US20160121014A1 - An elastic attachment adhesive and a disposable absorbent article made with the same - Google Patents
An elastic attachment adhesive and a disposable absorbent article made with the same Download PDFInfo
- Publication number
- US20160121014A1 US20160121014A1 US14/893,419 US201414893419A US2016121014A1 US 20160121014 A1 US20160121014 A1 US 20160121014A1 US 201414893419 A US201414893419 A US 201414893419A US 2016121014 A1 US2016121014 A1 US 2016121014A1
- Authority
- US
- United States
- Prior art keywords
- polymer
- adhesive composition
- article
- weight
- disposable absorbent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
Description
- This patent claims the benefit of or priorty to U.S. provisional application 61/828,453 and U.S. provisional application 61/828,468 both filed on May 29, 2013.
- Adhesives are often used to bond substrates together so as to maintain the two substrates in a fixed relation to each other. In the area of industrial adhesives, hot melt adhesives are commonly used to bond together a wide variety of articles including disposable absorbent articles comprising non-woven substrates e.g. adult incontinence products, disposable diapers, sanitary napkins, bed pads, puppy pads, medical dressings, etc.
- There can be multiple hot melt adhesives used in the manufacture of a disposable absorbent article. For example, in the manufacture of a disposable diaper, adhesives are used in construction (e.g. bonding the backsheet to the nonwoven and optionally the absorbent pad), elastic attachment (e.g. bonding the elastic material to the backsheet in for example the leg or waist area), and for the core stabilization (e.g. applying an adhesive to the absorbent core to increase the strength of the core).
- In one aspect, the invention features a disposable absorbent article selected from the group consisting of an adult incontinence product and a diaper including a first substrate and an elastic material; and an adhesive composition including a first polymer that is propylene-based and has a Mw of no greater than about 75,000 and a second polymer selected from a group consisting of propylene based polymers with a Mw of at least about 100,000 and styrene block copolymers with a styrene content of no greater than about 20%, where the propylene-based polymers have a polydispersity index of less than about 5 and where the adhesive composition is in contact with the elastic material and the first substrate.
- In one embodiment, the adhesive composition also is applied in at least one additional application selected from the group consisting of core stabilization and construction. In another embodiment, the adhesive composition also is applied as a core stabilization adhesive and construction adhesive.
- In one embodiment, the adhesive composition comprises no greater than about 20% by weight plasticizer; alternately the adhesive composition comprises no greater than about 18% by weight plasticizer.
- In one embodiment, the second polymer is present at from about 2% to about 15% by weight; alternately the said second polymer has an Mw of at least about 150,000.
- In one embodiment, the first polymer is a propylene homopolymer; alternately the first polymer is a propylene copolymer. In another embodiment, the first polymer is present at greater than about 25% by weight.
- In one embodiment, the second polymer is a hydrogenated styrene block copolymer. In another embodiment, styrene block copolymer additionally has a Melt Flow when tested according to ASTM 1238 (230° C., 5 kg) of no greater than about 5 g/10 min. Alternately, the second polymer is a propylene-based polymer. In another embodiment, the adhesive composition comprises at least about 35% total polymer.
- In another embodiment, the disposable absorbent article is selected from the group including an adult incontinence product and a diaper; alternately the disposable absorbent article is a diaper. In another embodiment, the adhesive composition bonds the elastic material to the first substrate resulting in creep resistant gathers.
- In a different aspect, the invention features a hot melt adhesive composition including a first polymer that is propylene-based and has a Mw of no greater than about 75,000 and a polydispersity index of less than about 5 and; a second polymer that is a hydrogenated styrene
- block copolymer with a styrene content of no greater than about 20%, and a Melt Flow when tested according to ASTM 1238 (230° C., 5 kg) of no greater than about 25 g/10 min and wherein the adhesive composition contains no greater than 18% by weight plasticizer.
