USRE30405E - Thermoplastic blend of partially cured monoolefin copolymer rubber and polyolefin plastic - Google Patents

Thermoplastic blend of partially cured monoolefin copolymer rubber and polyolefin plastic Download PDF

Info

Publication number
USRE30405E
USRE30405E US05/941,601 US94160178A USRE30405E US RE30405 E USRE30405 E US RE30405E US 94160178 A US94160178 A US 94160178A US RE30405 E USRE30405 E US RE30405E
Authority
US
United States
Prior art keywords
blend
curative
percent
semi
rubber
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
US05/941,601
Inventor
William K. Fischer
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Uniroyal Chemical Co Inc
Original Assignee
Uniroyal Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Uniroyal Inc filed Critical Uniroyal Inc
Priority to US05/941,601 priority Critical patent/USRE30405E/en
Application granted granted Critical
Publication of USRE30405E publication Critical patent/USRE30405E/en
Assigned to UNIROYAL CHEMICAL COMPANY, INC., WORLD HEADQUARTERS, MIDDLEBURY, CT. 06749, A CORP. OF NEW JERSEY reassignment UNIROYAL CHEMICAL COMPANY, INC., WORLD HEADQUARTERS, MIDDLEBURY, CT. 06749, A CORP. OF NEW JERSEY ASSIGNMENT OF ASSIGNORS INTEREST. Assignors: UNIROYAL, INC., A NEW YORK CORP.
Assigned to UNIROYAL CHEMICAL COMPANY, INC. reassignment UNIROYAL CHEMICAL COMPANY, INC. ASSIGNMENT OF ASSIGNORS INTEREST. Assignors: UNIROYAL, INC., A NJ CORP.
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

Thermoplastic blends of partially cured monoolefin copolymer rubber (such as EPM or EPDM rubber) with a polyolefin resin (such as polypropylene) exhibit good physical properties and are reprocessable. The partial cure of the rubber is effected by heating the rubber with a curative such as a peroxide. The blends are used to make molded or extruded articles which have good physical properties without requiring vulcanization; preferred blends have the characteristics of thermoplastic elastomers.

Description

This invention relates to a thermoplastic blend and a method of making same.
Thermoplastic elastomers, which can be processed and fabricated by methods used for thermoplastics and do not require vulcanization to develop elastomeric properties, are known (see, for example, U.S. Pat. No. 3,265,765, Holden et al., Aug. 9, 1966; also Hartman et al., "Butyl Grafted to Polyethylene yields Thermoplastic Elastomer" Rubber World, Oct., 1970, pages 59-64). Conventionally these materials have been made by special block copolymerization or polymer grafting methods. The present invention is based on the discovery that a thermoplastic elastomeric composition can be made by blending a certain rubber and resin.
Blends of monoolefin copolymers with polyolefins have been known (e.g., U.S. Pat. Nos. 3,256,366 Corbelli et al., June 14, 1966 and 3,456,038 Newman et al., July 15, 1969; British patent 1,043,078, Phillips Petroleum Co., Sept. 21, 1966; Canadian patents 789,074 Brender et al., July 2, 1968 and 792,277, Schreiber, Aug. 13, 1968; Belgian patent 731,950, Sumitomo Chemical Co., Oct. 23, 1969, etc.), but those blends have not had the characteristics of thermoplastic elastomers.
The present invention is based on the discovery that a thermoplastic blend having highly desirable characteristics is provided by a partially cured rubber in admixture with a resin. More particularly, the invention is based on a blend of partially cured monoolefin copolymer rubber and polyolefin plastic, which blend is thermoplastic and can be fabricated by such methods as molding and extrusion, into shaped articles, which do not require a vulcanization step to develop good physical properties. The invention thus provides thermoplastic elastomers which can be molded or otherwise shaped without necessity for performing an expensive and time-consuming vulcanization step in the shaped article. Furthermore the blends can be reprocessed, just like a typical thermoplastic material.
In accordance with the invention the monoolefin copolymer rubber, typified by saturated EPM (ethylene-propylene copolymer rubber) or unsaturated EPDM (ethylene-propylene-non-conjugated diene terpolymer rubber), is partially cured by the action of a conventional curing agent. The curing conditions are such that the cure of the rubber is only partial, that is, the rubber is not cross-linked to the state where it becomes almost entirely insoluble in the usual solvents for the uncured rubber. It has been found that monoolefin rubber which has thus been partially cured or crosslinked, provides, in admixture with a poly-olefin plastic, a thermoplastic material having the herein describe unusual combination of desirable characteristics.
In carrying out the invention the monoolefin copolymer rubber component of the blend is first mixed with a small amount of curative, and subjected to curing conditions. The amount of curative and the curing conditions are so selected as to produce only a partial cure of the rubber as evidenced by conventional tests suitable for determining the degree of cure or cross-linking of an elastomer, such as various solubility and swelling tests, including conventional gel determinations, tests for cross-link density, tests for combined sulfur when sulfur cures are used, and the like. Another method for determining a partial state of cure is to observe whether the material processes on a mill to form a continuous band or whether it fails to knit, which would indicate over-curing. The blend of the invention is provided by mixing the partially cured monoolefin rubber with a polyolefin plastic.
The monoolefin copolymer rubber employed in the blend of the invention is an amorphous, random, elastomeric copolymer of two or more monoolefins, with or without a copolymerizable polyene. Usually two monoolefins are used, but three or more may be used. Ordinarily one of the monoolefins is ethylene while the other is preferably propylene. However other alphamonoolefins may be used including those of the formula CH2 ═CHR where R is an alkyl radical having for example one to 12 carbon atoms (e.g., butene-1, pentene-1, hexene-1,4-methylpentene-1,5-methylhexene-1,4-ethylhexene-1, etc.). While the monoolefin copolymer rubber may be a saturated material, as in ehtylene-propylene binary copolymer rubber ("EPM") it is ordinarily preferred to include in the copolymer a small amount of at least one copolymerizable polyene to confer unsaturation on the copolymer. Although conjugated dienes such as butadiene or isoprene may be used for this purpose (British patent 983,437; Belgian patent 736,717, Sumitomo Chemical Co. Jan. 29, 1970) in practice it is usual to employ a non-conjugated diene, including the open-chain non-conjugated diolefins such as 1,4-hexadiene (U.S. Pat. No. 2,933,480 Gresham et al., Apr. 19, 1960) or a cyclic diene, especially a bridged ring cyclic diene, as in dicyclopentadiene (U.S. Pat. No. 3,211,709, Adamek et al., Oct. 12, 1965), or an alkyl-idenenorbornene as in methylenenorbornene or ethylidenenorbornene (U.S. Pat. No. 3,151,173, Nyce, Sept. 29, 1964), as well as cycloctadiene, methyltetrahydroindene, etc. (see also such U.S. Pats. Nos. as 3,093,620 and 3,093,621; also 3,538,192 col. 6, line 49 to col. 7, line 51). The polyenes employed are not limited to those having only two double bonds, but include those having three or more double bonds.
The polyolefin resin with which the semi-cured monoolefin copolymer rubber is mixed to make the blend of the invention is a solid, high molecular weight resinous plastic material made by polymerizing such olefins as ethylene, propylene, butene-1, pentene-1,4-methyl-pentene, etc., in conventional manner. Thus, such crystalline polyolefins as polyethylene (either of the low density [e.g., 0.910-0.925 g/cc], medium density [0.926-0.940 g/cc] or high density [e.g., 0.941-0.965 g/cc] type) may be used, whether prepared by high pressure processes or low pressure processes, including linear polyethylene. Polypropylene is a preferred polyolefin plastic, having highly crystalline isotactic and syndiotactic forms. Frequently the density of polypropylene is from 0.800 to 0.980 g/cc. Largely isotactic polypropylene having a density of from 0.900 to 0.910 g/cc may be mentioned particularly. Crystalline block copolymers of ethylene and propylene (which are plastics distinguished from amorphous, random ethylene-propylene elastomers) can also be used. Included among the polyolefin resins are the higher alpha-olefin modified polyethylenes and polypropylenes (see "Polyolefins," N. V. Boenig, Elsevier Publishing Co., N.Y., 1966).
The relative proportions of partially cured monoolefin copolymer rubber and polyolefin plastic employed in the blends of the invention may vary widely, for example from 10 to 90 parts by weight of partially cured mono-olefin copolymer rubber and correspondingly 90 to 10 parts of polyolefin plastic, depending on the characteristics desired in the blends. Of particular importance are the blends having an elastomeric character, containing a major proportion of the partially cured monoolefin co-polymer rubber, usually 50 to 90 parts of the semi-cured rubber, more preferably 60 to 80 parts, per 100 parts by weight of the blend of rubber and plastic.
