JPH10175802A - Wax for insect pest repellence and its production - Google Patents
Wax for insect pest repellence and its productionInfo
- Publication number
- JPH10175802A JPH10175802A JP8339183A JP33918396A JPH10175802A JP H10175802 A JPH10175802 A JP H10175802A JP 8339183 A JP8339183 A JP 8339183A JP 33918396 A JP33918396 A JP 33918396A JP H10175802 A JPH10175802 A JP H10175802A
- Authority
- JP
- Japan
- Prior art keywords
- wax
- repellent
- pest repellent
- insect pest
- pest
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、害虫忌避用ワック
スとその製造法に関する。The present invention relates to a pest repellent wax and a method for producing the same.
【０００２】[0002]
【従来の技術】家庭内特に台所で使用する機器はゴキブ
リを始めとする不快害虫あるいは衛生害虫により大きな
被害を被る場合があった。これらゴキブリは、餌により
誘引され、一般雑貨上あるいは機器内に侵入するため、
機器内を清潔にし、残菜を残さない等の工夫がなされて
きた。またそれを逆に利用したゴキブリ誘引捕獲器も市
販されている。2. Description of the Related Art Appliances used at home, particularly in kitchens, are often severely damaged by cockroaches and other unpleasant pests or sanitary pests. These cockroaches are attracted by bait and invade on general goods or equipment,
Various devices have been devised such as keeping the inside of the equipment clean and leaving no residual vegetables. A cockroach attracting and catching device that uses the reverse is also commercially available.
【０００３】また、ゴキブリの侵入を防止するため、例
えば防水構造の機器などが開発されているが、一般的で
なく、家庭で使用されるものは未だ紹介されていない。Further, in order to prevent cockroaches from invading, for example, devices having a waterproof structure have been developed. However, devices which are not common and are used at home have not been introduced yet.
【０００４】[0004]
【発明が解決しようとする課題】ゴキブリは、物の陰に
隠れようという性質から、機器の陰に潜む。一方、一般
家庭やビルの部屋では、深夜、人のいない時などでは、
ゴキブリが部屋中の誘引される場所に床面あるいは床か
ら10cm程度の壁面を使って移動している。その結果ゴキ
ブリに最適の温度環境を提供する熱を発する機器、食品
などを保存する場所に、ゴキブリが集まり不衛生な環境
を作っている。とりわけ、ゴキブリの至適環境を有する
機器ではそれら害虫に至適環境を与えていることにもな
る。Cockroaches hide behind equipment because of their nature of hiding behind objects. On the other hand, in ordinary homes and building rooms, at night, when there are no people,
A cockroach is moving to a place in the room where it is to be attracted, using the floor or a wall about 10 cm from the floor. As a result, cockroaches gather and create an unsanitary environment in places that store food-producing equipment and food that provide an optimal temperature environment for cockroaches. In particular, a device having an optimal environment for cockroaches provides the pest with an optimal environment.
【０００５】また、幼齢期のゴキブリは、小さな間隙か
らでも侵入する。侵入したゴキブリは内部で成長し、様
々な被害を発生させる。卵を持ったゴキブリが侵入した
場合は内部で増殖もする。さらにこれら害虫あるいはそ
の死骸が、電気機器においては充電部とりわけ高電圧部
に接触した場合誤動作の危険がある。[0005] In addition, cockroaches in childhood invade even from small gaps. Invading cockroaches grow inside and cause various damages. When cockroaches with eggs invade, they also grow inside. Furthermore, when these pests or their dead bodies come into contact with a charged part, particularly a high voltage part, in electric equipment, there is a risk of malfunction.
