KR101691487B1 - Functional Composition for Pipe - Google Patents

Functional Composition for Pipe Download PDF

Info

Publication number
KR101691487B1
KR101691487B1 KR1020160058798A KR20160058798A KR101691487B1 KR 101691487 B1 KR101691487 B1 KR 101691487B1 KR 1020160058798 A KR1020160058798 A KR 1020160058798A KR 20160058798 A KR20160058798 A KR 20160058798A KR 101691487 B1 KR101691487 B1 KR 101691487B1
Authority
KR
South Korea
Prior art keywords
resin
functional composition
weight
water
powder
Prior art date
Application number
KR1020160058798A
Other languages
Korean (ko)
Inventor
허재원
Original Assignee
주식회사 용전
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 용전 filed Critical 주식회사 용전
Priority to KR1020160058798A priority Critical patent/KR101691487B1/en
Application granted granted Critical
Publication of KR101691487B1 publication Critical patent/KR101691487B1/en

Abstract

Disclosed is a functional composition applied on a water and sewage pipe. According to an embodiment of the present invention, the functional composition applied on a water and sewage pipe comprises a resin, and bony coal powder, toreumallin powder and nontoxic stabilizer as additives. The stabilizer comprises magnesium aluminum hydroxy carbonate, zinc stearate, calcium stearate, stearic acid, polyethylene, a hydrocarbon mixture, and a fatty acid ester mixture. According to the present invention, the composition can adsorb harmful materials such as chlorine, trihalomethane, etc. included in supplied water in a water and sewage pipe.

Description

상하수관에 도포되는 기능성 조성물{Functional Composition for Pipe}Functional Composition for Pipe "

개시되는 발명은 상하수관에 도포되는 기능성 조성물에 관한 것으로서, 더욱 상세하게는 상,하수도관의 내벽면에 도포되어 잔류 염소 등의 유해물질을 제거하도록 하는 기능성 조성물에 관한 것이다.
The present invention relates to a functional composition applied to an upper drainage pipe, and more particularly to a functional composition which is applied to an inner wall surface of a sewage pipe to remove harmful substances such as residual chlorine.

유체가 흐르는 파이프, 특히 수도관은 수질 정화 및 살균 등이 제대로 이루어지지 않아 수질 오염이 심각한 문제로 대두되고 있다. Water pipes, especially water pipes, are not properly cleaned and sanitized, and water pollution is becoming a serious problem.

그런데 이 같은 수질 오염을 방지하기 위하여, 염소(cl)의 양을 늘리는 방식으로 소독 살균에 중점을 두기 때문에, 잔류하는 염소로부터 발암성 물질인 트리할로메탄(trihalomethane)이 생성하게 되어 큰 사회 문제가 되고 있다. However, in order to prevent such water pollution, since the amount of chlorine (cl) is increased to focus on disinfection and disinfection, trihalomethane, which is a carcinogenic substance, is generated from residual chlorine, .

이에 따라, 소비자는 여러 가지의 정수기나 정수 장치를 설치하거나, 상대적으로 안전하다고 여겨지는 물을 구입하여 사용하고 있는 실정이다.Accordingly, consumers have installed various water purifiers or water purification devices, or have purchased water that is considered to be relatively safe.

한편 국내 특허출원 10-2012-0076546호 "상수도용 파이프"가 개시되어 있다. On the other hand, Korean Patent Application No. 10-2012-0076546 "Pipes for Waterworks" is disclosed.

상기 선행기술은 내부 벽면에 기능성 조성물이 균일하게 도포되도록 제조된 것으로, 내부 벽면에 기능성 조성물이 분사되어 부착되므로 기능성 조성물이 뭉치지 않고 고르게 도포될 수 있어 기능성 조성물의 특성을 제대로 발휘할 수 있도록 한 것과 관련된다. The prior art is prepared so that the functional composition is uniformly applied to the inner wall surface, and the functional composition is sprayed on the inner wall surface, so that the functional composition can be uniformly applied without aggregation, do.

한편 종래 기술은 기능성 조성물의 효과가 안정적으로 제공되지 않고, 지속적으로 유지될 수 없어 기대에 못미치는 단점이 있었다.
On the other hand, the prior art has a disadvantage that the effect of the functional composition is not stably provided and can not be maintained continuously, which is inferior to the expectation.

