KR100909034B1 - Anti-fog Fabric - Google Patents
Anti-fog Fabric Download PDFInfo
- Publication number
- KR100909034B1 KR100909034B1 KR1020070130943A KR20070130943A KR100909034B1 KR 100909034 B1 KR100909034 B1 KR 100909034B1 KR 1020070130943 A KR1020070130943 A KR 1020070130943A KR 20070130943 A KR20070130943 A KR 20070130943A KR 100909034 B1 KR100909034 B1 KR 100909034B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- fabric
- water
- antifogging
- alcohol
- Prior art date
Abstract
본 발명은 김서림 방지용 원단에 관한 것으로, 더욱 상세하게는 이산화티탄, 불소계 코팅제, 알콜, 아크릴산 에스테르, 스틸렌 모노머, 무기질 화합물 및 물을 포함하여 이루어지는 김서림 방지용 조성물을 원단에 처리함으로써, 김서림 방지효과가 우수함과 동시에, 방오성 및 내구성이 우수하고, 잔유이온의 용출이 적으며, 닦임성이 매우 우수하고, 내세탁성 또한 우수하여 세탁 후에도 그 효과가 유지되도록 하는 것이다.The present invention relates to an antifogging fabric. More specifically, an antifogging composition comprising titanium dioxide, a fluorine-based coating agent, an alcohol, an acrylate ester, a styrene monomer, an inorganic compound, and water is treated to a fabric, so that an antifogging effect is excellent. At the same time, it is excellent in antifouling properties and durability, has little elution of residual ions, very excellent wipeability, and excellent washing resistance so that the effect is maintained even after washing.
상기와 같은 본 발명에 사용되는 김서림 방지용 조성물은, 이산화티탄 0.5∼5중량%, 불소계 코팅제 6∼20중량%, 알콜 17∼45중량%, 아크릴산 에스테르 6∼20중량%, 스틸렌 모노머 2∼10중량%, 무기질 화합물 0.5∼5중량% 및 물 40∼68중량%를 포함하여 이루어지며, 이와 같은 상기 조성물 3중량%에 물 97중량%를 혼합하고, 상기 혼합된 혼합액에 원단을 침지시킨 후, 원단을 건져내 물기를 제거시킨 것을 특징으로 한다.The antifogging composition used in the present invention as described above is 0.5 to 5% by weight of titanium dioxide, 6 to 20% by weight of fluorine-based coating agent, 17 to 45% by weight of alcohol, 6 to 20% by weight of acrylic acid ester, 2 to 10% by weight of styrene monomer. %, Inorganic compound 0.5-5% by weight and water 40-68% by weight, and 3% by weight of the composition is mixed with 97% by weight of water, and immersed the fabric in the mixed mixture, and then It is characterized by removing the water by scooping out.
Description
본 발명은 이산화티탄, 불소계 코팅제, 알콜, 아크릴산 에스테르, 스틸렌 모노머, 무기질 화합물 및 물을 포함하여 이루어지는 김서림 방지용 조성물로 처리한 김서림 방지용 원단에 관한 것이다. The present invention relates to an antifogging fabric treated with an antifogging composition comprising titanium dioxide, a fluorine-based coating agent, an alcohol, an acrylic acid ester, a styrene monomer, an inorganic compound, and water.
자동차 유리, 창유리, 안경 유리 등과 같은 유리 표면의 김서림(흐림)현상은 유리의 표면 특성, 유리면 내외부의 습도 및 온도차, 유리면에 부착되는 각종 오염물 등의 복합적인 요인으로 인해 발생되는 부착(접착) 습윤(adhesional wetting)의 결과로서 나타나는 현상이고, 이에 대한 김서림(흐림) 방지의 가능성은 확장 습윤(spreading wetting)에 의해 달성될 수 있는 것으로 알려져 있다.The surface blurring of glass surfaces such as automobile glass, window glass, and glasses glass is caused by adhesion (adhesion) wetting caused by complex factors such as the surface characteristics of the glass, the difference in humidity and temperature inside and outside the glass surface, and various contaminants attached to the glass surface. It is a phenomenon that appears as a result of adhesional wetting, and it is known that the possibility of anti-fogging can be achieved by spreading wetting.
