KR100370466B1 - Film for inkjet printer - Google Patents
Film for inkjet printer Download PDFInfo
- Publication number
- KR100370466B1 KR100370466B1 KR10-2000-0034834A KR20000034834A KR100370466B1 KR 100370466 B1 KR100370466 B1 KR 100370466B1 KR 20000034834 A KR20000034834 A KR 20000034834A KR 100370466 B1 KR100370466 B1 KR 100370466B1
- Authority
- KR
- South Korea
- Prior art keywords
- film
- weight
- parts
- inkjet printer
- receiving layer
- Prior art date
Abstract
본 발명은 잉크젯 프린터용 필름에 관한 것이다.The present invention relates to a film for an inkjet printer.
본 발명은, 수지제의 기재 필름의 일측면 또는 양측면에 잉크 수용층이 형성되는 구조를 지니며, 상기 잉크 수용층을 형성하는 코팅액 조성물은 비닐피롤리논과 아크릴의 공중합체, 폴리비닐피롤리덴 단독중합체, 폴리비닐알콜 단독중합체로 구성되는 바인더와 충진제와 혼합용매를 적용하여 구성되는 것을 특징으로 한다.The present invention has a structure in which an ink receiving layer is formed on one side or both sides of a base film made of a resin, and the coating liquid composition for forming the ink receiving layer is a copolymer of vinylpyrrolidone and acrylic, and a polyvinylpyrrolidin homopolymer. It is characterized by comprising a binder, a filler and a mixed solvent consisting of a polyvinyl alcohol homopolymer.
따라서, 본 발명의 목적은 기재 필름상에 잉크 수용층의 단일 코팅층 만을 형성함으로서 제조비용을 낮추고, 잉크 수용층에서 충진제의 함유량을 극소화함으로서 잉크 수용층의 경도, 표면의 평활도, 투명성을 향상시킨다.Accordingly, an object of the present invention is to reduce the manufacturing cost by forming only a single coating layer of the ink receiving layer on the base film, and to improve the hardness, surface smoothness and transparency of the ink receiving layer by minimizing the content of the filler in the ink receiving layer.
Description
본 발명은 잉크젯 프린터의 필름에 관한 것으로, 더욱 상세하게는, 잉크젯 프린터의 기재 필름상에 잉크 수용층의 단일 코팅층 만을 형성함으로서 제조비용을 낮추고, 또, 잉크 수용층에서 충진제의 함유량을 극소화함으로서 잉크 수용층의 경도, 표면의 평활도, 투명성을 향상시키는 잉크젯 프린터의 필름에 관한 것이다.The present invention relates to a film of an inkjet printer, and more particularly, to lowering the manufacturing cost by forming only a single coating layer of the ink receiving layer on the base film of the inkjet printer, and to minimizing the content of the filler in the ink receiving layer, It is related with the film of the inkjet printer which improves hardness, the smoothness of a surface, and transparency.
프린터의 방식 중 잉크젯 프린터 방식은 그 인쇄 속도가 빠르고 가격이 낮은 장점이 있는 반면, 최근에는 고해상도의 인쇄가 가능해졌기 때문에 이용도가 크게 증가되고 있다.The inkjet printer method of the printer method has the advantage that the printing speed and the price is low, while the use of the high-resolution printing has recently been increased significantly.
이러한 잉크젯 프린터는 최근에는 주로 오버헤드 프로젝트에 적용되는 프리젠테이션도구로 활용되고 있는데, 외벽 장식이나 디자인, 광고분야에서도 다양하게 적용될 수 있다.These inkjet printers are used as a presentation tool mainly applied to overhead projects in recent years, and may be applied to exterior wall decoration, design, and advertisement fields.
또한, 잉크젯 프린터는 잉크젯 프리터용 필름을 비롯하여 일반 용지, 코팅된 전용용지, 봉투에 사용되는 라벨 등 다양한 기록매체에 대해 포괄적으로 사용할 수 있다는 장점이 있다.In addition, the inkjet printer has an advantage that it can be comprehensively used for a variety of recording media, such as a film for the inkjet printer, plain paper, coated special paper, envelopes.
이러한 기록매체중 하나인 잉크젯 프린터용 필름의 일반적인 구조 및 구성성분을 도1을 참조하여 살펴보면 다음과 같다.The general structure and components of an inkjet printer film, which is one of such recording media, will be described with reference to FIG.