As indicated, an important feature of the invention resides in semi-curing the monoolefin copolymer rubber to be mixed with the polyolefin plastic. For this purpose any conventional curative may be employed, incuding such free-radical generating agents or cross-linking agents as the peroxides, whether aromatic or aliphatic as in the aromatic diacyl peroxides and aliphatic diacyl peroxides, dibasic acid peroxides, ketone peroxides, alkyl peroxyesters, alkyl hydroperoxides, e.g., diacetylperoxide, dibenzoylperoxide, bis-2,4-dichlorobenzoyl peroxide, di-tert.-butyl peroxide, dicumylperoxide, tert.-butylperbenzoate, tert.-butylcumyl peroxide, 2,5-bis (tert.-butylperoxy)-2,5-dimethylhexane, 2,5-bis-(tert.-butylperoxy)-2,5-dimethylhexyne-3; 4,4,4',4'-tetra-(tert.-butylperoxy)-2,2-dicyclohexylpropane, 1,4-bis-(tert.-butylperoxyisopropyl)-benzene, 1,1-bis-(tert.-butylperoxy)-3,3,5-trimethylcyclohexane, lauroyl peroxide, succinic acid peroxide, cyclohexanone peroxide, tert.-butyl peracetate, butyl hydroperoxide, etc. Also suitable are the azide types of curing agents including such materials as the azidofomates [e.g., tetramethylenebis(azidoformate); for others see U.S. Pat. No. 3,284,421, Breslow, Nov. 8, 1966], aromatic polyazides (e.g. 4,4'-diphenylmethan diazide; for others see U.S. Pat. No. 3,297,674, Breslow et al., Jan. 10, 1967), and sulfonazides such as p,p'-oxybis(benzene sulfonyl azide), etc. Other curatives that may be used include the aldehydeamine reaction products such as formaldehyde-ammonia, formaldehyde-ethylchloride-ammonia, acetaldehyde-ammonia, formaldehyde-aniline, butyraldehyde-aniline, heptaldehyde-aniline, heptaldehyde-formaldehyde-aniline, hexamethylenetetramine, alpha-ethyl-beta-propylacrolein-aniline; the substituted ureas [e.g., trimethylthiourea, diethylthiourea, dibutylthiourea, tripentylthiourea, 1,3-bis(2-benzothiazolyl-mercaptomethyl) urea, and N,N-diphenylthiourea]; guanidines (e.g., diphenylguanidine, di-o-tolylguandine, diphenylguanidine phthalate, and di-o-tolylguanidine salt of dicatechol borate); xanthates (e.g., zinc ethylxanthate, sodium isopropylxanthate, butylxanthic disulfide, potassium isopropylxanthate, and zinc butylxanthate; dithiocarbamates (e.g., copper dimethyl-,zinc dimethyl-, tellurium diethyl-, cadmium dicyclohexyl-, lead dimethyl-, selenium dibutyl-, zinc pentamethylene-, zinc didecyl-, and zinc isopropyloctyl-, dithiocarbamate); thiazoles [e.g., 2-mercaptobenzothiazole; zinc mercaptothiazolyl mercaptide, 2-benzothiazolyl-N,N-diethylthiocarbamyl sulfide, and 2,2'-dithiobis (benzothiazole)]; imidazoles (e.g., 2-mercaptoimidazoline and 2-mercapto-4,4,6-trimethyldihydropyrimidine); sulfenamides [e.g., N-t-butyl-2-benzothiazole-, N-cyclohexylbenzothiazole-, N,N-diisopropylbenzothiazole-, N-(2,6-dimethylmorpholino)-2-benzothiazole-, and N,N-diethylbenzothiazole-sulfenamide]; thiuramidisulfides (e.g., N,N'-diethyl-, tetrabutyl-, N,N'-di-isopropyldioctyl-, tetramethyl-, N,N'-dicyclohexyl-, and N,N'-tetralauryl- thiuramdisulfide); also paraquinonedioxime, dibenzoparaquinonedioxime, etc. as well as sulfur itself (see Encyclopedia of Chemica Technology, Vol. 17, 2nd edition, Interscience Publishers, 1968; also Organic Peroxides, Daniel Severn, Vol. 1, Wiley-Interscience, 1970). The peroxide curative may be used alone, or in conjunction with the usual auxilliary substances such as sulfur, maleimides including bismaleimides, poly-unsaturated compounds (e.g., cyanurate), acrylic esters (e.g., trimethylolpropanetrimethacrylate), etc. With sulfur curatives, such as sulfur itself or sulfur donors, it is usually desirable to include an accelerator of sulfur vulcanization as well as an activator (e.g., a metal salt or oxide), as in conventional practice. Mixed peroxide-type or mixed sulfur-type curing systems may be employed if desired such as dicumylperoxide plus 2,5-bis(tert.-butylperoxy)-2,5-dimethylhexane or sulfur plus tetramethylthiuramdisulfide. The preferred monoolefin copolymers having residual unsaturation, conferred by the presence of a polyene, such as EPDM, afford the widest choice of curatives. Reference may be had to "Vulcanization and Vulcanizing Agents," W. Hoffman, Palmerton Publishing Co., New York, 1967, for an extensive disclosure of curing agents.
In accordance with the invention, the amount of cure or cross-linking imparted to the monoolefin copolymer rubber component of the blend is only partial, as distinguished from a full or substantially complete cure or cross-linking. As indicated, various tests for cure or degree of cross-linking may be applied, one of the more convenient tests being the content of gel or insoluble material. For purposes of the invention, the gel content of the semi-cured or partially cross-linked monoolefin copolymer rubber should be substantially in excess of the gel content of the original rubber prior to the partial curing step. Thus, the gel content of the partially cured monoolefin copolymer rubber, measured in cyclohexane, will ordinarily be at least 10 percent in excess of the original gel content of the rubber, preferably at least 20 percent in excess, and more preferably at least 30 percent in excess of the gel content of the original uncured rubber. Ordinarily the gel content of the monoolefin copolymer rubber as semi-cured for purposes of the invention will be at least 30 percent but less than 90 percent in cyclohexane. In many cases the gel content, in cyclohexane, of the partially cured rubber preferably falls within the range of from 40 percent to 85 percent more preferably 55 to 75 percent. The gel is of course the portion of the rubber that is insoluble in the specified solvent, in this case cyclohexane, and is conveniently measured by immersing a sample of the material in the solvent for 48 hours at 73° F., taking an aliquot of the solution and determining the concentration of solute by evaporating the solvent. It will be understood that with other solvents at other temperatures, the gel value of a particular sample may be different. Thus, measured in boiling xylene the gel values of the present semi-cured monoolefin copolymer rubber would ordinarily be very much lower than (e.g., 30-40 percent lower) the given gel values in cyclohexane at 73° C.
The gel formed as a result of the described cross-linking treatment typically has a much lower swelling index than gel sometimes found in the original, untreated mono-olefin copolymer rubber. Typically the percent swell of the cyclohexane-insoluble gel formed as a result of the present semi-cure is at least 8 percent less, usually 10 percent to 70 percent less, than the percent swell of any gel present originally. Ordinarily the percent swell of the semi-cured monoolefin copolymer rubber is within the range of from 6 to 35 percent. (percent gel and percent swell are elucidated in more detail in U.S. Pat. No. 3,012,020, Kirk et al., Dec. 5, 1961.)
The desired semi-cure of the monoolefin copolymer rubber is brought about by mixing the rubber with a small amount of the curing or cross-linking agent, and subjecting the mixture of conventional curing conditions. It will be understood that the curing or cross-linking parameters (viz., the amount of curing agent, and/or the curing temperature and/or the curing time) will be so selected as to produce a partial or semi-cure, rather than a full or substantially complete cure. Thus, in many cases use of less than two-thirds, or use of less than one-half, and in some cases one-fourth or less, of the amount of curative conventionally required for full cure, is capable of producing the desired degree of partial cure in the monoolefin copolymer rubber, as evidenced by the development of a gel content in cyclohexane within the described range. Such gel content is distinguished from values of 100 percent gel content in cyclohexane displayed by the copolymer even before it is fully cured. Fully cured or cross-linked monoolefin copolymer rubber is almost entirely insoluble even in boiling xylene. It will also be understood that fully cured monoolefin copolymer rubber will not form a continuous sheet on a mill, that is, it is not a processable material.
