Abstract

PROBLEM TO BE SOLVED: To obtain a laminate transferable and freely drawable on a surface by a printer. SOLUTION: The laminate comprises a clear layer 22 made of at least one layer and having physical properties fixable with at least any of a thermal transfer ink, ink jet ink, toner, aqueous ink, oily ink, printing ink, pencil, crayon, paints, and Indian ink, light transmittance for transmitting a light for recognizing a skin of an object when it is brought into contact with the object and a water resistance, an adhesive layer 22 formed on one surface of the layer 21 and having water resistance, and a mounting sheet 24 stuck on the layer 22 via a water soluble paste layer 23.

Description

DETAILED DESCRIPTION OF THE INVENTION

[0001]

BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a transfer laminate capable of drawing on the surface.

[0002]

2. Description of the Related Art Conventionally, tattoo stickers shown in FIGS. 7 to 9 have been known as laminates. This tattoo sticker A
Is formed by sequentially laminating a water-soluble glue layer 2, an ink layer 3, an adhesive layer 4, and a release paper 5 on one side of a transfer paper 1.
In this tattoo seal A, the release paper 5 is peeled off as shown in FIG. 8, and then the transfer paper 1 is immersed in water to wet the water-soluble glue layer 2. Further, as shown in FIG. 9, when the adhesive layer 4 is applied to the skin 6 and the transfer paper 1 is slid in the plane direction, the adhesive layer 4 adheres to the skin 6. Since the tattoo pattern composed of the ink layer 3 is printed on the adhesive layer 4, it looks as if the tattoo is drawn on the skin 6.

In this tattoo seal A, the expansion and contraction of the skin 6
The ink layer 3 or the pressure-sensitive adhesive layer 4 is easily broken due to vibration and deformation, and the pressure-sensitive adhesive layer 4 is cracked and difficult to peel off when peeled off. is there.

Therefore, in order to solve such a problem, as shown in FIG.
Tattoo ink layer 9, stretchable clear layer 10, adhesive layer 1
1, a tattoo sticker B having a layer structure in which release paper 12 is sequentially formed
There is.

[0005] This tattoo sticker B uses the actual applicant No. 7-38154 of Cosmotec Co., Ltd., and the tattoo sticker B peels off the release paper 12 and puts water on the transfer paper 7. The adhesive layer 1 on the desired skin portion 13
When the transfer paper 7 is slid in the plane direction, as shown in FIG. 11, the adhesive layer 11 is attached to the skin 13 because the water-soluble glue layer 8 is melted.

[0006] Since the stretchable clear layer 10 and the ink layer 9 are formed on the pressure-sensitive adhesive layer 11, the skin 13 looks as if a tattoo has been made. Since the ink clear layer 10 supports the ink layer 9, even if the skin 13 contracts, deforms, or vibrates, the ink layer 9 does not break or separate, and there are also problems such as a tattoo seal A. Will be resolved. Further, since the stretchable clear layer 10 is present, even when the stretchable clear layer 10 is peeled off from the skin 13, the stretchable clear layer 10 can be peeled off integrally, and there is no problem that the broken tattoo adheres to the skin 13 and remains.

[0007]

However, the tattoo sticker B can solve the problems such as cracking of the tattoo of the tattoo sticker A, difficulty in peeling the tattoo from the skin 6, and rough skin due to scraping. The water-soluble glue layer 8 is formed by printing on one side, and then the ink layer 9 is printed on the water-soluble glue layer 8, and the stretchable clear layer 10 and the pressure-sensitive adhesive layer 11 are sequentially printed. .

[0008] For this reason, a tattoo pattern is determined at the time of printing the ink layer 9, and there is a disadvantage in that it is difficult to select a pattern according to various preferences. The same applies to the tattoo seal A.

[0009] The laminate of the present invention is made by paying attention to a conventional tattoo sticker, and a pattern can be freely printed by an image processing program or the like by a printer connected to information equipment such as a personal computer. Moreover, it is an object to provide a transferable laminate.

[0010]

In order to solve the above-mentioned problems, a laminate according to the first aspect of the present invention comprises a thermal transfer ink, an inkjet ink, a toner, a water-based ink, an oil-based ink,
Physical properties capable of fixing at least one of printing ink, pencil, crayon, paint, and black ink, at least light transmissivity that transmits light capable of recognizing the background of the object when brought into contact with the object, and water resistance A film comprising at least one layer having a water-resistant pressure-sensitive adhesive layer is formed on one side of the film, and a water-soluble or water-swellable glue layer is interposed in the pressure-sensitive adhesive layer. And a backing sheet is attached.