유리 표면에서 발생되는 김서림(흐림) 발생은, 유리 표면 내외의 온도차에 의해 공기중의 수분이 순간적으로 응결되어 액적상으로 유리면에 부착되며, 이들 액적의 미세한 입자들은 그들 사이에 작용하는 정전기적 반발력에 의하여 유리 표 면에 규칙적으로 배열하게 되는데, 이를 김서림(흐림) 현상이라 한다.The mist generation occurs on the glass surface. Moisture in the air is instantly condensed by the temperature difference between the surface of the glass and adheres to the glass surface in the form of droplets, and the fine particles of these droplets are electrostatic repulsive force acting between them. It is arranged regularly on the surface of the glass, which is called a mist (cloudy) phenomenon.
김서림(흐림)은 일반적으로 부착(접착) 습윤의 상태로 존재하게 되는데, 이를 해소하기 위해서는 확장습윤(spreading wetting)으로 이행시킬 필요가 있다.Cloudiness generally exists in the state of adhesion (adhesion), which needs to be shifted to spreading wetting.
즉, 유리 표면의 특성상 물에 대한 표면 장력이 낮은 조성물을 유리 표면에 도포하면 확장습윤 작용이 이루어져 상기 부착습윤에 기인하는 김서림(흐림) 현상이 방지됨으로써, 응시자의 시계를 확보할 수 있게 되는 것이다.That is, when a composition having a low surface tension with respect to water is applied to the glass surface due to the characteristics of the glass surface, expansion and wetting action is prevented, thereby preventing a blurring caused by the adhesion wetting, thereby securing a candidate's field of view. .
종래의 김서림(흐림) 방지제는, 사용 방법에 따라, 용기로부터 천에 묻혀서 도찰하는 방식, 수동 스프레이식, 에어졸식 등으로 분류할 수 있고, 성분 및 제형에 따르면, 비누 및 계면활성제를 중심으로 한 거품상태 타입과 알코올 및 글리콜류를 주체로 한 액상 타입으로 분류할 수 있다.Conventional anti-fog agents can be classified into a method of applying a coating onto a cloth from a container, a manual spray type, an aerosol type, etc., depending on the method of use, and according to the ingredients and formulations, It can be classified into foam type and liquid type mainly composed of alcohol and glycols.
비누 및 계면활성제를 주성분으로 하는 종래의 김서림 방지제는, 유효성분이 씻겨져 나감으로 인해 김서림(흐림) 방지성능이 장기간 지속되지 않는 경향이 있으므로, 겨울철이나 장마철의 차량 운행시에 운전자의 시야를 지속적으로 확보하기에 미흡한 점이 있었다. Conventional anti-fog agents, which consist mainly of soap and surfactants, do not have a long-term anti-fog performance due to washing out of the active ingredient, so the driver's vision is continuously secured when driving a vehicle in winter or in the rainy season. There was not enough to do.
또한, 알코올류 및 글리콜류를 주성분으로 하는 종래의 김서림 방지제는 김서림(흐림) 방지성능 자체는 계면활성제를 주성분으로 하는 상기 제품보다 오래 지속될 수 있으나, 김서림(흐림) 현상이 해소된 후에는 건조시에 글리콜류가 유리면에 잔존하여 유리면에 얼룩이 발생됨으로써, 난반사 현상 등이 나타나게 되어 미관 상 양호하지 않을 뿐만 아니라, 특히 운전자의 시야를 방해하는 단점이 있었다. In addition, conventional anti-fog agents, which are mainly composed of alcohols and glycols, may have a longer anti-fog performance than the above-mentioned products mainly containing surfactants, but when the anti-fog phenomenon is resolved, drying Eglycols remain on the glass surface to cause stains on the glass surface, resulting in a diffuse reflection phenomenon and the like, which is not only aesthetically appealing, but also hinders the driver's vision.
더욱이, 상기한 김서림 방지제들은 방지제를 스프레이한 후, 별도의 천으로 스프레이된 면을 닦아주어야 하는 사용상의 불편함이 있었다.Moreover, the anti-fog agents described above had inconveniences in use that require wiping the sprayed side with a separate cloth after spraying the inhibitor.
