JP6195523B2 - Actinic ray-sensitive or radiation-sensitive resin composition, resist film, pattern formation method, electronic device manufacturing method using the same, and electronic device - Google Patents

Description

  The present invention relates to an actinic ray-sensitive or radiation-sensitive resin using a developer containing an organic solvent, which is suitably used in an ultramicrolithography process such as the manufacture of VLSI and high-capacity microchips and other photofabrication processes The present invention relates to a composition, a resist film, a pattern formation method, an electronic device manufacturing method using these, and an electronic device. More specifically, the actinic ray-sensitive or radiation-sensitive resin composition using a developer containing an organic solvent, which can be suitably used for fine processing of a semiconductor element using an electron beam or EUV light (wavelength: around 13 nm). The present invention relates to a resist film, a pattern forming method, an electronic device manufacturing method using these, and an electronic device.

  Conventionally, in the manufacturing process of semiconductor devices such as IC and LSI, fine processing by lithography using a photoresist composition has been performed. In recent years, with the high integration of integrated circuits, the formation of ultrafine patterns in the submicron region and the quarter micron region has been required. Along with this, there is a tendency to shorten the exposure wavelength from g-line to i-line, and further to KrF excimer laser light. Furthermore, at present, in addition to excimer laser light, lithography using electron beams, X-rays, or EUV light is being developed.

These electron beams, X-rays, or EUV photolithography are positioned as next-generation or next-generation pattern forming techniques, and resist compositions having high contrast, high sensitivity, and high resolution are desired.
High sensitivity is a very important issue especially for shortening the wafer processing time. However, when trying to achieve high sensitivity, pattern collapse and scum occur, and these resists satisfy these characteristics at the same time. Development of the composition is highly desired.

  As one method for solving these problems, for example, Patent Documents 1 and 2 disclose resist compositions containing a specific resin.

Japanese Patent No. 3223977 JP 2004-45448 A

  However, in the ultrafine region, it is required to satisfy high sensitivity, high resolution, and scum reduction at a higher level simultaneously. The inventions disclosed in Patent Documents 1 and 2 are as described above. There was room for improvement.

  An object of the present invention is to solve the problem of the performance improvement technology in the microfabrication of a semiconductor device using an electron beam or extreme ultraviolet rays (EUV light), and has high sensitivity, high resolution (high resolution, etc.), and Provided are an actinic ray-sensitive or radiation-sensitive resin composition, a resist film, a pattern forming method, an electronic device manufacturing method using the same, and an electronic device that satisfy scum reduction at a high level simultaneously. There is.

That is, the present invention provides the following [1] to [14].
[1] Actinic rays containing a resin (A) having a partial structure in which acetal is decomposed by the action of an acid to generate a phenolic hydroxyl group and a partial structure in which the acetal is decomposed by the action of an acid to generate a carboxylic acid group Or radiation sensitive resin composition.
[2] The actinic ray-sensitive material according to [1], wherein the resin (A) is a resin having a repeating unit represented by the following general formula (3) and a repeating unit represented by the general formula (4). Radiation sensitive resin composition.
[3] The actinic ray-sensitive or radiation-sensitive resin composition according to [2], wherein the resin (A) is a resin further having a repeating unit represented by the following general formula (1).
[4] The actinic ray-sensitive or radiation-sensitive resin composition according to [22] or [3], wherein in the general formula (3), R ₃₄ is a group represented by the general formula (3-1) described later. .
[5] The actinic ray-sensitive or radiation-sensitive property according to any one of [2] to [4], wherein in the general formula (4), R ₄₄ is a group represented by the general formula (4-1) described later. Resin composition.
[6] The actinic ray-sensitive or radiation-sensitive resin composition according to any one of [2] to [5], wherein in general formula (3), L ₃ is a single bond and Ar ₃ is a phenylene group.
[7] The activity according to any one of [2] to [6], wherein in general formula (4), L ₄ is a single bond, a group having an aromatic ring, a group having a norbornyl structure or a group having an adamantyl structure. A light-sensitive or radiation-sensitive resin composition.
[8] The actinic ray-sensitive or radiation-sensitive resin composition according to any one of [1] to [7], further comprising a compound that generates an acid having a volume of 240 ³ or more upon irradiation with actinic rays or radiation.
[9] A resist film comprising the actinic ray-sensitive or radiation-sensitive resin composition according to any one of [1] to [8].
[10] (a) A step of forming the resist film according to [9], (b) a step of exposing the film, and (c) a pattern obtained by developing the exposed film using a developer. The pattern formation method which has the process to form.
[11] The pattern formation according to [10], wherein the step (c) is a step of (e ′) developing the exposed film using a developer containing an organic solvent to form a negative pattern. Method.
[12] The pattern forming method according to [10] or [11], wherein the exposure is performed using an X-ray, an electron beam, or EUV light.
[13] A method for manufacturing an electronic device, comprising the pattern forming method according to any one of [10] to [12].
[14] An electronic device manufactured by the method for manufacturing an electronic device according to [13].

  According to the present invention, an actinic ray-sensitive or radiation-sensitive resin composition, a resist film, a pattern forming method, and a pattern forming method that satisfy high sensitivity, high resolution, and scum reduction at the same time in a very high dimension. A method for manufacturing an electronic device using the device and an electronic device can be provided.

Hereinafter, embodiments of the present invention will be described in detail.
In the description of the group (atomic group) in this specification, the notation which does not describe substitution and non-substitution includes the thing which has a substituent with the thing which does not have a substituent. For example, the “alkyl group” includes not only an alkyl group having no substituent (unsubstituted alkyl group) but also an alkyl group having a substituent (substituted alkyl group).
In this specification, light includes not only extreme ultraviolet rays (EUV light) but also electron beams.
In addition, “exposure” in this specification includes not only exposure by extreme ultraviolet rays (EUV light) but also drawing by electron beams unless otherwise specified.
“Actinic light” or “radiation” in the present specification means, for example, an emission line spectrum of a mercury lamp, far ultraviolet rays represented by an excimer laser, extreme ultraviolet rays (EUV light), X-rays, electron beams and the like. In the present invention, light means actinic rays or radiation. In addition, the term “exposure” in the present specification is not limited to exposure with far ultraviolet rays such as mercury lamps and excimer lasers, X-rays, EUV light, etc., but also particle beams such as electron beams and ion beams, unless otherwise specified. Include drawing in exposure.

The actinic ray-sensitive or radiation-sensitive resin composition of the present invention has a partial structure in which acetal is decomposed by the action of an acid to generate a phenolic hydroxyl group, and a part in which acetal is decomposed by the action of an acid to generate a carboxylic acid group The resin (A) having a structure is contained.
With the actinic ray-sensitive or radiation-sensitive resin composition of the present invention, high sensitivity, high resolution (such as high resolution), and reduction in scum can be satisfied at a high level at the same time. The reason is not clear, but is presumed as follows.
That is, the resin (A) contained in the actinic ray-sensitive or radiation-sensitive resin composition of the present invention is, as described above, “partial structure in which acetal is decomposed by the action of an acid to generate a phenolic hydroxyl group”. “A partial structure in which an acetal is decomposed by the action of an acid to generate a carboxylic acid group”. These specific “partial structures” are considered to be highly sensitive because they are rapidly decomposed by the action of an acid and the polarity changes greatly.
In addition, by combining these specific “partial structures”, it is considered that both a high contact angle and a high dissolution contrast can be achieved, and an improvement in resolution and a reduction in scum can be achieved at a high level by reducing pattern collapse.

First, the actinic ray-sensitive or radiation-sensitive resin composition of the present invention (hereinafter also referred to as “the composition of the present invention”) will be described.
The composition of the present invention is typically a resist composition. The composition of the present invention is typically a chemically amplified resist composition.
The composition of the present invention comprises a resin (A) having a partial structure in which acetal is decomposed by the action of an acid to produce a phenolic hydroxyl group, and a partial structure in which the acetal is decomposed by the action of an acid to produce a carboxylic acid group (hereinafter referred to as “a”). , Also simply referred to as “resin (A)”. Below, this resin (A) is demonstrated first.

[1] Resin (A)
The resin (A) contained in the composition of the present invention has a partial structure in which acetal is decomposed by the action of an acid to generate a phenolic hydroxyl group, and a partial structure in which the acetal is decomposed by the action of an acid to generate a carboxylic acid group. It is resin which has.
That is, the resin (A) is a kind of acid-decomposable repeating unit, a partial structure in which acetal is decomposed by the action of an acid to generate a phenolic hydroxyl group, and an acetal is decomposed by the action of an acid to generate a carboxylic acid group. It has a partial structure.
The acid-decomposable repeating unit is, for example, a group that is decomposed by the action of an acid on the main chain or side chain of the resin, or both the main chain and side chain (hereinafter also referred to as “acid-decomposable group”). It is a repeating unit having

(A) The repeating unit represented by the general formula (3) and the repeating unit represented by the general formula (4) The resin (A) has a partial structure in which acetal is decomposed by the action of an acid to generate a phenolic hydroxyl group. It preferably has a repeating unit represented by the general formula (3).
Moreover, it is preferable that the said resin (A) has a repeating unit represented by General formula (4) which has a partial structure which acetal decomposes | disassembles by the effect | action of an acid and produces a carboxylic acid group.
Furthermore, the resin (A) is more preferably a resin having a repeating unit represented by the general formula (3) and a repeating unit represented by the general formula (4).

In general formula (3),
R ₃₁ , R ₃₂ and R ₃₃ each independently represents a hydrogen atom, an alkyl group, a cycloalkyl group, a halogen atom, a cyano group or an alkoxycarbonyl group. R ₃₂ may be bonded to L ₃ to form a ring, in which case R ₃₂ represents an alkylene group.
L ₃ represents a single bond or a divalent linking group, and in the case of forming a ring with R ₃₂ , represents a trivalent linking group.
Ar ₃ represents an aromatic ring group.
R ₃₄ represents a hydrogen atom, an alkyl group, a cycloalkyl group, an aryl group, an aralkyl group, an alkoxy group, an acyl group, or a heterocyclic group.
R ₃₅ represents a hydrogen atom, an alkyl group, a cycloalkyl group, an aryl group, an aralkyl group, an alkoxy group, an acyl group, or a heterocyclic group.
M ₃ represents a single bond or a divalent linking group.
Q ₃ represents an alkyl group, a cycloalkyl group, an aryl group or a heterocyclic group.
At least two of Q ₃ , M ₃ and R ₃₄ may be bonded to form a ring.

In general formula (4),
R ₄₁ , R ₄₂ and R ₄₃ each independently represents a hydrogen atom, an alkyl group, a cycloalkyl group, a halogen atom, a cyano group or an alkoxycarbonyl group. R ₄₂ may be bonded to L ₄ to form a ring, and R ₄₂ in this case represents an alkylene group.
L ₄ represents a single bond or a divalent linking group, and in the case of forming a ring with R ₄₂ , represents a trivalent linking group.
R ₄₄ represents a hydrogen atom, an alkyl group, a cycloalkyl group, an aryl group, an aralkyl group, an alkoxy group, an acyl group, or a heterocyclic group.
R ₄₅ represents a hydrogen atom, an alkyl group, a cycloalkyl group, an aryl group, an aralkyl group, an alkoxy group, an acyl group, or a heterocyclic group.
M ₄ represents a single bond or a divalent linking group.
Q ₄ represents an alkyl group, a cycloalkyl group, an aryl group, or a heterocyclic group.
At least two of Q ₄ , M ₄ and R ₄₄ may be bonded to form a ring.

Examples of the alkyl group represented by R _{31 to} R ₃₃ in the general formula (3) include an optionally substituted methyl group, ethyl group, propyl group, isopropyl group, n-butyl group, and sec-butyl group. , A tert-butyl group, a hexyl group, a 2-ethylhexyl group, an octyl group, a dodecyl group and the like, and an alkyl group having 20 or less carbon atoms, and an alkyl group having 10 or less carbon atoms are preferable.
The cycloalkyl group represented by R _{31 to} R ₃₃ may be monocyclic or polycyclic. For example, the cycloalkyl group may have 3 to 10 carbon atoms such as a cyclopropyl group, a cyclopentyl group, or a cyclohexyl group, which may have a substituent. Examples of the monocyclic cycloalkyl group.
The halogen atom R ₃₁ to R ₃₃ represents a fluorine atom, a chlorine atom, a bromine atom and an iodine atom, a fluorine atom is preferable.
As the alkyl group contained in the alkoxycarbonyl group R ₃₁ to R ₃₃ represent, the same alkyl groups represented by _R 31 _{to R 33} are preferred.
When R ₃₂ represents an alkylene group, the alkylene group preferably has 1 to 8 carbon atoms such as an optionally substituted methylene group, ethylene group, propylene group, butylene group, hexylene group, octylene group. Can be mentioned.
R _{31 to} R ₃₃ are each independently preferably a hydrogen atom or an alkyl group, and more preferably a hydrogen atom.

Examples of the divalent linking group represented by L ₃ include, for example, an alkylene group, a divalent aromatic ring group (a divalent group having an aromatic ring), -COO-L _1- , -OL- _1- , Examples thereof include a divalent group having a norbornyl structure, a divalent group having an adamantyl structure, -CONH-, and a group formed by combining two or more thereof. Here, L ₁ represents an alkylene group, a cycloalkylene group, a divalent aromatic ring group, or a group in which an alkylene group and a divalent aromatic ring group are combined.
L ₃ is preferably a single bond, a group represented by —COO—L ₁ — or a divalent aromatic ring group. L ₁ is preferably an alkylene group having 1 to 5 carbon atoms, more preferably a methylene group or a propylene group. As the divalent aromatic ring group, a 1,4-phenylene group, a 1,3-phenylene group, a 1,2-phenylene group, and a 1,4-naphthylene group are preferable, and a 1,4-phenylene group is more preferable.
In the case where L ₃ to form a ring with R _32, examples of the trivalent linking group represented by L _3, a specific example described above divalent linking groups represented by L ₃ 1 single Preferable examples include groups formed by removing any hydrogen atom.
L ₃ is preferably a single bond or —COO-L ₁ —, and preferably a single bond.

Ar ₃ represents an aromatic ring group, for example, an arylene group having 6 to 18 carbon atoms such as an optionally substituted phenylene group, tolylene group, naphthylene group, or, for example, thiophene, furan, pyrrole, Preferred examples include divalent aromatic ring groups containing heterocycles such as benzothiophene, benzofuran, benzopyrrole, triazine, imidazole, benzimidazole, triazole, thiadiazole, and thiazole.
Ar ₃ is preferably an arylene group having 6 to 18 carbon atoms such as a phenylene group or a naphthylene group, more preferably a phenylene group or a naphthylene group, and still more preferably a phenylene group.

