AR013856A1 - STEEL NICKEL AND PROCEDURE FOR THE MANUFACTURE OF LAMINATED AND FORGED PRODUCTS OF THIS STEEL - Google Patents
STEEL NICKEL AND PROCEDURE FOR THE MANUFACTURE OF LAMINATED AND FORGED PRODUCTS OF THIS STEELInfo
- Publication number
- AR013856A1 AR013856A1 ARP970104839A AR013856A1 AR 013856 A1 AR013856 A1 AR 013856A1 AR P970104839 A ARP970104839 A AR P970104839A AR 013856 A1 AR013856 A1 AR 013856A1
- Authority
- AR
- Argentina
- Prior art keywords
- steel
- max
- manufacture
- laminated
- procedure
- Prior art date
Abstract
El invento se refiere a un acero niquelífero para la fabricacion de productos laminados y forjados conteniendo el acero los siguientes elementosquímicos (porcentaje en peso): C 0,02% hasta 0,06%, Si 0,15% hasta 0,30%, Mn 1,60% hasta 1,80%,P max. 0,035%, S max. 0,008%, Al max. 0,020%, Cr 12,05%hasta 13, 5%, Nb 0,025% hasta 0,060%, N 0,010% hasta 0,035%, así como hierro e impurezas usuales. El acero contiene además: Ni 0,3% hasta 0,5%, V max. 0,07%,Ti max. 0,01%, W0,03% hasta 1,00% estando limitada la suma de C y Na max. 0,07% y la suma de V y Ti a max. 0,07%The invention relates to a nickeliferous steel for the manufacture of rolled and forged products containing the steel the following chemical elements (weight percentage): C 0.02% to 0.06%, If 0.15% to 0.30%, Mn 1.60% up to 1.80%, P max. 0.035%, S max. 0.008%, at max. 0.020%, Cr 12.05% up to 13.5%, Nb 0.025% up to 0.060%, N 0.010% up to 0.035%, as well as iron and usual impurities. The steel also contains: Ni 0.3% up to 0.5%, V max. 0.07%, Ti max. 0.01%, W0.03% up to 1.00% with the sum of C and Na max being limited. 0.07% and the sum of V and Ti to max. 0.07%
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
DE1996145139 DE19645139A1 (en) | 1996-10-24 | 1996-10-24 | Ni-containing steel and process for the production of rolled and forged products from this steel |
Publications (1)
Publication Number | Publication Date |
---|---|
AR013856A1 true AR013856A1 (en) | 2001-01-31 |
Family
ID=7810429
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
ARP970104839 AR013856A1 (en) | 1996-10-24 | 1997-10-20 | STEEL NICKEL AND PROCEDURE FOR THE MANUFACTURE OF LAMINATED AND FORGED PRODUCTS OF THIS STEEL |
Country Status (3)
Country | Link |
---|---|
AR (1) | AR013856A1 (en) |
DE (1) | DE19645139A1 (en) |
WO (1) | WO1998017835A1 (en) |
Families Citing this family (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
DE19652335C1 (en) * | 1996-12-03 | 1998-03-12 | Mannesmann Ag | Seamless corrosion resistant steel bottle production used for storing high purity or corrosive gas or liquid |
Family Cites Families (7)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US3385739A (en) * | 1965-04-13 | 1968-05-28 | Eaton Yale & Towne | Alloy steel articles and the method of making |
DE2333466C2 (en) * | 1973-06-30 | 1982-09-02 | Vacmetal Gesellschaft für Vakuum-Metallurgie mbH, 4600 Dortmund | Process for the manufacture of alloy steels |
DE3247568A1 (en) * | 1981-12-23 | 1983-06-30 | Kubota Ltd., Osaka | REACTOR TUBE FOR THERMAL CRACKING OR REFORMING HYDROCARBONS |
JPS63238217A (en) * | 1987-03-26 | 1988-10-04 | Kawasaki Steel Corp | Production of seamless steel pipe of martensitic stainless steel having excellent low-temperature toughness and stress corrosion cracking resistance |
