AU2001253399A1 - Alkaline pulp having low average degree of polymerization values and method of producing the same - Google Patents
Alkaline pulp having low average degree of polymerization values and method of producing the sameInfo
- Publication number
- AU2001253399A1 AU2001253399A1 AU2001253399A AU5339901A AU2001253399A1 AU 2001253399 A1 AU2001253399 A1 AU 2001253399A1 AU 2001253399 A AU2001253399 A AU 2001253399A AU 5339901 A AU5339901 A AU 5339901A AU 2001253399 A1 AU2001253399 A1 AU 2001253399A1
- Authority
- AU
- Australia
- Prior art keywords
- average degree
- producing
- polymerization
- same
- low average
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
The present invention provides compositions, useful for making lyocell fibers, having a high hemicellulose content, a low copper number and including cellulose that has a low average degree of polymerization (D.P.) and a narrow molecular weight distribution. Further, the present invention provides processes for making compositions, useful for making lyocell fibers, by contacting an alkaline pulp having a high hemicellulose content of at least about 7% with an oxidant sufficient to reduce the average degree of polymerization to about 200 to 1100 without substantially reducing the hemicellulose content or increasing the copper number of the pulp.
Applications Claiming Priority (3)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US09/574,538 US6331354B1 (en) | 1996-08-23 | 2000-05-18 | Alkaline pulp having low average degree of polymerization values and method of producing the same |
US09/574,538 | 2000-05-18 | ||
PCT/US2001/011897 WO2001088236A2 (en) | 2000-05-18 | 2001-04-11 | Alkaline pulp having low average degree of polymerization values and method of producing the same |
Publications (1)
Publication Number | Publication Date |
---|---|
AU2001253399A1 true AU2001253399A1 (en) | 2001-11-26 |
Family
ID=24296571
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
AU2001253399A Abandoned AU2001253399A1 (en) | 2000-05-18 | 2001-04-11 | Alkaline pulp having low average degree of polymerization values and method of producing the same |
Country Status (14)
Country | Link |
---|---|
US (4) | US6331354B1 (en) |
EP (1) | EP1311717B1 (en) |
JP (2) | JP2003533602A (en) |
KR (1) | KR100834248B1 (en) |
CN (1) | CN100402741C (en) |
AT (1) | ATE335873T1 (en) |
AU (1) | AU2001253399A1 (en) |
BR (1) | BR0110890B1 (en) |
CA (1) | CA2406517C (en) |
DE (1) | DE60122169T2 (en) |
ES (1) | ES2265428T3 (en) |
MX (1) | MXPA02011317A (en) |
TW (1) | TWI282829B (en) |
WO (1) | WO2001088236A2 (en) |
Families Citing this family (65)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US6471727B2 (en) * | 1996-08-23 | 2002-10-29 | Weyerhaeuser Company | Lyocell fibers, and compositions for making the same |
US6331354B1 (en) | 1996-08-23 | 2001-12-18 | Weyerhaeuser Company | Alkaline pulp having low average degree of polymerization values and method of producing the same |
US6686040B2 (en) * | 1999-02-24 | 2004-02-03 | Weyerhaeuser Company | Use of thinnings and other low specific gravity wood for lyocell products |
US6797113B2 (en) * | 1999-02-24 | 2004-09-28 | Weyerhaeuser Company | Use of thinnings and other low specific gravity wood for lyocell pulps method |
US6686039B2 (en) * | 1999-02-24 | 2004-02-03 | Weyerhaeuser Company | Use of thinnings and other low specific gravity wood for lyocell pulps |
US6685856B2 (en) * | 1999-02-24 | 2004-02-03 | Weyerhaeuser Company | Use of thinnings and other low specific gravity wood for lyocell products method |
US20030032705A1 (en) * | 2001-08-07 | 2003-02-13 | Otter James William | Ethylene terpolymer adhesive for condensing furnace heat exchanger laminate material |
US6833187B2 (en) * | 2003-04-16 | 2004-12-21 | Weyerhaeuser Company | Unbleached pulp for lyocell products |
US7097737B2 (en) * | 2003-04-16 | 2006-08-29 | Weyerhaeuser Company | Method of making a modified unbleached pulp for lyocell products |
US20040207110A1 (en) * | 2003-04-16 | 2004-10-21 | Mengkui Luo | Shaped article from unbleached pulp and the process |
