AU1873892A - Process for removing silica from aqueous liquors - Google Patents

Description

PROCESS FOR REMOVING SILICA FROM

AQUEOUS LIQUORS

The present invention relates to a process for removing silica from aqueous liquors.

It is known that soluble and colloidal silica present in water that is used in cooling water circuits in gas or coal fired power stations or other applications is undesirable since it tends to form extremely hard deposits that progressively reduce the heat transfer efficiency of the cooling water circuits. There are a number of known chemical and physical means for removing the silica deposits. However, all these known means have disadvantages. For example, one physical means comprises projecting a scraper bullet through the tubing in cooling water circuits to scrape away the deposits. The disadvantage of this technique is that there is an unacceptable risk of damage to the cooling water circuits.

An object of the present invention is to provide a process for removing soluble and colloidal silica from aqueous liquors to minimise the extent of the silica deposits.

According to the present invention there is provided a process for removing silica in dissolved and/or

colloidal form from an aqueous liquor comprising:

(a) precipitating/adsorbing the dissolved and

colloidal silica with/onto a

precipitant/adsorbent;

(b) adding a flocculent to the liquor to form

floccs of the precipitated/adsorbed silica and any other suspended solids in the liquor and the flocculent; and

(c) separating the floccs from the liquor.

The term "precipitant/adsorbent" is understood herein to mean any element or compound in soluble or insoluble form that is capable by mechanisms of

precipitation or adsorption of changing dissolved and/or colloidal silica into a state that can be separated more readily from the liquor.

It is preferred that step (a) comprises adjusting the pH of the liquor to promote precipitation/adsorption. It is particularly preferred that step (a) comprises adjusting the pH to be equal to or greater than 8.0.

It is more particularly preferred that step (a) comprises adjusting the pH to be equal or greater than 8.5. Typically, step (a) comprises adjusting the pH to be equal or greater than 9.0.

It is preferred that the process further comprises the step of adding an inert particulate carrier prior to or at the same time as the step (b) of adding the

flocculent.

It is particularly preferred that the inert

particulate carrier is added prior to the addition of the flocculent.

It is preferred that the process further comprises, after step (c), agitating the floccs to break up the floccs and separating the inert particulate carrier for recycling in the process.

It is preferred that the precipitant/adsorbent comprises a compound containing one or more of aluminium, magnesium, and iron. It is noted that in some situations the precipitant/adsorbent may already be in the liquor and the pH adjustment is required to promote precipitation/adsorption of the dissolved or colloidal silica with/onto the precipitant/adsorbent. It is also noted that in other situations it may be necessary to add the precipitant/adsorbent to the liquor, with or without pH adjustment.

It is particularly preferred that the

precipitant/adsorbent is a soluble aluminium salt such as sodium aluminate, aluminium sulphate or aluminium

chloride.

It is particularly preferred in situations where the precipitant/adsorbent is a soluble aluminium salt that the process comprises, after step (c), lowering the pH of the liquor to 7.5 or less to precipitate any soluble aluminium retained in the liquor.

The term "liquor" is understood herein to include aqueous and non-aqueous liquors.

The term "inert" as used herein in relation to

"particulate carrier" is understood herein to mean that the particulate carrier is not substantially attacked by the liquor. In other words, the term "inert" means that the particulate carrier exhibits both suitable chemical and physical stability in the liquors.

It is preferred that the inert particulate carrier is selected from the group consisting of sand, alumina, garnet, magnetite, hematite, ilmenite, and calcite.

The term "suspended solids" is understood herein to include organic and inorganic material. It is preferred that the flocculent is a

polyelectrolyte flocculent.

The term "polyelectrolyte flocculent" as used herein is understood to mean any suitable cationic, non-ionic and anionic flocculent.

The process of the present invention is described further by reference to the following examples.

Example 1

A series of experiments was carried out on water from the cooling water circuit of the Muja coal-fired power station in Collie, Western Australia. The water was at pH 8.0 and contained a total of 69 ppm silica in dissolved and colloidal form.

A number of samples of the water were tested to investigate the effect of the following parameters on the removal of silica from the water.

1. Precipitant/adsorbent, the following

precipitants/adsorbents were tested:

(a) soluble iron or aluminium containing

compounds;

(b) soluble aluminium containing compounds; and (c) a combination of soluble iron and aluminium containing compounds and lime.