The partial cure of the monoolefin copolymer rubber in admixture with the cross-linking agent may be brought about under dynamic conditions or under static conditions. To effect the semi-cure dynamically, the copolymer-curing agent mix may be worked on an open roll mill, or in an internal mixer (such as a Banbury mixer or an extruder). Frequently, working at a temperature of 160° to 400° F. for 5 or 10 minutes is sufficient to bring about the desired semi-cure. To effect the semi-cure statically, the copolymer-curing agent mix may be treated for example in an autoclave, for example at a temperature of 160° to 500° F. for 5 to 30 minutes.
The cross-linking treatment substantially exhausts the action of the curing agent so that there is little or no tendency for further advancement of cure to take place subsequently. Ordinarily, heating of the rubber-curative mix for a period of time equal to at least four half-lives of the peroxide or other curative is desirable. It is sometimes desirable to insure termination of the action of any remaining cross-linking agent, by adding to the mix, at the end of the partial curing step, a small amount of a free-radical scavenging agent, such as a stabilizer or antioxidant. In the dynamic semi-cure method, such stabilizer may be added and mixed in for the last minute or so of mixing. In the static semi-cure method, after removal of the semi-cured material from the autoclave, the semi-cured material may be subjected to one or more "refining" passes on a mill, and the stabilizer may be added in the course of or just prior to the blending with the poly-olefin plastic. Any conventional antioxidant or stabilizer may be used, including, by way of non limiting example, amine types, phenolic types, sulfides, phenyl alkanes, phosphites, etc. Representative materials are listed in "Rubber: Natural and Synthetic," Stern, Palmerton Publishing Co., New York, 1967, of which the disclosure at pages 244-256 is incorporated herein by reference; see also "Chemistry and Technology of Rubber" Davis & Blake, Reinhold, New York, 1937, Chapter XII. Included are such materials as 2,2,4-trimethyl-1,2-dihydroquinoline, diphenylamine acetone condensate, aldol alphanaphthylamine, octylated diphenylamine, N-phenyl-N'-cyclohexyl-p-phenylene diamine, 2,6-di.-tert.-butyl-4-methyl phenol, styrene-resorcinol resin, o-cresol monosulfide, di-p-cresol-2-propane, 2,5-di.-tert.-amylhydroquinone, dilauryl 3,3'-thiodipropionate, etc.
The thus partially cross-linked monoolefin copolymer rubber may be tested for gel content in cyclohexane and/or for processability (band formation on a mill). Such tests will reveal whether the polymer has received insufficient cross-linking on the one hand (gel content too low; swelling index high) or too much cross-linking on the other hand (gel content too high; inability to form a band on a tightly closed low-friction mill in spite of considerable refining). One or two preliminary tests on a small trial batch will usually suffice to establish a proper amount of particular curing agent to employ with a specific copolymer under a given set of pre-curing conditions. Appropriate manipulation of the variables may be made in any given case to produce a satisfactory result, using the working examples below as a guide.
Although in general the conditions under which the partial cure of the monoolefin copolymer rubber is effected may fall within the ranges of conventional vulcanizing conditions, it will be understood that care will be taken to limit the degree of cure, either by using reduced amount of curative and/or reduced duration or severity of the curing conditions, so that the rubber does not become completely cross-linked but remains at least partially soluble and thermoplastic, as distinguished from an insoluble, thermoset, fully cured rubber which is no longer processable. Although certain curing systems operate at room temperature it is more usual to heat the monoolefin copolymer containing the curative to bring about partial cure. Moderate heating (e.g. 100°-150° F.) is frequently sufficient although in some cases considerably higher temperatures (e.g., 300°-500° F. or more) may be used in the partial cure. The time required for the partial cure will vary with such factors as the particular copolymer rubber employed, the kind and amount of curative, and the temperature at which the partial cure is carried out, as well as other factors such as the size of the batch, the character of the heating device employed, whether the treatment is dynamic or static, etc. In general the time is inversely related to the temperature and concentration of curative, and more severe time-temperation conditions may be used in the static method than in the dynamic method.
The semi-cured monoolefin copolymer rubber is a thermoplastic, processable material as evidenced by the fact that it knits together to form a continuous sheet or band on a roll mill. In some cases where the degree of semi-cure has been relatively high, it may be necessary to break the material down slightly by milling, before it will band. Thus, if the semi-cured rubber has a gel content in cyclohexane in excess of 90 percent, it may be broken down by milling until the gel content is less than 90 percent, making it suitable for use in the invention. If the cure has gone beyond the point where the material can be broken down, the material is not suitable. The gel content of the semi-cured rubber at or prior to mixing with the resin should be less than 90 percent.
The thus pre-treated partially cross-linked monoolefin copolymer rubber may be blended with the polyolefin plastic in any appropriate conventional manner, for example on a roll mill, in a Banbury mixer or in an extruder to provide the thermoplastic blend of the invention. The mixing temperature should be sufficient to soften the plastic and form a uniform mix. Pigments, fillers, stabilizers, lubricants, u.v. screening agents, or other appropriate compounding or modifying ingredients may be included in the blend if desired. The blend of the invention provides a noteworthy combination of processability (including the ability to be reprocessed repeatedly) with good physical characteristics. The good physical characteristics include properties heretofore usually associated only with vulcanized or thermoset (not reprocessable) materials, notably low permanent set. The blends of the invention accordingly afford a way of producing thermo-formed shaped objects (e.g., by extrusion, injection or compression molding) which combine the convenience and speed of thermoplastic shaping with certain physical characteristics of thermoset or vulcanized elastomers.
Heretofore, certain desirable characteristics such as low permanent set have largely been obtainable only in vulcanized elastomers which required the molder to use a rather long dwell time in the mold to effect vulcanization. The vulcanized flash or scrap could not be reprocessed. On the other hand, thermoplastic materials could be molded rapidly and scrap could be reprocessed, but certain physical characteristics such as permanent set were usually rather poor. The present blends of partially pre-cured monoolefin copolymer rubber and polyolefin plastic combine in one material the advantages of rapid moldability and re-processability with the advantages of a vulcanizate (low permanent set).
It will be understood that in many plastic and elastomer shaping operations a considerable percentage of scrap is produced. Examples of this are in dieing out parts from extruded, press-molded or calendered sheet and sprues and runners which result from screw-injection molding. Such scrap produced from the blend of the invention may be chopped and re-extruded seven or more times with no significant deterioration in appearance or processing characteristics. The blends, in addition to being reprocessable, have enhanced properties including tensile strength and resistance to compression set, resistance to deterioration in oil, reduced elongation set, and improved resistance to abrasion and flex-cracking.
Useful articles that may be made from the blends of the invention by such methods as extrusion, screw-injection, blow molding, press molding, calendering and vacuum forming include extruded insulation on wire, gaskets, flexible tubing, balls, weatherstripping, flexible bumpers, etc.
The blend of the invention will of course invariably contain a substantial amount (e.g., at least 10 percent by weight) of each polymer, and the blends of particular interest are those in which the semi-cured monoolefin copolymer rubber constitutes at least half of the blend of the two polymers. The blends containing 50-90 percent (by weight, based on the sum of the weight of the two polymers) predominate in elastomeric properties and are preferred, while with decreasing amounts of partially cured monoolefin copolymer rubber the blends take on more the characteristics of a hard rubber or plastic. If desired, mixtures of EPM's or EPDM's or both may be used with one or more polyolefins.
In comparison to a commercially available thermoplastic elastomer which is a butadiene-styrene block copolymer known as Kraton 3125, blends of the invention have been observed to have higher hardness and, more importantly, much greater retention of hardness when heated to elevated temperatures of 200° or 300° F., for example. The heat deflection upon subjecting to 2,000 grams pressure per square inch for 1 hour at 250° F. was zero for compositions of the invention, but 67 percent for the conventional block copolymer. The volume change of compositions of the invention after immersion 24 hours at 150° F. in fuel B was of the order of 141 to 308 percent, whereas the block copolymer dissolved. In No. 2 oil, the volume change of compositions of the invention was 26-57 percent; the block copolymer changed 85 percent.
As indicated, processability, and particularly reprocessability, is an important characteristic of the blends of the invention. The processability of the blends may be evaluated by subjecting samples of the blend to such shaping operations as extrusion, injection molding, or compression molding, as described in the working examples below. Extrusion is the shaping method of choice where long continuous forms, such as hose, window seals, wire coatings, flat sheets, etc. are desired. It is important that the extruded article have acceptable surface smoothness. In most cases the materials of the invention are well adapted to extrusion methods, although in some cases, particularly where the gel level is on the high side, the extruded surfaces may not be as smooth to the touch as desirable. However, even the blends which are not satisfactorily extrudable can usually be shaped by injection molding. For satisfactory screw injection molding the material must form in the mold a homogeneous article of uniform strength. The flow viscosity characteristics of such blends are adequate to insure filling the mold under the operating conditions. The most highly semi-cured rubbers usually give blends of the invention which are ordinarily best shaped by press molding.
