KR20210108181A - Polyolefin based film compoistion and decoration sheet of high weather-proof comprising the same - Google Patents

Polyolefin based film compoistion and decoration sheet of high weather-proof comprising the same Download PDF

Info

Publication number
KR20210108181A
KR20210108181A KR1020200023067A KR20200023067A KR20210108181A KR 20210108181 A KR20210108181 A KR 20210108181A KR 1020200023067 A KR1020200023067 A KR 1020200023067A KR 20200023067 A KR20200023067 A KR 20200023067A KR 20210108181 A KR20210108181 A KR 20210108181A
Authority
KR
South Korea
Prior art keywords
polyolefin
film
stabilizer
sheet
decorative sheet
Prior art date
Application number
KR1020200023067A
Other languages
Korean (ko)
Other versions
KR102380387B1 (en
Inventor
함창수
권오익
Original Assignee
주식회사 한서마이크론
함창수
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 한서마이크론, 함창수 filed Critical 주식회사 한서마이크론
Priority to KR1020200023067A priority Critical patent/KR102380387B1/en
Publication of KR20210108181A publication Critical patent/KR20210108181A/en
Application granted granted Critical
Publication of KR102380387B1 publication Critical patent/KR102380387B1/en

Abstract

The present invention provides a polyolefin-based film composition for a decorative sheet comprising 100 parts by weight of a first polyolefin-based resin having an elongation of at least 800% and a melting point of 140 to 160℃ and exhibiting a melt index of 3.0 to 12.0 g/min under a temperature of 230℃; and 0.4 to 1.0 part by weight of a UV stabilizer. By employing a multi-structured film comprising the film composition in a decorative sheet, a high weather resistant decorative sheet for exterior materials having excellent weather resistance can be provided.

Description

데코시트용 폴리올레핀계 필름 조성물 및 이를 포함하는 고내후성 데코시트{POLYOLEFIN BASED FILM COMPOISTION AND DECORATION SHEET OF HIGH WEATHER-PROOF COMPRISING THE SAME} Polyolefin-based film composition for decoration sheet and high weather resistance decoration sheet comprising the same

본 기술은 건축분야의 데코시트 관련 기술로서, 구체적으로는 외장재로서 기능할 수 있는 데코시트를 제조하기 위하여 사용되는 폴리올레핀계 필름에 관한 기술이다. The present technology is a technology related to a decoration sheet in the construction field, specifically, a technology related to a polyolefin-based film used to manufacture a decoration sheet that can function as an exterior material.

일반적으로 데코시트라 함은 폴리염화비닐(PVC) 소재로 다양한 인쇄롤 패턴과 엠보롤 패턴으로 천연질감을 표현하여 일상 가정뿐만 아니라 사무용가구, 주거용가구, 주방용 가구의 표면 등에 널리 사용되고 있는 비점착 시트이다. 이러한 데코시트는 가구 내외장재, 사무용가구, 문짝 등의 건축자재, 부엌용 가구, 각종 오디오 케이스, 기타 인테리어 장식에 사용되어 왔다.In general, deco sheet is a polyvinyl chloride (PVC) material that expresses natural texture with various print roll patterns and emboss roll patterns. am. These decorative sheets have been used for interior and exterior furniture, office furniture, building materials such as doors, kitchen furniture, various audio cases, and other interior decorations.

그러나 PVC 소재의 경우, 물성 및 성형성이 우수한 반면, 염화비닐 수지에 가소제를 투입하여 가소성을 부여한 필름을 사용하므로, 소각 시 다이옥신과 같은 유독 가스가 발생하여 인체 및 환경에 유해한 문제가 발생되고 있다. However, in the case of PVC material, while excellent physical properties and moldability, plasticizer is added to vinyl chloride resin to use a plastic film, so toxic gas such as dioxin is generated during incineration, which is harmful to the human body and the environment. .

이러한 문제를 해결하기 위하여 최근에는 데코시트에 친환경적인 폴리올레핀계 수지 필름을 적용하는 시도들이 이루어지고 있다. 예를 들어, 한국등록특허 제10-0804826호에는 폴리올레핀계 유색필름층을 포함하는 데코시트가 개시되어 있고, 한국등록특허 제10-2013169호에는 가구 및 건축자재에 사용되는 이축연신 폴리프로필렌 데코시트 필름 등이 개시되어 있다. In order to solve this problem, attempts have recently been made to apply an eco-friendly polyolefin-based resin film to a decor sheet. For example, Korean Patent No. 10-0804826 discloses a decor sheet comprising a polyolefin-based colored film layer, and Korean Patent No. 10-2013169 discloses a biaxially stretched polypropylene decor sheet used for furniture and building materials. films and the like are disclosed.