상기 사용상의 불편함을 해소하기 위하여, 선출원된 국내 특허출원 제10-1997-0045570호에서는 가공된 면포 양면에 기모(起毛)형성시키는 제1공정과, 기모공정후 면포에 방습제를 침지시키는 제2공정과, 방습제에 침지된 면포를 탈수시키는 제3공정과, 탈수된 면포를 90-130℃의 열풍으로 건조시키는 제4공정과, 건조된 면포를 일정크기로 제단하는 제5공정과, 제단된 김서림 방지천을 포장하는 제5공정으로 되므로, 운전하기 전에 자동차의 유리 내측면을 한차례 닦아 주면, 운전도중 실내와 외부의 기온차가 심하거나 비가 내려도, 유리 내측면에 김이 서리지 않게 되어 유리 내면을 반복적으로 닦거나 히터, 에어컨 콘트롤러를 반복적으로 조작할 필요가 없게 되어, 쾌적한 환경에서 집중하여 운전할 수 있도록 하였으나, 파티클이 많아 시야가 좋지 못한 문제점이 있었다.In order to alleviate the inconvenience in use, the previously filed Korean Patent Application No. 10-1997-0045570 discloses a first step of raising the brush on both sides of the processed cotton cloth, and a second step of immersing the desiccant in the cotton cloth after the raising process. A third step of dehydrating the cotton cloth immersed in the desiccant, a fourth step of drying the dehydrated cotton cloth with hot air at 90-130 ° C., a fifth step of cutting the dried cotton cloth to a certain size, and Since it is the fifth process to wrap the anti-fog cloth, if you wipe the inner surface of the car once before driving, the inner surface of the glass will not be frosted even if the temperature difference between the inside and outside of the driving is severe or it rains. There is no need to repeatedly wipe or operate heater and air conditioner controller repeatedly, so that you can concentrate on driving in a pleasant environment. It was dots.
따라서, 본 발명의 목적은 상기한 종래의 김서림 방지제품이 갖는 제반문제점을 해소하기 위한 것으로, 이산화티탄, 불소계 코팅제, 알콜, 아크릴산 에스테르, 스틸렌 모노머, 무기질 화합물 및 물을 포함하여 이루어지는 김서림 방지용 조성물로 처리한 원단을 제공함으로써, 김서림 방지효과가 우수함과 동시에, 방오성 및 내구성이 우수하고, 잔유이온의 용출이 적으며, 닦임성이 매우 우수하고, 내세탁성 또한 우수하여 세탁 후에도 그 효과가 유지되도록 하는 것이다.Accordingly, an object of the present invention is to solve the problems of the conventional anti-fog products described above, comprising a composition for preventing anti-fog comprising titanium dioxide, fluorine-based coating agent, alcohol, acrylic ester, styrene monomer, inorganic compound and water By providing the treated fabric, it has excellent anti-fog effect, excellent antifouling property and durability, low elution of residual ions, very excellent wiping resistance, and excellent washing resistance, so that the effect can be maintained even after washing. It is.
상기한 목적을 달성하기 위하여 본 발명에 사용되는 김서림 방지용 조성물은, 이산화티탄 0.5∼5중량%, 불소계 코팅제 6∼20중량%, 알콜 17∼45중량%, 아크릴산 에스테르 6∼20중량%, 스틸렌 모노머 2∼10중량%, 무기질 화합물 0.5∼5중량% 및 물 40∼68중량%를 포함하여 이루어지며, 이와 같은 상기 조성물 3중량%에 물 97중량%를 혼합하고, 상기 혼합된 혼합액에 원단을 침지시킨 후, 원단을 건져내 물기를 제거하여 이루어지는 것을 특징으로 한다.The antifogging composition used in the present invention for achieving the above object is 0.5 to 5% by weight titanium dioxide, 6 to 20% by weight fluorine-based coating agent, 17 to 45% by weight alcohol, 6 to 20% by weight acrylic acid ester, styrene monomer It comprises 2 to 10% by weight, 0.5 to 5% by weight of inorganic compounds and 40 to 68% by weight of water, and mixed with 3% by weight of the composition, 97% by weight of water, and immersed the fabric in the mixed mixture solution After making the fabric, the fabric is picked up to remove moisture.