The elastomeric character of objects shaped without vulcanization from blends of the invention is perhaps evidenced most strikingly by the low elongation set at break, measured by ASTM D412. In the present preferred elastomeric blends, the elongation set at break is usually improved (i.e. decreased) by at least 30 percent, preferably by at least 50 percent. However other physical properties such as tensile strength and ultimate elongation at break are also significant, and the combined effect of these properties is conveniently expressed as a "performance factor," P.F., which is defined as follows:
P.F., psi×103 =[(Tensile, psi)×(Elongation, %)/Elongation Set at Break, %]
where the tensile strength and the elongation are measured by method ASTM D412. As will be made manifest in the working examples below, the "performance factor" of blends of the invention is improved (increased) by at least 20 percent more frequently by 45 percent, over the performance factor of otherwise similar blends in which the rubber is not semi-cured. In highly preferred blends, the performance factor is increased to two or more times its control value.
The reprocessability of the blends of the invention is demonstrated by the fact that blends of the invention have been extruded and re-extruded up to seven times and still retained desirable characteristics.
The following examples, in which all parts are expressed by weight, will serve to illustrate the practice of the invention in more detail.
EXAMPLE 1
In runs summarized in Table I, Part A and Part B an EPDM rubber semi-cured by hot-mastication with a peroxide curative is blended with various polyolefin plastics. The EPDM rubber to polyolefin plastic weight ratio ranges from 10:90 to 90:10. For comparison, some stocks are included containing no EPDM (Runs 17, 22 and 23); these are outside the invention. The EPDM rubber employed, identified as "EPDM-I," contains 47.5 percent ethylene, 47.5 percent propylene and 5 percent dicyclopentadiene, by weight; the Mooney viscosity is 65 (ML-4 at 250° F.); the gel content of the untreated EPDM is 3 percent (all gel contents expressed herein, unless otherwise indicated are measured by immersion in cyclohexane for 48 hours at 73° F.). The peroxide employed to semi-cure the EPDM, identified as "peroxide I," is 2,5-bis (tert-butylperoxy)-2,5-dimethylexane; it has a half-life at 347° F. of 0.98 minute; it is employed as a 50 percent active commercial preparation ("Varox"). For comparison some stocks are included in which no curative is used (Runs 1,2,3,18 and 20); these are outside the invention. The polyolefin plastics employed are polypropylene, high density polyethylene, and low density polyethylene. The polypropylene employed is a largely crystalline, isotactic polypropylene, having a metal flow index of 4.0 (ASTM D1238-57T, 230° C.), a specific gravity of 0.903, and 94 percent gel ("Profax 6523"). The polyethylene identified in Table I as "H. D. Polyethylene" is a high density polyethylene having a melt flow index of 0.3 (D 1238 E, 190° C.) a specific gravity of 0.956, and 90 percent gel ("Hifax 4601"). The polyethylene identified in Table I as "L. D. polyethylene" is a low density polyethylene having a melt flow index of 2.0 (D 1238, 190° C.) a specific gravity of 0.919, gel content nil ("DYNH"). Prior to blending the EPDM with the polyolefin resin, the EPDM is mixed with the indicated amount of peroxide curative on a warmed mill at a stock temperature usually not higher than 180° F., and then charged to a Banbury preheated to 240° F. The EPDM-peroxide mix is masticated until the temperature as read on a chart activated by a thermocouple located on the wall of the mixing chamber indicates a temperature of 360°-410° F. (see "cure temperature" in Table I). This ordinarily takes about 2-3 minutes. The mixing is continued at the temperature for an additional 7-8 minutes ("cure time" in Table I). The actual stock temperature is usually about 25°-30° F. higher than the chart temperature. One part (per 100 parts of EPDM) of an antioxidant, tris(nonylated phenyl) phosphite, is then added and blended in for 1 minute as a free-radical scavenger. The gel content, percent swell and Mooney viscosity of the thus semi-cured EPDM are then determined with the results shown in Table I.
In the next step of the process the semi-cured EPDM rubber is blended with the polyolefin plastic, in the amounts shown in Table I, in the Banbury mixer. The "blending temperature" listed in Table I is the maximum chart temperature achieved in the run (the actual stock temperatures are usually some 25° to 30° F. higher); the "blending time" is the length of time for which mixing is continued at that temperature. The blending time for the blends using semi-cured EPDM rubber is about 1 minute, but for the blends using EPDM rubber that has not been pre-cured (control stocks 1,2,3, 18 and 20) the blending time employed is about 7 minutes. The purpose of this is to essentially equalize the total masticating time at elevated temperature, for better comparison. The thus uniformly mixed blend is then discharged from the Banbury, formed into a sheet on a mill and chopped into pellets for further evaluation.
In Table I, the values listed as "calculated gel" are theoretical gel values of the blend calculated from the known gel contents of the two components of the blend, assuming no change in gel values of the ingredients in the course of the blending. Also listed are the actual gel values as measured on the blends, as well as the percent swell of the blends. The calculated values are somewhat less than the actual measured gel content; this may be attributed to entrappment or coating of portions of the relatively soluble EPDM by the less soluble polyolefin plastic.
The Mooney viscosities of the blends are also listed in Table I.
Portions of the pelletized blends are screw injection molded into test specimens, on which the physical properties are determined by standard test methods with the results shown in Table I. From the tensile strength, ultimate elongation and elongation set at break results, the value termed the "performance factor" as defined above is also calculated for each blend, as indicated in Table I.
The extrudability results listed in Table I are determined on a Brabender extruder (Type EX3A, No. 191) under the following conditions: screw compression ratio 2/1, screw speed 20 rpm, temperature at rear of barrel 375° F., temperature at front of barrel 400° F., die diameter one-eighth inch, temperature of die 420° F. The material is considered extrudable if the extrudate feels smooth to the touch, otherwise it is not.
The injection molding results listed in Table I are obtained by forming test pieces in an Ankerwerke screw injection molding machine (Model 75, Serial No. 1207-P, capacity 2 oz.), using a rear barrel temperature of 375° F., a front barrel temperature of 400° F., a nozzle temperature of 420° F. and a mold temperature of 100° F. The injection time is 3 seconds, holding time 10 seconds, and total cycle time is 30 seconds. The screw back pressure is 200 psi, screw speed "High," injection speed setting of 60 and maximum injection pressure is 1000 psi. The dimensions of the mold cavity are 2×6×0.075 inches. The injection molded samples are evaluated by observing whether the formed specimen is homogenous, e.g., without cracks, and of uniform strength indicating that the compositions have the flow viscosity characteristics adequate for filling the mold under the operating conditions.
Press moldability of the blends is evaluated in a Pasadena hydraulic press (Model No. PW220C) set for 400° F. The sample is preheated for about 3 minutes, pressed for 5 minutes at a pressure of about 500 psi and cooled to 100° F., before removal from the mold (dimensions 6×6×0.075 inches). The blend is considered press moldable if it is uniform in appearance and the cavity is completely filled, while excess material easily flashes out of the cavity.
Table I, Parts A and B, shows that in the course of the pre-curing step involving hot mastication with various amounts of peroxide curative the gel content of the EPDM rubber increases, from an original value of 3 percent to values within the range from 58 to 87 percent, while the % swell of the rubber decreases dramatically; also the Mooney viscosity increases. These changes are indicative of partial cure or cross-linking of the EPDM rubber.
Comparison of blends of the EPDM rubber, with and without semi-cure, with polyolefin plastic at the same ratio, vis., comparison of Run 1 (80:20 ratio, no pre-cure) with Run 6 (80-20 ratio, with semi-cure) shows that the blend based on semi-cured EPDM (Run 6) not only has higher actual gel, lower swelling index and higher Mooney viscosity, but, more significantly, has greatly reduced elongation set at break, and a "performance factor" increase of more than 300 percent, while retaining good processability as evidenced by the fact that it is extrudable and moldable. Thus, performance comparable to a vulcanized rubber is provided while retaining the processability of a thermoplastic material. It will be understood that no vulcanization or cure of the material takes place during the molding of the test specimens (the action of the peroxide curative having been essentially exhausted in the pre-curing step and any residual free radicals having been scavenged by the antioxidant) and the molded or extruded specimens remain thermoplastic and repeatedly reprocessable.
