WO2001034394A1 - A fluid for preparation of printing plates and method for use of same - Google Patents
A fluid for preparation of printing plates and method for use of same Download PDFInfo
- Publication number
- WO2001034394A1 WO2001034394A1 PCT/IL2000/000722 IL0000722W WO0134394A1 WO 2001034394 A1 WO2001034394 A1 WO 2001034394A1 IL 0000722 W IL0000722 W IL 0000722W WO 0134394 A1 WO0134394 A1 WO 0134394A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- marking fluid
- printing
- plate
- inkjet
- fluid
- Prior art date
Abstract
Description
Claims