삭제delete
본 발명에 따른 김서림 방지용 원단에 의하면, 김서림방지 효과가 우수할 뿐만 아니라, 방오성, 내구성, 흡수성 또한 우수하여 가정, 차량 뿐만 아니라 반도체 제조 등의 산업분야에 까지 그 사용범위를 확대할 수 있는 유용한 효과를 제공한다.According to the anti-fog fabric according to the present invention, not only the anti-fog effect is excellent, but also the antifouling property, durability, and absorbency is also excellent, useful effect that can extend the range of use not only in homes, vehicles, but also in the industrial field of semiconductor manufacturing, etc. To provide.
또한, 파티클이 극히 미량이고 잔유이온 등의 용출이 적으며, 내세탁성이 우수하여 세탁후에도 김서림 방지효과가 그대로 유지됨으로써, 장기간 사용할 수 있을 뿐만 아니라 그 비용이 절감되는 효과가 있는 것이다.In addition, the particles are very small amount, little elution of residual ions, etc., excellent washing resistance, the anti-fogging effect is maintained even after washing, it is not only can be used for a long time, but also has the effect of reducing the cost.
이하, 본 발명을 상세히 설명하면 다음과 같다.Hereinafter, the present invention will be described in detail.
먼저, 본 발명에 사용되는 김서림 방지용 조성물은 이산화티탄(Titanium dioxide), 불소계 코팅제, 알콜(alcohol), 아크릴산 에스테르(esther acrylate), 스틸렌 모노머(Stylene monomer), 무기질 화합물(inorganic compound) 및 물을 포함하여 구성된다.First, the antifogging composition used in the present invention includes titanium dioxide, fluorine-based coating agent, alcohol, alcohol, esther acrylate, styrene monomer, inorganic compound, and water. It is configured by.
먼저, 상기 이산화티탄은 천연광석에서 추출한 김서림 방지용 파우더(power)로서, 이를 미세하게 분쇄하여 조성물 내에서 고르게 분산시킨다. 이때 상기 이산화티탄은 그 입도를 바람직하게는 10㎛ 이하로 하는 것이 바람직하나, 이를 반드시 제한하는 것은 아니다.First, the titanium dioxide is an antifogging powder (power) extracted from natural ores, finely pulverized it and evenly dispersed in the composition. In this case, the titanium dioxide is preferably made to have a particle size of 10 μm or less, but is not necessarily limited thereto.
또한, 상기 이산화티탄은 조성물 내에 0.5∼5중량%로 포함되는 바, 이는 상기 이산화티탄이 0.5중량% 미만이 되면 그 역할이 미미하게 되고, 5중량%를 초과할 시에는 비휘발성 잔류물(nonvolatile remainder)로 인한 문제가 발생되기 때문이다.In addition, the titanium dioxide is contained in the composition of 0.5 to 5% by weight, which is a minor role when the titanium dioxide is less than 0.5% by weight, non-volatile residue (nonvolatile when more than 5% by weight) problem occurs due to remainder).
또한, 불소계 코팅제는 방오성(soil repellent 및 release)을 부여하여 미세하게 코팅시키는 역할을 하는 것으로, 바람직하게는 하이드록실레이티드 퍼플루오르알킬에틸 아크릴레이트 코폴리머(Hydroxylated perfluoroalklethyl acrylate copolymer)를 사용한다. 그리고, 상기 불소계 코팅제는 조성물 내에 6∼20중량%로 포함되는 바, 이는 상기 불소계 코팅제가 6중량% 미만이 되거나 20중량%를 초과하면 미세한 코팅이 어렵기 때문이다. In addition, the fluorine-based coating agent serves to provide fine coating by imparting antifouling properties (soil repellent and release), and preferably a hydroxylated perfluoroalklethyl acrylate copolymer is used. In addition, the fluorine-based coating agent is included in the composition of 6 to 20% by weight, because when the fluorine-based coating agent is less than 6% by weight or more than 20% by weight fine coating is difficult.
