KR20230172308A - Patch for reducing and preventing acne with excellent skin adhesion - Google Patents
Patch for reducing and preventing acne with excellent skin adhesion Download PDFInfo
- Publication number
- KR20230172308A KR20230172308A KR1020220073016A KR20220073016A KR20230172308A KR 20230172308 A KR20230172308 A KR 20230172308A KR 1020220073016 A KR1020220073016 A KR 1020220073016A KR 20220073016 A KR20220073016 A KR 20220073016A KR 20230172308 A KR20230172308 A KR 20230172308A
- Authority
- KR
- South Korea
- Prior art keywords
- patch
- skin
- acne
- adhesion
- sheet
- Prior art date
Abstract
본 발명은 피부 부착성이 우수한 여드름 완화 및 예방용 패치에 관한 것으로서, MgaZnbXc (a, b 및 c는 각 성분의 중량%로서, a+b+c=100중량%이고, i) 90≤a≤100, 0≤b≤10, 0≤c≤10 또는 ii) 0≤a≤10, 90≤b≤100, 0≤c≤10임)으로 표시되는 두께 0.7mm 이하의 사용자 피부와 접촉하는 생체분해성 금속 박판과, 그 일 단면에 위치한 점착 시트를 포함함으로써 패치가 피부에 접촉된 채 유지되어 우수한 여드름 치료 효과를 제공할 수 있고, 여드름 상처 주변에 습윤한 환경을 조성해 깨끗하게 낫기 위한 최적의 환경을 제공할 수 있으며, 패치의 교체시기를 알 수 있고, 부수적으로 심미적인 효과까지 제공할 수 있는 여드름 완화 및 예방용 패치를 제시한다.The present invention relates to a patch for acne relief and prevention with excellent skin adhesion, Mg a Zn b ) 90≤a≤100, 0≤b≤10, 0≤c≤10 or ii) 0≤a≤10, 90≤b≤100, 0≤c≤10) of the user's skin with a thickness of 0.7mm or less. By including a biodegradable metal sheet in contact with the skin and an adhesive sheet located on one end of the patch, the patch can be maintained in contact with the skin, providing excellent acne treatment effects, and creating a moist environment around acne wounds for clean healing. We present a patch for acne relief and prevention that can provide an optimal environment, allow you to know when to replace the patch, and provide additional aesthetic effects.
Description
본 발명은 피부 부착성이 우수한 여드름 완화 및 예방용 패치에 관한 것으로, 더욱 상세하게는 마그네슘을 주성분으로 포함하는 생체분해성 금속의 여드름 완화 및 예방 용도 및 이를 이용한 피부 부착용 패치에 관한 발명이다.The present invention relates to a patch for alleviating and preventing acne with excellent skin adhesion, and more specifically, to the use of a biodegradable metal containing magnesium as a main ingredient for alleviating and preventing acne, and to a patch for attaching to the skin using the same.
여드름이란 털 피지선 샘 단위의 만성 염증질환으로, 면포(Comedone, 모낭 속에 고여 딱딱해진 피지), 구진(Papule, 1cm 미만 크기의 솟아 오른 피부 병변), 고름물집, 결절, 거짓낭 등 다양한 피부 변화가 나타나며, 이에 따른 후유증으로 오목한 흉터 또는 확대된 흉터를 남기기도 한다. 특히 피지선이 모여 있는 얼굴, 목, 가슴 등에 많이 발생하며 털을 만드는 모낭에 붙어있는 피지선에 염증이 생기는 질환을 말한다.Acne is a chronic inflammatory disease of the sebaceous gland unit, causing various skin changes such as comedones (hardened sebum accumulated in hair follicles), papules (raised skin lesions less than 1 cm in size), pus blisters, nodules, and pseudocysts. As a result, concave scars or enlarged scars may be left behind. It occurs particularly frequently in the face, neck, and chest, where sebaceous glands are concentrated, and refers to a disease in which the sebaceous glands attached to hair follicles that produce hair become inflamed.
여드름의 정확한 원인은 밝혀지지 않고 있으나 한 가지 원인보다는 여러 원인이 복합적으로 작용하며, 그 한 원인으로 사춘기 때 남성호르몬의 과잉으로 피지선의 분비가 왕성해지고 모낭의 상피가 이각화증(불완전하고 미숙한 각질화를 보이는 비정상적 각질화)을 일으켜서 모낭이 막혀 여드름의 기본 병변인 면포가 형성되는 것이 있다.The exact cause of acne is not known, but it is caused by a combination of factors rather than a single cause. One of the causes is excessive secretion of male hormones during puberty, which causes the sebaceous glands to secrete actively and the epithelium of the hair follicles develop dyskeratosis (incomplete and immature keratinization). It causes abnormal keratinization that appears, causing hair follicles to become clogged, leading to the formation of comedones, which are the basic lesions of acne.
이 중 박테리아에 의한 여드름의 발진은 모낭 내에 상주하는 균 중 특히 프로피오니박테리움 아크네(Propionibacterium acnes)가 그 원인균으로 알려져 있다. 이 여드름 원인균은 피지를 먹고 자라면서 트러블 발생의 주된 원인이 되는데, 정상인에서는 이 균이 피부에 존재하더라도 전혀 문제를 일으키지 않으나, 모낭이 막혀 피지가 모낭 안에 쌓이게 되면 피지를 먹고 빠르게 자라난다.Among these, it is known that the cause of acne rashes caused by bacteria is particularly Propionibacterium acnes , which resides in hair follicles. This acne-causing bacteria grows by eating sebum and becomes the main cause of trouble. In normal people, this bacteria does not cause any problems even if it exists on the skin, but when the hair follicles are clogged and sebum accumulates in the hair follicles, it eats the sebum and grows quickly.
또한 이 여드름 원인균은 지방(트리글리세라이드)을 먹은 뒤 버터와 비슷한 물질, 즉 지방산을 배설한다. 이러한 화학적 변화는 건강한 약산성을 띄던 피부의 유분 pH 밸런스가 무너지면서 알칼리화 되어 결국 피부 자체 기능이 저하되고 피부의 악순환을 초래한다. 이러한 프로피오니박테리움 아크네에 의해 유발되는 여드름을 예방 및 완화시키기 위하여 통상 바르는 약 또는 먹는 약의 치료방법이 제안되어 왔다.Additionally, this acne-causing bacteria eats fat (triglyceride) and then excretes a substance similar to butter, that is, fatty acid. This chemical change causes the skin's healthy slightly acidic oil pH balance to break down and become alkalized, ultimately deteriorating the skin's own function and causing a vicious cycle in the skin. In order to prevent and alleviate acne caused by Propionibacterium acnes, treatment methods using commonly applied or ingested medications have been proposed.
본 출원인은 생체분해성 금속을 이용한 여드름 완화 및 예방용 패치를 개발한 바 있고 이에 대해 기 출원한 바 있다(한국등록특허 제10-2310566호).The present applicant has developed a patch for acne relief and prevention using biodegradable metal and has already filed an application for the same (Korean Patent No. 10-2310566).
한편, 시중에 하이드로콜로이드 시트 등 여드름 부위 보호용 패치가 다양하게 나와 있으나, 붙인 티가 나지 않도록 투명하면서도 얇게 만들어져 패치 자체가 말리며 떨어지는 경우가 빈번하게 일어났다. 따라서 본 발명자는 패치가 말리지 않고 고정될 수 있는 단단한 지지체를 고민하다가 본 발명자가 연구하였던 마그네슘 금속의 여드름 예방 및 완화 효과를 도입하여 패치의 말림성 또는 부착성을 보완하면서도 여드름 치료 효과가 더욱 우수한 본 발명을 고안하게 되었다.Meanwhile, there are a variety of patches for protecting acne areas, such as hydrocolloid sheets, on the market, but they are made transparent and thin so that they are not visible, so the patches themselves often dry up and fall off. Therefore, the present inventor was concerned about a solid support that would allow the patch to be fixed without curling, and then introduced the acne prevention and alleviation effect of magnesium metal, which the present inventor had studied, to create this product that complements the curling or adhesion of the patch and has a better acne treatment effect. came up with an invention.
본 발명은 종래 약물 전달 수단으로 개발되었던 본 발명 출원인의 마이크로 니들의 주성분으로 사용되던 생체분해성 금속 자체가 별도의 약물을 포함하지 않으면서도, 여드름 원인균에 대한 항균활성을 발현함을 확인하여, 특정의 생체분해성 금속의 여드름 치료용으로서의 새로운 용도를 제공하면서도, 적용 부위에서 최적의 사용 편의성 및 효과를 극대화할 수 있는 제형의 여드름 완화 및 예방용 패치를 제공하고자 한다.The present invention confirmed that the biodegradable metal itself, which was used as the main component of the applicant's microneedle, which was conventionally developed as a drug delivery means, expressed antibacterial activity against acne-causing bacteria without containing a separate drug, The aim is to provide a patch for acne relief and prevention in a formulation that maximizes effectiveness and optimal convenience of use at the application site, while providing a new use for acne treatment of biodegradable metal.
또한 본 발명은 인체 부작용이 적고, 피부에 밀착된 채 오래 유지될 수 있으며, 생체분해성 금속의 분해작용으로 인한 색변화로 그 교체시기를 알 수 있는 마커로서의 기능을 할 수 있는 여드름 완화 및 예방용 패치를 제공하고자 한다.In addition, the present invention has fewer side effects on the human body, can be maintained in close contact with the skin for a long time, and can function as a marker to indicate replacement time due to color change due to the decomposition of biodegradable metals for alleviating and preventing acne. We would like to provide a patch.
본 발명은 다음 화학식 1로 표시되고, 사용자 피부와 접촉하는 생체분해성 금속 박판 및 금속 박판의 일 단면에 위치한 점착 시트를 포함하고, 금속 박판은 두께가 0.7mm 이하인, 피부 부착성이 우수한 여드름 완화 및 예방용 패치를 제공한다.The present invention is represented by the following formula (1) and includes a biodegradable metal sheet in contact with the user's skin and an adhesive sheet located on one cross section of the metal sheet, wherein the metal sheet has a thickness of 0.7 mm or less, and has excellent skin adhesion to relieve acne and Prophylactic patches are provided.
