KR100941440B1 - Cube-corner type Reflective material and the method for producing the same which can present color - Google Patents

Cube-corner type Reflective material and the method for producing the same which can present color Download PDF

Info

Publication number
KR100941440B1
KR100941440B1 KR1020080029474A KR20080029474A KR100941440B1 KR 100941440 B1 KR100941440 B1 KR 100941440B1 KR 1020080029474 A KR1020080029474 A KR 1020080029474A KR 20080029474 A KR20080029474 A KR 20080029474A KR 100941440 B1 KR100941440 B1 KR 100941440B1
Authority
KR
South Korea
Prior art keywords
cube corner
base film
curable resin
color
ultraviolet curable
Prior art date
Application number
KR1020080029474A
Other languages
Korean (ko)
Other versions
KR20090104176A (en
Inventor
최상석
Original Assignee
최상석
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 최상석 filed Critical 최상석
Priority to KR1020080029474A priority Critical patent/KR100941440B1/en
Publication of KR20090104176A publication Critical patent/KR20090104176A/en
Application granted granted Critical
Publication of KR100941440B1 publication Critical patent/KR100941440B1/en

Abstract

본 발명은 베이스필름(500)과 상기 베이스필름의 일면에 형성된 재귀반사를 일으키는 입방체모서리를 가지는 큐브코너로 이루어지는 큐브코너층(5800)을 포함하여 이루어지는 큐브코너형 재귀반사물에 있어서, 상기 큐브코너층(5800)은 안료가 포함된 자외선경화수지가 경화되어 이루어진 것임을 특징으로 하는 칼라가 제공되는 큐브코너형 재귀반사물을 개시한다.The present invention relates to a cube corner type retroreflective object comprising a cube corner layer (5800) comprising a base film (500) and a cube corner having a cuboid corner causing retroreflection formed on one surface of the base film. Layer 5800 discloses a cube corner type retroreflector provided with a color, characterized in that the UV curable resin containing pigment is cured.

큐브코너, 재귀반사물, 칼라, 안료 Cube corner, Retro-reflective, Color, Pigment

Description

칼라가 제공되는 큐브코너형 재귀반사물 및 그 제조방법{Cube-corner type Reflective material and the method for producing the same which can present color}Cube-corner type Reflective material and the method for producing the same provided with color

본 발명은 칼라가 제공되는 큐브코너형 재귀반사물 및 그 제조방법에 관한 것이다. 본 발명에 따를 경우, 종래 칼라의 제공이 어려웠던 TPU와 같이 그 녹는점이 높은 소재를 베이스필름으로 하는 재귀반사물에 대하여도 쉽게 칼라를 제공할 수 있게 된다.The present invention relates to a cube corner type retroreflector provided with a collar and a method of manufacturing the same. According to the present invention, it is possible to easily provide a color to a retroreflective material having a high melting point material as a base film, such as a TPU, which is difficult to provide a conventional color.

재귀 반사물(Reflective material)은 입사된 광을 광원을 향하여 재귀반사하는 것으로서 이러한 재귀반사로 인하여 그 부착물의 식별력이 뛰어나 안전용 등으로 사용되는 것을 말한다. 이러한 재귀 반사물은 마이크로 초자구(Glass bead)형과 큐브코너(Cube corner)형으로 나눌 수 있는데, 일반적으로 큐브코너형 재귀반사소자는 마이크로 초자구형 재귀 반사물에 비해 광의 재귀반사율이 훨씬 우수하며 우천시 또는 수중에서도 재귀반사 기능을 최대한 발휘할 수 있는 장점을 가져 라벨이나 도로안전관련제품 등에 사용되고 있으며, 현재는 그 사용범위가 넓어져 신발 등에도 부착되어 사용되고 있고, 또한, 대한민국 특허출원 제10-2007-0032643에서와 같 이 의류 등의 원단에도 그 사용이 가능하게 되고 있다.Reflexive material (reflective material) is a retroreflective incident light toward the light source, and due to such a retroreflective means that it is used for safety, etc. because of excellent discrimination of the attachment. These retroreflectors can be divided into micro glass bead type and cube corner type. In general, the cube corner type retroreflective element has a much higher retroreflectivity of light than the micro ultramagnetism type retroreflective element. It is used in labels and road safety products as it has the advantage of showing the maximum retroreflective function even in rainy weather or underwater. Currently, its use range is widened and it is also attached to shoes, etc. Also, Korea Patent Application No. 10-2007 As in -0032643, it is also possible to use the same in fabrics such as clothing.

