JPH1088079A - Self-adhesive fabric tape - Google Patents
Self-adhesive fabric tapeInfo
- Publication number
- JPH1088079A JPH1088079A JP24019196A JP24019196A JPH1088079A JP H1088079 A JPH1088079 A JP H1088079A JP 24019196 A JP24019196 A JP 24019196A JP 24019196 A JP24019196 A JP 24019196A JP H1088079 A JPH1088079 A JP H1088079A
- Authority
- JP
- Japan
- Prior art keywords
- film layer
- polyolefin film
- layer
- colored
- adhesive tape
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【0001】[0001]
【発明の属する技術分野】本発明は、養生、包装などに
使用される布粘着テープに係り、特に、織布を基材とす
る粘着テープにおいて、織布の背面カラーの色彩が鮮や
かで、かつ太陽光線などによる粘着剤の劣化が少なく、
耐候性に優れた布粘着テープに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a cloth adhesive tape used for curing, packaging and the like, and more particularly, to an adhesive tape based on a woven fabric, in which the color of the back color of the woven fabric is vivid, and There is little deterioration of the adhesive due to sunlight, etc.
The present invention relates to a cloth adhesive tape having excellent weather resistance.
【0002】[0002]
【従来の技術】従来、養生、包装などに使用される布粘
着テープは、一般に、スフ布または綿布に1層または2
層のポリエチレンフィルムを積層した加工布を基材とし
て、これに天然ゴム系粘着剤を塗工してなるものであ
り、粗面に対する接着の順応性が良く、また、手で簡単
に切断できることを特徴として、広く用いられている。
特に、養生用の布粘着テープは屋外使用の場合が多く、
風雨、太陽光線、気温変化などの過酷な条件下で使用さ
れる。しかしながら、従来の養生用布粘着テープは、1
〜2か月間の使用にもかかわらず、紫外線などによる粘
着剤の劣化、およびこれに起因する被着体への糊残りの
問題が生じる。この問題を解決するため、本発明者ら
は、登録実用新案公報の第3005686号において、
紫外線による粘着剤の劣化を防止するため、織布の背面
に紫外線の透過を遮断する黒色のポリエチレンフィルム
を積層し、その上層に、黒色ポリエチレンフィルムを隠
蔽する着色フィルムをラミネートする工事用養生布粘着
テープを提案している。2. Description of the Related Art Conventionally, cloth adhesive tapes used for curing, packaging, etc., are generally made of one layer or two layers on a cloth or cotton cloth.
It is made by applying a natural rubber-based adhesive to a work cloth in which a layer of polyethylene film is laminated, and has good adaptability of adhesion to rough surfaces and can be easily cut by hand. It is widely used as a feature.
In particular, cloth adhesive tapes for curing are often used outdoors,
Used under severe conditions such as wind and rain, sun rays, and temperature changes. However, the conventional cloth adhesive tape for curing is 1
Despite use for up to two months, there is a problem of deterioration of the pressure-sensitive adhesive due to ultraviolet rays and the like, and a problem of adhesive residue on an adherend due to the deterioration. In order to solve this problem, the present inventors, in the registered utility model publication No. 3005686,
To prevent the adhesive from deteriorating due to ultraviolet rays, a black polyethylene film that blocks the transmission of ultraviolet rays is laminated on the back of the woven fabric, and a colored film that conceals the black polyethylene film is laminated on the upper layer. Suggest a tape.
【0003】[0003]
【発明が解決しょうとする課題】布粘着テープの織布の
背面に、紫外線の透過を遮断する黒色のポリエチレンフ
ィルムを積層することにより、確かに、紫外線による粘
着剤の劣化を防止することができ、また、被着体への糊
残りを大幅に減少させることが可能となった。しかし、
1層目に、黒色のポリエチレンフィルムを積層し、2層
目に、着色ポリエチレンフィルムを積層した場合、布粘
着テープの織布の背面カラーが暗くなり、着色ポリエチ
レンフィルム本来の鮮やかな色彩を発現させることは極
めて困難であった。By laminating a black polyethylene film for blocking the transmission of ultraviolet light on the back of the woven cloth of the cloth adhesive tape, it is possible to surely prevent the adhesive from deteriorating due to ultraviolet light. Also, it has become possible to greatly reduce the adhesive residue on the adherend. But,
When a black polyethylene film is laminated on the first layer and a colored polyethylene film is laminated on the second layer, the back color of the woven fabric of the cloth adhesive tape becomes dark, and the original vivid color of the colored polyethylene film is developed. It was extremely difficult.
