst composition comprises an organotin catalyst, an organoaluminum catalyst, and an organobismuth catalyst. 20 12. The reaction system according to claim 8 wherein the catalyst composition further. comprises at least one additional catalyst containing at least one metal selected from the group consisting of zinc and potassium. 25 13. A pultrusion process for preparing a fiber reinforced composite comprising the steps of: (a) pulling continuous fibers through an impregnation die while contacting the fibers with a catalyzed reaction mixture comprising an isocyanate reactive composition, a polyisocyanate composition, and a catalyst composition 30 sufficient to cause substantial polymerization of the catalyzed reaction mixture within the impregnation die to produce a composite of fibers coated by the catalyzed reaction mixture, which is not fully cured, 40 WO 2005/049301 PCT/US2004/038118 (b) directing the composite of fibers coated by the catalyzed reaction mixture through a heated curing die to further advance the cure of the catalyzed reaction mixture so as to produce a solid fiber reinforced composite, and (c) withdrawing the solid fiber reinforced composite from the curing die; 5 wherein said catalyst composition contains a combination of at least two different metals selected from the group consisting of any of the metals of Groups IIIB, IVB, VB, VIB, VIIB, VIIIB, IB, IA, IIA, IIIA, IVA, VA, VIA, the Lanthanide series, and the Actinide series of the Periodic Table of the Elements in effective 10 amounts, and wherein the catalyzed reaction mixture initially contains both free alcoholic -OH groups and free isocyanate (-NCO) groups, has a gel time 'of greater than 768 seconds at 25'C, and a gel time of less than 120 sec at 175°C. 15 14. A pultrusion process for preparing a fiber reinforced composite comprising the steps of: (a) pulling continuous fibers through an impregnation die while contacting the fibers with a catalyzed reaction mixture comprising an isocyanate reactive 20 composition, a polyisocyanate composition, and a catalyst composition sufficient to cause substantial polymerization of the catalyzed reaction mixture within the impregnation die to produce a composite of fibers coated by the catalyzed reaction mixture, which is not fully cured, (b) directing the composite of fibers coated by the catalyzed reaction mixture 25 through a heated curing die to further advance the cure of the catalyzed reaction mixture so as to produce a solid fiber reinforced composite, and (c) withdrawing the solid fiber reinforced composite from the curing die; wherein said catalyst composition contains a combination of at least two different 30 metals selected from the group consisting of any of the metals of Groups IIIB, IVB, VB, VIB, VIEB, VIIIB, IB, IIIA, IVA, VA, VIA, the Lanthanide series, and the Actinide series of the Periodic Table of the Elements in effective amounts, and 41 WO 2005/049301 PCT/US2004/038118 wherein the catalyzed reaction mixture initially contains both free alcoholic -OH groups and free isocyanate (-NCO) groups, has a gel time of greater than 768 seconds at 25 0 C, and a gel time of less than 120 sec at 175 0 C. 5 15. The process according to claim 14, wherein the catalyst composition comprises an organobismuth catalyst and an organotin catalyst. 16. The process according to claim 14, wherein the catalyst composition comprises an organotin catalyst and an organoaluminum catalyst. 10 17. The process according to claim 14, wherein the catalyst composition comprises an organobismuth catalyst and an organoaluminum catalyst. 18. The process according to claim 14, wherein the catalyst composition comprises an 15 organotin catalyst, an organoaluminum catalyst, and an organobismuth catalyst. 19. The process according to claim 15, wherein the catalyst composition further comprises at least one additional catalyst containing at least one metal selected from the group consisting of zinc and potassium. 20 20. The process according to claim 14, wherein the polyisocyanate composition comprises one or more polyisocyanates of the MDI series, has a number averaged functionality of isocyanate groups in the range of from 2.3 to 2.9, and a free isocyanate group content in the range of from 10% by weight to 33.6% by weight. 25 21. The process according to claim 14, wherein the isocyanate reactive composition comprises a mixture of (i) from 0 to 20% by weight of at least one polyol having a number averaged molecular weight of 1500 or greater and a number averaged functionality of 2 to 4, (ii) 60 to 100% by weight of at least one polyol having a 30 number averaged molecular weight between 250 and 750 and a number averaged functionality of 3 to 4, and (iii) 2 to about 30% by weight of a least one polyol having a number averaged functionality of 2 to 3 and a number averaged 42 WO 2005/049301 PCT/US2004/038118 molecular weight of less than 200; wherein the weights of (i) + (ii) + (iii) total 100% of said isocyanate reactive composition. 22. A fiber reinforced composite prepared according to the pultrusion process of 5 claim 13. 23. A fiber reinforced pultruded composite prepared from the reaction system of claim 1. 43