AU2002363125A1 - Method, composition and apparatus for controlled concrete - Google Patents

Description

METHOD. COMPOSITION AND APPARATUS FOR CONTROLLED CONCRETE

FIELD OF THE INVENTION

This invention relates to concrete materials and the use and apparatus for the use of such

materials. More particularly, the present invention relates to material that can in one instance be used as common concrete material and in another instance can be used as refractory concrete material.

Concrete materials have a variety of uses, including use as concrete in civil engineering

applications and as refractory material, such as in the steel production industry.

BACKGROUND OF THE INVENTION

Concrete materials can be applied by methods of mixing a batch of moldable concrete

material, transporting the material (conveyor belts, buckets, hoppers, pumps, and the like), and then

spreading such material into forms for setting into a hardened state. Typically, such concrete

materials are worked in the forms before the material hardening reaction sets the material in place

and becomes no longer pliable. Because the length of time in the hardening can represent dead time

in which further work cannot progress until hardening occurs, additives may be added to the concrete

material which will accelerate the rate of hardening. However, such additives cannot be so effective that hardening occurs in the application equipment or before completion of the working process to ensure homogeneity in the formed hardened structure. Accordingly, the use of accelerants cannot include accelerants which work too rapidly.

Concrete materials can be applied by either casting or projecting the refractory into place by dry application processes and wet application processes, such as by the "gunnite" and the "shotcrete" processes respectively, to provide a rapid formless application of a refractory. Field performance of gunnited or shotcreted refractory products can be good, but field installations are often affected by the problems of the existing technology which have very limited control of the smoothness and of the thiclcness of the application. To overcome these problems and achieve both the desired smooth finish and the controlled thickness, the refractory product applied by casting requires custom forms and may have issues with setting or curing times. Often, such setting processes require segmental casting and hardening such that seams are present in the refractory monolith, that is, the finished product is not a true monolithic form but has discontinuities which can be sources of performance problems.

What is needed is a concrete material, method and apparatus of application of such material to enable the continuous forming of a true monolithic structure with controlled dimensions. An objective of the present invention is a concrete material with a controlled hardening rate which can be used to form a continuous monolithic structure having controlled dimensions. Another objective of the present invention is to provide an apparatus capable of applying such material in order to form a seamless monolith without disruption of the surface of the structure and in a manner which can take advantage of the controlled hardening of the material. A further objective of the present

invention is a method of using such material and such apparatus, separately or together. These and

other objectives are provided herein.

RELATED ART

In US Patent Number 4,726,570 a system is provided for casting in a ladle using locking

means to hold a mandrel and associated members in the ladle against the buoyant force of a castable

refractory used in lining the ladle. When the castable refractory for solidified, the associated locking mechanism which locks the entire assembly to trunnions is released, and the entire assembly is lifted

from the ladle by use of suitable lifting equipment attached to a lifting eye.

In US Patent Number 5,958,312 a process is disclosed for the partial reconstruction of the

refractory lining in the upper zone of the wall area of a ladle as well as a device for performance of

the process. The process used a castable refractory with an inflating sealing body.

Japanese Application Number 10-064419, there is disclosed a refractory blend with

sodium polyacrylate for wet blasting construction. A liquid specific silicate is used as an

accelerating agent.

In Japanese Application Number 09-097895, there is disclosed a nozzle, and method of use, for mixing a monolithic refractory material and a hardening accelerator before executing the

monolithic refractory to the inside surface of a molten metal container.

SUMMARY OF THE INVENTION

In one aspect of the present invention is a method for forming a concrete structure using an advantageous method of mixing a concrete material and an accelerant composition. One advantage

of the invention is the critical control of the concrete hardening so that a monolithic structure can

be made. Further control can be obtained by the association or inclusion of selected optional

materials.

In another aspect, the present invention is an apparatus for performing the inventive method.

One element of such apparatus is the advantageous providing of a film as a slip-plane between the

concrete material and the apparatus so that a monolithic structure is obtained with controlled surface

tolerances.