그러나 종래의 데코시트에 사용되는 PVC 대체용 필름들은 내구성 및 내후성의 한계로 인하여 외장재용 데코시트로 활용되기 어려운 측면이 있었다. 즉, 종래의 데코시트는 전술한 바와 같이 인테리어용 시트로 주로 사용되어 오고 있고, 여전히 외장재용 데코시트로 활용되기 어려운 측면이 있다. However, the PVC replacement films used in the conventional decorative sheet were difficult to be utilized as a decorative sheet for exterior materials due to limitations in durability and weather resistance. That is, as described above, the conventional decorative sheet has been mainly used as an interior sheet, and it is still difficult to utilize as a decorative sheet for exterior materials.

본 발명은 전술한 문제점과 한계를 인식함으로써 안출된 발명으로서, 폴리올레핀계 수지필름을 도입하되, 내후성이 매우 우수하여 내장재 뿐만 아니라 구조물의 외장재로도 안정적으로 적용 가능한 고내후성 데코시트를 제공하는 것을 목적으로 한다. The present invention is an invention devised by recognizing the above-mentioned problems and limitations, and it introduces a polyolefin-based resin film, but has very excellent weather resistance, so as to provide a high-weather-resistant decorative sheet that can be stably applied not only as an interior material but also as an exterior material of a structure. do it with

또한, 본 발명은 상기 고내후성 데코시트에 적용될 수 있는 폴리올레핀계 다중필름을 제공하는 것을 목적으로 한다. In addition, an object of the present invention is to provide a polyolefin-based multi-film that can be applied to the high weather-resistance decorative sheet.

나아가, 본 발명은 상기 폴리올레핀계 다중필름에 포함되는 핵심적인 폴리올레핀계 필름 조성물을 제공하는 것을 목적으로 한다.Furthermore, an object of the present invention is to provide a core polyolefin-based film composition included in the polyolefin-based multi-film.

본 발명의 일 실시예에 따른 데코시트용 폴리올레핀계 필름 조성물은 적어도 800%의 신율 및 140℃ 내지 160℃의 융점을 갖고, 230℃의 온도 하에서 3.0g/min 내지 12.0g/min의 용융지수를 나타내는 제1 폴리올레핀계 수지 100 중량부; 및 UV 안정제 0.4 내지 1.0 중량부를 포함한다.The polyolefin-based film composition for a decoration sheet according to an embodiment of the present invention has an elongation of at least 800% and a melting point of 140° C. to 160° C., and a melt index of 3.0 g/min to 12.0 g/min under a temperature of 230° C. 100 parts by weight of the first polyolefin-based resin shown; and 0.4 to 1.0 parts by weight of a UV stabilizer.

상기 폴리올레핀계 수지로는 폴리프로필렌 수지가 사용될 수 있다.A polypropylene resin may be used as the polyolefin-based resin.

한편, 상기 UV 안정제는 흡수 특성의 UV 안정제 및 반사 특성의 UV 안정제를 동시에 포함하는 UV 안정제 복합체일 수 있으며, 상기 UV 안정제로는 HALS(Hindered Amine Light Stabilizer)계 안정제가 사용되는 것이 바람직하다.On the other hand, the UV stabilizer may be a UV stabilizer complex including a UV stabilizer of absorption characteristics and a UV stabilizer of reflection characteristics at the same time.

본 발명의 일 실시예에 따른 데코시트용 폴리올레핀계 다중필름은 제2 폴리올레핀계 수지로 이루어진 베이스 필름; 및 상기 베이스 필름의 일면에 연속하여 형성되고, 제1항의 필름 조성물로 이루어진 내후성 필름이 다중으로 적층되어 형성됨으로써 다층 구조를 갖는다.Polyolefin-based multi-film for decoration sheet according to an embodiment of the present invention is a base film made of a second polyolefin-based resin; And it is continuously formed on one surface of the base film, and has a multilayer structure by forming a weather resistant film made of the film composition of claim 1 by laminating multiple.