US6790527B1 (en) * | 2003-04-16 | 2004-09-14 | Weyerhaeuser Company | Lyocell fiber from unbleached pulp |
JP4550437B2 (en) * | 2004-01-20 | 2010-09-22 | ポリマテック株式会社 | Polybenzazole molded body and method for producing the same |
US20060070711A1 (en) * | 2004-09-30 | 2006-04-06 | Mengkui Luo | Low pH treatment of pulp in a bleach sequence to produce pulp having low D.P. and low copper number for use in lyocell manufacture |
US20060065377A1 (en) * | 2004-09-30 | 2006-03-30 | Mengkui Luo | High PH treatment of pulp in a bleach sequence to produce pulp having low D.P. and low copper number for use in lyocell manufacture |
US20060223992A1 (en) * | 2005-03-31 | 2006-10-05 | Mengkui Luo | Microcrystalline cellulose and method for making |
US20060219376A1 (en) * | 2005-03-31 | 2006-10-05 | Mengkui Luo | Microcrystalline cellulose and method for making |
PT2527531E (en) * | 2005-05-02 | 2014-11-03 | Int Paper Co | Ligno cellulosic materials and the products made therefrom |
CN100395385C (en) * | 2005-11-16 | 2008-06-18 | 东华大学 | Preparation method of lyocell fiber used for cord thread |
JP5371441B2 (en) * | 2005-12-23 | 2013-12-18 | ビーエーエスエフ ソシエタス・ヨーロピア | Solvent system based on molten ionic liquid, its production and its use to produce regenerated carbohydrates |
US8187421B2 (en) * | 2006-03-21 | 2012-05-29 | Georgia-Pacific Consumer Products Lp | Absorbent sheet incorporating regenerated cellulose microfiber |
US8187422B2 (en) * | 2006-03-21 | 2012-05-29 | Georgia-Pacific Consumer Products Lp | Disposable cellulosic wiper |
US7718036B2 (en) | 2006-03-21 | 2010-05-18 | Georgia Pacific Consumer Products Lp | Absorbent sheet having regenerated cellulose microfiber network |
US8540846B2 (en) | 2009-01-28 | 2013-09-24 | Georgia-Pacific Consumer Products Lp | Belt-creped, variable local basis weight multi-ply sheet with cellulose microfiber prepared with perforated polymeric belt |
AT503610B1 (en) * | 2006-05-10 | 2012-03-15 | Chemiefaser Lenzing Ag | METHOD FOR PRODUCING A PULP |
US7390566B2 (en) * | 2006-06-30 | 2008-06-24 | Weyerhaeuser Company | Viscose product |
US7670678B2 (en) * | 2006-12-20 | 2010-03-02 | The Procter & Gamble Company | Fibers comprising hemicellulose and processes for making same |
US7951264B2 (en) * | 2007-01-19 | 2011-05-31 | Georgia-Pacific Consumer Products Lp | Absorbent cellulosic products with regenerated cellulose formed in-situ |
US20080241536A1 (en) * | 2007-03-29 | 2008-10-02 | Weyerhaeuser Co. | Method for processing cellulose in ionic liquids and fibers therefrom |
WO2010033536A2 (en) | 2008-09-16 | 2010-03-25 | Dixie Consumer Products Llc | Food wrap basesheet with regenerated cellulose microfiber |
CN102341413B (en) * | 2009-03-09 | 2014-09-17 | 柯兰姆有限公司 | Shaped cellulose manufacturing process combined with pulp mill recovery system |
US9845575B2 (en) * | 2009-05-14 | 2017-12-19 | International Paper Company | Fibrillated blend of lyocell low DP pulp |
US9511167B2 (en) | 2009-05-28 | 2016-12-06 | Gp Cellulose Gmbh | Modified cellulose from chemical kraft fiber and methods of making and using the same |
US9512237B2 (en) | 2009-05-28 | 2016-12-06 | Gp Cellulose Gmbh | Method for inhibiting the growth of microbes with a modified cellulose fiber |
KR101797942B1 (en) | 2009-05-28 | 2017-11-15 | 게페 첼루로제 게엠베하 | Modified cellulose from chemical kraft fiber and methods of making and using the same |
US9512563B2 (en) | 2009-05-28 | 2016-12-06 | Gp Cellulose Gmbh | Surface treated modified cellulose from chemical kraft fiber and methods of making and using same |
JP6254078B2 (en) | 2011-05-23 | 2017-12-27 | ゲーペー ツェルローゼ ゲーエムベーハー | Conifer craft fibers with improved whiteness and brightness, and methods of making and using the same |
CA3202964A1 (en) | 2011-12-06 | 2013-06-13 | Delta Faucet Company | Ozone distribution in a faucet |
KR102093167B1 (en) | 2012-01-12 | 2020-03-26 | 게페 첼루로제 게엠베하 | A low viscosity kraft fiber having reduced yellowing properties and methods of making and using the same |