즉, 그 모체를 형성하는 수지재의 기재 필름(1)상에 잉크를 흡수하여 색상을 발하게 되는 잉크 수용층(2)이 형성된다.That is, the ink receiving layer 2 which absorbs ink and gives a color is formed on the base film 1 of the resin material which forms the mother body.
또, 상기 잉크 수용층(2)의 표면에는 상기 잉크 수용층(2)를 보호하고 잉크의 분산과 건조를 촉진시키는 기능을 하는 보호층(3)이 형성되어 있다.A protective layer 3 is formed on the surface of the ink receiving layer 2 to protect the ink receiving layer 2 and to promote the dispersion and drying of the ink.
또한, 상기 기재 필름(1)과 상기 잉크 수용층(2)의 사이에는 상기 잉크수용층(2)이 상기 기재 필름(1)에서 이탈되는 것을 방지하기 위하여 접착층(4)이 형성되어 있다.In addition, an adhesive layer 4 is formed between the base film 1 and the ink receiving layer 2 to prevent the ink receiving layer 2 from being separated from the base film 1.
상기 기재 필름(1)과 상기 잉크 수용층(2)을 형성하기 위한 코팅액 조성물은잉크의 주성분인 수성 염료와의 친화력이 높아서 잉크를 흡수하는 바인더와, 필름의 잉크 흡수력을 향상시키고 적용 보관시 필름들 사이의 밀착 현상을 방지하기 위한 충진제와 물성을 향상시키기 위한 각종 첨가제를 포함하며 용매로서는 물을 적용하는 경우가 많다.The coating liquid composition for forming the base film (1) and the ink receiving layer (2) has a high affinity with an aqueous dye, which is a main component of the ink, and a binder which absorbs ink, and improves the ink absorption of the film and the films during application storage. It contains a filler for preventing the adhesion phenomenon between and various additives for improving physical properties, and water is often applied as a solvent.
상기 잉크 수용층을 형성하는 코팅액 조성물중 바인더로 적용되는 수용성 고분자로는 적당한 분자량을 가지고 있는 폴리비닐피롤리돈, 폴리비닐알콜 등의 비닐계 고분자와, 폴리아크릴산, 폴리메틸메타크릴레이트 등의 아크릴계 고분자와, 폴리에틸렌 이민 등의 이민계 고분자 그리고 폴리에틸렌 옥사이드, 폴리프로필렌 옥사이드 등의 옥사이드계 고분자 등이 있다.As the water-soluble polymer applied as a binder in the coating liquid composition forming the ink receiving layer, a vinyl polymer such as polyvinylpyrrolidone and polyvinyl alcohol having an appropriate molecular weight, and an acrylic polymer such as polyacrylic acid and polymethyl methacrylate And imine-based polymers such as polyethylene imine and oxide-based polymers such as polyethylene oxide and polypropylene oxide.
또한, 상기 코팅액 조성물에 포함되는 충진제는 실리카, 티타늄 옥사이드, 알루미나, 탄산칼슘, 운모 등의 무기계의 충진제와 변성 스타치 등의 유기계의 총진제가 있다.In addition, the filler included in the coating solution composition includes inorganic fillers such as silica, titanium oxide, alumina, calcium carbonate, mica, and organic total fillers such as modified starch.
그 밖에도, 상기 코팅액 조성물에는 바인더, 충진제의 작용을 상승시키는 화합물과 제반 물성을 향상시키는 대전방지제, pH조절제 등의 첨가제가 포함된다.In addition, the coating liquid composition includes additives such as a binder, a compound for increasing the action of the filler, an antistatic agent for improving the physical properties, and a pH adjusting agent.
상기 코닝액 조성물에 적용되는 용매로는 물을 적용하는 경우가 많은데, 물을 용매로 사용할 경우에는 건조속도가 느리다는 문제점이 있다.As a solvent to be applied to the Corning liquid composition, water is often applied, but when water is used as a solvent, there is a problem that the drying speed is slow.