국내 특허출원 10-2012-0076546호.Korean Patent Application No. 10-2012-0076546. 국내 특허출원 10-2012-0052965호.Korean Patent Application No. 10-2012-0052965.

개시되는 발명에서는 유익한 기능이 지속적으로 장기간 유지될 수 있도록 하기 위한 것으로, 레진을 기반으로 하여 토르말린, 경탄 및 무독성 안정제로 이루어지는 상하수관에 도포되는 기능성 조성물을 제공하고자 한다.
The present invention aims at providing a functional composition applied to an upper drainage pipe made of tourmaline, a waxy and non-toxic stabilizer based on a resin so that beneficial functions can be continuously and prolonged for a long time.

개시되는 실시예의 목적은, 상,하수도관에 도포되는 것으로, 레진과, 첨가제로서 경탄 분말, 토르말린 분말 및 무독성 안정제를 포함하는 기능성 조성물에 의해 달성될 수 있다.The object of the disclosed embodiment can be achieved by a functional composition comprising a resin, a lightening powder as an additive, a tourmaline powder and a non-toxic stabilizer, which is applied to an upper and a drainage pipe.

상기 안정제는 마그네슘 알루미늄 하이드록시 탄소산염, 스테아린산 아연, 스테아린산 칼슘, 스테아린 산, 폴리에틸렌, 하이드로카본 혼합물, 지방산 에스테르 혼합물을 포함하는 것을 특징으로 한다.
The stabilizer is characterized by containing a magnesium aluminum hydroxy carbonate, zinc stearate, calcium stearate, stearic acid, polyethylene, a hydrocarbon mixture, and a fatty acid ester mixture.

개시된 실시예에 따르면, 상,하수도관용 파이프 내의 공급되는 물에 포함되어 있는 염소, 트리할로메탄 등의 유해물질을 흡착하여 제거할 수 있는 효과가 있다.
According to the disclosed embodiment, it is possible to adsorb and remove harmful substances such as chlorine, trihalomethane and the like contained in the water supplied in the upper and the drain pipes.

도 1 내지 도 3은 일 실시예에 따른 기능성 조성물이 도포된 상,하수도관을 나타낸 단면도.BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is a cross-sectional view of a sewage pipe with a functional composition applied thereto according to an embodiment; FIG.

이하, 첨부된 도면을 참조하여 바람직한 실시예들을 상세히 설명한다. 이때 첨부된 도면에서 동일한 구성 요소는 가능한 동일한 부호로 나타내고 있음에 유의하여야 한다. 또한 본 발명의 요지를 흐리게 할 수 있는 공지 기능 및 구성에 대한 상세한 설명은 생략할 것이다. Hereinafter, preferred embodiments will be described in detail with reference to the accompanying drawings. It should be noted that the same components are denoted by the same reference numerals as possible in the accompanying drawings. Further, the detailed description of well-known functions and constructions that may obscure the gist of the present invention will be omitted.

또한 이하에서 설명되는 본 명세서 및 청구범위에 사용된 용어나 단어는 통상적이거나 사전적인 의미로 한정해서 해석되어서는 아니 되며, 발명자는 그 자신의 발명을 가장 최선의 방법으로 설명하기 위해 용어의 개념으로 적절하게 정의할 수 있다는 원칙에 입각하여 본 발명의 기술적 사상에 부합하는 의미와 개념으로 해석되어야만 한다.
Also, the terms and words used in the present specification and claims should not be construed to be limited to ordinary or dictionary meanings, and the inventor is not limited to the concept of terms in order to describe his invention in the best way. It should be construed in accordance with the meaning and concept consistent with the technical idea of the present invention based on the principle that it can be properly defined.

개시되는 실시예에 적용되는 상,하수도관은 합성수지, 금속, 세라믹 등의 소재로 형성되며, 상,하수도관의 내벽에 기능성 조성물이 도포된다. The upper and the sewer pipes used in the disclosed embodiments are made of synthetic resin, metal, ceramic, or the like, and the functional composition is applied to the inner walls of the upper and the lower water pipes.

상기 기능성 이라 함은 정화성, 항균성, 탈취성을 포함하는 의미로서 정의되어진다. The term " functional " is defined as meaning including purifying property, antibacterial property, and deodorizing property.

