US20080003364A1 - Metal Inks - Google Patents
Metal Inks Download PDFInfo
- Publication number
- US20080003364A1 US20080003364A1 US11/427,270 US42727006A US2008003364A1 US 20080003364 A1 US20080003364 A1 US 20080003364A1 US 42727006 A US42727006 A US 42727006A US 2008003364 A1 US2008003364 A1 US 2008003364A1
- Authority
- US
- United States
- Prior art keywords
- metal
- precursor
- metal ink
- reducing agent
- substrate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
Description
- The United States Government has rights in this invention under Contract No. DE-AC36-99GO10337 between the United States Department of Energy and the National Renewable Energy Laboratory, a Division of the Midwest Research Institute.
- The following embodiments and aspects thereof are described and illustrated in conjunction with systems, tools and methods that are meant to be exemplary and illustrative, not limiting in scope. In various embodiments, one or more of the above-described problems have been reduced or eliminated, while other embodiments are directed to other improvements.
- An exemplary method comprises the steps of selecting a metal-organic (MO) precursor which is non-reacting at room temperature the MO precursors are configured or arranged to have a metal ion that is reduced to a pure metallic state at a potential positive of a reduction potential of the reducing agent, which includes formate ions; electing a reducing agent which is non-reacting at room temperature; reacting the MO precursor and the reducing agent at an activating temperature in the range of about 150-250° C. wherein reacting the MO precursor and the reducing agent produces substantially pure metal deposits on a substrate; and dissolving the MO precursor and the reducing agent in an organic solvent to produce a metal ink that remains in a liquid phase at room temperature; the organic solvent is selected from a group of organic solvents that have a sufficiently high boiling point so as to remain in a liquid phase at room temperature and provide viscosity and wetting properties for inkjet printing. The exemplary method further comprises elevating the temperature of the metal ink; reacting the reducing agent with the MO precursor; and producing a substantially uncontaminated metal deposit on a substrate.
- Another exemplary method comprises the steps of providing a metal ink in a liquid phase at room temperature; and applying the metal ink to a substrate at an elevated temperature by at least one of the following processes: spraying, dipping, spinning, direct-write deposition, and/or inkjet printing, wherein the metal ink reacts in a single step at the elevated temperature to produce substantially pure metal deposits on the substrate.
- A further exemplary method comprises the steps of providing a fire-through metal ink in a liquid phase at room temperature; and applying the fire-through metal ink to a coated surface or substrate of a solar cell by at least one of the following processes: spraying, dipping, spinning, direct-write deposition, and/or inkjet printing, wherein the fire-through metal ink reacts with the coated surface of the solar cell to produce electrical contacts with a p-n layer beneath the coated surface of the solar cell.
- An exemplary metal ink may be produced in accordance with the methods described above wherein the metal ink forms metal deposits at elevated temperatures and wherein the metal deposits consist of copper (Cu), gold (Au), silver (Ag), lead (Pb), palladium (Pd), platinum (Pt), cobalt (Co), iron (Fe), Tin (Sn), and other metal alloys. Additionally self-reducing and fire-through metal inks may be produced according to the exemplary methods described above. The fire-through metal ink further comprises a soluble metal complex and soluble organo-metallic reagent in a solution containing a particulate metal or metal organic precursor at room temperature.
- In addition to the exemplary aspects and embodiments described above, further aspects and embodiments will become apparent by reference to the drawings and by study of the following descriptions.
- Exemplary embodiments are illustrated in referenced figures of the drawings. It is intended that the embodiments and figures disclosed herein are to be considered illustrative rather than limiting.
-
FIG. 1 is a block diagram illustrating an exemplary system which may be implemented for inkjet printing of metal inks on various substrates. -
FIG. 2 is a conceptual view of an exemplary metal ink. -
FIGS. 3 a and 3 b illustrate an exemplary application of fire-through metal inks in the production of solar cells. -
FIG. 4 is a plot showing X-ray diffraction (XRD) analysis of exemplary nickel deposits. -
FIG. 5 are plots showing X-ray diffraction (XRD) analysis of exemplary silver, copper, and nickel deposits. -
FIG. 6 is a digital photograph showing exemplary copper lines that were inkjet printed on a printed circuit board in a nitrogen environment. -
FIG. 7 is a digital photograph showing an exemplary silver grid that was inkjet printed on a silicon solar cell in air. -
FIG. 8 is a three-dimensional illustration of a pattern etched in an anti-reflection coating for a silicon solar cell using an exemplary fire-through metal ink. - Deposition techniques, such as, e.g., vacuum deposition, screen printing and electroplating, are used for depositing a variety of inorganic and organic electronic materials on a substrate. As disclosed herein, inkjet printing is a viable, low-cost alternative to these deposition approaches. Inkjet printing is capable of producing high-resolution deposits on a substrate without the need for masking or templates. Inkjet printing is also a “non-contact” deposition technique (i.e., there is no contact between the print head and the substrate), making it well suited for producing metal deposits on thin and/or fragile polycrystalline substrates which could otherwise break using “contact” deposition techniques. In addition, inkjet printing may be used to produce three-dimensional (3-D) metal deposits on substrates.