이러한 큐브코너형 재귀반사물은 칼라(color)를 가지는 것이 좋은데, 이러한 경우 사람의 주목을 더욱 끌 수가 있고 의류, 신발 등에 사용되는 경우 패션제품으로서 가치를 더욱 올릴 수 있기 때문이다.This cube corner type retroreflective is good to have a color (color), in this case can attract more attention of people, and when used in clothing, shoes, etc. can further increase the value as a fashion product.

이와 같은 큐브코너형 재귀반사물은 기본적으로 베이스필름이 제공되고 상기 베이스필름의 상면에 양각의 큐브코너가 다수 개 형성된 큐브코너층을 가진다.Such a cube corner type retroreflective basically has a base film and a cube corner layer having a plurality of embossed cube corners formed on an upper surface of the base film.

일반적으로 이러한 큐브코너층은 상기 베이스필름의 상면에 자외선경화수지를 도포한 후, 상기 자외선경화수지에 음각의 큐브코너가 형성된 엠보싱벨트를 가압하여 상기 자외선경화수지를 대응하는 양각의 큐브코너로 형성하고, 이후 상기 양각의 큐브코너를 자외선을 조사하여 경화하여 형성된다.In general, such a cube corner layer is formed of an embossed cube corner corresponding to the ultraviolet curable resin by applying an ultraviolet curable resin to the upper surface of the base film, and then pressing the embossed belt having a negative cube corner formed on the ultraviolet curable resin. Then, the embossed cube corner is formed by irradiation with ultraviolet rays.

종래 이러한 큐브코너형 재귀반사물에서 칼라는 베이스필름을 통하여 제공되어왔다. 즉 상기 베이스필름의 제조 시 그 용융된 수지에 안료를 첨가하여 칼라를 가지도록 하였으며, 이에 따라, 큐브코너형 재귀반사물이 칼라를 가졌던 것이다. 이 경우, 통상적으로 베이스필름은 PVC를 재질로 하는 것을 사용하였는데, 이것은 PVC의 경우 그 녹는점이 높지 않아 용융상태에서 안료가 타버리는 등의 문제가 없어 안료를 용이하게 첨가할 수 있었기 때문이다.In the prior art cube corner type retroreflective color has been provided through the base film. In other words, when the base film is manufactured, a pigment is added to the molten resin to have a color. Accordingly, the cube corner type retroreflector had a color. In this case, the base film is typically made of a PVC material, since the melting point of the PVC is not high, because there is no problem such as burning of the pigment in the molten state, the pigment could be easily added.

그러나 PVC는 다이옥신 등의 환경문제를 유발할 수 있어 현재 그 사용이 꺼려지는 추세로서, 대안으로서, TPU(Thermo Poly Urethane)가 각광을 받고 있다.However, PVC can cause environmental problems, such as dioxin, and its use is currently reluctant. As an alternative, TPU (Thermo Poly Urethane) is in the spotlight.

하지만 TPU와 같은 경우는 녹는점이 상대적으로 높아 일반적으로 그 용융상태에서 안료를 첨가할 때 안료가 타버려 TPU를 소재로 하여 칼라를 가지는 베이스필 름을 만드는 것은 어렵고 이에 따라 TPU를 베이스필름으로 하는 경우 그 큐브코너형 재귀반사물은 칼라를 가지기 어려웠다.However, in the case of TPU, the melting point is relatively high. Generally, when the pigment is added in the molten state, the pigment burns, making it difficult to make a color base film made of the TPU material. The cube-cornered retroreflectors had a hard color.

이와 같이 종래 TPU와 같이 그 녹는점이 상대적으로 높은 것을 베이스필름의 소재로 하는 큐브코너형 재귀반사물은 칼라를 가지기 어려웠고, 이에 따라 칼라를 가지는 큐브코너형 재귀반사물의 경우는 PVC를 그 베이스필름의 소재로 하여왔던 것이다.As such, a cube corner retroreflector having a relatively high melting point, such as a conventional TPU, as a base film material, is difficult to have a color. It has been made of material.