The alkyl group or cycloalkyl group represented by R ₃₄ and R _{35 has the same} meaning as the alkyl group or cycloalkyl group represented by R _{31 to} R ₃₃ described above. The alkyl group or cycloalkyl group represented by R ₃₄ and R ₃₅ includes a group represented by general formula (3-1) described later.
The aryl group represented by R ₃₄ and R ₃₅ is preferably an aryl group having 6 to 10 carbon atoms, for example, an aryl group such as a phenyl group, a naphthyl group, an anthryl group; thiophene, furan, pyrrole, benzothiophene, benzofuran, benzopyrrole. , Triazine, imidazole, benzimidazole, triazole, thiadiazole, thiazole and other divalent aromatic ring groups containing a heterocyclic ring;
The aralkyl group represented by R ₃₄ and R ₃₅ is preferably an aralkyl group having 7 to 12 carbon atoms, and examples thereof include a benzyl group, a phenethyl group, and a naphthylmethyl group.
Examples of the alkyl group moiety of the alkoxy group represented by R ₃₄ and R ₃₅ include the same groups as the alkyl groups represented by the aforementioned R _{31 to} R ₃₃ .
Examples of the acyl group represented by R ₃₄ and R ₃₅ include aliphatic groups having 1 to 10 carbon atoms such as formyl group, acetyl group, propionyl group, butyryl group, isobutyryl group, valeryl group, pivaloyl group, benzoyl group, and naphthoyl group. An acyl group is mentioned, It is preferable that it is an acetyl group or a benzoyl group.
Examples of the heterocyclic group represented by R ₃₄ and R ₃₅ include thiirane, cyclothiolane, thiophene, furan, pyrrole, benzothiophene, benzofuran, benzopyrrole, triazine, imidazole, benzimidazole, triazole, thiadiazole, thiazole, pyrrolidone and the like. It is done.
The group represented by R ₃₄ is preferably an alkyl group, a cycloalkyl group, an aryl group or an aralkyl group, more preferably an alkyl group or a cycloalkyl group, and still more preferably an alkyl group.
As the group R ₃₅ represents a hydrogen atom, preferably an alkyl group, more preferably a hydrogen atom.

As the group (alkyl group or cycloalkyl group) represented by R ₃₄ , a group represented by General Formula (3-1) is most preferable.

In General Formula (3-1), R _3a , R _3b, and R _3c each independently represent a substituent other than a hydrogen atom, and each may be bonded to form a ring.
R _3a , R _3b and R _3c are preferably alkyl groups.
Specific examples of the group represented by the general formula (3-1) are shown below, but the present invention is not limited thereto.

  Although the specific example of the repeating unit represented by General formula (3) below is shown, this invention is not limited to these.

R ₄₁ , R ₄₂ , R ₄₃ , L ₄ , R ₄₄ , R ₄₅ , M ₄ and Q ₄ in the general formula (4) are respectively R ₃₁ , R ₃₂ , R ₃₃ , L ₃ in the general formula (3). , R ₃₄ , R ₃₅ , M ₃ and Q ₃ .

Regarding R ₄₁ , R ₄₂ , R ₄₃ , R ₄₄ , R ₄₅ , M ₄ and Q ₄ in the general formula (4), preferred ranges are also R ₃₁ , R ₃₂ , R ₃₃ , R ₃₄ , R ₃₅ , M _3. and is the same _{as that} of Q _3.
Therefore, for example, as the group represented by R ₄₄ , like R ₃₄ , an alkyl group, a cycloalkyl group, an aryl group, and an aralkyl group are preferable, an alkyl group and a cycloalkyl group are more preferable, and an alkyl group is still more preferable.
As the group that R ₄₄ represents (alkyl group or a cycloalkyl group), a group represented by the general formula (4-1) are most preferred.
In General Formula (4-1), R _4a , R _4b, and R _4c each independently represent a substituent other than a hydrogen atom, and each may be bonded to form a ring.
R _4a , R _4b and R _4c are preferably alkyl groups.
Specific examples of the group represented by the general formula (4-1) include those exemplified as the specific examples of the group represented by the general formula (3-1).

L ₄ in the general formula (4) is synonymous with L ₃ in the general formula (3) as described above, but is a single bond, a divalent group having an aromatic ring, or a divalent group having a norbornyl structure. Or a divalent group having an adamantyl structure.

  Although the preferable specific example of the partial structure represented by the following general formula (b-0) in General formula (4) is shown below, this invention is not limited to these.

_R 41 in the general formula _{(b-0), R 42} , R 43 and _{L 4,} respectively, the same meanings as _{R 41,} R _{42, R 43} and _{L 4} in the general formula (4). * Represents a bond connected to the carbon atom to which R ₄₄ and R ₄₅ in General Formula (4) are bonded (the same applies to the following specific examples).

  Although the specific example of the repeating unit represented by General formula (4) below is shown, this invention is not limited to these.

  Each of the repeating unit represented by the general formula (3) and the repeating unit represented by the general formula (4) may be one kind or a combination of two or more kinds.

In the resin (A), the total content of the repeating unit represented by the general formula (3) and the repeating unit represented by the general formula (4) is based on all the repeating units in the resin (A). 5 to 95 mol% is preferable, 10 to 80 mol% is more preferable, 20 to 60 mol% is further preferable, and 30 to 50 mol% is most preferable.
Moreover, in the said resin (A), ratio ((3) :( 4)) of the repeating unit represented by General formula (3) and the repeating unit represented by General formula (4) is 5: 95- 95: 5 is preferable, 10:90 to 90:10 is more preferable, and 20:80 to 80:20 is still more preferable.

(B) Repeating Unit Represented by General Formula (1) The resin (A) is preferably a resin having a repeating unit represented by the following general formula (1).

In general formula (1),
R ₁₁ , R ₁₂ and R ₁₃ each independently represents a hydrogen atom, an alkyl group, a cycloalkyl group, a halogen atom, a cyano group or an alkoxycarbonyl group. R ₁₃ may be bonded to Ar ₁ to form a ring, in which case R ₁₃ represents an alkylene group.
X ₁ represents a single bond or a divalent linking group.
Ar ₁ represents an (n + 1) -valent aromatic ring group, and when bonded to R ₁₃ to form a ring, represents an (n + 2) -valent aromatic ring group.
n represents an integer of 1 to 4.

Specific examples of the alkyl group, cycloalkyl group, halogen atom, alkoxycarbonyl group of R ₁₁ , R ₁₂ , and R ₁₃ in formula (1), and the substituents that these groups may have are the above general formula (3) Are the same as the specific examples described for each group represented by R ₃₁ , R ₃₂ and R ₃₃ .

Ar ₁ represents an (n + 1) -valent aromatic ring group. The divalent aromatic ring group in the case where n is 1 may have a substituent, for example, an arylene group having 6 to 18 carbon atoms such as a phenylene group, a tolylene group, a naphthylene group, and an anthracenylene group, or Examples of preferred aromatic ring groups include heterocycles such as thiophene, furan, pyrrole, benzothiophene, benzofuran, benzopyrrole, triazine, imidazole, benzimidazole, triazole, thiadiazole, thiazole.

Specific examples of the (n + 1) -valent aromatic ring group in the case where n is an integer of 2 or more include (n-1) arbitrary hydrogen atoms removed from the above-described specific examples of the divalent aromatic ring group. The group formed can be preferably mentioned.
The (n + 1) -valent aromatic ring group may further have a substituent.

  Examples of the substituent that the above-described alkylene group and (n + 1) -valent aromatic ring group may have include an alkyl group, a methoxy group, an ethoxy group, a hydroxyethoxy group, a propoxy group, a hydroxypropoxy group, a butoxy group and other alkoxy groups, phenyl And aryl groups such as groups.

Examples of the divalent linking group for X ₁ include —COO— and —CONR ₆₄ —.
_-CONR 64 represented by X ₁ - _{(R 64} represents a hydrogen atom, an alkyl group) The alkyl group for _{R 64} in, preferably an optionally substituted methyl group, an ethyl group, a propyl group , An isopropyl group, an n-butyl group, a sec-butyl group, a hexyl group, a 2-ethylhexyl group, an octyl group, a dodecyl group, or the like, and an alkyl group having a carbon number of 8 or less is more preferable. Can be mentioned.
X ₁ is preferably a single bond, —COO—, or —CONH—, and more preferably a single bond or —COO—.

Ar ₁ is more preferably an aromatic ring group having 6 to 18 carbon atoms which may have a substituent, and particularly preferably a benzene ring group, a naphthalene ring group or a biphenylene ring group.
The repeating unit (b) preferably has a hydroxystyrene structure. That is,
Ar ₁ is preferably a benzene ring group.

  n represents an integer of 1 to 4, preferably 1 or 2, and more preferably 1.

  Specific examples of the repeating unit represented by the general formula (1) are shown below, but the present invention is not limited thereto. In the formula, a represents 1 or 2.

  The resin (A) may contain two or more types of repeating units represented by the general formula (1).

  The content of the repeating unit represented by the general formula (1) (the total when containing a plurality of types) is in the range of 3 to 98 mol% with respect to all the repeating units in the resin (A). It is preferably within the range of 10 to 80 mol%, more preferably within the range of 25 to 70 mol%.

(C) Repeating unit having a polar group other than the repeating unit represented by formula (1) The resin (A) preferably contains a repeating unit (c) having a polar group. By including the repeating unit (c), for example, the sensitivity of the composition containing a resin can be improved. The repeating unit (c) is preferably a non-acid-decomposable repeating unit (that is, having no acid-decomposable group).
Examples of the “polar group” that the repeating unit (c) may contain include the following (1) to (4). In the following, “electronegativity” means a value by Pauling.

(1) A functional group including a structure in which an oxygen atom and an atom having an electronegativity difference of 1.1 or more are bonded by a single bond. Examples of such a polar group include a hydroxy group and the like. And a group containing a structure represented by O—H.
(2) Functional group including a structure in which a nitrogen atom and an atom having a difference in electronegativity of the nitrogen atom of 0.6 or more are bonded by a single bond. Examples of such a polar group include an amino group and the like. And a group containing a structure represented by N—H.
(3) Functional group including a structure in which two atoms having electronegativity different by 0.5 or more are bonded by a double bond or a triple bond. Examples of such a polar group include C≡N, C═O, N = And a group containing a structure represented by O, S═O or C═N.
(4) Functional group having an ionic moiety Examples of such a polar group include a group having a moiety represented by N ⁺ or S ⁺ .
Specific examples of the partial structure that can be included in the “polar group” are given below.

  The “polar group” that the repeating unit (c) may contain includes, for example, (I) a hydroxy group, (II) a cyano group, (III) a lactone group or a sultone group (cyclic sulfonate ester), (IV) a carboxylic acid group, or At least selected from the group consisting of a sulfonic acid group, a group corresponding to (V) an amide group, a sulfonamide group or a derivative thereof, (VI) an ammonium group or a sulfonium group, and a group formed by combining two or more thereof. One is preferred.

The polar group is selected from a hydroxyl group, a cyano group, a lactone group, a sultone group, a carboxylic acid group, a sulfonic acid group, an amide group, a sulfonamide group, an ammonium group, a sulfonium group, and a group formed by combining two or more thereof. It is particularly preferably an alcoholic hydroxy group, a cyano group, a lactone group, a sultone group, or a group containing a cyanolactone structure.
When the resin further contains a repeating unit having an alcoholic hydroxy group, the exposure latitude (EL) of the composition containing the resin can be further improved.
When the resin further contains a repeating unit having a cyano group, the sensitivity of the composition containing the resin can be further improved.
If the resin further contains a repeating unit having a lactone group or a sultone group, the dissolution contrast with respect to the developer containing an organic solvent can be further improved. This also makes it possible to further improve the dry etching resistance, coating properties, and adhesion to the substrate of the resin-containing composition.
If the resin further contains a repeating unit having a group containing a lactone structure having a cyano group, the dissolution contrast with respect to the developer containing an organic solvent can be further improved. This also makes it possible to further improve the sensitivity, dry etching resistance, applicability, and adhesion to the substrate of the composition containing the resin. In addition, this makes it possible for a single repeating unit to have a function attributable to each of the cyano group and the lactone group, thereby further increasing the degree of freedom in designing the resin.

  When the polar group of the repeating unit (c) is an alcoholic hydroxy group, it is preferably represented by at least one selected from the group consisting of the following general formulas (I-1H) to (I-10H). In particular, it is more preferably represented by at least one selected from the group consisting of the following general formulas (I-1H) to (I-3H), and may be represented by the following general formula (I-1H). Further preferred.

Where
Each Ra independently represents a hydrogen atom, an alkyl group or a group represented by —CH ₂ —O—Ra ₂ . Here, Ra ₂ represents a hydrogen atom, an alkyl group, or an acyl group.
R ₁ represents an (n + 1) valent organic group.
R ₂ independently represents a single bond or an (n + 1) -valent organic group when m ≧ 2.
W represents a methylene group, an oxygen atom or a sulfur atom.
n and m represent an integer of 1 or more. In the general formula (I-2H), (I-3H) or (I-8H), n is 1 when R ₂ represents a single bond.
l represents an integer of 0 or more.
L ₁ represents a linking group represented by —COO—, —OCO—, —CONH—, —O—, —Ar—, —SO ₃ — or —SO ₂ NH—. Here, Ar represents a divalent aromatic ring group.
Each R independently represents a hydrogen atom or an alkyl group.
R ₀ represents a hydrogen atom or an organic group.
L ₃ represents a (m + 2) -valent linking group.
R ^L each independently represents an (n + 1) -valent linking group when m ≧ 2.
R ^S each independently represents a substituent when p ≧ 2. For p ≧ 2, plural structured R ^S may be bonded to each other to form a ring.
p represents an integer of 0 to 3.

Ra represents a hydrogen atom, an alkyl group, or a group represented by —CH ₂ —O—Ra ₂ . Ra is preferably a hydrogen atom or an alkyl group having 1 to 10 carbon atoms, and more preferably a hydrogen atom or a methyl group.
W represents a methylene group, an oxygen atom or a sulfur atom. W is preferably a methylene group or an oxygen atom.
R ₁ represents an (n + 1) valent organic group. R ₁ is preferably a non-aromatic hydrocarbon group. In this case, R ₁ may be a chain hydrocarbon group or an alicyclic hydrocarbon group. R ₁ is more preferably an alicyclic hydrocarbon group.
R ₂ represents a single bond or an (n + 1) valent organic group. R ₂ is preferably a single bond or a non-aromatic hydrocarbon group. In this case, R ₂ may be a chain hydrocarbon group or an alicyclic hydrocarbon group.
When R ₁ and / or R ₂ is a chain hydrocarbon group, the chain hydrocarbon group may be linear or branched. The chain hydrocarbon group preferably has 1 to 8 carbon atoms. For example, when R ₁ and / or R ₂ is an alkylene group, R ₁ and / or R ₂ are methylene group, ethylene group, n-propylene group, isopropylene group, n-butylene group, isobutylene group or sec- A butylene group is preferred.
When R ₁ and / or R ₂ is an alicyclic hydrocarbon group, the alicyclic hydrocarbon group may be monocyclic or polycyclic. This alicyclic hydrocarbon group has, for example, a monocyclo, bicyclo, tricyclo or tetracyclo structure. The carbon number of this alicyclic hydrocarbon group is usually 5 or more, preferably 6 to 30, and more preferably 7 to 25.

Examples of the alicyclic hydrocarbon group include those having the partial structures listed below. Each of these partial structures may have a substituent. In each of these partial structures, the methylene group (—CH ₂ —) includes an oxygen atom (—O—), a sulfur atom (—S—), a carbonyl group [—C (═O) —], a sulfonyl group [ -S (= O) _2- ], a sulfinyl group [-S (= O)-], or an imino group [-N (R)-] (R is a hydrogen atom or an alkyl group).

