KR100950999B1 - Health aticle comprising a far-infrared radiative composition containing the montmorillonite - Google Patents

Abstract

The present invention removes impurities precipitated by dissolving montmorillonite in water, followed by aging and agitation for 2 to 4 days in a bubble bath equipped with a bubble generator maintained at 40 to 60 ° C. to incubate live bacteria as aerobic microorganisms, The culture was dried at a temperature of 40-60 ° C., and then 94-99.9% by weight of 1000-1200 mesh montmorillonite powder sterilized at -40--45 ° C. and 0.1-6% by weight of 1000-1200 mesh titanium oxide. It relates to a health product comprising a far-infrared radiation composition containing montmorillonite.

The present invention by using the montmorillonite powder to improve the absorption and deodorizing power of the existing products such as diapers to improve the skin sores, and can remove the anion generated from the montmorillonite powder, and the fishy odor generated in the urine or body secretions It has an effect.

Montmorillonite, Titanium Oxide, Diapers, Pads, Far Infrared

Description

Health product containing far-infrared radiation composition containing montmorillonite {Health aticle comprising a far-infrared radiative composition containing the montmorillonite}

The present invention relates to a health product comprising a far-infrared radiation composition containing montmorillonite, and more specifically, to montmorillonite and titanium oxide powder which emits far infrared rays and anions, and contains antibacterial power, deodorizing power, and a large amount of minerals. A health product comprising a constructed far infrared radiation composition.

Far-infrared rays are electron waves whose radiation and radiation wavelengths are about several micrometers to about 400 micrometers, and are excellent in a heating effect and a drying effect. For this reason, fibers having a far-infrared effect, in which a spinning agent is incorporated into the fiber or coated on the surface, or the spinning agent (or the absorbent) itself are embedded in diapers, health pads, bedding, clothing, or underwear. It is widely used.

For example, Patent Literature 1 impregnates zeolite and charcoal powder onto the compressed cotton of a diaper, and covers the outer circumferential surface with a good air permeability to increase sterilization effect and hygroscopicity by charcoal powder, and to keep the dry state for a long time. Disclosed is a charcoal-added diaper that prevents skin crushing during use.

However, products such as diapers are composed of a nonwoven fabric by adding charcoal powder and / or zeolite as absorbent material inside the compressed cotton. At this time, the absorbent amount of the absorbent material is about 2 to 5 times the volume, so the diaper can be absorbed. The amount of urine was very small. Therefore, when the infant wears the diaper for a long time, the skin becomes crushed, odor is generated and at the same time bacteria grow, causing various diseases, causing growth and other problems.

Patent Document 1: Korean Utility Model Application No. 1999-0028975

In the present invention, montmorillonite, a natural mineral, is aged to activate far-infrared rays, anions, antimicrobial activity, deodorizing power, and a large amount of minerals, and by mixing titanium oxide having an oxidizing ability of ozone with urine or a far-infrared radiation composition. Odors from body secretions could be adsorbed and oxidized.

Accordingly, an object of the present invention is to increase the absorption and deodorization power of diapers and / or pads by using montmorillonite having excellent deodorizing and absorbing power, and to remove the fishy odor generated from urine or body secretions by adding titanium oxide powder (TiO ₂ ). To provide a health product comprising a far-infrared radiation composition containing montmorillonite.

The health product comprising the far-infrared radiation composition containing the montmorillonite of the present invention for achieving the above object is dissolved in montmorillonite in water to remove impurities precipitated, and then in a tank with a bubble generator is maintained at 40 ~ 60 ℃ After aging and stirring for 4 days, aerobic microorganisms were cultured, and the culture was dried at a temperature of 40 to 60 ° C., and then sterilized at -40 to -45 ° C., montmorillonite of 1000 to 1200 mesh. Far-infrared radiation composition comprising 94 to 99.9% by weight of powder and 0.1 to 6% by weight of titanium oxide of 1000 to 1200 mesh.

In the health product comprising the far-infrared radiation composition of the present invention, the powder is characterized in that powdered by the air-flow grinding method.

In the health product comprising the far-infrared radiation composition of the present invention, the health product is characterized in that the diaper or pad.

The present invention by using the montmorillonite powder to improve the absorption and deodorizing power of the existing products such as diapers to improve the skin sores, and can remove the anion generated from the montmorillonite powder, and the fishy odor generated in the urine or body secretions It has an effect.

Looking at the present invention in more detail as follows.

Montmorillonite is a silicon mineral produced by volcanic activity of the Cretaceous Period, about 12 million years ago, which is beneficial to the human body such as chlorite, hornblende, titanium oxide, potassium, sodium, and aerobic microorganisms not found in amino acids and general minerals. Probiotics) and titanium oxides promote capillary expansion and blood circulation to help cell activation, boost immunity, and consequently help babies grow.