- In one embodiment, the hot melt adhesive composition has a total polymer content is at least about 35% by weight. In another embodiment, the hot melt adhesive has a creep of no greater than about 6% when tested according to the Elastic Attachment Creep Test.
- In reference to the invention, these terms have the meanings set forth below: Propylene-based refers to a polymer that comprises at least about 50% by weight propylene.
- The inventors have discovered that certain adhesive compositions have superior shear properties, low odor and good thermal stability. These properties make the adhesive composition useful for elastic attachment and at least one additional adhesive application in the manufacture of a disposable absorbent article selected from the group consisting of an adult incontinence article and a diaper.
- The disposable absorbent article includes a nonwoven substrate and an adhesive composition. The adhesive composition is used for elastic attachment (e.g.bonding the elastic material to the backsheet in for example the leg or waist area) in the nonwoven article.
- The disposable absorbent article can be selected from the group consisting of adult incontinence products, disposable diapers, sanitary napkins, bed pads, puppy pads, medical dressings and surgical gowns.
- The adhesive can be used for at least one additional application in the disposable absorbent article. Possible additional applications include construction (e.g.bonding the backsheet to the nonwoven and optionally, the absorbent pad) and core stabilization (e.g. applying an adhesive to the absorbent core to increase the strength of the core).
- The adhesive composition is a hot melt adhesive. The adhesive can be a pressure sensitive adhesive. The adhesive composition can be light in color and can have good thermal stability. The adhesive can have an Initial Gardner Color after manufacturing of less than about 3, or even less than about 2. The adhesive has a viscosity change of no more than about 20%, no more than about 15%, or even no more than about 10% when tested according to the Thermal Stability Test Method. The light color and good thermal stability make it possible to hold the adhesive in a molten bulk tank until it is needed for use.
- The adhesive composition has a static peel when tested according to the Static Peel Test that is greatly improved versus prior art olefin based hot melt adhesives currently on the market (NW1137 available from HB Fuller Company is used as a control). The Static Peel can be 15% greater than the static peel of NW1137, 20% greater than the static peel of NW1137, or even 50% greater than the static peel of NW1137.
- The adhesive composition has a static peel when tested according to the Static Peel Test of no less than about 65 seconds, no less than about 75 seconds, no less than about 100 seconds, or even from about 75 seconds to about 225 seconds.
- The adhesive composition has a creep when tested according to the Elastic Attachment Creep Test of no greater than about 8%, or even no greater than about 6%, or even no greater than about 5%.
- The adhesive composition has low viscosity at application temperature. The viscosity can be no greater than about 10,000 cps at around 150° C., or even no greater than about 8,000 cps at around 150° C.
- The light color, low viscosity and good shear properties make it possible to use the adhesive for elastic attachment in the manufacture of a disposable absorbent article.
- The adhesive composition includes at least two different polymers. Useful propylene-based polymers for the first and/or second polymer include propylene homopolymers. Alternately, one or more of the two different propylene-based polymers can be copolymers of propylene with one or more other monomers (e.g. ethylene, butene, pentene, octene, etc.). The propylene-based polymers can be based entirely on olefins, i.e. do not contain any functional groups. The propylene-based polymers can comprise greater than 75% by weight propylene or even greater than 80% by weight propylene. The propylene-based polymers can have a polydispersity (Mw/Mn) of less than about 5, less than about 3, or even about 2. Useful propylene-based polymers can have a density of no greater than about 0.90, no greater than about 0.89, or even no greater than about 0.88. Useful propylene-based polymers include single-site (e.g.metallocene) catalyzed propylene-based polymers.
- The first polymer is a propylene-based polymer. The first polymer can have a molecular weight (Mw) of less than about 75,000, less than about 60,000, less than about 50,000 or even between about 30,000 and about 70,000. The first polymer can be present in the adhesive composition at no less than about 20% by weight, no less than about 25% by weight, no less than about 30% by weight, from about 15% to about 50% by weight, or even from about 25% to about 45% by weight. Useful commercially available first polymers include LICOCENE PP 1602 and LICOCENE PP2602 both available from Clariant International Ltd. (Muttenz, Switzerland) and L-MODU X400S and L-MODU X600S available from Idemitsu Kosan Co., Ltd. (Japan).