하지만 전술한 바와 같이 환경 등의 문제의 대두로 PVC를 소재로 하여 베이스필름을 사용하는 것은 꺼려지고 있며, TPU 등과 같이 환경친화적인 것이 사용되어야 하는 것이다.However, as mentioned above, it is reluctant to use a base film made of PVC as a material for environmental problems, and an environment-friendly one such as a TPU should be used.

그러므로 TPU 등과 같이 그 녹는점이 상대적으로 높은 것을 그 베이스필름의 소재로 하여도 용이하게 칼라를 가질 수 있는 칼라가 제공되는 큐브코너형 재귀반사물 및 그 제조방법이 요청된다. 본 발명은 이러한 요청을 만족시킨다.Therefore, there is a need for a cube corner type retroreflective material and a method of manufacturing the same, in which a color having a relatively high melting point, such as a TPU, can be easily used as a material of the base film. The present invention satisfies this request.

본 발명의 목적은 TPU 등과 같이 그 녹는점이 상대적으로 높은 것을 그 베이스필름의 소재로 하여도 용이하게 칼라를 가질 수 있는 칼라가 제공되는 큐브코너형 재귀반사물 및 그 제조방법을 제공하는 것이다.It is an object of the present invention to provide a cube corner type retroreflective object and a method for manufacturing the same, which are provided with a color that can have a color easily even if the melting point is relatively high, such as TPU.

본 발명의 목적에 따라 본 발명은 베이스필름을 제공하는 베이스필름제공단계와; 상기 베이스필름의 일면에 안료가 첨가된 자외선경화수지를 도포하는 안료가 첨가된 자외선경화수지의 도포단계와; 상기 베이스필름의 일면에 도포된 안료가 첨가된 자외선경화수지에 대하여 재귀반사를 일으키는 입방체모서리를 가지는 큐브코너로 이루어지는 큐브코너층을 형성하는 큐브코너층 형성단계를 포함하여 이루어지는 것을 특징으로 하는 칼라가 제공되는 큐브코너형 재귀반사물의 제조방법을 제공한다.According to the object of the present invention, the present invention provides a base film providing step; Applying a pigment-added ultraviolet curable resin to which the pigment is added to one surface of the base film and the ultraviolet curable resin added; The color is characterized in that it comprises a cube corner layer forming step of forming a cube corner layer consisting of a cube corner having a cube corner causing retroreflection to the ultraviolet curable resin added to the pigment applied to one surface of the base film It provides a method for producing a cube corner type retroreflective provided.

본 발명의 실시예에서, 상기 큐브코너층 형성단계는 상기 베이스필름의 일면에 도포된 안료가 첨가된 자외선경화수지에 대하여 음각의 큐브코너가 형성된 가압수단으로 상기 자외선경화수지를 가압하여 상기 자외선경화수지에 대하여 대응하는 양각의 큐브코너를 형성하는 가압단계와; 상기 양각의 큐브코너가 형성된 자외선경화수지에 자외선을 조사하여 경화하는 경화단계를 포함하여 이루어진다.In the embodiment of the present invention, the step of forming the cube corner layer is the ultraviolet curing by pressing the ultraviolet curable resin with a pressure means formed with a negative cube corner with respect to the ultraviolet curable resin is added to the pigment coated on one surface of the base film A pressing step of forming a cube corner having a corresponding relief with respect to the resin; It comprises a curing step of curing by irradiating ultraviolet light on the ultraviolet curable resin formed with the embossed cube corner.

본 발명에 따를 경우 상기 베이스필름은 TPU로서 이루어지는 것이 바람직하다.According to the present invention, the base film is preferably made of a TPU.

또한, 상기 음각의 큐브코너가 형성된 가압수단은 음각의 큐브코너가 그 표면에 형성된 엠보싱벨트인 것이 바람직하다.In addition, it is preferable that the pressing means in which the intaglio cube corner is formed is an embossed belt in which the intaglio cube corner is formed on the surface thereof.

다른 측면에서 본 발명은 베이스필름과; 상기 베이스필름의 일면에 형성된 재귀반사를 일으키는 입방체모서리를 가지는 큐브코너로 이루어지는 큐브코너층을 포함하여 이루어지는 큐브코너형 재귀반사물에 있어서, 상기 큐브코너층은 안료가 포함된 자외선경화수지가 경화되어 이루어진 것임을 특징으로 하는 칼라가 제공되는 큐브코너형 재귀반사물을 제공한다.In another aspect, the present invention is a base film; In the cube corner type retroreflective object comprising a cube corner layer consisting of a cube corner having a cuboid corner causing a retroreflection formed on one surface of the base film, wherein the cube corner layer is cured UV curable resin containing pigment It provides a cube corner type retroreflective provided with a collar, characterized in that made.