Far-infrared rays emitted from montmorillonite have a characteristic of being radiated at human body temperature of 37 ~ 37.5 ℃, unlike ocher which is emitted only at high temperature, and absorbed by human body, promoting metabolism and circulating blood with excellent deodorization and anion which activates cells. It is effective in preventing the aging of the human body and adsorbing the waste and harmful substances accumulated in the human body.

Montmorillonite promotes capillary expansion and blood circulation by negative ions, which helps cell activation and stabilizes the air with "air vitamin action", which helps to stabilize nerves and strengthen immune system. The far-infrared radiation of montmorillonite promotes blood circulation by radiation of far-infrared rays having a wavelength of 5 to 20㎛, and has excellent deodorizing and absorbing power, and the far-infrared radiation distribution is evenly distributed on either side and high thermal conductivity. Thus, as time passes, urine, sweat and / or blood may be evaporated with water vapor to further maximize moisturizing power.

Montmorillonite is better than any other mineral on earth with its ability to control moisture. Existing loess or minerals have a moisture absorption ratio of 1: 1, but montmorillonite has a ratio of about 1: 3, which is three times higher than that of ordinary powder. It has strong adsorption power and fine porous particles, which causes capillary phenomenon, which is very effective in adsorbing, decomposing and removing contaminants in the skin layer, various pollutants, various bacteria and heavy metals.

In the present invention, looking at the process of obtaining montmorillonite powder, first, the montmorillonite is dissolved in ordinary water to undergo a predetermined purification process to remove the precipitate. The montmorillonite thus purified is cultured in aerobic microorganisms through aging and stirring (about 500 to 1000 rpm) for about 2 to 4 days in a bubble bath equipped with a bubble generator maintained at 40 to 60 ° C. After the incubation, the culture is dried at a temperature of 40 ~ 60 ℃ to completely remove the moisture, and then ground to form a powder having a particle size of 1000 ~ 1200 mesh. The grinding method at this time is preferably an airflow grinding method, which is a grinding method by air so that impurities such as iron are not added, and the grinding particle size is preferably limited to 1000 to 1200 mesh. This is to compensate for the shortcomings of the conventional crushing grinding method. The disadvantage of crushing is that there is a risk that (iron) powder or other foreign matter may be generated during contact (friction) of the rod and the service member during the grinding process. Therefore, it was possible to prevent the occurrence of iron and foreign matters by using airflow pulverization method using air pressure instead of friction or contact method with each other. It is preferable to. On the other hand, when the aging temperature is less than 40 ℃ microbial growth is slow, if it exceeds 60 ℃ microbial growth is very disappeared to maintain a 40 to 60 ℃ to obtain aerobic microorganisms. This pulverized powder is subjected to a sterilization process for the stability of the product, it is preferable that the sterilization process at -40 ~ -45 ℃ does not destroy the produced enzyme.

In this pretreated montmorillonite powder, about 800,000 aerobic microorganisms (probiotics) per 1g, which are beneficial to the human body, not found in ocher or any other minerals, are multiplied, and the enzymes they produce include catalase and diphenoloxadiase. Enzymes such as saccharase and protease exist, and the catalase enzyme is known to be more excellent in hydrogen peroxide and lipid peroxidation and detoxification which are causes of aging.

The present invention can be prepared by mixing 94 to 99.9% by weight of the montmorillonite powder thus obtained and 0.1 to 6% by weight of titanium oxide powder to the absorbent layer (usually compressed cotton) of products such as conventional diapers or pads to prepare a diaper or pad have.

Referring to FIG. 1, a diaper according to an embodiment of the present invention includes a filter sheet layer 10 through which moisture such as urine, blood, and sweat pass directly, and a dry sheet layer 20 for detoxifying bacteria such as ammonia and mold. , Absorbing sheet layer 30 that emits far infrared rays and / or anions, a water-repellent waterproof sheet layer 40 which does not leak sweat / blood as residual moisture, but passes air, and a label that is adhered to or adhered to the fabric of clothes It consists of the sheet layer 50.

The absorbent sheet layer 30 may further maximize the moisturizing power by evaporating urine, sweat, and / or blood in a vapor state using the skin warming effect of montmorillonite. In addition, the montmorillonite powder 60 having a particle size of 1000 to 1200 mesh is processed and added to and / or impregnated into the dry sheet layer 20 and / or the absorbent sheet layer 30 to remove ammonia odors and mold bacteria and release anions. By helping blood circulation, cell activation, immune function.

On the other hand, O ₃ (ozone) released together with the anion emanating from the existing loess or natural minerals can not be good for the human body. Negative ions promote blood circulation, help cell activation, help immunity, and even help baby growth, but there are many side effects in which fishy smells occur due to the occurrence of O ₃ (ozone). Therefore, it was confirmed that addition of titanium oxide (TiO ₂ ) powder, which acts as a photocatalyst, prevented the release of ozone and eliminated the characteristic fishy smell.