[화학식 1][Formula 1]
MgaZnbXc Mg a Zn b X c
화학식 1에서 a, b 및 c는 각 성분의 중량%로서, a+b+c=100중량%이고, i) 90≤a≤100, 0≤b≤10, 0≤c≤10 또는 ii) 0≤a≤10, 90≤b≤100, 0≤c≤10임.In Formula 1, a, b and c are the weight percent of each component, a+b+c=100 weight%, i) 90≤a≤100, 0≤b≤10, 0≤c≤10 or ii) 0 ≤a≤10, 90≤b≤100, 0≤c≤10.
바람직한 일 구현예에 있어서, 금속 박판은 상기 화학식 1에서 a, b 및 c는 각 성분의 중량%로서, a+b+c=100중량%이고, i) 95≤a≤100, 0≤b≤5, 0≤c≤5 또는 ii) 0≤a≤5, 95≤b≤100, 0≤c≤5일 수 있다.In a preferred embodiment, the thin metal plate has the following formula: In Formula 1, a, b, and c are weight percent of each component, a+b+c=100 weight%, i) 95≤a≤100, 0≤b≤ 5, 0≤c≤5 or ii) 0≤a≤5, 95≤b≤100, 0≤c≤5.
본 발명의 바람직한 일 구현예에 있어서, 금속 박판은 불가피한 불순물을 포함한 순도 95% 이상의 Mg인 것일 수 있다.In a preferred embodiment of the present invention, the thin metal plate may be Mg with a purity of 95% or more including unavoidable impurities.
또한 본 발명의 바람직한 일 구현예에 있어서, 점착 시트는 두께가 0.3mm 이하일 수 있다.Additionally, in a preferred embodiment of the present invention, the adhesive sheet may have a thickness of 0.3 mm or less.
본 발명의 바람직한 일 구현예에 있어서, 금속 박판은 두께가 0.5mm 이하일 수 있다.In a preferred embodiment of the present invention, the thin metal plate may have a thickness of 0.5 mm or less.
또한, 본 발명의 일 구현예에 의한 피부 부착성이 우수한 여드름 완화 및 예방용 패치에 있어서, 표면에 적어도 하나 이상의 미세 홈을 가질 수 있으며, 상기 미세 홈은, 방사상으로 교차된 형태일 수 있고, 특히 십자 형태일 수 있다.In addition, in the acne relief and prevention patch with excellent skin adhesion according to an embodiment of the present invention, it may have at least one fine groove on the surface, and the fine groove may be radially crossed, In particular, it may be in the shape of a cross.
본 발명의 바람직한 일 구현예에 있어서, 상기 미세 홈은 금속 박판의 양면이 관통된 것일 수 있다.In a preferred embodiment of the present invention, the micro groove may be formed through both sides of a thin metal plate.
본 발명에 따른 피부 부착성이 우수한 여드름 완화 및 예방용 패치에 있어서, 점착 시트는 관찰면의 반대면이 관찰될 수 있을 정도의 투명성을 가지는 것일 수 있다.In the acne relief and prevention patch with excellent skin adhesion according to the present invention, the adhesive sheet may be transparent enough to allow the opposite side of the observation side to be observed.
본 발명의 바람직한 일 구현예에 있어서, 점착 시트는 필름, 폼, 하이드로겔 및 하이드로콜로이드로 구성된 습윤 드레싱재에서 선택된 1종일 수 있다.In a preferred embodiment of the present invention, the adhesive sheet may be one type selected from wet dressing materials consisting of films, foams, hydrogels, and hydrocolloids.
또한 상기의 바람직한 일 구현예에 의한 피부 부착성이 우수한 여드름 완화 및 예방용 패치에 있어서, 점착 시트는 하이드로콜로이드 습윤 드레싱재일 수 있으며, 특히 하이드로콜로이드 습윤 드레싱재는 두께가 0.3mm 이하인 것으로 제공될 수 있다.In addition, in the patch for acne relief and prevention with excellent skin adhesion according to the above preferred embodiment, the adhesive sheet may be a hydrocolloid wet dressing material. In particular, the hydrocolloid wet dressing material may be provided with a thickness of 0.3 mm or less. .
본 발명의 화학식 1로 표시되는 생체분해성 금속 박판을 적용한 패치는 자체적으로 여드름 원인균에 대한 항균 활성을 가져 여드름 완화 및 예방용으로 유용하며, 특히 생체분해성 금속 박판의 유연성으로 인해 피부로부터 들뜨거나 밀리지 않고 밀착된 상태로 유지되어 더욱 우수한 여드름 치료 효과를 제공할 수 있고, 동시에 외부 감염원으로부터 보호하고, 치료 부위 주변으로 습윤한 환경을 조성해 흉터가 남지 않고 깨끗하게 치료될 수 있도록 최적의 환경을 보장할 수 있다.The patch applied with the biodegradable metal sheet represented by Formula 1 of the present invention has antibacterial activity against acne-causing bacteria on its own and is useful for alleviating and preventing acne. In particular, due to the flexibility of the biodegradable metal sheet, it does not lift or slide away from the skin. It can provide better acne treatment effects by remaining in close contact, and at the same time protects against external infectious agents and creates a moist environment around the treatment area, ensuring an optimal environment for clean treatment without leaving scars. .
또한, 본 발명의 패치는 생체분해성 금속 박판이 부식되어 색이 변하는 것을 외부에서 관찰할 수 있어 패치의 교체 시기를 쉽게 확인할 수 있으며, 금속을 다양한 형태로 제작하여 심미적인 효과도 얻을 수 있다.In addition, the patch of the present invention can be observed from the outside as the biodegradable metal sheet corrodes and changes color, making it easy to check when to replace the patch, and aesthetic effects can also be obtained by manufacturing the metal in various shapes.
도 1은 항균 시험에 제공한 본 발명 시트의 시편 사진이다.
도 2 내지 도 4는 항균 내지 항진균 시험결과 사진으로, 도 2는 Propionibacterium acnes ATCC 6919에 대한 시험결과이고, 도 3은 Staphylococcus epidermidis ATCC 12228에 대한 시험결과이며, 도 4는 Trichophyton rubrum ATCC 28188에 대한 시험결과이다.
도 5는 미세 관통 가공이 되지 않은 직경 10mm의 원형 마그네슘 박판 시료를 두께별로 나타낸 사진이다.
도 6은 십자 형태('+'형태)로 관통 가공한 직경 10mm의 원형 마그네슘 박판 시료를 두께별로 나타낸 사진이다.
도 7은 실시예 2에 따른 피부 부착성 평가 시 하이드로콜로이드 점착 시트 단독 또는 무관통 마그네슘 패치 시료를 피부 부착 정도(말림, 들뜸, 떨어짐, 이상 없음)에 따라 나타낸 사진이다.
도 8은 실시예 2에 따른 피부 부착성 평가 시 '+'형태 관통 마그네슘 패치 시료를 피부 부착 정도(들뜸, 떨어짐, 이상 없음)에 따라 나타낸 사진이다.
도 9 및 10은 실시예 3에 따른 식별성 평가 시 마그네슘 합금 패치 시료의 부식으로 인한 색상 변화 여부를 마그네슘 합금의 두께별로 관찰한 사진이다.
도 11은 실시예 3에 따른 식별성 평가 시 마그네슘 합금 패치 시료를 마그네슘 합금 두께별로 하루 이상 두고 관찰한 사진이다.Figure 1 is a photograph of a specimen of the sheet of the present invention subjected to an antibacterial test.
Figures 2 to 4 are photographs of antibacterial and antifungal test results, Figure 2 is a test result for Propionibacterium acnes ATCC 6919, Figure 3 is a test result for Staphylococcus epidermidis ATCC 12228, and Figure 4 is a test result for Trichophyton rubrum ATCC 28188. It is a result.
Figure 5 is a photograph showing circular magnesium thin plate samples with a diameter of 10 mm that have not been micro-penetrated by thickness.
Figure 6 is a photograph showing circular magnesium thin plate samples with a diameter of 10 mm processed through a cross shape ('+' shape) by thickness.
Figure 7 is a photograph showing the hydrocolloid adhesive sheet alone or pain-free magnesium patch samples according to the degree of skin adhesion (curling, lifting, falling off, no abnormality) when evaluating skin adhesion according to Example 2.
Figure 8 is a photograph showing '+' shaped penetrating magnesium patch samples according to the degree of skin adhesion (lifting, falling off, no abnormality) when evaluating skin adhesion according to Example 2.
Figures 9 and 10 are photographs showing whether the color of the magnesium alloy patch sample changes due to corrosion during the identification evaluation according to Example 3, depending on the thickness of the magnesium alloy.
Figure 11 is a photograph of magnesium alloy patch samples observed for more than a day for each magnesium alloy thickness during the identification evaluation according to Example 3.
전술한, 그리고 추가적인 본 발명의 양상들은 첨부된 도면을 참조하여 설명되는 바람직한 실시예들을 통하여 더욱 명백해질 것이다. 이하에서는 본 발명의 이러한 실시예를 통해 당업자가 용이하게 이해하고 재현할 수 있도록 상세히 설명하기로 한다.The foregoing and additional aspects of the present invention will become more apparent through preferred embodiments described with reference to the accompanying drawings. Hereinafter, these embodiments of the present invention will be described in detail so that those skilled in the art can easily understand and reproduce them.
본 발명은 출원인이 한국등록특허 제10-2310566호에서 개발한 여드름 예방 및 완화용 생체분해성 금속을 이용한 패치가 피부에 부착된 채 유지됨으로써 우수한 여드름 치료 효과를 나타낼 수 있도록 다각적인 연구를 지속적으로 수행한 결과로 얻어진 것이다.The present invention continues to conduct multifaceted research to ensure that the patch using biodegradable metal for preventing and alleviating acne, developed by the applicant in Korean Patent No. 10-2310566, can exhibit excellent acne treatment effects by remaining attached to the skin. It was obtained as a result.
