WO2021188273A1

WO2021188273A1 - Flame resistant knit fabric

Info

Publication number: WO2021188273A1
Application number: PCT/US2021/019604
Authority: WO
Inventors: John W. RINGO
Original assignee: Milliken & Company
Priority date: 2020-03-19
Filing date: 2021-02-25
Publication date: 2021-09-23
Also published as: US20210292936A1

Abstract

A flame resistant knit fabric (10) having a first weft yarn set and a second weft yarn set. The first weft yarn set contains flame resistant yarns (100) and the second weft yarn set contains second weft yarns (200). The knit fabric (10) is knit such that the first weft yarns (100) are interlinked with one another by a plurality of knit stitches, the second weft yarns (200) are interlinked with one another by a plurality of knit stitches, and the first weft yarns (100) are not interlinked with the second weft yarns (200).

Description

FLAME RESISTANT KNIT FABRIC

FIELD OF THE INVENTION

[0001 ] The present invention generally relates to flame resistant knit fabrics for use as coverings for support articles such as mattresses.

BACKGROUND

[0002] It is well known in the textile industry to produce fire resistant products for use in upholstered furniture, mattresses, foundations, automotive seating, public transportation seating, aircraft seating and the like, using needlepunched, highloft, spunbond or spunlace nonwoven or woven or conventional knit fabrics formed of natural or synthetic fibers, and then treating these fabrics with fire retarding chemicals. Conventional fire retarding (FR) chemicals include borate-based, halogen-based, phosphorus-based, melamine-based and/or antimony-based chemicals. Unfortunately, such treated fabrics are heavier than similar types of non-fire retardant fabrics and have reduced wear life. Although flame resistant chemically treated fabrics will self-extinguish and exhibit limited melt behavior when a flame is removed, they typically form brittle chars, shrink and crack open after exposure to a direct flame allowing the underlying materials to ignite. There is a need for low cost, but high performing barrier materials for use in support articles.

BRIEF SUMMARY

[0003] A flame resistant knit fabric having a first weft yarn set and a second weft yarn set. The first weft yarn set contains flame resistant yarns and the second weft yarn set contains second weft yarns. The knit fabric is knitted such that the first weft yarns are interlinked with one another by a plurality of knit stitches, the second weft yarns are interlinked with one another by a plurality of knit stitches, and the first weft yarns are not interlinked with the second weft yarns. A flame resistant support article containing the flame resistant knit fabric as well as methods for making the knit fabric and support article are also disclosed.

BRIEF DESCRIPTION OF THE DRAWINGS

[0004] Figures 1 and 2 illustrate schematically exemplary flame resistant knit fabrics.

[0005] Figure 3 is a micrograph of the outer surface of one exemplary flame resistant knit fabric.

[0006] Figure 4 is a micrograph of the inner surface of one exemplary flame resistant knit fabric.

[0007] Figure 5 illustrates schematically the exemplary flame resistant fabric after burning.

[0008] Figure 6 illustrates schematically one embodiment of a flame resistant support article being a mattress.

DETAILED DESCRIPTION

[0009] “Flame resistant”, in this application means a material that provides a thermal barrier and reduces body burn as described in NFPA 1971 and allows the user time to escape the flames and/or fire. Such a fiber, yarn, fabric, or article would preferably resist ignition and be self-extinguishing. In its preferred usage in the present application, the term "flame barrier" means a product incorporated into or on top of a composite article that when tested with a composite type test method, such as: CPSC (Consumer Product Safety Council) CFR 1633, California Test Bulletin 129 (TB 129) or California Test Bulletin 603 (TB603) for mattresses and foundations and California Test Bulletin 133 (TB 133) for upholstered furniture, the flame barrier allows for the continued use of conventional materials such as dress cover fabrics, fiber-fillings and polyurethane foams, while still passing these stringent large open flame tests. It is understood by someone skilled in the art that flame bafflers made of the tubular knit flame barriers described in this invention, even at overall lower basis weights, can be made to pass less stringent open flame tests such California's Revised Test Bulletin 117 (TB 117- draft 02/02 version) and British Standard 5852.