상기 코팅액 조성물에 있어서, 바인더로서 상기 고분자들의 단독중합체만을 적용하는 경우에는 잉크 수용층의 강도와 잉크 투과성이 부족하여 잉크 수용층의 표면에 보호층을 형성해야 하고, 또한 잉크 수용층이 기재 필름에서 이탈되기 쉬워서 기재 필름과 잉크 수용층 사이에 접착층을 형성해야 하므로, 공정 단계가 많아져서 생산성이 저하되고 제조비용이 높다는 문제점이 있다.In the coating liquid composition, when only the homopolymer of the above polymers is used as the binder, the strength of the ink receiving layer and the ink permeability are insufficient, so that a protective layer must be formed on the surface of the ink receiving layer, and the ink receiving layer is easily separated from the base film. Since the adhesive layer must be formed between the base film and the ink receiving layer, there are problems in that the number of process steps increases and the productivity is lowered and the manufacturing cost is high.
코팅액 조성물에 포함되는 충진제는 3 - 15 중량부를 적용하는데, 충진제의 양이 증가할수록 코팅 종료 후 용매의 건조 속도는 향상되지만, 과다 사용할 경우 잉크 수용층의 경도가 감소되며 표면의 평활도가 불량해져서 프리터에서의 성능이 저하되며 건조후 탁도가 심해져서 투명성이 저하된다는 문제점이 있다.The filler contained in the coating liquid composition is applied to 3 to 15 parts by weight, the drying rate of the solvent after the end of the coating increases as the amount of the filler is increased, but when used in excess, the hardness of the ink receiving layer is reduced and the surface smoothness is poor, so There is a problem that the performance is lowered and the turbidity after drying is worse, the transparency is lowered.
상기 문제점들을 개선하려는 많은 연구개발이 진행되어, 일본 공개특허 소 57-14091호에서는 잉크 수용층으로서 유기미립자를 60%이상 사용한 다공질층을 기재 필름상에 형성한 잉크젯 프린터용 필름이 개시되었지만, 투명성이 부족하였고 소수성 중합체를 적용하였기 때문에 잉크 흡수성능이 저하된다는 문제점이 발생 되었다.Although many research and developments have been made to improve the above problems, Japanese Laid-Open Patent Publication No. 57-14091 discloses an ink jet printer film in which a porous layer using at least 60% of organic fine particles as an ink receiving layer is formed on a base film. Insufficient and the hydrophobic polymer is applied, the problem that the ink absorption performance is lowered.
또한 일본 공개특허 소 61-19389호에서는 폴리비닐알콜과 젤리틴으로 구성된 바인더에 입경 8 - 30mm인 실리카를 첨가한 잉크 수용층이 형성된 잉크젯 프린터용 필름이 개시되었지만, 음 이온화된 염료를 사용한 잉크로 인쇄시 잉크의 정착성과 건조성이 저하되는 문제점이 있다.In addition, Japanese Patent Laid-Open No. 61-19389 discloses an ink jet printer film having an ink receiving layer in which silica having a particle size of 8 to 30 mm is added to a binder composed of polyvinyl alcohol and gelatin, but is printed with ink using an anionized dye. There is a problem in that the fixing property and drying property of the ink decreases.
또한 일본 공개특허 평 7-25133호에서는 기재 필름상에 평균 입경 5 - 15㎛ 구상 미립자 고분자를 함유하는 수용성 코팅액을 상기 구상 미립자의 평균 입경보다 얇은 두께로 코팅하는 잉크 수용층이 형성된 잉크젯 프린터용 필름이 개시되었지만, 내수성과 내약품성이 저하되는 문제점이 있다.In addition, Japanese Patent Laid-Open No. 7-25133 discloses an ink jet printer film having an ink receiving layer for coating a water-soluble coating liquid containing an average particle diameter of 5-15 μm spherical particulate polymer on a base film with a thickness smaller than the average particle diameter of the spherical fine particles. Although disclosed, there is a problem that the water resistance and chemical resistance is lowered.
본 발명의 목적은 기재 필름상에 잉크 수용층의 단일 코팅층 만을 형성함으로서 제조비용이 낮은 잉크젯 프린터용 필름을 제공하는데 있다.SUMMARY OF THE INVENTION An object of the present invention is to provide a film for an inkjet printer having low manufacturing cost by forming only a single coating layer of an ink receiving layer on a base film.