본 발명의 일 실시예에 따른 고내후성 데코시트는 시트의 적어도 일부 층상 영역에 전술한 폴리올레핀계 다중필름을 포함한다. The high weather resistance decorative sheet according to an embodiment of the present invention includes the above-described polyolefin-based multi-film in at least a portion of the layered region of the sheet.

본 발명에 따른 데코시트는 다중 구조, 예를 들어, 3중 구조의 폴리올레핀(PO)계 필름층을 도입함으로써, 기본적으로 PVC 수지를 대체함에 따라 친환경적인 내외장재로 기능할 수 있음은 물론 고내후성 폴리올레핀계 필름 조성물에 의한 고내후성 폴리올레핀계 필름을 형성함으로써, 외장재용 데코시트로 안정적으로 적용될 수 있다.The decor sheet according to the present invention can function as an eco-friendly interior and exterior material by basically replacing PVC resin by introducing a polyolefin (PO)-based film layer having a multi-structure, for example, a triple structure, as well as a high-weather-resistant polyolefin By forming a highly weather-resistant polyolefin-based film by the film-based composition, it can be stably applied as a decorative sheet for exterior materials.

본 발명에 따른 데코시트는 폴리올레핀계 다중 필름 내의 일부 단위필름에 UV 안정제 및 기타 기능성 첨가제들을 포함시킴으로써, 데코시트의 내후성을 현저히 향상시킬 수 있음을 확인하였고, 이에 따라 본 발명의 데코시트는 건물 외벽의 데코용 외장재로서 충분히 기능할 수 있다. 실제로 출원인은 본 데코시트를 활용함으로써 외장재로서 3년간 내구성의 변화 없이 안정적으로 유지되고 있는 실 사례를 보유하고 있다.It was confirmed that the decorative sheet according to the present invention can significantly improve the weather resistance of the decorative sheet by including a UV stabilizer and other functional additives in some unit films in the polyolefin-based multi-film, and accordingly, the decorative sheet of the present invention is a building exterior wall It can sufficiently function as an exterior material for decoration of In fact, the applicant has a real case that has been stably maintained without change in durability for 3 years as an exterior material by using this decorative sheet.

종래의 데코시트는 베이스 필름으로서 PVC 수지 또는 PET 수지를 조합하여 사용함으로써, 폴리올레핀계 수지 대비 상대적으로 높은 비중을 갖는다. 본 발명에 따른 데코시트는 폴리프로필렌 등 폴리올레핀계 수지를 베이스로 한 시트로서, 상대적으로 낮은 비중을 가짐으로써 데코시트의 경량화를 실현할 수 있고 나아가 탄소배출량을 현저히 줄일 수 있는 장점을 갖는다.The conventional decor sheet has a relatively high specific gravity compared to the polyolefin-based resin by using a combination of PVC resin or PET resin as a base film. The decorative sheet according to the present invention is a sheet based on a polyolefin-based resin such as polypropylene, and by having a relatively low specific gravity, it is possible to realize weight reduction of the decorative sheet and further has the advantage of significantly reducing carbon emission.

한편, 본 발명의 데코시트는 신율이 우수한 폴리올레핀계 필름을 베이스로 하고 있어 피착재와의 층간 박리현상이 없고 작업성 및 내구성이 우수하여, 굴곡부에서 흔히 발생할 수 있는 백화 현상을 현저히 저감할 수 있다.On the other hand, the decorative sheet of the present invention is based on a polyolefin-based film with excellent elongation, there is no delamination between the layers with the adherend, and has excellent workability and durability. .

본 발명의 일 실시예에 따른 데코시트는 3중 구조의 폴리올레핀계 다중필름을 데코시트 내 다양한 위상으로 배치시킬 수 있다. 이에 따라 기본적으로 PVC계 데코시트를 대체할 수 있는 친환경적인 데코시트로 기능함은 물론, 다중 구조의 필름 설계에 변화를 주어 수요자의 니즈에 따라 다양한 하이브리드적인 물성을 갖는 데코시트의 개발이 가능하다.The decoration sheet according to an embodiment of the present invention can be arranged in various phases in the polyolefin-based multi-film having a triple structure in the decoration sheet. Accordingly, it is possible not only to function as an eco-friendly decoration sheet that can basically replace PVC-based decoration sheets, but also to change the design of the multi-structured film to develop decoration sheets with various hybrid properties according to the needs of consumers. .