본 발명에서 여드름 치료용 금속에 관련한 기재와 피부에서 일어나는 일련의 금속적 반응에 대한 관련 기재는 한국등록특허 제10-2310566호에 기재된 내용에 따름은 물론이다.In the present invention, descriptions related to metals for treating acne and descriptions related to a series of metallic reactions that occur in the skin are of course in accordance with the contents described in Korean Patent No. 10-2310566.
따라서, 본 발명은 일 관점에서, 화학식 1로 표시되는 생체분해성 금속이며 항여드름균 효과를 가지는 여드름 피부 치료용 패치를 제공한다.Therefore, in one aspect, the present invention provides a patch for treating acne skin that is made of a biodegradable metal represented by Chemical Formula 1 and has an anti-acne bacteria effect.
[화학식 1][Formula 1]
MgaZnbXc Mg a Zn b X c
화학식 1에서 a, b 및 c는 각 성분의 중량%로서, a+b+c=100중량%이고, i) 90≤a≤100, 0≤b≤10, 0≤c≤10 또는 ii) 0≤a≤10, 90≤b≤100, 0≤c≤10이다.In Formula 1, a, b and c are the weight percent of each component, a+b+c=100 weight%, i) 90≤a≤100, 0≤b≤10, 0≤c≤10 or ii) 0 ≤a≤10, 90≤b≤100, 0≤c≤10.
즉, 상기 생체분해성 금속은 마그네슘 또는 아연을 가장 많이 포함하는 것이 바람직하다. 따라서 상기 화학식 1에서 a, b 및 c는 각 성분의 중량%로서, a+b+c=100중량%이고, i) 95≤a≤100, 0≤b≤5, 0≤c≤5 또는 ii) 0≤a≤5, 95≤b≤100, 0≤c≤5인 것이 바람직할 수 있다.That is, it is preferable that the biodegradable metal contains the largest amount of magnesium or zinc. Therefore, in Formula 1, a, b and c are the weight% of each component, and a+b+c=100% by weight, i) 95≤a≤100, 0≤b≤5, 0≤c≤5 or ii ) It may be preferable that 0≤a≤5, 95≤b≤100, 0≤c≤5.
X는 마그네슘 또는 아연 이외의 성분으로서, Ca, Fe, Mn, Si, Na, Zr, Ce 및 P로 구성된 군에서 선택되는 1종 이상인 것이 바람직할 수 있으나, 마그네슘 또는 아연과 합금을 만들기 위한 조성이기만 하다면 그 종류에 제한은 없다.X is a component other than magnesium or zinc, and may preferably be one or more selected from the group consisting of Ca, Fe, Mn, Si, Na, Zr, Ce, and P, but it is only a composition for making an alloy with magnesium or zinc. If so, there is no limit to the type.
본 발명에 따른 생체분해성 금속은 피부 표면에 부착된 후 분해 및 흡수되어 금속이온 및 분해 산물을 체내에 방출하는 특성을 갖는 금속으로, 마그네슘(Mg), 칼슘(Ca), 아연(Zn) 등은 알칼리 토금속 계열의 생체분해성 금속으로서, 하기의 반응식 1 내지 3으로 나타낸 것과 같이, 물과 반응하여 수소가스를 방출하는 메커니즘을 갖는다.The biodegradable metal according to the present invention is a metal that attaches to the skin surface and then decomposes and is absorbed, releasing metal ions and decomposition products into the body. Magnesium (Mg), calcium (Ca), zinc (Zn), etc. As a biodegradable metal of the alkaline earth metal series, it has a mechanism to react with water and release hydrogen gas, as shown in Schemes 1 to 3 below.
[반응식 1][Scheme 1]
Mg + 2H2O → Mg(OH)2 + H2 (gas)Mg + 2H 2 O → Mg(OH) 2 + H 2 (gas)
[반응식 2][Scheme 2]
Ca + 2H2O → Ca(OH)2 + H2 (gas)Ca + 2H 2 O → Ca(OH) 2 + H 2 (gas)
[반응식 3][Scheme 3]
Zn + 2H2O → Zn(OH)2 + H2 (gas)Zn + 2H 2 O → Zn(OH) 2 + H 2 (gas)
상기 반응식 1 내지 3에서 나타나는 금속의 분해 과정에서 발생하는 OH- 이온으로 인한 국지적 pH의 증가로 인해 생체분해성 금속의 선택적 항여드름균 활성 효과가 발생하는 것으로 예측되며, 마그네슘 또는 아연 금속에 상기 화학식 1에 따른 X 성분들이 포함되어 분해 속도가 가속화될 경우, 더욱 신속한 항균 효과가 기대된다.It is predicted that the selective anti-acne activity effect of the biodegradable metal occurs due to an increase in local pH due to OH - ions generated during the decomposition of the metal shown in Schemes 1 to 3, and the magnesium or zinc metal in Formula 1 If the decomposition rate is accelerated by the inclusion of X components, a more rapid antibacterial effect is expected.
본 발명에 있어서, 상기 생체분해성 금속은 마그네슘(Mg), 아연(Zn) 등을 단독 소재로 하여 제조되는 것이 바람직할 수 있고, 특히 생체적합성에 있어 마그네슘 단독소재의 생체분해성 금속이 가장 바람직한 것일 수 있다. 여기서, 마그네슘 단독소재 또는 아연 단독소재라는 용어는 금속 생산 과정에서 발생되는 불가피한 불순물을 포함하는 것 이외에, 순도 95% 이상의 순수 마그네슘이나 아연을 의미하며, 바람직하게는 순도 97% 이상의 순수 마그네슘이나 아연을 의미한다.In the present invention, the biodegradable metal may preferably be manufactured using magnesium (Mg), zinc (Zn), etc. as a sole material. In particular, in terms of biocompatibility, a biodegradable metal made of magnesium alone may be most preferable. there is. Here, the term magnesium-only material or zinc-only material means pure magnesium or zinc with a purity of 95% or higher, in addition to including inevitable impurities generated during the metal production process, and preferably pure magnesium or zinc with a purity of 97% or higher. it means.
다른 한편으로, 생체분해성 금속은 피부 표면에서의 분해속도를 가속화시키기 위하여, 즉 갈바닉 회로를 생성시키기 위하여 2 이상의 금속을 소재로 하여 제조될 수 있다. 본 발명에 있어서, 상기 생체분해성 금속은 갈바닉 회로를 생성하기 위하여 상기 화학식 1로 표시되는 금속 표면에 다른 종류의 제2의 금속이 코팅된 것일 수 있다. 이때 제2의 금속은 나트륨, 마그네슘, 칼륨, 철, 니켈, 아연, 갈륨, 셀레늄, 스트론튬, 지르코늄, 몰리브덴, 니오븀, 탄탈륨, 타이타늄, 규소, 은, 금, 망간, 칼슘 등을 예시할 수 있으나 이에 한정되는 것은 아니다. 이때, 상기 철(Fe)을 포함하는 경우 특히 크롬이나 니켈이 포함되지 않아야 한다.On the other hand, biodegradable metals can be manufactured using two or more metals to accelerate the decomposition rate on the skin surface, that is, to create a galvanic circuit. In the present invention, the biodegradable metal may be one in which a different type of second metal is coated on the surface of the metal represented by Chemical Formula 1 to create a galvanic circuit. At this time, the second metal may include sodium, magnesium, potassium, iron, nickel, zinc, gallium, selenium, strontium, zirconium, molybdenum, niobium, tantalum, titanium, silicon, silver, gold, manganese, calcium, etc. It is not limited. At this time, when iron (Fe) is included, chromium or nickel should not be included.
한편, 상기 화학식 1로 표시되는 생체분해성 금속은 사용자의 피부와 접촉함으로써 여드름 치료 효과를 나타내기 위해 금속 박판 형태로 제공된다.Meanwhile, the biodegradable metal represented by Formula 1 is provided in the form of a thin metal plate to exhibit an acne treatment effect by contacting the user's skin.
이 때 '금속 박판'이란, 얇은 판재 형태의 금속 자체를 의미하며, '접촉'이란, 금속 박판을 피부에 직접적으로 접촉시키는 구성이든, 연결부재 등을 통해 금속 박판의 분해산물이 피부에 작용할 수 잇도록 간접적으로 접촉시키는 구성이든 제한이 없다.In this case, 'sheet metal' refers to the metal itself in the form of a thin plate, and 'contact' refers to the possibility that the decomposition products of the sheet metal can act on the skin, whether it is a configuration that directly contacts the sheet metal with the skin or through a connecting member. There is no limit to the configuration that indirectly contacts the device.
다만, 여드름 원인균에 대한 항균효과를 높여 여드름 치료 효과를 높이려면, 금속 박판을 사용자의 피부에 직접 접촉시켜 접촉 표면적을 넓히는 것이 바람직하며, 동시에 피부에 접촉된 상태가 유지될 수 있도록 피부에 밀착되는 형태로 제공되는 것이 가장 바람직하다.However, in order to increase the effectiveness of acne treatment by increasing the antibacterial effect against acne-causing bacteria, it is desirable to expand the contact surface area by directly contacting the user's skin with a metal sheet, and at the same time, attach a metal plate that adheres closely to the skin so that it can be maintained in contact with the skin. It is most preferable that it be provided in the following form.
보통의 금속 박판은 큰 강성(stiffness)으로 인해 피부 표면에 밀착되지 않고 금새 들뜨거나 떨어지는 것이 일반적이므로, 피부 부착성 향상을 위해 금속 박판을 유연하게 만들어야 하며, 금속 박판이 얇을수록 유연해지므로 본 발명에 따른 금속 박판은 두께가 0.7mm 이하인 것을 특징으로 한다.Because ordinary thin metal plates do not adhere closely to the skin surface due to their great stiffness, they usually lift or fall off quickly, so the thin metal plates must be made flexible to improve skin adhesion, and the thinner the metal thin plates are, the more flexible the present invention is. The thin metal plate according to is characterized in that it has a thickness of 0.7 mm or less.