따라서 개시되는 실시예에서 언급하고 있는 기능성은, 레진에 첨가제로서 경탄 분말, 토르말린 분말 및 무독성 안정제를 포함하는 것으로 이해되어져야 한다.
Thus, the functionality referred to in the disclosed embodiments should be understood to include light powders, tourmaline powders and non-toxic stabilizers as additives to the resin.

한편, 청구범위를 포함하는 본 명세서에서, "첨가제로 포함한다"는 것의 의미는 레진보다 실질적으로 적은 양으로 포함한다는 의미이면서 또한 전술하는 바의 기능성을 나타낼 수 있을 만큼의 양으로 포함한다는 의미로서 정의될 수 있다. 여기서 "레진보다 실질적으로 적은 양"이란 레진과 첨가제의 통상적인 비율을 넘어서지 않는 양으로 정의될 수 있다.On the other hand, in the present specification including the claims, the meaning of "comprising as an additive" means that the resin is contained in a substantially smaller amount than the resin, and that the resin is contained in an amount sufficient to exhibit the above- Can be defined. Here, "substantially less amount of resin" can be defined as an amount not exceeding the conventional ratio of resin and additive.

당업자라면 본 출원의 출원시를 기준으로 당업계에 공지된 기술과 본 발명의 하기 실시예 및 실험예에 기초하는 한 그의 통상의 능력 범위 내에서 전술하는 바의 기능성을 나타낼 수 있는(그 기능성의 정도에 있어서는 차이는 있더라도) 제조에 적합한 레진과 첨가제의 비율을 결정할 수 있을 것이다.
Those skilled in the art will appreciate that, based on the time of the filing of the present application, those skilled in the art will be able to demonstrate the foregoing functionality within the scope of ordinary skill in the art based on techniques known in the art and the following Examples and Experimental Examples of the invention The ratio of the resin and additive suitable for manufacture may be determined.

예컨데, 개시되는 실시예에 따르면, 상하수관에 도포되는 기능성 조성물에 있어서, 레진 100 중량부를 기준으로 하여 경탄 분말 2~5 중량부, 토르말린 분말 26~35 중량부, 안정제 3~5 중량부를 포함하는 것이다.For example, according to the disclosed embodiment, a functional composition applied to an upper sewer pipe comprises 2 to 5 parts by weight of a light powder, 26 to 35 parts by weight of a tourmaline powder, and 3 to 5 parts by weight of a stabilizer based on 100 parts by weight of the resin will be.

상기 레진은 멜라민수지, 수용성 우레탄 수지, 아크릴수지, 요소 수지, 글리옥살 수지로 이루어지는 군에서 택일된다. The resin is selected from the group consisting of a melamine resin, a water-soluble urethane resin, an acrylic resin, a urea resin, and a glyoxal resin.

경탄은 암석질 부분으로 거의 이루어지되 석탄질 부분이 매우 적고, 석탄과 비교하면 휘발분, 고정 탄소가 적고 회분이 매우 많다. 숯의 일종에 해당된다. The wonderland is almost made up of rocky parts, with very few coalous parts, less volatile and fixed carbon than coal, and a lot of ash. It is a type of charcoal.

토르말린은 일명 전기석으로 불리우며, 수정과 같은 결정구조를 가지는 육방정계에 속하는 광물이다. Tourmaline is called a tourmaline and is a mineral belonging to the hexagonal system with crystalline structure like crystal.

토르말린(tourmaline)은 음 이온(minus Ion) 방출 효과를 강력하고, 물을 순간적으로 정화하는 효과가 있다. Tourmaline has a powerful minus ion emission effect, and has the effect of instantly purifying water.

즉, 전기석(tourmaline)은 영구적으로 마이너스 이온(minus Ion)이나 정전기를 방출하고 계속하는 특성이 있고, 상기 마이너스 이온(minus Ion)이 건강을 증진하고 유지하다고 잘 알려져 있다. In other words, it is well known that tourmaline permanently emits minus ions or static electricity, and that the minus ions maintain and maintain health.

전기석은 특히, 물의 존재하는 곳에서 수압이 걸리는 곳에서 그 특성이 현저하다는 것을 주지의 사실이다.It is well known that tourmaline is remarkable in particular where water pressure is present in the presence of water.