【0004】本発明の目的は、上記従来技術の有してい
た課題点を解消し、布粘着テープの織布の背面カラーの
色彩が鮮やかで、かつ、耐候性に優れた布粘着テープを
提供することにある。SUMMARY OF THE INVENTION An object of the present invention is to solve the above-mentioned problems of the prior art, and to provide a cloth adhesive tape which has a vivid back color of the woven fabric of the cloth adhesive tape and is excellent in weather resistance. Is to do.
【0005】[0005]
【課題を解決するための手段】上記本発明の目的を達成
するために、本発明は特許請求の範囲に記載のような構
成とするものである。すなわち、本発明は請求項1に記
載のように、織布を基材とする粘着テープにおいて、該
基材の粘着剤塗工面とは反対側の基材面側から、順次、
それぞれ所定の色に着色したポリオレフィンフィルム層
を少なくとも三層積層し、色彩が鮮明で耐候性に優れた
積層構造のフィルム層を設けた布粘着テープとするもの
である。また、本発明は請求項2に記載のように、請求
項1において、三層構造の着色したポリオレフィンフィ
ルム層のうち、基材に隣接した第1の着色ポリオレフィ
ンフィルム層を、厚さが10〜20μmの白色もしくは
黒色のポリエチレンフィルム層にした布粘着テープとす
るものである。また、本発明は請求項3に記載のよう
に、請求項1において、三層構造の着色したポリオレフ
ィンフィルム層のうち、最上層である第3の着色ポリオ
レフィンフィルム層を、厚さが15〜40μmの所定の
色に着色したポリエチレンフィルム層にした布粘着テー
プとするものである。また、本発明は請求項4に記載の
ように、請求項1において、基材に隣接した第1の着色
したポリオレフィンフィルム層が黒色のポリエチレンフ
ィルム層である場合、中間層にあたる第2の着色ポリオ
レフィンフィルム層を、厚さが20〜40μmの白色の
ポリエチレンフィルム層にした布粘着テープとするもの
である。また、本発明は請求項5に記載のように、請求
項1において、基材に隣接した第1の着色したポリオレ
フィンフィルム層が白色のポリエチレンフィルム層であ
る場合、中間層にあたる第2の着色ポリオレフィンフィ
ルム層を、厚さが20〜40μmの白色のポリエチレン
フィルム層とするか、もしくは最上層である第3の着色
ポリオレフィンフィルム層と同色の厚さが20〜40μ
mのポリエチレンフィルム層にした布粘着テープとする
ものである。本発明の織布を基材とする布粘着テープ
は、粘着剤塗工面とは反対側の基材面に、少なくとも三
層の着色したポリオレフィンフィルムを積層した構造と
するものである。すなわち、基材に隣接した第1のポリ
オレフィンフィルム層には、紫外線の透過を遮断する、
例えば、黒色のポリオレフィンフィルム、または紫外線
を散乱する、例えば、白色のポリオレフィンフィルムを
積層し、上記第1のフィルム層が黒色のポリオレフィン
フィルム層である場合には、中間層にあたる第2のフィ
ルム層に白色のポリオレフィンフィルム層を積層し、第
1のフィルム層が、白色のポリオレフィンフィルム層で
ある場合には、中間層にあたる第2のフィルム層に白色
のポリオレフィンフィルム、もしくは最上層である第3
のフィルム層と同色のポリオレフィンフィルム層を積層
し、さらに、第3のフィルム層として、所定の色に着色
したポリオレフィンフィルム層を積層した構造とするも
のである。 また、本発明の布粘着テープに用いられる
ポリオレフィンフィルム層としては、ポリエチレンフィ
ルム層が最も好ましく使用される。また、着色したポリ
オレフィンフィルムの各層の厚さは、基材に隣接した第
1のポリオレフィンフィルム層が10〜20μm、中間
層にあたる第2のポリオレフィンフィルム層が20〜4
0μm、最上層である第3のポリオレフィンフィルム層
が15〜40μmの範囲にあることが望ましい。また、
粘着剤としては、一般に天然ゴム系粘着剤が用いられ
る。本発明の布粘着テープは、請求項1ないし請求項5
に記載のような構成とすることにより、布粘着テープの
織布の背面カラーの色彩が鮮やかで、かつ、耐候性に優
れ、その結果として、屋外での長期間使用後も被着体へ
の糊残りなどが生じることのない布粘着テープを実現で
きる効果がある。Means for Solving the Problems In order to achieve the object of the present invention, the present invention is configured as described in the claims. That is, the present invention, as described in claim 1, in a pressure-sensitive adhesive tape based on a woven fabric, from the substrate surface side opposite to the pressure-sensitive adhesive-coated surface of the substrate, sequentially,
At least three layers of polyolefin film layers each colored in a predetermined color are laminated to form a cloth adhesive tape provided with a film layer having a laminated structure with clear colors and excellent weather resistance. In addition, as described in claim 2, in the present invention, among the three-layered colored polyolefin film layers, the first colored polyolefin film layer adjacent to the base material has a thickness of 10 to 10 in claim 1. The cloth adhesive tape is a 20 μm white or black polyethylene film layer. According to the present invention, the third colored polyolefin film layer, which is the uppermost layer, of the three-layered colored polyolefin film layer according to the first aspect, has a thickness of 15 to 40 μm. Of a cloth adhesive tape formed into a polyethylene film layer colored in a predetermined color. Further, according to the present invention, when the first colored polyolefin film layer adjacent to the base material is a black polyethylene film layer, the second colored polyolefin corresponding to the intermediate layer according to the first aspect of the present invention. A cloth adhesive tape in which the film layer is a white polyethylene film layer having a thickness of 20 to 40 μm. Further, according to the present invention, in the case where the first colored polyolefin film layer adjacent to the substrate is a white polyethylene film layer, the second colored polyolefin corresponding to the intermediate layer according to the first aspect of the present invention. The film layer is a white polyethylene film layer having a thickness of 20 to 40 μm, or the same color as the third colored polyolefin film layer as the uppermost layer has a thickness of 20 to 40 μm.