만일 금속 박판의 두께가 0.7mm 이상일 경우 금속 박판을 피부에 부착시키기 위한 점착 시트의 크기나 두께와 무관하게, 금속 박판의 강성으로 인해 피부로부터 떨어지거나 들뜨는 현상이 생겨 여드름 치료 효과가 떨어지게 된다.If the thickness of the metal sheet is more than 0.7 mm, regardless of the size or thickness of the adhesive sheet for attaching the metal sheet to the skin, the rigidity of the metal sheet causes it to fall or lift off the skin, reducing the acne treatment effect.
또한, 금속 박판의 두께가 0.7mm 이하로 얇을 경우, 생체분해성 금속이 여드름에서 발생한 삼출물이나 수분과 반응하여 분해되는 과정에서 부식으로 인해 금속 박판의 전면부터 후면까지 전부 색이 변하는 모습을 외부에서 관찰할 수 있어, 본 발명에 따른 피부 치료용 패치의 교체시기를 파악할 수 있는 효과도 제공할 수 있다.In addition, if the thickness of the metal sheet is thinner than 0.7mm, the color of the metal sheet from the front to the back can be observed from the outside due to corrosion as the biodegradable metal reacts with the exudate or moisture generated from acne and decomposes. This can also provide the effect of being able to determine the replacement time of the skin treatment patch according to the present invention.
다만, 금속 박판의 두께가 0.07mm 이하일 경우, 금속의 가공 자체가 어렵기 때문에 0.07mm 이상인 것이 바람직하다.However, when the thickness of the thin metal plate is 0.07 mm or less, it is preferable that it is 0.07 mm or more because metal processing itself is difficult.
한편, 금속 박판의 유연성을 더욱 증가시키기 위하여 그 표면에 적어도 하나 이상의 미세 홈을 갖는 것이 바람직하다. 특히 미세 홈이 방사상으로 교차된 형태일 경우 금속 박판은 다양한 굴곡면의 다양한 방향으로 더욱 잘 구부러질 것이고, 이에 따라 표면이 고르지 않은 피부에 더욱 밀착시킬 수 있으며, 금속 박판의 표면적도 증가하여 상승된 여드름 치료 효과를 갖게 된다.Meanwhile, in order to further increase the flexibility of the thin metal plate, it is desirable to have at least one fine groove on the surface. In particular, if the fine grooves are radially intersecting, the thin metal plate will bend better in various directions on various curved surfaces, allowing it to adhere more closely to the skin with an uneven surface, and the surface area of the thin metal plate will also increase, increasing the It has an acne treatment effect.
상기 금속 박판 표면의 미세 홈은 십자('+'형태) 형태일 수 있으며, 아예 금속 박판의 양면이 관통된 형태로 제공될 수도 있다. 관통된 형태로 제공될 경우 밀착성으로 인해 금속 박판의 표면 접촉 면적이 증가함은 물론이며, 여드름 상처로부터 발생한 삼출물이나 수분이 금속 박판의 관통 홈 사이를 통과하여 이하에서 기재하는 습윤 드레싱재 시트로 흡수될 수 있고, 삼출물 등이 통과하는 과정에서 금속 박판을 신속하게 분해하여 더욱 우수한 항여드름균 효과를 기대할 수 있다.The fine grooves on the surface of the thin metal plate may be in the shape of a cross ('+' shape), or may be provided in the form of penetrating both sides of the thin metal plate. When provided in a penetrating form, not only does the surface contact area of the metal sheet increase due to adhesion, but also the exudate or moisture generated from acne wounds passes between the penetration grooves of the metal sheet and is absorbed into the wet dressing material sheet described below. This can be done, and the thin metal plate can be quickly decomposed during the process of exudate passing through, so an even better anti-acne effect can be expected.
만일 삼출물 등이 관통 홈을 통과함으로써 습윤 드레싱재 시트의 중간 부분으로 흡수될 수 있는 구성이 결여되어 있는 경우, 삼출물 등은 금속 박판 접촉면 사이에 들어차다가 외곽 부분을 따라 습윤 드레싱재로 흡수될 것이며, 습윤 드레싱재 시트 외곽 부분이 부풀어 접착성에 악영향을 미치게 될 것이다.If there is a lack of structure that allows exudate, etc. to be absorbed into the middle part of the wet dressing material sheet by passing through the through groove, the exudate, etc. will be trapped between the contact surfaces of the thin metal plates and then absorbed into the wet dressing material along the outer portion, The outer portion of the wet dressing sheet will swell, adversely affecting adhesion.
한편, 본 발명의 금속 박판의 양면 중 일 단면엔 점착 시트가 위치한다. 점착 시트는 금속 박판이 사용자의 피부에 접촉된 상태가 유지될 수 있도록 부착시키기 위해 포함하는 구성이며, 따라서 금속 박판의 피부 접촉면의 반대면에 위치하고, 점착 시트의 크기나 모양에 아무런 제한이 없으나, 금속 박판의 크기보다 그 크기가 더 커서 금속 박판 전부를 덮을 수 있는 것이 바람직하다.Meanwhile, an adhesive sheet is located on one side of both sides of the thin metal plate of the present invention. The adhesive sheet is a component that attaches a thin metal plate to the user's skin so that it can remain in contact with the user's skin. Therefore, it is located on the opposite side of the skin contact surface of the thin metal plate, and there are no restrictions on the size or shape of the adhesive sheet. It is preferable that the size is larger than the size of the metal sheet so that it can cover the entire metal sheet.
구체적으로 점착 시트는, 금속 박판의 모양과 무관한 가장 큰 직경을 기준으로, 그 둘레로 테두리 1mm 이상을 갖도록 구성될 수 있다. 즉, 금속 박판의 가장 큰 직경이 점착 시트보다 1mm 이상 작도록 함으로써 금속 박판이 다양한 모양을 갖더라도 점착 시트를 벗어나지 않도록 하는 것을 특징으로 하며, 이 경우 금속 박판을 별 모양 등 심미감을 위해 다양한 모양 변형을 주더라도 안정적으로 피부에 점착될 수 있도록 하는 효과를 제공한다.Specifically, the adhesive sheet may be configured to have an edge of 1 mm or more around the largest diameter, which is unrelated to the shape of the thin metal plate. In other words, the largest diameter of the thin metal plate is 1 mm or more smaller than the adhesive sheet to prevent the thin metal plate from leaving the adhesive sheet even if it has various shapes. In this case, the thin metal plate can be modified into various shapes for aesthetics, such as a star shape. It provides the effect of stably adhering to the skin even when applied.
또한 상기 점착 시트는 금속 박판이 관찰될 수 있을 정도의 투명성을 갖는 것이 바람직하다. 투명 또는 반투명의 점착 시트는 금속 박판의 색이 변하는 것을 외부에서 관찰할 수 있도록 하여 본 발명에 따른 피부 치료용 패치의 교체시기를 파악할 수 있도록 한다. 또한 금속 박판 주변의 시트 부위는 피부색을 띄게 되므로 피부에 붙이더라도 티가 나지 않아 심미적인 효과가 있다.In addition, the adhesive sheet preferably has transparency to the extent that the thin metal plate can be observed. The transparent or translucent adhesive sheet allows the color change of the metal sheet to be observed from the outside, allowing the user to determine when to replace the skin treatment patch according to the present invention. In addition, the sheet area around the metal sheet becomes skin-colored, so it is not noticeable even when attached to the skin, providing an aesthetic effect.
위와 같은 효과는 점착 시트가 얇을수록 우수해지지만, 지나치게 얇으면 점착 시트가 피부에 부착되지 않고 말려 올라갈 수 있으므로 주의해야 하는데, 본 발명에 따른 금속 박판과 함께 사용 시 금속 박판으로 인해 점착 시트가 평평하게 유지되므로 시트가 말리거나 떨어지지 않는 효과를 얻을 수 있다. 특히 점착 시트가 아래에서 기재하는 습윤 드레싱재로 이루어진 시트일 경우, 시트가 말리거나 들뜨지 않고 피부에 밀착된 채 유지되면 삼출물 등의 흡수 기능을 온전히 발휘할 수 있어 상승적 효과를 얻을 수 있다.The above effect becomes better as the adhesive sheet is thinner, but if it is too thin, the adhesive sheet may not adhere to the skin and may roll up, so care must be taken. However, when used with the thin metal plate according to the present invention, the adhesive sheet becomes flat due to the thin metal plate. Since it is maintained flat, you can achieve the effect of preventing the sheet from curling or falling off. In particular, when the adhesive sheet is a sheet made of the wet dressing material described below, if the sheet is maintained in close contact with the skin without curling or lifting, it can fully exert its function of absorbing exudates, etc., resulting in a synergistic effect.
더불어서 얇은 점착 시트에 점착된 금속 박판이 상기한 바와 같이 관통 홈을 가지게 되면, 피부로부터 발생한 삼출물이나 수분이 홈을 통해 점착 시트 방향으로 빠져나가는 과정이 더욱 용이해 질 것이고, 그 과정에서 일어나는 금속 박판의 부식으로 인한 색 변화를 더욱 관찰하기 용이해 질 것이다.In addition, if the metal sheet adhered to the thin adhesive sheet has a through groove as described above, the process of exudate or moisture generated from the skin escaping through the groove toward the adhesive sheet will become easier, and the metal sheet that occurs in the process will become easier. It will be easier to observe color changes due to corrosion.
이러한 상승된 여드름 치료 효과, 피부 부착성, 교체시기 파악 등의 효과를 가짐과 동시에 금속 박판의 제조방법을 간소화할 수 있는 미세 홈 형태는 십자('+'형태) 형태이다.The shape of the micro grooves, which can simplify the manufacturing method of thin metal plates while having such effects such as increased acne treatment effect, skin adhesion, and identification of replacement time, is in the shape of a cross ('+' shape).