JPH06104868B2 (en) * | 1990-08-03 | 1994-12-21 | 新日本製鐵株式会社 | Method for manufacturing high strength martensitic stainless steel line pipe |
JP3116156B2 (en) * | 1994-06-16 | 2000-12-11 | 新日本製鐵株式会社 | Method for producing steel pipe with excellent corrosion resistance and weldability |
JPH08109444A (en) * | 1994-10-07 | 1996-04-30 | Nippon Steel Corp | Production of seamless martensitic stainless steel tube for oil well use, excellent in crushing pressure |
-
1996
- 1996-10-24 DE DE1996145139 patent/DE19645139A1/en not_active Withdrawn
-
1997
- 1997-10-07 WO PCT/DE1997/002359 patent/WO1998017835A1/en active Application Filing
- 1997-10-20 AR ARP970104839 patent/AR013856A1/en unknown
Also Published As
Publication number | Publication date |
---|---|
DE19645139A1 (en) | 1998-04-30 |
WO1998017835A1 (en) | 1998-04-30 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
ES2121985T3 (en) | MANGANESE RICH AUSTENITIC STEEL SHEET WITH SUPERIOR CONFORMABILITY, STRENGTH AND WELDABILITY, AND PROCEDURE FOR ITS MANUFACTURE. | |
BRPI0406958A (en) | Martensitically Alloy and Alloy Production Method | |
SE8501011L (en) | STOCK AND WAY TO MANUFACTURE THE SAME | |
ATE243779T1 (en) | LOW ALLOY, HIGH STRENGTH, HEAT RESISTANT STEEL | |
MX157485A (en) | IMPROVED PROCEDURE FOR PREPARING A WEAR-RESISTANT AUSTENITIC STEEL | |
AR012333A1 (en) | STEEL FOR THE MANUFACTURE OF A BEARING PART, PROCEDURE FOR THE MANUFACTURE OF A BEARING PART, STEEL TUBE WITHOUT WELDING AND STEEL BEARING PIECE. | |
AR004345A1 (en) | STEEL FOR THE MANUFACTURE OF A FORGED PART THAT HAS A BAINITIC STRUCTURE AND PROCEDURE FOR THE MANUFACTURE OF A PART | |
ES2048281T3 (en) | AUSTENITIC STAINLESS STEEL ALLOY. | |
BR9508120A (en) | Nickel-based alloy and method | |
AU2003278256A8 (en) | Very high mechanical strength steel and method for making a sheet thereof coated with zinc or zinc alloy | |
SE9602494L (en) | Use of a steel as a material for cutting tool holders | |
CA2265002A1 (en) | Hot working die steel and member comprising the same for high-temperature use | |
AR013856A1 (en) | STEEL NICKEL AND PROCEDURE FOR THE MANUFACTURE OF LAMINATED AND FORGED PRODUCTS OF THIS STEEL | |
CA2314325A1 (en) | Powder material for powder plasma build-up welding and metal formed by powder plasma build-up welding | |
JPS5672156A (en) | Low-alloy heat-resistant steel for high temperature use | |
ES2054582A1 (en) | Use of a steel for cold-rollers. | |
JPS55145154A (en) | Rail steel with low weld crack sensibility and thermal expansion coefficient | |
JPS552775A (en) | High manganese heat resistant steel | |
MY120184A (en) | Fe-cr-ni alloy for electron gun electrodes | |
CA2220727A1 (en) | Cavitation erosion resistant steel | |
ES543202A0 (en) | PROCEDURE FOR OBTAINING STAINLESS STEEL | |
EP1228253B8 (en) | Steel composition, method for making same and parts produced from said compositions, particularly valves | |
JPS5524701A (en) | Welding material for high mn stable austenite non- magnetic steel | |
TW200641153A (en) | Ultra-high strength weathering steel and method for making same | |
JPS57188652A (en) | High-strength austenite steel with superior cold work hardenability |