또한, 본 발명의 고내후성 폴리올레핀계 다중필름은 복수의 폴리올레핀계 수지 조성물을 준비하여 공압출에 의하여 제조됨으로써, 데코시트의 주요 구성인 폴리올레핀계 다중 필름의 제조 공정을 획기적으로 단순화시킬 수 있다.In addition, the high weather resistance polyolefin-based multi-film of the present invention can be prepared by co-extrusion by preparing a plurality of polyolefin-based resin compositions, thereby dramatically simplifying the manufacturing process of the polyolefin-based multi-film, which is the main component of the decor sheet.

본 발명에 따른 고내후성 데코시트용 필름 조성물은 복수의 UV 안정제를 컴파운드화한 UV 안정제 복합체를 포함하므로, 내후성 향상에 기여할 수 있을 뿐만 아니라 외장재용 데코시트의 구체적인 용도나 시공 환경을 고려하여 다양한 복수의 UV 안정제 복합체를 사전에 분류해 놓음으로써, 다양한 환경에 최적화된 고내후성 데코시트의 제조가 가능하도록 한다. Since the film composition for a high-weather-resistant decorative sheet according to the present invention includes a UV stabilizer composite obtained by compounding a plurality of UV stabilizers, it can contribute to improving weather resistance as well as various pluralities in consideration of the specific use or construction environment of the decorative sheet for exterior materials. By pre-classifying the UV stabilizer complex of

도 1은 본 발명의 일 실시예에 따른 데코시트용 폴리올레핀계 다중필름의 증상 구조를 개념적으로 도시한 단면도이다.
도 2는 본 발명의 일 실시예에 따른 고내후성 데코시트 및 피착재의 모습을 개념적으로 도시한 단면도이다.
도 3은 도 1의 폴리올레핀계 다중필름이 도 2의 데코시트 상지필름에 배치 적용된 모습을 개념적으로 도시한 단면도이다. 1 is a cross-sectional view conceptually showing the symptom structure of a polyolefin-based multi-film for decoration sheets according to an embodiment of the present invention.
Figure 2 is a cross-sectional view conceptually showing the appearance of the high weather resistance decorative sheet and the adherend according to an embodiment of the present invention.
3 is a cross-sectional view conceptually illustrating a state in which the polyolefin-based multi-film of FIG. 1 is disposed and applied to the decorative sheet upper film of FIG. 2 .

이하에서 본 발명의 일 실시예에 따른 데코시트용 폴리올레핀계 필름 조성물, 데코시트용 폴리올레핀계 다중필름 및 이를 포함하는 고내후성 데코시트에 대하여 순차적으로 자세하게 설명하도록 한다. 또한, 상기 다중필름 및 데코시트에 대해서는 첨부된 도면을 참조하여 설명하도록 한다. 그러나 하기 설명들은 본 발명의 기술사상을 구체화하여 설명하기 위한 예시적인 설명들이며, 하기 설명들에 의하여 본 발명의 기술사상이 제한되지 않는다. 하기 설명 이외의 다양한 실시예들이 가능함이 당연하며, 본 발명의 기술사상은 오직 후술하는 청구범위에 의하여 해석되고 제한될 수 있을 뿐이다. Hereinafter, a polyolefin-based film composition for a decoration sheet according to an embodiment of the present invention, a polyolefin-based multi-film for a decoration sheet, and a high weather resistance decoration sheet including the same will be sequentially described in detail. In addition, the multi-film and decor sheet will be described with reference to the accompanying drawings. However, the following descriptions are exemplary descriptions for concretely explaining the technical idea of the present invention, and the technical idea of the present invention is not limited by the following description. It is natural that various embodiments other than the following description are possible, and the technical spirit of the present invention can only be interpreted and limited by the claims described below.

또한, 하기 설명을 위하여 참조되는 도면 내 각 층들의 스케일은 설명을 위하여 개념적으로 과장된 것일 수 있으므로, 도면의 스케일에 의하여 본 발명 데코시트의 크기나 두께의 기술요소가 제한되는 것은 아니다. In addition, since the scale of each layer in the drawings referenced for the following description may be conceptually exaggerated for description, the technical elements of the size or thickness of the present invention decor sheet are not limited by the scale of the drawings.

