AT251185B - Verfahren zur Herstellung von Formgebilden aus Polyglykolid - Google Patents

Verfahren zur Herstellung von Formgebilden aus Polyglykolid

Info

Publication number
AT251185B
AT251185B AT101565A AT101565A AT251185B AT 251185 B AT251185 B AT 251185B AT 101565 A AT101565 A AT 101565A AT 101565 A AT101565 A AT 101565A AT 251185 B AT251185 B AT 251185B
Authority
AT
Austria
Prior art keywords
sep
polyglycolide
production
molded articles
weight
Prior art date
Application number
AT101565A
Other languages
English (en)
Original Assignee
Wolfen Filmfab Veb
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wolfen Filmfab Veb filed Critical Wolfen Filmfab Veb
Application granted granted Critical
Publication of AT251185B publication Critical patent/AT251185B/de

Description


   <Desc/Clms Page number 1> 
 
 EMI1.1 
 
 EMI1.2 
 

 <Desc/Clms Page number 2> 

 
 EMI2.1 
 

 <Desc/Clms Page number 3> 

 
 EMI3.1 
 
 EMI3.2 
 
<tb> 
<tb> gebilden476, <SEP> 5 <SEP> g <SEP> cyclischem <SEP> Diglykolid <SEP> (Säurezahl <SEP> 0,20) <SEP> = <SEP> 95,3 <SEP> Gew.-%
<tb> 20, <SEP> 0 <SEP> g <SEP> cyclischem <SEP> Dilactid <SEP> (Säurezahl <SEP> 0, <SEP> 10) <SEP> = <SEP> 4,0 <SEP> Gew.-%
<tb> 2,5 <SEP> g <SEP> Zinn <SEP> (II)-stearat <SEP> = <SEP> 0,5 <SEP> Gew.-%
<tb> 1,0 <SEP> g <SEP> Tetracyclohexyl-orthosilikat <SEP> (0,07 <SEP> g <SEP> Si) <SEP> = <SEP> 0,2 <SEP> Gew.-%
<tb> 
 
 EMI3.3 
 
 EMI3.4 
 
<tb> 
<tb> DieUc
<tb> Einfüllstutzen <SEP> 12
<tb> Heizzone <SEP> I <SEP> 90
<tb> Heizzone <SEP> n <SEP> 140
<tb> Heizzone <SEP> III <SEP> 185
<tb> Spritzkopf <SEP> 210
<tb> 
 
 EMI3.5 
 
 EMI3.6 
 
<tb> 
<tb> Faden <SEP> werden470,

  0 <SEP> g <SEP> cyclisches <SEP> Diglykolid <SEP> = <SEP> 94,0 <SEP> Gew.-%
<tb> 20, <SEP> 0 <SEP> g <SEP> cyclisches <SEP> Dilactid <SEP> = <SEP> 4,0 <SEP> Gew.-%
<tb> 7,5 <SEP> g <SEP> Tetta-n-butoxy-siloxan <SEP> (1, <SEP> 4 <SEP> g <SEP> Si)
<tb> (HandelsproduktmîtderBezeichnungn-Butylsîlikat40) <SEP> = <SEP> 1, <SEP> 5Gew.-o <SEP> 
<tb> 2.

   <SEP> 5 <SEP> g <SEP> Zinn(II)-stearat <SEP> = <SEP> 0,5 <SEP> Ggew.-%.
<tb> 
 

 <Desc/Clms Page number 4> 

 
 EMI4.1 
 
 EMI4.2 
 
<tb> 
<tb> der <SEP> verschiedenen <SEP> Heizzonen <SEP> sindUG
<tb> Einfüllstutzen <SEP> 12
<tb> Heizzone <SEP> I <SEP> 80
<tb> Heizzone <SEP> II <SEP> 130
<tb> Heizzone <SEP> III <SEP> 190
<tb> Spritzkopf <SEP> 200.
<tb> 
 
 EMI4.3 
 
 EMI4.4 
 
<tb> 
<tb> relative <SEP> Viskosität473,75 <SEP> g <SEP> cyclisches <SEP> Diglykolid <SEP> (Säurezahl <SEP> 0,20) <SEP> = <SEP> 94,75 <SEP> Gew.-%
<tb> 20,0 <SEP> g <SEP> cyclisches <SEP> Dilactid <SEP> (Säurezahl <SEP> 0,10) <SEP> = <SEP> 4,0 <SEP> Gew.-%
<tb> 2,5 <SEP> g <SEP> Zinn(II)-stearat <SEP> = <SEP> 0,5 <SEP> Gew.-%
<tb> 3. <SEP> 75 <SEP> g <SEP> hochdisperse <SEP> Kieselsäure <SEP> (1.

   <SEP> 75 <SEP> g <SEP> Si) <SEP> = <SEP> 0,75 <SEP> Gew.-%.
<tb> 
 
 EMI4.5 
 
 EMI4.6 
 
<tb> 
<tb> Viskosität <SEP> der474, <SEP> 0 <SEP> g <SEP> cyclischem <SEP> Diglykolid <SEP> (Säurezahl <SEP> 0,20) <SEP> = <SEP> 94,8 <SEP> Gew.-%
<tb> 20, <SEP> 0 <SEP> g <SEP> cyclischem <SEP> Dilactid <SEP> (Säurezahl <SEP> 0,10) <SEP> = <SEP> 4,0 <SEP> Gew.%
<tb> 2,3 <SEP> g <SEP> Zinn <SEP> (III)-stearat <SEP> = <SEP> 0,5 <SEP> Gew.-%
<tb> 2,5 <SEP> g <SEP> hochdisperser <SEP> Kieselsäure <SEP> (1,17 <SEP> g <SEP> Si) <SEP> = <SEP> 0,5 <SEP> Gew.-%
<tb> 1,0 <SEP> g <SEP> Tetra-cyclohexyl-orthosilikat <SEP> (0,07 <SEP> g <SEP> Si) <SEP> = <SEP> 0,2 <SEP> Gew.-%.
<tb> 
 
 EMI4.7 
 

**WARNUNG** Ende DESC Feld kannt Anfang CLMS uberlappen**.

Claims (1)

  1. <Desc/Clms Page number 5> EMI5.1
AT101565A 1964-12-10 1965-02-05 Verfahren zur Herstellung von Formgebilden aus Polyglykolid AT251185B (de)