AU2001278625A1 - Soda-lime-silica glass compositions - Google Patents
Soda-lime-silica glass compositionsInfo
- Publication number
- AU2001278625A1 AU2001278625A1 AU2001278625A AU7862501A AU2001278625A1 AU 2001278625 A1 AU2001278625 A1 AU 2001278625A1 AU 2001278625 A AU2001278625 A AU 2001278625A AU 7862501 A AU7862501 A AU 7862501A AU 2001278625 A1 AU2001278625 A1 AU 2001278625A1
- Authority
- AU
- Australia
- Prior art keywords
- glass
- cao
- silica glass
- typical
- na2o
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A soda lime silica glass suitable for forming by the float process is disclosed, having a composition containing 6- 12.4 wt % Na2O and 10.2-17 wt % CaO. The glass may also contain 68-75 wt % SiO2, 0-4 wt % A12O3, 0-3 wt % K2O, 0-5.5 wt % MgO. 0-2 wt % Fe2O3 and 0-0.5 wt % SO3. Compared with a typical known commercially produced soda lime silica glass, the proportion of Na2O is reduced in order to reduce raw material costs, and the proportion of CaO is increased. CaO and MgO may be adjusted relative to each other according to limestone and dolomite prices in the manufacturing locality: The above oxides are also adjusted to maintain the physical and optical properties of the glass as close as possible to those of the typical glass, two exceptions being the liquidus temperature, which is higher than the typical glass, and the fracture toughness, which is lower, and results in improved toughenability.
Applications Claiming Priority (3)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
GBGB0020471.9A GB0020471D0 (en) | 2000-08-19 | 2000-08-19 | Glass compositions |
GB0020471.9 | 2000-08-19 | ||
PCT/GB2001/003683 WO2002016277A1 (en) | 2000-08-19 | 2001-08-17 | Soda-lime-silica glass compositions |
Publications (1)
Publication Number | Publication Date |
---|---|
AU2001278625A1 true AU2001278625A1 (en) | 2002-03-04 |
Family
ID=9897935
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
AU2001278625A Abandoned AU2001278625A1 (en) | 2000-08-19 | 2001-08-17 | Soda-lime-silica glass compositions |
Country Status (6)
Country | Link |
---|---|
EP (1) | EP1313674B1 (en) |
AT (1) | ATE269276T1 (en) |
AU (1) | AU2001278625A1 (en) |
DE (1) | DE60103908T2 (en) |
GB (1) | GB0020471D0 (en) |
WO (1) | WO2002016277A1 (en) |
Families Citing this family (17)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US6878652B2 (en) | 2001-02-09 | 2005-04-12 | Ppg Industries Ohio, Inc. | Methods of adjusting glass melting and forming temperatures without substantially changing bending and annealing temperatures and glass articles produced thereby |
US6797658B2 (en) * | 2001-02-09 | 2004-09-28 | Ppg Industries Ohio, Inc. | Methods of adjusting temperatures of glass characteristics and glass articles produced thereby |
PT104282A (en) | 2008-12-05 | 2010-06-07 | Univ Do Porto | DSC SOLAR CELL GLASS SELECTION PROCESS |
CA2797415A1 (en) * | 2010-05-20 | 2011-11-24 | Cardinal Fg Company | Glass substrates for high temperature applications |
CN103819086B (en) * | 2012-11-16 | 2016-12-21 | 神华集团有限责任公司 | Method for preparing basic formula of soda-lime silicate glass and method for extracting aluminum from fly ash and co-producing glass |
WO2014082205A1 (en) | 2012-11-27 | 2014-06-05 | 神华集团有限责任公司 | Method for preparing soda-lime-silica glass basic formula and method for extracting aluminum from fly ash for co-production of glass |
US10611664B2 (en) | 2014-07-31 | 2020-04-07 | Corning Incorporated | Thermally strengthened architectural glass and related systems and methods |
MX2017001386A (en) | 2014-07-31 | 2017-08-21 | Corning Inc | Thermally tempered glass and methods and apparatuses for thermal tempering of glass. |
US11097974B2 (en) | 2014-07-31 | 2021-08-24 | Corning Incorporated | Thermally strengthened consumer electronic glass and related systems and methods |
GB201505091D0 (en) | 2015-03-26 | 2015-05-06 | Pilkington Group Ltd | Glass |
KR102492060B1 (en) | 2016-01-12 | 2023-01-26 | 코닝 인코포레이티드 | Thin thermally and chemically strengthened glass-based articles |
US11795102B2 (en) | 2016-01-26 | 2023-10-24 | Corning Incorporated | Non-contact coated glass and related coating system and method |