[0010] The flame resistant knit fabric may be formed in any suitable manner and pattern. In one embodiment, the knit fabric is a tubular fabric, and in another embodiment, the knit fabric is a circular knit. These knits are advantageous for use as a barrier material for support articles such as mattresses as the knit would only require two seams to enclose the mattress.

[0011] Referring now to Figure 1A, there is shown a schematic of one exemplary flame resistant knit fabric 10. The knit fabric 10 contains a first weft yarn set and a second weft yarn set. The first weft yarn comprises first weft yarns 100 being flame resistant yarns. The second weft yarn set comprises second weft yarns 200. The knit fabric is knitted such that the first weft yarns are interlinked with one another by a plurality of knit stitches and the second weft yarns are interlinked with one another by a plurality of knit stitches. The first weft yarns and the second weft yarns are not interlinked.

[0012] In the embodiment shown in Figure 1 , the first weft yarn set has a repeating pattern of a knit stitch on a first needle and a welt on a second needle. A welt is also referred to as weft, miss, or float stitch. This stitch is created by not allowing the needle to raise high enough to receive a new yarn, causing the yarn to float behind the face stitches. The second weft yarn set has the same repeating pattern of stitches by offset from the first weft yarn set by one course so that its repeating pattern would be a welt on a first needle and a knit stitch on a second needle.

[0013] Some examples of other suitable patterns include a knit stitch, a welt, and a welt or a knit stitch, a knit stitch, and a welt. Any combination and repeat pattern of knit stitches, tuck stitches, welts, and any other stitch may be used in the first and/or second weft yarn sets so long as the first weft yarn set is interlinked. Preferably, the second weft yarns are interlinked with one another by a plurality of knit stitches and the first weft yarns and the second weft yarns are not interlinked. [0014] The first weft yarns 100 of the first weft yarn set are flame resistant yarns. These may be any suitable flame resistant yarn including inherently flame resistant yarns and chemically treated flame resistant yarns. In one preferred embodiment, the flame resistant yarns comprise continuous filament silica fibers also referred to as fiberglass fibers. In another embodiment, the flame resistant yarns can be flame resistant core spun yarns which has a core of a typically flame resistant material surrounded by at least one sheath of other fibers/yarns. More information on the core spun yarns and the method of making the yarns may be found in US Patent 6,410,140 (Land et al.), which is incorporated herein in its entirety.

[0015] The size of the product yarn will vary depending on the final application of the yarn and the particular fabric characteristics desired but is preferably within the range of from about 30/1 to 1/1 conventional cotton count, preferably from about 21/1 to 5/1 conventional cotton count for one embodiment.

[0016] The second weft yarns 200 of the second weft yarn set may be any suitable yarn. In one embodiment, the second weft yarns 200 are flame resistant spun yarns. In another embodiment, the second weft yarns do not contain continuous fibers such as monofilament or multifilament fibers. In another embodiment, the second weft yarns do not contain fiberglass. In another embodiment, the second weft yarns comprise monofilament or multifilament fibers. In one preferred embodiment, the second weft yarns 200 are formed from a blend of at least two of the following: fire resistant rayon, modacrylic, and cotton, polyester staple fibers. When exposed to flame, the second weft yarns may melt and/or degrade.

[0017] In one embodiment, shown in Figure 2, the second weft yarn set comprises an alternating arrangement of an A yarn 201 and a B yarn 203. These yarns are alternated in the set preferably in a 1:1 alternating pattern (but the pattern could also be 2:2, 1 :2, 2:1 , or other suitable ratio and pattern). Preferably, the A yarn comprises a blend of polyester and flame resistant rayon fibers. Preferably, the A yarn consists essentially of (being defined as the yarn contains at least 97% by weigh) a blend of polyester and flame resistant rayon fibers. Preferably, all of the fibers in the A yarns are staple yarns. Preferably, the B yarn comprises a blend of cotton and modacrylic fibers. Preferably, the A yarn consists essentially of (being defined as the yarn contains at least 97% by weigh) a blend of cotton and modacrylic fibers. Preferably, all of the fibers in the B yarns are staple yarns.