EP3483316A1 (en) * | 2012-02-14 | 2019-05-15 | International Paper Company | Composite polymer |
AU2013249725B2 (en) | 2012-04-18 | 2017-04-20 | Gp Cellulose Gmbh | The use of surfactant to treat pulp and improve the incorporation of kraft pulp into fiber for the production of viscose and other secondary fiber products |
JP6075976B2 (en) * | 2012-06-15 | 2017-02-08 | 日本製紙株式会社 | Method for producing dissolved kraft pulp |
US20140155301A1 (en) * | 2012-11-30 | 2014-06-05 | Api Intellectual Property Holdings, Llc | Processes and apparatus for producing nanocellulose, and compositions and products produced therefrom |
CA2898417C (en) | 2013-02-08 | 2021-07-27 | Arthur J. Nonni | Softwood kraft fiber having an improved .alpha.-cellulose content and its use in the production of chemical cellulose products |
JP6379116B2 (en) | 2013-03-14 | 2018-08-22 | ゲーペー ツェルローゼ ゲーエムベーハー | Method for making high performance, low viscosity kraft fiber using acid bleaching sequence and fiber made by the process |
KR102180665B1 (en) | 2013-03-15 | 2020-11-23 | 게페 첼루로제 게엠베하 | A low viscosity kraft fiber having an enhanced carboxyl content and methods of making and using the same |
CO7150300A1 (en) | 2013-06-27 | 2014-12-29 | Univ Antioquia | Production of a new multipurpose agglomerated cellulosic excipient |
US20150184338A1 (en) * | 2013-12-31 | 2015-07-02 | Weyerhaeuser Nr Company | Treated kraft pulp compositions and methods of making the same |
SE538064C2 (en) * | 2014-06-17 | 2016-02-23 | Valmet Oy | Method of producing dissolving pulp from lignocellulosic materials |
SE538752C2 (en) * | 2014-11-21 | 2016-11-08 | Innventia Ab | Process for the production of a treated pulp, treated pulp, and textile fibres produced from the treated pulp |
US9382337B2 (en) * | 2014-12-09 | 2016-07-05 | Rayonier Performance Fibers, Llc | Hydrogel forming material from byproduct pulp fines |
KR101714384B1 (en) * | 2014-12-26 | 2017-03-09 | 도레이케미칼 주식회사 | Thermaplastic cellulose ester yarn, and Manufacturing method thereof |
SG10201503723TA (en) * | 2015-05-12 | 2016-12-29 | Pt Sateri Viscose Internat | Dissolving Pulp |
CN115093008A (en) | 2015-12-21 | 2022-09-23 | 德尔塔阀门公司 | Fluid delivery system comprising a disinfection device |
SE539163C2 (en) * | 2016-01-18 | 2017-04-25 | Valmet Oy | Chlorine dioxide stage for controlling viscosity in dissolving pulps |
US9926665B2 (en) | 2016-02-25 | 2018-03-27 | International Paper Company | Crosslinked cellulose as precursor in production of high-grade cellulose derivatives and related technology |
JP6423838B2 (en) * | 2016-09-23 | 2018-11-14 | 日本製紙株式会社 | Method for producing dissolved kraft pulp |
EP3541849B1 (en) | 2016-11-16 | 2023-11-15 | GP Cellulose GmbH | Modified cellulose from chemical fiber and methods of making and using the same |
EP3536833A1 (en) | 2018-03-06 | 2019-09-11 | Lenzing Aktiengesellschaft | Lyocell fibres without mannan |
EP3536850A1 (en) | 2018-03-06 | 2019-09-11 | Lenzing Aktiengesellschaft | Pulp and lyocell articles with reduced cellulose content |
TWI814782B (en) * | 2018-03-06 | 2023-09-11 | 奧地利商蘭仁股份有限公司 | Solvent-spun cellulosic fibre |
EP3536852A1 (en) | 2018-03-06 | 2019-09-11 | Lenzing Aktiengesellschaft | Pulp and lyocell fibre with adjustable degree of whiteness |
TW201938591A (en) | 2018-03-06 | 2019-10-01 | 奧地利商蘭仁股份有限公司 | Dissolving pulp |
US11352748B2 (en) | 2018-07-31 | 2022-06-07 | International Paper Company | Crosslinked pulps, cellulose ether products made therefrom; and related methods of making pulps and cellulose ether products |
KR102254525B1 (en) * | 2020-12-14 | 2021-05-24 | (주)네오피에스 | Eco-friendly fabric with excellent UV protection and antibacterial properties and its manufacturing method |
CN112853796A (en) * | 2021-01-07 | 2021-05-28 | 杭州融凯盛科技有限公司 | Preparation method for modifying papermaking pulp into pulp special for lyocell fibers |
Family Cites Families (125)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US1860432A (en) * | 1928-08-22 | 1932-05-31 | Brown Co | Process of lowering the solution viscosity of cellulose fiber |