[0011] A laminate according to a second aspect of the present invention is the laminate according to the first aspect, wherein the film has elasticity.

The laminate according to claim 3 of the present invention is characterized in that
3. The laminate according to claim 2, wherein a surface of the film exposed to the outside air has been subjected to at least one of a matting treatment, a matte treatment, a rough surface treatment, and an unevenness forming treatment.

The laminate according to claim 4 of the present invention is characterized in that:
4. The laminate according to claim 3, wherein at least one of the thermal transfer ink, the inkjet ink, the toner, the water-based ink, the oil-based ink, the printing ink, the pencil, the crayon, the paint, and the black is provided on the surface of the film exposed to the outside air. Wherein a fixing enhancement process capable of fixing is performed.

The laminate according to claim 5 of the present invention is characterized in that:
5. The laminate according to claim 4, wherein the pressure-sensitive adhesive layer is peelable from at least one of skin, leather, plastic, rubber, metal, glass, paper, cloth, plant, ceramic, stone, and wood. It has a characteristic adhesive strength.

The laminate according to claim 6 of the present invention is characterized in that:
6. The laminate according to claim 5, wherein at least one of a cut line and a cut line is formed on at least the film and the backing sheet.

The laminate according to claim 7 of the present invention is characterized in that:
7. The laminate according to claim 6, wherein the film is printed in advance with a drawing margin left.

The laminate according to claim 8 of the present invention is characterized in that:
8. The laminate according to claim 7, wherein the laminate is printer paper.

According to the laminate of the first aspect of the present invention, the film is exposed on the surface, and at least one of thermal transfer ink, ink jet ink, toner, water-based ink, oil-based ink, printing ink, pencil, crayon, paint, and black ink. Since it has the property of fixing either one, drawing can be performed by a printer.

According to an image processing program of a recent personal computer, an image can be produced, an image can be taken in through a communication line, or a photographed image can be processed by a digital camera or a video camera. Some models are capable of direct printing. Therefore, it is possible to print various images in which the enlargement, shrinkage, layout editing, deformation, color correction, image framing frame, character string addition, etc. are performed in a desired form.

In particular, in a printer using a color thermal transfer ribbon, since the ink for drawing an image has water resistance, the image does not run off even if the image side is immersed in water. Further, even if the ink easily flows with water, such as a dye-based ink image of a current ink jet printer, the film has water resistance, so that if only the mount side is immersed in water, a color image will not flow. Even for a water-soluble ink image, the image can be prevented from flowing into water by coating the surface of the printed image with a new film or film after printing the image by the printer.

Further, since the film has a light-transmitting property to transmit light capable of recognizing the background of at least the object when the film is brought into contact with the object and transmits the color of the surface of the object to be attached, Unlike the impression like this, it is possible to see the contents when the object is transparent plastic or glass, and when the object is skin or leather, only the letters and patterns are put on the skin or leather surface You can make it look like it was displayed.

In the present invention, the film may be composed of one layer, but may be composed of a plurality of layers. When the image ink is water-resistant, the film may have a number of small holes to prevent stuffiness.

If the film has elasticity, the image may be broken even after the film is attached to the object, even if the object is soft, such as skin, leather, a plastic sheet, or rubber. And it can be peeled off at the time of peeling.

If the surface of the laminate has been subjected to at least one of a matting treatment, a matte treatment, a rough surface treatment, and an unevenness forming treatment, the laminate adheres to skin, nails, leather, plastic film and the like. In this case, the gloss is not generated or the gloss is low, and the change in the gloss of the surface with the object to be adhered is small, so if the object is adhered to a plastic film with irregularities on the skin, nails, leather, surface, etc. Because the difference from the surface is hard to see, the sense of unity is improved.

According to a fourth aspect of the present invention, there is provided a fixing enhancement process capable of fixing at least one of a thermal transfer ink, an ink jet ink, a toner, a water-based ink, an oil-based ink, a printing ink, a pencil, a crayon, a paint, and a black ink (for example, a fixing layer). , Rough surface treatment, etc.), the ink or the like on the film is fixed, and the drop of the ink or the like is prevented.