【０００６】さらに忌避剤単独で床面などに塗工処理し
た場合、その上を人間などが歩行したりすれば、忌避剤
は床に接触した靴などに添着し、床面から持ち去られ持
続性が期待できない。さらに金属表面の害虫忌避処理に
ついては金属表面に塗装する方法もあるが、塗膜の耐久
性にもよるが長期使用中に劣化剥離する場合もある。そ
こで、随時、補給追加のできる害虫忌避用ワックスの形
態が要望されていた。Further, when a repellent is applied alone to a floor or the like, if a person walks on the repellent, the repellent adheres to shoes or the like in contact with the floor, and is removed from the floor to maintain durability. Can not expect. In addition, there is a method of coating the metal surface with the insect repellent treatment on the metal surface, but depending on the durability of the coating film, it may be degraded and peeled off during long-term use. Therefore, a form of a pest repellent wax that can be replenished at any time has been demanded.
【０００７】そこで、害虫の生息雰囲気の温度に対する
誘引に忌避効果があり、かつ薬剤に短時間触れても忌避
作用の大きい害虫忌避用ワックスが嘱望されていた。Therefore, there has been a demand for a pest repellent wax which has a repellent effect in inducing the temperature of the atmosphere in which the pests inhabit and which has a large repellent action even when touched with a drug for a short time.
【０００８】本発明は、前記従来の害虫忌避用ワックス
の問題点に鑑み、樹脂・金属表面上で安定した害虫忌避
効果を示す害虫忌避用ワックスを提供すること、また害
虫忌避剤がワックスから溶出しても環境汚染の原因とな
りにくい害虫忌避用ワックスを提供すること、さらに前
記優れた性質を有する害虫忌避用ワックスを製造する方
法を提供することを目的とする。The present invention has been made in view of the above-mentioned problems of the conventional pest repellent wax, and provides a pest repellent wax exhibiting a stable pest repellent effect on a resin or metal surface, and the pest repellent is eluted from the wax. It is an object of the present invention to provide a pest repellent wax which does not easily cause environmental pollution and to provide a method for producing a pest repellent wax having the above excellent properties.
【０００９】[0009]
【課題を解決するための手段】本発明は、ろう中に害虫
忌避剤を分散してなる害虫忌避用ワックスあるいは、液
体ポリッシュ中に害虫忌避剤を分散してなる害虫忌避用
ワックスを提供するものである。前記液体ポリッシュ
は、ワックス成分、乳化剤、シリコン樹脂、溶剤などを
混合分散してなり、その害虫忌避剤はピレスロイド系害
虫忌避剤であることを特徴とする。さらに具体的には、
α-シアノ-3-フェノキシヘ゛ンシ゛ル クリサンテマート、1-エチニル-2-メチル-2-ヘ゜ンテ
ニル クリサンテマート、O-フェニルフェノールと、p-t-オクチルフェノールを混合し
た薬剤であることを特徴とする。The present invention provides a pest repellent wax in which a pest repellent is dispersed in wax or a pest repellent wax in which a pest repellent is dispersed in liquid polish. It is. The liquid polish is obtained by mixing and dispersing a wax component, an emulsifier, a silicone resin, a solvent and the like, and the insect repellent is a pyrethroid-based insect repellent. More specifically,
α-cyano-3-phenoxypentyl chrysanthemate, 1-ethynyl-2-methyl-2-pentenyl chrysanthemate, a drug obtained by mixing O-phenylphenol and pt-octylphenol.
【００１０】あるいは、害虫忌避剤は、少なくともエム
ペントリン、エトフェンプロックスを混合した薬剤であ
ることを特徴とする。[0010] Alternatively, the insect repellent is characterized in that it is a drug obtained by mixing at least empentrin and etofenprox.
【００１１】害虫忌避剤は、担体に担持させた後分散さ
せることをを特徴とし、担体が微粉末シリカゲルあるい
は気相法合成シリカ、アルミナであることを特徴とす
る。The pest repellent is characterized in that it is carried on a carrier and then dispersed, and the carrier is finely divided silica gel, silica synthesized by a gas phase method, or alumina.