본 발명의 또다른 목적은 잉크 수용층에서 충진제의 함유량을 극소화함으로서 잉크 수용층의 경도, 표면의 평활도, 투명성이 향상되는 잉크젯 프린터용 필름을 제공하는데 있다.It is still another object of the present invention to provide a film for an ink jet printer in which the hardness, surface smoothness and transparency of the ink receiving layer are improved by minimizing the content of the filler in the ink receiving layer.
도 1은 종래의 기술에 의한 잉크젯 프린터용 필름의 단면도.1 is a cross-sectional view of a film for an ink jet printer according to the prior art.
도 2는 본 발명에 의한 잉크젯 프린터용 필름의 단면도.2 is a cross-sectional view of a film for an inkjet printer according to the present invention.
*** 도면의 주요부분에 대한 부호의 설명 ****** Explanation of symbols for main parts of drawing ***
1 : 기재 필름1: base film
2 : 잉크 수용층2: ink receiving layer
3 : 보호층3: protective layer
4 : 접착층4: adhesive layer
상기한 목적을 달성하기 위하여 본 발명은, 수지제의 기재 필름의 일측면 또는 양측면에 잉크 수용층이 형성되는 구조를 지니며, 상기 잉크 수용층을 형성하는 코팅액 조성물은 비닐피롤리논과 아크릴의 공중합체, 폴리비닐피롤리덴 단독중합체, 폴리비닐알콜 단독중합체로 구성되는 바인더와 충진제와 혼합용매를 적용하여 구성되는 것을 특징으로 하는 잉크젯 프린터용 필름을 제공한다.In order to achieve the above object, the present invention has a structure in which the ink receiving layer is formed on one side or both sides of the base film made of a resin, the coating liquid composition for forming the ink receiving layer is a copolymer of vinylpyrrolidone and acrylic, Provided is a film for an inkjet printer, comprising a binder, a filler, and a mixed solvent composed of a polyvinylpyrrolidin homopolymer and a polyvinyl alcohol homopolymer.
바람직하게는, 본 발명에 따른 잉크젯 프린터용 필름의 코팅액 조성물에서 바인더는 비닐피롤리돈과 아크릴의 공중합체 5 ∼ 15중량부, 폴리비닐피롤리덴 단독중합체 5 ∼ 15중량부, 폴리비닐알콜 단독중합체 15 ∼ 25중량부로 구성되는 것이 바람직하다.Preferably, in the coating liquid composition of the inkjet printer film according to the present invention, the binder is 5 to 15 parts by weight of a copolymer of vinylpyrrolidone and acrylic, 5 to 15 parts by weight of polyvinylpyrrolidin homopolymer, and polyvinyl alcohol alone. It is preferable that it consists of 15-25 weight part of polymers.
바람직하게는, 본 발명에 따른 잉크젯 프린터용 필름에서 상기 코팅액 조성물에서 충진제로는 실리카를 0.005 ∼ 0.2 중량부 적용하는 것이 바람직하다.Preferably, 0.005 to 0.2 parts by weight of silica is preferably applied as the filler in the coating liquid composition in the film for an ink jet printer according to the present invention.
또한 바람직하게는, 본 발명에 따른 잉크젯 프린터용 필름에서 상기 코팅액 조성물에 적용되는 혼합용매는 물 37 ∼ 47중량부, 알콜 42 ∼ 52중량부, 용매 혼화제 0.005 ∼ 1.0 중량부를 적용하며 조성되는 것이 바람직하다.Also preferably, in the inkjet printer film according to the present invention, the mixed solvent applied to the coating solution composition is preferably 37 to 47 parts by weight of water, 42 to 52 parts by weight of alcohol, and 0.005 to 1.0 parts by weight of a solvent admixture. Do.
또한 바람직하게는, 본 발명에 따른 잉크젯 프린터용 필름에서 상기 혼합용매에 적용되는 경화제는 멜라민인 것이 바람직하다.Also preferably, in the film for ink jet printers according to the present invention, the curing agent applied to the mixed solvent is preferably melamine.
또한 바람직하게는, 상기 기재 필름을 폴리에틸렌 테레프탈레이트 필름이고, 투명 또는 백색 필름중 하나로 구비되는 것이 바람직하다.Also preferably, the base film is a polyethylene terephthalate film and is preferably provided as one of a transparent or white film.