또한, 하기 실시예에서는 데코시트용 폴리올레핀계 다중필름을 3중 구조로 예시하여 설명하나, 이러한 다중필름의 층상 구조, 예를 들면 층의 개수나 다중필름의 데코시트 내 위상(위치나 방향)은 요구되는 데코시트의 물성이나 용도 등에 따라 변형 실시될 수 있다.In addition, in the following examples, the polyolefin-based multi-film for the decoration sheet is illustrated and described as a triple structure, but the layered structure of such a multi-film, for example, the number of layers or the phase (position or direction) in the decoration sheet of the multi-film Deformation may be carried out according to the required physical properties or use of the decorative sheet.

1. 데코시트용 폴리올레핀계 필름 조성물1. Polyolefin-based film composition for decoration sheet

본 발명에 따른 데코시트용 폴리올레핀계 필름 조성물은, 폴리올레핀계 수지 및 UV 안정제를 포함한다. 상기 데코시트용 폴리올레핀계 필름 조성물은 단위필름을 형성하는 조성물로서, 후술하는 바와 같이 상기 단위필름은 다중필름을 구성하는 일부의 층으로서 기능한다. The polyolefin-based film composition for a decorative sheet according to the present invention includes a polyolefin-based resin and a UV stabilizer. The polyolefin-based film composition for a decoration sheet is a composition for forming a unit film, and as will be described later, the unit film functions as a partial layer constituting a multi-film.

상기 폴리올레핀계 수지로는 적어도 800%의 신율 및 140℃ 내지 160℃의 융점을 갖고, 230℃의 온도 하에서 3.0g/min 내지 12.0g/min의 용융지수를 나타내는 수지가 사용되며, 예를 들면, 폴리프로필렌 수지를 사용할 수 있다. 상기 폴리올레핀계 수지의 세부 종류는 최종 제품인 데코시트의 물성을 고려하여 변화될 수 있다. As the polyolefin-based resin, a resin having an elongation of at least 800% and a melting point of 140° C. to 160° C., and a melt index of 3.0 g/min to 12.0 g/min under a temperature of 230° C. is used, for example, A polypropylene resin may be used. The detailed type of the polyolefin-based resin may be changed in consideration of the physical properties of the decorative sheet, which is the final product.

상기 UV 안정제로서는, 흡수 특성의 UV 안정제 및 반사 특성의 UV 안정제를 동시에 포함하는 UV 안정제 복합체가 사용될 수 있다. 이러한 복합체는 복수의 고형 UV 안정제를 압출 등에 의하여 혼합함으로써 컴파운드화될 수 있다. 한편, 상기 UV 안정제로서는 HALS(Hindered Amine Light Stabilizer)계 UV 안정제가 사용될 수 있다. 구체적으로, 상기 UV 안정제로서는 Ciba-gagi사의 Chimasorbⓡ 및 Tinuvinⓡ이 동량으로 혼합되어 사용될 수 있다. 상기 UV 안정제는 상기 폴리올레핀계 수지 100 중량부 대비 0.1 내지 1.0 중량부가 되도록 사용되는 것이 바람직하다. As the UV stabilizer, a UV stabilizer complex including a UV stabilizer having absorption characteristics and a UV stabilizer having reflection characteristics at the same time may be used. Such a composite may be compounded by mixing a plurality of solid UV stabilizers by extrusion or the like. On the other hand, as the UV stabilizer, a HALS (Hindered Amine Light Stabilizer)-based UV stabilizer may be used. Specifically, as the UV stabilizer, Ciba-gagi's Chimasorb ⓡ and Tinuvin ⓡ may be mixed in the same amount and used. The UV stabilizer is preferably used so as to be 0.1 to 1.0 parts by weight based on 100 parts by weight of the polyolefin-based resin.

상기 데코시트용 폴리올레핀계 필름 조성물은, 최종 제품인 데코시트의 내후성을 극대화하여 상기 데코시트가 건물 외벽 등 외장재로 기능할 수 있도록 한다. The polyolefin-based film composition for the decoration sheet maximizes the weather resistance of the decoration sheet, which is the final product, so that the decoration sheet can function as an exterior material such as an exterior wall of a building.