토르말린(tourmaline)은 물에 접촉하는 순간에 전기분해를 일으키고, 대량의 정전기인 마이너스 이온(minus Ion)을 방출한다. 또한 4~14㎛의 원적외선 방사 효과에 인하고 물의 분자를 세분화하고, 인간의 혈액 또는 체액의 건강에 있어서 최상의 조건이라고 알려진 약 pH 7.5의 약한 알칼리수로 정제한다. Tourmaline causes electrolysis at the moment of contact with water and releases a large amount of static electricity minus ions. It is further purified by weak alkaline water of about pH 7.5, which is known as the best condition for the health of human blood or body fluids, by subdividing the molecules of water by the far infrared radiation effect of 4 ~ 14 ㎛.

나아가 염소를 흡착하여 분해하기 때문에, 염소 처리된 유체의 염소량을 줄이고 염소 살균의 폐해를 줄일 수 있다.
Furthermore, since chlorine is adsorbed and decomposed, the amount of chlorine in the chlorinated fluid can be reduced, and the harmful effect of chlorine sterilization can be reduced.

한편 상기 안정제는, 마그네슘 알루미늄 하이드록시 탄소산염, 스테아린산 아연, 스테아린산 칼슘, 스테아린 산, 폴리에틸렌, 하이드로카본 혼합물, 지방산 에스테르 혼합물을 포함하여 이루어지는 것이다. On the other hand, the stabilizer includes a magnesium aluminum hydroxy carbonate, zinc stearate, calcium stearate, stearic acid, polyethylene, a hydrocarbon mixture, and a fatty acid ester mixture.

일 실시예에 따르면, 상기 안정제는, 마그네슘 알루미늄 하이드록시 탄소산염 30~45 중량%, 스테아린산 아연 20~30 중량%, 스테아린산 칼슘 10~15 중량%, 스테아린 산 1~5 중량%, 폴리에틸렌 10~20 중량%, 하이드로카본 혼합물 1~3 중량%, 지방산 에스테르 혼합물 1~3 중량%를 포함하여 이루어진다.
According to one embodiment, the stabilizer is selected from the group consisting of 30-45 wt% magnesium aluminum hydroxycarbonate, 20-30 wt% zinc stearate, 10-15 wt% calcium stearate, 1-5 wt% stearic acid, 10-20 wt% polyethylene 1 to 3% by weight of a hydrocarbon mixture, and 1 to 3% by weight of a fatty acid ester mixture.

도 1에 나타낸 바와 같이, 개시된 발명에 따른 기능성 조성물은 상,하수도관(100)의 내벽에 일정 두께의 층상으로 형성된다. 이를 분말층(200)이라 한다. As shown in FIG. 1, the functional composition according to the disclosed invention is formed as a layer having a certain thickness on the inner wall of the sewage pipe 100. This is referred to as a powder layer 200.

또는 도 2에 나타낸 바와 같이, 개시된 발명에 따른 기능성 조성물은 상,하수도관(100)의 내벽에 반구 형상으로 부분적으로 형성될 수 있다. 이를 분말도트(300)라 한다. Alternatively, as shown in FIG. 2, the functional composition according to the disclosed invention may be partially formed in a hemispherical shape on the inner wall of the sewage pipe 100. This is referred to as a powder dot 300.

또는 도 3에 나타낸 바와 같이, 개시된 발명에 따른 기능성 조성물은 상,하수도관(100)의 내벽에 일정 두께의 층상으로 형성되되 요부와 철부로 이루어지고 나사산 형상으로 이루어질 수 있다. 이를 가이드베인층(400)이라 한다. 3, the functional composition according to the disclosed invention is formed as a layer having a predetermined thickness on the inner wall of the sewage pipe 100, and may be formed into a thread-like shape, which is composed of a main portion and a convex portion. This is referred to as a guide vane layer 400.

상기 가이드베인층(400)은 나사산 형상으로 형성됨으로써 물이 흐를때 와류를 형성할 수 있게 되고, 요부와 철부에 의해 보다 물과의 접속시칸이 길어지게 되고, 아울러 물의 회전력을 부가함으로써 기능성 조성물이 보다 용이하면서 신속하게 물속에 용융될 수 있게 된다.
The guide vane layer 400 is formed in a threaded shape so that a vortex can be formed when water flows. The guide vane layer 400 has a longer length when connected with water by the recessed portion and the convex portion, So that it can be melted in water more easily and quickly.

