WO2005059500A1 - Process for detecting leaks in sealed packages - Google Patents
Process for detecting leaks in sealed packages Download PDFInfo
- Publication number
- WO2005059500A1 WO2005059500A1 PCT/US2004/042264 US2004042264W WO2005059500A1 WO 2005059500 A1 WO2005059500 A1 WO 2005059500A1 US 2004042264 W US2004042264 W US 2004042264W WO 2005059500 A1 WO2005059500 A1 WO 2005059500A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- package
- process according
- indicator
- film
- leak
- Prior art date
Abstract
Description
Claims