2. pH.

3. Contact time of precipitant/adsorbent and

water prior to addition of inert particulate carrier.

4. Inert particulate carrier (IPC).

The results of the experiments are set out in Table 1 below. With reference to Table 1, the experiments T1 to T7 and T10 to T24 were carried out in accordance with the following sequence of steps.

1. Addition of precipitant/adsorbent to liquor.

2. Adjustment of pH. 3. Addition of inert particulate carrier and

polyelectrolyte flocculent (Zetag 92 in a cationic flocculent produced by Allied

Colloids) after prescribed contact time of precipitant/adsorbent and water. 4. Separation of floccs of precipitated/adsorbed silica, inert particulate carrier, polyelectrolyte flocculent and suspended solids in the liquor.

The experiments T8 and T9 were carried out without the addition of precipitant/adsorbent and in the case of the experiment T8 without adjustment of pH. TABLE 1

Test Precipitant/ pH Batch IPC Silica Silica

Adsorbent Contact Used Assay Removal tPPn) Time (ppn) %

Fe⁺³ Al⁺³ CaO (hrs:mins)

T1 77 - - 10 0:45 Magnetite 4 94

T2 77 - - 9.5 0:45 " 22 68

T3 77 - - 9.2 0:17 " 24 65

T4 20 - - 10 0:45 " 30 56 T5 77 - - 8.0 0:45 " 18 74

T6 20 - - 8.5 2:0 " 41 41

T6 20 - - 8.0 14:0 " 44 36

T7 77 - - 9.5 0:01 " 22 68

T8 - - - 8.0 0:00 " 53 23

T9 - - - 9.5 0:10 " 59 14

T10 - 92 - 9.5 0:15 " 1 99

T13 - 45 - 9.5 0:15 " 8 88

T14 77 - - 9.5 0:45 Silica 18 74

T15 - 92 - 9.3 0:15 " < 1 > 99

T16 - 92 - 9.3 0:40 Magnetite < 1 > 99

T17 100 60 0.2 9.6 1:10 " 29 66

T18 100 60 0.2 9.6 1:10 " 6 93

T19 50 30 0.1 8.9 1:10 " 4 95

T20 50 30 0.1 8.7 1:10 " 27 68

T21 50 30 0.25 9.0 2:10 " 5 94

T22 25 15 0.2 9.1 2:10 " 16 81 T23 - 25 - 9.6 0:15 " 9 89

T24 - 25 - 9.6 0:15 " 18 79

The results for experiments T5 and T8 and for experiments T2 and T9 in Table 1 indicate clearly that the addition of a precipitant/adsorbent to the water at the feed level of pH 8.0 followed by the addition of inert particulate carrier and polyelectrolyte flocculent produced a significantly higher removal of silica from the water than the addition of inert particulate carrier and polyelectrolyte flocculent without the addition of precipitant/adsorbent. It can also be seen from Table 1 that an increase of the pH of the water above the feed level of pH 8.0 following the addition of a precipitant/adsorbent and prior to the addition of inert particulate carrier and polyelectrolyte flocculent produced a further increase in the removal of silica from the water. In this regard, the results for experiments T1, T10, T15, T16, T18, T19 and T21 indicate that in excess of 90% of the silica in the water was removed by such a process.

In summary, it can be seen from Table 1 that generally there was an increase in the removal of silica:

(a) with an increase in the addition of

precipitant/adsorbent at a given pH (cf the results of experiments T10/T13 and T1/T4); and

(b) with an increase in the pH at a given

concentration of precipitant/adsorbent (cf the results of experiments T4/T6).

Example 2

A further series of experiments was carried out on water from the cooling water circuit of the Muja

coal-fired power station.

The experiments focussed on the use of alumina as the precipitant/adsorbent and the inert particulate carrier. The following is a brief outline of the experimental procedure.

1. Addition of calcined or hydrated alumina to water.

2. Adjustment of pH to be higher than 9.0. 3. Agitation of water/alumina.

4. Addition of polyelectrolyte flocculent (Zetag

92).