In yet another aspect, the invention is a novel mixture composition of a concrete material and

an accelerant composition. An optional substance can be associated for further control of the hardening process. DESCRIPTIONS OF THE FIGURES

h Figure 1 there is depicted an apparatus embodied by the present invention in an initial step

of the construction process of a monolithic ladle lining.

In Figure 2 there is depicted the same apparatus in a subsequent step of the construction process.

In Figures 1 and 2 there is depicted use of an apparatus consistent with the present invention.

In Figure 1 there is depicted one embodiment of the present invention in which construction of a

monolilthic lining for a steel ladle is being performed. Depicted is an apparatus containing upright

support beam 1, horizontal support base 2, and angle brace 3. These members are rigidly fixed and

moved on casters 12 and anchored with positioning jack 11. Moving platform 4, provides a base for

an operator of the apparatus to stand. The operator positions adjustable slip-form braces 6, which

are perpendicularly attached to slip-form 5. The slip-form 5, can they be moved by unrolling or

rolling hoist cable 10 through the power of hoist motor 9. The operator controls such movement.

Slip-form 5 is positioned at a desired distance from the existing wall 14 and is set on existing floor

15. Concrete 13 is placed into the space between wall 14 and slip-form 5. Film dispensing roll 7

dispenses polymer film 8 into position between concrete 13 and slip-form 5. The interface between

slip-form 5 and polymer film 8 provides a slip-plane so that slip-form 5 can be repositioned once

concrete 13 has become sufficiently stabled to maintain structural integrity. Figure 2 depicts the elevation of slip-form 5 up the wall to enable the placement of additional concrete 13 to monolithically form with the previously placed concrete 13 as depicted in Figure 1.

DETAILED DESCRIPTION OF THE INVENTION

One embodiment of the present invention is a method for installing a concrete composition. This embodied process has the following: admixing (a) a first composition comprising a concrete composition, and (b) a second composition comprising an accelerant composition to form a castable or projectable admixture; casting or projecting the admixture into a space between a base structure and a moveable form having a surface area in an adjacent position relative to the base structure; enabling the admixture to set to form a structure with a free structure surface; and, moving the form to a different adjacent position. This above process is effectively repeated to form a monolithic structure section having a surface area larger than the surface area of the moveable form. A monolithic structure section is one in which the different structure sections formed between the form and the base structure are connected with a continuous structure. That is, no seams or other line of discontinuity are present so as to result in a difference in performance. For instance, in an application in which the base structure is a refractory vessel, the monolithic structure can be a ladle wall having a free surface which is exposed to molten metal during use of the vessel. The monolithic form of the wall results in there not being a seam or other discontinuity which enables molten metal to reach the vessel's outer metal wall in a manner which threatens a melt-down of the vessel.

The inventive process enables the practitioner to have the option to produce a monolithic structure having a variability of thickness of less than about 10 millimeters, preferable less than about 5 millimeters.

The accelerant composition useable in the present invention is the dry form of preferably one of the known accelerants used in the concrete art. A preferred form of the accelerant composition is a powder. Also, the present invention affords the option of using known accelerants in a form, which enables use of such accelerants which was not heretofore possible for the present applications. For instance, some known accelerants in a liquid state are too fast acting for use in the present applications. However, when used in a solid state, such as a powder, such material can now be used through use of the present inventive method. Such accelerating agents typically are believed to function by causing thickening or gelling, such as that resulting from flocculation associated with a rise in the pH of the composition. Such accelerating agents can also function by firming or hard- setting the concrete bond, that is, causing the onset of the bond phase of the system in which rigidity and load-bearing characteristics arise. In the present process the accelerant powder can be mixed with the concrete composition when the concrete composition is being transported from a holding state to being delivered to the site of use, such as in a concrete or refractory form. This can also be done with an intermediate, short-term holding step before delivery to the site of use. A preferred method of delivery is termed the "shotcreteing" method. In this method the concrete composition

is delivered under pressure, such as by air or water pressure, through a nozzle to a surface for

deposit. Advantageously, the accelerant is transported into the nozzle for mixing with the concrete

composition prior to its projection from the nozzle. Such mixing may alternatively be provided by

auger action.