- The second polymer is selected from the group consisting of propylene-based polymers and styrenic block copolymers.
- The second polymer can be a propylene-based polymer. The propylene-based polymer can have a molecular weight (Mw) of at least about 100,000, at least about 125,000, at least about 150,000, between about 125,000 and about 400,000, or even between about 150,000 and 250,000. The second polymer can be present in the composition at no greater than about 20%, no greater than about 15% by weight, or even between about 2% by weight and about 15% by weight. Useful commercially available second polymers, that are propylene-based polymers include VISTAMAXX 6202 and VISTAMAXX 6102 available from ExxonMobil Chemical (Houston, Tex.) and VERSIFY 3300 available from Dow Chemical Company (Houston, Tex.).
- The second polymer can be a styrene block copolymer. The styrene block copolymer can be hydrogenated. Useful hydrogenated styrene block copolymers include, e.g., styrene-ethylene/butadiene-styrene block copolymer, styrene-ethylene/propylene-styrene block copolymer, styrene-ethylene/ethylene/propylene-styrene block copolymer, and combinations thereof.
- The styrenic block copolymer can have a styrene content of no greater than about 20% by weight, no greater than about 18% by weight, or even no greater than about 15% by weight. The styrene block copolymer can also have a Melt Flow when tested according to ASTM 1238 (230° C., 5 kg) of less than about 25 g/10 min, less than about 20 g/10 min, less than about 10g/10 min, or even less than about 5 g/10min.
- Suitable hydrogenated styrene block copolymers are commercially available under a variety of trade designations including, e.g., the SEPTON series of trade designations from Kuraray Co. Ltd (Houston, Tex.) including, e.g., SEPTON S2063 and S2007 hydrogenated styrene-isoprene-styrene block copolymers, the KRATON G series of trade designations from Kraton Performance Polymers Inc. (Houston, Tex.) including, e.g., KRATON G 1645M, KRATON G 1657 styrene-ethylene/butdiene-styrene block copolymers.
- The adhesive composition can include no greater than about 20% by weight, no greater than about 15% by weight, between about 2% and 20% by weight, or even between about 5% and 15% by weight of the styrenic block copolymer.
- The adhesive composition can include two second polymers i.e. one propylene-based polymer and one styrene block copolymer.
- The first polymer is lower in molecular weight than the second polymer.
- The total polymer content of the adhesive can be at least about 20% by weight, at least about 25% by weight, at least about 30% by weight, at least about 35% by weight, or even from about 35% by weight to about 50% by weight.
- The adhesive composition can include a plasticizer. The plasticizer can be saturated (e.g. mineral oil, paraffinic oil, etc.) in order to improve heat stability for bulk handling. Suitable plasticizers include, e.g., naphthenic oils, paraffinic oils (e.g., cycloparaffin oils), mineral oils, phthalate esters, adipate esters, olefin oligomers (e.g., oligomers of polypropylene, polybutene, and hydrogenated polyisoprene), polybutenes, polyisoprene, hydrogenated polyisoprene, polybutadiene, benzoate esters, animal oil, plant oils (e.g. castor oil, soybean oil), derivatives of oils, glycerol esters of fatty acids, polyesters, polyethers, lactic acid derivatives and combinations thereof.
- Useful commercially available plasticizers include CALSOL 550 oil from Calumet Specialty Products Partners, LP (Indianapolis, Ind.), KAYDOL OIL from Sonneborn (Tarrytown N.Y.) PARAPOL polybutene from Exxon Mobil Chemical Company (Houston, Tex.), OPPANOL polyisobutylene from BASF (Ludwigsjhafen, Germany), KRYSTOL 550 mineral oil from Petrochem Carless Limited (Surrey, England) and PURETOL 15 mineral oil from Petro Canada Lubricants Inc. (Mississauga, Ontario).