As described in the fifth aspect, by changing the adhesive according to the adhesive object, it is possible to transfer to various objects, and it is possible to select the difficulty of peeling by adjusting the adhesive force. Applications include tattoo stickers (skin), nail polish sheets (nail), and character design transfer stickers (leather, transparent plastic, glass, rubber, metal, paper, cloth, plant surfaces, ceramics, stone, wood).

According to a sixth aspect of the present invention, if at least a film is cut out or formed with a cut line, a desired image is drawn on a portion of a desired type by setting a format when printing by an image program of a personal computer. This makes it possible to separate the backing paper, the water-soluble glue layer, the adhesive, and the film without separating them with scissors or the like after drawing. In this case, a non-cut portion may be left in a part of the cut line without completely cutting the die.

According to a seventh aspect of the present invention, the film is printed in advance (for example, a border, a pattern, a number / symbol, a character string, a bar code, a hologram image, a national flag, an emblem, an insignia, etc.),
By enabling the desired drawing in the margin,
Drawing can be performed not only by printing with a printer, but also by handwriting, stamping a plate, or the like.

According to the eighth aspect of the present invention, by forming the laminate into printer paper, it is possible to load the printer and draw freely.

[0030]

Next, a laminate according to a preferred embodiment of the present invention will be described with reference to the drawings.

FIG. 1 shows a cross-sectional structure of the laminate according to the embodiment. This laminate is a printer paper. The printer paper 20 has a water-resistant adhesive layer 22 formed on one side of a stretchable clear layer 21 as a film, and a water-soluble adhesive layer 23 on the adhesive layer 22. , A mount 24 is formed.

The total thickness of the printer paper 20 is 235 μm
± 30 μm, for example, A3, A4, A5, A6,
B4, B5, B6, and a size that can be printed by a commercially available printer of postcard size.

The stretchable clear layer 21 is formed of a thermal transfer ink (preferably a color ink, but may be a single color ink ribbon) of a thermal transfer ribbon used in a thermal transfer type printer, or an ink jet ink of an ink jet type printer. , Toner, having physical properties capable of fixing at least one of water-based ink, oil-based ink, printing ink, pencil, crayon, paint, black ink, and light transmittance,
It is made of a film having water resistance and a matte surface.

The composition of the stretchable clear layer 21 is as follows.
When a rubber component is a main component and at least a resin component is added, a plasticizer is usually added, but sometimes it is not added. In the case of a rubber component, it is not necessary to add a plasticizer.

As an example of the resin / rubber component, ethylene-
Olefinic copolymers such as vinyl acetate copolymer, ethylene-vinyl alcohol copolymer, ethylene-vinyl chloride copolymer, ethylene-acrylate copolymer, ethylene-acrylate-maleic anhydride copolymer, ethyl Acrylic resins such as acrylate-butyl acrylate copolymer, ethyl acrylate-vinyl acetate copolymer, one-pack type thermoplastic aliphatic urethane resins, polyamide resins, vinyl acetate resins, ethyl silicon and butyl Various silicone resins such as silicon, natural rubber,
SBR, chloroprene rubber, acrylic rubber, NBR, butyl rubber, isoprene rubber, urethane rubber, ethylene-
Various rubbers such as vinyl acetate copolymer rubber and silicone rubber are exemplified.

The components that can be added to the stretchable clear layer 21 include various fillers, various coloring agents, and other additives. Coloring agents include pigments, dyes, metal powders, fluorescent materials, phosphorescent materials, and fluorescent materials. Coloring includes various colors including white, metal colors, fluorescence, and phosphorescence.
A solvent is added as necessary in addition to the above components, and a film is formed by a method such as coating or printing.

The stretchable clear layer 21 is preferably a single layer, but may have a structure including a plurality of layers. The surface of the stretchable clear layer 21 is treated by matting or satin finish so as not to have luster. The matte-treated surface layer can fix the ink of the color ribbon by the thermal transfer printer. The stretchable clear layer 21 is made of a special elastomer and has a light transmitting property. The light transmissivity refers to a degree of transparency at which the color of the object can be seen through the naked eye at least when the object is brought into contact with the object, and the color and ground pattern of the object can be seen through. If present, coloring (white
(Including black and gray), and if the color of the object to be pasted or the color close to the color, the sense of unity with the object to be pasted can be further improved.