상기 데코시트용 폴리올레핀계 필름 조성물은, 위의 성분들 외에 산화방지제, 내열안정제, 안티-블로킹제 등 수지 업계에서 통상 사용될 수 있는 기능성 첨가제들을 포함할 수 있다.The polyolefin-based film composition for the decorative sheet may include functional additives that are commonly used in the resin industry, such as antioxidants, heat-resistant stabilizers, and anti-blocking agents, in addition to the above components.

아울러, 상기 폴리올레핀계 수지는 단일 수지로도 사용될 수 있으나, 물성이 다소 차이가 있는 이종의 폴리올레핀 수지들의 블렌드를 포함할 수 있고, 이러한 수지 블렌드는 최종 제품인 데코시트의 요구되는 물성이나 용도 등을 고려하여 설계 될 수 있다. In addition, the polyolefin-based resin may be used as a single resin, but may include a blend of heterogeneous polyolefin resins having somewhat different physical properties, and such a resin blend considers the required physical properties and uses of the decor sheet, which is the final product. can be designed by

2. 데코시트용 폴리올레핀계 다중필름2. Polyolefin-based multi-film for decoration sheets

도 1은 본 발명의 일 실시예에 따른 데코시트용 폴리올레핀계 다중필름의 증상 구조를 개념적으로 도시한 단면도이다. 1 is a cross-sectional view conceptually showing the symptom structure of a polyolefin-based multi-film for decoration sheets according to an embodiment of the present invention.

도 1을 참조하면, 데코시트용 폴리올레핀계 다중필름(100)은 폴리올레핀계 수지 또는 이들의 블렌드로 이루어진 베이스 필름(110) 및 상기 상기 베이스 필름(110) 상에 연속하여 형성되고 전술한 폴리올레핀계 필름 조성물로 이루어진 다중의 단위필름(122, 124)들을 포함한다. Referring to FIG. 1 , the polyolefin-based multi-film 100 for decoration sheets is continuously formed on the base film 110 and the base film 110 made of a polyolefin-based resin or a blend thereof, and the above-described polyolefin-based film It includes multiple unit films 122 and 124 made of the composition.

상기 베이스 필름(110)을 이루는 폴리올레핀계 수지는 단위필름 내의 폴리올레핀계 수지와 동일한 수지를 사용해도 되고, 이와 다른 물성을 갖는 수지가 사용될 수도 있다. 각 층의 수지 배합은, 최종 제품인 데코시트의 물성이나 기능을 고려하여 다양하게 설계될 수 있다. The polyolefin-based resin constituting the base film 110 may use the same resin as the polyolefin-based resin in the unit film, or a resin having different physical properties may be used. The resin composition of each layer can be designed in various ways in consideration of the physical properties and functions of the decorative sheet, which is the final product.

3. 고내후성 데코시트3. High weather resistance decorative sheet

도 2는 본 발명의 일 실시예에 따른 고내후성 데코시트 및 피착재의 모습을 개념적으로 도시한 단면도이다.Figure 2 is a cross-sectional view conceptually showing the appearance of the high weather resistance decorative sheet and the adherend according to an embodiment of the present invention.

도 2를 참조하면, 고내후성 데코시트(1000)은 하지필름(L)과 상지필름(H)은 접착증(40)의 의하여 결합된 형태를 갖는다. 하지필름(L)은 피착재(5)와 결합 또는 융착되는 필름으로서 기능하고, 상기 상지필름(H)은 다양한 기능성 부재들을 포함할 수 있고, 시각적으로 외부에 노출되는 필름이다. Referring to FIG. 2 , the high weather resistance decorative sheet 1000 has a form in which the lower film (L) and the upper film (H) are combined by adhesion (40). The base film L functions as a film that is bonded or fused to the adherend 5 , and the upper film H may include various functional members, and is a film that is visually exposed to the outside.

전술한 데코시트용 폴리올레핀계 다중필름은 상기 하지필름(H) 또는 상지필름(L)에 배치될 수 있으며, 상기 데코시트가 외장재로 사용될 경우, 고내후성을 발현하기 위하여 상기 상지필름(H)에 배치된다. The above-mentioned polyolefin-based multi-film for decoration sheet may be disposed on the base film (H) or the upper film (L), and when the decor sheet is used as an exterior material, it is applied to the upper film (H) in order to express high weather resistance. are placed

물론, 상기 폴리올레핀계 다중필름은 상지필름(H) 및 하지필름(L)에 동시에 배치될 수도 있으며, 이 경우 하지필름(L)에 포함되는 다중필름의 경우 피착재(5)와의 결합력을 고려하여 추가적으로 물성이 개질되어야 한다. Of course, the polyolefin-based multi-film may be simultaneously disposed on the upper film (H) and the lower film (L). In addition, the physical properties must be modified.