전술한 분말층(200), 분말도트(300), 가이드베인층(400)은 모두 기능성 조성물이 경화되어 형성되는 것이므로 고체 분말로서 정의된다.
The powder layer 200, the powder dot 300, and the guide vane layer 400 described above are all defined as a solid powder because the functional composition is formed by curing.

한편, 개시되는 실시예에 따른 기능성 조성물이란 경탄과 토르말린을 주성분으로 하는 레진이며, 최초 배합시에는 점성을 갖는 액상이지만 대상면에 도포된 후 일정시간 경과후에는 단단하게 경화된 층을 형성하게 된다.
On the other hand, the functional composition according to the disclosed embodiment is a resin containing chrysanthemum and tourmaline as a main component, which is a liquid having a viscosity at the time of initial mixing, but forms a hardened layer after a certain period of time after being applied to the object surface .

한편, 전술한 바의 기능성의 관점에 봤을 때, 하기 실험예가 보여주는 바와 같이, 개시되는 실시예에 따른 기능성 조성물에는 레진에 경탄 분말과 토르말린 분말이 모두 포함되는 것이 바람직하다.
From the viewpoint of the above-mentioned functionalities, as shown in the following experimental examples, it is preferable that the functional composition according to the disclosed embodiment contains both a light powder and a tourmaline powder in the resin.

상기에서 개시되는 실시예에 따른 기능성 조성물은 경탄 분말, 토르말린 분말이 포함될 때, 그것들 중 한 가지 성분이 포함되든지, 두 가지 성분이 포함되든지를 불문하고, 그것들이 레진과의 배합량은 하기 실시예 및 실험예가 보여주듯이 레진 100 중량부를 기준으로 하여 경탄 분말 2~5 중량부, 토르말린 분말 26~35 중량부, 안정제 3~5 중량부인 것이 바람직하다. The functional composition according to the above-described embodiments is characterized in that when blended powders, tourmaline powders are included, whether they contain one of them, or whether they contain two components, It is preferable that 2 to 5 parts by weight of lightening powder, 26 to 35 parts by weight of tourmaline powder and 3 to 5 parts by weight of stabilizer are based on 100 parts by weight of resin.

이때 경탄 분말이 2 중량부 이하인 경우 효능 효과의 확신이 힘들며 저 점도에 따른 경시 변화시의 안정성을 유지하기 힘든 단점이 있고, 5 중량부 이상인 경우에는 혼합이 힘든 페이스트 상으로 품질의 균일성과 과다한 함량의 사용에 따른 안전상의 단점이 있다. At this time, when the light weight powder is less than 2 parts by weight, it is difficult to assure the efficacy and it is difficult to maintain the stability at the time of aging according to the low viscosity. When the light weight powder is more than 5 parts by weight, the uniformity of quality, There is a disadvantage in terms of safety as a result of the use thereof.

또한 토르말린 분말이 26 중량부 이하인 경우 효능 효과의 확신이 힘들며 저 점도에 따른 경시 변화시의 안정성을 유지하기 힘든 단점이 있고, 35 중량부 이상인 경우에는 혼합이 힘든 페이스트 상으로 품질의 균일성과 과다한 함량의 사용에 따른 안전상의 단점이 있다. When the amount of the tourmaline powder is less than 26 parts by weight, it is difficult to confirm the efficacy of the composition and it is difficult to maintain stability at the time of aging due to low viscosity. When the amount of the tourmaline powder is more than 35 parts by weight, There is a disadvantage in terms of safety as a result of the use thereof.

가장 바람직하게는 레진 100kg 기준으로 경탄 분말은 3kg, 토르말린 30kg, 안정제 4kg으로 포함되는 경우이다. 그 이유는 하기 실시예 및 실험예에서 확인할 수 있다.
Most preferably, the lightening powder is contained in an amount of 3 kg, 30 kg of tourmaline and 4 kg of stabilizer based on 100 kg of resin. The reason can be confirmed in the following examples and experimental examples.