- The plasticizer is present in the adhesive composition at no greater than about 25% by weight, no greater than about 20% by weight, no greater than about 18% by weight, between about 5% and about 30% by weight, between about 5% and about 20% by weight, or even between about 10% by weight and about 18% by weight.
- The adhesive can include a tackifying agent. The tackifying agent can be at least partially hydrogenated in order to improved stability for bulk handling. The tackifying agent can be fluid or solid at room temperature. Suitable classes of tackifying agents include, e.g., aromatic, aliphatic and cycloaliphatic hydrocarbon resins, mixed aromatic and aliphatic modified hydrocarbon resins, aromatic modified aliphatic hydrocarbon resins, and hydrogenated versions thereof; terpenes, modified terpenes and hydrogenated versions thereof; natural rosins, modified rosins, rosin esters, and hydrogenated versions thereof; low molecular weight polylactic acid; and combinations thereof. Examples of useful natural and modified rosins include gum rosin, wood rosin, tall oil rosin, distilled rosin, hydrogenated rosin, dimerized rosin and polymerized rosin. Examples of useful rosin esters include e.g., glycerol esters of pale wood rosin, glycerol esters of hydrogenated rosin, glycerol esters of polymerized rosin, pentaerythritol esters of natural and modified rosins including pentaerythritol esters of pale wood rosin, pentaerythritol esters of hydrogenated rosin, pentaerythritol esters of tall oil rosin, and phenolic-modified pentaerythritol esters of rosin.
- Useful tackifying agents are commercially available under a variety of trade designations including, e.g., the ESCOREZ series of trade designations from Exxon Mobil Chemical Company (Houston, Tex.) including ESCOREZ 5400 and ESCOREZ 5600, the EASTOTAC series of trade designations from Eastman Chemical (Kingsport, Tenn.) including EASTOTAC H-100R and EASTOTAC H-100L and the WINGTACK series of trade designations from Cray Valley HSC (Exton, Pa.) including WINGTACK 86, WINGTACK EXTRA, and WINGTACK 95 and the PICCOTAC and KRISTALEX series of trade designations from Eastman Chemical Company (Kingsport, Tenn.) including, e.g., PICCOTAC 8095 and KRISTALEX 3100.
- The adhesive composition can include at least about 10% by weight, at least about 20% by weight, from about 5% by weight to about 60% by weight, from about 10% by weight to about 50% by weight, or even from about 10% by weight to about 40% by weight tackifying agent.
- The adhesive composition can include a wax. Useful classes of wax include, e.g., paraffin waxes, microcrystalline waxes, high density low molecular weight polyethylene waxes, by-product polyethylene waxes, polypropylene waxes, Fischer-Tropsch waxes, oxidized Fischer-Tropsch waxes, functionalized waxes such as acid, anhydride, and hydroxy modified waxes, animal waxes, vegetable waxes (e.g. soy wax) and combinations thereof Useful waxes are solid at room temperature and preferably have a Ring and Ball softening point of from 50° C. to 170° C. Useful waxes are commercially available from a variety of suppliers including EPOLENE N and C series of trade designations from Westlake Chemical Corporation (Houston, Tex.) including e.g. EPOLENE N-21 and the LICOCENE series of trade designations from Clariant International Ltd. (Muttenz, Switzerland) including e.g. TP LICOCENE PP 6102.
- The adhesive composition can include no greater than about 10% by weight, no greater than about 5% by weight, from about 1% by weight to about 10% by weight, from about 1% by weight to about 5% by weight wax, or even from about 1% by weight to about 3% by weight wax.