한편, 상기의 점착 시트는 필름, 폼(foam), 하이드로겔 및 하이드로콜로이드로 구성된 습윤 드레싱재에서 선택된 1종으로 제공될 수 있다. 상처 드레싱이란 상처의 오염 방지 및 보호에 사용하는 기구 및 재료로, 본 발명에 따른 점착 시트가 습윤 드레싱재로 제공될 경우, 박테리아 등의 외부 감염원으로부터 보호하고, 산소 교환이 가능하며, 여드름으로 인한 상처 치료 과정에서 생성되는 삼출물(진액)과 수분을 흡수하는 등 상처 주위에 균형 잡힌 습윤한 환경을 조성시킴으로써 흉터가 남지 않고 깨끗하게 치료할 수 있는 효과를 가지게 된다. 습윤 드레싱재의 종류로는 대표적으로 필름, 폼, 하이드로겔 및 하이드로콜로이드 드레싱재가 있다.Meanwhile, the adhesive sheet may be provided as one type selected from wet dressing materials composed of film, foam, hydrogel, and hydrocolloid. Wound dressings are devices and materials used to prevent and protect wounds from contamination. When the adhesive sheet according to the present invention is provided as a wet dressing material, it protects against external infectious agents such as bacteria, enables oxygen exchange, and protects against acne. By creating a balanced, moist environment around the wound by absorbing exudate (sulphate) and moisture generated during the wound healing process, it has the effect of cleanly treating the wound without leaving a scar. Typical types of wet dressing materials include film, foam, hydrogel, and hydrocolloid dressing.
필름 드레싱은 통상적으로 폴리우레탄 성분의 얇고 투명한 필름 형태로 만들어진다. 투명하게 제조될 수 있어 드레싱을 유지한 채 상처를 관찰할 수 있고, 폴리우레탄은 O2 및 CO2와 같은 기체는 투과 가능하지만 액체 및 미생물 유기체는 투과되지 않으므로, 미생물 이동을 방지하고 상처를 보호할 수 있다.Film dressings are typically made of a thin, transparent film of polyurethane. It can be manufactured transparently, allowing the wound to be observed while maintaining the dressing. Polyurethane is permeable to gases such as O 2 and CO 2 but impermeable to liquids and microbial organisms, preventing the movement of microorganisms and protecting the wound. can do.
폼(foam) 드레싱은 주로 폴리우레탄의 합성물질이며 두께나 접착력 유무에 따라 2차적으로 필름이나 친수콜로이드를 결합시킨 복합 형태 등으로 다양하게 제작되고 있으며, 삼출물이 중간 정도이거나 많을 경우 사용이 가능하다.Foam dressings are mainly a synthetic material of polyurethane, and are produced in various forms, such as secondary films or composite forms that combine hydrocolloids, depending on the thickness or adhesive strength. They can be used when the exudate is medium or large. .
하이드로겔 드레싱은 겔 형태의 수분이 함유된 제품이며, 삼출물을 흡수하기 보다는 상처 부위의 습윤 환경을 극대화하기 위해 사용된다. 친수성 다공성 구조를 가지고 있어 상처의 수분 손실을 제어하고, 상처를 촉촉하게 유지할 수 있으며, 가스 교환이 가능하고, 비부착성으로 인해 다른 드레싱보다 쉽게 제거할 수 있는 특징을 지닌다.Hydrogel dressing is a product that contains water in the form of a gel and is used to maximize the wet environment of the wound area rather than absorb exudate. It has a hydrophilic porous structure, so it can control moisture loss from the wound, keep the wound moist, enable gas exchange, and have the characteristics of being easier to remove than other dressings due to its non-adhesive nature.
하이드로콜로이드 드레싱은 접착력이 있는 드레싱 제재로 생분해성 및 통기성이 있는 2층 구조의 드레싱이다. 치유를 촉진시키기 위한 별도의 1차 또는 2차 드레싱 없이도 상처에 부착할 수 있다. 내부층은 카르복시 메틸 셀룰로오스, 펙틴, 젤라틴 또는 엘라스토머로 구성되어 자체 접착 겔 형성이 가능하고, 외부층은 상처를 밀봉하는 폴리우레탄 필름으로 구성되어 박테리아, 이물질로부터 피부를 보호한다. 상처에서 삼출물이 나오면 이를 습윤 겔 형태로 유지시켜 상처의 습윤 환경을 유지하며, 반투명 형태의 제품이 많이 있어 상처의 상태를 모니터링하기 쉽고, 필름으로 코팅되어 있어 액체, 물, 박테리아는 투과할 수 없다. 피부에 부착 시 주변 마찰로부터 보호할 수 있고 상처의 통증을 줄여주는 효과도 있다.Hydrocolloid dressing is an adhesive dressing material with a two-layer structure that is biodegradable and breathable. It can be attached to the wound without a separate primary or secondary dressing to promote healing. The inner layer is made of carboxymethyl cellulose, pectin, gelatin or elastomer to form a self-adhesive gel, and the outer layer is made of polyurethane film that seals the wound and protects the skin from bacteria and foreign substances. When exudate comes out of the wound, it is maintained in the form of a wet gel to maintain the wound's wet environment. Many products are translucent, making it easy to monitor the condition of the wound. It is coated with a film, so liquid, water, and bacteria cannot penetrate. . When attached to the skin, it can protect against surrounding friction and also has the effect of reducing the pain of wounds.
본 발명에 따른 피부 부착성이 우수하면서도, 삼출물 흡수 등을 통해 상처의 습윤 환경을 유지하고, 금속 박판의 부식 정도를 모니터링하여 교체 시기를 파악하기 쉬우며, 인체에 대한 부작용이 적은 피부 치료용 패치를 제공하기 위하여 상기 점착 시트는 하이드로콜로이드 드레싱재로 제공되는 것이 바람직하다.A skin treatment patch according to the present invention that has excellent skin adhesion, maintains a moist environment in the wound through exudate absorption, etc., monitors the degree of corrosion of the metal sheet, makes it easy to determine replacement time, and has fewer side effects on the human body. In order to provide, the adhesive sheet is preferably provided as a hydrocolloid dressing material.
한편, 본 발명에 따른 여드름 완화 및 예방용 패치의 점착 시트는 두께가 0.3mm 이하인 것을 특징으로 한다. 두께가 0.3mm를 초과할 경우 피부로부터 들뜨거나 떨어져 피부 부착성이 감소하게 되는 것을 아래 실시예 2의 표 2 및 3에서 파악할 수 있다.Meanwhile, the adhesive sheet of the patch for alleviating and preventing acne according to the present invention is characterized by a thickness of 0.3 mm or less. It can be seen from Tables 2 and 3 in Example 2 below that when the thickness exceeds 0.3mm, it lifts or separates from the skin and skin adhesion decreases.
상기 및 이하의 기재에서 금속 박판의 모양은 제한이 없다. 따라서 일반적인 원형, 삼각형, 사각형 등 다양한 모양으로 제공될 수 있으며, 얇은 하이드로콜로이드 밴드를 통해 외관에서 관찰이 가능한 금속 박판은, 그 금속의 광택과 모양으로 인해 피부 점착 시 심미성을 제공할 수 있다는 부가적인 효과가 있다.In the above and below descriptions, the shape of the thin metal plate is not limited. Therefore, it can be provided in various shapes such as general circles, triangles, and squares. The metal sheet, which can be observed on the exterior through a thin hydrocolloid band, has the additional advantage of providing aesthetics when adhered to the skin due to the luster and shape of the metal. It works.
본 발명은 생체분해성 금속 박판을 포함하여 여드름을 치료할 수 있는 여드름 완화 및 예방용 패치를 개발한 것으로, 이러한 패치의 효과는 이하에서 기재되는 실시예를 통해, 상술한 생체분해성 금속을 시편으로 하여 피부에 존재하는 다양한 균들에 대하여 그 활성을 평가하고, 그것이 택일적으로 여드름 원인균에 대해서만 활성을 나타냄을 규명하는 방법을 통해 확인하고자 하며, 또한 패치의 피부 부착 우수성(부착성 평가) 및 교체 시기 확인 가부(식별성 평가)를 확인하고자 한다.The present invention has developed a patch for acne relief and prevention that can treat acne, including a biodegradable metal sheet, and the effect of this patch has been demonstrated through the examples described below by applying the above-mentioned biodegradable metal as a specimen to the skin. We aim to confirm through a method of evaluating the activity against various bacteria present in the skin and confirming that it is selectively active only against acne-causing bacteria, and also check the excellent adhesion of the patch to the skin (adhesion evaluation) and the replacement time. We want to check (identity evaluation).
이하, 본 발명을 실시예에 의거 상세히 설명하는바, 본 발명이 이들 실시예에 의해 한정되는 것이 아님은 물론이다.Hereinafter, the present invention will be described in detail based on examples. Of course, the present invention is not limited to these examples.
<실시예 1> 여드름 항균 효과 평가<Example 1> Acne antibacterial effect evaluation
본 발명의 생체분해성 금속에 대한 항여드름균 활성을 평가하기 위하여 한국화학융합시험연구원에 시료를 제공하여 다음과 같은 방법으로 항균 및 항진균 시험을 수행하였다.In order to evaluate the anti-acne fungal activity of the biodegradable metal of the present invention, samples were provided to the Korea Testing and Research Institute, and antibacterial and antifungal tests were performed in the following manner.
이때 제공한 시료는 제조 시 발생되는 불가피한 불순물을 포함한 순수 Mg(순도 95% 이상의 마그네슘)를 이용하여 시트를 제작(두께 100㎛)한 것으로, 도 1의 사진과 같이 소정 규격으로 절단하여 실험의 시료로써 사용되었다.The sample provided at this time was made into a sheet (thickness of 100㎛) using pure Mg (magnesium with a purity of 95% or more) containing inevitable impurities generated during manufacturing. It was cut to a predetermined size as shown in the photo in Figure 1 and used as a sample for the experiment. It was used as.