한편, 개시되는 실시예에 따른 기능성 조성물에 포함되는 레진으로서는, 그것이 첨가제로서 포함되는 경탄 분말, 토르말린 분말이 전술한 바의 기능성을 나타내는 것을 방해하지 않는다면, 의도하는 용도에 따라 당업계에 공지된 임의의 수지를 사용할 수 있다.On the other hand, as the resin included in the functional composition according to the disclosed embodiment, it is possible to use any of the resins known in the art depending on the intended use, as long as it does not interfere with the performance of the lighten powder or the tourmaline powder, Can be used.

예컨대 레진은 멜라민수지, 수용성 우레탄 수지, 아크릴수지, 요소 수지, 글리옥살 수지로 이루어지는 군에서 택일될 수 있다. For example, the resin may be selected from the group consisting of a melamine resin, a water-soluble urethane resin, an acrylic resin, a urea resin, and a glyoxal resin.

또한 레진은 내열성능을 충족시키는 것이 바람직하다. 즉 파이프 압출시 파이프의 열을 견디면서 기능성 조성물이 부착되어야 하므로 내열성능을 갖는 것이어야 한다.
It is also preferable that the resin satisfies the heat resistance performance. That is, when the pipe is extruded, the functional composition must be adhered to the pipe while being able to withstand the heat of the pipe.

이와 같이 구성되는 실시예의 작용을 설명하면 다음과 같다. Hereinafter, the operation of the embodiment will be described.

기능성 조성물을 파이프가 압출되는 과정에서 동시에 압축시키는 것으로, 파이프의 내벽면에 형성됨으로써 기능성 조성물이 흐르는 물에 노출되도록 하여 기능성 조성물의 특성을 제대로 발휘하게 하고, 기능성 조성물이 뭉치는 것을 방지할 수 있다.
The functional composition is simultaneously compressed in the process of extruding the pipe so that the functional composition is exposed to the flowing water by being formed on the inner wall surface of the pipe so that the properties of the functional composition can be exhibited properly and the functional composition can be prevented from being aggregated .

이하 몇가지 실시예를 참조하여 설명한다. 그러나 이러한 실시예가 본 발명의 범위를 제한하는 것은 아니다.
The following description will be made with reference to several embodiments. However, these examples do not limit the scope of the present invention.

<실시예> 기능성 조성물의 제조
EXAMPLES Preparation of functional compositions

<실시예 1> 기능성 조성물의 제조예 1Example 1 Production of Functional Composition Example 1

시중에 유통되는 레진 100kg에 경탄 3kg, 토르말린 30kg, 안정제 4kg을 혼합한다. 100 kg of commercially available resin is mixed with 3 kg of bright coal, 30 kg of tourmaline and 4 kg of stabilizer.

안정제는 4kg은, 마그네슘 알루미늄 하이드록시 탄소산염 1.64kg, 스테아린산 아연 1kg, 스테아린산 칼슘 0.52kg, 스테아린 산 0.08kg, 폴리에틸렌 0.6kg, 하이드로카본 혼합물 0.08kg, 지방산 에스테르 혼합물0.08kg을 혼합하여 제조하였다.
4 kg of stabilizer was prepared by mixing 1.64 kg of magnesium aluminum hydroxycarbonate, 1 kg of zinc stearate, 0.52 kg of calcium stearate, 0.08 kg of stearic acid, 0.6 kg of polyethylene, 0.08 kg of a hydrocarbon mixture and 0.08 kg of a fatty acid ester mixture.

<실시예 2> 기능성 조성물의 제조예 2&Lt; Example 2 > Preparation of functional composition Example 2

시중에 유통되는 레진 100kg에 경탄 4kg, 토르말린 40kg, 안정제 5kg을 혼합한다. 100 kg of commercially available resin is mixed with 4 kg of scorching, 40 kg of tourmaline and 5 kg of stabilizer.

안정제는 5kg은, 마그네슘 알루미늄 하이드록시 탄소산염 1.9kg, 스테아린산 아연 1.34kg, 스테아린산 칼슘 0.7kg, 스테아린 산 0.1kg, 폴리에틸렌 0.72kg, 하이드로카본 혼합물 0.12kg, 지방산 에스테르 혼합물0.12kg을 혼합하여 제조하였다.
5 kg of the stabilizer was prepared by mixing 1.9 kg of magnesium aluminum hydroxy carbonate, 1.34 kg of zinc stearate, 0.7 kg of calcium stearate, 0.1 kg of stearic acid, 0.72 kg of polyethylene, 0.12 kg of a hydrocarbon mixture and 0.12 kg of a fatty acid ester mixture.