- Briefly, metal inks disclosed herein are well suited for inkjet printing on any of a wide variety of substrates. For example, the printed inks adhere well to glass, silicon (Si), printed circuit boards (PCB), and many other substrates. The metal inks undergo a reducing reaction wherein pure, highly conductive metal deposits on the substrates at relatively low temperatures. Inkjet printing the metal inks enables the controlled deposition of metal lines and grids, in addition to multi-layer and multi-component metal features on the substrates.
- The metal inks may also be readily tailored for a variety of different uses, e.g., by addition of adhesion promoters, doping compounds, and/or other additives that further enhance the mechanical and/or electronic properties of the resulting metal deposit. For example, the metal inks may include etching agents for use in the production of high efficiency solar cells.
- Exemplary metal inks, and systems and methods for production and use of the metal inks, may be better understood with reference to the figures and following discussion.
-
FIG. 1 is a block diagram illustrating anexemplary system 10 which may be implemented for inkjet printing of metal inks on various substrates. Theexemplary system 10 may include anink jet 12 and atranslation stage 14 for positioning a substrate 16 (e.g., in the X or Y directions) adjacent theink jet 12. Aheating element 18 may also be provided, e.g., on thetranslation stage 14 directly adjacent thesubstrate 16. One or more optional gas supplies (illustrated inFIG. 1 bygas cylinder 20 and attached supply lines) may also be provided for controlling atmospheric conditions for printing the metal inks on thesubstrate 16. For example, the gas supplies may be used to provide an inert (e.g., nitrogen or argon) atmosphere during the inkjet printing process. -
Exemplary system 10 may also include acontroller 22.Controller 22 may be implemented to control various process parameters, such as, e.g., operation of thetranslation stage 14 to position thesubstrate 16 adjacent theink jet 12, application rate of the metal inks by theink jet 12 onto thesubstrate 16, increasing/decreasing temperature of theheating element 18, and/or application of one or more gasses from the gas supplies. - In an exemplary embodiment, the
controller 22 may be implemented as a desktop or laptop personal computer (PC) executing control software developed using LabVIEW. LabVIEW is a graphical programming language available from National Instruments (NI) for data acquisition and instrumentation control. Such control software may be readily developed by one having ordinary skill in the art after becoming familiar with the teachings herein. Therefore, further discussion is not needed to fully enable thecontroller 22. It is noted, however, that anysuitable controller 22 may be implemented and is not limited to a PC executing software developed with LabVIEW. - In an exemplary embodiment, the
ink jet 12 may be implemented as a piezoelectric print head (commercially available from MicroFab Technologies, Inc., Plano, Tex., 75074). The print head may have a 30-50 μm orifice and may be operated using a piezoelectric actuator for ejecting the ink, e.g., at a drop generation rate of up to about 2000 Hertz (Hz). - Inkjet printing of metal inks enables direct production of patterned deposits on the
substrate 16 using a non-vacuum process that produces results comparable to those obtained using traditional vacuum-based techniques. In addition, inkjet printing is a non-contact process which enables production of patterned deposits on thin and/orfragile substrates 16 that could not otherwise be accomplished using traditional contact-based techniques. It is noted, however, that other techniques for applying the metal inks to the substrate are also contemplated. Other direct application techniques may include, but are not limited to spraying, dipping, and/or spinning techniques. -
FIG. 2 is a conceptual view of an exemplary metal ink. Exemplary metal inks may comprise one or more metal-organic (MO) precursors (illustrated by molecular structure 26) and a reducing agent (illustrated by the formate ion 28) dissolved in water orother solvent 24. The metal ion (M) may be a chelated metal with a set of ligands that readily decompose to impart solubility to solution. Such an embodiment is well-suited for processing by inkjet printing or other direct application techniques. - The
solvent 24 may be selected based on a number of design considerations. For example, the polarity of thesolvent 24 may be selected based on the solubility of theMO precursor 26. The viscosity of thesolvent 24 may be selected based on the stability of the metal ink. Other factors may include, but are not limited to desired boiling point, evaporation rate, viscosity, and surface tension. For example, thesolvent 24 may have a high boiling point so that it does not change to a gas phase during the inkjet printing process. The solvent 24 may also be selected such that it provides the desired viscosity and wetting properties suitable for inkjet printing. Exemplary solvents include, but are not limited to, polyethers (di-glymes, triglymes, tetraglymes), ethylene glycol mono- and bis alkyl ethers, ethylene glycol, alcohols, aldehydes, water, surfactants, and/or combinations thereof. - A wide variety of