이때 상기 베이스필름은 TPU를 소재로 하여 이루어지는 것이 바람직하다.At this time, the base film is preferably made of a TPU material.

본 발명에 따를 경우, 큐브코너형 재귀반사물에 있어서, 종래 TPU 등과 같이 상대적으로 녹는점이 높은 소재를 베이스필름으로 할 경우 그 칼라의 연출이 어려웠던 것을, 매우 간편하고 효율적인 방식으로 용이하게 칼라를 연출할 수 있게 한다. According to the present invention, in the case of a cube corner type retroreflective material, when the base film is made of a material having a relatively high melting point, such as a conventional TPU, it is difficult to produce the color in a very simple and efficient manner. To be able.

또한 본 발명에 따를 경우, 큐브코너형 재귀반사물에 있어서, 소량으로 다양한 칼라를 쉽게 연출할 수 있도록 한다.In addition, according to the present invention, in the cube corner type retroreflective, it is possible to easily produce a variety of colors in a small amount.

이제 본 발명의 바람직한 실시예를 첨부한 도면을 참고로 하여 설명한다.Preferred embodiments of the present invention will now be described with reference to the accompanying drawings.

먼저 도 1은 본 발명에 따른 칼라가 제공되는 큐브코너형 재귀반사물의 제조방법을 보이는 도면이다.1 is a view showing a method of manufacturing a cube corner type retroreflective material provided with a collar according to the present invention.

우선, 베이스필름(500)이 제공된다. (도 1의 (a))First, a base film 500 is provided. (FIG. 1A)

본 발명에 따를 경우 상기 베이스필름(500)은 TPU를 재질로 하는 것이 바람직하다.According to the present invention, the base film 500 is preferably made of a TPU material.

다음, 상기 베이스필름(500)의 일면에 안료가 첨가된 자외선경화수지(580)를 도포한다. (도 1의 (b)) 이에 따라 상기 자외선경화수지(580)는 칼라를 띄게 되며, 결과적으로, 완성되는 큐브코너형 재귀반사물이 칼라를 가지게 된다.Next, a UV-curing resin 580 to which a pigment is added is applied to one surface of the base film 500. (B) of FIG. 1, the ultraviolet curable resin 580 has a color, and as a result, the finished cube corner type retroreflector has a color.

이때, 상기 안료는 자외선경화수지(580)가 반투명을 형성할 정도로 첨가한다. 이것은 후술되는 자외선조사공정에 따라 자외선이 조사되었을 때 자외선이 투과되어 경화가 이루어질 수 있도록 하기 위함이다.In this case, the pigment is added to the extent that the ultraviolet curable resin 580 forms translucent. This is to allow ultraviolet rays to pass through and to be cured when the ultraviolet rays are irradiated according to the ultraviolet irradiation process described below.

다음, 상기 도포된 안료가 첨가된 자외선경화수지(580)에 대하여 재귀반사를 일으키는 입방체모서리를 가지는 큐브코너로 이루어지는 큐브코너층(5800)을 형성하게 된다.Next, to form a cube corner layer 5800 consisting of a cube corner having a cube corner causing retroreflection to the UV-curable resin 580 to which the applied pigment is added.

이와 같이 자외선경화수지(580)에 대하여 큐브코너를 형성하기 위한 방법은 당업계에서 알려진 모든 방법을 사용할 수 있으며, 개별적인 방법 또는 연속적인 방법에 의해 제조할 수 있다. As such, the method for forming the cube corner with respect to the UV curable resin 580 can be used by any method known in the art, can be prepared by a separate method or a continuous method.

통상적으로 자외선경화수지에 대하여 큐브코너를 형성하는 방법은 가열, 가압, 자외선 조사, 냉각 등을 공정을 포함한다. 이때, 가압은 자외선 경화수지를 큐브코너(5800)로 형성하기 위하여 음각의 코브코너형상을 상기 자외선경화수지에 가압하여 양각의 큐브코너형상을 이루는 것을 말한다. Typically, the method of forming a cube corner with respect to the ultraviolet curable resin includes a process of heating, pressurization, ultraviolet irradiation, cooling and the like. In this case, the pressurization refers to forming an embossed cube corner shape by pressing an intaglio cove corner shape onto the ultraviolet curable resin to form an ultraviolet curable resin into a cube corner 5800.