US2811518A (en) * | 1955-06-07 | 1957-10-29 | Rayonier Inc | Alkaline refining of wood pulp |
NL224413A (en) | 1957-01-28 | |||
US3023104A (en) | 1960-07-05 | 1962-02-27 | American Viscose Corp | Food compositions incorporating cellulose crystallite aggregates |
US3141875A (en) | 1961-03-15 | 1964-07-21 | Fmc Corp | Crystallite aggregates disintegrated in acid medium |
US3251824A (en) | 1961-08-22 | 1966-05-17 | Fmc Corp | Method of preparing stable aqueous dispersion-forming cellulosic aggregates |
US3255071A (en) | 1963-10-25 | 1966-06-07 | Theodor N Kleinert | Process for production of alkali cellulose in the absence of an aqueous liquid phase |
US3388119A (en) | 1965-07-19 | 1968-06-11 | Fmc Corp | Non-fibrous particulate cellulose and method of making same |
US3539365A (en) | 1967-02-13 | 1970-11-10 | Fmc Corp | Dispersing and stabilizing agent comprising beta-1,4 glucan and cmc and method for its preparation |
SE314581B (en) | 1968-10-29 | 1969-09-08 | Mo Och Domsjoe Ab | |
SE335053B (en) | 1969-05-13 | 1971-05-10 | Mo Och Domsjoe Ab | |
US3632469A (en) * | 1969-06-05 | 1972-01-04 | Ethyl Corp | Process for the manufacture of dissolving grade pulp |
US3833438A (en) | 1972-08-30 | 1974-09-03 | Asahi Chemical Ind | Process for the manufacture of a non-woven web of continuous filaments through the wet stretch spinning method |
DE2311180C3 (en) | 1973-03-07 | 1982-02-25 | Chemiefaser Lenzing AG, 4860 Lenzing, Oberösterreich | Process for the production of flame-retardant regenerated cellulose fibers |
US4338158A (en) | 1976-04-09 | 1982-07-06 | Weyerhaeuser Company | Pulping in the presence of a protector |
AU508480B2 (en) | 1977-04-13 | 1980-03-20 | Asahi Kasei Kogyo Kabushiki Kaisha | Microcrystalline cellulose excipient and pharmaceutical composition containing thesame |
US4416698A (en) | 1977-07-26 | 1983-11-22 | Akzona Incorporated | Shaped cellulose article prepared from a solution containing cellulose dissolved in a tertiary amine N-oxide solvent and a process for making the article |
US4211574A (en) | 1977-07-26 | 1980-07-08 | Akzona Incorporated | Process for making a solid impregnated precursor of a solution of cellulose |
US4246221A (en) | 1979-03-02 | 1981-01-20 | Akzona Incorporated | Process for shaped cellulose article prepared from a solution containing cellulose dissolved in a tertiary amine N-oxide solvent |
US4142913A (en) | 1977-07-26 | 1979-03-06 | Akzona Incorporated | Process for making a precursor of a solution of cellulose |
US4144080A (en) | 1977-07-26 | 1979-03-13 | Akzona Incorporated | Process for making amine oxide solution of cellulose |
US4256613A (en) | 1977-11-25 | 1981-03-17 | Akzona Incorporated | Composition and process for making precipitated nylon-cellulose biconstituent composition |
US4145532A (en) | 1977-11-25 | 1979-03-20 | Akzona Incorporated | Process for making precipitated cellulose |
US4196282A (en) | 1977-11-25 | 1980-04-01 | Akzona Incorporated | Process for making a shapeable cellulose and shaped cellulose products |
US4324593A (en) | 1978-09-01 | 1982-04-13 | Akzona Incorporated | Shapeable tertiary amine N-oxide solution of cellulose, shaped cellulose product made therefrom and process for preparing the shapeable solution and cellulose products |
US4295927A (en) | 1979-06-15 | 1981-10-20 | Weyerhaeuser Company | Method and apparatus for treating pulp with oxygen and storing the treated pulp |
US4298426A (en) | 1979-06-15 | 1981-11-03 | Weyerhaeuser Company | Method and apparatus for treating pulp with oxygen in a multi-stage bleaching sequence |
US4295926A (en) | 1979-06-15 | 1981-10-20 | Weyerhaeuser Company | Method and apparatus for treating pulp with oxygen |
US4295925A (en) | 1979-06-15 | 1981-10-20 | Weyerhaeuser Company | Treating pulp with oxygen |
US4290815A (en) | 1980-01-28 | 1981-09-22 | Akzona Incorporated | Use of co-solvents in amine N-oxide solutions |
SE434284B (en) | 1980-05-07 | 1984-07-16 | Mo Och Domsjoe Ab | PROCEDURES FOR OXYGEN DELIGNIFICATION OF CHEMICAL CONSUMPED CELLULOSAMASSA TO WHICH AROMATIC DIAMINES ARE PROVIDED |