For example, when R ₁ and / or R ₂ is a cycloalkylene group, R ₁ and / or R ₂ may be an adamantylene group, a noradamantylene group, a decahydronaphthylene group, a tricyclodecanylene group, a tetracyclododeca group. Nylene group, norbornylene group, cyclopentylene group, cyclohexylene group, cycloheptylene group, cyclooctylene group, cyclodecanylene group, or cyclododecanylene group are preferable, and adamantylene group, norbornylene group, cyclohexylene group, cyclopentylene It is more preferable that they are a len group, a tetracyclododecanylene group, or a tricyclodecanylene group.
The non-aromatic hydrocarbon group of R ₁ and / or R ₂ may have a substituent. Examples of the substituent include an alkyl group having 1 to 4 carbon atoms, a halogen atom, a hydroxy group, an alkoxy group having 1 to 4 carbon atoms, a carboxy group, and an alkoxycarbonyl group having 2 to 6 carbon atoms. The above alkyl group, alkoxy group and alkoxycarbonyl group may further have a substituent. As this substituent, a hydroxy group, a halogen atom, and an alkoxy group are mentioned, for example.
L ₁ represents a linking group represented by —COO—, —OCO—, —CONH—, —O—, —Ar—, —SO ₃ — or —SO ₂ NH—. Here, Ar represents a divalent aromatic ring group. L ₁ is preferably a linking group represented by —COO—, —CONH— or —Ar—, and more preferably a linking group represented by —COO— or —CONH—.
R represents a hydrogen atom or an alkyl group. The alkyl group may be linear or branched. Carbon number of this alkyl group becomes like this. Preferably it is 1-6, More preferably, it is 1-3. R is preferably a hydrogen atom or a methyl group, and more preferably a hydrogen atom.

R ₀ represents a hydrogen atom or an organic group. Examples of the organic group include an alkyl group, a cycloalkyl group, an aryl group, an alkynyl group, and an alkenyl group. R ₀ is preferably a hydrogen atom or an alkyl group, and more preferably a hydrogen atom or a methyl group.
L ₃ represents a (m + 2) -valent linking group. That is, L ₃ represents a trivalent or higher linking group. Examples of such a linking group include corresponding groups in specific examples described later.
R ^L represents a (n + 1) -valent linking group. That is, R ^L represents a divalent or higher linking group. Examples of such a linking group include an alkylene group, a cycloalkylene group, and corresponding groups in the specific examples described below. R ^L may be bonded to each other or bonded to the following R ^S to form a ring structure.
R ^S represents a substituent. Examples of the substituent include an alkyl group, an alkenyl group, an alkynyl group, an aryl group, an alkoxy group, an acyloxy group, an alkoxycarbonyl group, and a halogen atom.
n is an integer of 1 or more. n is preferably an integer of 1 to 3, and more preferably 1 or 2. When n is 2 or more, it is possible to further improve the dissolution contrast with respect to a developer containing an organic solvent. Accordingly, in this way, the limit resolution and roughness characteristics can be further improved.
m is an integer of 1 or more. m is preferably an integer of 1 to 3, and more preferably 1 or 2.
l is an integer of 0 or more. l is preferably 0 or 1.
p is an integer of 0-3.
The content of the repeating unit having an alcoholic hydroxy group is preferably from 1 to 60 mol%, more preferably from 3 to 50 mol%, still more preferably from 5 to 40 mol%, based on all repeating units in the resin (A). It is.
Specific examples of the repeating unit represented by any one of the general formulas (I-1H) to (I-10H) are shown below. In specific examples, Ra is as defined in general formulas (I-1H) to (I-10H).

  When the polar group of the repeating unit (c) is an alcoholic hydroxy group or a cyano group, it is a repeating unit having an alicyclic hydrocarbon structure substituted with a hydroxyl group or a cyano group as one embodiment of a preferable repeating unit. Is mentioned. At this time, it is preferable not to have an acid-decomposable group. The alicyclic hydrocarbon structure in the alicyclic hydrocarbon structure substituted with a hydroxyl group or a cyano group is preferably an adamantyl group, a diamantyl group, or a norbornane group. As the alicyclic hydrocarbon structure substituted with a preferred hydroxyl group or cyano group, partial structures represented by the following general formulas (VIIa) to (VIIc) are preferable. This improves the substrate adhesion and developer compatibility.

In general formulas (VIIa) to (VIIc),
R ₂ c to R ₄ c each independently represents a hydrogen atom, a hydroxyl group, or a cyano group. However, at least one of R ₂ c to R ₄ c represents a hydroxyl group. Preferably, one or two of R ₂ c to R ₄ c are a hydroxyl group and the rest are hydrogen atoms. In general formula (VIIa), more preferably, _two of R ₂ c to R ₄ c are a hydroxyl group and the rest are hydrogen atoms.

  Examples of the repeating unit having a partial structure represented by the general formulas (VIIa) to (VIIc) include the repeating units represented by the following general formulas (AIIa) to (AIIc).

In the general formulas (AIIa) to (AIIc),
R ₁ c represents a hydrogen atom, a methyl group, a trifluoromethyl group, or a hydroxymethyl group.

R ₂ c to R ₄ c are in the general formula (VIIa) ~ _(VIIc), same meanings as R 2 c~R ₄ c.

  The resin (A) may or may not contain a repeating unit having a hydroxyl group or a cyano group. However, when it is contained, the content of the repeating unit having a hydroxyl group or a cyano group is in the resin (A). The total repeating unit is preferably 1 to 60 mol%, more preferably 3 to 50 mol%, still more preferably 5 to 40 mol%.

  Specific examples of the repeating unit having a hydroxyl group or a cyano group are given below, but the present invention is not limited thereto.

The repeating unit (c) may be a repeating unit having a lactone structure or a sultone structure as a polar group.
As the repeating unit having a lactone structure or a sultone structure, a repeating unit represented by the following general formula (AII) is more preferable.

In general formula (AII),
Rb ₀ represents a hydrogen atom, a halogen atom or an optionally substituted alkyl group (preferably having 1 to 4 carbon atoms).
Preferable substituents that the alkyl group of Rb ₀ may have include a hydroxyl group and a halogen atom. Examples of the halogen atom for Rb ₀ include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom. Rb ₀ is preferably a hydrogen atom, a methyl group, a hydroxymethyl group or a trifluoromethyl group, and particularly preferably a hydrogen atom or a methyl group.

Ab represents a single bond, an alkylene group, a divalent linking group having a monocyclic or polycyclic cycloalkyl structure, an ether bond, an ester bond, a carbonyl group, or a divalent linking group obtained by combining these. Ab is preferably a single bond or a divalent linking group represented by —Ab ₁ —CO ₂ —.
Ab ₁ is a linear or branched alkylene group, a monocyclic or polycyclic cycloalkylene group, and preferably a methylene group, an ethylene group, a cyclohexylene group, an adamantylene group, or a norbornylene group.
V represents a group having a lactone structure or a sultone structure.

  As the group having a lactone structure or a sultone structure, any group having a lactone structure or a sultone structure can be used, but a 5- to 7-membered lactone structure or sultone structure is preferable, and a 5 to 7-membered structure is preferable. Those in which other ring structures are condensed in a form forming a bicyclo structure or a spiro structure in the lactone structure or sultone structure of the ring are preferable. Repeat having a lactone structure represented by any of the following general formulas (LC1-1) to (LC1-17) or a sultone structure represented by any of the following general formulas (SL1-1) or (SL1-2) More preferably it has units. A lactone structure or a sultone structure may be directly bonded to the main chain. Particularly preferred structures are (LC1-1), (LC1-4), (LC1-5), (LC1-6), (LC1-8), (LC1-13), (LC1-14), (SL1- 1).

The lactone structure portion or sultone structure may or may not have a substituent (Rb ₂ ). Preferred substituents (Rb ₂ ) include an alkyl group having 1 to 8 carbon atoms, a monovalent cycloalkyl group having 4 to 7 carbon atoms, an alkoxy group having 1 to 8 carbon atoms, and an alkoxycarbonyl group having 2 to 8 carbon atoms. , Carboxyl group, halogen atom, hydroxyl group, cyano group, acid-decomposable group and the like. More preferably, they are a C1-C4 alkyl group, a cyano group, and an acid-decomposable group. n ₂ represents an integer of 0-4. When n ₂ is 2 or more, a plurality of substituents (Rb ₂ ) may be the same or different, and a plurality of substituents (Rb ₂ ) may be bonded to form a ring. .

  The repeating unit having a lactone structure or a sultone structure usually has an optical isomer, but any optical isomer may be used. One optical isomer may be used alone, or a plurality of optical isomers may be mixed and used. When one kind of optical isomer is mainly used, the optical purity (ee) thereof is preferably 90% or more, more preferably 95% or more.

The resin (A) may or may not contain a repeating unit having a lactone structure or a sultone structure, but when it contains a repeating unit having a lactone structure or a sultone structure, the repeating unit in the resin (A) The content of is preferably in the range of 1 to 70 mol%, more preferably in the range of 3 to 65 mol%, still more preferably in the range of 5 to 60 mol% with respect to all repeating units.
Specific examples of the repeating unit having a lactone structure or a sultone structure in the resin (A) are shown below, but the present invention is not limited thereto. In the formula, Rx represents H, CH ₃ , CH ₂ OH, or CF ₃ .

  Moreover, it is also one of the especially preferable aspects that the polar group which a repeating unit (c) can have is an acidic group. Preferred acidic groups include phenolic hydroxyl groups, carboxylic acid groups, sulfonic acid groups, fluorinated alcohol groups (eg hexafluoroisopropanol group), sulfonamide groups, sulfonylimide groups, (alkylsulfonyl) (alkylcarbonyl) methylene groups, Alkylsulfonyl) (alkylcarbonyl) imide group, bis (alkylcarbonyl) methylene group, bis (alkylcarbonyl) imide group, bis (alkylsulfonyl) methylene group, bis (alkylsulfonyl) imide group, tris (alkylcarbonyl) methylene group, A tris (alkylsulfonyl) methylene group is mentioned. Of these, the repeating unit (c) is more preferably a repeating unit having a carboxyl group. By containing the repeating unit having an acidic group, the resolution in the contact hole application is increased. The repeating unit having an acidic group includes a repeating unit in which an acidic group is directly bonded to the main chain of the resin, such as a repeating unit of acrylic acid or methacrylic acid, or an acidic group in the main chain of the resin through a linking group. It is preferable to use a polymerization initiator or a chain transfer agent having a repeating unit bonded to each other, or an acidic group, at the time of polymerization and introduce it at the end of the polymer chain. Particularly preferred are repeating units of acrylic acid or methacrylic acid.

The acidic group that the repeating unit (c) may have may or may not contain an aromatic ring, but when it has an aromatic ring, it is preferably selected from acidic groups other than phenolic hydroxyl groups. When the repeating unit (c) has an acidic group, the content of the repeating unit having an acidic group is preferably 30 mol% or less, and 20 mol% or less with respect to all the repeating units in the resin (A). More preferably. When resin (A) contains the repeating unit which has an acidic group, content of the repeating unit which has an acidic group in resin (A) is 1 mol% or more normally.
Specific examples of the repeating unit having an acidic group are shown below, but the present invention is not limited thereto.
In specific examples, Rx represents H, CH ₃ , CH ₂ OH, or CF ₃ .

(D) Repeating unit having a plurality of aromatic rings The resin (A) may have a repeating unit (d) having a plurality of aromatic rings represented by the following general formula (c1).

In general formula (c1),
R ₃ represents a hydrogen atom, an alkyl group, a halogen atom, a cyano group or a nitro group,
Y represents a single bond or a divalent linking group,
Z represents a single bond or a divalent linking group;
Ar represents an aromatic ring group,
p represents an integer of 1 or more.

The alkyl group as R ₃ may be either linear or branched, for example, methyl group, ethyl group, n-propyl group, i-propyl group, n-butyl group, sec-butyl group, t-butyl. Group, n-pentyl group, n-hexyl group, n-heptyl group, n-octyl group, n-nonyl group, n-decanyl group and i-butyl group, and may further have a substituent. Preferred examples of the substituent include an alkoxy group, a hydroxyl group, a halogen atom, and a nitro group. Among them, examples of the alkyl group having a substituent include a CF ₃ group, an alkyloxycarbonylmethyl group, an alkylcarbonyloxymethyl group, and hydroxymethyl. Group, alkoxymethyl group and the like are preferable.

Examples of the halogen atom as R ₃ include a fluorine atom, a chlorine atom, a bromine atom and an iodine atom, and a fluorine atom is particularly preferable.
Y represents a single bond or a divalent linking group, and examples of the divalent linking group include an ether group (oxygen atom), a thioether group (sulfur atom), an alkylene group, an arylene group, a carbonyl group, a sulfide group, Sulfone group, —COO—, —CONH—, —SO ₂ NH—, —CF ₂ —, —CF ₂ CF ₂ —, —OCF ₂ O—, —CF ₂ OCF ₂ —, —SS—, —CH ₂ SO ₂ CH ₂ —, —CH ₂ COCH ₂ —, —COCF ₂ CO—, —COCO—, —OCOO—, —OSO ₂ O—, amino group (nitrogen atom), acyl group, alkylsulfonyl group, —CH═CH And —C—C≡C—, an aminocarbonylamino group, an aminosulfonylamino group, or a combination thereof. Y preferably has 15 or less carbon atoms, more preferably 10 or less carbon atoms.

Y is preferably a single bond, —COO— group, —COS— group, —CONH— group, more preferably —COO— group, —CONH— group, and particularly preferably —COO— group.
Z represents a single bond or a divalent linking group, and examples of the divalent linking group include an ether group (oxygen atom), a thioether group (sulfur atom), an alkylene group, an arylene group, a carbonyl group, a sulfide group, Sulfone group, —COO—, —CONH—, —SO ₂ NH—, amino group (nitrogen atom), acyl group, alkylsulfonyl group, —CH═CH—, aminocarbonylamino group, aminosulfonylamino group, or these Examples include groups consisting of combinations.
Z is preferably a single bond, an ether group, a carbonyl group, or —COO—, more preferably a single bond or an ether group, and particularly preferably a single bond.

Ar represents an aromatic ring group, specifically, phenyl group, naphthyl group, anthracenyl group, phenanthrenyl group, quinolinyl group, furanyl group, thiophenyl group, fluorenyl-9-one-yl group, anthraquinonyl group, phenanthralkyl. A nonyl group, a pyrrole group, etc. are mentioned, A phenyl group is preferable. These aromatic ring groups may further have a substituent. Preferred examples of the substituent include an alkyl group, an alkoxy group, a hydroxyl group, a halogen atom, a nitro group, an acyl group, an acyloxy group, an acylamino group, and a sulfonylamino group. Group, aryl group such as phenyl group, aryloxy group, arylcarbonyl group, heterocyclic residue, etc. Among them, phenyl group suppresses deterioration of exposure latitude and pattern shape caused by out-of-band light It is preferable from the viewpoint.
p is an integer of 1 or more, and is preferably an integer of 1 to 3.

  The repeating unit (d) is more preferably a repeating unit represented by the following formula (c2).

In general formula (c2), R ₃ represents a hydrogen atom or an alkyl group. The thing preferable as an alkyl group as R < ₃ > is the same as that of general formula (c1).

Here, regarding extreme ultraviolet (EUV light) exposure, leakage light (out-of-band light) generated in the ultraviolet region with a wavelength of 100 to 400 nm deteriorates surface roughness, resulting in bridges between patterns and disconnection of patterns. , Resolution and LWR performance tend to decrease.
However, the aromatic ring in the repeating unit (d) functions as an internal filter that can absorb the out-of-band light. Therefore, from the viewpoint of high resolution and low LWR, the resin (A) preferably contains the repeating unit (d).
Here, it is preferable that the repeating unit (d) does not have a phenolic hydroxyl group (a hydroxyl group directly bonded on an aromatic ring) from the viewpoint of obtaining high resolution.

  Specific examples of the repeating unit (d) are shown below, but are not limited thereto.

  The resin (A) may or may not contain the repeating unit (d), but when it is contained, the content of the repeating unit (d) is 1 to 30 with respect to the entire repeating unit (A). It is preferably in the range of mol%, more preferably in the range of 1 to 20 mol%, and still more preferably in the range of 1 to 15 mol%. The repeating unit (d) contained in the resin (A) may contain a combination of two or more types.