즉 도 1의 (c)를 참고로, 상기 베이스필름(500)의 일면에 도포된 안료가 첨가된 자외선경화수지(580)에 대하여, 예를 들어, 음각의 큐브코너가 그 표면에 형성된 엠보싱벨트가 가압수단(50)으로서 제공되고 이것이 상기 자외선경화수지(580)를 가압하여 상기 자외선경화수지(580)에 대하여 대응하는 양각의 큐브코너층을 형성하게 되고, 다음, 도 1의 (d)에서 보이는 것과 같이, 이렇게 양각의 큐브코너층이 형성된 자외선경화수지(580)에 대하여 자외선을 조사하여 경화시켜 상기 베이스필름(500)의 일면에 재귀반사를 일으키는 입방체모서리를 가지는 큐브코너로 이루어지는 큐브코너층(5800)이 형성되는 것이다.That is, with reference to Figure 1 (c), with respect to the UV-curing resin 580 to which the pigment applied to one surface of the base film 500, for example, an embossed belt in which a negative cube corner is formed on the surface Is provided as a pressurizing means 50, which pressurizes the ultraviolet curable resin 580 to form a corresponding embossed cube corner layer with respect to the ultraviolet curable resin 580, and then in FIG. As can be seen, a cube corner layer made of a cube corner having a cuboid corner causing retroreflective reflection on one surface of the base film 500 by irradiating ultraviolet rays to the ultraviolet curable resin 580 having the embossed cube corner layer formed thereon. 5800 is formed.

상기 자외선경화수지는 기계적 강도 및 열적 안정성이 기본적으로 요구되며 내환경성, 내박리성, 내황변성, 점성정도, 이형성도 그 선정에 있어서 중요한 요소이다. 이를 고려하여, 본 발명에 따를 경우 상기 자외선경화수지는 그 표면에 상기 큐브코너를 형성하기에 적합한 반응성 수지인 광개시제와 아크릴레이트기를 갖는 1층 이상의 화합물의 배합물을 포함할 수 있으며, 보다 구체적으로, 광개시제를 포함하고, 예비 중합체, 올리고머 또는 단량체에 중합성 불포화 결합 또는 에폭시 기를 적절히 혼합한 조성물을 포함할 수 있다.The UV curable resin basically requires mechanical strength and thermal stability, and environmental resistance, peeling resistance, yellowing resistance, viscosity, and release property are also important factors in the selection thereof. In consideration of this, according to the present invention, the ultraviolet curable resin may include a combination of a photoinitiator, which is a reactive resin suitable for forming the cube corner on the surface thereof, and at least one compound having an acrylate group, and more specifically, A photoinitiator may be included, and a composition including appropriately mixed polymerizable unsaturated bonds or epoxy groups with a prepolymer, oligomer or monomer may be included.

상기 예비 중합체인 올리고머는 불포화 지칼폰산과 다가알콜과의 축합물의 불포화 에스테르류, 에폭시수지, 폴리에스테르메타크릴레이트, 폴리에텔메탈크릴레이트, 폴리에텔아크릴레이트등의 아크릴레이트류 등이 사용될 수 있다. 특히, 광중합성의 올리고머로는 폴리에스테르 아크릴레이트, 에폭시 아크릴레이트, 우레탄 아크릴레이트 및 스피라나(spirana) 아크릴레이트를 포함할 수 있다. 폴리에스테르 아크릴레이트는 플라스틱 또는 금속에서의 접착성을 향상시키기 위해서 널리 쓰이는 것으로 취급이 용이하고 안료분사성이 양호한 특성을 지닌 수지이며, 에폭시 아크릴레이트는 에폭시 수지의 성질을 갖고 있기 때문에 경도 유연성 경화성이 우수하고 산소에 대해서도 비교적 안정성이 양호한 특성을 지닌 수지이다.As the oligomer, the prepolymer may be an unsaturated ester of a condensate of unsaturated zalphonic acid and a polyalcohol, an acrylate such as epoxy resin, polyester methacrylate, polyether methacrylate, polyether acrylate, or the like. In particular, the photopolymerizable oligomer may include polyester acrylate, epoxy acrylate, urethane acrylate and spirana acrylate. Polyester acrylate is widely used to improve adhesion in plastic or metal. It is easy to handle and has good pigment spraying property. Epoxy acrylate has properties of epoxy resin, so it is hard and flexible. It is a resin having excellent characteristics and good stability with respect to oxygen.