DE3034685C2 (en) | 1980-09-13 | 1984-07-05 | Akzo Gmbh, 5600 Wuppertal | Cellulose molding and spinning mass with low proportions of low molecular weight breakdown products |
ZA834139B (en) | 1982-06-08 | 1984-03-28 | Courtaulds Plc | Polymer solutions |
JPS60139873A (en) | 1983-12-26 | 1985-07-24 | 旭化成株式会社 | Modification of fiber material |
GB2208277B (en) | 1987-07-30 | 1991-11-13 | Courtaulds Plc | Cellulosic fibre |
US4939016A (en) | 1988-03-18 | 1990-07-03 | Kimberly-Clark Corporation | Hydraulically entangled nonwoven elastomeric web and method of forming the same |
US5330567A (en) | 1988-08-16 | 1994-07-19 | Lenzing Aktiengesellschaft | Process and arrangement for preparing a solution of cellulose |
US5094690A (en) | 1988-08-16 | 1992-03-10 | Lenzing Aktiengesellschaft | Process and arrangement for preparing a solution of cellulose |
AT395246B (en) | 1990-07-16 | 1992-10-27 | Chemiefaser Lenzing Ag | SOLUTION OF CELLULOSE IN WATER AND N-METHYL-MORPHOLIN-N-OXIDE |
US5520869A (en) | 1990-10-12 | 1996-05-28 | Courtaulds Plc | Treatment of fibre |
AT395724B (en) | 1990-12-07 | 1993-02-25 | Chemiefaser Lenzing Ag | METHOD FOR PRODUCING CELLULOSE MOLDED BODIES |
DE4040242A1 (en) | 1990-12-15 | 1992-06-17 | Peter Roger Dipl Ing Nyssen | METHOD AND DEVICE FOR PRODUCING FINE FIBERS FROM THERMOPLASTIC POLYMERS |
GB9103297D0 (en) | 1991-02-15 | 1991-04-03 | Courtaulds Plc | Fibre production method |
GB9109091D0 (en) | 1991-04-25 | 1991-06-12 | Courtaulds Plc | Dyeing |
CA2071185C (en) | 1991-06-14 | 1995-02-07 | Jorge Luiz Colodette | Process for delignifying lignocellulosic pulp by means of oxygen |
GB9122318D0 (en) | 1991-10-21 | 1991-12-04 | Courtaulds Plc | Treatment of elongate members |
JP3190979B2 (en) | 1991-11-19 | 2001-07-23 | 旭化成株式会社 | Method for producing cellulose molded article |
US5605567A (en) | 1991-12-05 | 1997-02-25 | Weyerhaueser Company | Method of producing cellulose dope |
US5277857A (en) | 1992-01-17 | 1994-01-11 | Viskase Corporation | Method of making a cellulose food casing |
ATA53792A (en) | 1992-03-17 | 1995-02-15 | Chemiefaser Lenzing Ag | METHOD FOR PRODUCING CELLULOSIC MOLDED BODIES, DEVICE FOR IMPLEMENTING THE METHOD AND USE OF A SPINNING DEVICE |
AT397927B (en) | 1992-05-27 | 1994-08-25 | Chemiefaser Lenzing Ag | BACKFLOWABLE FILTER DEVICE FOR FILTRATION OF HIGH VISCUS LIQUIDS |
US5362867A (en) | 1992-05-27 | 1994-11-08 | Formosa Chemicals & Fibre Corporation | Method of making cellulose yarn solution |
US5417909A (en) | 1992-06-16 | 1995-05-23 | Thuringisches Institut Fur Textil- Und Kunststoff-Forschung E.V. | Process for manufacturing molded articles of cellulose |
US5693296A (en) | 1992-08-06 | 1997-12-02 | The Texas A&M University System | Calcium hydroxide pretreatment of biomass |
GB2270030B (en) | 1992-08-19 | 1996-06-19 | Courtaulds Plc | Method of producing fibre or film |
EP0590401B1 (en) * | 1992-09-24 | 1999-12-15 | Daicel Chemical Industries, Ltd. | Process for the preparation of a fatty acid ester of cellulose |
AT398588B (en) | 1992-12-02 | 1994-12-27 | Voest Alpine Ind Anlagen | METHOD FOR THE PRODUCTION OF VISCOSE CELLS |
JPH06220213A (en) | 1993-01-22 | 1994-08-09 | Mokushitsu Shinsozai Gijutsu Kenkyu Kumiai | Lignocellulose molding and its preparation |
FR2700772A1 (en) | 1993-01-27 | 1994-07-29 | Michelin Rech Tech | Composition, capable of giving fibers or films, based on cellulose formate. |
JPH06234881A (en) | 1993-02-10 | 1994-08-23 | Mitsubishi Rayon Co Ltd | Liquid-crystalline cellulose solution |
DE69430654T2 (en) | 1993-02-16 | 2003-02-06 | Mitsubishi Rayon Co | SOLUTION OF CELLULOSE FOR MOLDING AND METHOD FOR PRODUCING MOLDS THEREOF |
GB9304151D0 (en) | 1993-03-02 | 1993-04-21 | Courtaulds Plc | Fibre |
BR9400682A (en) | 1993-03-05 | 1994-10-18 | Akzo Nv | Apparatus for the fusing spinning of multifilament yarns and their application |
GB9304887D0 (en) | 1993-03-10 | 1993-04-28 | Courtaulds Plc | Fibre treatment |