MO precursors 26 may be used for producing the metal inks. In an exemplary embodiment, the MO precursor includes a metal ion (M) that is reduced to its pure metallic state at a potential positive of the reduction potential of the reducing agent (e.g., −0.20 V for formate). Accordingly, metal inks may be produced for copper (Cu), gold (Au), silver (Ag), lead (Pb), palladium (Pd), platinum (Pt), cobalt (Co), iron (Fe), tin (Sn), and metal alloys. - The reducing agent (e.g., formate ion 28) provides a counter-ion for reaction with the
MO precursor 26. At room temperature, the reducing agent does not react with theMO precursor 26. Accordingly, theMO precursor 26 may remain soluble, e.g., as ametal ink solution 24 that is suitable for inkjet printing. During the inkjet printing process, however, the temperature of themetal ink solution 24 is elevated to an activating temperature (e.g., in the range of about 150-250° C.). This activating temperature causes the reducing agent to react with theMO precursor 26 and form pure metal deposits on the substrate. - In an exemplary embodiment, formate (HCO2 −) 28 may be used as the reducing agent. During the inkjet printing process, the temperature of the metal ink is elevated, causing the formate ions to react with the
MO precursor 26. This reaction produces an uncontaminated metal deposit on the substrate, along with a carbon dioxide (CO2) byproduct. It is noted, however, that formate is merely an example of a reducing agent that may be used. Other reducing agents may also be used, such as, e.g., halide or nitrate salts, alcohols, aldehydes, acetals, ethylene glycol, ethylene glycol diformate, benzaldehyde, acetealdehyde, etc. - In alternative embodiments, reducing conditions may be applied in a second step following application of the metal ink. For example, the
MO precursor 26 may be deposited on the substrate at temperatures below about 100° C., and then in a second step, annealed with a forming gas or vapors of organic reducing agents (e.g., ethylene, glycol, formaldehyde, acetaldehyde, hydrazine, etc.) to reduce the MO precursor to a pure metal deposit on the substrate. - Before continuing, it should be noted that the metal ink may also comprise other components, e.g., to enhance the inkjet printing process in air or an inert atmosphere at relatively low temperatures. The specific composition of the metal ink may depend at least to some extent on various design considerations. Exemplary design considerations include, but are not limited to, the MO precursor, the substrate that the metal ink is being applied to, and the application that the printed substrate will be used for.
- For purposes of illustration, the metal ink may include components, such as, e.g., dispersants, binders, and/or surfactants, for enhancing deposition, resolution, and/or adhesion of the metal inks to the substrate. For example, the surface properties of the ink may be adjusted for higher printing resolution by adding surfactants such as, Triton X-100, alkyl sulfonate, alkyl phosphate and phosphonate, alkyl amine and ammonium, etc.
- In addition, one or more process parameters may be adjusted for the particular metal ink being used to optimize the inkjet printing process and/or properties of the printed features. For example, the substrate temperature, gas flow rate, and/or application rate of the metal inks may be adjusted to optimize deposition rate of the metal ink, purity/phase of the deposited metal, and/or adhesion to the substrate. Or for example, the substrate temperature, gas flow rate, and/or application rate of the metal inks may be adjusted to optimize resolution, quality, thickness, conductivity and other electrical properties of the printed features.
- The metal inks may be used for coating a substrate with metal (e.g., by spraying, dipping, and/or spinning techniques) and/or for producing metal features on a substrate (e.g., as lines, grids, or patterns) by inkjet printing or other direct-write deposition techniques. In addition, the metal inks may be used in a wide variety of different applications. It is readily appreciated that applications of this technology may include, but are not limited to, printed circuit boards (PCBs), touch-screen display devices, organic light emitting diodes (OLEDs), organic solar cells, cell phone displays, photo-voltaic devices (e.g., solar cells), catalysts, decorative coatings, structural materials, optical devices, flexible electronics, and other electronic and micro-electronic devices, to name only a few examples.
- In an exemplary embodiment, the metal inks may be inkjet printed on a substrate in air or inert environment (e.g., nitrogen or argon) by heating the substrate to about 180° C. (100-200° C.), and then applying the metal ink using a drop generation rate of about 50 Hz (25-100 Hz). This embodiment results in a deposition rate of about 1 μm per pass. Thicker deposits may be obtained by inkjet printing multiple layers.