- The adhesive composition optionally includes additional components including, e.g., stabilizers, antioxidants, additional polymers (e.g. styrenic block copolymers, amorphous poly-alpha olefins, polyethylene copolymers), adhesion promoters, ultraviolet light stabilizers, corrosion inhibitors, colorants (e.g., pigments and dyes), fillers, surfactants, wetness indicators, superabsorbents and combinations thereof.
- Useful antioxidants include, e.g., pentaerythritol tetrakis[3,(3, 5-di-tert-butyl-4hydroxyphenyl)propionate], 2,2′-methylene bis(4-methyl-6-tert-butylphenol), phosphites including, e.g., tris-(p-nonylphenyl)-phosphite (TNPP) and bis(2,4-di-tert-butylphenyl)4, 4′-diphenylene-diphosphonite, di-stearyl-3,3′-thiodipropionate (DSTDP), and combinations thereof. Useful antioxidants are commercially available under a variety of trade designations including, e.g., the IRGANOX series of trade designations including, e.g., IRGANOX 1010, IRGANOX 565, and IRGANOX 1076 hindered phenolic antioxidants and IRGAFOS 168 phosphite antioxidant, all of which are available from BASF Corporation (Florham Park, N.J.), and ETHYL 702 4,4′-methylene bis(2,6-di-tert-butylphenol). When present, the adhesive composition preferably includes from about 0.1% by weight to about 2% by weight antioxidant.
- The adhesive composition can be applied to (i.e. such that it is in direct contact with) or incorporated in a variety of substrates including, e.g., films (e.g., polyolefin (e.g., polyethylene and polypropylene) films), release liners, porous substrates, cellulose substrates, sheets (e.g., paper, and fiber sheets), paper products, woven and nonwoven webs, fibers (e.g., synthetic polymer fibers and cellulose fibers) and tape backings.
- The adhesive composition is also useful in a variety of applications and constructions including, e.g., disposable absorbent articles including, e.g., disposable diapers, adult incontinence products, sanitary napkins, medical dressings (e.g., wound care products) bandages, surgical pads, pet training pads (e.g. puppy pads) and meat-packing products and components of absorbent articles including, e.g., an absorbent element, absorbent cores, impermeable layers (e.g., backsheets), tissue (e.g., wrapping tissue), acquisition layers and woven and nonwoven web layers (e.g., top sheets, absorbent tissue) and elastics.
- The adhesive composition is useful on substrates made from a variety of fibers including, e.g., natural cellulose fibers such as wood pulp, cotton, silk and wool; synthetic fibers such as nylon, rayon, polyesters, acrylics, polypropylenes, polyethylene, polyvinyl chloride, polyurethane, and glass; recycled fibers, and various combinations thereof.
- Various application techniques can be used to apply the composition to a substrate including, e.g., slot coating, spraying including, e.g., spiral spraying and random spraying, screen printing, foaming, engraved roller, extrusion and meltblown application techniques.
- The adhesive composition is thermally stable, low in viscosity and has good heat resistance in a shear mode. These properties make it useful for multiple applications in the construction of a disposable absorbent article.
- The adhesive is used for elastic attachment applications, which include bonding elastic material to either the leg and/or waist area. The elastic material can be bonded to polyethylene, polypropylene or nonwoven substrates to result in creep resistant gathers.
- The adhesive can also be used for construction applications. In a typical construction application in the manufacture of a disposable absorbent article, a body fluid impermeable backsheet is bonded to a nonwoven substrate. The adhesive may also be used to bond at least one additional layer or material selected from the group consisting of absorbents, tissues, elastomeric materials, superabsorbent polymers, and combinations thereof. The body fluid impermeable backsheet is typically a polyolefin film (e.g. polyethylene, polypropylene, ethylene vinyl acetate, ethylene copolymer, etc.).