Preferably, the process uses a second composition having the accelerant effectively in

association with a carrier to control dispersion and/or transportation of the accelerant. Such carrier

can be a powder, a liquid or a melt. The associated substance can optionally be present as a coating

on the accelerant powder. Preferably, such coatings can include fatty acids, or other soluble

encapsulation compositions.

Preferably, the carrier is a liquid and, more preferably, an organic liquid composition. Non- limiting examples of carrier substances are glycols. Preferred organic liquids are ethylene glycols,

propylene glycols, or other glycols which are liquid at room temperatures; oils, such as mineral or

synthetic oils; or other suitable liquids having viscosities and flash-points suitable for the present

uses.

Preferably, the second composition further comprises a carrier differing from the coating on

the accelerant powder. The carrier comprises one or more of a substance selected from a group

consisting of a powder, a liquid and a melt. The carrier works best when it is miscible in water. The term concrete composition contemplates one or many of calcium aluminum or

equivalent systems of inorganic materials used in engineering materials which harden to perform

useful functions of strength and load-bearing. Preferably, the concrete composition contains one or

more cement(s) selected from the group consisting of a calcium aluminate cement, calcium silicate

cement, a silicate bonded cement, a chlorine-bonded cement, a colloidal silica binder cement and a

colloidal alumina binder cement. In a preferred process, the concrete composition is a refractory

composition.

Preferably, the accelerant composition is from about 0.05 to about 5 weight percent of the

total weight of projectable admixture, more preferably from about 0.1 to about 1 weight percent of

the total weight of projectable admixture.

hi another embodiment, the process uses an accelerant composition which comprises both

a flocculating agent and a setting agent. More preferably, the process further comprises adjusting

the proportion of the flocculating agent and the setting agent to effectively control the action of the

accelerant powder to enable the projectable composition to temporarily flow. This adjustment can

be from job to job or during the course of a particular job as the conditions warrant.

In yet another embodiment, the process is used to construct a non-horizontal structure. For

example, one use can be to construct a vessel wall lining in a refractory vessel, h such an

application a form is provided adjacent to a vertical wall. Such form is parallel to the internal surface of the vessel and serves to hold a concrete composition in place until such composition

sufficiently sets or firms to be able to stand in place after removal of the form. Preferably, the

process further comprises supplying a slip-plane between the concrete composition and the moveable

form to enable the moving of the form to a different adjacent position so that the free wall surface

maintains integrity. The form can be moved up the wall, after starting the process at a lower or

bottom position of the vessel. In this use the process forms a wall section from bottom to top of the vessel in one monolithic form since the form is moved once a sufficient amount of the refractory

material in the lower portion of the mold firms and additional refractory material is supplied to fill

the then vacant space between wall and form above the material. This material bonds monolithically

with the existing material in the mold as the existing material in the upper portion of the mold is still

in a moldable state so as to be practically seamless. Optionally, the form could be moved laterally,

horizontal to the vessel bottom.

Preferably, the process uses an apparatus which disposes a film or equivalent barrier between

the refractory material and the form. This serves to provide a "slip-plane" function which prevents

frictional interaction between the form surface and the setting surface of the refractory, thereby avoiding erosion or abrasion of the refractory surface and disrupting the refractory surface.

Optionally, the process uses a slip-plane which comprises one or more materials selected from a

plastic, a rubber, a metallic foil, a paper and a screen. Preferably, the matrix is a latex or polymer

composition, such as, for example, a polyethylene, polypropylene, or polyester film. Similarly, in an application in which the formed structure is a horizontal monolithic structure

with a free top surface, the embodied process has the following:

admixing (a) a first composition comprising a concrete composition, and (b) a second

composition comprising an accelerant, preferably a powder, to form a castable or projectable

admixture; casting or projecting the admixture into a space between a base structure and a moveable

form having a surface area in an adjacent position relative to the base structure; enabling the admixture to set form a structure with a free structure surface; and,

working the admixture to form a monolithic structure having a variability of thickness of a

desired thickness.