【００１２】具体的な製法は、忌避剤を有機溶剤に溶解
し、この溶液に乳化剤、ワックス成分、シリコン樹脂、
溶剤、水を加えてなるか、あるいは忌避剤を有機溶剤に
溶解し、この溶液に微粉末シリカゲルあるいは気相法合
成シリカおよびアルミナの少なくとも一方からなる担
体、乳化剤、ワックス成分、シリコン樹脂、溶剤、水を
加えてなることを特徴とする。A specific production method is to dissolve a repellent in an organic solvent and add an emulsifier, a wax component, a silicone resin,
Solvent, water is added, or the repellent is dissolved in an organic solvent, and a carrier comprising at least one of fine powder silica gel or vapor-phase synthetic silica and alumina, an emulsifier, a wax component, a silicone resin, a solvent, It is characterized by adding water.
【００１３】[0013]
【発明の実施の形態】以下、本発明の実施の形態につい
て図面を参照して説明する。害虫忌避用ワックスに用い
る忌避剤は、安全性の高い薬剤であればどのような薬剤
でもいいが、嗅覚刺激忌避だけでなく少なくとも接触刺
激忌避効果を有する薬剤を含まなければならない。Embodiments of the present invention will be described below with reference to the drawings. The repellent used for the pest repellent wax may be any drug as long as it is a highly safe drug, but it must contain not only an olfactory stimulus repellent but also a drug having at least a contact stimulus repellent effect.
【００１４】害虫忌避用ワックスに混合する害虫忌避剤
は、接触忌避効果を有するα-シアノ-3-フェノキシヘ゛ンシ゛ル クリサンテ
マート、1-エチニル-2-メチル-2-ヘ゜ンテニル クリサンテマート、嗅覚刺激忌避
効果を有するO-フェニルフェノールと、p-t-オクチルフェノールで、それら
を混合し、害虫忌避剤を調製した。The pest repellent to be mixed with the pest repellent wax is α-cyano-3-phenoxypentyl chrysanthemate, 1-ethynyl-2-methyl-2-pentenyl chrysanthemate, which has a contact repellent effect; They were mixed with O-phenylphenol and pt-octylphenol, which have an effect, to prepare a pest repellent.
【００１５】具体的には、ワックス塗装表面１００ｃｍ
2当り、α-シアノ-3-フェノキシヘ゛ンシ゛ル クリサンテマートを０．５〜１５
ｍｇ、1-エチニル-2-メチル-2-ヘ゜ンテニル クリサンテマートを２〜３０ｍ
ｇ、O-フェニルフェノールを１〜１０ｍｇ、p-t-オクチルフェノールを２〜
２０ｍｇが、実質上ワックス表面に存在する構成となる
ように混合したもので、良好な忌避性能が得られた。中
でも最も優れた忌避性能がえられるように、α-シアノ-3-フ
ェノキシヘ゛ンシ゛ル クリサンテマートを０．４２５ｍｇ、1-エチニル-2-メチル-
2-ヘ゜ンテニル クリサンテマートを１２．７５ｍｇ、O-フェニルフェノールを
３．４ｍｇ、p-t-オクチルフェノールを８．１６ｍｇとなるよう
に混合したものを調製した。Specifically, a wax-coated surface of 100 cm
Per 2, the α- cyano-3-Fenokishihe Bu Njiru chestnut Sante Mart 0.5-15
mg, 1-ethynyl-2-methyl-2-pentenyl chrysanthemate 2-30 m
g, 1 to 10 mg of O-phenylphenol, 2 to pt-octylphenol
20 mg was mixed so that the composition substantially existed on the wax surface, and good repelling performance was obtained. Among them, 0.425 mg of α-cyano-3-phenoxyphensidyl chrysanthemate and 1-ethynyl-2-methyl-
A mixture was prepared by mixing 12.75 mg of 2-pentenyl chrysanthemate, 3.4 mg of O-phenylphenol, and 8.16 mg of pt-octylphenol.