<실시예 3> 기능성 조성물의 제조예 3Example 3 Production of Functional Composition Example 3

시중에 유통되는 레진 100kg에 경탄 5kg, 토르말린 60kg, 안정제 4kg을 혼합한다. 100 kg of commercially available resin is mixed with 5 kg of agar, 60 kg of tourmaline and 4 kg of stabilizer.

안정제는 4kg은, 마그네슘 알루미늄 하이드록시 탄소산염 1.64kg, 스테아린산 아연 1kg, 스테아린산 칼슘 0.52kg, 스테아린 산 0.08kg, 폴리에틸렌 0.6kg, 하이드로카본 혼합물 0.08kg, 지방산 에스테르 혼합물0.08kg을 혼합하여 제조하였다.
4 kg of stabilizer was prepared by mixing 1.64 kg of magnesium aluminum hydroxycarbonate, 1 kg of zinc stearate, 0.52 kg of calcium stearate, 0.08 kg of stearic acid, 0.6 kg of polyethylene, 0.08 kg of a hydrocarbon mixture and 0.08 kg of a fatty acid ester mixture.

<실험예> 실시예 1 내지 실시예 3에 따른 기능성 조성물의 정화 효과, 항균효과 실험<Experimental Example> Purification effect and antibacterial effect test of the functional composition according to Examples 1 to 3

pHpH 트리할로메탄 제거율Trihalomethane removal rate 테트라클로라이드 제거율Tetrachloride removal rate 실시예 1Example 1 7.17.1 60~62%60 to 62% 40~42%40 to 42% 실시예 2Example 2 7.37.3 65~68%65 to 68% 43~45%43 to 45% 실시예 3Example 3 7.57.5 78~80%78 to 80% 46~48%46-48%

상기 <표 1>에서 확인되는 바와 같이, 토르말린 함량이 높은 <실시예 3>의 기능성 조성물의 경우 원수의 알칼리도를 높이고, 트리할로메탄 및 테트라클로라이드의 제거율이 높아지므로 향상된 정화효과를 가지고 있음을 알 수 있다.
As can be seen from the above Table 1, the functional composition of Example 3 having a high content of tourmaline has an enhanced purifying effect because it enhances alkalinity of raw water and increases the removal efficiency of trihalomethane and tetrachloride Able to know.

<실험예> 실시예 1 내지 실시예 3에 따른 기능성 조성물의 항균 효과 실험<Experimental Example> Antibacterial effect test of functional composition according to Examples 1 to 3

항균성은 대장균(Escherichia coli)과 녹농균(Pseudomonas aeruginosa)을 사용하여 평가하였다. 항균성은 박테리아 감소율로서 평가하였다. Antimicrobial activity was evaluated using Escherichia coli and Pseudomonas aeruginosa. The antimicrobial activity was evaluated as the bacterial reduction rate.

용기에 각 미생물의 배양액 0.5㎖(각 배양액은 대장균 10 /㎖와 녹농균 10 /㎖를 포함함)를 기능성 조성물에 접종한 다음 24 시간 동안 상온에서 방치한 후에 생균수를 계수하여 박테리아 감소율을 산출하여 하기 <표 2>에 나타내었다.The functional composition was inoculated in a container with 0.5 ml of the culture solution of each microorganism (each culture solution contained 10 / ml of Escherichia coli and 10 / ml of Pseudomonas aeruginosa) and allowed to stand at room temperature for 24 hours. Then, the viable cell count was counted to calculate the bacterial reduction rate Table 2 shows the results.

감소율의 부호가 마이너스인 것은 박테리아의 증가를 의미한다.The minus sign of the rate of decrease implies an increase in bacteria.

대장균Escherichia coli 녹농균P. aeruginosa 실시예 1Example 1 37~39%37 to 39% 31~33%31 to 33% 실시예 2Example 2 24~26%24-26% 21~23%21-23% 실시예 3Example 3 30~31%30 to 31% 18~20%18-20%

상기 <표 2>의 결과는 <실시예 3>의 기능성 조성물은 항균성을 갖고 있음을 보여준다.
The results of Table 2 show that the functional composition of Example 3 has antimicrobial activity.