Similarly the other blends of the invention exemplified exhibit desirable decrease in elongation set at break, and increase in "performance factor," while retaining thermoplastic reprocessability.
In the foregoing example polypropylene resin having a melt flow index of 0.8 (D 1238 L, 190° C.), a specific gravity of 0.903 and 99 percent gel ("Profax 6723"), may be substituted. Dicumyloperoxide ("Dicup 40") may be substituted as the peroxide curative.
                                  TABLE I                                 
__________________________________________________________________________
PART A BLENDS OF EPDM WITH POLYOLEFIN PLASTICS                            
                    Run No.                                               
                    1  2  3  4  5  6  7  8  9  10 11 12                   
__________________________________________________________________________
EPDM I, pts         100                                                   
                       100                                                
                          100                                             
                             100                                          
                                100                                       
                                   100                                    
                                      100                                 
                                         100                              
                                            100                           
                                               100                        
                                                  100                     
                                                     100                  
Peroxide I, pts     -- -- -- .75                                          
                                .875                                      
                                   .823                                   
                                      .875                                
                                         .73                              
                                            .875                          
                                               .75                        
                                                  .875                    
                                                     1.0                  
Peroxide, moles × 10.sup.3 /100 g. EPDM                             
                    -- -- -- 2.9                                          
                                3.4                                       
                                   2.4                                    
                                      3.4                                 
                                         2.9                              
                                            3.4                           
                                               2.9                        
                                                  3.4                     
                                                     3.9                  
Cure temp. °F., max                                                
                    -- -- -- 360                                          
                                360                                       
                                   410                                    
                                      360                                 
                                         360                              
                                            360                           
                                               360                        
                                                  360                     
                                                     360                  
Cure time, minutes  -- -- -- 8  8  7  8  8  8  8  8  7                    
Gel, percent        3  3  3  68 73 60 65 58 65 58 65 82                   
Swell, percent      62 62 62 12 12 21 12 12 12 12 12 13                   
ML-4 at 250° F.                                                    
                    65 65 65 -- -- -- -- -- -- -- -- --                   
MS-4 at 250° F.                                                    
                    -- -- -- 47 60 -- 53 40 53 40 53 --                   
Masterbatch (EPDM), pts                                                   
                    80 70 60 90 90 80 80 70 70 60 60 60                   
Polypropylene, pts  20 30 40 10 10 20 20 30 30 40 40 40                   
H.D. polyethylene, pts                                                    
                    -- -- -- -- -- -- -- -- -- -- -- --                   
L.D. polyethylene pts                                                     
                    -- -- -- -- -- -- -- -- -- -- -- --                   
Blending Temp. °F., max                                            
                    360                                                   
                       360                                                
                          360                                             
                             360                                          
                                360                                       
                                   360                                    
                                      360                                 
                                         360                              
                                            360                           
                                               360                        
                                                  360                     
                                                     360                  
Blending time, minutes at temp                                            
                    7  7  7  1  1  1  1  1  1  1  1  1                    
Calc. gel, percent  23 33 41 71 75 67 71 69 73 72 76 87                   
Actual gel, percent 31 42 53 79 81 74 82 81 85 85 89 95                   
Swell, percent      13 9  6  8  8  5  7  6  5  5  5  4                    
ML-5 at 350° F.                                                    
                    18 17 19 56 61 37 41 35 35 30 34 45                   
Tensile strength, p.s.i.                                                  
                    830                                                   
                       1,125                                              
                          1,590                                           
                             450                                          
                                500                                       
                                   690                                    
                                      1,500                               
                                         1,600                            
                                            1,950                         
                                               2,000                      
                                                  2,390                   
                                                     1,510                
100% modulus, p.s.i.                                                      
                    830                                                   
                       1,050                                              
                          1,400                                           
                             -- 500                                       
                                   680                                    
                                      1,490                               
                                         1,500                            
                                            1,860                         
                                               1,900                      
                                                  -- 1,500                
Elongation, percent 120                                                   
                       220                                                
                          420                                             
                             80 130                                       
                                   100                                    
                                      100                                 
                                         190                              
                                            150                           
                                               210                        
                                                  80 110                  
Elongation set at break, percent                                          
                    40 80 200                                             
                             5  13 8  13 50 35 75 25 15                   
Hardness, shore A   75 87 90 58 60 77 80 88 90 94 94 94                   
Performance factor, p.s.i. × 10.sup.3                               
                    2.5                                                   
                       3.1                                                
                          3.3                                             
                             7.2                                          
                                5.0                                       
                                   8.6                                    
                                      11.5                                
                                         6.1                              
                                            8.4                           
                                               5.6                        
                                                  7.6                     
                                                     11.0                 
Extrudable          Yes                                                   
                       Yes                                                
                          Yes                                             
                             Yes                                          
                                Yes                                       
                                   Yes                                    
                                      Yes                                 
                                         Yes                              
                                            Yes                           
                                               Yes                        
                                                  Yes                     
                                                     No                   
Injection moldable  Yes                                                   
                       Yes                                                
                          Yes                                             
                             Yes                                          
                                Yes                                       
                                   Yes                                    
                                      Yes                                 
                                         Yes                              
                                            Yes                           
                                               Yes                        
                                                  Yes                     
                                                     Yes                  
Press moldable      Yes                                                   
                       Yes                                                
                          Yes                                             
                             Yes                                          
                                Yes                                       
                                   Yes                                    
                                      Yes                                 
                                         Yes                              
                                            Yes                           
                                               Yes                        
                                                  Yes                     
                                                     Yes                  
__________________________________________________________________________

                                  TABLE I                                 
__________________________________________________________________________
PART B BLENDS OF EPDM WITH POLYOLEFIN PLASTICS                            
                    Run No.                                               
                    13 14 15 16 17 18 19 20 21 22 23                      
__________________________________________________________________________
EPDM I, pts         100                                                   
                       100                                                
                          100                                             
                             100                                          
                                -- 100                                    
                                      100                                 
                                         100                              
                                            100                           
                                               -- --                      
Peroxide I, pts     1.125                                                 
                       1.25                                               
                          .75                                             
                             .75                                          
                                -- -- .75                                 
                                         -- .75                           
                                               -- --                      
Peroxide, moles × 10.sup.3 /100 g EPDM                              
                    4.3                                                   
                       5.3                                                
                          2.9                                             
                             2.9                                          
                                -- -- 2.9                                 
                                         -- 2.9                           
                                               -- --                      
Cure temp. °F. max                                                 
                    360                                                   
                       370                                                
                          360                                             
                             360                                          
                                -- -- 360                                 
                                         -- 360                           
                                               -- --                      
Cure time, minutes  7  7  7  7  -- -- 7  -- 7  -- --                      
Gel, percent        85 87 66 66 -- 3  64 3  60 -- --                      
Swell, percent      10 10 -- -- -- 62 15 62 16 -- --                      
ML-4 at 250° F.                                                    
                    -- -- -- -- -- 65 -- 65 -- -- --                      
MS-4 at 250° F.                                                    
                    -- -- 88 88 -- -- 48 -- 45 -- --                      
Masterbatch (EPDM), pts                                                   
                    60 60 35 10 -- 80 80 80 80 -- --                      
Polyproylene I, pts 40 40 65 90 100                                       
                                   -- -- -- -- -- --                      
H.D. polyethylene, pts                                                    
                    -- -- -- -- -- 20 20 -- -- 100                        
                                                  --                      
L.D. polyethylene, pts                                                    
                    -- -- -- -- -- -- -- 20 20 -- 100                     
Blending temp. °F., max                                            
                    360                                                   
                       360                                                
                          360                                             
                             360                                          
                                -- 360                                    
                                      360                                 
                                         360                              
                                            360                           
                                               -- --                      
Blending time, minutes at temp                                            
                    1  1  1  1  -- 7  1  7  1  -- --                      
Calc. gel, percent  89 90 84 92 -- 20 66 2.4                              
                                            48 -- --                      
Actual gel, percent 94 95 95 99 94 45 80 46 73 90 0                       
Swell, percent      3  3  2  2  -- 8  7  10 7  -- --                      
ML-5 at 350° F.                                                    
                    43 39 20 36 .sup.(1)                                  
                                   21 35 23 30 -- --                      
Tensile strength, p.s.i.                                                  
                    1,530                                                 
                       1,520                                              
                          3,080                                           
                             4,400                                        
                                4,320                                     
                                   780                                    
                                      900                                 
                                         240                              