[0018] The flame resistant knit fabric has an upper surface and a lower surface (thought the upper and lower surfaces can be reversed and do not indicate the orientation that the fabric is used in a finished article), wherein the majority of the upper surface comprises the first weft yarns and the majority of the lower surface comprises the second weft yarns. Majority means greater than 50% by weight. Figure 3 is a micrograph of the outer surface of one exemplary flame resistant knit fabric. Figure 4 is a micrograph of the inner surface of one exemplary flame resistant knit fabric.

[0019] After the flame resistant knit fabric is exposed to heat and/or flame, in one embodiment, the second weft yarns 200 and are compromised. These yarns may be completely melted, disintegrated, or have a significant reduction in their physical properties. The first weft yarns 100 will remain and provide the integrity of the knit fabric. Because the first weft yarns are interlinked with one another through the plurality of knit stitches, the first weft yarns will still form an interconnected grid and the knit will still have integrity after burning. An illustration of the knit fabric 15 having the second weft yarns 200 removed through burning is shown in Figure 5.

[0020] The flame resistant knit fabric 10 may be used as a flame barrier to any suitable article. Figure 6 illustrates a flame resistant support article 20 (in this Figure a mattress 12) surrounded by the flame resistant knit fabric 10 (part of the knit fabric 10 was removed in order to show lower layers in the Figure). The flame resistant knit fabric 10 preferably completely encapsulates the support article.

[0021 ] The support article may be any article providing support and flame resistance. Some examples of support articles include, but are not limited to, upholstered furniture, mattresses, foundations, automotive seating, public transportation seating, aircraft seating, and the like. In one preferred embodiment, the support article is a mattress. Example

[0022] The first weft yarn set was yarns of continuous filament fiberglass. The second weft yarn set was in an alternating pattern of A yarns and B yarns such as illustrated in Figure 2. The A yarns were formed from a blend of 25% wt polyester and 75% wt flame resistant rayon staple fibers and the B yarns were formed from a blend of 50 % wt cotton and 50 % wt modacrylic staple fibers.

[0023] The first and second weft yarn sets were circular knitted into a 3.4 ounce per square yard single knit, knit welt knit construction as shown in Figures 3 and 4.

[0024] All references, including publications, patent applications, and patents, cited herein are hereby incorporated by reference to the same extent as if each reference were individually and specifically indicated to be incorporated by reference and were set forth in its entirety herein.

[0025] The use of the terms “a” and “an” and “the” and similar referents in the context of describing the invention (especially in the context of the following claims) are to be construed to cover both the singular and the plural, unless otherwise indicated herein or clearly contradicted by context. The terms “comprising,” “having,” “including,” and “containing” are to be construed as open-ended terms (i.e. , meaning “including, but not limited to,”) unless otherwise noted. Recitation of ranges of values herein are merely intended to serve as a shorthand method of referring individually to each separate value falling within the range, unless otherwise indicated herein, and each separate value is incorporated into the specification as if it were individually recited herein. All methods described herein can be performed in any suitable order unless otherwise indicated herein or otherwise clearly contradicted by context. The use of any and all examples, or exemplary language (e.g., “such as”) provided herein, is intended merely to better illuminate the invention and does not pose a limitation on the scope of the invention unless otherwise claimed. No language in the specification should be construed as indicating any non-claimed element as essential to the practice of the invention.