상기 자외선경화수지(580)에 대하여 큐브코너층(5800)를 형성하는 방법은, 예를 들어, 대한민국특허등록 제0614309호에서 개시되는 엠보싱벨트를 이용할 수 있다. 이를 도 2를 참고로 설명한다.As a method of forming the cube corner layer 5800 with respect to the ultraviolet curable resin 580, for example, an embossed belt disclosed in Korean Patent Registration No. 0614309 can be used. This will be described with reference to FIG. 2.

먼저, 냉각롤(6)과 가열롤(2) 사이에 상기 특허에 따른 원통형의 엠보싱벨트(5)를 끼워 장착한다. 상기 엠보싱벨트(5)는 그 표면에 음각의 큐브코너형상(5S)이 형성된 것이다. First, the cylindrical embossing belt 5 according to the patent is fitted between the cooling roll 6 and the heating roll 2. The embossed belt 5 is formed with a negative cube corner shape 5S on its surface.

이렇게 상기 냉각롤(6)과 가열롤(2)에 끼워진 원통형 엠보싱벨트(5)는 일정한 방향으로 회전하게 된다. Thus, the cylindrical embossing belt 5 fitted to the cooling roll 6 and the heating roll 2 is rotated in a predetermined direction.

이 상태에서 상기 베이스필름(500)을 롤(12)에 감긴 상태에서 가이드 롤을 경유하여 상기 엠보싱벨트(5)를 향하여 전진하게 되는데, 이때 상기 베이스필름(500)의 표면에 자외선경화수지공급장치(14)에 의해 일정한 양의 자외선 경화수지를 공급한다. 이때 상기 자외선경화수지공급장치(14)는 연출하고자 하는 칼라에 대한 안료가 첨가된 자외선경화수지(580)를 상기 베이스필름(500)의 표면에 공급하는 것이다.In this state, the base film 500 is rolled toward the embossing belt 5 via a guide roll in a state in which the roll 12 is wound. At this time, an ultraviolet curable resin supply device on the surface of the base film 500. A constant amount of ultraviolet curable resin is supplied by (14). In this case, the ultraviolet curable resin supply device 14 supplies the ultraviolet curable resin 580 to which the pigment for the color to be produced is applied to the surface of the base film 500.

이 경우 자외선경화수지는 특성상 온도변화에 민감하기 때문에. 본 발명에서는 자외선경화수지공급장치(14)의 주변환경을 일정한 온도, 습도를 유지하여 자외선 경화형수지의 점성(점도)을 일정한 수준으로 유지하도록 한다. 상기 자외선경화수지공급장치(14)는 일정한 양이 토출되도록 압력계가 부착되어 있으며, 진행 방향의 속도에 따라 자동적으로 압력콘트롤이 될 수 있도록 구성되어 있다.In this case, the UV curable resin is sensitive to temperature changes due to its characteristics. In the present invention, by maintaining a constant temperature, humidity of the surrounding environment of the ultraviolet curing resin supply device 14 to maintain the viscosity (viscosity) of the ultraviolet curable resin at a constant level. The ultraviolet curing resin supply device 14 is attached to a pressure gauge so that a predetermined amount is discharged, it is configured to be a pressure control automatically in accordance with the speed of the traveling direction.

상기 자외선 경화형수지의 공급장치(14)는 토출되는 부위가 여러 부분이 있을 수 있으며, 상기 베이스필름(500)의 표면에 공급된 자외선경화수지는 실리콘 고무롤(4)과 상기 원통형 엠보싱벨트(5)의 사이를 통과하면서 그 두께가 조절되면서, 상기 엠보싱벨트의 음각의 큐브코너형상(5S)에 따라 양각의 큐브코너(5800)의 형상을 가지게 된다. The UV-curable resin supply device 14 may have a portion to be discharged, and the UV curable resin supplied to the surface of the base film 500, the silicone rubber roll (4) and the cylindrical embossing belt (5) While the thickness of the embossed belt is passed while passing through the shape of the embossed belt corner 5S has a shape of the cube corner 5800.

