AT256361B - Verfahren zur Herstellung von Verbundsicherheitsgläsern mit Zwischenschichten aus Organopolysiloxanelastomeren - Google Patents

Verfahren zur Herstellung von Verbundsicherheitsgläsern mit Zwischenschichten aus Organopolysiloxanelastomeren

Info

Publication number
AT256361B
AT256361B AT445365A AT445365A AT256361B AT 256361 B AT256361 B AT 256361B AT 445365 A AT445365 A AT 445365A AT 445365 A AT445365 A AT 445365A AT 256361 B AT256361 B AT 256361B
Authority
AT
Austria
Prior art keywords
production
intermediate layers
safety glasses
laminated safety
organopolysiloxane elastomers
Prior art date
Application number
AT445365A
Other languages
English (en)
Original Assignee
Dow Corning
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dow Corning filed Critical Dow Corning
Application granted granted Critical
Publication of AT256361B publication Critical patent/AT256361B/de

Links

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B17/00—Layered products essentially comprising sheet glass, or glass, slag, or like fibres
    • B32B17/06—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material
    • B32B17/10—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin
    • B32B17/10005—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing
    • B32B17/1055—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing characterized by the resin layer, i.e. interlayer
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C67/00—Shaping techniques not covered by groups B29C39/00 - B29C65/00, B29C70/00 or B29C73/00
    • B29C67/24—Shaping techniques not covered by groups B29C39/00 - B29C65/00, B29C70/00 or B29C73/00 characterised by the choice of material
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B17/00—Layered products essentially comprising sheet glass, or glass, slag, or like fibres
    • B32B17/06—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material
    • B32B17/10—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin
    • B32B17/10005—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing
    • B32B17/10009—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing characterized by the number, the constitution or treatment of glass sheets
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/24—Structurally defined web or sheet [e.g., overall dimension, etc.]
    • Y10T428/24942—Structurally defined web or sheet [e.g., overall dimension, etc.] including components having same physical characteristic in differing degree
    • Y10T428/2495—Thickness [relative or absolute]
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/31504—Composite [nonstructural laminate]
    • Y10T428/31551—Of polyamidoester [polyurethane, polyisocyanate, polycarbamate, etc.]
    • Y10T428/31609—Particulate metal or metal compound-containing
    • Y10T428/31612—As silicone, silane or siloxane
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/31504—Composite [nonstructural laminate]
    • Y10T428/31652—Of asbestos
    • Y10T428/31663—As siloxane, silicone or silane
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/31504—Composite [nonstructural laminate]
    • Y10T428/31652—Of asbestos
    • Y10T428/31667—Next to addition polymer from unsaturated monomers, or aldehyde or ketone condensation product

Landscapes

  • Engineering & Computer Science (AREA)
  • Mechanical Engineering (AREA)
  • Laminated Bodies (AREA)
  • Joining Of Glass To Other Materials (AREA)
AT445365A 1964-05-18 1965-05-17 Verfahren zur Herstellung von Verbundsicherheitsgläsern mit Zwischenschichten aus Organopolysiloxanelastomeren AT256361B (de)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
US368089A US3312587A (en) 1964-05-18 1964-05-18 Stable silicone rubber interlayers for glass

Publications (1)

Publication Number Publication Date
AT256361B true AT256361B (de) 1967-08-25

Family

ID=23449814

Family Applications (1)

Application Number Title Priority Date Filing Date
AT445365A AT256361B (de) 1964-05-18 1965-05-17 Verfahren zur Herstellung von Verbundsicherheitsgläsern mit Zwischenschichten aus Organopolysiloxanelastomeren

Country Status (4)

Country Link
US (1) US3312587A (de)
AT (1) AT256361B (de)
DE (1) DE1246232B (de)
GB (1) GB1093454A (de)