According to the present invention, montmorillonite is rich in beneficial minerals of the human body and by adding titanium oxide (TiO ₂ ) to it, when it receives light (heat) on the same principle as the photosynthesis of plants, it causes a catalytic reaction to produce various harmful substances as harmless substances. It acts as a photocatalyst to oxidize and reduce. Maintain the titanium oxide powder in the total weight of 0.1 to 6% by weight. At this time, if the weight of the titanium oxide powder is less than 0.1% by weight, there is almost no effect of removing fishy odor. When the titanium oxide powder weight is 0.5 to 2% by weight, the most stable absorption and deodorizing power can be obtained.

As described above, there is a limit to the existing compression pad of the diaper or pad and the absorbent material inside the diaper or pad, so that when worn for a long time, the skin becomes soaked and bacteria grow. In the present invention, by releasing urine and sweat (blood) using the skin warming effect in the state of water vapor, the skin moisturizing power is increased, and the mineral powder particles into which the absorbent material enters the absorbent layer sheet 30 at an existing 200-250 mesh level. Through the 1000 ~ 1200 mesh to produce a very fine particle size powder was able to further increase the water adsorption capacity. It also helps to keep it dry for a long time and prevents skin sores. And in order to prevent residual moisture or blood (sweat) on one side, as shown in Figure 2 by double the quilted wire from the filter layer sheet 10 to the absorbent layer sheet 30 can be prevented from one side falling or leaks. there was.

Lastly, the mercury and lead components remaining from natural minerals (montmorillonite) are completely removed by mercury and lead components by centrifugation and defensive methods to prevent the occurrence of hydrogen peroxide and lipid peroxide, which causes skin problems. Could prevent.

Hereinafter, the present invention will be described in more detail with reference to the following examples, but the scope of the present invention is not limited to the following examples.

Example 1

1 L of water and 1 kg of montmorillonite were mixed, and impurities precipitated were removed, and aged in a water tank equipped with a bubble generator maintained at about 50 ° C. while stirring at about 700 rpm for 3 days to incubate aerobic microorganisms. 90 g of sterile physiological saline was measured with 10 g of the sample by the cosmetic microbial limit test method. As a result, the bacterial count of 7.9 × 10 ⁵ CFU / g was confirmed. The culture was dried at about 50 ° C., then powdered to 1000-1200 mesh by air flow grinding, and then sterilized at −40 to 45 ° C.

10g of the powder was tested by using KFIA-FI-1042 method at room temperature 24 ℃, 51% humidity, and 108 / 수 of anions in the air using a charged particle measuring device. As a result, it was expressed as the number of IONs per unit volume, which was about 226 ION / cc. In addition, the deodorization rate of the powder was measured and shown in Table 1 below.

Test Items Elapsed time (minutes) Control (ppm) ^{1 )} Example 1 (ppm) Deodorization rate (%)   Deodorization test Early 500 500 30 490 45 91 60 480 30 94 90 460 20 96 120 450 15 97

1) Control was measured with no sample.

Test Method: KFIA-FI-1004

Test gas: Ammonia

Gas concentration measurement: gas detector

Meanwhile, the deep water after removing the salt was aged at about 8 ° C. for 3 days, and the powder and the deep water were mixed at a weight ratio of 3: 1 to prepare a cosmetic massage pack of the present invention.

Example 2

980 g of montmorillonite according to Example 1 and 20 g of TiO ₂ powdered into 1000 to 1200 mesh by air flow pulverization were mixed and provided as an absorbent material to the diaper having the structure as shown in FIG.

The diaper according to Example 2 thus prepared was worn for 30 months on 30 infants with skin sores. As a result, skin sores were improved in all 30 infants, and the germ propagation could be prevented by radiating far-infrared rays.

As described above, the present invention is very useful as a baby diaper, a female pad or a general bedding pad because of excellent absorption and deodorizing power.

1 is a schematic view showing the structure and operation of a diaper comprising a far infrared ray emitting composition according to the present invention.

2 is a schematic view showing a structure in which a quilted wire is formed in a diaper including a far-infrared radiation composition according to the present invention.

-Explanation of symbols for the main parts of the drawing-

10: filter sheet layer 20: dry sheet layer

30: absorbent sheet layer 40: waterproof sheet layer

50: cover sheet layer 60: montmorillonite

Claims (3)

After dissolving montmorillonite in water to remove precipitates, aging and stirring for 2 to 4 days in a bubble bath equipped with a bubble generator maintained at 40 to 60 ℃ to incubate the aerobic microorganisms, and then obtained culture 94-99.9% by weight of 1000-1200 mesh montmorillonite powder and 1000-1200 mesh, which were dried at a temperature of 40-60 ° C. and then sterilized at -40--45 ° C., and then powdered by air flow pulverization. A health product comprising a far-infrared radiation composition containing montmorillonite, characterized in that it comprises a far-infrared radiation composition composed of 0.1 to 6% by weight of titanium oxide. delete The method according to claim 1, The health product comprises a far-infrared radiation composition containing montmorillonite, characterized in that the diaper or pad.

Images