The surface of the stretchable clear layer 21 exposed to the outside air can be matte-treated, matte-finished, electric-discharge machined,
The processing is performed so that no gloss is generated or the gloss is reduced due to the formation of unevenness. When fine irregularities are formed on the stretchable clear layer 21, it is difficult to distinguish the irregularities from the surface of the skin, leather, nails, and the like, so that the sense of unity is further improved and the ink and the like placed on the surface are less likely to peel. In addition, it is possible to make the stretchable clear layer 21 water-resistant so that the dye-based ink does not flow into the water, but conversely, a large number of holes are formed or water-permeable is adhered. The water vapor of the skin may be released so that the adhered portion is not stuffy.

The thickness of the stretchable clear layer 21 is 3 to 50 μm,
Preferably it is 8 to 25 μm. If the thickness is less than 3μm,
Cracks and difficulty in peeling after use occur. When the thickness exceeds 50 μm, the film is too strong to follow the skin, leather, film and the like. In this embodiment, the thickness of the stretchable clear layer 21 is 17 μm ± 3 μm.

The stretchability of the stretchable clear layer 21 is determined by the strength against breakage and the modulus. The breaking strength of the stretchable clear layer 21 is 50 to 1000%, preferably 250 to 800%.
%. If the breaking strength is less than 50%, skin, leather,
The film cannot withstand bending or stretching. In order to improve the followability to the bending and expansion / contraction, 250% or more is desirable. When the breaking strength exceeds 1000%, stickiness occurs due to the flexibility of the stretchable clear layer, adhesion of dust and the like becomes remarkable, and peeling becomes difficult. Therefore, the stretchable clear layer 2
A preferable upper limit of the breaking strength of 1 is 800%.

The modulus of the stretchable clear layer 21 is 5 to 1
It is 50 kg / cm 2, preferably 15 to 80 kg / cm 2. 100
The% modulus is an index indicating elasticity,
If this is less than 5 kg / square cm, the pattern printed on the sticker when it is stuck on the skin is likely to collapse, and 150 kg / sq.
If it exceeds cm, the pattern tends to crack when it is attached to the skin.

The pressure-sensitive adhesive layer 22 formed on one side of the stretchable clear layer 21 is made of an acrylic resin and has a thickness of 8
μm ± 4 μm. The pressure-sensitive adhesive layer 22 has adhesiveness to skin, leather, and plastic. The adhesive strength of the adhesive layer 22 is 180 ° peel force according to JISZ0237, and is 0.9 mm ± 0.2 kg / 25 mm. The material of the adhesive layer 22 is rubber-based, acrylic-based, or silicon-based. The pressure-sensitive adhesive layer 22 is formed to cover the stretchable clear layer 21 by, for example, a screen printing method. When the pressure-sensitive adhesive layer 22 is used for skin, a pressure-sensitive adhesive such as a bandage is used. The value of the adhesive strength of the adhesive layer 22 measured in accordance with JIS-Z0237 exceeds 120 g / 25 mm width and is about 2000 g / 25 mm width or less.

The adhesive layer 22 has adhesiveness to at least one of rubber, metal, glass, paper, cloth, plant surface, ceramics, stone, wood, etc. Decoration and information display.

A mount 24 coated with a water-soluble glue layer 23 is attached to the lower surface of the adhesive layer 22. Water-soluble glue layer 2
No. 3 dissolves in water in 20 to 30 seconds. The mount 24 is white paper, and a water-soluble glue layer made of a water-soluble resin such as gelatin, CMC, or polyvinyl alcohol is coated on a paper having a property of absorbing water.

The printer paper 20 is, for example,
On one surface of the stretchable clear layer 21 as a film, a water-resistant pressure-sensitive adhesive layer 22 is applied by printing to form a backing sheet 24.
A water-soluble glue layer 23 is formed on the surface of the
The adhesive layer 22 is formed by bonding and cutting.

According to the printer paper 20 of this embodiment, since the stretchable clear layer 21 has light transmittance, is subjected to a matting process, and can fix the ink 25 of the color printer, as shown in FIG. Color printing can be performed on the surface of the conductive clear layer 21. After printing, cut out according to letters and patterns, apply water to the mount 24 and paste it on the skin 27 or the like.
(See FIG. 4) and, as shown in FIG. 5, so-called nail art such as nail polish on the nail 29 can be easily performed and easily peeled off.