<시험 장치 및 재료><Testing equipment and materials>
(1) 시험 장치(1) Test device
Autoclave (코아텍, 대한민국)Autoclave (Coaretech, Korea)
Dry oven (Jisico, 대한민국)Dry oven (Jisico, Korea)
Water bath (Polyscience, USA)Water bath (Polyscience, USA)
Incubator (Memmert, Germany)Incubator (Memmert, Germany)
pH meter (Thermo Orion, USA)pH meter (Thermo Orion, USA)
Stop watch (Time Art, Japan)Stop watch (Time Art, Japan)
Vortex mixer (Thermolyne, USA)Vortex mixer (Thermolyne, USA)
Container (Iwaki Pyrex, Japan)Container (Iwaki Pyrex, Japan)
Sterile pipette (Falcon, USA)Sterile pipette (Falcon, USA)
Petri dish (SPL, 대한민국)Petri dish (SPL, Korea)
Volumetric flask (Myung Sung, 대한민국)Volumetric flask (Myung Sung, South Korea)
Mechanical shaker (Jisico, 대한민국)Mechanical shaker (Jisico, Korea)
Clean bench (수공양행, 대한민국)Clean bench (Sugong Corporation, Korea)
Colony counter (덕우과학, 대한민국)Colony counter (Dukwoo Science, Korea)
Anaerobic container (DIFCO, USA)Anaerobic container (DIFCO, USA)
(2) 시험 재료(2) Test material
1) 시험균주1) Test strain
한국미생물보존센터로부터 분양받음Received from Korea Microorganism Conservation Center
- Propionibacterium acnes ATCC 6919- Propionibacterium acnes ATCC 6919
- Staphylococcus epidermidis ATCC 12228- Staphylococcus epidermidis ATCC 12228
- Trichophyton rubrum ATCC 28188- Trichophyton rubrum ATCC 28188
2) 배지 및 시약2) Media and reagents
- Reinforced clostridial medium broth (DIFCO, USA)- Reinforced clostridial medium broth (DIFCO, USA)
- Brain heart infusion broth (DIFCO, USA)- Brain heart infusion broth (DIFCO, USA)
- Sabouraud dextrose broth (DIFCO, USA)- Sabouraud dextrose broth (DIFCO, USA)
- Reinforced clostridial medium agar (DIFCO, USA)- Reinforced clostridial medium agar (DIFCO, USA)
- Tryptic soy agar (DIFCO, USA)- Tryptic soy agar (DIFCO, USA)
- Sabouraud dextrose agar (DIFCO, USA)- Sabouraud dextrose agar (DIFCO, USA)
- GaspakTM EZ (DIFCO, USA)- GaspakTM EZ (DIFCO, USA)
- 0.05 % polysorbate 80 solution- 0.05% polysorbate 80 solution
- 멸균액체파라핀- Sterile liquid paraffin
(3) 시험방법 (Test method)(3) Test method
1) 시험방법1) Test method
a. 시험균의 전배양 및 조제a. Pre-culture and preparation of test bacteria
P. acnes는 Reinforced clostridial medium (RCM) broth에 접종하여 (35 ±1) ℃에서 3일 동안 배양하였다. 배양된 균액을 새로운 RCM broth에 접종하고 상기와 동일한 조건으로 배양한 후, 이 과정을 1회 추가로 반복하였다. 균주의 모든 배양 과정에서 멸균 액체 파라핀을 이용하여 혐기적 조건을 유지시켜 주었다. 이 후 시험균액으로 사용하였다. P. acnes was inoculated into reinforced clostridial medium (RCM) broth and cultured at (35 ±1) °C for 3 days. The cultured bacterial solution was inoculated into new RCM broth and cultured under the same conditions as above, and this process was repeated one additional time. Anaerobic conditions were maintained using sterile liquid paraffin during all cultivation processes of the strain. Afterwards, it was used as a test bacterial solution.
S. epidermidis는 Brain heart infusion broth에 접종하여 (35 ±1)℃에서 (18 ~ 24)시간 동안 배양 후 시험균액으로 사용하였다. S. epidermidis was inoculated into brain heart infusion broth and cultured at (35 ±1)°C for (18 to 24) hours before being used as a test bacterial solution.
T. rubrum는 Sabouraud dextrose agar에 접종하여 (25 ±1) ℃에서 14일 동안 배양하였다. 시험균이 자란 고체 배지 위에 0.05% polysorbate 80 solution을 분주하고 spreader를 이용하여 포자를 떼어낸 후 거즈를 통과시켜 균사를 제거하였다. 이런 방식으로 조제된 spore solution을 (1 ~ 9)×107 CFU/mL가 되도록 조정하여 시험균액으로 사용하였다. T. rubrum was inoculated on Sabouraud dextrose agar and cultured at (25 ± 1) °C for 14 days. 0.05% polysorbate 80 solution was dispensed onto the solid medium on which the test bacteria grew, spores were removed using a spreader, and hyphae were removed by passing through gauze. The spore solution prepared in this way was adjusted to (1 ~ 9) × 10 7 CFU/mL and used as a test bacterial solution.
b. 시험 절차b. test procedure
미리 준비된 Reinforced clostridial medium (RCM) agar, Tryptic soy agar 및 Sabouraud dextrose agar 위에 각각의 균 배양액을 멸균된 면봉으로 고르게 접종하고 배지 중앙에 준비된 시료(20㎜×20㎜)를 올려놓았다. 이후 P. acnes는 혐기 조건 (35 ±1)℃ 에서 5일 동안 배양하였으며, S. epidermidis는 (35 ±1) ℃ 에서 (24 ±2)시간, T. rubrum는 (25 ±1) ℃에서 7일 동안 배양하였다. 이 후, 시료 주위의 균 성장저지대(Zone of inhibition)를 측정하는 방식으로 시험을 실시하였다.Each bacterial culture was evenly inoculated onto the pre-prepared Reinforced clostridial medium (RCM) agar, Tryptic soy agar, and Sabouraud dextrose agar using a sterilized cotton swab, and the prepared sample (20 mm × 20 mm) was placed in the center of the medium. Afterwards, P. acnes was cultured at anaerobic conditions (35 ±1)°C for 5 days, S. epidermidis was cultured at (35 ±1)°C for (24 ±2) hours, and T. rubrum was cultured at (25 ±1)°C for 7 days. Cultured for one day. Afterwards, the test was conducted by measuring the zone of inhibition for bacterial growth around the sample.
2) 결과 판독2) Reading the results
다음 식 1에 따라 성장저지대의 폭(W)을 계산하였다.The width (W) of the growth zone was calculated according to the following equation 1.
<식 1><Equation 1>
W = (T-D)/2 W = (T-D)/2
W : 저지대의 폭 (mm)W: Width of lowlands (mm)
T : 시료와 저지대의 전체지름 (mm)T: Total diameter of sample and low zone (mm)
D : 시료의 지름 (mm)D: Sample diameter (mm)
상기 표 1로 요약한 것과 같이, P. acnes에 대한 항균효과 결과, 시료와 저지대의 전체지름(T)은 32mm, 시료의 지름(D)은 20mm로 관찰되었다. 따라서 상기의 계산식에 따라 저지대의 폭(W)은 6.0mm로 확인되었다(도 2 참조).As summarized in Table 1 above, as a result of the antibacterial effect against P. acnes , the total diameter (T) of the sample and the low area was observed to be 32 mm, and the diameter (D) of the sample was observed to be 20 mm. Therefore, according to the above calculation formula, the width (W) of the low-lying area was confirmed to be 6.0 mm (see Figure 2).
S. epidermidis에 대한 항균효과 결과, 시료와 저지대의 전체지름(T)은 20mm, 시료의 지름(D)은 20mm로 관찰되었다. 따라서 상기의 계산식에 따라 저지대의 폭 (W)은 0.0mm로 확인되었다(도 3 참조).As a result of the antibacterial effect against S. epidermidis , the total diameter (T) of the sample and the low area was observed to be 20 mm, and the diameter (D) of the sample was observed to be 20 mm. Therefore, according to the above calculation formula, the width (W) of the low-lying area was confirmed to be 0.0 mm (see Figure 3).
T. rubrum에 대한 항진균효과 결과, 시료와 저지대의 전체지름 (T)은 20mm, 시료의 지름 (D)은 20mm로 관찰되었다. 따라서 상기의 계산식에 따라 저지대의 폭 (W)은 0.0mm로 확인되었다(도 4 참조).As a result of the antifungal effect against T. rubrum , the total diameter (T) of the sample and the lowland was observed to be 20 mm, and the diameter (D) of the sample was observed to be 20 mm. Therefore, according to the above calculation formula, the width (W) of the low-lying area was confirmed to be 0.0 mm (see Figure 4).
본 시험 조건하에서 시료[Mg Micro Carrier Multi Care로 명명]에 대한 P. acnes, S. epidermidis 및 T. rubrum의 저지대는 각각 6.0mm, 0.0mm 및 0.0mm로 나타났다.Under these test conditions, the low zone of P. acnes , S. epidermidis and T. rubrum for the sample [named Mg Micro Carrier Multi Care] was found to be 6.0 mm, 0.0 mm and 0.0 mm, respectively.
결과적으로, 본 발명의 생체분해성 금속은 여드름 원인균에 대해서만 항균 활성을 가지며, 나머지는 항균 내지 항진균효과가 관찰되지 않았다.As a result, the biodegradable metal of the present invention has antibacterial activity only against acne-causing bacteria, and no antibacterial or antifungal effects were observed for the rest.