【００１６】持続性について、薬剤の蒸気圧がそれぞれ
異なるため、薬効の持続性に一番大きな影響の与える配
合量の最低値を維持できる期間の長い組合せが要求され
る。As for the sustainability, since the vapor pressures of the drugs are different from each other, a combination having a long period capable of maintaining the minimum value of the compounding amount which has the greatest effect on the sustainability of the medicinal effect is required.
【００１７】忌避性能については、嗅覚刺激による忌避
と神経伝達系による触角などの接触忌避があり、害虫忌
避剤を配置した面の上にポリエステル製メッシュを積層
しその上での効果を観察した。積層した場合効果が表れ
なくなる場合を接触忌避とした。Regarding the repelling performance, there are repelling by olfactory stimulation and contact repelling such as an antenna by a nerve transmission system, and a polyester mesh is laminated on the surface on which the pest repellent is arranged, and the effect on the mesh is observed. The case where the effect was not exhibited when the layers were laminated was regarded as contact repellent.
【００１８】本発明忌避剤は、嗅覚刺激忌避と接触忌避
を併用することで、忌避処理を施した表面が汚れあるい
は埃で覆われた場合も嗅覚忌避が発揮されるように、し
かも比較的長期にわたり忌避効果が発揮される薬剤の組
み合わせ条件を見いだした。The repellent of the present invention is used in combination with olfactory irritation repellent and contact repellent so that the olfactory repellent is exerted even when the repellent-treated surface is covered with dirt or dust and has a relatively long term. For a long time, we have found a combination condition of drugs that exerts a repellent effect.
【００１９】嗅覚刺激忌避効果を有する忌避剤として、
エムペントリンあるいは、エトフェンプロックスを混合
して用いても同様の効果が期待できる。As a repellent having an olfactory stimulation repellent effect,
Similar effects can be expected even when empentrin or etofenprox is used in combination.
【００２０】[0020]
（実施の形態１）図１の製法で調製された害虫忌避剤を
用い、必要により抗カビ剤としてＴＢＺを加え、さらに
必要により抗菌剤として銀錯体系抗菌材を加え、（表
１）成分表の割合で調製した害虫忌避用ワックスを準備
した。(Embodiment 1) The pest repellent prepared by the production method of FIG. 1 was used, TBZ was added as an antifungal agent if necessary, and a silver complex antibacterial material was further added as an antibacterial agent, if necessary. The pest repellent wax prepared at the ratio of 1 was prepared.
【００２１】[0021]
【表１】 なお、この害虫ワックスの製法は、図１に示すように、
まず、忌避剤成分を、温度が６０℃未満、室温（ＲＴ）
より大きい条件で、溶解する（溶解工程）。次に、担体
とその溶解した忌避剤成分を室温下で混ぜて担持させる
（担持工程）。次に、ワックスと溶媒とを混ぜたワック
スエマルジョンを、その担持された材料と室温下で混ぜ
る（混合工程）。最後に、その混合した材料を、室温下
で、シリコンオイルと水と混ぜる（調整工程）。このよ
うにして害虫ワックスが出来上がる。[Table 1] In addition, the manufacturing method of this pest wax is as shown in FIG.
First, a repellent component is prepared by adding a component having a temperature of less than 60 ° C.
Dissolve under larger conditions (dissolution step). Next, the carrier and the dissolved repellent component are mixed and supported at room temperature (supporting step). Next, the wax emulsion obtained by mixing the wax and the solvent is mixed with the carried material at room temperature (mixing step). Finally, the mixed material is mixed with silicon oil and water at room temperature (adjustment step). In this way, the pest wax is completed.
【００２２】（表１）に示す配合物を各々加熱撹拌した
後、ホモジナイザーを用いて充分乳化した乳液を実験に
供した。After each of the formulations shown in Table 1 was heated and stirred, a fully emulsified emulsion using a homogenizer was used for the experiment.
【００２３】このワックスを塩ビ床材に塗布し、約１時
間自然乾燥させ、約１００μｍの厚みのワックス被膜を
得た。This wax was applied to a PVC flooring material and air-dried for about 1 hour to obtain a wax coating having a thickness of about 100 μm.