- The adhesive can be used to contain and/or provide strength to the absorbent core of a disposable absorbent article (i.e. as a core stabilization adhesive). The absorbent core can include many different materials including natural cellulose fibers (e.g. wood pulp, fibers, cotton, fluff, etc.) and superabsorbent polymers (e.g.polyacrylates). In some disposable absorbent articles, the absorbent core is substantially cellulose free. In a cellulose free core, the absorbent core consists of adhesive and superabsorbent polymer.
- The invention will now be described by way of the following examples. All parts, ratios, percents and amounts stated in the Examples are by weight unless otherwise specified.
- Test procedures used in the examples and throughout the specification, unless stated otherwise, include the following.
- Viscosity is determined in accordance with ASTM D-3236 entitled, “Standard Test Method for Apparent viscosity of Adhesives and Coating Materials,” (Oct. 31, 1988), using a Brookfield Thermosel viscometer Model RVDV 2 and a number 27 spindle. The results are reported in centipoise (cps).
- A hot melt composition is held at 300° F. (149° C.) for periods of 24 hours, 48 hours, 72 hours, and 96 hours. Viscosity and/or Molten Gardner Color of the aliquots can then be tested. Thermal stability is recorded as the change in viscosity over 96 hours and is calculated as a percent change according to the following formula:
-
((final viscosity-initial viscosity)/initial viscosity)*100 - The adhesive is tested (in the molten state) to determine Gardner color by comparing the color of the sample against the Gardner Color Standards as set forth in ASTM D-1544. The comparison is made using a Gardner Delta Comparator equipped with an Illuminator available from Pacific Scientific (Bethesda, Md.).
- Adjust hot melt applicator and laminator to recommended settings for the desired adhesive. The goal is to make an application of a uniform adhesive spiral measuring a width of approximately 12.7 mm (0.5 inches). Adjustments can be made based on the type of adhesive or application. The adhesive was applied to the treated side of a polyethylene film (DH-284 PE White available from Clopay Plastic Products Company, Augusta, Ky.) at a coat weight of 6.0 gram/m2 and nipped to the nonwoven (UNIPRO 45 available from Midwest Filtration Company, Cincinnati, Ohio) substrate.
- Bonds are made with the test adhesive/s and NW1137 as a control.
- Once the pattern width and desired adhesive coat weight has been achieved run several feet of material then insert sheets of paper in to nip to make the sample starting points (about 10 paper sheets), take care to insert the paper 90° square to the lamination this will insure a straight bond line to start the peel. Leave each of the adhesive laminations on the roll until they are ready to be tested, in approximately 24 hrs.
- Unroll the samples and cut test coupons 100 mm long in the machine direction 50 mm of paper tag to start the peel and 50 mm of bonded substrate. Then cut the test coupons 40 mm wide in the cross-machine, with the middle spiral in the center. When cutting the test coupons be sure to cut the coupons in such a way as to maintain a straight and square line at the test start point. Prepare 3 samples. Roll and staple the tag end of the unbonded poly film then roll and staple the tag end of the unbonded nonwoven. This will allow a secure place to hold the test samples in place during the static peel.
- Place the test coupons and the 100 g test weights in a 37° C. oven for at least 30 min to equilibrate. To begin the test attached the poly film end of the test coupon to the top of the rack in the oven and then carefully attach the 100 g weight to the nonwoven end of the test sample when the weight is released start the timer, stop the timer when the poly and nonwoven are completely separated and the weight falls. Repeat the test alternating between the control adhesive and the test adhesive until at least 3 replicates of each adhesive have been tested.
- Report the average time to failure of the test sample/s and NW1137 in seconds, plus any additional descriptive and pertinent information such as substrate failure or any variations in the application or test method.
- The hot melt adhesive is applied in molten form to LYCRA 689 dtex strands (pre-stretched to 240%) using a Nordson SURE WRAP nozzle, an application temperature of 140° C. and a coat weight of 0.15 g/linear meter. The adhesive coated pre-stretched elastic was then laminated between a polypropylene based nonwoven (VS26-26 g/m2) and a polyethylene back sheet (Article No. 30163544 available from Hutamaki).