US5662858A (en) | 1993-04-21 | 1997-09-02 | Lenzing Aktiengesellschaft | Process for the production of cellulose fibres having a reduced tendency to fibrillation |
AT399348B (en) | 1993-05-05 | 1995-04-25 | Chemiefaser Lenzing Ag | FORM- OR SPIDING MASS CONTAINING CELLULOSE AND USE OF CERTAIN SUBSTANCES FOR YOUR STABILIZATION |
GB9309617D0 (en) | 1993-05-11 | 1993-06-23 | Courtaulds Fibres Ltd | Fibre production process |
US5652001A (en) | 1993-05-24 | 1997-07-29 | Courtaulds Fibres Limited | Spinnerette |
ZA943387B (en) | 1993-05-24 | 1995-02-17 | Courtaulds Fibres Holdings Ltd | Spinning cell |
US5413631A (en) | 1993-05-24 | 1995-05-09 | Courtaulds (Holding) Limited | Formation of a cellulose-based premix |
TW295607B (en) | 1993-05-24 | 1997-01-11 | Courtaulds Fibres Holdings Ltd | |
TR28495A (en) | 1993-05-24 | 1996-09-02 | Courtaulds Fibres Holdings Ltd | Production of cellulose fiber, cured from the strainer, curled. |
TW256860B (en) | 1993-05-24 | 1995-09-11 | Courtaulds Fibres Holdings Ltd | |
US5527178A (en) | 1993-05-24 | 1996-06-18 | Courtaulds Fibres (Holdings) Limited | Jet assembly |
US5370322A (en) | 1993-05-24 | 1994-12-06 | Courtaulds Fibres (Holdings) Limited | Filtering particulate cellulosic-based material |
US5354524A (en) | 1993-05-24 | 1994-10-11 | Alan Sellars | Monitoring concentration of dope in product manufacture |
US5354371A (en) | 1993-05-28 | 1994-10-11 | Courtaulds Fibres (Holdings) Limited | Transport of solutions of cellulose through pipes |
JPH0716222A (en) | 1993-06-30 | 1995-01-20 | Hitachi Medical Corp | Ultrasonic transmitting and receiving circuit |
AT401271B (en) | 1993-07-08 | 1996-07-25 | Chemiefaser Lenzing Ag | METHOD FOR PRODUCING CELLULOSE FIBERS |
AT403584B (en) | 1993-09-13 | 1998-03-25 | Chemiefaser Lenzing Ag | METHOD AND DEVICE FOR PRODUCING CELLULOSIC FLAT OR TUBE FILMS |
AT399519B (en) | 1993-09-14 | 1995-05-26 | Chemiefaser Lenzing Ag | FORM- OR SPINNING CONTAINER CONTAINING CELLULOSE AND METHOD FOR PRODUCING CELLULOSIC MOLDED BODIES |
AT400581B (en) | 1993-10-19 | 1996-01-25 | Chemiefaser Lenzing Ag | METHOD FOR PRODUCING SOLUTIONS OF CELLULOSE |
ATA249893A (en) | 1993-12-10 | 1994-12-15 | Chemiefaser Lenzing Ag | METHOD FOR PRODUCING CELLULOSIC MOLDED BODIES AND MOLDED OR. SPIDING MASS |
DE4342442C2 (en) * | 1993-12-13 | 1996-11-21 | Akzo Nobel Nv | Process for the production of level-off DP cellulose (LODP cellulose) and its disaggregation to microcrystalline cellulose |
US5629055A (en) | 1994-02-14 | 1997-05-13 | Pulp And Paper Research Institute Of Canada | Solidified liquid crystals of cellulose with optically variable properties |
ATA43094A (en) | 1994-03-01 | 1995-04-15 | Chemiefaser Lenzing Ag | METHOD FOR PRODUCING CELLULOSIC MOLDED BODIES, SOLUTION OF A TERT. AMINOXIDS AND THEIR WORK-UP |
GB9404510D0 (en) | 1994-03-09 | 1994-04-20 | Courtaulds Fibres Holdings Ltd | Fibre treatment |
GB9407496D0 (en) | 1994-04-15 | 1994-06-08 | Courtaulds Fibres Holdings Ltd | Fibre treatment |
GB9408742D0 (en) | 1994-05-03 | 1994-06-22 | Courtaulds Fibres Holdings Ltd | Fabric treatment |
SE9401771D0 (en) * | 1994-05-24 | 1994-05-24 | Hans Olof Samuelson | Process for removal of metal compounds in lignocellulosic pulp |
GB9410912D0 (en) | 1994-06-01 | 1994-07-20 | Courtaulds Plc | Fibre treatment |
FI95607C (en) | 1994-06-03 | 1996-02-26 | Valtion Teknillinen | Process and enzyme preparations for treating cellulose pulp |
DE4420304C1 (en) | 1994-06-10 | 1995-09-21 | Fraunhofer Ges Forschung | Flexible cellulose, low modulus cellulose fibres for textile applications |
GB9412500D0 (en) | 1994-06-22 | 1994-08-10 | Courtaulds Fibres Holdings Ltd | Fibre manufacture |
GB9412501D0 (en) | 1994-06-22 | 1994-08-10 | Courtaulds Fibres Holdings Ltd | Manufacture of fibre |
AT401393B (en) | 1994-09-05 | 1996-08-26 | Chemiefaser Lenzing Ag | METHOD FOR PRODUCING CELLULOSE FIBERS |
AT401392B (en) | 1994-09-05 | 1996-08-26 | Chemiefaser Lenzing Ag | METHOD FOR PRODUCING A CELLULOSIC MOLDED BODY |
