AT515350A1 - Process for the preparation of a concentrate of a wood preservative, concentrate produced therewith and process for the treatment of wood - Google Patents
Process for the preparation of a concentrate of a wood preservative, concentrate produced therewith and process for the treatment of wood Download PDFInfo
- Publication number
- AT515350A1 AT515350A1 ATA50100/2014A AT501002014A AT515350A1 AT 515350 A1 AT515350 A1 AT 515350A1 AT 501002014 A AT501002014 A AT 501002014A AT 515350 A1 AT515350 A1 AT 515350A1
- Authority
- AT
- Austria
- Prior art keywords
- wood
- concentrate
- leaves
- polar solvent
- solvent
- Prior art date
Abstract
Die Erfindung betrifft ein Verfahren zur Herstellung eines Konzentrats für ein Holzschutzmittel. Erfindungsgemäß umfasst das Verfahren folgende Schritte: a) Bereitstellen von Blättern einer Pflanze; b) optional Zerkleinern der Blätter; c) Extraktion von Lipochromen aus den Blättern mit zumindest einem nicht polaren Lösungsmittel; d) Abtrennung der extrahierten Lipochrome aus dem Lösungsmittel als hydrophobe, insbesondere ölige oder harzige Phase. Des Weiteren betrifft die Erfindung ein so hergestelltes Konzentrat sowie ein Verfahren zur Oberflächenbehandlung von Holz.The invention relates to a method for producing a concentrate for a wood preservative. According to the invention, the method comprises the following steps: a) providing leaves of a plant; b) optionally crushing the leaves; c) extraction of lipochromes from the leaves with at least one non-polar solvent; d) separation of the extracted lipochromes from the solvent as a hydrophobic, especially oily or resinous phase. Furthermore, the invention relates to a concentrate thus produced and to a process for the surface treatment of wood.
Description
Verfahren zur Herstellung eines Konzentrats eines Holzschutzmittels, damit hergestelltes Konzentrat und Verfahren zur Behandlung von HolzProcess for the preparation of a concentrate of a wood preservative, concentrate produced therewith and process for the treatment of wood
Die Erfindung betrifft ein Verfahren zur Herstellung eines Konzentrats eines Holzschutzmittels.The invention relates to a method for producing a concentrate of a wood preservative.
Des Weiteren betrifft die Erfindung ein derart hergestelltes Konzentrat.Furthermore, the invention relates to a concentrate produced in this way.
Schließlich betrifft die Erfindung ein Verfahren zur Oberflächenbehandlung von Holz.Finally, the invention relates to a method for the surface treatment of wood.
Holz wird aufgrund seines vielfältigen Eigenschaftsspektrums in vielen Bereichen der Bauwirtschaft eingesetzt. Ein innerer Aufbau des Holzes erlaubt es, dieses sowohl für Anwendungen mit geringer Belastung wie Terrassendielen oder Verschalungen als auch statisch hoch belastete Bauten einzusetzen. Während des Wachstums bzw. als Baum wird der innere Aufbau des Holzes durch die Rinde des Baumstammes vor äußeren Einwirkungen geschützt. Der Rinde kommt somit eine Schutzfunktion zu. Nach Fällen eines Baumstammes und Aufarbeitung desselben, beispielsweise als Schnittholz, liegt der innere Aufbau des Holzes frei. Um dennoch eine Schutzwirkung des später eingesetzten Schnittholzes zu erreichen, wird dieses häufig mit einem Oberflächenschutz versehen. Dieser Oberflächenschutz soll äußere Einwirkungen möglichst lang hintanhalten.Due to its diverse range of properties, wood is used in many areas of the construction industry. An internal structure of the wood allows it to be used both for low-stress applications such as decking or cladding as well as statically heavily loaded buildings. During growth or as a tree, the internal structure of the wood is protected by the bark of the tree trunk from external influences. The bark thus has a protective function. After felling a tree trunk and working it up, for example as lumber, the internal structure of the wood is free. In order nevertheless to achieve a protective effect of the lumber used later, this is often provided with a surface protection. This surface protection should withhold external influences for as long as possible.