[0026] Preferred embodiments of this invention are described herein, including the best mode known to the inventors for carrying out the invention. Variations of those preferred embodiments may become apparent to those of ordinary skill in the art upon reading the foregoing description. The inventors expect skilled artisans to employ such variations as appropriate, and the inventors intend for the invention to be practiced otherwise than as specifically described herein. Accordingly, this invention includes all modifications and equivalents of the subject matter recited in the claims appended hereto as permitted by applicable law. Moreover, any combination of the above- described elements in all possible variations thereof is encompassed by the invention unless otherwise indicated herein or otherwise clearly contradicted by context.

Claims

WHAT IS CLAIMED IS:

1. A flame resistant knit fabric comprising a first weft yarn set and a second weft yarn set, wherein the first weft yarn set comprises flame resistant yarns and the second weft yarn set comprises second weft yarns, wherein the knit fabric is knit such that the first weft yarns are interlinked with one another by a plurality of knit stitches, the second weft yarns are interlinked with one another by a plurality of knit stitches, and the first weft yarns are not interlinked with the second weft yarns.

2. The flame resistant knit fabric of claim 1 , wherein the first weft yarn set has a repeating stitch pattern comprising a knit stitch on a first needle and a welt on a second needle.

3. The flame resistant knit fabric of claim 2, wherein the second weft yarn set has a repeating stitch pattern comprising a welt on a first needle and a knit stitch on a second needle.

4. The flame resistant knit fabric of claim 3, wherein the knit stitches of the first weft yarn are in the same wale as the welts of the second weft yarn.

5. The flame resistant knit fabric of claim 1 , wherein the flame resistant yarns comprise continuous filament silica.

6. The flame resistant knit fabric of claim 1 , wherein the second weft yarns comprise an alternating arrangement of A yarns and B yarns, wherein the A yarns comprise a mixture of polyester and flame resistant rayon fibers, and wherein the B yarns comprise a mixture of modacrylic and cotton fibers.

7. The flame resistant knit fabric of claim 1 , wherein the flame resistant knit fabric has an upper surface and a lower surface, wherein the majority of the upper surface comprises the first weft yarns and the majority of the lower surface comprises the second weft yarns.

8. A flame resistant support article comprising: a support article comprising a resilient material; and a knit fabric at least partially surrounding the support article, wherein the knit fabric comprises a first weft yarn set and a second weft yarn set, wherein the first weft yarn set comprises a flame resistant yarns and the second weft yarn set comprises second weft yarns, wherein the knit fabric is knit such that the first weft yarns are interlinked with one another by a plurality of knit stitches, the second weft yarns are interlinked with one another by a plurality of knit stitches, and the first weft yarns are not interlinked with the second weft yarns.

9. The flame resistant support article of claim 8, wherein the first weft yarn set has a repeating stitch pattern comprising a knit stitch on a first needle and a welt on a second needle, wherein the second weft yarn set has a repeating stitch pattern comprising a welt on a first needle and a knit stitch on a second needle, and wherein the knit stitches of the first weft yarn are in the same wale as the welts of the second weft yarn.

10. The flame resistant support article of claim 8, wherein the knit fabric fully encapsulates the support article.

11. The flame resistant support article of claim 8, wherein the support article is a mattress.

12. The flame resistant support article of claim 8, wherein the article is selected from the group consisting of a cushion, pillow, office panel, and seat.

13. The flame resistant support article of claim 8, wherein the first weft yarn set has a repeating stitch pattern comprising a knit stitch on a first needle, a welt on a second needle and a welt on a third needle.

14. The flame resistant support article of claim 8, wherein the second weft yarns comprise an alternating arrangement of A yarns and B yarns, wherein the A yarns comprise a mixture of polyester and flame resistant rayon fibers, and wherein the B yarns comprise a mixture of modacrylic and cotton fibers.

15. The flame resistant support article of claim 8, wherein the flame resistant knit fabric has an upper surface and a lower surface, wherein the majority of the upper surface comprises the first weft yarns and the majority of the lower surface comprises the second weft yarns.