그리고, 상기 알콜은 프로필 알콜(Propyl alcohol)과 에틸 알콜(Ethyl alcohol)의 혼합물을 사용하는 바, 상기 프로필 알콜은 침투성을 향상시키고 에틸 알콜은 용해성 및 분산성을 향상시키는 역할을 하기 때문이다. 그리고, 상기 알콜은 조성물 내에 17∼45중량%로 포함되는 바, 이는 상기 알콜이 17중량% 미만이 되면 침투성 및 분산성이 좋지 못하게 되고, 45중량%를 초과하면 과량이 되어 김서림 방지효과가 저하될 우려가 있기 때문이다.In addition, since the alcohol uses a mixture of propyl alcohol and ethyl alcohol, the propyl alcohol improves permeability and ethyl alcohol plays a role in improving solubility and dispersibility. In addition, the alcohol is included in the composition at 17 to 45% by weight, which means that the permeability and dispersibility is poor when the alcohol is less than 17% by weight, and when it exceeds 45% by weight, the antifogging effect is lowered. Because there is a fear.
상기 아크릴산 에스테르는 김서림 방지용 조성물의 내구성을 향상시키기 위한 것으로, 바람직하게는 에틸 아크릴레이트(Ethyl acrylate)를 사용하는 것이나, 이를 제한하지는 않는다. 그리고, 상기 아크릴산 에스테르는 조성물 내에 6∼20중량%로 포함되는 바, 이는 상기 아크릴산 에스테르가 6중량% 미만이 되면 조성물의 내구성이 좋지 못하게 되고, 20중량%를 초과하더라도 더 이상의 내구성 증가효과가 나타나지 않으므로 비경제적이기 때문이다.The acrylic ester is to improve the durability of the antifogging composition, preferably using ethyl acrylate (Ethyl acrylate), but is not limited thereto. And, the acrylic ester is contained in 6 to 20% by weight in the composition, which is when the acrylic ester is less than 6% by weight becomes poor durability of the composition, even if more than 20% by weight no longer increase the durability effect This is because it is uneconomical.
상기 스틸렌 모노머는 표면코팅제로서의 역할을 위한 것으로, 조성물 내에 2∼10중량%로 포함되는 바, 이는 상기 스틸렌 모노머가 2중량% 미만이 되면 표면코팅이 용이하게 이루어지지 못하고, 10중량%를 초과하더라도 더 이상의 증진된 효과가 나타나지 않으므로 비경제적이기 때문이다.The styrene monomer is to serve as a surface coating agent, it is included in the composition 2 to 10% by weight, which is not easily made when the styrene monomer is less than 2% by weight, even if it exceeds 10% by weight This is because it is uneconomical because no further enhanced effect appears.
그리고, 상기 무기질 화합물은 표면코팅 및 슬립제(slip agent) 역할을 위한 것으로, 일반적으로 에스테르 공중합체를 이용할 수 있으나, 이를 반드시 제한하지는 않는다. 상기 무기질 화합물은 조성물 내에 0.5∼5중량%로 포함되는 데, 상기 무기질 화합물이 0.5중량% 미만이 되면 박리강도가 좋지 못하고, 5중량%를 초과하면 부착성이 좋지 못한 문제점이 있기 때문이다.In addition, the inorganic compound is intended to act as a surface coating and a slip agent (slip agent), and generally may use an ester copolymer, but is not necessarily limited thereto. The inorganic compound is contained in 0.5 to 5% by weight in the composition, because when the inorganic compound is less than 0.5% by weight peel strength is not good, if it exceeds 5% by weight there is a problem in poor adhesion.
또한, 상기 조성물 내에는 물이 포함되는 바, 물은 용매로서 사용되는 것이며, 그 혼합비는 조성물 내에서 40∼68중량%로 한다.In addition, since water is contained in the said composition, water is used as a solvent and the mixing ratio is 40 to 68 weight% in a composition.
상기와 같이 되는 김서림 방지용 조성물은 방오성이 우수할 뿐만 아니라, UV 컷(UV CUT)효과가 있으며, 소취성이 있어 김서림 방지용 조성물로서 우수한 효과를 갖는 것이다.The antifogging composition as described above is not only excellent in antifouling property, but also has a UV cut (UV CUT) effect, and has a deodorant property and thus has an excellent effect as an antifogging composition.
이하, 상기 김서림 방지용 조성물로 처리한 김서림 방지용 원단에 대해 설명하면 다음과 같다.Hereinafter, the antifogging fabric treated with the antifogging composition will be described.