Bei bekannten Verfahren gemäß dem Stand der Technik wird das Holz üblicherweise mit einem flüssigen Oberflächenschutz imprägniert. Zur Beschleunigung des Verfahrens und für einen möglichst effektiven Oberflächenschutz wird dies zumeist unter Druck und erhöhter Temperatur durchgeführt. Durch die Imprägnierung der Oberfläche des Holzes wird dieses widerstandsfähig gegen äußere Einflüsse. Hierbei ist allerdings nachteilig, dass zumeist künstlich hergestellte Öle oder Lacke eingesetzt werden, die teilweise giftig sind. Manchmal stellt sich eine Giftigkeit erst Jahre nach dem erstmaligen Einsatz eines Oberflächenschutzmittels heraus, sodass bei Verbau des Holzes im Innenbereich Menschen potenziell bereits kausal verursachte Gesundheitsbeeinträchtigungen erleiden können, ehe die Giftigkeit des Oberflächenschutzmittels nachweislich festgestellt wird.In known processes according to the prior art, the wood is usually impregnated with a liquid surface protection. To speed up the process and for the most effective surface protection, this is usually carried out under pressure and elevated temperature. By impregnating the surface of the wood this becomes resistant to external influences. This is disadvantageous, however, that mostly artificially produced oils or paints are used, which are partially toxic. Sometimes, toxicity does not develop until years after the first use of a surface-protection agent, so that people can potentially suffer health effects that are already causally caused when the wood is indoors, before the toxicity of the surface-protection agent can be proven.
Von diesem Stand der Technik ausgehend ist es Aufgabe der Erfindung, ein Verfahren zur Herstellung eines Konzentrats eines Holzschutzmittels anzugeben, das biologischer Natur ist und rein oder nach Verdünnung mit einem Lösungsmittel zum Holzschutz einsetzbar ist.Starting from this prior art, it is an object of the invention to provide a method for producing a concentrate of a wood preservative, which is biological in nature and can be used purely or after dilution with a solvent for wood preservation.
Ein weiteres Ziel der Erfindung ist es, ein entsprechendes Konzentrat anzugeben.Another object of the invention is to provide a corresponding concentrate.
Darüber hinaus ist es ein Ziel der Erfindung, ein Verfahren zur Oberflächenbehandlung von Holz anzugeben, das zu einem nachhaltigen Schutz des behandelten Holzes auf Basis biologischer Stoffe führt.In addition, it is an object of the invention to provide a method for the surface treatment of wood, which leads to a sustainable protection of the treated wood based on biological substances.
Die verfahrensmäßige Aufgabe der Erfindung wird gelöst, wenn ein Verfahren zur Herstellung eines Konzentrats eines Holzschutzmittels folgende Schritte umfasst: a) Bereitstellen von Blättern einer Pflanze; b) optional Zerkleinern der Blätter; c) Extraktion von Lipochromen aus den Blättern mit zumindest einem nicht polaren Lösungsmittel; d) Abtrennung der extrahierten Lipochrome aus dem Lösungsmittel als hydrophobe, insbesondere ölige oder harzige Phase.The procedural object of the invention is achieved if a method for producing a concentrate of a wood preservative comprises the following steps: a) providing leaves of a plant; b) optionally crushing the leaves; c) extraction of lipochromes from the leaves with at least one non-polar solvent; d) separation of the extracted lipochromes from the solvent as a hydrophobic, especially oily or resinous phase.