이상, 첨부된 도면을 참조하여 본 고안의 실시 예들을 설명하였지만, 본 고안이 속하는 기술분야에서 통상의 지식을 가진 자는 본 고안이 그 기술적 사상이나 필수적인 특징을 변경하지 않고서 다른 구체적인 형태로 실시될 수 있다는 것을 이해할 수 있을 것이다. 그러므로 이상에서 기술한 실시 예들은 모든 면에서 예시적인 것이며 한정적이 아닌 것으로 이해해야만 한다.
While the embodiments of the present invention have been described with reference to the accompanying drawings, those skilled in the art will appreciate that various modifications, additions and substitutions are possible, without departing from the scope and spirit of the invention as disclosed in the accompanying claims. It will be understood. It is therefore to be understood that the above-described embodiments are illustrative in all aspects and not restrictive.

100 : 상,하수도관 200 : 분말층
300 : 분말도트 400 : 가이드베인층100: phase, sewer pipe 200: powder layer
300: powder dot 400: guide vane layer

Claims (10)

상,하수관에 도포되는 기능성 조성물에 있어서,
레진 100 중량부를 기준으로 하여 경탄 분말 2~5 중량부, 토르말린 분말 26~35 중량부, 안정제 3~5 중량부를 포함하여 이루어지되,
상기 레진은 멜라민수지, 수용성 우레탄 수지, 아크릴수지, 요소 수지, 글리옥살 수지로 이루어지는 군에서 택일되며,
상기 안정제는 마그네슘 알루미늄 하이드록시 탄소산염 30~45 중량%, 스테아린산 아연 20~30 중량%, 스테아린산 칼슘 10~15 중량%, 스테아린 산 1~5 중량%, 폴리에틸렌 10~20 중량%, 하이드로카본 혼합물 1~3 중량%, 지방산 에스테르 혼합물 1~3 중량%을 포함하는 혼합물임을 특징으로 하는 상,하수관에 도포되는 기능성 조성물.In the functional composition applied to the upper and the sewer pipes,
2 to 5 parts by weight of lightening powder, 26 to 35 parts by weight of tourmaline powder and 3 to 5 parts by weight of stabilizer based on 100 parts by weight of resin,
The resin is selected from the group consisting of melamine resin, water-soluble urethane resin, acrylic resin, urea resin, and glyoxal resin,
Wherein the stabilizer is selected from the group consisting of 30-45 wt% magnesium aluminum hydroxycarbonate, 20-30 wt% zinc stearate, 10-15 wt% calcium stearate, 1-5 wt% stearic acid, 10-20 wt% polyethylene, To 3% by weight of a fatty acid ester, and 1 to 3% by weight of a fatty acid ester mixture. 삭제delete 삭제delete 삭제delete 삭제delete 상기 제1항의 상,하수도관에 도포되는 기능성 조성물을 이용하여 상,하수도관의 내벽에 소정의 두께를 갖는 분말층을 형성하여서 이루어짐을 특징으로 하는 상,하수도관 형성구조.And a powder layer having a predetermined thickness is formed on the inner wall of the sewage pipe by using the functional composition applied to the upper and the sewer pipes of the first aspect. 상기 제1항의 상,하수도관에 도포되는 기능성 조성물을 이용하여 상,하수도관의 내벽에 반구 형상으로 부분적으로 형성되는 분말도트를 형성하여서 이루어짐을 특징으로 하는 상,하수도관 형성구조.Wherein the powdered dots are partially formed in a hemispherical shape on the inner wall of the sewage pipe by using the functional composition applied to the upper and the sewage pipes of the first aspect of the present invention. 상기 제1항의 상,하수도관에 도포되는 기능성 조성물을 이용하여 상,하수도관의 내벽에 일정 두께의 층상으로 형성하되,
요부와 철부로 이루어지고 나사산 형상으로 이루어지는 가이드베인층으로 형성하여서 이루어짐을 특징으로 하는 상,하수도관 형성구조.A functional composition applied to the upper and the sewage pipes of claim 1 is used to form a layer having a certain thickness on the inner wall of the sewage pipe,
And a guide vane layer formed of a recessed portion and a convex portion and formed in a threaded shape. 삭제delete 삭제delete
KR1020160058798A 2016-05-13 2016-05-13 Functional Composition for Pipe KR101691487B1 (en)