FI102301B1 (en) | 1994-10-13 | 1998-11-13 | Ahlstrom Machinery Oy | Process for treating cellulose pulp |
US5545371A (en) | 1994-12-15 | 1996-08-13 | Ason Engineering, Inc. | Process for producing non-woven webs |
EP0858526A1 (en) | 1995-02-17 | 1998-08-19 | Ahlstrom Machinery Oy | Method of pretreating pulp to be bleached with peroxide |
ZA961712B (en) | 1995-03-03 | 1996-09-06 | Akzo Nobel Nv | Centrifugal spinning process for spinnable solutions |
AT402410B (en) | 1995-04-19 | 1997-05-26 | Chemiefaser Lenzing Ag | METHOD FOR PRODUCING A CELLULOSE SUSPENSION |
AT402411B (en) | 1995-04-19 | 1997-05-26 | Chemiefaser Lenzing Ag | PLANT AND INTEGRATED FILM AND FIBER FACTORY FOR THE PRODUCTION OF CELLULOSIC FILMS AND FIBERS |
AT405576B (en) | 1995-05-04 | 1999-09-27 | Chemiefaser Lenzing Ag | METHOD FOR CONTROLLING A FLOWING CELLULOSE SUSPENSION |
AT403057B (en) | 1995-05-09 | 1997-11-25 | Chemiefaser Lenzing Ag | METHOD FOR PRODUCING CELLULOSIC MOLDED BODIES |
FR2735794B1 (en) | 1995-06-26 | 1997-09-19 | Elysees Balzac Financiere | PROCESS FOR THE PREPARATION OF A MIXTURE OF CELLULOSIC FIBERS AND MICROFIBERS |
AT403296B (en) | 1995-08-11 | 1997-12-29 | Chemiefaser Lenzing Ag | METHOD FOR PRODUCING A CELLULOSE MOLDED BODY |
AT402739B (en) | 1995-09-19 | 1997-08-25 | Chemiefaser Lenzing Ag | METHOD FOR PRODUCING A CELLULOSIC MOLDED BODY |
FI105701B (en) | 1995-10-20 | 2000-09-29 | Ahlstrom Machinery Oy | Method and arrangement for treatment of pulp |
US5762797A (en) | 1995-12-15 | 1998-06-09 | Patrick; Gilbert | Antimicrobial filter cartridge |
US6136244A (en) | 1996-02-14 | 2000-10-24 | Akzo Nobel N.V. | Process for preparing cellulose fibres and filaments |
DE19628263A1 (en) | 1996-07-12 | 1998-01-15 | Fraunhofer Ges Forschung | Process for the preparation of cellulose solutions in water-containing amine oxide |
US6306334B1 (en) | 1996-08-23 | 2001-10-23 | The Weyerhaeuser Company | Process for melt blowing continuous lyocell fibers |
US6331354B1 (en) * | 1996-08-23 | 2001-12-18 | Weyerhaeuser Company | Alkaline pulp having low average degree of polymerization values and method of producing the same |
US6210801B1 (en) * | 1996-08-23 | 2001-04-03 | Weyerhaeuser Company | Lyocell fibers, and compositions for making same |
US6235392B1 (en) | 1996-08-23 | 2001-05-22 | Weyerhaeuser Company | Lyocell fibers and process for their preparation |
DE69716092T2 (en) * | 1996-08-23 | 2003-01-30 | Weyerhaeuser Co | LYOCELL FIBERS AND METHOD FOR THEIR PRODUCTION |
US6221487B1 (en) * | 1996-08-23 | 2001-04-24 | The Weyerhauser Company | Lyocell fibers having enhanced CV properties |
US6057438A (en) * | 1996-10-11 | 2000-05-02 | Eastman Chemical Company | Process for the co-production of dissolving-grade pulp and xylan |
US5695377A (en) | 1996-10-29 | 1997-12-09 | Kimberly-Clark Worldwide, Inc. | Nonwoven fabrics having improved fiber twisting and crimping |
WO1998022642A1 (en) | 1996-11-21 | 1998-05-28 | Toyo Boseki Kabushiki Kaisha | Regenerated cellulosic fibers and process for producing the same |
AU9778398A (en) * | 1997-10-01 | 1999-04-23 | Weyerhaeuser Company | Cellulose treatment and the resulting product |
US6001303A (en) | 1997-12-19 | 1999-12-14 | Kimberly-Clark Worldwide, Inc. | Process of making fibers |
GB2337957A (en) | 1998-06-05 | 1999-12-08 | Courtaulds Fibres | Method of manufacture of a nonwoven fabric |
DE19856582C1 (en) * | 1998-12-08 | 2001-03-15 | Rhodia Acetow Ag | Process for the production of chemical pulp from wood chips |
-
2000
- 2000-05-18 US US09/574,538 patent/US6331354B1/en not_active Expired - Lifetime
-
2001
- 2001-04-11 MX MXPA02011317A patent/MXPA02011317A/en active IP Right Grant
- 2001-04-11 DE DE60122169T patent/DE60122169T2/en not_active Expired - Fee Related
- 2001-04-11 KR KR1020027015493A patent/KR100834248B1/en not_active IP Right Cessation
- 2001-04-11 ES ES01926892T patent/ES2265428T3/en not_active Expired - Lifetime
- 2001-04-11 BR BRPI0110890-5A patent/BR0110890B1/en not_active IP Right Cessation
- 2001-04-11 AU AU2001253399A patent/AU2001253399A1/en not_active Abandoned