이 경우, 상기 자외선 경화수지는 기계적인 성질 및 모재의 종류에 따라 적당한 첨가재를 혼합하여 효과적인 접착성 및 이형성을 가지도록 하는 것이 바람직하다.In this case, it is preferable that the ultraviolet curable resin is mixed with a suitable additive according to the mechanical properties and the type of the base material to have effective adhesiveness and release property.

이후 상기 기재필름(500) 상의 자외선경화수지는 2차 가압롤(7)과 3차 가압롤(8) 사이에 설치되는 자외선 조사장치(9)에 의하여 일차적으로 경화가 이루어지고 이후 냉풍장치(10)와 냉각롤(6)을 통과하면서 2차적으로 경화가 이루어지게 된다. Thereafter, the ultraviolet curable resin on the base film 500 is primarily cured by an ultraviolet irradiation device 9 installed between the secondary press roll 7 and the tertiary press roll 8 and then the cold air blower 10. ) And hardening is made while passing through the cooling roll (6).

상기 자외선 조사장치(9)와 관련되어 이는 상하 높이 조절이 될 수 있도록 하며 자외선을 조사할 경우 전체 면적에 대하여 균일한 농도 및 명암으로 조사하여 경화속도의 차이로 인해 기포 발생 또는 크랙현상이 발생하지 않도록 하는 것이 바람직하다.In relation to the ultraviolet irradiation device (9), it can be adjusted up and down height, and when irradiated with ultraviolet rays, irradiated with uniform concentration and contrast with respect to the entire area, bubbles or cracks do not occur due to the difference in curing rate. It is desirable to avoid.

이후, 상기 자외선경화수지(580)가 경화되어 큐브코너층(5800)이 형성된 상기 베이스필름(500)은 분리롤(11)을 경유하여 회수롤(18)에 감겨져 회수된다.Thereafter, the ultraviolet curable resin 580 is cured, and the base film 500 having the cube corner layer 5800 is wound on the recovery roll 18 via the separation roll 11 to be recovered.

이와 같은 방식으로 상기 베이스필름(500)의 상면에 큐브코너층(5800)을 형성할 수 있는 것이다. 이 경우 상기 큐브코너층(5800)은 안료에 따른 칼라를 띄게 되며, 이에 따라, 전체 재귀반사물이 칼라를 띄게 된다.In this manner, the cube corner layer 5800 may be formed on the top surface of the base film 500. In this case, the cube corner layer 5800 has a color according to the pigment, and thus, the entire retroreflective object has a color.

본 발명에 따를 경우, 자외선경화수지(580)에 안료를 첨가하여 칼라를 가지는 자외선경화수지(580)를 베이스필름(500)의 일면에 도포하고 이후 상기 자외선경화수지(580)에 대하여 큐브코너층(5800)을 형성하는 것으로서, 단순히 자외선경화수지에 대하여 안료의 혼합만으로 간단히 칼라를 연출할 수 있게 된다. 이것은 종래 대량으로 생산되는 베이스필름(500)에 칼라를 연출하는 것과 비교하여, 소량으로 다양한 칼라를 연출할 수 있는 장점을 가지게 된다.According to the present invention, by adding a pigment to the ultraviolet curable resin 580, the ultraviolet curable resin 580 having a color is applied to one surface of the base film 500 and then the cube corner layer for the ultraviolet curable resin 580 By forming (5800), the color can be simply produced by simply mixing the pigment with respect to the ultraviolet curable resin. This has the advantage that can produce a variety of colors in a small amount, compared to the color to produce a conventional base film 500 produced in large quantities.

이로서 본 발명의 목적이 달성되었음을 이해할 수 있을 것이다.It will be appreciated that this has been achieved the object of the present invention.

본 발명은 실시예를 중심으로 설명되었으나, 이에 한정되지 않으며, 본 발명의 사상에 따라 그 권리범위는 다음의 청구범위에 의한다.Although the present invention has been described with reference to the embodiments, the present invention is not limited thereto, and the scope of the present invention is defined by the following claims according to the spirit of the present invention.

도 1은 본 발명에 따른 칼라가 제공되는 큐브코너형 재귀반사물을 제조하는 공정을 보이는 도면;1 is a view showing a process for producing a cube corner type retroreflector provided with a collar according to the present invention;

도 2는 본 발명에 따른 칼라가 제공되는 큐브코너형 재귀반사물을 제조하는 공정의 실시예를 보이는 도면.Figure 2 shows an embodiment of a process for producing a cube corner type retroreflective provided with a collar according to the present invention.