  The resin (A) in the present invention may appropriately have a repeating unit other than the repeating units (a) to (d). As an example of such a repeating unit, a repeating unit that has an alicyclic hydrocarbon structure that does not have a polar group (for example, the acid group, hydroxyl group, and cyano group) and does not exhibit acid decomposability can be included. Thereby, the solubility of the resin can be appropriately adjusted during development using a developer containing an organic solvent. Examples of such a repeating unit include a repeating unit represented by the general formula (IV).

In general formula (IV), R ₅ represents a hydrocarbon group having at least one cyclic structure and having no polar group.
Ra represents a hydrogen atom, an alkyl group, or a —CH ₂ —O—Ra ₂ group. In the formula, Ra ₂ represents a hydrogen atom, an alkyl group, or an acyl group. Ra is preferably a hydrogen atom, a methyl group, a hydroxymethyl group or a trifluoromethyl group, particularly preferably a hydrogen atom or a methyl group.

The cyclic structure possessed by R ₅ includes a monocyclic hydrocarbon group and a polycyclic hydrocarbon group. Examples of the monocyclic hydrocarbon group include cycloalkenyl having 3 to 12 carbon atoms such as cyclopentyl group, cyclohexyl group, cycloheptyl group, cyclooctyl group and the like, and cycloalkyl groups having 3 to 12 carbon atoms and cyclohexenyl group. Groups. The preferred monocyclic hydrocarbon group is a monocyclic hydrocarbon group having 3 to 7 carbon atoms, more preferably a cyclopentyl group or a cyclohexyl group.

The polycyclic hydrocarbon group includes a ring assembly hydrocarbon group and a bridged cyclic hydrocarbon group, and examples of the ring assembly hydrocarbon group include a bicyclohexyl group and a perhydronaphthalenyl group. As the bridged cyclic hydrocarbon ring, for example, bicyclic such as pinane, bornane, norpinane, norbornane, bicyclooctane ring (bicyclo [2.2.2] octane ring, bicyclo [3.2.1] octane ring, etc.) Hydrocarbon rings and tricyclic hydrocarbon rings such as homobredan, adamantane, tricyclo [5.2.1.0 ^2,6 ] decane, tricyclo [4.3.1.1 ^2,5 ] undecane ring, tetracyclo [ 4.4.0.1 ^2,5 . 1 ^7,10 ] dodecane, and tetracyclic hydrocarbon rings such as perhydro-1,4-methano-5,8-methanonaphthalene ring. The bridged cyclic hydrocarbon ring includes a condensed cyclic hydrocarbon ring such as perhydronaphthalene (decalin), perhydroanthracene, perhydrophenanthrene, perhydroacenaphthene, perhydrofluorene, perhydroindene, perhydroindene. A condensed ring in which a plurality of 5- to 8-membered cycloalkane rings such as a phenalene ring are condensed is also included.

Preferred examples of the bridged cyclic hydrocarbon ring include a norbornyl group, an adamantyl group, a bicyclooctanyl group, a tricyclo [5.2.1.0 ^2,6 ] decanyl group, and the like. More preferable examples of the bridged cyclic hydrocarbon ring include a norbornyl group and an adamantyl group.

  These alicyclic hydrocarbon groups may have a substituent. Preferred examples of the substituent include a halogen atom, an alkyl group, a hydroxyl group substituted with a hydrogen atom, and an amino group substituted with a hydrogen atom. It is done. Preferred halogen atoms include bromine, chlorine and fluorine atoms, and preferred alkyl groups include methyl, ethyl, butyl and t-butyl groups. The alkyl group described above may further have a substituent, and examples of the substituent that may further include a halogen atom, an alkyl group, a hydroxyl group substituted with a hydrogen atom, and an amino group substituted with a hydrogen atom. The group can be mentioned.

  Examples of the substituent for the hydrogen atom include an alkyl group, a cycloalkyl group, an aralkyl group, a substituted methyl group, a substituted ethyl group, an alkoxycarbonyl group, and an aralkyloxycarbonyl group. Preferred alkyl groups include alkyl groups having 1 to 4 carbon atoms, preferred substituted methyl groups include methoxymethyl, methoxythiomethyl, benzyloxymethyl, t-butoxymethyl, 2-methoxyethoxymethyl groups, and preferred substituted ethyl groups. 1-ethoxyethyl, 1-methyl-1-methoxyethyl, preferred acyl groups include formyl, acetyl, propionyl, butyryl, isobutyryl, valeryl, pivaloyl groups, etc., aliphatic acyl groups having 1 to 6 carbon atoms, alkoxycarbonyl Examples of the group include an alkoxycarbonyl group having 1 to 4 carbon atoms.

The resin (A) has an alicyclic hydrocarbon structure having no polar group, and may or may not contain a repeating unit that does not exhibit acid decomposability. The content is preferably 1 to 20 mol%, more preferably 5 to 15 mol%, based on all repeating units in the resin (A).
Specific examples of the repeating unit having an alicyclic hydrocarbon structure having no polar group and not exhibiting acid decomposability are shown below, but the present invention is not limited thereto. In the formula, Ra represents H, CH ₃ , CH ₂ OH, or CF ₃ .

  Moreover, resin (A) may further contain the repeating unit represented by following General formula (5).

R ⁴¹ represents a hydrogen atom or a methyl group. L ⁴¹ represents a single bond or a divalent linking group. L ⁴² represents a divalent linking group. S represents a structural site that decomposes upon irradiation with actinic rays or radiation to generate an acid in the side chain.

  Although the specific example of the repeating unit represented by General formula (5) below is shown, this invention is not limited to this.

  The content of the repeating unit represented by the general formula (5) in the resin (A) is preferably in the range of 1 to 40 mol%, and in the range of 2 to 30 mol% with respect to all the repeating units of the resin (A). Is more preferable, and the range of 5 to 25 mol% is particularly preferable.

  Further, the resin (A) may contain the following monomer components in view of the effects such as improvement of Tg, improvement of dry edging resistance, the above-described internal filter of out-of-band light, and the like.

  In the resin (A) used in the composition of the present invention, the content molar ratio of each repeating structural unit is the resist dry etching resistance, standard developer suitability, substrate adhesion, resist profile, and general resist requirements. It is appropriately set in order to adjust the resolution, heat resistance, sensitivity, etc., which are performance.

  Specific examples of the resin (A) are shown below, but the present invention is not limited thereto.

The form of the resin (A) in the present invention may be any of random type, block type, comb type, and star type.
Resin (A) is compoundable by the radical, cation, or anion polymerization of the unsaturated monomer corresponding to each structure, for example. It is also possible to obtain the desired resin by conducting a polymer reaction after polymerization using an unsaturated monomer corresponding to the precursor of each structure.
For example, as a general synthesis method, an unsaturated monomer and a polymerization initiator are dissolved in a solvent, and a batch polymerization method in which polymerization is performed by heating, a solution of an unsaturated monomer and a polymerization initiator in a heating solvent for 1 to 10 hours. The dropping polymerization method etc. which are dropped and added over are mentioned, and the dropping polymerization method is preferable.

Examples of the solvent used for the polymerization include a solvent that can be used in preparing the actinic ray-sensitive or radiation-sensitive resin composition described below, and more preferably the composition of the present invention. Polymerization is preferably carried out using the same solvent as used in the above. Thereby, generation | occurrence | production of the particle at the time of a preservation | save can be suppressed.
The polymerization reaction is preferably performed in an inert gas atmosphere such as nitrogen or argon. As a polymerization initiator, a commercially available radical initiator (azo initiator, peroxide, etc.) is used to initiate the polymerization. As the radical initiator, an azo initiator is preferable, and an azo initiator having an ester group, a cyano group, or a carboxyl group is preferable. Preferred examples of the initiator include azobisisobutyronitrile, azobisdimethylvaleronitrile, dimethyl 2,2′-azobis (2-methylpropionate) and the like. If necessary, the polymerization may be performed in the presence of a chain transfer agent (for example, alkyl mercaptan).

The reaction concentration is 5 to 70% by mass, preferably 10 to 50% by mass. The reaction temperature is usually from 10 ° C to 150 ° C, preferably from 30 ° C to 120 ° C, more preferably from 40 ° C to 100 ° C.
The reaction time is usually 1 to 48 hours, preferably 1 to 24 hours, more preferably 1 to 12 hours.
After completion of the reaction, the mixture is allowed to cool to room temperature and purified. Purification can be accomplished by a liquid-liquid extraction method that removes residual monomers and oligomer components by combining water and an appropriate solvent, and a purification method in a solution state such as ultrafiltration that extracts and removes only those having a specific molecular weight or less. , Reprecipitation method that removes residual monomer by coagulating resin in poor solvent by dripping resin solution into poor solvent and purification in solid state such as washing filtered resin slurry with poor solvent A normal method such as a method can be applied. For example, the resin is precipitated as a solid by contacting a solvent (poor solvent) in which the resin is hardly soluble or insoluble in a volume amount of 10 times or less, preferably 10 to 5 times that of the reaction solution.

The solvent (precipitation or reprecipitation solvent) used in the precipitation or reprecipitation operation from the polymer solution may be a poor solvent for the polymer, and may be a hydrocarbon, halogenated hydrocarbon, nitro, depending on the type of polymer. A compound, ether, ketone, ester, carbonate, alcohol, carboxylic acid, water, a mixed solvent containing these solvents, and the like can be appropriately selected for use. Among these, as a precipitation or reprecipitation solvent, a solvent containing at least an alcohol (particularly methanol or the like) or water is preferable.
The amount of the precipitation or reprecipitation solvent used can be appropriately selected in consideration of efficiency, yield, and the like, but generally 100 to 10000 parts by mass, preferably 200 to 2000 parts by mass with respect to 100 parts by mass of the polymer solution, More preferably, it is 300-1000 mass parts.
The temperature for precipitation or reprecipitation can be appropriately selected in consideration of efficiency and operability, but is usually about 0 to 50 ° C., preferably around room temperature (for example, about 20 to 35 ° C.). The precipitation or reprecipitation operation can be performed by a known method such as a batch method or a continuous method using a conventional mixing vessel such as a stirring tank.
The precipitated or re-precipitated polymer is usually subjected to conventional solid-liquid separation such as filtration and centrifugation, and dried before use. Filtration is performed using a solvent-resistant filter medium, preferably under pressure. Drying is performed at a temperature of about 30 to 100 ° C., preferably about 30 to 50 ° C. under normal pressure or reduced pressure (preferably under reduced pressure).

In addition, once the resin is precipitated and separated, it may be dissolved again in a solvent, and the resin may be brought into contact with a hardly soluble or insoluble solvent. That is, after completion of the radical polymerization reaction, a solvent in which the polymer is hardly soluble or insoluble is brought into contact, the resin is precipitated (step a), the resin is separated from the solution (step b), and dissolved again in the solvent. (Step c), and then contact the resin solution A with a solvent in which the resin is hardly soluble or insoluble in a volume amount less than 10 times that of the resin solution A (preferably 5 times or less volume). This may be a method including precipitating a resin solid (step d) and separating the precipitated resin (step e).
The polymerization reaction is preferably performed in an inert gas atmosphere such as nitrogen or argon. As a polymerization initiator, a commercially available radical initiator (azo initiator, peroxide, etc.) is used to initiate the polymerization. As the radical initiator, an azo initiator is preferable, and an azo initiator having an ester group, a cyano group, or a carboxyl group is preferable. Preferred examples of the initiator include azobisisobutyronitrile, azobisdimethylvaleronitrile, dimethyl 2,2′-azobis (2-methylpropionate) and the like. If desired, an initiator is added or added in portions, and after completion of the reaction, it is put into a solvent and a desired polymer is recovered by a method such as powder or solid recovery. The concentration of the reaction is 5 to 50% by mass, preferably 10 to 30% by mass. The reaction temperature is usually from 10 ° C to 150 ° C, preferably from 30 ° C to 120 ° C, more preferably from 60 ° C to 100 ° C.

  The molecular weight of the resin (A) in the present invention is not particularly limited, but the weight average molecular weight is preferably in the range of 1000 to 100,000, more preferably in the range of 1500 to 60000, and in the range of 2000 to 30000. It is particularly preferred. By setting the weight average molecular weight in the range of 1000 to 100,000, it is possible to prevent heat resistance and dry etching resistance from being deteriorated, and also to prevent developability from being deteriorated and the film forming property from being deteriorated due to increased viscosity. be able to. Here, the weight average molecular weight of the resin indicates a molecular weight in terms of polystyrene measured by GPC (carrier: THF or N-methyl-2-pyrrolidone (NMP)).

  Moreover, dispersity (Mw / Mn) becomes like this. Preferably it is 1.00-5.00, More preferably, it is 1.00-3.50, More preferably, it is 1.00-2.50. The smaller the molecular weight distribution, the better the resolution and the resist shape, and the smoother the side wall of the resist pattern, the better the roughness.

  In this specification, the weight average molecular weight (Mw) and dispersity of the resin are, for example, HLC-8120 (manufactured by Tosoh Corp.) and TSK gel Multipore HXL-M (manufactured by Tosoh Corp., 7. 8 mm HD × 30.0 cm) can be determined by using THF (tetrahydrofuran) or NMP (N-methyl-2-pyrrolidone) as the eluent.

Resin (A) in this invention can be used individually by 1 type or in combination of 2 or more types. The content of the resin (A) is preferably 20 to 99 mass%, more preferably 30 to 99 mass%, based on the total solid content in the actinic ray-sensitive or radiation-sensitive resin composition of the present invention. 40-99 mass% is still more preferable.
[2] (B) Compound capable of generating acid upon irradiation with actinic ray or radiation The composition of the present invention usually comprises a compound that generates acid upon irradiation with actinic ray or radiation (hereinafter also referred to as “acid generator”). It is preferable to contain.
The acid generator is not particularly limited as long as it is a publicly known acid generator, but upon irradiation with actinic rays or radiation, at least any of organic acids such as sulfonic acid, bis (alkylsulfonyl) imide, and tris (alkylsulfonyl) methide. Compounds that generate such are preferred.
The compound (B) that generates an acid upon irradiation with actinic rays or radiation may be in the form of a low molecular compound or may be incorporated in a part of the polymer. Further, the form of the low molecular compound and the form incorporated in a part of the polymer may be used in combination.
When the compound (B) that generates an acid upon irradiation with actinic rays or radiation is in the form of a low molecular compound, the molecular weight is preferably 3000 or less, more preferably 2000 or less, and 1000 or less. Is more preferable.
When the compound (B) that generates an acid upon irradiation with actinic rays or radiation is in a form incorporated in a part of the polymer, the resin (A) is incorporated into a part of the resin (A) described above. You may comprise, You may incorporate in resin different from resin (A).
More preferred examples include compounds represented by the following general formulas (ZI), (ZII), and (ZIII).

In the general formula (ZI),
R ₂₀₁ , R ₂₀₂ and R ₂₀₃ each independently represents an organic group.
The carbon number of the organic group as R ₂₀₁ , R ₂₀₂ and R ₂₀₃ is generally 1 to 30, preferably 1 to 20.
Two of R _{201 to} R ₂₀₃ may be bonded to form a ring structure, and the ring may contain an oxygen atom, a sulfur atom, an ester bond, an amide bond, or a carbonyl group. Examples of the group formed by combining two of R _{201 to} R ₂₀₃ include an alkylene group (eg, butylene group, pentylene group).
Z ⁻ represents a non-nucleophilic anion (an anion having an extremely low ability to cause a nucleophilic reaction).

  Non-nucleophilic anions include, for example, sulfonate anions (aliphatic sulfonate anions, aromatic sulfonate anions, camphor sulfonate anions, etc.), carboxylate anions (aliphatic carboxylate anions, aromatic carboxylate anions, aralkyls). Carboxylate anion, etc.), sulfonylimide anion, bis (alkylsulfonyl) imide anion, tris (alkylsulfonyl) methide anion and the like.