- 2001-04-11 JP JP2001584616A patent/JP2003533602A/en active Pending
- 2001-04-11 EP EP01926892A patent/EP1311717B1/en not_active Expired - Lifetime
- 2001-04-11 AT AT01926892T patent/ATE335873T1/en not_active IP Right Cessation
- 2001-04-11 WO PCT/US2001/011897 patent/WO2001088236A2/en active IP Right Grant
- 2001-04-11 CN CNB018096204A patent/CN100402741C/en not_active Expired - Lifetime
- 2001-04-11 CA CA002406517A patent/CA2406517C/en not_active Expired - Lifetime
- 2001-05-04 TW TW090110757A patent/TWI282829B/en not_active IP Right Cessation
- 2001-10-10 US US09/975,174 patent/US6440523B1/en not_active Expired - Lifetime
- 2001-10-10 US US09/975,670 patent/US7083704B2/en not_active Expired - Fee Related
- 2001-10-10 US US09/975,598 patent/US6491788B2/en not_active Expired - Lifetime
-
2008
- 2008-09-10 JP JP2008231654A patent/JP2009019326A/en active Pending
Also Published As
Publication number | Publication date |
---|---|
MXPA02011317A (en) | 2003-04-25 |
BR0110890B1 (en) | 2012-02-22 |
US6440523B1 (en) | 2002-08-27 |
EP1311717A2 (en) | 2003-05-21 |
US20020034638A1 (en) | 2002-03-21 |
ES2265428T3 (en) | 2007-02-16 |
KR100834248B1 (en) | 2008-05-30 |
ATE335873T1 (en) | 2006-09-15 |
US20020088572A1 (en) | 2002-07-11 |
TWI282829B (en) | 2007-06-21 |
JP2003533602A (en) | 2003-11-11 |
DE60122169T2 (en) | 2007-08-23 |
BR0110890A (en) | 2003-12-30 |
DE60122169D1 (en) | 2006-09-21 |
CN1432087A (en) | 2003-07-23 |
JP2009019326A (en) | 2009-01-29 |
US20020041961A1 (en) | 2002-04-11 |
US7083704B2 (en) | 2006-08-01 |
CA2406517C (en) | 2009-06-30 |
EP1311717B1 (en) | 2006-08-09 |
WO2001088236A2 (en) | 2001-11-22 |
CN100402741C (en) | 2008-07-16 |
CA2406517A1 (en) | 2001-11-22 |
WO2001088236A3 (en) | 2003-02-27 |
KR20030013421A (en) | 2003-02-14 |
US6331354B1 (en) | 2001-12-18 |
US6491788B2 (en) | 2002-12-10 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
AU2001253399A1 (en) | Alkaline pulp having low average degree of polymerization values and method of producing the same | |
CA2323437A1 (en) | Lyocell fibers, and compositions for making the same | |
AU690763B2 (en) | Cationic biopolymers | |
ATE256705T1 (en) | METHYCELLULOSE WITH IMPROVED GEL STRENGTH | |
CA2096738A1 (en) | Paper and a method of paper manufacture | |
PL348046A1 (en) | Dispersions of silyl-terminated polymers with a high solids content, their production and their use | |
AU2001271424A1 (en) | Method to manufacture paper using fiber filler complexes | |
AU2002363709A1 (en) | Electrically conductive thermoplastic polymer composition | |
EP0381125A3 (en) | Polymeric-containing compositions with improved oxidative stability | |
MXPA03001056A (en) | Process for sizing paper. | |
WO1997036037A3 (en) | Aldehyde-modified cellulosic fibers for paper products having high initial wet strength | |
MY131000A (en) | High melt strength polymers and method of making same | |
CA2520236A1 (en) | Low ph treatment of pulp in a bleach sequence to produce pulp having low d.p. and low copper number for use in lyocell manufacture | |
WO2002004556A3 (en) | Ethylene inter-polymer blends | |
EP1113107A3 (en) | Paper quality improver composition | |
CA2384461A1 (en) | Method in connection with the production of mechanical pulp | |
EP1105571B1 (en) | Additive composition for paper making | |
MY158094A (en) | Cellulosic product and process for its production | |
CA2520226A1 (en) | High ph treatment of pulp in a bleach sequence to produce pulp having low d.p. and low copper number for use in lyocell manufacture | |
PT1252391E (en) | Method for improving printability and coatability of paper and board | |
WO2003033564A1 (en) | Pellet of polytrimethylene terephthalate and process for producing the same | |
CA2394412A1 (en) | Soft printing paper | |
DE69816050D1 (en) | RESISTANT CABLE AGAINST DENDRITE FORMATION | |
EP1707669A3 (en) | Microcrystalline cellulose and method for making | |
MY126115A (en) | Monovinylidene aromatic polymers with improved toughness and rigidity and a process for their preparation |