상기 접착층(40)에 사용되는 접착제는 상기 하지필름(L) 및 상지필름(H)의 층상구조, 강도 등을 고려하여 적절히 선택될 수 있으며, 접착층(40)의 소재는 특별히 제한되지 않는다. The adhesive used for the adhesive layer 40 may be appropriately selected in consideration of the layer structure, strength, etc. of the base film (L) and the upper film (H), and the material of the adhesive layer 40 is not particularly limited.

한편, 상기 데코시트(1000)와 피착재(5)의 계면에는 프라이머가 도포되어 형성된 프라이머층(30)이 형성될 수 있다. 상기 프라이머 처리는 피착재(5) 또는 하지필름(L)의 하부에 선택적으로 처리될 수도 있고, 이와 다르게, 상기 피착재(5) 및 하지필름(L)에 동시에 처리될 수도 있다. 프라이머층(30)은 융착 계면의 표면 상태를 균일하게 함으로써, 융착 강도를 향상시키기 위한 층이다. 상기 프라이머층(30)을 이루는 수지로서는, 다양할 수 있으나, 경우에 따라서는 프라이머층(30)에 상기 하지필름(L)의 하부면을 이루는 수지와 혼용성이 증가되도록 첨가제가 부가될 수 있다. On the other hand, the primer layer 30 formed by applying a primer to the interface between the decor sheet 1000 and the adherend 5 may be formed. The primer treatment may be selectively treated on the lower portion of the adherend 5 or the underlying film L, or alternatively, may be simultaneously processed on the adherend 5 and the underlying film L. The primer layer 30 is a layer for improving the fusion strength by making the surface state of the fusion interface uniform. The resin constituting the primer layer 30 may be various, but in some cases, additives may be added to the primer layer 30 to increase compatibility with the resin constituting the lower surface of the base film L. .

상기 피착재(5)는 목재, 금속재, 합판재 등 특별히 제한되지 않으나, 상기 피착재(5)의 재질에 따라 상기 하지필름(L)을 이루는 베이스 수지 조성이 세부적으로 변화될 수 있다. The adherend 5 is not particularly limited, such as wood, metal, plywood, etc., but the composition of the base resin constituting the base film L may be changed in detail according to the material of the adherend 5 .

도 3은 도 1의 폴리올레핀계 다중필름이 도 2의 데코시트 상지필름에 배치 적용된 모습을 개념적으로 도시한 단면도이다. 3 is a cross-sectional view conceptually illustrating a state in which the polyolefin-based multi-film of FIG. 1 is disposed and applied to the decorative sheet upper film of FIG. 2 .

도 3을 참조하면, 상지필름(H)는 데코시트용 폴리올레핀계 다중필름(100) 및 상기 다중필름(100)의 하부에 형성된 인쇄층(200) 및 데코시트의 최외각을 형성하는 상기 다중필름(100)의 상부에 형성된 열경화성 수지층(300)을 포함한다. Referring to FIG. 3 , the upper film (H) is a polyolefin-based multi-film 100 for a decor sheet, and a printed layer 200 formed under the multi-film 100 and the multi-film forming the outermost layer of the decor sheet. It includes a thermosetting resin layer 300 formed on the upper portion (100).

상기 인쇄층(200)은 상기 다중필름(100)의 일면에 인쇄되어 형성된 층으로서, 상기 인쇄는 패턴 및 다양한 시각효과를 포함할 수 있다. 상기 인쇄층(200)의 인쇄 방식에는 크게 국한되지 않으나, 다양한 패턴 효과를 효율적으로 나타낼 수 있는 그라비아 인쇄 방식 등이 사용될 수 있다.The printing layer 200 is a layer formed by printing on one surface of the multi-film 100, and the printing may include a pattern and various visual effects. Although the printing method of the printing layer 200 is not particularly limited, a gravure printing method capable of efficiently exhibiting various pattern effects may be used.