Families Citing this family (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3616839A (en) * 1967-06-30 1971-11-02 Swedlow Inc Glass-silicone resin-stretched acrylic resin laminates
GB1272774A (en) * 1968-08-23 1972-05-03 English Electric Co Ltd Laminated structures
JPS61244546A (ja) * 1985-04-22 1986-10-30 信越ポリマ−株式会社 耐熱防眩シ−ト
US5378535A (en) * 1992-07-29 1995-01-03 Pilkington Aerospace, Inc. Primer system for silicone elastomers
US20070202442A1 (en) * 2006-02-24 2007-08-30 Eastman Kodak Company Method and apparatus for merging a mask and a printing plate
WO2008103407A1 (en) 2007-02-22 2008-08-28 Dow Corning Corporation Composite article having excellent fire resistance
US20100146886A1 (en) * 2007-02-22 2010-06-17 Bizhong Zhu Composite Article Having Excellent Fire Resistance
CN101646559A (zh) * 2007-02-22 2010-02-10 陶氏康宁公司 具有优良的耐火性和抗冲击性的复合制品及其制备方法
ITBO20070588A1 (it) * 2007-08-13 2009-02-14 Silicon Biosystems Spa Metodo per legare uno strato di silicone ad un substrato di polimero metacrilico

Family Cites Families (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US2557778A (en) * 1949-04-21 1951-06-19 Dow Corning Bonding rubber to glass
US2860083A (en) * 1956-01-07 1958-11-11 Silicone rubber adhesive
FR1317551A (de) * 1961-03-22 1963-05-08

Also Published As

Publication number Publication date
US3312587A (en) 1967-04-04
DE1246232B (de) 1967-08-03
GB1093454A (en) 1967-12-06

Similar Documents

Publication Publication Date Title
AT254386B (de) Verfahren zur Herstellung von Kathetern mit verbesserter physiologischer Verträglichkeit
AT255761B (de) Verfahren zur Herstellung von Organopolysiloxan-Elastomeren
AT298516B (de) Verfahren zur Herstellung von Distickstoffmonoxyd
AT266369B (de) Verfahren zur Herstellung von hitzebeständigen Verbundsicherheitsgläsern
CH455260A (de) Verfahren zur Herstellung von Polyurethan-Schichtstoffen
AT262626B (de) Verfahren zur Herstellung von Schichtstoffen
CH442747A (de) Verfahren zur Herstellung von transparenten Polyamiden
AT285962B (de) Verfahren zur Herstellung von Schichtkörpern
AT299259B (de) Verfahren zur Herstellung von Distickstoffmonoxyd
AT303988B (de) Verfahren zur Herstellung von Verbundglas
CH418765A (de) Verfahren zur Herstellung von Magnetschichten
AT257935B (de) Verfahren zur Herstellung von Lösungen im wesentlichen linearer Polyurethanelastomerer
CH448520A (de) Verfahren zur Herstellung von transparenten, thermoplastischen Polyamiden
CH448493A (de) Verfahren zur Herstellung von Füllmittel enthaltenden Kunststoffschichten
CH497279A (de) Verfahren zur Herstellung von mit Deckschichten versehenen Formkörpern
AT277493B (de) Verfahren zur Herstellung von Glasgegenständen mit erhöhter Bruchfestigkeit
CH493327A (de) Verfahren zur Herstellung von planebenem, dreischichtigem Halbzeug für planebene Bauelemente
AT258851B (de) Verfahren zur Herstellung von Poliertüchern mit waschfester Imprägnierung
CH508679A (de) Verfahren zur Herstellung von Polyolefinoxiden mit erhöhtem Molgewicht
AT251290B (de) Verfahren zur Herstellung von Esterimidharz
AT255759B (de) Verfahren zur Herstellung von hitzebeständigen Organopolysiloxanelastomeren
CH486512A (de) Verfahren zur Herstellung von aromatischen Polyamiden
AT312183B (de) Verfahren zur Herstellung von Verbundsicherheits- oder Verbundpanzergläsern unter Verwendung oder Mitverwendung von Schichten aus amorphen Polyamiden
AT246357B (de) Verfahren zur Herstellung von Glasgegenständen mit großer mechanischer Festigkeit
CH475228A (de) Verfahren zur Herstellung von Tetrafluoräthylenoxyd