In performing the invention, one selects a carrier which will enable the dispersion of the

accelerant composition and will enable a rate of dissolution of the accelerant to effect the subsequent rate of hardening. That is, one may balance the dispersion characteristics of the liquid and any

attenuation or other impact of the liquid on the dissolution rate on the accelerant. For example, upon

admixing the concrete composition and the accelerant composition, which is a mixture of accelerant

powder and carrier, the accelerant powder, being initially undissolved, dissolves at a predetermined

rate based upon particle size, accelerant powder coating, or carrier liquid. Accordingly, in a

preferred embodiment, after creation of the admixture, the initial hardening reaction is not occurring

or is occurring but at a relatively slower rate than with the presence of a pre-dissolved accelerant.

After a period of time, the rate accelerates as the accelerant dissolves and the concrete material commences to interact. The reaction continues to create a flocculation or setting.

In a preferred embodiment the moldable composition is a pumpable composition. The

pumpable composition comprises an admixture of a first composition containing a concrete

composition. This composition can be flowed through a pumping apparatus in which air or water,

which provides a projecting force, and an accelerant composition containing an accelerant powder

and optional substance(s) are mixed prior to projection through the nozzle to the surface upon which

the material is to be molded. Preferably, the optional substance includes an organic liquid. The

delayed reaction caused by the accelerant powder's dissolution permits the initial forming as by, for example, blades or vibrators, prior to any significant commencement of the hardening reaction under

acceleration due to the presence of the accelerant. Preferably such timing permits the continuous

formation of a monolithic form by fast incremental movement or by continuous movement of the application apparatus.

The method of the present invention allows the pumpable material to flow into a slip-form cavity and take the shape of the cavity prior to achieving a set. The delayed reaction between the

concrete material and the accelerant subsequently achieves a fast set which allows rapid movement

of the slip-form. The set material that is exposed as the slip-form is moved retains both a smooth

surface and the substantially-exact dimensions of the slip-form. The set material can support weight

immediately thus eliminating the need for a custom, application specific form, to achieve both

smoothness and thickness control. Unlike the prior art in which only the use of custom forms for

casting could achieve both the smoothness and dimensional tolerances, the present invention eliminates such restrictive practices. In prior methods, when casting, the material is entirely fluid

in the mold which creates a requirement of a mold or form of great strength. In accordance with the

present invention the new process requires only a relatively smaller amount of material to be fluid

at any one time, there by enabling use of a lighter and simpler forming structure, h addition,

conventional casting typically requires an extended cure time in the mold (excluding quick set

materials), often as much as 24-48 hours to achieve an acceptable set before form removal. The

present invention advantageously enables the elimination of extra cure time prior to mold removal after achieving the desired set.

The addition of the accelerant powder and carrier at the projection nozzle with this new

method is an advantage over the use of a quick set castable. The new inventive composition can be

held as a wet mix in hoppers or mixers for extended periods of time without fear of premature

setting. Then, in accordance with the present invention, the material sets after it has been admixed

with the accelerator soon after it enters the slip-form. This allows for far greater field flexibility on

installation.

The accelerant powder of the present invention comprises one or more compound(s) selected

from the known accelerant powders of the concrete or refractory arts, as well as accelerants not

heretofore used in such applications. Preferably, the accelerant powder is selected from alkali

compounds. Preferred alkali compounds are sodium, lithium or potassium compounds. Non-limiting

examples include sodium silicate, sodium aluminate, lithium carbonate, lithium citrate, potassium silicate, potassium aluminate, potassium carbonate, sodium carbonate, and lithium hydroxide. Other

known accelerants are also usable. Such accelerants include organic compounds, such as

triethanolamine or sulfate compounds, as non-limiting examples. The physical properties of the

accelerant powder can also be a consideration in the selection and use of the powder. Accordingly,

in yet another preferred embodiment, the accelerant powder is characterized by having a particle size

distribution which is effective to control the rate of dissolution and subsequent reaction. Complete dissolution is not necessary for effective reactions in all cases. Preferably, the particle size is small

enough to suspend the powder in the carrier media, but large enough to control dissolution for the

desired reaction rate.

The organic liquid can be any which is compatible with the other materials and the intended

use. Preferably, the relative proportions of concrete material, accelerant powder and organic liquid

are proportioned such that the moldable composition is moldable from about fifteen seconds to about

5 minutes. Such proportion enables the placement of the concrete material in a variety of field uses.