상기 열경화성 수지층(300)은 상기 다중필름(100) 상에 열경화성 수지를 오버코팅하여 형성되어, 일종의 보호층으로 기능하며 전체적인 데코시트의 내구성 향상에 기여할 수 있다. The thermosetting resin layer 300 is formed by overcoating a thermosetting resin on the multi-film 100 , and functions as a kind of protective layer and can contribute to improving the durability of the overall decorative sheet.

이처럼, 본 발명에 따른 데코시트는 전술한 폴리올레핀계 필름 조성물로 이루어진 필름 및 이를 포함하는 다중필름을 도입함으로써, 기후적 조건이 열악한 환경에서도 내후성이 우수한 외장재로 기능할 수 있다. 나아가, 본 발명은 다중 구조의 폴리올레핀계 수지를 이용한 데코시트의 새로운 층상 플랫폼을 제공함으로써 향후, 내외장재 시공이 필요한 다양한 산업분야에서 기술적 파급력이 클 것으로 기대하고 있다. As such, the decorative sheet according to the present invention can function as an exterior material having excellent weather resistance even in an environment with poor climatic conditions by introducing a film made of the above-described polyolefin-based film composition and a multi-film including the same. Furthermore, the present invention is expected to have a large technological ripple effect in various industrial fields requiring interior and exterior construction in the future by providing a new layered platform of decor sheets using polyolefin-based resins of multiple structures.

Claims (6)

적어도 800%의 신율 및 140℃ 내지 160℃의 융점을 갖고, 230℃의 온도 하에서 3.0g/min 내지 12.0g/min의 용융지수를 나타내는 제1 폴리올레핀계 수지 100 중량부; 및
UV 안정제 0.4 내지 1.0 중량부를 포함하는,
데코시트용 폴리올레핀계 필름 조성물.
100 parts by weight of a first polyolefin-based resin having an elongation of at least 800% and a melting point of 140°C to 160°C, and a melt index of 3.0 g/min to 12.0 g/min under a temperature of 230°C; and
containing 0.4 to 1.0 parts by weight of a UV stabilizer,
A polyolefin-based film composition for decorative sheets.
 제1항에 있어서,
상기 폴리올레핀계 수지는 폴리프로필렌을 포함하는 것을 특징으로 하는 데코시트용 폴리올레핀계 필름 조성물.
According to claim 1,
The polyolefin-based resin is a polyolefin-based film composition for a decor sheet, characterized in that it comprises polypropylene.
 제1항에 있어서,
상기 UV 안정제는 흡수 특성의 UV 안정제 및 반사 특성의 UV 안정제를 동시에 포함하는 UV 안정제 복합체인 것을 특징으로 하는 폴리올레핀계 필름 조성물.
According to claim 1,
The UV stabilizer is a polyolefin-based film composition, characterized in that it is a UV stabilizer complex including a UV stabilizer of absorption characteristics and a UV stabilizer of reflection characteristics.
 제1항에 있어서,
상기 UV 안정제는 HALS(Hindered Amine Light Stabilizer)계 안정제를 포함하는 것을 특징으로 하는 폴리올레핀계 필름 조성물.
According to claim 1,
The UV stabilizer is a polyolefin-based film composition comprising a HALS (Hindered Amine Light Stabilizer)-based stabilizer.
 제2 폴리올레핀계 수지로 이루어진 베이스 필름; 및
상기 베이스 필름의 일면에 연속하여 형성되고, 제1항의 필름 조성물로 이루어진 단위 필름이 다중으로 적층되어 형성됨으로써 다층 구조를 갖는,
데코시트용 폴리올레핀계 다중필름.
a base film made of a second polyolefin-based resin; and
It is continuously formed on one surface of the base film, and has a multilayer structure by forming a unit film made of the film composition of claim 1 by laminating multiple,
Polyolefin-based multi-film for decorative sheets.
 시트의 적어도 일부 층상 영역에 제5항의 폴리올레핀계 다중필름을 포함하는 고내후성 데코시트.






A high-weather-resistant decorative sheet comprising the polyolefin-based multi-film of claim 5 in at least a portion of the layered region of the sheet.
KR1020200023067A 2020-02-25 2020-02-25 Polyolefin based film compoistion and decoration sheet of high weather-proof comprising the same KR102380387B1 (en)