m, which is a cloth adhesive tape having a polyethylene film layer. The cloth adhesive tape using a woven fabric as a base material of the present invention has a structure in which at least three colored polyolefin films are laminated on a base material surface opposite to a surface coated with an adhesive. That is, the first polyolefin film layer adjacent to the base material blocks transmission of ultraviolet light,
For example, a black polyolefin film, or a layer that scatters ultraviolet light, for example, a white polyolefin film is laminated, and when the first film layer is a black polyolefin film layer, a second film layer corresponding to an intermediate layer is formed. When a white polyolefin film layer is laminated and the first film layer is a white polyolefin film layer, the second film layer corresponding to the intermediate layer is a white polyolefin film or the third layer which is the uppermost layer.
And a polyolefin film layer of the same color as the film layer of the above is laminated, and a polyolefin film layer colored in a predetermined color is laminated as a third film layer. As the polyolefin film layer used for the cloth adhesive tape of the present invention, a polyethylene film layer is most preferably used. The thickness of each layer of the colored polyolefin film is 10 to 20 μm for the first polyolefin film layer adjacent to the base material, and 20 to 4 μm for the second polyolefin film layer corresponding to the intermediate layer.
It is preferable that the thickness of the third polyolefin film layer, which is the uppermost layer, is in the range of 15 to 40 μm. Also,
As the adhesive, a natural rubber-based adhesive is generally used. The cloth adhesive tape of the present invention is characterized in that:
By the configuration as described in the above, the color of the back color of the woven fabric of the cloth adhesive tape is vivid, and excellent in weather resistance, as a result, even after long-term outdoor use, This has the effect of realizing a cloth adhesive tape free of adhesive residue and the like.
【0006】[0006]
【発明の実施の形態】以下に本発明の実施の形態の一例
を挙げ、本発明の布粘着テープについて、さらに具体的
に説明する。図1に示すように、スフ布よりなる基材5
の片面に、1層目として、厚さが約10μmとなるよう
に黒色のポリエチレンフイルム層1を設け、2層目とし
て、厚さが約20μmとなるように白色のポリエチレン
フイルム層2を設けた。さらに、3層目として、厚さが
約20μmの青色のポリエチレンフイルム層3を設け
た。次に、スフ布よりなる基材5の他面に、天然ゴム系
の粘着剤を約75μm塗工し粘着剤層4を形成した布粘
着テープを作製した。これにより、布粘着テープの織布
の背面カラーの色彩が鮮やかで、かつ、耐候性に優れ、
その結果として、屋外での長期間使用後も被着体への糊
残りなどが生じない良好な布粘着テープを得ることがで
きた。BEST MODE FOR CARRYING OUT THE INVENTION The cloth adhesive tape of the present invention will be described more specifically with reference to an example of an embodiment of the present invention. As shown in FIG. 1, a base material 5 made of soft cloth
On one side, a black polyethylene film layer 1 having a thickness of about 10 μm was provided as a first layer, and a white polyethylene film layer 2 was provided as a second layer having a thickness of about 20 μm. . Further, as a third layer, a blue polyethylene film layer 3 having a thickness of about 20 μm was provided. Next, a cloth adhesive tape in which a natural rubber-based adhesive was applied to about 75 μm on the other surface of the base material 5 made of soft cloth to form an adhesive layer 4 was produced. As a result, the color of the back color of the woven cloth of the cloth adhesive tape is vivid and has excellent weather resistance,
As a result, it was possible to obtain a good cloth adhesive tape free of adhesive residue and the like even after long-term outdoor use.