CN111065609A (en) | 2017-08-24 | 2020-04-24 | 康宁股份有限公司 | Glass with improved tempering capability |
TWI785156B (en) | 2017-11-30 | 2022-12-01 | 美商康寧公司 | Non-iox glasses with high coefficient of thermal expansion and preferential fracture behavior for thermal tempering |
IT201800006000A1 (en) * | 2018-06-04 | 2019-12-04 | METHOD FOR MAKING A SAFETY GLASS AND GLASS SO OBTAINED | |
WO2021025981A1 (en) | 2019-08-06 | 2021-02-11 | Corning Incorporated | Glass laminate with buried stress spikes to arrest cracks and methods of making the same |
EP4296243A1 (en) | 2022-06-20 | 2023-12-27 | IPGR e. V. | Mixture of raw materials, method for reducing the content of sodium oxide (na2o) in glass and container glass |
Family Cites Families (7)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4701425A (en) * | 1986-05-19 | 1987-10-20 | Libbey-Owens-Ford Co. | Infrared and ultraviolet absorbing glass compositions |
FR2660921B1 (en) * | 1990-04-13 | 1993-11-26 | Saint Gobain Vitrage Internal | GLASS IN TINTED GLASS, PARTICULARLY FOR THE ROOF OF MOTOR VEHICLES. |
US5030594A (en) * | 1990-06-29 | 1991-07-09 | Ppg Industries, Inc. | Highly transparent, edge colored glass |
RU2013392C1 (en) * | 1991-10-28 | 1994-05-30 | Юлия Алексеевна Щепочкина | Glass |
KR100206628B1 (en) * | 1992-04-22 | 1999-07-01 | 마쯔무라 미노루 | Glass panes for vehicles |
FR2765569B3 (en) * | 1997-07-01 | 1999-07-16 | Saint Gobain Vitrage | GLASS COMPOSITION OF THE SILICO-SODO-CALCIUM TYPE |
JPH11240735A (en) * | 1998-02-27 | 1999-09-07 | Asahi Glass Co Ltd | Glass composition for use as substrate |
-
2000
- 2000-08-19 GB GBGB0020471.9A patent/GB0020471D0/en not_active Ceased
-
2001
- 2001-08-17 DE DE60103908T patent/DE60103908T2/en not_active Expired - Fee Related
- 2001-08-17 AT AT01956706T patent/ATE269276T1/en not_active IP Right Cessation
- 2001-08-17 EP EP01956706A patent/EP1313674B1/en not_active Expired - Lifetime
- 2001-08-17 AU AU2001278625A patent/AU2001278625A1/en not_active Abandoned
- 2001-08-17 WO PCT/GB2001/003683 patent/WO2002016277A1/en active IP Right Grant
Also Published As
Publication number | Publication date |
---|---|
WO2002016277A1 (en) | 2002-02-28 |
ATE269276T1 (en) | 2004-07-15 |
DE60103908T2 (en) | 2005-07-28 |
EP1313674A1 (en) | 2003-05-28 |
EP1313674B1 (en) | 2004-06-16 |
WO2002016277A8 (en) | 2002-08-29 |
GB0020471D0 (en) | 2000-10-11 |
DE60103908D1 (en) | 2004-07-22 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
AU2001278625A1 (en) | Soda-lime-silica glass compositions | |
US5380685A (en) | Bronze-colored infrared and ultraviolet radiation absorbing glass | |
KR910009578A (en) | Neutral gray low permeability nickel-free glass | |
US5364820A (en) | Neutral gray-colored infrared and ultraviolet radiation absorbing glass | |
EP0555552B1 (en) | Green-colored infrared and ultraviolet radiation absorbing glass and method of producing same | |
CA2048061C (en) | Ultraviolet absorbing green tinted glass | |
AU699949B2 (en) | Glass compositions | |
KR880000342A (en) | Tempered Glass Products and Manufacturing Method | |
TW200513447A (en) | UV-radiation absorbing glass with reduced absorption of visible light and methods of making and using same | |
KR960705749A (en) | Glass composition (GLASS COMPOSlTlON) | |
MXPA05008807A (en) | Colored glass compositions and automotive vision panels with reduced transmitted color shift. | |
SE9603215L (en) | Very dark gray lime-soda silicate glass | |
EP0439602A1 (en) | Infrared radiation absorbing blue glass composition | |
CA2265691C (en) | Blue colored glass composition | |
JPH09315835A (en) | Deep gray glass | |
SK282996B6 (en) | Mineral fibre | |
ATE307096T1 (en) | SODA LIME GLASS-LIKE GLASS COMPOSITIONS | |
JPH10265239A (en) | Ultraviolet ray and infrared ray absorption glass | |
KR970059125A (en) | Method of manufacturing glass | |
ATE427920T1 (en) | COLORED GLASS COMPOSITIONS AND AUTOMOTIVE GLAZING WITH REDUCED COLOR TRANSMITTANCE SHIFT | |
MXPA03011768A (en) | Grey glass composition for production of windows. | |
CA2148663A1 (en) | Champagne colored glasses | |
TH52473A (en) | Glass mixtures | |
RU2001103794A (en) | Method for the production of mineral fibers from rocks | |
SU1020389A1 (en) | Glass |