  The aliphatic moiety in the aliphatic sulfonate anion and the aliphatic carboxylate anion may be an alkyl group or a cycloalkyl group, preferably a linear or branched alkyl group having 1 to 30 carbon atoms and a carbon number. 3-30 cycloalkyl groups are mentioned.

  The aromatic group in the aromatic sulfonate anion and aromatic carboxylate anion is preferably an aryl group having 6 to 14 carbon atoms such as a phenyl group, a tolyl group, and a naphthyl group.

  The alkyl group, cycloalkyl group and aryl group mentioned above may have a substituent. Specific examples thereof include nitro groups, halogen atoms such as fluorine atoms, carboxyl groups, hydroxyl groups, amino groups, cyano groups, alkoxy groups (preferably having 1 to 15 carbon atoms), cycloalkyl groups (preferably having 3 to 15 carbon atoms). ), An aryl group (preferably 6 to 14 carbon atoms), an alkoxycarbonyl group (preferably 2 to 7 carbon atoms), an acyl group (preferably 2 to 12 carbon atoms), an alkoxycarbonyloxy group (preferably 2 to 2 carbon atoms). 7), an alkylthio group (preferably 1 to 15 carbon atoms), an alkylsulfonyl group (preferably 1 to 15 carbon atoms), an alkyliminosulfonyl group (preferably 1 to 15 carbon atoms), an aryloxysulfonyl group (preferably carbon) Number 6-20), alkylaryloxysulfonyl group (preferably C7-20), cycloalkylary Examples thereof include an oxysulfonyl group (preferably having 10 to 20 carbon atoms), an alkyloxyalkyloxy group (preferably having 5 to 20 carbon atoms), a cycloalkylalkyloxyalkyloxy group (preferably having 8 to 20 carbon atoms), and the like. . About the aryl group and ring structure which each group has, an alkyl group (preferably C1-C15) can further be mentioned as a substituent.

  The aralkyl group in the aralkyl carboxylate anion is preferably an aralkyl group having 7 to 12 carbon atoms, such as a benzyl group, a phenethyl group, a naphthylmethyl group, a naphthylethyl group, and a naphthylbutyl group.

  Examples of the sulfonylimide anion include saccharin anion.

The alkyl group in the bis (alkylsulfonyl) imide anion and tris (alkylsulfonyl) methide anion is preferably an alkyl group having 1 to 5 carbon atoms. Examples of substituents for these alkyl groups include halogen atoms, alkyl groups substituted with halogen atoms, alkoxy groups, alkylthio groups, alkyloxysulfonyl groups, aryloxysulfonyl groups, cycloalkylaryloxysulfonyl groups, and the like. A fluorine atom or an alkyl group substituted with a fluorine atom is preferred.
The alkyl groups in the bis (alkylsulfonyl) imide anion may be bonded to each other to form a ring structure. This increases the acid strength.

Examples of other non-nucleophilic anions include fluorinated phosphorus (eg, PF ₆ ⁻ ), fluorinated boron (eg, BF ₄ ⁻ ), and fluorinated antimony (eg, SbF ₆ ⁻ ). .

  Examples of the non-nucleophilic anion include an aliphatic sulfonate anion in which at least α-position of the sulfonic acid is substituted with a fluorine atom, an aromatic sulfonate anion substituted with a fluorine atom or a group having a fluorine atom, and an alkyl group having a fluorine atom And a tris (alkylsulfonyl) methide anion in which the alkyl group is substituted with a fluorine atom. The non-nucleophilic anion is more preferably a perfluoroaliphatic sulfonate anion (more preferably 4 to 8 carbon atoms), a benzenesulfonate anion having a fluorine atom, still more preferably a nonafluorobutanesulfonate anion, or perfluorooctane. A sulfonate anion, a pentafluorobenzenesulfonate anion, and a 3,5-bis (trifluoromethyl) benzenesulfonate anion.

  From the viewpoint of acid strength, the pKa of the generated acid is preferably −1 or less in order to improve sensitivity.

  Moreover, as a non-nucleophilic anion, the anion represented with the following general formula (AN1) is also mentioned as a preferable aspect.

Where
Xf each independently represents a fluorine atom or an alkyl group substituted with at least one fluorine atom.
R ¹ and R ² each independently represent a hydrogen atom, a fluorine atom or an alkyl group, and when there are a plurality of R ¹ and R ² , they may be the same or different.
L represents a divalent linking group, and when there are a plurality of L, L may be the same or different.
A represents a cyclic organic group.
x represents an integer of 1 to 20, y represents an integer of 0 to 10, and z represents an integer of 0 to 10.

The general formula (AN1) will be described in more detail.
The alkyl group in the alkyl group substituted with the fluorine atom of Xf preferably has 1 to 10 carbon atoms, more preferably 1 to 4 carbon atoms. The alkyl group substituted with a fluorine atom of Xf is preferably a perfluoroalkyl group.
Xf is preferably a fluorine atom or a perfluoroalkyl group having 1 to 4 carbon atoms. Specific examples of Xf include fluorine atom, CF ₃ , C ₂ F ₅ , C ₃ F ₇ , C ₄ F ₉ , CH ₂ CF ₃ , CH ₂ CH ₂ CF ₃ , CH ₂ C ₂ F ₅ , CH ₂ CH ₂ C ₂ F ₅ , CH ₂ C ₃ F ₇ , CH ₂ CH ₂ C ₃ F ₇ , CH ₂ C ₄ F ₉ , CH ₂ CH ₂ C ₄ F ₉ may be mentioned, among which a fluorine atom and CF ₃ are preferable. In particular, it is preferable that both Xf are fluorine atoms.

The alkyl group of R ¹ and R ² may have a substituent (preferably a fluorine atom), and preferably has 1 to 4 carbon atoms. More preferably, it is a C1-C4 perfluoroalkyl group. Specific examples of the alkyl group having a substituent for R ¹ and R ² include CF ₃ , C ₂ F ₅ , C ₃ F ₇ , C ₄ F ₉ , C ₅ F ₁₁ , C ₆ F ₁₃ , and C ₇ F _{15. , C 8 F 17, CH 2} CF 3, CH 2 CH 2 CF 3, CH 2 C 2 F 5, CH 2 CH 2 C 2 F 5, CH 2 C 3 F 7, CH 2 CH 2 C 3 F 7, CH ₂ C ₄ F ₉ and CH ₂ CH ₂ C ₄ F ₉ can be mentioned, among which CF ₃ is preferable.
R ¹ and R ² are preferably a fluorine atom or CF ₃ .

x is preferably 1 to 10, and more preferably 1 to 5.
y is preferably 0 to 4, and more preferably 0.
z is preferably 0 to 5, and more preferably 0 to 3.
The divalent linking group of L is not particularly limited, and is —COO—, —OCO—, —CO—, —O—, —S—, —SO—, —SO ₂ —, an alkylene group, a cycloalkylene group, An alkenylene group or a linking group in which a plurality of these groups are linked can be exemplified, and a linking group having a total carbon number of 12 or less is preferred. Among these, —COO—, —OCO—, —CO—, and —O— are preferable, and —COO— and —OCO— are more preferable.

The cyclic organic group of A is not particularly limited as long as it has a cyclic structure, and is not limited to alicyclic groups, aryl groups, and heterocyclic groups (not only those having aromaticity but also aromaticity). And the like).
The alicyclic group may be monocyclic or polycyclic, and may be a monocyclic cycloalkyl group such as a cyclopentyl group, a cyclohexyl group, or a cyclooctyl group, a norbornyl group, a tricyclodecanyl group, a tetracyclodecanyl group, or a tetracyclododecane group. A polycyclic cycloalkyl group such as a nyl group and an adamantyl group is preferred. Among them, an alicyclic group having a bulky structure having 7 or more carbon atoms, such as a norbornyl group, a tricyclodecanyl group, a tetracyclodecanyl group, a tetracyclododecanyl group, an adamantyl group, or the like is present in the film in the post-exposure heating step. Diffusivity can be suppressed, which is preferable from the viewpoint of improving MEEF.
Examples of the aryl group include a benzene ring, a naphthalene ring, a phenanthrene ring, and an anthracene ring.
Examples of the heterocyclic group include those derived from a furan ring, a thiophene ring, a benzofuran ring, a benzothiophene ring, a dibenzofuran ring, a dibenzothiophene ring, and a pyridine ring. Of these, those derived from a furan ring, a thiophene ring and a pyridine ring are preferred.

  In addition, examples of the cyclic organic group may include a lactone structure, and specific examples include those represented by the general formulas (LC1-1) to (LC1-17) that the resin (A) may have. Can be mentioned.

  The cyclic organic group may have a substituent, and examples of the substituent include an alkyl group (which may be linear, branched or cyclic, preferably 1 to 12 carbon atoms), cyclo Alkyl group (which may be monocyclic, polycyclic or spirocyclic, preferably 3 to 20 carbon atoms), aryl group (preferably 6 to 14 carbon atoms), hydroxy group, alkoxy group, ester group, amide Group, urethane group, ureido group, thioether group, sulfonamide group, sulfonic acid ester group and the like. The carbon constituting the cyclic organic group (carbon contributing to ring formation) may be a carbonyl carbon.

_Examples of the organic group for R ₂₀₁ , R _202, and R ₂₀₃ include an aryl group, an alkyl group, and a cycloalkyl group.
Of R ₂₀₁ , R ₂₀₂ and R ₂₀₃ , at least one is preferably an aryl group, more preferably all three are aryl groups. As the aryl group, in addition to a phenyl group, a naphthyl group, and the like, a heteroaryl group such as an indole residue and a pyrrole residue can be used. Preferred examples of the alkyl group and cycloalkyl group represented by R _{201 to} R ₂₀₃ include a linear or branched alkyl group having 1 to 10 carbon atoms and a cycloalkyl group having 3 to 10 carbon atoms. More preferable examples of the alkyl group include a methyl group, an ethyl group, an n-propyl group, an i-propyl group, and an n-butyl group. More preferable examples of the cycloalkyl group include a cyclopropyl group, a cyclobutyl group, a cyclopentyl group, a cyclohexyl group, and a cycloheptyl group. These groups may further have a substituent. Examples of the substituent include halogen atoms such as nitro groups and fluorine atoms, carboxyl groups, hydroxyl groups, amino groups, cyano groups, alkoxy groups (preferably having 1 to 15 carbon atoms), cycloalkyl groups (preferably having 3 to 15 carbon atoms). ), An aryl group (preferably 6 to 14 carbon atoms), an alkoxycarbonyl group (preferably 2 to 7 carbon atoms), an acyl group (preferably 2 to 12 carbon atoms), an alkoxycarbonyloxy group (preferably 2 to 2 carbon atoms). 7) and the like, but are not limited thereto.

In _the case of forming the two members ring structure of R 201 _{to R 203,} it is preferably a structure represented by the following general formula (A1).

In general formula (A1),
R ^{1a to} R ^13a each independently represents a hydrogen atom or a substituent.
It is preferable that 1-3 are not a hydrogen atom among R ^{< 1a} > -R < ^13a >, and it is more preferable that any one of R ^{< 9a} > -R < ^13a > is not a hydrogen atom.
Za is a single bond or a divalent linking group.
X ⁻ has the same meaning as Z ⁻ in formula (ZI).

Specific examples when R ^{1a to} R ^13a are not a hydrogen atom include a halogen atom, a linear, branched, cyclic alkyl group, alkenyl group, alkynyl group, aryl group, heterocyclic group, cyano group, nitro group, carboxyl group , Alkoxy group, aryloxy group, silyloxy group, heterocyclic oxy group, acyloxy group, carbamoyloxy group, alkoxycarbonyloxy group, aryloxycarbonyloxy group, amino group (including anilino group), ammonio group, acylamino group, amino Carbonylamino group, alkoxycarbonylamino group, aryloxycarbonylamino group, sulfamoylamino group, alkyl and arylsulfonylamino group, mercapto group, alkylthio group, arylthio group, heterocyclic thio group, sulfamoyl group, sulfo group, alkyl And arylsulfinyl groups, alkyl and arylsulfonyl groups, acyl groups, aryloxycarbonyl groups, alkoxycarbonyl groups, carbamoyl groups, aryl and heterocyclic azo groups, imide groups, phosphino groups, phosphinyl groups, phosphinyloxy groups, phosphini Ruamino group, phosphono group, silyl group, hydrazino group, ureido group, boronic acid group (—B (OH) ₂ ), phosphato group (—OPO (OH) ₂ ), sulfato group (—OSO ₃ H), other Known substituents are listed as examples.
As a case where R ^{1a to} R ^13a are not a hydrogen atom, a linear, branched or cyclic alkyl group substituted with a hydroxyl group is preferable.

Examples of the divalent linking group for Za include an alkylene group, an arylene group, a carbonyl group, a sulfonyl group, a carbonyloxy group, a carbonylamino group, a sulfonylamide group, an ether bond, a thioether bond, an amino group, a disulfide group, and — (CH _{2 ) n -CO -, - (CH} 2) n -SO 2 -, - CH = CH-, an aminocarbonylamino group, and an amino sulfonylamino group (n is an integer of 1 to 3).

In addition, as a preferable structure when at least one of R ₂₀₁ , R ₂₀₂ and R ₂₀₃ is not an aryl group, paragraphs 0046 to 0048 of JP-A-2004-233661, paragraphs 0040 to 340 of JP-A-2003-35948 Compounds exemplified as formulas (I-1) to (I-70) in U.S. Patent Application Publication No. 2003 / 0224288A1, and formula (IA-1) in U.S. Patent Application Publication No. 2003 / 0077540A1. ) To (IA-54) and cation structures such as compounds exemplified as formulas (IB-1) to (IB-24).

In general formulas (ZII) and (ZIII),
R ₂₀₄ to R ₂₀₇ each independently represents an aryl group, an alkyl group or a cycloalkyl group.

The aryl group, alkyl group, and cycloalkyl group of R _{204 to} R ₂₀₇ are the same as the aryl group described as the aryl group, alkyl group, and cycloalkyl group of R _{201 to} R ₂₀₃ in the aforementioned compound (ZI).
The aryl group, alkyl group, and cycloalkyl group of R _{204 to} R ₂₀₇ may have a substituent. Even the substituent, an aryl group of R ₂₀₁ to R ₂₀₃ in the above compound (ZI), alkyl groups include those which may have a cycloalkyl group.

Z ⁻ represents a non-nucleophilic anion, and examples thereof include the same as the non-nucleophilic anion of Z ^{− in} formula (ZI).

  Examples of the acid generator further include compounds represented by the following general formulas (ZIV), (ZV), and (ZVI).

In general formulas (ZIV) to (ZVI),
Ar ₃ and Ar ₄ each independently represents an aryl group.
R ₂₀₈ , R ₂₀₉ and R ₂₁₀ each independently represents an alkyl group, a cycloalkyl group or an aryl group.
A represents an alkylene group, an alkenylene group or an arylene group.
Specific examples of the aryl group represented by Ar ₃ , Ar ₄ , R ₂₀₈ , R _209, and R ₂₁₀ are the same as the specific examples of the aryl group represented by R ₂₀₁ , R _202, and R ₂₀₃ in the general formula (ZI). Can be mentioned.
Specific examples of the alkyl group and cycloalkyl group represented by R ₂₀₈ , R ₂₀₉ and R ₂₁₀ include specific examples of the alkyl group and cycloalkyl group represented by R ₂₀₁ , R ₂₀₂ and R ₂₀₃ in the general formula (ZI), respectively. The same can be mentioned.
The alkylene group of A is an alkylene group having 1 to 12 carbon atoms (for example, methylene group, ethylene group, propylene group, isopropylene group, butylene group, isobutylene group, etc.), and the alkenylene group of A is 2 carbon atoms. ˜12 alkenylene groups (for example, ethenylene group, propenylene group, butenylene group, etc.), and as the arylene group of A, C 6-10 arylene groups (for example, phenylene group, tolylene group, naphthylene group, etc.) Each can be mentioned.