또한 바람직하게는, 상기 비닐피롤리덴과 아크릴의 공중합체를 합성하기 위한 중합조성물중 아크릴계 모노머는 15 ∼ 25중량부, 비밀피롤리돈 모노머는 15 ∼ 25중량부이며, 혼합용매를 포함하는 것이 바람직하다.Also preferably, the acrylic monomer is 15 to 25 parts by weight, the secret pyrrolidone monomer is 15 to 25 parts by weight in the polymerization composition for synthesizing the copolymer of vinylpyrrolidene and acrylic, and contains a mixed solvent. desirable.
또한 바람직하게는, 상기 아크릴계 모노머의 공중합체는 아크릴계 모노머로서 디메틸 아크릴아미드, 아크릴산, 타이드록시에틸 메타크릴레이트 중 적어도 한가지를 적용하는 것이 바람직하다.Also preferably, the copolymer of the acrylic monomer is preferably at least one of dimethyl acrylamide, acrylic acid, and hydroxyethyl methacrylate as the acrylic monomer.
이하에서는 본 발명에 따른 잉크젯 프린터용 필름의 바람직한 실시예를 첨부된 도면을 참조하여 상세히 설명한다.Hereinafter, with reference to the accompanying drawings, a preferred embodiment of a film for an inkjet printer according to the present invention will be described in detail.
도 2를 참조하면 본 발명에 의한 잉크젯 프린터용 필름은 기재 필름(1)상에 잉크 수용층(2)이 단일층으로 형성되는 구조이며, 상기 잉크 수용층(2)을 형성하는 코팅액 조성물은 비닐롤리돈과 아크릴 공중합체와 폴리비닐피롤리덴 단독중합체, 폴리비닐알콜 단독중합체로 구성되는 바인더와 실리카로 구성되는 충진제, 각종 첨가제로 구성되며 용매는 알콜과 물의 혼합용매로 구비된다.Referring to FIG. 2, the film for an inkjet printer according to the present invention has a structure in which an ink receiving layer 2 is formed as a single layer on a base film 1, and the coating liquid composition forming the ink receiving layer 2 is vinylrollidone. And an acrylic copolymer, a polyvinylpyrrolidene homopolymer, a binder composed of a polyvinyl alcohol homopolymer, a filler composed of silica, and various additives. The solvent is provided with a mixed solvent of alcohol and water.
상기 기재 필름으로는 폴리에틸렌 테레프탈레이트 필름이나 셀롤로오스 아세테이트 필름, 폴리에틸렌 필름, 폴리프로필렌 필름이 적용된다.As said base film, a polyethylene terephthalate film, a cellulose acetate film, a polyethylene film, and a polypropylene film are applied.
상기 기재 필름은 투명 또는 백색 필름 모두 적용 가능하고, 두께는 80∼120㎛의 범위내에 속하는 것이 바람직하다.It is preferable that both the said base film is applicable to a transparent or white film, and thickness exists in the range of 80-120 micrometers.
만일 상기의 범위를 벗어나게 되면 프린팅에 적합하지 않다.If it is out of the above range, it is not suitable for printing.
바람직하게, 기재 필름(q)으로는 코팅액 조성물과 집합성이 우수한 폴리에틸렌 데레프달레이트 필름이 적용된다.Preferably, as the base film (q), a coating solution composition and a polyethylene delevalate film having excellent collection properties are applied.
상기 잉크 수용층을 형성하는 코팅액 조성물중에서 바인더는 비닐피롤리돈과 아크릴의 공중합체, 폴리비닐피롤리덴 단독중합체, 폴리비닐알콜 단독중합체로 구성된다.In the coating liquid composition forming the ink receiving layer, the binder is composed of a copolymer of vinylpyrrolidone and acrylic, a polyvinylpyrrolidin homopolymer, and a polyvinyl alcohol homopolymer.
그 중에서 비닐피롤리덴 단독중합체 또는 폴리비닐알콜 단독중합체로 구성된다.Among them, it is composed of vinylpyrrolidin homopolymer or polyvinyl alcohol homopolymer.