본 발명에 따른 김서림 방지용 원단은, 상기에서 설명된 김서림 방지용 조성물을 이용하여 되는 것으로, 상기 김서림 방지용 조성물을 물로 희석하고, 상기 희석된 조성물과 물의 혼합액에 원단을 침지시킨 후, 원단을 건져내 물기를 제거하여 이루어지는 것이다.The anti-fog fabric according to the present invention is to use the anti-fog composition described above, dilute the anti-fog composition with water, immerse the fabric in a mixture of the diluted composition and water, and then drain the fabric to dry It is made by removing.
이때 상기 조성물의 희석은, 상기 조성물 1∼5중량%에 물 95∼99중량%를 혼합하여 희석하는 데, 이는 조성물의 원단내 침투성 등을 고려한 것으로, 상기 희석비율을 한정하는 것은 아니다. 그리고, 상기 희석된 혼합액에 원단을 침지시키는 것은, 원단이 혼합액에 의해 젖은 상태가 되는 것으로 족한 것으로, 이를 장시간 침지시킴을 의미하는 것은 아니다.At this time, the dilution of the composition is diluted by mixing 95 to 99% by weight of water to 1 to 5% by weight of the composition, which takes into account the permeability of the composition, etc., and does not limit the dilution ratio. In addition, immersing the fabric in the diluted mixed solution is sufficient that the fabric is wetted by the mixed solution, and does not mean to immerse it for a long time.
또한, 상기 원단을 건져내 물기를 제거하는 것 역시 그 방법이나 압력 또는 힘을 제한하지 않는 것으로, 망글이라는 압력을 주어 짜주는 설비를 1번 통과하는 것으로 족하다.In addition, the removal of water by removing the fabric is also not limited to the method or pressure or force, it is enough to pass through the facility to give a pressure to the mangle pressure.
그리고, 상기 원단으로는 모든 종류의 원단을 모두 사용가능한 것이나, 흡수력, 김서림 방지효과 등을 고려할 때 니트 극세사로, 50d, 75d, 120d 및 150d 중 어느 하나인 것을 사용하는 것이 바람직하나, 이를 반드시 제한하지 않는다.As the fabric, all kinds of fabrics can be used, but in consideration of absorbency and antifogging effect, it is preferable to use any one of 50d, 75d, 120d, and 150d as a knit microfiber, but must be limited thereto. I never do that.
또한, 상기 니트 극세사란 분할사를 가연처리한 후 편직하여 정련분할 후에 고수축 처리한 것으로, 폴리에스테르(Polyester)와 나일론(Nylon)의 혼용율이 7:3 ∼ 8:2인 것이다. 상기 폴리에스테르와 나일론의 혼용율은 수축성과 흡수성을 고려한 수치로서, 이를 제한하는 것은 아니다.In addition, the knit microfiber yarn is twisted after the divided yarn is knitted and then subjected to high shrinkage after scouring and dividing, and a mixing ratio of polyester and nylon is 7: 3 to 8: 2. The mixing ratio of the polyester and nylon is a value in consideration of shrinkage and water absorption, but is not limited thereto.
또한, 상기 공정 후에 별도의 건조공정을 거치거나 자연건조할 수 있음은 당연한 것으로, 그 실시를 제한하지 않는다.In addition, it is obvious that the drying process may be carried out after a separate drying process or natural drying, and the implementation thereof is not limited.