In particular, due to light transmittance and matting effect,
Since the gloss and the background color such as labels and stickers are not visible or hard to see, it is possible to express the image as if directly painted on the skin 27, nails 29 and the like.

When adhered to leather, it is possible to create an expression as if printing or drawing was performed directly on leather due to the light transmittance and the matting effect. Adhesion to metal or plastic films, stones, ceramics, and fabrics makes it possible to temporarily decorate and display information and then peel it off to return it to its original state, or to display other decorations and information. If adhered to a plant, a white pattern (drawing) can be formed on the surface of the plant by blocking sunlight or the like.

In particular, since a program capable of creating or displaying a document on a personal computer or a program capable of displaying or creating an image can be freely printed on the surface of the elastic clear layer 21, fonts and image data can be displayed and created. By processing, a personal image can be easily displayed on various objects, and as shown in FIG. 6, the image 30 can be drawn multiple times to form the transfer seal 31.

The surface of the stretchable clear layer 21 may be preliminarily printed with a picture or border. Also, a cut line may be provided only on the stretchable clear layer 21 or on the mount 24. Although the laminate is the printer paper 20 in this embodiment, it is formed like a label in advance, and paints (oil-based, water-based), crayons, oil-based pens, water-based pens, line markers, colored pencils, pencils, ballpoint pens, ink, lipsticks, Drawing (including characters) may be made possible with cosmetics or the like. Further, by making it possible to support medicines, fragrances, chemicals, and the like, it is also conceivable that the wound is inconspicuously closed, the fragrance is supported, and chemical treatment is performed. Alternatively, printing may be performed while leaving a drawing margin on the stretchable clear layer 21, and drawing may be performed at a predetermined position by a format setting of a computer image program or a document creation program.

[0051]

According to the laminate of the first aspect of the present invention, the film is exposed on the surface, and the thermal transfer ink / inkjet ink, toner / water-based ink / oil-based ink / printing ink / pencil / crayon / paint / ink Has the property of fixing at least one of the above, so that drawing can be performed by a printer.

According to an image processing program of a personal computer in recent years, it is possible to produce an image, capture an image via a communication line, or process a photographed image of a digital camera, a video camera, or the like. Some models are capable of direct printing. Therefore, it is possible to print various images in which the enlargement, shrinkage, layout editing, deformation, color correction, image framing frame, character string addition, etc. are performed in a desired form.

In particular, in a printer using a color thermal transfer ribbon, since the ink for drawing an image has water resistance, the image does not run off even if the image side is immersed in water. Further, even with ink which easily flows with water, such as a dye-based ink image of a current ink jet printer, since the film has water resistance, a color image will not flow if only the mount side is immersed in water. Even for a water-soluble ink image, the image can be prevented from flowing into water by coating the surface of the printed image with a new film or film after printing the image by the printer.

Further, since the film has a light-transmitting property and transmits the color of the surface of the object to be affixed, unlike a label-like impression, when the object is a transparent plastic or glass, the contents can be removed. When the object is skin or leather, it can be seen as if only characters and pictures were displayed on the skin or leather surface.

If the film has elasticity, the image may be broken even after the film is attached to the object, even if the object is soft, such as skin, leather, a plastic sheet, or rubber. And it can be peeled off at the time of peeling.

When the surface of the laminate has been subjected to at least one of a matting treatment, a matte treatment, a rough surface treatment, and an unevenness forming treatment, the laminate adheres to the skin, nails, leather, plastic film and the like. In this case, the gloss is not generated or the gloss is low, and the change in the gloss of the surface with the object to be adhered is small, so if the object is adhered to a plastic film with irregularities on the skin, nails, leather, surface, etc. Because the difference from the surface is hard to see, the sense of unity is improved.

According to a fourth aspect of the present invention, there is provided a fixing enhancement process capable of fixing at least one of a thermal transfer ink, an ink jet ink, a toner, an aqueous ink, an oil ink, a printing ink, a pencil, a crayon, a paint, and a black ink (for example, a fixing layer). , Rough surface treatment, etc.), the ink or the like on the film is fixed, and the drop of the ink or the like is prevented.

As described in claim 5, by changing the pressure-sensitive adhesive according to the pressure-sensitive adhesive object, transfer to various objects can be performed, and the difficulty of peeling can be selected by adjusting the pressure-sensitive adhesive force. Applications include tattoo stickers (skin), nail polish sheets (nail), and character design transfer stickers (leather, transparent plastic, glass, rubber, metal, paper, cloth, plant surfaces, ceramics, stone, wood).