In a preferred refractory composition, the second composition comprises from about 30 to about 60 weight percent of accelerant powder and from about 40 to about 70 weight percent

propylene glycol.

h yet another embodiment, the present invention is an apparatus comprising (a) a first

application means for applying a moldable concrete composition to a base surface to produce a monolithic mass adhering to the base surface; (b) a forming means for slip-forming an outer surface

of the monolithic mass at a distance from the base surface; (c) a second application means for

applying a protective barrier between the monolithic mass and the forming means effective to

maintain the integrity of the outer surface; (d) a structural means for positioning the first application

means relative to the base surface effectively to produce the monolithic mass; and, (e) a control means for controlling the forming of the monolithic mass by effectively controlling positioning of

the structural means so that the monolithic mass maintains integrity and adheres to the base surface.

Preferably, the control means is exercised to maintain the dimensional tolerance desired. This embodiment can be used with known concrete compositions or the compositions of the present

invention, h an alternative preferred embodiment the apparatus further comprises a mixing means

for admixing a concrete composition and a concrete accelerant composition to produce the moldable

concrete composition. Embodiments can further comprise a means for admixing pressurized air to

provide the moldable concrete composition with sufficient energy to be projected through ambient

air to the surface.

A preferred mixing apparatus for use with the present invention is a shotcreteing apparatus.

Alternatively, a screw auger can be used to mix the materials and delivery of the material may be

by transportation without projection.

The following examples are intended to exemplify the invention and, in no aspect

whatsoever, limit it. EXAMPLE 1

CASTABLE FORMULATION

Samples of a castable formulation are produced using the following materials and amounts.

Material Sizing Wt. percent

White Fused Alumina 0-5000 Microns 60

Alumina Magnesia Spinel 0-700 Microns 20

Alumina Cement 5

Calcined Alumina 15

Dispersant As needed

This formulation is mixed with water to achieve a static flow of 65percent.

One sample (Sample A) of the castable formulation is mixed with 0.3 weight percent based

on weight of the castable formulation of sodium silicate solution (44 percent solids by weight). This

causes floccing to zero flow state within 15 seconds. This sample becomes too thick to flow into

a mold.

Another sample (Sample B) of the castable formulation is mixed with 0.3 percent of an

accelerator formulation containing 42 percent sodium silicate powder, 7 percent hydrated alumina

powder, and 51 percent propylene glycol liquid. All percentages of the accelerator foπnulation are percents by weight. Sample B produces the following results: Initial Flow Good Flow

Initial Floccing 0:48 (minutes/seconds)

Initial Firming 1:10 (minutes/seconds)

Final Set 4:05 (minutes/seconds)

"Good flow" means that the material still flows (as prior to accelerator addition).

"Final set" means that the material is not deformable to firm finger pressure.

EXAMPLE 2

A second Sample A is formulated as in Example 1. A different Sample B is formulated

using an addition of 0.45 percent (by weight) of an accelerator containing 20 percent sodium silicate

powder, 30 percent lithium carbonate powder, and 50 percent propylene glycol liquid. All

percentages of the accelerator formulation are percents by weight. Sample B produces the following

results:

Initial Flow Good Flow

Initial Floccing 0:44 (minutes/seconds)

Initial Firming 4:00 (minutes/seconds)

Final Set 8:15 (minutes/seconds)

A benefit of maintaining good flowability of Sample B of Examples 1 and 2 is that the

materials can be readily molded following the addition of the accelerator to enable a uniform

monolithic structure to be constructed.

Claims (27)

We claim:

1. A process for installing a concrete composition, the process comprising:

admixing (a) a first composition comprising a concrete composition, and (b) a second composition

comprising an accelerant powder to form a projectable admixture;

projecting the admixture into a space between a base wall and a moveable form having a surface area in an adjacent position relative to the base;

enabling the admixture to set to form a wall with a free wall surface; and, moving the form to a different adjacent position;

whereby the above process is repeated to form a monolithic wall section having a surface area larger than the surface area of the form.