Ein mit einem erfindungsgemäßen Verfahren erzielter Vorteil ist darin zu sehen, dass durch Einsatz von Blättern einer Pflanze und der Extraktion von Lipochromen aus denselben die letztlich erhaltene hydrophobe, insbesondere ölige oder harzige Phase ein biogenes Terpentinöl bzw. Terpentinprodukt darstellt, das aus Naturprodukten gewonnen ist. Im Unterschied zu künstlich hergestellten, teilweise giftigen Terpentinölen und Gemischen mit diesen gemäß dem Stand der Technik ist daher eine spätere Gesundheitsgefährdung durch giftige Oberflächenschutzmittel nahezu ausgeschlossen. Darüber hinaus ergibt sich der Vorteil, dass durch die Gewinnung des Konzentrats aus Blättern einer Pflanze ähnlich wie bei den Pflanzen selbst eine fungizide Wirkung erreicht wird. Ferner ist auch ein guter UV-Schutz gegeben, da die Blattpigmente aufgrund konjugierter Doppelbindungssysteme Lichtquanten absorbieren und somit antioxidative Eigenschaften aufweisen. Zusammen mit den für akzessorische Pigmente spezifischen Kopf- und Endgruppen an den Isopren-Einheiten ist die protektive Absorption im kurzwelligeren schädlicheren UV-A- bis Blaulichtbereich des Tageslichtes am stärksten, was die Lipochrome von anderen Terpenen weiter unterscheidet. Schließlich ist aufgrund der hydrophoben Natur der öligen bzw. harzigen Phase bei späterer Verwendung als Holzschutzmittel auch ein gewünschter Flüssigwasserschutz gegeben.An advantage achieved by a method according to the invention is that by using leaves of a plant and extracting lipochromes from them, the hydrophobic, especially oily or resinous phase ultimately obtained is a biogenic turpentine or turpentine product obtained from natural products. In contrast to artificially prepared, partially toxic turpentine oils and mixtures with these according to the prior art, therefore, a subsequent health hazard is virtually excluded by toxic surface protection agents. In addition, there is the advantage that a fungicidal action is achieved by obtaining the concentrate from leaves of a plant similar to the plants themselves. Furthermore, there is also good UV protection since the leaf pigments absorb light quanta due to conjugated double bond systems and thus have antioxidant properties. Together with the accessory end-capped capillary groups on the isoprene units, the protective absorption in the shorter-wavelength, more harmful UV-A to blue-light areas of daylight is strongest, which further differentiates the lipochromes from other terpenes. Finally, owing to the hydrophobic nature of the oily or resinous phase, later use as a wood preservative also provides desired liquid water protection.
Die bei der Extraktion der Blätter zurückbleibende Cellulose kann im Sinne einer vollständigen Verwertung des Ausgangsproduktes weiterverarbeitet werden, z. B. für oder in Baustoffen wie Wärmedämmplatten. Günstig ist es, wenn für die Blätter Laub eingesetzt wird. Im Herbst, wenn das Laub von den Bäumen fällt, weisen die Blätter mit sattgelber bis rötlicher oder roter Farbe einen besonders hohen Anteil an Lipochromen auf. Besonders geeignet ist das Laub von Lichtholzarten wie Ahorn, Buche, Birke, Eiche, Pappel oder Esche. Auch die Blätter von Sträuchern oder Stauden können eingesetzt werden.The remaining in the extraction of leaves cellulose can be further processed in the sense of a complete recovery of the starting material, eg. B. for or in building materials such as thermal insulation panels. It is favorable if foliage is used for the leaves. In autumn, when the leaves fall from the trees, the leaves with a rich yellow to reddish or red color have a particularly high proportion of lipochromes. Particularly suitable is the foliage of light wood species such as maple, beech, birch, oak, poplar or ash. The leaves of shrubs or perennials can be used.
Um die Extraktion zeitlich auf ein Minimum zu beschränken, kann vorgesehen sein, dass die Blätter im Schritt b) zu einem Mehl zerkleinert werden. Durch die Zerkleinerung ergibt sich eine Vergrößerung der Oberfläche, was zu einer rascheren Extraktion führt.In order to limit the extraction time to a minimum, it can be provided that the leaves are comminuted to a flour in step b). The comminution results in an enlargement of the surface, which leads to a more rapid extraction.
Ebenfalls in Bezug auf eine möglichst wirksame und kurze Extraktion ist es bevorzugt, dass die Blätter vor Schritt c) eine Restfeuchte von weniger als 10 % aufweisen oder auf eine solche Restfeuchte getrocknet werden.Also with regard to a most effective and short extraction, it is preferred that the leaves before step c) have a residual moisture of less than 10% or are dried to such residual moisture.
Die Extraktion der Lipochrome wird mit Vorteil mit einer Emulsion mit zumindest einem polaren Lösungsmittel sowie zumindest einem nicht polaren Lösungsmittel durchgeführt. Nach diesem Schritt c) können Feststoffe aus der Emulsion abgetrennt werden. Vorher kann gegebenenfalls noch eine Abtrennung allfälliger fester Bestandteile durchgeführt werden, beispielsweise durch Zentrifugieren.The extraction of the lipochromes is advantageously carried out with an emulsion comprising at least one polar solvent and at least one non-polar solvent. After this step c) solids can be separated from the emulsion. If necessary, a separation of any solid constituents may be carried out beforehand, for example by centrifuging.