- Inkjet printing multiple layers of metal inks also enables deposition of a contact formation layer, followed by a separate metal forming layer. Accordingly, the contact formation process can be better controlled, and also results in conductor lines having higher conductivity.
-
FIGS. 3 a and 3 b illustrate an exemplary application of metal inks (i.e., so called “fire-through” metal inks) in the production ofsolar cells 30. In traditional silicon solar cell fabrication, a paste containing silver and glass frits is applied to a silicon-nitride anti-reflection (AR) coating over a silicon p-n junction. This paste helps the silver metal adhere to the AR coating, and enables the silver metal to “burn through” the AR coating and establish electrical contact with the silicon p-n junction. During this process, however, molten glass frits may flow between the silver and the silicon p-n junction, increasing resistance of the contacts and decreasing performance of the solar cells. - The metal inks disclosed herein may be implemented as fire-through metal inks (in place of the glass frits paste) for fabricating solar cells. Use of fire-through metal inks overcome the disadvantages of pastes containing glass frits, while at the same time offering other advantages (e.g., smaller, high resolution contacts resulting in a smaller shadow area). By eliminating glass frits, the fire-through metal inks also eliminate the need for other constituents needed in the pastes for controlling physical properties of the glass frits (e.g., softening agents). Removing these and other constituents of the pastes also helps to improve conductivity and reduce contact resistance in the finished
solar cell 30. - In an exemplary embodiment, the fire-through metal inks may comprise soluble chemical precursors (metal complexes and organo-metallic reagents) to various metal oxides. These precursors are provided in a solution containing a particulate metal or metal organic precursor at room temperature. The fire-through metal inks may be applied to the anti-reflection (AR) coating 34 of the solar cell (e.g., by inkjet printing or other deposition techniques). For purposes of illustration, fire-through metal inks are shown by the
deposits 32 inFIG. 3 a after application on theAR coating 34 by inkjet printing. - The fire-through metal inks may be used at relatively low process temperatures. For example, process temperatures may be in the range of about 200-500° C., well below temperatures considered to be detrimental to solar cells. In addition, the fire-through metal inks may be applied by inkjet printing, spin-coating, or other highly-controlled deposition processes, thereby enabling the production of patterns having uniform and controlled thickness, patterns, and other features.
- During and/or following application, the printed ink reacts with the
AR coating 34. During this reaction, the oxide precursor and metal precursor decompose (or “burn through”) theAR coating 34 and establish electrical contact with thep-n junction 36. For example, the metal deposits 38 are shown following “burn through” in contact with thep-n layer 36 inFIG. 3 b. It is noted that the precursor reacts directly at the interface between the metal deposits 38 and the p-n junction, thereby controlling properties of the interface (e.g., size, shape) without adversely affecting conductivity of the metal deposits 38. - In an exemplary embodiment, the metal inks may comprise lead acetate in ethylene glycol. When deposited on the AR coating 34 (e.g., by inkjet printing), the lead acetate is reduced to PbO, forming continuous layers and patterns of controlled thickness, as illustrated in
FIG. 3 a. The PbO completely etches the AR coating at temperatures as low as about 500° C. after only 10 minutes, as illustrated inFIG. 3 b. Increasing the temperature increases the etching rates. For example, increasing the temperature to about 750° C. for 10 min produced 1 μm deep etch pits, which is comparable to rates achieved using commercial glass frits at similar temperatures. In other exemplary embodiments, tin or zinc may be used in place of lead. - It is noted that the fire-through metal inks are not limited to any particular composition or formulation. For example, both mixed and single-oxide liquid chemical precursors may be used to facilitate the “burn-through” process on solar cell substrates having an AR coating. Mixed component solutions may include, but are not limited to, lead (lead acetate, lead formate), boron (such as boric acid) and silicon (silane). Still other chemical precursors may be used. Likewise, other functional components, such as, e.g., reducing agents, binders, and solvents may also be added to the fire-through metal inks to control chemical and/or physical properties of the fire-through metal inks and/or product.
- The following examples are provided to illustrate production and use of various metal inks that may be inkjet printed to produce metallic features, such as, e.g., layers and patterns on a substrate. The inkjet printing system was operated at 10-60 V 50-1000 Hz, and using an x-y translation speed of 1-30 mm/sec.
- In one example, nickel inks were produced by adding 0.5 gram (g) nickel(II) formate dihydrate [Ni(HCO2)2.2H2O] to 0.2 miliLiters (mL) ethylene diamine and 2.0 mL ethylene glycol. In this example, the ethylene diamine complexed Ni(II) to make the metal soluble, and the formate served as the reducing agent.