상기와 같이 되는 김서림 방지용 원단은, 파티클(Particle)이 극히 미량이고 흡수성이 우수하며, 잔유이온 등의 용출성분이 적고, 닦임성이 매우 우수하며 닦인 면을 재오염시키지 않는 특성이 있고, 내세탁성 또한 우수한 것으로,The anti-fog fabric as described above has a very small amount of particles and excellent water absorption, less elution components such as residual ions, very excellent wiping property, and does not recontaminate the wiped surface, and wash-resistant The castle is also excellent,
안경용 클리너, 카메라 렌즈 클리너, 자동차용 클리너, 와이퍼(wiper), 가정이나 호텔 등의 욕실이나 창문의 성에나 김서림 방지 등의 분야에 적용될 수 있는 것일 뿐만 아니라, 하드디스크 또는 플로피 디스크의 제조공정, 액정의 편광판, CD 및 MD의 제조공정, VIDEO DECK 제조공정, 콘텍트렌지의 제조공정, 카메라 에셈블리(Assembly), 프린트 기판의 청소, 의약품 제조공정, 영화필름의 청소, 반도체 및 집적회로의 제조공정, 정밀도장 전의 청소 등의 다양한 분야에 응용될 수 있는 것이다. It is not only applicable to fields such as eyeglass cleaners, camera lens cleaners, car cleaners, wipers, bathrooms or windows in homes and hotels, but also in the manufacture of hard disks or floppy disks, and liquid crystals. Polarizer, CD and MD manufacturing process, video deck manufacturing process, contact manufacturing process, camera assembly, printed board cleaning, pharmaceutical manufacturing process, film film cleaning, semiconductor and integrated circuit manufacturing process, It can be applied to various fields such as cleaning of precision field.
상기 본 발명에 따른 김서림 방지용 원단의 김서림 방지 성능을 테스트한 결과는 다음과 같았다.The results of testing the antifogging performance of the antifogging fabric according to the present invention was as follows.
먼저, 테스트 방법으로는 테스트 시편(안경)을 물로 깨끗이 닦고, 이를 건조한 후에 본 발명에 따른 김서림 방지원단(75D N/P 니트극세사 편물)(실시예)과 일반원단(비교예)으로 시편을 각각 5회 반복하여 닦은 후, 하기 조건하에서 김서림이 사라지는 시간을 체크하였다.(상기 테스트는 육안으로 측정하였다.)First, as a test method, the test specimen (glasses) is wiped clean with water, and after drying it, the antifogging fabric (75D N / P knit microfiber knitted fabric) according to the present invention (Example) and the general fabric (Comparative Example), respectively After wiping five times repeatedly, the time at which the steaming disappears was checked under the following conditions. (The test was visually measured.)
조건 1. 시편을 가볍게 제공된 원단으로 5회 닦고, 상기 시편을 100℃ 정도의 수면 5cm 높이에서 5초간 노출시킨 후, 김이 완전히 사라진 시간을 체크하였다.(이때 상기 시편은 물에 젖지 않도록 한다.)Conditions 1. Wipe the specimen five times with a lightly provided fabric, and expose the specimen for 5 seconds at a height of 5 cm on the surface of water at 100 ° C., and then check the time when the steam disappeared completely. )
조건 2. 시편을 제공된 원단으로 5회 닦은 후 -10℃의 조건하에서 시편을 10초간 노출하고, 김이 사라지는 시간을 측정하였다.Conditions 2. After wiping the specimen five times with the provided fabric, the specimen was exposed for 10 seconds under the condition of −10 ° C., and the time for disappearing of the steam was measured.
또한, 상기 원단을 5회 세탁한 후, 상기와 동일한 조건으로 김이 사라지는 시간을 측정하였다. (세탁처리조건: KS K ISO 6330:2001, 6B 40℃, 망건조)In addition, after washing the fabric five times, the time for disappearing the steam under the same conditions as described above was measured. (Washing conditions: KS K ISO 6330: 2001, 6B 40 ℃, net drying)
그 측정결과는 하기 표 1과 같았다.The measurement results are shown in Table 1 below.
상기 표 1에서 확인할 수 있는 바와 같이, 본 발명에 따른 김서림 방지용 원단은 김서림 방지효과가 우수함을 확인할 수 있었다. 또한 5회 세탁후에도 그 효과가 지속되어 세탁성 또한 우수함을 확인할 수 있었다.As can be seen in Table 1, the antifogging fabric according to the present invention was confirmed that the antifogging effect is excellent. In addition, the effect persists even after five washes, and it was confirmed that washing performance was also excellent.
이상에서와 같이, 본 발명은 상기한 실시예에 한하여 설명하였지만, 반드시 이를 한정하는 것은 아닌 것으로, 본 발명의 범주와 사상을 벗어나지 않는 범위 내에서 다양한 변형 실시가 가능함은 물론이다.As described above, the present invention has been described with reference to the above embodiments, but it is not necessarily limited thereto, and various modifications can be made without departing from the scope and spirit of the present invention.
Claims (8)