- The elastic contracts creating gathers when released from the roll. 14 cms was removed from roll, stretched 100%, and stapled to corrugated board. The corrugated board was aged for 2 hours at 40° C. Elastic creep is reported as a percent and is measured by estimating the portion of the bond in which the elastic pulls away (or creeps) from the substrates.
-
TABLE 1 Polymer Properties VISTA- L-MODU L-MODU LICOCENE MAXX VERSIFY KRATON X400S X600S PP1602 6202 2300 G-1645M Supplier Idemitsu Idemitsu Clariant Exxon Dow Kraton Kosan Kosan Co., Mobil Chemical Polymers Co., Ltd. LTd. Chem. Co. Company U.S. LLC Polymer Type PP Homo- PP Homo- PP/PE PP/PE PP/PE SEBS Polymer Polymer copolymer Copolymer copolymer Ethylene content 0 0 15 (wt %) Styrene content 12.5 (wt %) Mw 45,000 70,000 47,600 184,000 Mw/Mn 2 2 4.6 2.1 2-3 Mass Flow Rate 18 (230° C., 2.0 (230° C., 3.25(230° C., (g/10 min) 2.16 kg) 2.16 kg) 2.16 kg) Density .87 .87 .87 .861 .867 -
TABLE 2 Examples Example Example Example Example Example Comp. 1* Comp. 2* 1 2 3 4 5 KRATON G 10 1645M L-MODU S-400 32 35 23 17 35 VISTAMAXX 6202 8 5 10 11 ESCOREZ 5400 34.8 34.8 39.8 39.8 34.8 CALSOL 550 20 20 22 25 15 EPOLENE N-21 3 3 3 5 3 IRGANOX 1076 0.2 0.2 0.2 0.2 0.2 COEXTRUSION 2 2 2 2 2 COATING Molten Viscosity at 3150 4800 6825 4650 6400 4500 8075 150degC (cps) Initial Gardner 3 2 1 1 1 1 1 Color Thermal Stability −25% +15% +7.3% +14.0% +6.5% +4.4% +18.3 (% change in viscosity) Static Peel 201 72 89 124 67 39 108 (seconds) Static Peel (% +23.6% +72.2% −6.9% −45.8% +50.0% increase versus NW1137) - The adhesive compositions of Examples 1-4 were prepared by combining and mixing the components in the percentages set forth in Table 2 in a sigma blade mixer operating at 177 ° C.
- The adhesive composition of Example 5 was prepared in an appropriate sized batch by placing the correct ratios of all components except for the polymers in a can, in an oven at a temperature of 177° C. until the ingredients are molten. Once the composition is molten, the can is placed in a heating mantle (e.g. Glas-Col, Terre Haute, Ind.), which maintains the temperature of the composition at around 150° C., and the composition is mixed with an upright mixer (e.g. Stirrer Type RZRI mixer (Caframo, Wiarton, Ontario, Canada)) while the polmers are slowly added. Mixing is continued until the polymers have been completely added and a smooth and homogeneous molten composition is achieved.
- The coextrusion coating contains the following in the stated weight percentages:
- ESCOREZ 5415—Exxon Mobil Chemical Company (Houston, Tex.) 34.8%
- KRATON G1652—Kraton Performance Polymers Inc. (Houston, Tex.) 25%
- SHELL MICROWAX HMP—Shell Deutschland Oil GmbH 39.6%
- IRGANOX 1072 0.6%
-
- Comparative 1 is HL1358LO is an SIS (styrene-isoprene-styrene) based hot melt adhesive commercially available from HB Fuller Company
- Comparative 2 is NW1137 is an ethylene-octene based hot melt adhesive commercially available from HB Fuller Company
- Example 5 was tested according to the Elastic Attachment Creep Test. A value of 4-5% was obtained.
- Other embodiments are within the claims.
Claims (20)