- The nickel inks were spray printed on glass substrates in an air environment at temperatures of about 250° C. to produce metallic nickel deposits on the glass. The nickel deposits had electrical properties comparable to bulk nickel. Specifically, a 4 micron layer of Ni metal deposited by spray deposition exhibited a resistivity of about 100 μΩ cm (compared to bulk Ni which has a resistivity of about 7 μΩ cm). X-ray diffraction (XRD) analysis (
plot 40 shown inFIG. 4 ) of the nickel deposits confirmed that the deposit was a pure nickel metal, and other phases of nickel (e.g., NiO) were not present. - In another example, silver (Ag) inks were produced by adding 1.0 g silver trifluoroacetate [Ag(CF3CO2)] to 2.0 mL of ethylene glycol and 1.0 mL Triton X-100. Silver inks were also produced by adding 2.0 g silver trifluoroacetate to 1.5 mL H2O and 0.2 mL ethylene glycol. In this example, the ethylene glycol and Triton X-100 served as the reducing agents and also helped lower the processing temperature for silver formation to 180° C. The Triton X-100 also served as a surfactant for better resolution printing.
- In yet another example, copper (Cu) inks were produced by adding 0.2 g copper(II) formate tetrahydrate [Cu(HCO2)2.4H2O] to 0.5 mL ethanolamine and 2.0 mL ethylene glycol. In this example, the ethanolamine increased the solubility of the copper(II) formate tetrahydrate. The formate served as the reducing agent.
- The Ag, Cu and Ni inks were printed on substrates heated to about 200-250° C. in air. Although better results were obtained by inkjet printing metal inks containing Cu in an inert atmosphere (N2 or Ar), copper deposition was also possible in air when followed by rapid thermal processing. In all cases, results of X-ray diffraction analysis (
plot 50 shown inFIG. 5 ) showed that the metal deposits were pure metal, without detectable traces of carbon or oxides. - Thick (up to 15 μm), highly conducting lines of Ag and Cu were printed on a variety of substrates demonstrating good adhesion to glass, silicon, and printed circuit boards. For purposes of illustration,
FIG. 6 is aphotograph 60 showing 5 μm thick and 300 μm wide copper “lines” 62 that were inkjet printed on a printedcircuit board 64 in a nitrogen environment at about 200° C.FIG. 7 is a photograph 70 showing a 10 μm thick and 250 μm wide silver “grid” 72 that was inkjet printed on a siliconsolar cell 74 in air at about 200° C. - The metal deposits exhibited conductivities comparable to those of the bulk metals. For example, the silver deposits exhibited conductivities of about 2 μΩ·cm, the copper deposits exhibited conductivities of about 10 μΩ·cm, and the nickel deposits exhibited conductivities of about 100 μΩ·cm. It is noted that the conductivity for the silver deposits is essentially the same as bulk silver metal, and although the resistivity for the copper and nickel deposits is approximately one order of magnitude higher than the bulk metals, these results are comparable to conductivities achieved for copper and nickel deposits using conventional screen printing techniques.
- The following examples are provided to illustrate the production and use of so-called fire-through metal inks that may be inkjet or spray printed on a SiN anti-reflection (AR) coating in the fabrication of solar cells. In this example, the fire-through metal inks were produced by adding 1.0 g lead acetate hydrate [Pb(CH3CO2)2.H2O] to 3.0 mL ethylene glycol.
- The fire-through metal inks were inkjet printed on the AR coating to produce 15 μm thick, 300 μm wide contacts. Ohmic contacts were achieved at low temperatures (650-750° C.) with a very short annealing cycle (less than one minute). A 1 μm deep, 70 μm
wide etch pattern 80 obtained by inkjet printing and consequent thermal processing at 750° C. for 10 min of theAR coating 82 on a silicon p-n junction is shown inFIG. 8 . Complete burn-through of the AR coating was observed at temperatures as low as 500 C. Layered printing decreased the processing temperature for contact formation to as low as 650° C., and improved performance of the printed cell. - It is noted that the Examples discussed above are provided for purposes of illustration and are not intended to be limiting. Still other embodiments of processes for the production and use of metal inks will be readily appreciated by those having ordinary skill in the art after understanding the teachings herein.
- While a number of exemplary aspects and embodiments have been discussed above, those of skill in the art will recognize certain modifications, permutations, additions and sub combinations thereof. It is therefore intended that the following appended claims and claims hereafter introduced are interpreted to include all such modifications, permutations, additions and sub-combinations as are within their true spirit and scope.
Claims (20)