Claims (6)

(a) 베이스필름을 제공하는 베이스필름제공단계와;(a) a base film providing step of providing a base film; (b) 상기 베이스필름의 일면에 안료가 첨가된 자외선경화수지를 도포하는 안료가 첨가된 자외선경화수지의 도포단계와;(b) a step of applying a pigment-added UV-curable resin to which the pigment-added UV-curable resin is applied to one surface of the base film; (c) 상기 베이스필름의 일면에 도포된 안료가 첨가된 자외선경화수지에 대하여 재귀반사를 일으키는 입방체모서리를 가지는 큐브코너로 이루어지는 큐브코너층을 형성하는 큐브코너층 형성단계를 포함하여 이루어지는 것을 특징으로 하는 칼라가 제공되는 큐브코너형 재귀반사물의 제조방법.(c) a cube corner layer forming step of forming a cube corner layer made of a cube corner having a cube corner causing retroreflection to the ultraviolet curable resin to which the pigment coated on one surface of the base film is added. Method of producing a cube corner type retroreflective provided with a collar. 제1항에 있어서, The method of claim 1, 상기 큐브코너층 형성단계는 The cube corner layer forming step (c1) 상기 베이스필름의 일면에 도포된 안료가 첨가된 자외선경화수지에 대하여 음각의 큐브코너가 형성된 가압수단으로 상기 자외선경화수지를 가압하여 상기 자외선경화수지에 대하여 대응하는 양각의 큐브코너를 형성하는 가압단계와;(c1) pressurizing the ultraviolet curable resin with a pressing means having a negative cube corner formed on the ultraviolet curable resin to which the pigment coated on one surface of the base film is formed to form an embossed cube corner with respect to the ultraviolet curable resin; Pressing step; (c2) 상기 양각의 큐브코너가 형성된 자외선경화수지에 자외선을 조사하여 경화하는 경화단계를 포함하여 이루어지는 것을 특징으로 하는 칼라가 제공되는 큐브코너형 재귀반사물의 제조방법.(c2) a method for producing a cube corner type retroreflective provided with a color, characterized in that it comprises a curing step of curing by irradiating the ultraviolet curable resin on which the embossed cube corner is formed. 제1항 또는 제2항에 있어서,The method according to claim 1 or 2, 상기 베이스필름은 TPU로서 이루어지는 것을 특징으로 하는 칼라가 제공되는 큐브코너형 재귀반사물의 제조방법.The base film is a method of producing a cube corner type retroreflective provided with a color, characterized in that consisting of a TPU. 제2항에 있어서,The method of claim 2, 음각의 큐브코너가 형성된 가압수단은 음각의 큐브코너가 그 표면에 형성된 엠보싱벨트인 것을 특징으로 하는 칼라가 제공되는 큐브코너형 재귀반사물의 제조방법.Method for producing a cube corner type retro-reflective article provided with a collar, characterized in that the pressing means is formed with a negative cube corner is an embossed belt formed on the surface of the negative cube corner. 베이스필름과; 상기 베이스필름의 일면에 형성된 재귀반사를 일으키는 입방체모서리를 가지는 큐브코너로 이루어지는 큐브코너층을 포함하여 이루어지는 큐브코너형 재귀반사물에 있어서, A base film; In the cube corner type retroreflective object comprising a cube corner layer made of a cube corner having a cuboid corner causing a retroreflection formed on one surface of the base film, 상기 큐브코너층은 안료가 포함된 자외선경화수지가 경화되어 이루어진 것임을 특징으로 하는 칼라가 제공되는 큐브코너형 재귀반사물.The cube corner layer is a cube corner type retroreflective provided with a color, characterized in that the cured UV-curable resin containing a pigment. 제5항에 있어서,The method of claim 5, 상기 베이스필름은 TPU를 소재로 하여 이루어진 것을 특징으로 하는 칼라가 제공되는 큐브코너형 재귀반사물.The base film is a cube corner type retroreflective provided with a color, characterized in that made of a TPU material.
KR1020080029474A 2008-03-31 2008-03-31 Cube-corner type Reflective material and the method for producing the same which can present color KR100941440B1 (en)