【００２４】この被膜は、通常の使用条件下で物理的に
約１ヶ月の耐久性があった。１ヶ月後被膜を温水の中に
浸漬し、被膜を塩ビ床材より剥離させた。The coating was physically durable for about one month under normal use conditions. One month later, the coating was immersed in warm water, and the coating was peeled off from the PVC flooring.
【００２５】その後、再び前記と同様害虫忌避用ワック
スを塗布し、実用に供した。After that, a pest repellent wax was applied again in the same manner as described above and put to practical use.
【００２６】本発明害虫忌避用ワックスの害虫忌避効果
を（表２）に、抗黴効果、抗ＭＲＳＡ効果、抗ウイルス
効果を確認する実験の結果を（表３）に示す。The pest repellent effect of the pest repellent wax of the present invention is shown in (Table 2), and the results of experiments for confirming the antifungal, anti-MRSA and antiviral effects are shown in (Table 3).
【００２７】また、害虫忌避剤に影響を及ぼさない限り
で、ワックスの種類、溶媒、乳化剤を変更・選択するこ
とも可能である。It is also possible to change and select the type of wax, the solvent and the emulsifier as long as they do not affect the insect repellent.
【００２８】さらにワックスの耐久性を向上させるため
に、ウレタンなどの樹脂成分を混合させることも可能で
ある。In order to further improve the durability of the wax, a resin component such as urethane can be mixed.
【００２９】[0029]
【表２】 [Table 2]
【００３０】[0030]
【表３】 カビ抵抗性試験（４種黴混合 Aspergillus niger,Peni
cillium citrinum,Cladosporium cladosporioides,Fusa
rium proliferatum） ＋ ：抗黴性なし ± ：若干の抗黴性あり − ：抗黴性あり 抗菌試験（E.coli、S.aureus、B.subtills、MRSA） ＋ ：菌数が増殖（抗菌性なし） ± ：菌数の減少が１０2以下 − ：菌数の減少が１０2以上 抗かび試験：日本工業規格のカビ抵抗性試験（ＪＩＳ
Ｚ ２９１１）の繊維製品用防黴試験によるハローテス
ト法に準じた。用いたかびは、Cladosporium cladospor
oides, Chaetomium globosum, Penicillium citrinumお
よびAsperigillus nigerであった。評価は１４日後に行
った。[Table 3] Mold resistance test (four kinds of molds mixed Aspergillus niger, Peni
cillium citrinum, Cladosporium cladosporioides, Fusa
rium proliferatum) +: No antifungal property ±: Some antifungal property-: Antifungal property Antibacterial test (E.coli, S.aureus, B.subtills, MRSA) +: Proliferation (no antibacterial property) ) ±: Decrease in bacterial count of 10 2 or less −: Decrease in bacterial count of 10 2 or more Antifungal test: Mold resistance test according to Japanese Industrial Standards (JIS)
Z 2911) according to the halo test method based on an antifungal test for textile products. The mold used was Cladosporium cladospor
oides, Chaetomium globosum, Penicillium citrinum and Asperigillus niger. Evaluation was performed 14 days later.
【００３１】抗菌試験：Escherichia coli, Staphyloco
ccus aureus, Bacillus subtillisを用い、滴下試験法
に準じた。評価は７日後に行った。滴下試験は、前培養
を行い、対数増殖期にある細菌の約１０5ＣＦＵ／ｍｌ
液を試験片上に滴下し、１８時間３５℃雰囲気中で培養
する。この培養液を採取しそこに生存する菌数を計測す
るものである。Antibacterial test: Escherichia coli, Staphyloco
Using ccus aureus and Bacillus subtillis, the drop test method was followed. The evaluation was performed after 7 days. In the drop test, preculture was performed, and about 10 5 CFU / ml of the bacteria in the logarithmic growth phase was used.
The solution is dropped on the test piece and cultured in an atmosphere at 35 ° C. for 18 hours. This culture solution is collected and the number of bacteria surviving there is measured.