Nach der Extraktion wird das zumindest eine nicht polare Lösungsmittel vom zumindest einen polaren Lösungsmittel abgetrennt. Das nicht polare Lösungsmittel, welches die gewünschten Lipochrome enthält, kann anschließend mit einer alkoholischen Lösung einer Base, z. B. methanolischer Kalilauge, umgesetzt werden, um Chlorophyllreste zu verseifen. Anschließend kann Wasser zugegeben werden, um die Base sowie den Alkohol abzutrennen und so eine lipophile Pigmentlösung zu erhalten. Nach diesenAfter extraction, the at least one non-polar solvent is separated from the at least one polar solvent. The non-polar solvent containing the desired lipochromes may then be treated with an alcoholic solution of a base, e.g. As methanolic potassium hydroxide solution can be reacted to saponify chlorophyll. Then, water can be added to separate the base and the alcohol to obtain a lipophilic pigment solution. After these
Schritten kann dann das nicht polare Lösungsmittel zum Erhalt der hydrophoben Phase im Schritt d) durch Destillation abgetrennt werden. Zurück bleibt das lipophile Produkt eines Blattauszuges in Form eines Terpentinöls oder -harzes aus natürlichen Stoffen.Steps can then be separated from the non-polar solvent to obtain the hydrophobic phase in step d) by distillation. What remains is the lipophilic product of a leaf extract in the form of a turpentine oil or resin from natural substances.
Mit besonderem Vorteil ist bei Ausbildung einer öligen Phase vorgesehen, dass ein Teil der erhaltenen öligen Phase in den Prozess rückgeführt wird, und zwar als nicht polares Lösungsmittel im Schritt c). Abgesehen vom Anlauf des Prozesses ist dann bei der kontinuierlichen Verfahrensführung kein Einsatz eines künstlich hergestellten Terpentinöls erforderlich.With particular advantage, when an oily phase is formed, it is provided that part of the resulting oily phase is recycled to the process, specifically as a non-polar solvent in step c). Apart from the start of the process is then in the continuous process management no use of an artificially produced turpentine necessary.
Das weitere Ziel der Erfindung wird durch ein Konzentrat erreicht, das nach einem erfindungsgemäßen Verfahren erhältlich ist.The further object of the invention is achieved by a concentrate obtainable by a process according to the invention.
Ein Vorteil eines erfindungsgemäßen Konzentrats liegt darin, dass dieses biologischer Natur und daher hinsichtlich einer möglichen Gesundheitsgefährdung unbedenklich ist. Das Konzentrat kann eingesetzt werden, um durch Verdünnung ein Holzschutzmittel zu erhalten, welches ebenfalls ein geringes Gesundheitsgefährdungspotenzial aufweist. Für die Verdünnung kommt üblicherweise zumindest ein Alkohol zum Einsatz, der bei Bedarf mit einem weiteren Lösungsmittel, beispielsweise einem Aldehyd oder Keton, gemischt sein kann.An advantage of a concentrate according to the invention is that this biological nature and therefore with regard to a possible health hazard is harmless. The concentrate can be used to obtain a wood preservative by dilution, which also has a low health hazard potential. For dilution usually at least one alcohol is used, which may be mixed with another solvent, for example an aldehyde or ketone, if necessary.
Das noch weitere Ziel der Erfindung wird erreicht durch ein Verfahren zur Oberflächenbehandlung von Holz, welches folgende Schritte umfasst: a) Bereitstellen von Holz und optional mechanische Bearbeitung einer Oberfläche des Holzes oder eines Teils davon; b) optional Beaufschlagung der Oberfläche mit einer Saccharide enthaltenen Lösung; c) danach Behandlung der Oberfläche mit einem erfindungsgemäßen Konzentrat oder Holzschutzmittel.The still further object of the invention is achieved by a method of surface treatment of wood comprising the steps of: a) providing wood and optionally mechanically working a surface of the wood or a part thereof; b) optionally impinging on the surface with a solution containing saccharides; c) thereafter treatment of the surface with a concentrate or wood preservative according to the invention.