2. The process of claim 1 wherein the second composition comprises the accelerant

effectively in association with one or more of a carrier substance(s) selected from the group

consisting of a powder, a liquid and a melt such that the one or more of the components controls the

action of the accelerant composition to enable the projectable composition to temporarily flow.

3. The process of claim 2 wherein the carrier substance(s) is an organic liquid composition.

4. The process of claim 1 wherein the process is performed to provide a variability of

thickness less than about ten millimeters.

5. The process of claim 2 wherein the carrier is miscible in water.

6. The process of claim 1 wherein the concrete composition comprises one or more

cement(s) selected from the group consisting of a calcium aluminate cement, a silicate bonded

cement, a chlorine-bonded cement, a colloidal silica binder cement, a calcium silicate cement, and

a colloidal alumina binder cement.

7. The process of claim 1 wherein the accelerant powder is from about 0.05 to about 5 weight percent of the total weight of projectable admixture.

8. The process of claim 7 wherein the accelerant powder is from about 0.1 to about 1

weight percent of the total weight of projectable admixture.

9. The process of claim 1 wherein the concrete composition is a refractory composition.

10. The process of claim 1 wherein the accelerant powder comprises a flocculating agent

and a setting agent.

11. The process of claim 10 further comprising adjusting the proportion of the

flocculating agent and the setting agent to effectively control the action of the accelerant powder to

enable the projectable composition to temporarily flow.

12. The process of claim 1 further comprising supplying a slip-plane between the concrete composition and the moveable form to enable moving the form to a different adjacent position so that the free wall surface maintains integrity.

13. The process of claim 12 wherein the slip-plane comprises one or more material selected from the group consisting of a plastic, a rubber, a metallic foil, a paper and a screen.

14. The process of claim 13 wherein the material is a latex or polymer composition.

15. A moldable composition comprising an admixture of (a) a first composition comprising a concrete composition, and (b) a second composition comprising (i) an accelerant powder and (ii) an organic liquid composition, the organic liquid composition being effectively associated with the accelerant powder so that, when the admixture is made, a reaction between the first composition and the accelerant powder is controlled to enable the moldable composition to temporarily flow.

16. The composition of claim 15 wherein the moldable composition is a pumpable composition.

17. The composition of claim 15 wherein the moldable composition is a castable composition.

18. The composition of claim 15 wherein the accelerant powder comprises one or more

compound(s) selected from the group consisting of sodium silicate, sodium aluminate, lithium

carbonate, lithium citrate, potassium silicate, potassium aluminate, potassium carbonate, sodium

carbonate, and lithium hydroxide.

19. The composition of claim 15 wherein the accelerant powder is characterized by

having a particle size distribution which is effective to control the rate of the reaction.

20. The composition of claim 15 wherein the organic liquid is a glycol.

21. The composition of claim 15 wherein the organic liquid is an oil.

22. The composition of claim 20 wherein the second composition comprises from about

30 to about 60 weight percent of accelerant powder and from about 40 to about 70 weight percent

propylene glycol.

23. The composition of claim 15 wherein the moldable composition is moldable from

about fifteen seconds to about 5 minutes.

24. An apparatus comprising:

(a) a first application means for applying a moldable concrete composition to a base surface to produce a monolithic mass adhering to the base surface;

(b) a forming means for slip-forming an outer surface on the monolithic mass at a distance from the base surface;

(c) a second application means for applying a protective barrier between the monolithic mass and the forming means effective to maintain the integrity of the outer surface;

(d) a structural means for positioning the first application means relative to the base surface effectively to produce the monolithic mass; and,

(e) a control means for controlling the forming of the monolithic mass by effectively controlling positioning of the structural means so that the monolithic mass maintains integrity and adheres to the base surface.

25. The apparatus of claim 24 further comprising a mixing means for admixing a concrete composition and a concrete accelerant composition to produce the moldable concrete composition.

26. The apparatus of claim 24 wherein the first application means further comprises a means for admixing pressurized air to provide the moldable concrete composition with sufficient energy to be projected tlirough ambient air to the surface.

27. The apparatus of claim 24 where the variability of thickness of the monolithic mass is less than about 10 millimeters.