【００３２】（表２）より、本実施例の害虫忌避用ワッ
クスは実用的な害虫忌避性能を有することがわかる。Table 2 shows that the pest repellent wax of this example has practical pest repellency.
【００３３】餌に誘引されるゴキブリを忌避する場合
と、生活環境のゴキブリ至適温度に誘引されるゴキブリ
を忌避する場合があり、前者を餌誘引忌避、後者を熱誘
引忌避と呼ばれ、ゴキブリの場合、餌誘引より熱誘引の
方が高い誘引性を示す。そこで熱誘引性について評価し
た。チャバネゴキブリ雌雄各１００匹ずつを１００００
ｃｍ2の箱の中に放し、中央にゴキブリ至適温度である
２７±５℃に制御されたヒーターを有し害虫忌避用ワッ
クスを所定量その表面に塗工した１００ｃｍ2の塩ビ床
材をその箱の右半分中央に設置する。左半分中央には、
中央に２７±５℃に制御されたヒーターを有し害虫忌避
用ワックスを処理しない１００ｃｍ2の塩ビ床材（対照
品）を設置する。６時間にヒーターを配置した塩ビ床材
上に上る様子をビデオレコーダーに録画し、そのゴキブ
リの数を計数することで忌避性能を評価した。実際に
は、ヒーター周辺に集まり、そのまま集まり続けるた
め、６時間後の生息数を計数した。There are cases where cockroaches repelled by bait are repelled, and cases where cockroaches are repelled to the optimum temperature in the living environment. In the case of, heat attraction shows higher attraction than bait attraction. Therefore, the heat attraction was evaluated. 10,000 cockroaches male and female each 10,000
release in a box of cm 2, the center cockroaches optimum temperature at which 27 ± 5 ° C. predetermined amount of repellent wax having a controlled heater PVC flooring 100 cm 2 was applied to the surface thereof Installed in the center of the right half of the box. In the center of the left half,
A 100 cm 2 PVC flooring (control product) having a heater controlled at 27 ± 5 ° C. in the center and not treating the insect repellent wax is installed. The state of climbing on a PVC flooring material provided with a heater for 6 hours was recorded on a video recorder, and the number of cockroaches was counted to evaluate repellent performance. Actually, the number of inhabitants after 6 hours was counted in order to gather around the heater and keep gathering as it is.
【００３４】（実施の形態２）図１の製法で調製された
害虫忌避材を用い、必要により抗カビ剤としてＴＢＺを
加え、さらに必要により抗菌剤として銀錯体系抗菌材を
加え、それらを、担体に吸着担持させ、忌避薬剤として
製剤した後、（表１）成分表の割合で調製した害虫忌避
用ワックスを準備した。(Embodiment 2) The pest repellent prepared by the production method shown in FIG. 1 is used, TBZ is added as an antifungal agent if necessary, and a silver complex antibacterial material is further added as an antibacterial agent if necessary. After being adsorbed and carried on a carrier and formulated as a repellent drug, (1) a pest repellent wax prepared at the ratio in the component table was prepared.
【００３５】ここで、前記担体として、シリカゲル、気
相法合成シリカあるいはアルミナ微粒子（商品名アエロ
ジル）などを用いることができる。また、包摂化合物を
用いることもできる。本発明では、微粒子シリカゲル粉
末を用いた。Here, as the carrier, silica gel, fumed silica or alumina fine particles (trade name Aerosil) can be used. Also, inclusion compounds can be used. In the present invention, fine silica gel powder was used.
【００３６】忌避性能については、実施の形態１と同様
に試験し、同様の性能を得た。The repelling performance was tested in the same manner as in the first embodiment, and the same performance was obtained.
【００３７】[0037]
【発明の効果】以上のように本発明は、樹脂表面上で安
定した害虫忌避効果を示す害虫忌避剤を用いた害虫忌避
用ワックスを提供できる。As described above, the present invention can provide a pest repellent wax using a pest repellent which exhibits a stable pest repellent effect on a resin surface.