<실시예 2> 부착성 평가<Example 2> Adhesion evaluation
(1) 시험 재료 준비(1) Preparation of test materials
1) 마그네슘 박판1) Magnesium sheet
불가피한 불순물을 포함한 순수 순도 95% 이상의 금속 마그네슘으로 이루어진 직경 10mm의 원형 박판(이하, '무관통 마그네슘 박판'으로 기재. 도 5. a 내지 e 참조)과, 마찬가지로 불가피한 불순물을 포함한 순수 순도 95% 이상의 금속 마그네슘 박판에 십자('+'모양) 형태로 관통하여 내부 가공시킨 원형 박판(이하, '관통 마그네슘 박판'으로 기재. 도 6. a 내지 e 참조)을 각각 0.07mm, 0.1mm, 0.3mm, 0.5mm 및 0.8mm의 두께로 준비하였다.A circular thin plate with a diameter of 10 mm made of metallic magnesium with a pure purity of 95% or more including unavoidable impurities (hereinafter referred to as 'non-penetrated magnesium thin plate'; see Figure 5. a to e), and a circular thin plate with a pure purity of 95% or more including unavoidable impurities. Circular thin plates (hereinafter referred to as 'penetrated magnesium thin plates'; see Figures 6. a to e) that were internally processed by penetrating a metal magnesium thin plate in the shape of a cross ('+' shape) were 0.07 mm, 0.1 mm, 0.3 mm, and 0.3 mm, respectively. It was prepared in thicknesses of 0.5mm and 0.8mm.
2) 패치 시료 준비2) Patch sample preparation
상기 무관통 및 +관통 마그네슘 박판에 직경 12mm의 하이드로콜로이드 점착 시트를 금속 박판 주변으로 1mm 정도의 테두리가 남게끔 점착시켜 패치 시료를 준비하였다. 이 때 하이드로콜로이드 점착 시트의 두께는 각각 0.1mm, 0.2mm, 0.3mm 및 0.4mm이었다.A patch sample was prepared by attaching a hydrocolloid adhesive sheet with a diameter of 12 mm to the non-penetrating and + penetrating magnesium sheets, leaving a border of about 1 mm around the metal sheet. At this time, the thickness of the hydrocolloid adhesive sheet was 0.1 mm, 0.2 mm, 0.3 mm, and 0.4 mm, respectively.
(2) 시험 방법(Test Method)(2) Test Method
상기 시료들을 손등 위에 접착시킨 후 하루 이상 관찰하여 시료가 피부로부터 들뜨거나 하이드로콜로이드 시트가 말리는지 여부 등을 아래 표로 나타내었으며, 하이드로콜로이드 점착 시트가 말려있는 모습(도 7. a 참조), 하이드로콜로이드 점착 시트가 피부로부터 떨어진 모습(도 7. b 참조), 패치 시료가 피부로부터 들뜬 모습(도 7. c 참조), 패치 시료 자체가 피부로부터 떨어진 모습(도 7. d 참조), 및 패치 시료가 이상 없이 피부에 밀착된 모습(도7. e 참조)을 도 7에 사진으로 나타내었다.The samples were observed for more than a day after adhering them to the back of the hand, and the table below shows whether the sample lifts from the skin or the hydrocolloid sheet is rolled. The hydrocolloid adhesive sheet is rolled up (see Figure 7. a), and the hydrocolloid sheet is rolled up. The adhesive sheet separated from the skin (see Figure 7. b), the patch sample lifted from the skin (see Figure 7. c), the patch sample itself separated from the skin (see Figure 7. d), and the patch sample A photograph showing the product in close contact with the skin without any abnormalities (see Figure 7 e) is shown in Figure 7.
(3) 결과 판독(3) Reading the results
무관통 마그네슘 박판 패치 시료에 대한 부착성 평가 결과는 아래 표 2에, +관통 마그네슘 박판 패치 시료에 대한 부착성 평가 결과는 아래 표 3에 나타내었다.The adhesion evaluation results for the non-penetrating magnesium thin plate patch samples are shown in Table 2 below, and the adhesion evaluation results for the +penetrating magnesium thin plate patch samples are shown in Table 3 below.
박판
두께
(mm)Mg
thin plate
thickness
(mm)
*말림: 시트 자체적으로 말려 올라가 사용 불가*Curled: The sheet rolls up on its own and cannot be used.
**들뜸: 피부에 완벽하게 부착되지 않음**Lifting: Not completely adhered to the skin.
***떨어짐: 부착 후 수 시간 내 떨어짐***Falling: Falling off within a few hours after attachment
****이상 없음: 말리거나 들뜸, 떨어짐 현상 없음****No problems: No curling, lifting, or falling off.
마그네슘 박판 없이 하이드로콜로이드 점착 시트만 피부에 부착시킨 경우, 시트의 두께가 0.1mm 이하로 얇아지면 피부에 대한 점착력이 감소해 자체적으로 말리는 모습이 관찰되었으나(도 7. a 참조), 마그네슘 박판과 함께 피부에 부착시키면 피부에 이상 없이 부착되어 있는 모습을 관찰할 수 있었다. 다만, 마그네슘 박판 두께가 0.3mm 이상이면 오히려 마그네슘의 유연성이 감소해 패치 시료가 피부로부터 들뜨는 모습이 관찰되었다(도 7. c 참조).When only the hydrocolloid adhesive sheet was attached to the skin without the magnesium sheet, when the thickness of the sheet became thinner than 0.1 mm, it was observed that the adhesive strength to the skin decreased and dried on its own (see Figure 7. a), but with the magnesium sheet, the skin When attached to the skin, it was observed that it was attached to the skin without any problems. However, when the thickness of the magnesium sheet was 0.3 mm or more, the flexibility of magnesium decreased and the patch sample was observed to lift from the skin (see Figure 7. c).
또한, 하이드로콜로이드 점착 시트의 두께가 0.4mm 이상으로 두꺼우면 마그네슘 박판의 존재 여부나 박판 두께와 무관하게 피부로부터 떨어지거나 들뜨는 모습이 관찰되었다(도 7. b 및 c 참조).In addition, when the thickness of the hydrocolloid adhesive sheet was thicker than 0.4 mm, it was observed to fall off or lift off the skin regardless of the presence or absence of the magnesium sheet or the thickness of the sheet (see Figure 7, b and c).
결론적으로, 두께 0.1mm 이하의 마그네슘 박판과 두께 0.3mm 이하의 하이드로콜로이드 시트가 함께 사용될 경우 패치 시료가 밀리거나 들뜨지 않고 피부에 밀착된 상태로 하루 이상 유지되었다(도 7. e 참조).In conclusion, when a magnesium sheet with a thickness of 0.1 mm or less and a hydrocolloid sheet with a thickness of 0.3 mm or less were used together, the patch sample remained in close contact with the skin for more than a day without being pushed or lifted (see Figure 7. e).
박판
두께
(mm)Mg
thin plate
thickness
(mm)
*들뜸: 피부에 완벽하게 부착되지 않음*Lifting: Not completely adhered to the skin
**떨어짐: 부착 후 수시간 내 떨어짐**Falling: Falling off within a few hours after attachment
***이상 없음: 들뜸, 떨어짐 현상 없음***No problem: No lifting or falling off.
+관통 가공한 마그네슘 박판의 두께가 0.8mm 이상일 경우 하이드로콜로이드 시트의 두께와 무관하게 금속 박판의 강성으로 인해 패치 시료가 피부로부터 들뜨거나 떨어지는 것을 관찰하였다(도 8. a 및 b 참조).+ When the thickness of the through-processed magnesium sheet was 0.8 mm or more, it was observed that the patch sample lifted or fell from the skin due to the rigidity of the metal sheet regardless of the thickness of the hydrocolloid sheet (see Figure 8, a and b).
또한 +관통 가공한 마그네슘 박판의 두께와 무관하게, 하이드로콜로이드 시트의 두께가 0.4mm 이상으로 두꺼울 경우 패치 시료가 피부로부터 들뜨거나 떨어지는 것을 관찰하였다(도 8. a 및 b 참조).In addition, regardless of the thickness of the +penetrated magnesium sheet, it was observed that the patch sample lifted or fell from the skin when the thickness of the hydrocolloid sheet was thicker than 0.4 mm (see Figure 8, a and b).
따라서 상기한 효과를 전부 나타내는 최적의 조건은 두께 0.7mm 이하의 +관통 마그네슘 박판과 두께 0.3mm 이하의 하이드로콜로이드 점착 시트를 함께 사용하는 것이며, 특히 +관통 마그네슘 박판의 두께가 0.5mm 이하인 것이 가장 바람직하다.Therefore, the optimal condition to achieve all of the above effects is to use a + penetrating magnesium sheet with a thickness of 0.7 mm or less and a hydrocolloid adhesive sheet with a thickness of 0.3 mm or less. In particular, it is most desirable that the thickness of the + penetrating magnesium sheet is 0.5 mm or less. do.
<실시예 3> 식별성 평가<Example 3> Identification evaluation
(1) 시험 재료 준비(1) Preparation of test materials
1) 마그네슘 합금 박판1) Magnesium alloy sheet
불가피한 불순물을 포함한 순수 마그네슘 97중량%, 아연 3중랑%, 칼슘 0.1중량%를 포함하는 마그네슘 합금으로 이루어진 직경 10mm의 원형 박판(이하, '무관통 마그네슘 합금 박판'으로 기재)과, 마찬가지로 불가피한 불순물을 포함한 순수 마그네슘 97중량%, 아연 3중랑%, 칼슘 0.1중량%를 포함하는 합금 박판에 십자('+'모양) 형태로 관통하여 내부 가공시킨 마그네슘 합금 박판(이하, '+관통 마그네슘 합금 박판'으로 기재)을 각각 0.07mm, 0.1mm, 0.3mm, 0.5mm 및 0.8mm의 두께로 준비하였다.A circular thin plate with a diameter of 10 mm (hereinafter referred to as 'non-penetrated magnesium alloy thin plate') made of a magnesium alloy containing 97% by weight of pure magnesium, 3% by weight of zinc, and 0.1% by weight of calcium, including inevitable impurities, and A magnesium alloy sheet (hereinafter referred to as '+ penetrating magnesium alloy sheet') that is internally processed by penetrating an alloy sheet containing 97% by weight of pure magnesium, 3% by weight of zinc, and 0.1% by weight of calcium in a cross ('+' shape) shape. substrate) were prepared with thicknesses of 0.07mm, 0.1mm, 0.3mm, 0.5mm, and 0.8mm, respectively.