  Among acid generators, particularly preferred examples are given below.

In the present invention, the compound (B) that generates the acid has a volume by irradiation with actinic rays or radiation from the viewpoint of suppressing the diffusion of the acid generated by exposure to the non-exposed portion and improving the resolution. preferably 240 Å ³ or more of a size acid compound that generates the, more preferably a compound capable of generating an acid volume of 300 Å ³ or more dimensions, generating an acid volume of 350 Å ³ or more dimensions More preferably, the compound is a compound that generates an acid having a volume of 400 ³ or more. However, from the viewpoint of sensitivity and coating solvent solubility, the volume is preferably 2000 ³ or less, and more preferably 1500 ³ or less. The volume value was determined using “WinMOPAC” manufactured by Fujitsu Limited. That is, first, the chemical structure of the acid according to each example is input, and then the most stable conformation of each acid is determined by molecular force field calculation using the MM3 method with this structure as the initial structure. By performing molecular orbital calculation using the PM3 method for these most stable conformations, the “accessible volume” of each acid can be calculated.
In the present invention, particularly preferred acid generators are exemplified below. In addition, the calculated value of the volume is appended to a part of the example (unit ^{３ 3} ). In addition, the calculated value calculated | required here is a volume value of the acid which the proton couple | bonded with the anion part.

An acid generator can be used individually by 1 type or in combination of 2 or more types.
The content of the acid generator in the composition is preferably 0.1 to 50% by mass, more preferably 0.5 to 40% by mass, and still more preferably 1 to 30% by mass, based on the total solid content of the composition. %.

[3] (C) Resist solvent (coating solvent)
The solvent that can be used in preparing the composition is not particularly limited as long as it dissolves each component. For example, alkylene glycol monoalkyl ether carboxylate (propylene glycol monomethyl ether acetate (PGMEA; also known as 1-methoxy- 2-acetoxypropane)), alkylene glycol monoalkyl ether (propylene glycol monomethyl ether (PGME; 1-methoxy-2-propanol), etc.), lactic acid alkyl ester (ethyl lactate, methyl lactate, etc.), cyclic lactone (γ-butyrolactone) Etc., preferably 4 to 10 carbon atoms, chain or cyclic ketone (2-heptanone, cyclohexanone, etc., preferably 4 to 10 carbon atoms), alkylene carbonate (ethylene carbonate, propylene) Boneto etc.), alkyl acetate such as carboxylic acid alkyl (butyl acetate is preferred), and the like alkoxy alkyl acetates (ethyl ethoxypropionate). Other usable solvents include, for example, the solvents described in US Patent Application Publication No. 2008 / 0248425A1 after [0244].

  Of the above, alkylene glycol monoalkyl ether carboxylate and alkylene glycol monoalkyl ether are preferred.

These solvents may be used alone or in combination of two or more. When mixing 2 or more types, it is preferable to mix the solvent which has a hydroxyl group, and the solvent which does not have a hydroxyl group. The mass ratio of the solvent having a hydroxyl group and the solvent having no hydroxyl group is from 1/99 to 99/1, preferably from 10/90 to 90/10, and more preferably from 20/80 to 60/40.
The solvent having a hydroxyl group is preferably an alkylene glycol monoalkyl ether, and the solvent having no hydroxyl group is preferably an alkylene glycol monoalkyl ether carboxylate.

[4] Basic compound The actinic ray-sensitive or radiation-sensitive resin composition according to the present invention may further contain a basic compound. The basic compound is preferably a compound having a stronger basicity than phenol. Moreover, this basic compound is preferably an organic basic compound, and more preferably a nitrogen-containing basic compound.

  Although the nitrogen-containing basic compound which can be used is not specifically limited, For example, the compound classified into the following (1)-(7) can be used, Especially, (4) ammonium salt mentioned later is preferable.

  (1) Compound represented by general formula (BS-1)

In general formula (BS-1),
Each R independently represents a hydrogen atom or an organic group. However, at least one of the three Rs is an organic group. This organic group is a linear or branched alkyl group, a monocyclic or polycyclic cycloalkyl group, an aryl group, or an aralkyl group.
Examples of the compound represented by the general formula (BS-1) (description of each group, specific examples of the compound represented by the general formula (BS-1), etc.) are described in JP-A-2013-015572. Reference can be made to the description of 0471-0481, the contents of which are incorporated herein.

(2) Compound having nitrogen-containing heterocyclic structure This nitrogen-containing heterocyclic ring may have aromaticity or may not have aromaticity. Moreover, you may have two or more nitrogen atoms. Furthermore, you may contain hetero atoms other than nitrogen. Specifically, for example, compounds having an imidazole structure (2-phenylbenzimidazole, 2,4,5-triphenylimidazole, etc.), compounds having a piperidine structure [N-hydroxyethylpiperidine and bis (1,2,2) , 6,6-pentamethyl-4-piperidyl) sebacate], compounds having a pyridine structure (such as 4-dimethylaminopyridine), and compounds having an antipyrine structure (such as antipyrine and hydroxyantipyrine).
Examples of compounds having a preferred nitrogen-containing heterocyclic structure include, for example, guanidine, aminopyridine, aminoalkylpyridine, aminopyrrolidine, indazole, imidazole, pyrazole, pyrazine, pyrimidine, purine, imidazoline, pyrazoline, piperazine, aminomorpholine and Aminoalkylmorpholine is mentioned. These may further have a substituent.

  Preferred substituents include, for example, amino group, aminoalkyl group, alkylamino group, aminoaryl group, arylamino group, alkyl group, alkoxy group, acyl group, acyloxy group, aryl group, aryloxy group, nitro group, hydroxyl group And a cyano group.

  Particularly preferable basic compounds include, for example, imidazole, 2-methylimidazole, 4-methylimidazole, N-methylimidazole, 2-phenylimidazole, 4,5-diphenylimidazole, 2,4,5-triphenylimidazole, 2 -Aminopyridine, 3-aminopyridine, 4-aminopyridine, 2-dimethylaminopyridine, 4-dimethylaminopyridine, 2-diethylaminopyridine, 2- (aminomethyl) pyridine, 2-amino-3-methylpyridine, 2- Amino-4-methylpyridine, 2-amino5-methylpyridine, 2-amino-6-methylpyridine, 3-aminoethylpyridine, 4-aminoethylpyridine, 3-aminopyrrolidine, piperazine, N- (2-aminoethyl) ) Piperazine, N- (2-aminoethyl) ) Piperidine, 4-amino-2,2,6,6 tetramethylpiperidine, 4-piperidinopiperidine, 2-iminopiperidine, 1- (2-aminoethyl) pyrrolidine, pyrazole, 3-amino-5-methylpyrazole 5-amino-3-methyl-1-p-tolylpyrazole, pyrazine, 2- (aminomethyl) -5 methylpyrazine, pyrimidine, 2,4-diaminopyrimidine, 4,6-dihydroxypyrimidine, 2-pyrazoline, 3 -Pyrazolin, N-aminomorpholine and N- (2-aminoethyl) morpholine.

  A compound having two or more ring structures is also preferably used. Specific examples include 1,5-diazabicyclo [4.3.0] non-5-ene and 1,8-diazabicyclo [5.4.0] -undec-7-ene.

(3) Amine compound having a phenoxy group An amine compound having a phenoxy group is a compound having a phenoxy group at the terminal opposite to the N atom of the alkyl group contained in the amine compound. The phenoxy group is, for example, a substituent such as an alkyl group, an alkoxy group, a halogen atom, a cyano group, a nitro group, a carboxy group, a carboxylic acid ester group, a sulfonic acid ester group, an aryl group, an aralkyl group, an acyloxy group, and an aryloxy group. You may have.

This compound more preferably has at least one oxyalkylene chain between the phenoxy group and the nitrogen atom. The number of oxyalkylene chains in one molecule is preferably 3-9, more preferably 4-6. Among the oxyalkylene chains, —CH ₂ CH ₂ O— is particularly preferable.

  Specific examples include 2- [2- {2- (2,2-dimethoxy-phenoxyethoxy) ethyl} -bis- (2-methoxyethyl)]-amine, and paragraph [0066] of US2007 / 0224539A1. ] Compounds (C1-1) to (C3-3) exemplified in the above.

  The amine compound having a phenoxy group is prepared by reacting, for example, a primary or secondary amine having a phenoxy group with a haloalkyl ether, and adding an aqueous solution of a strong base such as sodium hydroxide, potassium hydroxide or tetraalkylammonium. And then extracted with an organic solvent such as ethyl acetate and chloroform. In addition, the amine compound having a phenoxy group reacts by heating a primary or secondary amine and a haloalkyl ether having a phenoxy group at the terminal, and a strong base such as sodium hydroxide, potassium hydroxide or tetraalkylammonium. It can also be obtained by adding an aqueous solution and then extracting with an organic solvent such as ethyl acetate and chloroform.

(4) Ammonium salt As the basic compound, an ammonium salt can be appropriately used, and a quaternary ammonium salt is preferable.
The cation of the ammonium salt is preferably a tetraalkylammonium cation substituted with an alkyl group having 1 to 18 carbon atoms, such as a tetramethylammonium cation, a tetraethylammonium cation, a tetra (n-propyl) ammonium cation, or a tetra (i-propyl) ammonium. Cations, tetra (n-butyl) ammonium cation, tetra (n-heptyl) ammonium cation, tetra (n-octyl) ammonium cation, dimethylhexadecylammonium cation, benzyltrimethyl cation, etc. are more preferred, and tetra (n-butyl) ammonium Most preferred are cations.
Examples of the anion of the ammonium salt include hydroxide, carboxylate, halide, sulfonate, borate, and phosphate. Of these, hydroxide or carboxylate is particularly preferred.

As the halide, chloride, bromide and iodide are particularly preferable.
As the sulfonate, an organic sulfonate having 1 to 20 carbon atoms is particularly preferable. Examples of the organic sulfonate include alkyl sulfonates having 1 to 20 carbon atoms and aryl sulfonates.

  The alkyl group contained in the alkyl sulfonate may have a substituent. Examples of the substituent include a fluorine atom, a chlorine atom, a bromine atom, an alkoxy group, an acyl group, and an aryl group. Specific examples of the alkyl sulfonate include methane sulfonate, ethane sulfonate, butane sulfonate, hexane sulfonate, octane sulfonate, benzyl sulfonate, trifluoromethane sulfonate, pentafluoroethane sulfonate, and nonafluorobutane sulfonate.

  Examples of the aryl group contained in the aryl sulfonate include a phenyl group, a naphthyl group, and an anthryl group. These aryl groups may have a substituent. As this substituent, a C1-C6 linear or branched alkyl group and a C3-C6 cycloalkyl group are preferable, for example. Specifically, for example, methyl, ethyl, n-propyl, isopropyl, n-butyl, i-butyl, t-butyl, n-hexyl and cyclohexyl groups are preferable. Examples of the other substituent include an alkoxy group having 1 to 6 carbon atoms, a halogen atom, cyano, nitro, an acyl group, and an acyloxy group.

The carboxylate may be an aliphatic carboxylate or an aromatic carboxylate, and examples thereof include acetate, lactate, bilbate, trifluoroacetate, adamantane carboxylate, hydroxyadamantane carboxylate, benzoate, naphthoate, salicylate, phthalate, phenolate, and the like. In particular, benzoate, naphthoate, phenolate and the like are preferable, and benzoate is most preferable.
In this case, as the ammonium salt, tetra (n-butyl) ammonium benzoate,
Tetra (n-butyl) ammonium phenolate and the like are preferable.
In the case of hydroxide, this ammonium salt is a tetraalkylammonium hydroxide having 1 to 8 carbon atoms (tetramethylammonium hydroxide, tetraethylammonium hydroxide, tetra- (n-butyl) ammonium hydroxide, etc.). It is particularly preferred that

(5) A compound having a proton acceptor functional group and generating a compound which is decomposed by irradiation with actinic rays or radiation to decrease or disappear the proton acceptor property or change from proton acceptor property to acidity ( PA)
The composition according to the present invention has a proton acceptor functional group as a basic compound, and is decomposed by irradiation with actinic rays or radiation, resulting in a decrease, disappearance, or a proton acceptor property. It may further contain a compound that generates a compound that has been changed to acidity (hereinafter also referred to as compound (PA)).
As a compound (PA) having a proton acceptor functional group and decomposing upon irradiation with actinic rays or radiation to generate a compound whose proton acceptor property is lowered, disappeared, or changed from proton acceptor property to acidity Can be referred to the descriptions in paragraphs 0379 to 0425 of JP 2012-32762 A (corresponding to [0386] to [0435] of the corresponding US Patent Application Publication No. 2012/0003590), the contents of which are described in the present specification. Incorporated.

  In the composition of the present invention, the compounding ratio of the compound (PA) in the whole composition is preferably 0.1 to 10% by mass, more preferably 1 to 8% by mass in the total solid content.

(6) Guanidine Compound The composition of the present invention may further contain a guanidine compound.
As the guanidine compound, description in paragraphs 0374 to 0378 of JP 2012-32762 A (corresponding to [0382] to [0385] of the corresponding US Patent Application Publication No. 2012/0003590) can be referred to, and the contents thereof are described in this application. Incorporated in the description.
(7) Low molecular weight compound having a nitrogen atom and having a group capable of leaving by the action of an acid The composition of the present invention comprises a low molecular weight compound having a nitrogen atom and having a group capable of leaving by the action of an acid (hereinafter referred to as “low molecular weight compound”). In this case, it is possible to contain “low molecular compound (D)” or “compound (D)”. The low molecular compound (D) preferably has basicity after the group capable of leaving by the action of an acid is eliminated.
As the low molecular weight compound (D), description in paragraphs 0324 to 0337 of JP2012-133331A can be referred to, and the contents thereof are incorporated in the present specification.
In the present invention, the low molecular compound (D) can be used singly or in combination of two or more.

  The composition of the present invention may or may not contain the low molecular compound (D), but when it is contained, the content of the compound (D) is the total solid of the composition combined with the basic compound described above. Based on the minutes, it is usually 0.001 to 20% by mass, preferably 0.001 to 10% by mass, and more preferably 0.01 to 5% by mass.

  When the composition of the present invention contains an acid generator, the ratio of the acid generator and the compound (D) used in the composition is: acid generator / [compound (D) + the following basic compound] (mole Ratio) = 2.5 to 300. In other words, the molar ratio is preferably 2.5 or more from the viewpoint of sensitivity and resolution, and is preferably 300 or less from the viewpoint of suppressing the reduction in resolution due to the thickening of the resist pattern over time until post-exposure heat treatment. The acid generator / [compound (D) + basic compound] (molar ratio) is more preferably 5.0 to 200, and still more preferably 7.0 to 150.

  Other examples that can be used in the composition according to the present invention include compounds synthesized in Examples of JP-A No. 2002-363146, and compounds described in paragraph 0108 of JP-A No. 2007-298869. It is done.

  A photosensitive basic compound may be used as the basic compound. As the photosensitive basic compound, for example, JP-T-2003-524799 and J. Org. Photopolym. Sci & Tech. Vol. 8, P.I. 543-553 (1995) etc. can be used.

  The molecular weight of the basic compound is usually 100-1500, preferably 150-1300, and more preferably 200-1000.