【図1】本発明の実施の形態で例示した布粘着テープの
断面構造を示す模式図。FIG. 1 is a schematic diagram showing a cross-sectional structure of a cloth adhesive tape exemplified in an embodiment of the present invention.
1…黒色のポリエチレンフィルム層(1層目) 2…白色のポリエチレンフィルム層(2層目) 3…青色のポリエチレンフィルム層(3層目) 4…粘着剤層 5…基材 1: black polyethylene film layer (first layer) 2: white polyethylene film layer (second layer) 3: blue polyethylene film layer (third layer) 4: adhesive layer 5: base material
フロントページの続き (72)発明者 柳川 史郎 神奈川県川崎市多摩区登戸3819番地 株式 会社スリオンテック内Continued on the front page (72) Inventor Shiro Yanagawa 3819 Notobe, Tama-ku, Kawasaki City, Kanagawa Prefecture Inside Sliontec Co., Ltd.
Claims (5)
基材の粘着剤塗工面とは反対側の基材面側から、順次、
それぞれ所定の色に着色したポリオレフィンフィルム層
を少なくとも三層積層し、色彩が鮮明で耐候性に優れた
積層構造のフィルム層を設けてなることを特徴とする布
粘着テープ。1. A pressure-sensitive adhesive tape comprising a woven fabric as a base material, in order from the base material surface side opposite to the pressure-sensitive adhesive-coated surface of the base material,
A cloth pressure-sensitive adhesive tape comprising a laminate of at least three polyolefin film layers each colored in a predetermined color and provided with a laminated layer having a clear color and excellent weather resistance.
リオレフィンフィルム層のうち、基材に隣接した第1の
着色ポリオレフィンフィルム層は、厚さが10〜20μ
mの白色もしくは黒色のポリエチレンフィルム層である
ことを特徴とする布粘着テープ。2. A three-layered colored polyolefin film layer according to claim 1, wherein the first colored polyolefin film layer adjacent to the substrate has a thickness of 10 to 20 μm.
(c) a white or black polyethylene film layer.
リオレフィンフィルム層のうち、最上層である第3の着
色ポリオレフィンフィルム層は、厚さが15〜40μm
の所定の色に着色したポリエチレンフィルム層であるこ
とを特徴とする布粘着テープ。3. A three-layered colored polyolefin film layer according to claim 1, wherein the third colored polyolefin film layer, which is the uppermost layer, has a thickness of 15 to 40 μm.
A cloth film adhesive tape characterized by being a polyethylene film layer colored in a predetermined color.
着色したポリオレフィンフィルム層が黒色のポリエチレ
ンフィルム層である場合、中間層にあたる第2の着色ポ
リオレフィンフィルム層は、厚さが20〜40μmの白
色のポリエチレンフィルム層であることを特徴とする布
粘着テープ。4. The method according to claim 1, wherein when the first colored polyolefin film layer adjacent to the substrate is a black polyethylene film layer, the second colored polyolefin film layer serving as an intermediate layer has a thickness of 20 to 40%. A cloth adhesive tape, which is a 40 μm white polyethylene film layer.
着色したポリオレフィンフィルム層が白色のポリエチレ
ンフィルム層である場合、中間層にあたる第2の着色ポ
リオレフィンフィルム層を、厚さが20〜40μmの白
色のポリエチレンフィルム層とするか、もしくは最上層
である第3の着色ポリオレフィンフィルム層と同色の厚
さが20〜40μmのポリエチレンフィルム層としてな
ることを特徴とする布粘着テープ。5. The method according to claim 1, wherein when the first colored polyolefin film layer adjacent to the substrate is a white polyethylene film layer, the second colored polyolefin film layer serving as an intermediate layer has a thickness of 20 to 50%. A cloth pressure-sensitive adhesive tape comprising a 40 μm white polyethylene film layer or a polyethylene film layer having the same color as the third colored polyolefin film layer as the uppermost layer and having a thickness of 20 to 40 μm.