Durch ein erfindungsgemäßes Verfahren kann eine Oberfläche von Holz hochwirksam mit einem Oberflächenschutz biologischer Natur überzogen werden. Sofern erforderlich, kann die Oberfläche des Holzes mechanisch vorbearbeitet werden, beispielsweise durch Schleifen oder andere Prozesse, mit welchen die Oberfläche des Holzes aufgeraut wird. Anschließend erfolgt vorzugsweise eine Beaufschlagung der Oberfläche mit einerBy a method according to the invention, a surface of wood can be highly effectively coated with a surface protection of a biological nature. If necessary, the surface of the wood can be mechanically preprocessed, for example by grinding or other processes with which the surface of the wood is roughened. Subsequently, preferably a loading of the surface with a
Saccharide enthaltenden Lösung, insbesondere Polysaccharide. Die Polysaccharide sind üblicherweise in einem geeigneten Lösungsmittel wie Wasser oder Alkohol gelöst. Die Beaufschlagung mit einer solchen Lösung erfolgt in der Regel bei erhöhter Temperatur und erhöhtem Druck, insbesondere in einem Kesseldruckverfahren. Die Polysaccharide dringen bei der Beaufschlagung bis in einen Bereich von etwa 3 cm von der Oberfläche in das Holz ein. Dadurch wird eine Feuchtigkeitsregulierung erreicht, weil Holzporen mit einem Material ausgefüllt werden, das eine hohe Wasserbindungskapazität aufweist. Durch die hohe Wasserbindungskapazität gibt insbesondere porenfüllendes Pektin Feuchtigkeit nur zeitverzögert an die Umgebung ab. Umgekehrt speichert das Pektin bei Wasserüberschuss dasselbe. Dadurch wird quasi oberflächennah eine Schutzschicht eingezogen, welche vor allem eine Schimmelanfälligkeit des Holzes stark herabsetzt. Dieser Schritt ist jedoch bloß optional und nicht zwingend erforderlich. Anschließend erfolgt eine Behandlung der Oberfläche mit einem erfindungsgemäßen Holzschutzmittel, wobei die bereits erwähnten Vorteile einer UV-Beständigkeit, antioxidativer Eigenschaften sowie einer fungiziden Wirkung erreicht werden. Gegebenenfalls kann auch das Konzentrat in reiner Form eingesetzt werden, wenngleich dies aus Kostengründen nicht bevorzugt ist. Insbesondere wird auch aufgrund der Hydrophobie eine wasserabweisende Schutzschicht erhalten, die zur Langlebigkeit des Holzes beiträgt und insbesondere auch, optional mit der darunter vorgesehenen Feuchtigkeitsregulierung, Schäden durch Austrocknung wie Verzug von Holz durch Wasseraufnahme und Schwundrisse und Abschieferungen durch zu schnelles ungleichmäßiges Trocknen weitgehend unterbindet.Saccharide-containing solution, in particular polysaccharides. The polysaccharides are usually dissolved in a suitable solvent such as water or alcohol. The application of such a solution is usually carried out at elevated temperature and elevated pressure, in particular in a boiler pressure method. The polysaccharides penetrate when exposed to a range of about 3 cm from the surface into the wood. As a result, moisture regulation is achieved because wood pores are filled with a material having a high water binding capacity. Due to the high water binding capacity, in particular pore-filling pectin releases moisture to the environment only with a time delay. Conversely, the pectin stores the same with excess water. As a result, a protective layer is drawn in virtually near the surface, which greatly reduces the susceptibility to mold of the wood. However, this step is merely optional and not mandatory. Subsequently, a treatment of the surface with a wood preservative according to the invention, wherein the already mentioned advantages of UV resistance, antioxidant properties and a fungicidal action are achieved. Optionally, the concentrate can also be used in pure form, although this is not preferred for cost reasons. In particular, a water-repellent protective layer is also obtained due to the hydrophobicity, which contributes to the longevity of the wood and in particular, optionally with the moisture regulation provided below, damage due to dehydration such as distortion of wood through water absorption and shrinkage cracks and Abschieferungen largely prevented by too rapid uneven drying.