                                            450                           
                                               4000                       
                                                  1800                    
100% modulus, p.s.i.                                                      
                    1,500                                                 
                       1,500                                              
                          2,840                                           
                             -- -- 600                                    
                                      840                                 
                                         230                              
                                            440                           
                                               -- --                      
Elongation, percent 40 50 160                                             
                             30 15 560                                    
                                      200                                 
                                         590                              
                                            130                           
                                               900                        
                                                  600                     
Elongation set at break, percent                                          
                    5  3  140                                             
                             -- 5  278                                    
                                      38 188                              
                                            13 -- --                      
Hardness, shore A   94 95 94 96 95 69 76 62 66 -- --                      
Performance factor, p.s.i. × 10.sup.3                               
                    12.2                                                  
                       2.5                                                
                          3.5                                             
                             -- -- 1.6                                    
                                      4.8                                 
                                         .75                              
                                            4.5                           
                                               -- --                      
Extrudable          No No Yes                                             
                             Yes                                          
                                Yes                                       
                                   Yes                                    
                                      Yes                                 
                                         Yes                              
                                            Yes                           
                                               Yes                        
                                                  Yes                     
Injection moldable  Yes                                                   
                       Yes                                                
                          Yes                                             
                             Yes                                          
                                Yes                                       
                                   Yes                                    
                                      Yes                                 
                                         Yes                              
                                            Yes                           
                                               Yes                        
                                                  Yes                     
Press moldable      Yes                                                   
                       Yes                                                
                          Yes                                             
                             Yes                                          
                                Yes                                       
                                   Yes                                    
                                      Yes                                 
                                         Yes                              
                                            Yes                           
                                               Yes                        
                                                  Yes                     
__________________________________________________________________________
 .sup.(1) Off scale
EXAMPLE 2
In runs 24-35, summarized in Table II, the EPDM rubber employed, identified as "EPDM II," contains 70 percent ethylene, 25 percent propylene and 5 percent 5-ethylidene-2-norbornene; the Mooney viscosity ML-4 at 250° F. is 60, MS-4 at 250° F. is 23, the gel content is 30 percent with 35 percent swell. In Run 24, which is included as a control, no pre-cure is imparted to the EPDM. In Runs 25, 26 and 27, the EPDM is semi-cured by hot mastication in the Banbury using as the curative the same peroxide as in Example 1. In Runs 28-31 the substance identified in Table II as "accelerator I" is tetramethyl thiuramidisulfide, actually a sulfur donor curative for the EPDM. In Runs 32-35, in addition to the sulfur donor there is included an accelerator ("accelerator II"), 4,4'-dithiodimorpholine; Runs 33-35 further include sulfur. Runs 28-35 also have 2 parts of zinc oxide (not shown in Table II) present during the pre-cure. The procedure is essentially the same as in Example 1, that is, the EPDM is hot masticated with the curatives in the Banbury mixer to the maximum temperature shown (actual stock temperatures being 25°-30° F. higher than the chart temperatures shown in Table II), and continued for the time indicated. Reduced cure times are employed in Runs 28-35 because the curatives used act more rapidly. As in Example 1, 1 part of tris(nonylphenyl) phosphite antioxidant is added at the end of the semi-cure step to scavenge any residual free radicals. The gel content increases, the swelling index goes down, and the Mooney viscosity increases, as a result of the partial curing step (compare Run 24 with the other runs).
80 Parts of the thus semi-cured EPDM (designated "masterbatch" in Table II) is blended with 20 parts of the same polypropylene resin as used in Example 1, by hot mixing in the Banbury. The blending time and temperature (chart temperatures; actual stock temperatures 25°-30° F. higher) are as shown in Table II. The blend is removed from the Banbury, formed into a sheet and chopped into pellets, and the material is evaluated as described in Example 1.
Of the results summarized in Table II, particularly significant is the decrease in elongation set at break, in the blends based on semi-cured EPDM as compared to Run 24 based on EPDM that has not been semi-cured. Also significant is the increase in the "performance factor." However, in Run 35, in which the cure of the EPDM became too far advanced in the pre-curing step, as evidenced by a high gel content of 90 percent in the treated EPDM, the blend is no longer processable.
                                  TABLE II                                
__________________________________________________________________________
BLENDS OF EPDM WITH POLYPROPYLENE                                         
                    Run Number                                            
                    24 25 26 27 28 29 30 31 32 33 34 35                   
__________________________________________________________________________
EPDM II, pts        100                                                   
                       100                                                
                          100                                             
                             100                                          
                                100                                       
                                   100                                    
                                      100                                 
                                         100                              
                                            100                           
                                               100                        
                                                  100                     
                                                     100                  
Peroxide, I pts     -- .5 .625                                            
                             .75                                          
                                -- -- -- -- -- -- -- --                   
Accelerator I, pts  -- -- -- -- .5 1.0                                    
                                      1.5                                 
                                         2.0                              
                                            .5 .25                        
                                                  .5 1.0                  
Accelerator II, pts -- -- -- -- -- -- -- -- .5 .25                        
                                                  .5 1.0                  
Sulfur, pts         -- -- -- -- -- -- -- -- -- .1 .2 .4                   
Cure temp. °F. max                                                 
                    -- 360                                                
                          360                                             
                             360                                          
                                360                                       
                                   360                                    
                                      360                                 
                                         360                              
                                            360                           
                                               360                        
                                                  360                     
                                                     360                  
Cure time, minutes  -- 7  7  7  4  4  4  4  4  4  4  4                    
Gel, percent        30 47 60 67 36 42 52 59 60 68 74 90                   
Swell, percent      35 14 -- 13 27 17 15 12 16 11 -- 6                    
MS-4 at 250° F.                                                    
                    23 56 67 91 43 61 74 82 78 91 .sup.(1)                
                                                     .sup.(1)             
Masterbatch(EDPM) pts                                                     
                    80 80 80 80 80 80 80 80 80 80 80 80                   
Polypropylene, pts  20 20 20 20 20 20 20 20 20 20 20 20                   
Blending temp. °F. ca                                              
                    340                                                   
                       340                                                
                          340                                             
                             340                                          
                                340                                       
                                   340                                    
                                      340                                 
                                         340                              
                                            340                           
                                               340                        
                                                  340                     
                                                     340                  
Blending time, minutes                                                    
                    7  1  1  1  1  1  1  1  1  1  1  1                    
Calc. gel, percent  43 57 67 73 48 53 61 66 67 73 78 91                   
Actual gel, percent 37 74 88 81 60 69 76 81 82 78 87 93                   
Swell, percent      13 7  4  4  10 7  5  6  5  6  6  4                    
ML-5 at 350° F.                                                    
                    17 42 74 44 21 26 32 39 38 38 .sup.(1)                
                                                     88                   
Tensile strength, p.s.i.                                                  
                    1,275                                                 
                       1,210                                              
                          1,350                                           
                             1,230                                        
                                1,350                                     
                                   1,230                                  
                                      1,340                               
                                         1,340                            
                                            1,280                         
                                               1,500                      
                                                  1,610                   
                                                     1,390                
100 percent modulus, p.s.i.                                               
                    1,040                                                 
                       1,200                                              
                          1,200                                           
                             -- 1,200                                     
                                   1,190                                  
                                      1,190                               
                                         1,250                            
                                            1,200                         
                                               1,380                      
                                                  1,600                   
                                                     1,200                
Elongation, percent 420                                                   
                       120                                                
                          100                                             
                             80 310                                       
                                   270                                    
                                      220                                 
                                         170                              
                                            220                           
                                               230                        
                                                  110                     
                                                     140                  
Elongation set at break, percent                                          
                    120                                                   
                       15 10 13 75 55 45 23 43 43 15 23                   
Hardness, shore A   83 85 89 86 84 86 84 86 86 85 85 86                   
Performance factor, p.s.i. × 10.sup.3                               
                    4.5                                                   
                       9.7                                                
                          13.5                                            
                             12.3                                         
                                5.6                                       
                                   6.0                                    
                                      6.6                                 
                                         9.9                              
                                            6.5                           
                                               8.0                        
                                                  11.8                    
                                                     8.5                  
Extrudable          Yes                                                   
                       Yes                                                
                          No No Yes                                       
                                   Yes                                    
                                      Yes                                 
                                         Yes                              
                                            No Yes                        
                                                  No No                   
Injection moldable  Yes                                                   
                       Yes                                                
                          Yes                                             
                             Yes                                          
                                Yes                                       
                                   Yes                                    
                                      Yes                                 
                                         Yes                              
                                            Yes                           
                                               Yes                        
                                                  No No                   
Press moldable      Yes                                                   
                       Yes                                                
                          Yes                                             
                             Yes                                          
                                Yes                                       
                                   Yes                                    
                                      Yes                                 
                                         Yes                              
                                            No Yes                        
                                                  Yes                     
                                                     No                   
__________________________________________________________________________
 .sup.(1) Off scale.