상기 비닐피롤리덴은 기재 필름과의 접합성이 뛰어나며 충진제와의 혼화성도 우수하다. 또한 폴리비닐알콜은 내수성과 알콜에 대한 용해도가 우수하여 물과 알콜의 혼합용매에 적합한 특징을 지니고 있다.The vinylpyrrolidene is excellent in adhesion to the base film and excellent in compatibility with the filler. In addition, polyvinyl alcohol has excellent features in water and alcohol solubility in water and alcohol mixed solvents.
구체적으로 바인더는 비닐피롤리돈과 아크릴의 공중합체 5 ∼ 15중량부, 폴리비닐롤리덴 단독중합체 5 ∼ 15중량부, 폴리비닐알콜 단독중합체 15 ∼ 25중량부로 구성된다.Specifically, the binder is composed of 5 to 15 parts by weight of a copolymer of vinylpyrrolidone and acryl, 5 to 15 parts by weight of polyvinylidene homopolymer, and 15 to 25 parts by weight of polyvinyl alcohol homopolymer.
상기 비닐피롤리돈과 아크릴의 공중합체를 중합하기 위한 중합조성물은 아크릴계 모노머로서 디데틸 아크릴아미노, 아크릴산, 하이드록시에틸 메타크릴레드 중 적어도 한가지를 적용하며, 비닐피롤리돈 모노머는 15 ∼ 25중량부, 아크릴계 모노머는 15 ∼ 25중량부가 적용되고 일반적인 중합개시제가 적용되며 용매는 물과 알콜의 혼합용매가 적용된다.The polymerization composition for polymerizing the copolymer of vinylpyrrolidone and acryl is at least one of didecyl acrylamino, acrylic acid, and hydroxyethyl methacrylate as an acrylic monomer, and a vinylpyrrolidone monomer is 15 to 25 weight. In addition, 15-25 weight part of acryl-type monomers are applied, a general polymerization initiator is applied, and the solvent is a mixed solvent of water and alcohol.
또한, 종래 기술에 따른 코팅액 조성물에는 필름의 잉크 흡수력과 용매의 건조속도를 증가시키고, 적충 보관시 필름들 사이의 밀착 현상을 방지하기 위하여 충진제를 3 ∼ 15중량부 포함하지만, 본 발명에 따른 코팅액 조성물에서는 비닐피롤리돈과 아크릴의 공중합체의 잉크 흡수력과 상기 혼합용매의 증발성이 우수하므로, 충진제는 단지 필름을 적충 보관할 때 필름들 사이의 밀착 현상을 방지할 목적으로 소량 함유된다.In addition, the coating liquid composition according to the prior art includes 3 to 15 parts by weight of a filler in order to increase the ink absorption power of the film and the drying speed of the solvent, and to prevent adhesion between the films during storage, but the coating liquid according to the present invention. In the composition, since the ink absorption ability of the copolymer of vinylpyrrolidone and acryl and the evaporation property of the mixed solvent are excellent, a filler is contained in a small amount only for the purpose of preventing adhesion between the films when the film is properly stored.
바람직하게는, 친수성이 우수한 실리카를 0.005 ∼ 0.2중량부 적용한다.Preferably, 0.005-0.2 weight part of silica excellent in hydrophilicity is applied.
상기 코팅액 조성물의 용매를 물만을 단독적으로 적용하게 되면 코팅 후의 건조시간이 증가되기 때문에, 물에 비해 증발성이 우수한 알콜을 코팅액의 물성이 저하되지 않은 범위내에서 물과 적당량 혼합하고 물과 알콜의 혼화성을 향상시키는 용매 혼화제를 소량 첨가하는 혼합용매를 적용한다.If only the solvent of the coating liquid composition is applied to water alone, the drying time after coating increases, so that an alcohol having excellent evaporation property compared to water is mixed with an appropriate amount of water within a range in which the physical properties of the coating liquid are not degraded, The mixed solvent which adds a small amount of solvent admixtures which improves miscibility is applied.
바람직하게, 상기 혼합용매는 물 37 ∼ 47중량부, 알콜 42 ∼ 52중량부, 용매 혼화제 0.005 ∼ 1.0중량부를 혼합하여 조성된다.Preferably, the mixed solvent is formed by mixing 37 to 47 parts by weight of water, 42 to 52 parts by weight of alcohol, and 0.005 to 1.0 parts by weight of a solvent admixture.