  These basic compounds may be used individually by 1 type, and may be used in combination of 2 or more types.

  When the composition according to the present invention contains a basic compound, the content is preferably 0.01 to 10.0% by mass based on the total solid content of the composition, It is more preferable that it is 8.0 mass%, and it is especially preferable that it is 0.2-5.0 mass%.

  The molar ratio of the basic compound to the photoacid generator is preferably 0.01 to 10, more preferably 0.05 to 5, and still more preferably 0.1 to 3. If this molar ratio is excessively increased, sensitivity and / or resolution may be reduced. If this molar ratio is excessively small, there is a possibility that pattern thinning occurs between exposure and heating (post-bake). More preferably, it is 0.05-5, More preferably, it is 0.1-3. The photoacid generator at the molar ratio is based on the total amount of the repeating unit represented by the general formula (5) of the resin and the photoacid generator that the resin may further contain. Is.

[5] Compound that decomposes by the action of an acid to generate an acid The actinic ray-sensitive or radiation-sensitive resin composition of the present invention further includes one or two compounds that decompose by the action of an acid to generate an acid. More than one species may be included. The acid generated from the compound that decomposes by the action of the acid to generate an acid is preferably a sulfonic acid, a methide acid, or an imido acid.

  Although the example of the compound which decomposes | disassembles by the effect | action of the acid which can be used for this invention and generate | occur | produces an acid is shown below, it is not limited to these.

The compound which decomposes | disassembles by the effect | action of the said acid and generate | occur | produces an acid can be used individually by 1 type or in combination of 2 or more types.
In addition, content of the compound which decomposes | disassembles by the effect | action of an acid and generate | occur | produces an acid is 0.1-40 mass% on the basis of the total solid of the actinic-ray-sensitive or radiation-sensitive resin composition of this invention. It is preferable that it is 0.5-30 mass%, and it is still more preferable that it is 1.0-20 mass%.

[6] Hydrophobic resin (HR)
The actinic ray-sensitive or radiation-sensitive resin composition of the present invention may have a hydrophobic resin (HR) separately from the resin (A).
The hydrophobic resin is preferably designed to be unevenly distributed on the surface of the resist film. However, unlike the surfactant, it is not always necessary to have a hydrophilic group in the molecule, and the polar / nonpolar substance is uniformly mixed. There is no need to contribute.
Examples of the effect of adding the hydrophobic resin include control of the static / dynamic contact angle of the resist film surface with respect to water, suppression of outgas, and the like.

The hydrophobic resin has at least one of “fluorine atom”, “silicon atom”, and “CH ₃ partial structure contained in the side chain portion of the resin” from the viewpoint of uneven distribution on the film surface. It is preferable to have two or more types.
When the hydrophobic resin contains a fluorine atom and / or a silicon atom, the fluorine atom and / or silicon atom in the hydrophobic resin may be contained in the main chain of the resin or in the side chain. It may be.

When the hydrophobic resin contains a fluorine atom, it may be a resin having an alkyl group having a fluorine atom, a cycloalkyl group having a fluorine atom, or an aryl group having a fluorine atom as a partial structure having a fluorine atom. preferable.
The alkyl group having a fluorine atom (preferably having 1 to 10 carbon atoms, more preferably 1 to 4 carbon atoms) is a linear or branched alkyl group in which at least one hydrogen atom is substituted with a fluorine atom, and further a fluorine atom It may have a substituent other than.
The cycloalkyl group having a fluorine atom is a monocyclic or polycyclic cycloalkyl group in which at least one hydrogen atom is substituted with a fluorine atom, and may further have a substituent other than a fluorine atom.
Examples of the aryl group having a fluorine atom include those in which at least one hydrogen atom of an aryl group such as a phenyl group or a naphthyl group is substituted with a fluorine atom, and may further have a substituent other than a fluorine atom. .
Examples of the repeating unit having a fluorine atom or a silicon atom include those exemplified in paragraph 0519 of US2012 / 0251948A1.

Further, as described above, the hydrophobic resin preferably includes a CH ₃ partial structure in the side chain portion.
Here, the CH ₃ partial structure of the side chain portion in the hydrophobic resin (hereinafter also simply referred to as “side chain CH ₃ partial structure”) includes a CH ₃ partial structure of an ethyl group, a propyl group, or the like. Is.
On the other hand, methyl groups directly bonded to the main chain of the hydrophobic resin (for example, α-methyl groups of repeating units having a methacrylic acid structure) contribute to the uneven distribution of the surface of the hydrophobic resin due to the influence of the main chain. Since it is small, it is not included in the CH ₃ partial structure in the present invention.

More specifically, when the hydrophobic resin includes a repeating unit derived from a monomer having a polymerizable moiety having a carbon-carbon double bond, such as a repeating unit represented by the following general formula (M). a _is, if R 11 _{to R 14} is CH ₃ "itself", the CH ₃ is not included in the CH ₃ partial structure contained in the side chain portion in the present invention.
Meanwhile, CH ₃ partial structure exists through some atoms from C-C backbone, and those falling under CH ₃ partial structures in the present invention. For example, when R ₁₁ is an ethyl group (CH ₂ CH ₃ ), it has “one” CH ₃ partial structure in the present invention.

In the general formula (M),
R < ₁₁ > -R < ₁₄ > represents a side chain part each independently.
Examples of R _{11 to} R _{14 in the} side chain portion include a hydrogen atom and a monovalent organic group.
Examples of the monovalent organic group for R _{11 to} R ₁₄ include an alkyl group, a cycloalkyl group, an aryl group, an alkyloxycarbonyl group, a cycloalkyloxycarbonyl group, an aryloxycarbonyl group, an alkylaminocarbonyl group, and a cycloalkylaminocarbonyl. Group, an arylaminocarbonyl group, and the like, and these groups may further have a substituent.

The hydrophobic resin is preferably a resin having a repeating unit having a CH ₃ partial structure in the side chain portion. As such a repeating unit, the repeating unit represented by the following general formula (II) and the following general unit It is more preferable to have at least one repeating unit (x) among the repeating units represented by the formula (III).

  Hereinafter, the repeating unit represented by formula (II) will be described in detail.

In the general formula (II), X _b1 represents a hydrogen atom, an alkyl group, a cyano group or a halogen atom, R ₂ has one or more CH ₃ partial structure represents a stable organic radical to acid. Here, the organic group that is stable to acid is more preferably an organic group that does not have the “acid-decomposable group” described in the resin (A).

The alkyl group of _Xb1 preferably has 1 to 4 carbon atoms, and examples thereof include a methyl group, an ethyl group, a propyl group, a hydroxymethyl group, and a trifluoromethyl group, and a methyl group is preferable.
X _b1 is preferably a hydrogen atom or a methyl group.
Examples of R ₂ include an alkyl group, a cycloalkyl group, an alkenyl group, a cycloalkenyl group, an aryl group, and an aralkyl group having one or more CH ₃ partial structures. The above cycloalkyl group, alkenyl group, cycloalkenyl group, aryl group and aralkyl group may further have an alkyl group as a substituent.
R ₂ is preferably an alkyl group or an alkyl-substituted cycloalkyl group having one or more CH ₃ partial structures.
The acid-stable organic group having one or more CH ₃ partial structures as R ₂ preferably has 2 or more and 10 or less CH ₃ partial structures, and more preferably 2 or more and 8 or less.
Preferred specific examples of the repeating unit represented by the general formula (II) are shown below. Note that the present invention is not limited to this.

The repeating unit represented by the general formula (II) is preferably an acid-stable (non-acid-decomposable) repeating unit, and specifically, a group that decomposes by the action of an acid to generate a polar group. It is preferable that it is a repeating unit which does not have.
Hereinafter, the repeating unit represented by formula (III) will be described in detail.

In the above general formula (III), X _b2 represents a hydrogen atom, an alkyl group, a cyano group, or a halogen atom, R ₃ represents an acid-stable organic group having one or more CH ₃ partial structures, n represents an integer of 1 to 5.
The alkyl group of _Xb2 preferably has 1 to 4 carbon atoms, and examples thereof include a methyl group, an ethyl group, a propyl group, a hydroxymethyl group, and a trifluoromethyl group, and a hydrogen atom is preferable.
X _b2 is preferably a hydrogen atom.
Since R ₃ is an organic group that is stable against acid, more specifically, R ₃ is preferably an organic group that does not have the “acid-decomposable group” described in the resin (A).

R ₃ includes an alkyl group having one or more CH ₃ partial structures.
The acid-stable organic group having one or more CH ₃ partial structures as R ₃ preferably has 1 or more and 10 or less CH ₃ partial structures, more preferably 1 or more and 8 or less, More preferably, it is 1 or more and 4 or less.
n represents an integer of 1 to 5, more preferably an integer of 1 to 3, and still more preferably 1 or 2.

  Preferred specific examples of the repeating unit represented by the general formula (III) are shown below. Note that the present invention is not limited to this.

  The repeating unit represented by the general formula (III) is preferably an acid-stable (non-acid-decomposable) repeating unit, and specifically, a group that decomposes by the action of an acid to generate a polar group. It is preferable that it is a repeating unit which does not have.

In the case where the hydrophobic resin contains a CH ₃ partial structure in the side chain portion, and particularly when it does not have a fluorine atom and a silicon atom, the repeating unit represented by the general formula (II) and the general formula ( The content of at least one repeating unit (x) among the repeating units represented by III) is preferably 90 mol% or more, more preferably 95 mol% or more, based on all repeating units of the hydrophobic resin. It is more preferable. Content is 100 mol% or less normally with respect to all the repeating units of hydrophobic resin.

  The hydrophobic resin contains at least one repeating unit (x) among the repeating units represented by the general formula (II) and the repeating unit represented by the general formula (III) as all repeating units of the hydrophobic resin. On the other hand, the surface free energy of hydrophobic resin increases by containing 90 mol% or more. As a result, the hydrophobic resin tends to be unevenly distributed on the surface of the resist film.

In addition, the hydrophobic resin includes the following groups (x) to (z) both when (i) a fluorine atom and / or a silicon atom are included, and (ii) when a side chain portion includes a CH ₃ partial structure. It may have at least one group selected from
(X) an acid group,
(Y) a group having a lactone structure, an acid anhydride group, or an acid imide group,
(Z) a group decomposable by the action of an acid

Examples of the acid group (x) include a phenolic hydroxyl group, a carboxylic acid group, a fluorinated alcohol group, a sulfonic acid group, a sulfonamide group, a sulfonylimide group, an (alkylsulfonyl) (alkylcarbonyl) methylene group, and an (alkylsulfonyl) (alkyl Carbonyl) imide group, bis (alkylcarbonyl) methylene group, bis (alkylcarbonyl) imide group, bis (alkylsulfonyl) methylene group, bis (alkylsulfonyl) imide group, tris (alkylcarbonyl) methylene group, tris (alkylsulfonyl) A methylene group etc. are mentioned.
Preferred acid groups include fluorinated alcohol groups (preferably hexafluoroisopropanol), sulfonimide groups, and bis (alkylcarbonyl) methylene groups.

The repeating unit having an acid group (x) includes a repeating unit in which an acid group is directly bonded to the main chain of the resin, such as a repeating unit of acrylic acid or methacrylic acid, or a resin having a linking group. Examples include a repeating unit in which an acid group is bonded to the main chain, and a polymerization initiator or chain transfer agent having an acid group can be introduced at the end of the polymer chain at the time of polymerization. preferable. The repeating unit having an acid group (x) may have at least one of a fluorine atom and a silicon atom.
The content of the repeating unit having an acid group (x) is preferably from 1 to 50 mol%, more preferably from 3 to 35 mol%, still more preferably from 5 to 20 mol%, based on all repeating units in the hydrophobic resin. It is.
Specific examples of the repeating unit having an acid group (x) are shown below, but the present invention is not limited thereto. In the formula, Rx represents a hydrogen atom, CH ₃ , CF ₃ , or CH ₂ OH.

As the group having a lactone structure, the acid anhydride group, or the acid imide group (y), a group having a lactone structure is particularly preferable.
The repeating unit containing these groups is a repeating unit in which this group is directly bonded to the main chain of the resin, such as a repeating unit of acrylic acid ester and methacrylic acid ester. Alternatively, this repeating unit may be a repeating unit in which this group is bonded to the main chain of the resin via a linking group. Or this repeating unit may be introduce | transduced into the terminal of resin using the polymerization initiator or chain transfer agent which has this group at the time of superposition | polymerization.
Examples of the repeating unit having a group having a lactone structure include those similar to the repeating unit having a lactone structure described above in the section of the resin (A).

  The content of the repeating unit having a group having a lactone structure, an acid anhydride group, or an acid imide group is preferably 1 to 100 mol% based on all repeating units in the hydrophobic resin, and preferably 3 to 98. It is more preferable that it is mol%, and it is still more preferable that it is 5-95 mol%.

  Examples of the repeating unit having a group (z) that is decomposed by the action of an acid in the hydrophobic resin include the same repeating units having an acid-decomposable group as mentioned for the resin (A). The repeating unit having a group (z) that decomposes by the action of an acid may have at least one of a fluorine atom and a silicon atom. In the hydrophobic resin, the content of the repeating unit having a group (z) that decomposes by the action of an acid is preferably 1 to 80 mol%, more preferably 10 to 10%, based on all repeating units in the hydrophobic resin. It is 80 mol%, More preferably, it is 20-60 mol%.

When the hydrophobic resin has a fluorine atom, the content of the fluorine atom is preferably 5 to 80% by mass and more preferably 10 to 80% by mass with respect to the weight average molecular weight of the hydrophobic resin. Moreover, it is preferable that the repeating unit containing a fluorine atom is 10-100 mol% in all the repeating units contained in hydrophobic resin, and it is more preferable that it is 30-100 mol%.
When the hydrophobic resin has a silicon atom, the content of the silicon atom is preferably 2 to 50% by mass and more preferably 2 to 30% by mass with respect to the weight average molecular weight of the hydrophobic resin. Moreover, it is preferable that it is 10-100 mol% in the repeating unit containing a silicon atom in all the repeating units contained in hydrophobic resin, and it is more preferable that it is 20-100 mol%.

On the other hand, in the case where the hydrophobic resin contains a CH ₃ partial structure in the side chain portion, it is also preferred that the hydrophobic resin does not substantially contain a fluorine atom and a silicon atom. The content of the repeating unit having an atom or silicon atom is preferably 5 mol% or less, more preferably 3 mol% or less, more preferably 1 mol% or less, based on all repeating units in the hydrophobic resin. More preferably, it is ideally 0 mol%, ie it does not contain fluorine and silicon atoms. Moreover, it is preferable that hydrophobic resin is substantially comprised only by the repeating unit comprised only by the atom chosen from a carbon atom, an oxygen atom, a hydrogen atom, a nitrogen atom, and a sulfur atom. More specifically, it is preferable that the repeating unit composed only of atoms selected from a carbon atom, an oxygen atom, a hydrogen atom, a nitrogen atom and a sulfur atom is 95 mol% or more in the total repeating units of the hydrophobic resin. 97 mol% or more is more preferable, 99 mol% or more is further preferable, and ideally 100 mol%.

The weight average molecular weight in terms of standard polystyrene of the hydrophobic resin is preferably 1,000 to 100,000, more preferably 1,000 to 50,000, and still more preferably 2,000 to 15,000.
Moreover, the hydrophobic resin may be used alone or in combination.
The content of the hydrophobic resin in the composition is preferably 0.01 to 10% by mass, more preferably 0.05 to 8% by mass with respect to the total solid content in the composition of the present invention. 7 mass% is still more preferable.