2) 패치 시료 준비2) Patch sample preparation
상기 무관통 및 +관통 마그네슘 합금 박판에 직경 12mm의 하이드로콜로이드 점착 시트를 금속 박판 주변으로 1mm 정도의 테두리가 남게끔 점착시켜 패치 시료를 준비하였다. 이때 하이드로콜로이드 점착 시트의 두께는 0.3mm로 준비하였다.A patch sample was prepared by attaching a hydrocolloid adhesive sheet with a diameter of 12 mm to the non-penetrating and + penetrating magnesium alloy thin plates, leaving a border of about 1 mm around the metal thin plates. At this time, the thickness of the hydrocolloid adhesive sheet was prepared at 0.3mm.
(2) 시험 방법(Test Method)(2) Test Method
0.9%의 생리식염수에 적신 거즈 위에 상기 무관통 및 +관통 마그네슘 합금 패치 시료를 올려두고 하루 이상 관찰하였다. 도 9 및 도 10은 마그네슘 합금 박판의 부식이 약간 진행된 후의 모습을 나타낸 사진이며, 도 11은 하루 이상 지난 후의 모습을 나타낸 사진이다. The non-painful and +penetrating magnesium alloy patch samples were placed on gauze soaked in 0.9% physiological saline solution and observed for more than a day. Figures 9 and 10 are photos showing the magnesium alloy thin plate after corrosion has progressed slightly, and Figure 11 is a photo showing the appearance after more than one day.
(3) 결과 판독(3) Reading the results
두께가 0.07mm, 0.1mm 및 0.3mm인 마그네슘 합금의 경우 부식으로 인해 무관통 및 +관통 패치 시료에서 색상이 변함을 외부에서 관찰할 수 있었다(도 9 참조). 그러나 두께가 0.5mm 및 0.8mm의 마그네슘 합금의 경우는 외부에서 부식이 거의 관찰되지 않아 색상에 변화가 나타나지 않았다(도 10 참조).In the case of magnesium alloys with thicknesses of 0.07 mm, 0.1 mm, and 0.3 mm, color changes were observed externally in the non-penetrating and + penetrating patch samples due to corrosion (see Figure 9). However, in the case of magnesium alloys with a thickness of 0.5 mm and 0.8 mm, little corrosion was observed on the outside and no change in color was observed (see Figure 10).
마그네슘 합금 패치 시료를 하루 이상 관찰한 결과, 마그네슘 합금의 두께가 0.8mm인 경우 부식이 주로 거즈에 부착된 쪽에서 진행되어 외부에서 색상 변화를 관찰하기 어려웠으나, 두께가 0.5mm인 경우 약간의 부식이 일어난 것을 외부에서 관찰할 수 있었으며, 두께가 0.3mm 이하인 경우엔 부식으로 인한 색상 변화를 명백히 관찰할 수 있었다(도 11 참조).As a result of observing magnesium alloy patch samples for more than a day, when the thickness of the magnesium alloy was 0.8mm, corrosion mainly progressed on the side attached to the gauze, making it difficult to observe color changes from the outside, but when the thickness was 0.5mm, slight corrosion occurred. What had happened could be observed from the outside, and if the thickness was less than 0.3 mm, the color change due to corrosion could be clearly observed (see Figure 11).
결론적으로, 마그네슘 합금 박판의 두께가 0.7mm 이하인 경우 패치 시료의 교체시기를 파악할 수 있었으며, 특히 두께가 0.5mm 이하인 경우 식별성이 가장 우수했다.In conclusion, when the thickness of the magnesium alloy thin plate was 0.7 mm or less, it was possible to identify the replacement time of the patch sample. In particular, when the thickness was 0.5 mm or less, identification was the best.
본 발명은 도면에 도시된 일실시 예를 참고로 설명되었으나, 이는 예시적인 것에 불과하며, 본 기술 분야의 통상의 지식을 가진 자라면 이로부터 다양한 변형 및 균등한 타 실시예가 가능하다는 점을 이해할 것이다.The present invention has been described with reference to an embodiment shown in the drawings, but this is merely illustrative, and those skilled in the art will understand that various modifications and other equivalent embodiments are possible therefrom. .
Claims (13)
상기 금속 박판의 일 단면에 위치한 점착 시트를 포함하고,
상기 금속 박판은,
두께가 0.7mm 이하인, 피부 부착성이 우수한 여드름 완화 및 예방용 패치.
[화학식 1]
MgaZnbXc
화학식 1에서 a, b 및 c는 각 성분의 중량%로서, a+b+c=100중량%이고, i) 90≤a≤100, 0≤b≤10, 0≤c≤10 또는 ii) 0≤a≤10, 90≤b≤100, 0≤c≤10임.A biodegradable metal sheet represented by the following formula (1) and in contact with the user's skin; and
It includes an adhesive sheet located on one cross-section of the thin metal plate,
The metal thin plate is,
A patch for acne relief and prevention with a thickness of 0.7 mm or less and excellent adhesion to the skin.
[Formula 1]
Mg a Zn b X c
In Formula 1, a, b and c are the weight percent of each component, a+b+c=100 weight%, i) 90≤a≤100, 0≤b≤10, 0≤c≤10 or ii) 0 ≤a≤10, 90≤b≤100, 0≤c≤10.
상기 금속 박판은,
화학식 1에서 a, b 및 c는 각 성분의 중량%로서, a+b+c=100중량%이고, i) 95≤a≤100, 0≤b≤5, 0≤c≤5 또는 ii) 0≤a≤5, 95≤b≤100, 0≤c≤5 인 것을 특징으로 하는, 피부 부착성이 우수한 여드름 완화 및 예방용 패치.According to paragraph 1,
The metal thin plate is,
In Formula 1, a, b and c are the weight% of each component, and a+b+c=100% by weight, i) 95≤a≤100, 0≤b≤5, 0≤c≤5 or ii) 0 A patch for relieving and preventing acne with excellent skin adhesion, characterized in that ≤a≤5, 95≤b≤100, 0≤c≤5.
상기 금속 박판은,
불가피한 불순물을 포함한 순수 순도 95% 이상의 Mg인 것을 특징으로 하는, 피부 부착성이 우수한 여드름 완화 및 예방용 패치.According to paragraph 1,
The metal thin plate is,
A patch for relieving and preventing acne with excellent adhesion to the skin, characterized by Mg with a purity of 95% or more including unavoidable impurities.
상기 점착 시트는 두께가 0.3mm 이하인, 피부 부착성이 우수한 여드름 완화 및 예방용 패치.According to paragraph 1,
The adhesive sheet is a patch for relieving and preventing acne with excellent skin adhesion and has a thickness of 0.3 mm or less.
상기 금속 박판은 두께가 0.5mm 이하인, 피부 부착성이 우수한 여드름 완화 및 예방용 패치.According to claims 1 to 4,
A patch for alleviating and preventing acne with excellent skin adhesion, wherein the metal sheet has a thickness of 0.5 mm or less.
상기 금속 시트는,
표면에 적어도 하나 이상의 미세 홈을 갖는, 피부 부착성이 우수한 여드름 완화 및 예방용 패치.According to paragraph 1,
The metal sheet is,
A patch for relieving and preventing acne that has excellent skin adhesion and has at least one fine groove on the surface.
상기 미세 홈은,
방사상으로 교차된 형태인 것을 특징으로 하는, 피부 부착성이 우수한 여드름 완화 및 예방용 패치.According to clause 6,
The fine grooves are,
A patch for relieving and preventing acne with excellent skin adhesion, characterized in that it has a radially crossed shape.
상기 미세 홈은,
십자 형태인 것을 특징으로 하는, 피부 부착성이 우수한 여드름 완화 및 예방용 패치.In clause 7,
The fine grooves are,
A patch for alleviating and preventing acne, characterized by a cross shape and excellent adhesion to the skin.
상기 미세 홈은,
상기 금속 박판의 양면이 관통된 것임을 특징으로 하는, 피부 부착성이 우수한 여드름 완화 및 예방용 패치.According to claims 6 to 8,
The fine grooves are,
A patch for alleviating and preventing acne with excellent skin adhesion, characterized in that both sides of the thin metal plate are penetrated.
상기 점착 시트는,
관찰면의 반대면이 관찰될 수 있을 정도의 투명성을 갖는, 피부 부착성이 우수한 여드름 완화 및 예방용 패치.According to paragraph 1,
The adhesive sheet is,
A patch for acne relief and prevention that has excellent skin adhesion and is transparent enough to allow observation of the opposite side of the observation surface.
상기 점착 시트는,
필름, 폼, 하이드로겔 및 하이드로콜로이드로 구성된 습윤 드레싱재에서 선택된 1종인 것을 특징으로 하는, 피부 부착성이 우수한 여드름 완화 및 예방용 패치.According to clause 10,
The adhesive sheet is,
A patch for alleviating and preventing acne with excellent skin adhesion, characterized in that it is a type selected from wet dressing materials composed of film, foam, hydrogel, and hydrocolloid.
상기 점착 시트는,
하이드로콜로이드 습윤 드레싱재인 것을 특징으로 하는, 피부 부착성이 우수한 여드름 완화 및 예방용 패치.According to clause 11,
The adhesive sheet is,
A patch for relieving and preventing acne with excellent skin adhesion, characterized by being a hydrocolloid wet dressing material.
상기 하이드로콜로이드 습윤 드레싱재는,
두께가 0.3mm 이하인, 피부 부착성이 우수한 여드름 완화 및 예방용 패치.According to clause 12,
The hydrocolloid wet dressing material,
A patch for acne relief and prevention with a thickness of 0.3 mm or less and excellent adhesion to the skin.