그 밖에도, 상기 코팅액 조성물에는 동상의 분산제, 대전방지제, pH조절제 등의 첨가제가 포함된다.In addition, the coating liquid composition may include additives such as a frostbite dispersant, an antistatic agent, and a pH adjuster.
일반적으로 잉크 수용중의 단위면적당 코팅 도포량이 클수록 잉크 흡수도가 증가하는 경향이지만, 일정한 코팅 도포량에 도달하면 더 이상 잉크 흡수도는 증가되지 않는다.In general, the greater the amount of coating applied per unit area in the ink reception tends to increase the ink absorbency, but once the constant amount of coating is reached, the ink absorption no longer increases.
⑴ 비닐피롤리돈과 아크릴의 공중합체 합성합성 copolymerization of vinylpyrrolidone with acrylic
중합조에 디메틸 아크릴아미드, 아크릴산, 하이드록시에틸 메타-릴레이드의 아크릴모노머, 증류수와 공업용 메탄올의 혼합용매, 중합개시제로서 아조미스이소부딜로니트릴을 넣고 90℃에서 500pm의 속도로 3∼4시간동안 교반시켜 비닐피롤리돈과 아크릴의 공중합체를 합성한다.Dimethyl acrylamide, acrylic acid, hydroxyethyl meta-relay acryl monomer, mixed solvent of distilled water and industrial methanol, and azomisisobutyronitrile as polymerization initiators were added to the polymerization tank at a temperature of 500 pm at 90 ° C. for 3 to 4 hours. By stirring, a copolymer of vinylpyrrolidone and acryl is synthesized.
⑵ 코팅액 조성물의 형성⑵ Formation of coating liquid composition
반응기에 바인더로서 상기 공중합체와 폴리비닐피롤리덴 단독중합체, 폴리비닐알콜 단독중합체와 잉크 흡수제로서 실리카, 용매로서 증류수와 공업용 메탄올의 혼합용매를 넣고 상온에서 교반하여 코팅액 조성물을 형성한다.In the reactor, a copolymer, a polyvinylpyrrolidene homopolymer, a polyvinyl alcohol homopolymer, a silica as an ink absorbent, a mixed solvent of distilled water and industrial methanol as a solvent are added and stirred at room temperature to form a coating solution composition.
⑶ 잉크 수용층 형성⑶ Form ink receiving layer
기재 필름상에 상기 코팅액 조성물을 도포하고, 두께 조절기구를 사용하여 도포물의 두께와 코팅 도포량을 조절하고, 건조시켜 잉크 수용층을 형성한다.The coating liquid composition is coated on the base film, and the thickness adjusting mechanism is used to adjust the thickness of the coating and the coating amount, and to dry, thereby forming an ink receiving layer.
⑷ 권취⑷ winding
잉크 수용층이 형성된 필름을 용도에 따른 소정의 크기로 권취한다.The film in which the ink receiving layer is formed is wound to a predetermined size according to the use.
본 발명에 의한 잉크젯 프린터용 필름은 기재 필름상에 잉크 수용층의 단일코팅층만을 형성하고 보호층과 접착층이 생략됨으로서, 제조 공정이 단순화되고 제조비용이 낮다.The film for an ink jet printer according to the present invention forms only a single coating layer of the ink receiving layer on the base film and omits the protective layer and the adhesive layer, thereby simplifying the manufacturing process and lowering the manufacturing cost.
또한, 상기 잉크젯 프린터용 필름은 잉크 수용층의 충진제 함량이 극소화도기 때문에 잉크 수용층의 경도, 표면의 평활도, 투명성이 우수한다.In addition, the inkjet printer film is excellent in hardness, surface smoothness and transparency of the ink receiving layer because the filler content of the ink receiving layer is minimized.
지금까지는 본 발명의 실시 예에 대하여 한정하여 도시하고 또 설명하였지만 이에 한정되지 않고 당 분야에서 통상의 지식을 가진 자에 의해 다양한 변경 사용이 가능하다.So far, the embodiments of the present invention have been illustrated and described with reference to the present invention. However, the present invention is not limited thereto, and various modifications can be used by those skilled in the art.
그러나, 그와 같은 단순한 변경은 본 발명의 권리범위에 속함이 명백하다.However, such a simple change is obviously included in the scope of the present invention.
Claims (8)