EXAMPLE 3
Table III summarizes Runs 36-40. The EPDM employed is the same as in Example 1. Run 36 is a control, involving no semi-cure of the EPDM. In Runs 37-40, partial cure is imparted to the EPDM by hot mastication in the Banbury mixer with a peroxide curative, benzoyl peroxide ("Luperco BPO"), identified as "peroxide II" in Table III, which has a half life of 0.4 hour at 212° F. The procedure is as described in Example 1. The "performance factor" is increased in Runs 37-40, compared to the control, Run 36, while retaining processability and reprocessability.
              TABLE III                                                   
______________________________________                                    
Blends of EPDM with Polypropylene                                         
______________________________________                                    
Run No.           36     37     38   39   40                              
EPDM I, pts.      100    100    100  100  100                             
Peroxide II, pts.        1.0    1.25 1.67 1.86                            
Peroxide, moles × 10.sup.2 /100g                                    
EPDM                     4.4    5.3  7.0  7.8                             
Cure Temp., °F.   240    240  240  240                             
Cure Time, minutes       4      4    4    4                               
Gel, %            3      45     50   62   61                              
Swell, %          65                                                      
MS-4 at 250°F.                                                     
                  23     64     67   65   67                              
Masterbatch, pts. 80     80     80   80   80                              
Polypropylene, pts.                                                       
                  20     20     20   20   20                              
Blending Temp., °F. max.                                           
                  340    370    370  370  370                             
Blending Time, minutes                                                    
                  7      2      2    4    3                               
Calc. Gel, %      23     55     59   69   68                              
Actual Gel, %     31     62     69   67   79                              
Swell, %          13     9      8    8    8                               
ML-5 at 350° F.   18                                               
Tensile Strength, psi                                                     
                  830    810    910  980  1000                            
100% Modulus, psi 830    800    910  930  990                             
Elongation, %     120    140    170  160  140                             
Elongation Set at break, %                                                
                  40     33     40   38   23                              
Hardness, Shore A 75     79     78   77   80                              
Performance Factor, psi × 10.sup.3                                  
                  2.5    3.4    3.9  4.1  6.1                             
Extrudable        yes    yes    yes  yes  yes                             
Injection Moldable                                                        
                  yes    yes    yes  yes  yes                             
Press Moldable    yes    yes    yes  yes  yes                             
______________________________________
EXAMPLE 4
This example illustrates partial pre-cure of the EPDM rubber by heating under static conditions in an autoclave, rather than under dynamic conditions (hot mastication in a Banbury) as in previous examples. The materials employed are as previously identified. Run 43 (Table IV) is a control in which no semi-cure is undertaken. In Runs 44-48 the EPDM rubber is mixed on a mill at room temperature with the indicated amount of the peroxide curative and the batch is then placed in an autoclave and heated at 400° F. for the time indicated to effect the semi-cure statically. In some cases the thus partially cured EPDM is refined by passing it three times through a mill at 200°-350° F.; in other cases the refining step is omitted. The increase in gel content, decrease in percent swell and increase in Mooney viscosity (in Runs 44-48) are indicative of partial cross-linking of the EPDM as a result of the static treatment with curative.
After blending with the polypropylene resin [at which time 1% of tris(nonylphenyl) phosphite is also mixed in] as in previous examples, and determination of physical properties and processability of the blends marked decrease in elongation set at break with increase in "performance factor," while retaining thermoplastic reprocessability are found in Runs 44-48 of the invention as indicated in Table IV.
              TABLE IV                                                    
______________________________________                                    
BLENDS OF EPDM WITH POLYPROPYLENE                                         
             Run No.                                                      
             43   44     45     46   47   48                              
______________________________________                                    
EPDM I, pts.   100    100    100  100  100  100                           
Perozide I, pts.                                                          
               --     .125   .125 .375 .375 .75                           
Cure temp., °F.                                                    
               --     400    400  400  400  400                           
Cure time, minutes                                                        
               --     20     20   20   20   15                            
Refined        --     No     Yes  No   Yes  No                            
Gel, percent   3      89     2.6  61   60   76                            
Swell, percent 62     48     46   35   36   --                            
MS-4 at 250° F.                                                    
               37     --     --   --   --   53                            
Masterbatch, pts.                                                         
               80     80     80   80   80   80                            
Polypropylene, pts.                                                       
               20     20     20   20   20   20                            
Blending temp., °F., max.                                          
               360    360    360  360  360  360                           
Blending time, minutes                                                    
               7      1      1    1    1    1                             
Calc, gel, percent                                                        
               23     50     40   68   67   79                            
Actual gel, percent                                                       
               31     --     --   --   --   84                            
Swell, percent 13     --     --   --   --   --                            
ML-5 at 350° F.                                                    
               18     --     --   --   --   36                            
Tensile Strength, p.s.i.                                                  
               830    990    530  1,080                                   
                                       1,100                              
                                            820                           
100% modulus, p.s.i.                                                      
               830    --     --   --   --   --                            
Elongation, percent                                                       
               120    120    110  100  120  88                            
Elongation set at                                                         
break percent  40     28     20   15   18   9                             
Hardness, Shore A                                                         
               75     75     74   80   80   90                            
Performance factor,                                                       
p.s.i. × 10.sup.2                                                   
               2.5    4.2    5.1  7.2  7.3  7.6                           
Extrudable     Yes    Yes    Yes  Yes  Yes  No                            
Injection moldable                                                        
               Yes    Yes    Yes  Yes  Yes  Yes                           
Press moldable Yes    Yes    Yes  Yes  Yes  Yes                           
______________________________________
EXAMPLE 5
Table V illustrates the practice of the invention with a saturated EPM binary copolymer rubber [40% ethylene, 60 percent propylene, by weight; ML-4 at 250° F. is less than 20; gel content, nil ("Vistalon 404")]. The curative identified as "OBSA" in Table V, is p,p-oxybis(benzenesulfonyl-azide). No curative is used in Run 49 (a control). In runs 50-53 the curative, in the amounts shown, is mixed with the EPM on an unheated roll mill. The EPM-curative mix is placed in an autoclave and heated to 360° F., under a pressure of 150 psi steam for 20 minutes to effect the partial cure statically. The steam pressure prevents the mixture from blowing. The resulting semi-cured EPM is removed from the autoclave and blended with the polypropylene along with 1 percent of the antioxidant, in the Banbury at the blending temperature (chart temperature) shown for the time indicated. Table V shows that the semi-cure increases the gel content and Money viscosity, and decreases the swelling index of the EPM. In the blends, elongation set at break is greatly reduced, and "performance factor" is greatly increased.
              TABLE V                                                     
______________________________________                                    
Blends of EPM with Polypropylene                                          
______________________________________                                    
Run No.           49     50     51   52   53                              
EPM, pts          100    100    100  100  100                             
OBSA, pts.               0.5    1.0  1.5  2.0                             
Cure Temp. °F.    360    360  360  360                             
Cure Time, minutes       20     20   20   20                              
Gel, %            0      66     77   82   83                              
Swell, %          90+    23     14   11   11                              
MS-4 at 250° F.                                                    
                  20     50     62   75   79                              
Masterbatch, pts  80     80     80   80   80                              
Polypropylene, pts.                                                       
                  20     20     20   20   20                              
Blending Temp. °F.                                                 
                  360    360    360  360  360                             
Blending Time, minutes at temp.                                           
                  7      2      2    2    2                               
Calc. Gel%        19     72     81   85   85                              
Actual Gel, %     31     66     77   80   83                              
Swell, %          12     8      9    8    7                               
ML-5 at 350° F.                                                    
                  8      41     48   47   50                              
Tensile Strength, psi                                                     
                  650    960    1040 1180 1150                            
100% Modulus, psi 450                                                     
Elongation, %     440    80     70   40   60                              
Elongation Set at break, %                                                
                  220    8      10   5    10                              
Hardness, Shore A 72     80     85   85   76                              
Performance Factor, psi × 10.sup.3                                  
                  1.3    9.6    7.3  9.5  6.9                             
Extrudable        yes    no     no   no   no                              
Injection Modable yes    yes    yes  no   no                              
Press Moldable    yes    yes    yes  yes  yes                             
______________________________________

Claims (44)

Having thus described our invention what we claim and desire to protect by Letters Patent is:
1. A thermoplastic reprocessable blend of (A) a rubbery copolymer of ethylene and at least one other copolymerizable monoolefin of the formula CH2 ═CHR where R is an alkyl radical having from one to 12 carbon atoms, with or without at least one copolymerizable polyene, said copolymer being partially cross-linked, prior to blending to a gel content of at least 30 percent but less than 90 percent by weight measured by immersion in cyclohexane for 48 hours at 73° F., and (B) an uncross-linked resinous polyolefin, the weight ratio of (A) to (B) being from 10:90 to 90:10.Iadd., said partial cross-linking having been accomplished by the action of a curative, the action of the curative being substantially exhausted so that there is little or no tendency for further cure to take place subsequently.Iaddend..