If at least the film is cut out or cut out as described in claim 6, a desired image is drawn on a desired type of part by setting a format when printing by an image program of a personal computer. This makes it possible to separate the backing paper, the water-soluble glue layer, the adhesive, and the film without separating them with scissors or the like after drawing. In this case, a non-cut portion may be left in a part of the cut line without completely cutting the die.

According to a seventh aspect of the present invention, the film is printed in advance (for example, a border, a pattern, a number / symbol, a character string, a bar code, a hologram image, a national flag, an emblem, an insignia, etc.),
By enabling the desired drawing in the margin,
Drawing can be performed not only by printing with a printer, but also by handwriting, stamping a plate, or the like.

According to the eighth aspect of the present invention, by forming the laminate into printer paper, it is possible to load the printer and freely draw images.

[Brief description of the drawings]

FIG. 1 is a sectional view showing a layer structure of a printer paper according to an embodiment of the present invention.

FIG. 2 is a cross-sectional view showing a layer structure in a state of being printed on the printer paper of FIG.

FIG. 3 is an explanatory diagram showing a layer structure of a portion to be transferred when the transfer is performed by applying water to a mount of printer paper cut after printing in FIG. 2;

FIG. 4 is an explanatory view showing a state in which a stretchable clear layer cut out after printing is attached to skin.

FIG. 5 is an explanatory view showing a state in which a stretchable clear layer cut out after printing is attached to a nail;

FIG. 6 is a reference drawing of a transfer sticker made of printed printer paper.

FIG. 7 is a sectional view showing a layer structure of a conventional tattoo seal A.

FIG. 8 is a cross-sectional view of a state in which release paper is removed from the tattoo seal A of FIG. 7;

FIG. 9 is an explanatory view showing a state in which the tattoo seal A of FIG. 7 is put on the skin, water is applied, and the transfer paper is peeled off;

FIG. 10 is a sectional view showing a layer structure of a conventional tattoo seal B.

11 is an explanatory view showing a state in which the tattoo sticker B of FIG. 10 is put on the skin, water is applied thereto, and the transfer paper is peeled off;

[Explanation of symbols]

 Reference Signs List 20 printer paper (laminate) 21 stretchable clear layer 22 adhesive layer 23 water-soluble glue layer 24 mount

────────────────────────────────────────────────── ─── Continued on the front page (51) Int.Cl. ⁶ Identification symbol FI B41M 3/12 B41M 3/12 G03G 7/00 G03G 7/00 A (72) Inventor Tsuyoshi Kobayashi 1-5 Taito, Taito-ku, Tokyo -1 Inside Toppan Label Co., Ltd.

Claims (8)

[Claims] 1. A heat transfer ink / ink jet ink, toner / water-based ink / oil-based ink / printing ink / pencil / crayon / paint / ink and at least one of the following properties: Light transmissivity that transmits light capable of recognizing the background of the object, and a film having at least one layer having water resistance, a water-resistant adhesive layer is formed on one surface of the film,
A laminate, wherein a mount is attached to the pressure-sensitive adhesive layer with a glue layer having at least one of a water-soluble property and a water-swellable property interposed therebetween. 2. The laminate according to claim 1, wherein said film has elasticity. 3. The laminate according to claim 1, wherein a surface of the film exposed to the outside air is subjected to at least one of a matting treatment, a matte treatment, a rough surface treatment, and an unevenness forming treatment. A laminate. 4. The laminate according to claim 1, wherein said thermal transfer ink, ink jet ink, toner, water-based ink, oil-based ink, printing ink, pencil, and crayon are provided on the surface of said film exposed to the outside air. ·paints·
A laminate, which has been subjected to a fixing enhancement process capable of fixing at least one of black ink. 5. The laminate according to any one of claims 1 to 4, wherein the pressure-sensitive adhesive layer comprises skin, leather, plastic, rubber, metal, glass, paper, cloth, plant, ceramic, stone,
A laminate having adhesive strength to at least one of trees. 6. The laminate according to claim 1, wherein at least one of a cut line and a cut line is formed on at least the film and the mount. . 7. The laminate according to claim 1, wherein the film is printed in advance with a drawing margin left. 8. The laminate according to claim 1, wherein said laminate is printer paper.