5. Agitation of water/alumina/flocculent.

6. Separation of floccs of precipitated/adsorbed silica, alumina, and polyelectrolyte flocculent.

The results of the experiments are set out in Table below.

The results in Table 2 indicate that the addition of a precipitant/adsorbent, followed by adjustment of pH to be higher than 9.0, and subsequent addition of a polyelectrolyte flocculent substantially removed the silica from the water.

Example 3 A further series of experiments was carried out on water from the cooling water circuit of the Muja

coal-fired power station. The water contained a total of 50 ppm silica in dissolved and colloidal form. The experiments focused on the effect of pH on the removal of silica from the water.

The experiments were carried out in accordance with the following sequence of steps.

1. Addition of 10 ppm or 20 ppm of a soluble aluminium containing compound as

precipitant/adsorbent.

2. Adjustment of pH.

3. Addition of inert particulate carrier and polyelectrolyte flocculent.

The results of the experiments are set out in Table 3 below.

The results in Table 3 above indicate that at a given concentration of precipitant/adsorbent there was an increase in the removal of silica with an increase in the pH. In particular, the results for the experiments based on the addition of 20 ppm precipitant/adsorbent indicate that there was a significant increase in silica removal at pH levels equal to and above 8.0.

Example 4 A series of experiments was carried out on water from the cooling water circuit of a Queensland Nickel Pty. Ltd. plant at Gladstone, Queensland.

The make-up water to the cooling circuit contained 72 ppm dissolved and colloidal silica and the cooling tower water contained 278 ppm dissolved and colloidal silica.

The experiments focussed on the effect of the amount of the addition of precipitant/adsorbent on the removal of silica from the water. The experiments were carried out in accordance with the following sequence of steps:

1. Addition of soluble aluminium containing compounds as precipitant/adsorbent.

2. Adjustment of pH to 9.6.

3. Addition of inert particulate carrier and polyelectrolyte flocculent. The results of the experiments are set out in Table 4 below.

The results in Table 4 above indicate that at a given pH there was an increase in the removal of silica with an increase in the addition of

precipitant/adsorbent.

By way of summary, the experimental results presented in Examples 1 and 2 establish that it is possible with the process of the invention to

substantially remove soluble and colloidal silica from water. This is a significant outcome in relation to the coal and gas fired power station industry in particular and for industry in general which relies on the use of cooling water circuits. Many modifications may be made to the process of the present invention as described above without departing from the spirit and scope of the present invention.

Claims (12)

CLAIMS :

1. A process for removing silica in dissolved and/or colloidal form from an aqueous liquor comprising:

(a) precipitating/adsorbing the dissolved and colloidal silica with/onto a precipitant/adsorbent;

(b) adding a flocculent to the liquor to form floccs of the precipitated/adsorbed silica and any other suspended solids in the liquor and the flocculent; and (c) separating the floccs from the liquor.

2. The process defined in claim 1, wherein step (a) comprises adjusting the pH of the liquor to promote precipitation/adsorption.

3. The process defined in claim 2, wherein step (a) comprises adjusting the pH to be equal to or greater than 8.0.

4. The process defined in claim 3, wherein step (a) comprises adjusting the pH to be equal or greater than 8.5.

5. The process defined in claim 4, wherein step (a) comprises adjusting the pH to be equal or greater than 9.0.

6. The process defined in any one of the preceding claims, further comprising the step of adding an inert particulate carrier prior to or at the same time as the step (b) of adding the flocculent.

7. The process defined in claim 6, wherein the inert particulate carrier is added prior to the addition of the flocculent.

8. The process defined in any one of the preceding claims, further comprising, after step (c), agitating the floccs to break up the floccs and separating the inert particulate carrier for recycling in the process.

9. The process defined in any one of the preceding claims, wherein the precipitant/adsorbent comprises a compound containing one or more of aluminium, magnesium, and iron.

10. The process defined in claim 9, wherein the precipitant/adsorbent is a soluble aluminium salt such as sodium aluminate, aluminium sulphate or aluminium

chloride.

11. The process defined in any one of the

preceding claims, wherein the inert particulate carrier is selected from the group consisting of sand, alumina, magnetite, hematite, ilmenite, and calcite.

12. The process defined in any one of the

preceding claims, wherein the flocculent is a

polyelectrolyte flocculent.