2. A blend as in claim 1 in which the said mono-olefin is propylene.
3. A blend as in claim 1 in which (A) is a saturated ethylene-propylene binary copolymer.
4. A blend as in claim 1 in which (A) is an unsaturated terpolymer of ethylene, propylene, and a non-conjugated diene.
5. A blend as in claim 4 in which the diene is dicyclopentadiene.
6. A blend as in claim 4 in which the diene is 5-ethylidene-2-norbornene.
7. A blend as in claim 1 in which the said gel content of (A) is from 40 to 85 percent.
8. A blend as in claim 1 in which the said gel content of (A) is from 55 to 85 percent.
9. A blend as in claim 1 in which (B) is selected from the group consisting of polyethylene and polypropylene.
10. A blend as in claim 1 in which (B) is polyethylene.
11. A blend as in claim 10 in which the polyethylene has a density of 0.910 to 0.925 g/cc.
12. A blend as in claim 10 in which the polyethylene has a density of 0.926 to 0.940 g/cc.
13. A blend as in claim 10 in which the polyethylene has a density of 0.941 to 0.965 g/cc.
14. A blend as in claim 1 in which (B) is polypropylene.
15. A blend as in claim 14 in which the polypropylene is isotactic.
16. A blend as in claim 1 in which the weight ratio of (A) to (B) is from 50:50 to 90:10.
17. A blend as in claim 1 in which the weight ratio of (A) to (B) is from 60:40 to 80:20.
18. A blend as in claim 1 in which (A) is semi-cured with a peroxide curative.
19. A blend as in claim 18 in which (A) is saturated ethylene-propylene binary copolymer.
20. A blend as in claim 18 in which (A) is an unsaturated ethylene-propylene-non-conjugated diene terpolymer.
21. A blend as in claim 18 in which the peroxide curative is 2,5-bis(tert.-butylperoxy)-2,5-dimethylhexane.
22. A blend as in claim 18 in which the peroxide curative is benzoyl peroxide.
23. A blend as in claim 1 in which (A) is semi-cured with an azide curative.
24. A blend as in claim 23 in which the azide curative is p,p'-oxybis(benzenesulfonylazide).
25. A blend as in claim 1 in which (A) is unsaturated ethylene-propylene-non-conjugated diene terpolymer semi-cured with a sulfur curative.
26. A thermoplastic reprocessable blend of
A. a monoolefin copolymer rubber selected from the group consisting of saturated ethylene-propylene binary copolymer rubber and unsaturated ethylene-propylene-non-conjugated diene terpolymer rubber, partially cross-linked, prior to blending, to a gel content of from 40 to 85 percent, measured by immersion in cyclohexane for 48 hours at 73° F., the percent swell of the said partially cross-linked rubber being 10 to 70 percent less than the percent swell prior to cross-linking of the rubber, said partially cross-linked rubber being capable of forming a coherent band on a roll mill, and
B. an uncross-linked resinous polyolefin selected from the group consisting of polyethylene and polypropylene, the weight ratio of (A) to (B) being from 60:40 to 80:20, the said blend, when formed into a molded test specimen without further cross-linking, having a performance factor (defined as the value obtained by multiplying the tensile strength in psi by the ultimate elongation in percent and dividing by the elongation set in percent) being at least 20 percent in excess of the performance factor of an otherwise identical blend containing the same rubber without partial cross-linking, whereby the said blend containing the partially cross-linked rubber has the characteristics of a thermoplastic elastomer.Iadd., said partial cross-linking having been accomplished by the action of a curative, the action of the curative being substantially exhausted so that there is little or no tendency for further cure to take place subsequently.Iaddend..
27. A method of making a thermoplastic reprocessable blend comprising in combination the steps of
a. providing (A) a rubbery copolymer of ethylene and at least one other copolymerizable monoolefin of the formula CH2 ═CHR where R is an alkyl radical having from one to 12 carbon atoms, with or without at least one copolymerizable polyene,
b. semi-curing the said rubbery copolymer until it has a gel content, measured by immersion in cyclohexane for 48 hours at 73° F., at least 10 percent higher than the gel content of the said rubbery copolymer prior to said semi-cure, but less than 90%,
c. providing (B) an uncross-linked resinous polyolefin, and
d. uniformly blending (A) and (B) at a temperature in excess of the softening temperature of (B), the weight ratio of (A) to (B) being from 10:90 to 90:10.Iadd., said semi-curing being accomplished by the action of a curative, the action of the curative being substantially exhausted so that little or no further cure takes place subsequently.Iaddend.. .[.28. A method as in claim 27 in which the action of the curative in step (b) is
substantially exhausted..]. 29. A method as in claim 27 in which the said semi-curing step (b) is carried out by heating the said rubbery copolymer (A) at curing temperature in admixture with a curative for said rubbery copolymer until the said gel content is at least 20 percent higher than
the gel content of the starting rubbery copolymer. 30. A method as in claim 27 in which the said semi-curing step (b) is carried out by heating the said rubbery copolymer (A) at curing temperature in admixture with a curative for said rubbery copolymer until the said gel content is at least 30 percent higher than the gel content of the starting rubbery copolymer.
1. A method as in claim 30 in which the said gel content after the
semi-curing step (b) is within the range of from 40 to 85 percent. 32. A method as in claim 30 in which the said rubbery copolymer (A) after the semi-curing step (b) has percent swell at least 8% less than the percent
swell prior to the semi-cure. 33. A method as in claim 32 in which the
curative is a peroxide curative. 34. A method as in claim 33 in which the
peroxide curative is 2,5-bis(tert.-butylperoxy)-2,5-dimethylhexane. 35. A method as in claim 33 in which the peroxide curative is benzoyl peroxide.
6. A method as in claim 32 in which the curative is an azide curative.
A method as in claim 36 in which the azide curative is
p,p'-oxybis(benzenesulfonylazide). 38. A method as in claim 32 in which (A) is an unsaturated ethylene-propylene-non-conjugated diene terpolymer
rubber and the said curative is a sulfur curative. 39. A method as in claim 32 in which the semi-curing step (b) is carried out under dynamic conditions while masticating the mixture of rubbery copolymer and
curative. 40. A method as in claim 32 in which the semi-curing step (b) is
carried out under static conditions. 41. A method of making a thermoplastic reprocessable blend comprising in combination the steps of
a. providing (A) a monoolefin copolymer rubber selected from the group consisting of saturated ethylene propylene binary copolymer rubber and unsaturated ethylene-propylene-non-conjugated diene terpolymer rubber,
b. heating the said rubbery copolymer at curing temperature in admixture with a curative for said rubbery copolymer until the gel content of the copolymer, measured by immersion in cyclohexane at 73° F. is within the range of from 40 to 85 percent, the percent swell after said heating being 10 percent to 70 percent less than prior to said heating, the thus-treated rubbery copolymer being in a semi-cured thermoplastic state and capable of being formed into a coherent band on a roll mill,
c. providing (B) an uncross-linked resinous polyolefin, and
d. uniformly blending (A) and (B) by masticating at a temperature in excess of the softening temperature of (B), the weight ratio of (A) to (B) being from 60:40 to 80:20, the resulting blend being a thermoplastic elastomeric composition.Iadd., the action of the curative being substantially exhausted so that little or no further cure takes place
subsequently.Iaddend.. 42. A method as in claim 41 in which the action of the curative in step (b) is substantially exhausted and thereafter an
antioxidant is added to scavenge any residual free radicals. 43. A method as in claim 42 in which step (b) is carried out while masticating the
mixture of rubbery copolymer and curative in a heated internal mixer. 44. A method as in claim 42 in which step (b) is carried out statically in
a heated autoclave. 45. A method of making a thermoplastic elastomeric shaped article comprising carrying out the steps of claim 42, and thereafter shaping the blend into a desired shape without further cure, whereby the shaped blend can be reprocessed.
US05/941,601 1971-01-20 1978-09-11 Thermoplastic blend of partially cured monoolefin copolymer rubber and polyolefin plastic Expired - Lifetime USRE30405E (en)