Grundsätzlich ist es nicht erforderlich, dass die Beaufschlagung mit der Saccharide enthaltenen Lösung unter speziellen Bedingungen durch geführt wird. Um jedoch eine rasche Verfahrensführung zu ermöglichen, ist es von Vorteil, dass die Beaufschlagung im Schritt b) unter erhöhtem Druck und/oder durch Tränken und Erwärmen durchgeführt wird. Für die Beaufschlagung der Oberfläche mit einer Saccharide enthaltenen Lösung können beliebige Saccharide eingesetzt werden. Insbesondere im Hinblick auf eine möglichst biogene Natur der Oberflächenbehandlung ist vorzugsweise vorgesehen, dass im Schritt b) Polysaccharide aus der Hüllschicht von Bakterien eingesetzt werden. Diese Hüllschicht bzw. Glycocalix kann relativ einfach aus angezüchteten Bodenalgen gewonnen werden und besteht hauptsächlich aus 1,4-vernetzen Pyranosesacchariden und stellt ein stark hygroskopisch wirkendes Bindemittel dar. Bevorzugt werden hierfür aerophytische oder terrestrische Algen eingesetzt.Basically, it is not necessary that the application of the solution containing saccharides is carried out under special conditions. However, in order to enable rapid process management, it is advantageous that the application in step b) is carried out under elevated pressure and / or by soaking and heating. For the treatment of the surface with a solution containing saccharides any saccharides can be used. In particular with regard to the most biogenic nature possible of the surface treatment, it is preferably provided that polysaccharides from the coating layer of bacteria are used in step b). This envelope layer or glycocalix can be obtained relatively easily from cultivated soil algae and consists mainly of 1,4-crosslinked pyranose saccharides and represents a strongly hygroscopic binder. Aerophytic or terrestrial algae are preferably used for this purpose.
Weitere Merkmale, Vorteile und Wirkungen der Erfindung ergeben sich aus dem nachfolgend dargestellten Ausführungsbeispiel. In den Zeichnungen, auf welche dabei Bezug genommen werden, zeigen:Further features, advantages and effects of the invention will become apparent from the embodiment illustrated below. In the drawings, which are referred to, show:
Fig. 1 ein Verfahrensschema;Fig. 1 is a process diagram;
Fig. 2 eine schematische Darstellung eines Teils eines oberflächenbehandelten Holzes.Fig. 2 is a schematic representation of a part of a surface-treated wood.
In Fig. 1 ist ein erfindungsgemäßes Verfahren schematisch dargestellt. Das Verfahren beginnt mit der Bereitstellung von Blättern einer Pflanze, insbesondere Laub. Das Laub wird mit Vorteil zu einem Pulver oder Mehl zerkleinert, sodass eine durchschnittliche Größe der Partikel kleiner als 1 mm ist. Anschließend erfolgt eine Extraktion von Lipochromen aus den Blättern. Hierfür wird das Blattmehl in einem Lösungsmittel getränkt. Bezogen auf 1 kg Blattsubstanz kann eine Extraktionslösung 5 kg Ethanol, 20 kg Aceton, 4 kg 0,1 N HCl, 30 kg Terpentinöl und 75 kg Wasser enthalten. Die Lösung wird mit dem Blattmehl eine ausreichend lange Zeit umgesetzt, um eine Rohpigmentmischung zu erhalten. Wenn eine besonders ökologische Verfahrensführung gewünscht ist, kann anstelle von HCl auch eine andere Säure wie Essigsäure eingesetzt werden. Möglich ist es auch, den Trennprozess mit zusätzlichen Maßnahmen wie Anlegen einer Spannung zu fördern.In Fig. 1, a method according to the invention is shown schematically. The process begins with the provision of leaves of a plant, especially foliage. The foliage is advantageously comminuted to a powder or flour so that an average size of the particles is less than 1 mm. This is followed by extraction of lipochromes from the leaves. For this purpose, the leaf meal is soaked in a solvent. Based on 1 kg of foliar substance, an extraction solution may contain 5 kg of ethanol, 20 kg of acetone, 4 kg of 0.1 N HCl, 30 kg of turpentine oil and 75 kg of water. The solution is reacted with the leaf meal for a sufficient time to obtain a crude pigment mixture. If a particularly ecological process management is desired, instead of HCl, another acid such as acetic acid can be used. It is also possible to promote the separation process with additional measures such as applying a voltage.