【００３８】また樹脂中より溶出しても環境汚染の原因
となりにくい害虫忌避剤を用いた害虫忌避用ワックスを
提供できる。Further, it is possible to provide a pest repellent wax which uses a pest repellent which is less likely to cause environmental pollution even if it is eluted from the resin.
【００３９】さらに被膜使用後は容易に剥離できる害虫
忌避用ワックスを提供できる。Further, it is possible to provide a pest repellent wax which can be easily peeled off after using the coating.
【図１】本発明の一実施の形態に用いる、害虫忌避用ワ
ックスの基本構造工程図FIG. 1 is a basic structural process diagram of a pest repellent wax used in one embodiment of the present invention.
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.6 識別記号 ＦＩ Ａ０１Ｎ 53/08 Ａ０１Ｎ 53/00 ５０８Ａ ──────────────────────────────────────────────────続 き Continued on the front page (51) Int.Cl. 6 Identification code FI A01N 53/08 A01N 53/00 508A
Claims (11)
虫忌避用ワックス。1. A pest repellent wax in which a pest repellent is dispersed in a wax.
れている害虫忌避用ワックス。2. A pest repellent wax in which a pest repellent is dispersed in a liquid polish.
クス成分、乳化剤、シリコン樹脂、溶剤を混合分散して
製造されたものである請求項２記載の害虫忌避用ワック
ス。3. The pest repellent wax according to claim 2, wherein the liquid polish is produced by mixing and dispersing at least a wax component, an emulsifier, a silicone resin, and a solvent.
である請求項１又は２記載の害虫忌避用ワックス。4. The insect repellent wax according to claim 1, wherein the insect repellent is a pyrethroid-based insect repellent.
リサンテマート、1-エチニル-2-メチル-2-ヘ゜ンテニル クリサンテマート、O-フェニルフェノ
ールと、p-t-オクチルフェノールを混合した薬剤である請求項１又
は２記載の害虫忌避用ワックス。5. The pest repellent is a drug obtained by mixing α-cyano-3-phenoxypentyl chrysanthemate, 1-ethynyl-2-methyl-2-pentenyl chrysanthemate, O-phenylphenol and pt-octylphenol. The pest repellent wax according to claim 1 or 2, wherein
ンを混合した薬剤である請求項１又は２記載の害虫忌避
用ワックス。6. The pest repellent wax according to claim 1, wherein the pest repellent is a drug containing at least empentrin.
ロックスを混合した薬剤である請求項１又は２記載の害
虫忌避用ワックス。7. The pest repellent wax according to claim 1, wherein the pest repellent is a drug mixed with at least etofenprox.
散されて製造された請求項１又は２記載の害虫忌避用ワ
ックス。8. The pest repellent wax according to claim 1, wherein the pest repellent is carried on a carrier and then dispersed.
リカ、又はアルミナであることを特徴とする請求項８記
載の害虫忌避用ワックス。9. The pest repellent wax according to claim 8, wherein the carrier is finely divided silica gel, vapor-phase synthetic silica, or alumina.
に、乳化剤、ワックス成分、シリコン樹脂、溶剤、水を
加える、請求項２記載の害虫忌避用ワックスの製造法。10. The method for producing a pest repellent wax according to claim 2, wherein the repellent is dissolved in an organic solvent, and an emulsifier, a wax component, a silicone resin, a solvent, and water are added to the solution.
に、微粉末シリカゲル、気相法合成シリカ又はアルミナ
からなる担体、乳化剤、ワックス成分、シリコン樹脂、
溶剤、水を加える請求項２記載の害虫忌避用ワックスの
製造法。11. A repellent is dissolved in an organic solvent, and a carrier made of fine powdered silica gel, fumed silica or alumina, an emulsifier, a wax component, a silicone resin,
The method for producing a pest repellent wax according to claim 2, wherein a solvent and water are added.