Anschließend erfolgen ein Zentrifugieren und ein Abtrennen der hydrophilen Unterphase. Die lipophile Phase wird anschließend mit methanolischer Kalilauge im Verhältnis 1:0,5 umgesetzt, wobei Chlorophyllreste verseift werden. Anschließend erfolgt eine Zugabe von Wasser, ein Zentrifugieren und danach ein Abtrennen der wässrigen Unterphase. Zurück bleibt die lyophile Pigmentlösung, aus der das Lösungsmittel abdestilliert wird, und zwar etwa bei 60 °C. Anschließend kann die so gewonnene ölige Terpentinölphase erneut zentrifugiert werden, um diese aufzukonzentrieren. Dabei kann ein Teil des so gewonnenen Öls wieder in den Prozess rückgeführt werden, wie dies in Fig. 1 dargestellt ist. Der Rest des Terpentinöls ist für einen Einsatz zur Oberflächenbehandlung von Holz einsetzbar.This is followed by centrifuging and separation of the hydrophilic lower phase. The lipophilic phase is then reacted with methanolic potassium hydroxide in a ratio of 1: 0.5, whereby chlorophyll residues are saponified. This is followed by addition of water, centrifuging and then separation of the aqueous lower phase. What remains is the lyophilic pigment solution from which the solvent is distilled off, at about 60 ° C. Subsequently, the thus obtained oily turpentine oil phase can be centrifuged again to concentrate them. In this case, a part of the oil thus obtained can be recycled back into the process, as shown in Fig. 1. The rest of the turpentine oil is suitable for use in the surface treatment of wood.
In Fig. 2 ist ein Teil eines mit einem derartigen Holzschutzmittel behandelten Holzes 1 dargestellt. Das Holz 1 wird zunächst vorbehandelt, beispielsweise gebürstet, um die Oberfläche 2 aufzurauen. Anschließend erfolgt eine Beaufschlagung mit einer Lösung, die Hüllreste von Bakterien aufweist, die hauptsächlich aus Polysacchariden bestehen. Eine Behandlung mit einer derartigen Lösung führt zu einer Schicht 3, die sich bis circa 3 cm unter die Oberfläche 2 des Holzes 1 erstrecken kann. Dadurch wird eine feuchtigkeitsregulierende Schicht gebildet, weil die Polysaccharide Poren im Holz 1 ausfüllen und quasi eine Wassersperre darstellen. Anschließend wird oberflächennah bis zu einer Eindringtiefe von circa 200 pm bis 500 pm unter Bildung einer oberflächennahen Decklage 4 das eigentliche Holzschutzmittel aufgebracht, welches das zuvor erläuterte Öl rein oder gegebenenfalls in Verdünnung enthält. Sofern eine Verdünnung vorgesehen ist, kann jedes Lösungsmittel eingesetzt werden, dass einerseits das Öl bzw. Konzentrat löst und andererseits rasch verdampft; hierfür kommen beispielsweise kurzkettige Alkohole infrage.In Fig. 2, a part of a wood treated with such a wood preservative 1 is shown. The wood 1 is first pretreated, for example brushed, to roughen the surface 2. Subsequently, an application is made with a solution which has hull residues of bacteria, which consist mainly of polysaccharides. A treatment with such a solution leads to a layer 3, which can extend to about 3 cm below the surface 2 of the wood 1. As a result, a moisture-regulating layer is formed because the polysaccharides fill pores in the wood 1 and represent a quasi water barrier. Subsequently, the actual wood preservative is applied near the surface to a penetration depth of about 200 .mu.m to 500 .mu.m, forming a near-surface cover layer 4, which contains the previously explained oil pure or optionally in dilution. If a dilution is intended, any solvent can be used, on the one hand dissolves the oil or concentrate and on the other hand evaporates quickly; For example, short-chain alcohols come into question.
Als zusätzliche Variante zur noch besseren Ausnutzung der in den Blättern enthaltenen Naturstoffe ist es auch möglich, aus der hydrophilen Phase, die bei der Extraktion des Blattmehls erhalten wird, Gerbstoffe abzutrennen und diese zusammen mit der Polysaccharide enthaltenden Lösung in das Holz 1 einzubringen.As an additional variant for even better utilization of the natural substances contained in the leaves, it is also possible to separate tannins from the hydrophilic phase, which is obtained in the extraction of the leaf meal, and to introduce these into the wood 1 together with the polysaccharide-containing solution.
Claims (14)