  It is natural that the hydrophobic resin has few impurities such as metals, and the residual monomer or oligomer component is preferably 0.01 to 5% by mass, more preferably 0.01 to 3% by mass, 0.05-1 mass% is still more preferable. Thereby, a composition having no change over time such as foreign matter in liquid or sensitivity can be obtained. The molecular weight distribution (Mw / Mn, also referred to as dispersity) is preferably in the range of 1 to 5, more preferably 1 to 3, and still more preferably from the viewpoints of resolution, resist shape, resist pattern sidewall, roughness, and the like. It is the range of 1-2.

As the hydrophobic resin, various commercially available products can be used, and can be synthesized according to a conventional method (for example, radical polymerization). For example, as a general synthesis method, a monomer polymerization method in which a monomer species and an initiator are dissolved in a solvent and heating is performed, and a solution of the monomer species and the initiator is dropped into the heating solvent over 1 to 10 hours. The dropping polymerization method is added, and the dropping polymerization method is preferable.
The reaction solvent, the polymerization initiator, the reaction conditions (temperature, concentration, etc.) and the purification method after the reaction are the same as described in the resin (A), but in the synthesis of the hydrophobic resin, the reaction concentration Is preferably 30 to 50% by mass.

  In addition, as the hydrophobic resin, those described in JP 2011-248019 A, JP 2010-175859 A, and JP 2012-032544 A can also be preferably used.

[7] Surfactant The composition of the present invention may further contain a surfactant. By containing a surfactant, when an exposure light source having a wavelength of 250 nm or less, particularly 220 nm or less, is used, it is possible to form a pattern with less adhesion and development defects with good sensitivity and resolution. Become.
As the surfactant, it is particularly preferable to use a fluorine-based and / or silicon-based surfactant.

  Examples of the fluorine-based and / or silicon-based surfactant include surfactants described in [0276] of US Patent Application Publication No. 2008/0248425. Also, F-top EF301 or EF303 (manufactured by Shin-Akita Kasei Co., Ltd.); Florard FC430, 431 or 4430 (manufactured by Sumitomo 3M Co., Ltd.); Megafac F171, F173, F176, F189, F113, F110, F177, F120 or R08 (manufactured by DIC Corporation); Surflon S-382, SC101, 102, 103, 104, 105 or 106 (manufactured by Asahi Glass Co., Ltd.); Troisol S-366 (manufactured by Troy Chemical Co., Ltd.); GF-300 or GF-150 (manufactured by Toa Gosei Chemical Co., Ltd.), Surflon S-393 (manufactured by Seimi Chemical Co., Ltd.); EFtop EF121, EF122A, EF122B, RF122C, EF125M, EF135M, EF351, EF352, EF801, EF802 or EF601 ( ( PF636, PF656, PF6320 or PF6520 (OMNOVA); or FTX-204G, 208G, 218G, 230G, 204D, 208D, 212D, 218D or 222D (manufactured by Neos) Good. Polysiloxane polymer KP-341 (manufactured by Shin-Etsu Chemical Co., Ltd.) can also be used as a silicon-based surfactant.

  In addition to known surfactants as described above, the surfactant is a fluoroaliphatic compound produced by a telomerization method (also referred to as a telomer method) or an oligomerization method (also referred to as an oligomer method). You may synthesize. Specifically, a polymer having a fluoroaliphatic group derived from this fluoroaliphatic compound may be used as a surfactant. This fluoroaliphatic compound can be synthesized, for example, by the method described in JP-A-2002-90991.

The polymer having a fluoroaliphatic group is preferably a copolymer of a monomer having a fluoroaliphatic group and (poly (oxyalkylene)) acrylate or methacrylate and / or (poly (oxyalkylene)) methacrylate. Even if it distributes, block copolymerization may be sufficient.
Examples of the poly (oxyalkylene) group include a poly (oxyethylene) group, a poly (oxypropylene) group, and a poly (oxybutylene) group. In addition, units having different chain length alkylene in the same chain, such as poly (block connection body of oxyethylene, oxypropylene, and oxyethylene) and poly (block connection body of oxyethylene and oxypropylene) Also good.

Furthermore, a copolymer of a monomer having a fluoroaliphatic group and (poly (oxyalkylene)) acrylate or methacrylate is composed of a monomer having two or more different fluoroaliphatic groups and two or more different (poly (oxyalkylene). )) It may be a ternary or higher copolymer obtained by copolymerizing acrylate or methacrylate simultaneously.
Examples of commercially available surfactants include Megafac F178, F-470, F-473, F-475, F-476, and F-472 (manufactured by DIC Corporation). Further, a copolymer of an acrylate or methacrylate having a C ₆ F ₁₃ group and (poly (oxyalkylene)) acrylate or methacrylate, an acrylate or methacrylate having a C ₆ F ₁₃ group and (poly (oxyethylene)) acrylate or methacrylate And a copolymer of (poly (oxypropylene)) acrylate or methacrylate, a copolymer of an acrylate or methacrylate having a C ₈ F ₁₇ group and (poly (oxyalkylene)) acrylate or methacrylate, and C ₈ F ₁₇ Copolymerization of a group-containing acrylate or methacrylate with (poly (oxyethylene)) acrylate or methacrylate and (poly (oxypropylene)) acrylate or methacrylate Body, and the like.

Further, surfactants other than fluorine-based and / or silicon-based surfactants described in [0280] of US Patent Application Publication No. 2008/0248425 may be used.
One of these surfactants may be used alone, or two or more thereof may be used in combination.
When the composition of the present invention contains a surfactant, the content thereof is preferably 0 to 2% by mass, more preferably 0.0001 to 2% by mass, further based on the total solid content of the composition. Preferably it is 0.0005-1 mass%.

[8] Other additives In addition to the components described above, the composition of the present invention has a molecular weight of 3000 or less as described in carboxylic acid, carboxylic acid onium salt, Proceeding of SPIE, 2724, 355 (1996), etc. A blocking compound, a dye, a plasticizer, a photosensitizer, a light absorber, an antioxidant, and the like can be appropriately contained.
In particular, carboxylic acid is preferably used for improving the performance. As the carboxylic acid, aromatic carboxylic acids such as benzoic acid and naphthoic acid are preferable.
The content of the carboxylic acid is preferably 0.01 to 10% by mass, more preferably 0.01 to 5% by mass, and still more preferably 0.01 to 3% by mass in the total solid content concentration of the composition.

The actinic ray-sensitive or radiation-sensitive resin composition of the present invention is preferably used at a film thickness of 10 to 250 nm, more preferably at a film thickness of 20 to 200 nm, from the viewpoint of improving resolution. More preferably, it is preferably used at 30 to 100 nm. Such a film thickness can be obtained by setting the solid content concentration in the composition to an appropriate range to give an appropriate viscosity and improving the coating property and film forming property.
The solid content concentration of the actinic ray-sensitive or radiation-sensitive resin composition of the present invention is usually 1.0 to 10% by mass, preferably 2.0 to 5.7% by mass, and more preferably 2.0. It is -5.3 mass%. By setting the solid content concentration within the above range, it is possible to uniformly apply the resist solution on the substrate, and it is possible to form a resist pattern having excellent line width roughness. The reason for this is not clear, but perhaps the solid content concentration is 10% by mass or less, preferably 5.7% by mass or less, which suppresses aggregation of the material in the resist solution, particularly the photoacid generator. As a result, it is considered that a uniform resist film was formed.
The solid content concentration is a weight percentage of the weight of other resist components excluding the solvent with respect to the total weight of the actinic ray-sensitive or radiation-sensitive resin composition.

  In the actinic ray-sensitive or radiation-sensitive resin composition of the present invention, the above components are dissolved in a predetermined organic solvent, preferably the mixed solvent, filtered, and then applied onto a predetermined support (substrate). Use. The pore size of the filter used for filter filtration is preferably 0.1 μm or less, more preferably 0.05 μm or less, and still more preferably 0.03 μm or less made of polytetrafluoroethylene, polyethylene, or nylon. In filter filtration, for example, as in JP-A-2002-62667, circulation filtration may be performed, or filtration may be performed by connecting a plurality of types of filters in series or in parallel. The composition may be filtered multiple times. Furthermore, you may perform a deaeration process etc. with respect to a composition before and behind filter filtration.

[9] Pattern Forming Method The present invention relates to an actinic ray-sensitive or radiation-sensitive film (hereinafter also referred to as a resist film) formed using the above-described composition of the present invention.
Moreover, the pattern forming method of the present invention includes:
(A) a step of forming a film (resist film) with an actinic ray-sensitive or radiation-sensitive resin composition;
It is preferable to have at least a step of (a) exposing the film, and (c) developing the exposed film using a developer to form a pattern.
The developer in the step (c) may be a developer containing an organic solvent or an alkali developer.
Specifically, the pattern forming method of the present invention includes:
(A) a step of forming a film (resist film) with an actinic ray-sensitive or radiation-sensitive resin composition;
(A) a step of exposing the film; and (c) a step of developing the exposed film using a developer containing an organic solvent to form a negative pattern.
Further, the exposure in the step (ii) may be immersion exposure.
The pattern forming method of the present invention preferably comprises (i) a heating step after (b) the exposure step.
The pattern forming method of the present invention may further include (e) a step of developing using an alkali developer when the developer in the step (c) is a developer containing an organic solvent. On the other hand, when the developer in the step (c) is an alkali developer, (e) it may further include a step of developing using a developer containing an organic solvent.
In the present invention, a portion with low exposure intensity is removed by the organic solvent development step, but a portion with high exposure strength is also removed by further performing the alkali development step. In this way, by the multiple development process in which development is performed a plurality of times, a pattern can be formed without dissolving only the intermediate exposure intensity region, so that a finer pattern than usual can be formed (Japanese Patent Laid-Open No. 2008-292975 [0077]. ] And the same mechanism).
In the pattern forming method of the present invention, the order of the alkali development step and the organic solvent development step is not particularly limited, but it is more preferable to perform the alkali development before the organic solvent development step.
The pattern formation method of this invention can have (b) exposure process in multiple times.
The pattern formation method of this invention can have (e) a heating process in multiple times.

  The resist film is formed from the actinic ray-sensitive or radiation-sensitive resin composition of the present invention described above, and more specifically, is preferably formed on a substrate. In the pattern forming method of the present invention, a step of forming a film of an actinic ray-sensitive or radiation-sensitive resin composition on a substrate, a step of exposing the film, and a developing step are generally known methods. Can be performed.

  This composition can be applied to, for example, a spinner and a substrate on a substrate (eg, silicon / silicon dioxide coating, silicon nitride and chromium-deposited quartz substrate) used for manufacturing precision integrated circuit elements and imprint molds. It is applied using a coater or the like. Thereafter, it can be dried to form an actinic ray-sensitive or radiation-sensitive film.

Before forming the resist film, an antireflection film may be coated on the substrate in advance.
As the antireflection film, any of an inorganic film type such as titanium, titanium dioxide, titanium nitride, chromium oxide, carbon, and amorphous silicon, and an organic film type made of a light absorber and a polymer material can be used. In addition, as the organic antireflection film, commercially available organic antireflection films such as DUV30 series, DUV-40 series manufactured by Brewer Science, AR-2, AR-3, AR-5 manufactured by Shipley, etc. may be used. it can.

It is also preferable to include a preheating step (PB; Prebake) after the film formation and before the exposure step. It is also preferable to include a post-exposure heating step (PEB; Post Exposure Bake) after the exposure step and before the development step.
The heating temperature is preferably 70 to 120 ° C., more preferably 80 to 110 ° C. for both PB and PEB.
The heating time is preferably 30 to 300 seconds, more preferably 30 to 180 seconds, and still more preferably 30 to 90 seconds.
Heating can be performed by means provided in a normal exposure / developing machine, and may be performed using a hot plate or the like.
The reaction of the exposed part is promoted by baking, and the sensitivity and pattern profile are improved.
It is also preferable to include a heating step (Post Bake) after the rinsing step. The developing solution and the rinsing solution remaining between the patterns and inside the patterns are removed by baking.

Examples of actinic rays or radiation include infrared light, visible light, ultraviolet light, far ultraviolet light, X-rays, and electron beams. As these actinic rays or radiation, for example, those having a wavelength of 250 nm or less, particularly 220 nm or less are more preferable. Examples of such actinic rays or radiation include KrF excimer laser (248 nm), ArF excimer laser (193 nm), F ₂ excimer laser (157 nm), X-rays, and electron beams. Examples of preferable actinic rays or radiation include KrF excimer laser, ArF excimer laser, electron beam, X-ray and EUV light. More preferred are electron beam, X-ray and EUV light.

In the present invention, the substrate on which the film is formed is not particularly limited, and silicon, SiN, inorganic substrates such as SiO ₂ and SiN, coated inorganic substrates such as SOG, semiconductor manufacturing processes such as IC, liquid crystal, and thermal head For example, a substrate generally used in a circuit board manufacturing process or other photofabrication lithography process can be used. Further, if necessary, an organic antireflection film may be formed between the film and the substrate.

When the pattern forming method of the present invention includes a step of developing using an alkali developer, examples of the alkali developer include sodium hydroxide, potassium hydroxide, sodium carbonate, sodium silicate, sodium metasilicate, and aqueous ammonia. Inorganic amines such as ethylamine, primary amines such as n-propylamine, secondary amines such as diethylamine and di-n-butylamine, tertiary amines such as triethylamine and methyldiethylamine, dimethylethanolamine, and triethanol Alcohol amines such as amine, tetramethylammonium hydroxide, tetraethylammonium hydroxide, tetrapropylammonium hydroxide, tetrabutylammonium hydroxide, tetrapentylammonium hydroxide, tetrahexyl Tetraalkylammonium hydroxide such as ammonium hydroxide, tetraoctylammonium hydroxide, ethyltrimethylammonium hydroxide, butyltrimethylammonium hydroxide, methyltriamylammonium hydroxide, dibutyldipentylammonium hydroxide, trimethylphenylammonium hydroxide, trimethylbenzyl Alkaline aqueous solutions such as quaternary ammonium salts such as ammonium hydroxide and triethylbenzylammonium hydroxide, and cyclic amines such as pyrrole and pihelidine can be used.
Furthermore, an appropriate amount of alcohol or surfactant may be added to the alkaline aqueous solution.
The alkali concentration of the alkali developer is usually from 0.1 to 20% by mass.
The pH of the alkali developer is usually from 10.0 to 15.0.
In particular, an aqueous solution of 2.38% by mass of tetramethylammonium hydroxide is desirable.

As a rinsing solution in the rinsing treatment performed after alkali development, pure water can be used and an appropriate amount of a surfactant can be added.
In addition, after the developing process or the rinsing process, a process of removing the developing solution or the rinsing liquid adhering to the pattern with a supercritical fluid can be performed.

When the pattern forming method of the present invention includes a step of developing using a developer containing an organic solvent, the developer in the step (hereinafter also referred to as an organic developer) includes a ketone solvent and an ester solvent. Polar solvents such as solvents, alcohol solvents, amide solvents, ether solvents, and hydrocarbon solvents can be used.
Examples of the ketone solvent include 1-octanone, 2-octanone, 1-nonanone, 2-nonanone, acetone, 2-heptanone (methyl amyl ketone), 4-heptanone, 1-hexanone, 2-hexanone, diisobutyl ketone, Examples include cyclohexanone, methylcyclohexanone, phenylacetone, methylethylketone, methylisobutylketone, acetylacetone, acetonylacetone, ionone, diacetylalcohol, acetylcarbinol, acetophenone, methylnaphthylketone, isophorone, and propylene carbonate.
Examples of ester solvents include methyl acetate, butyl acetate, ethyl acetate, isopropyl acetate, pentyl acetate, isopentyl acetate, amyl acetate, propylene glycol monomethyl ether acetate, ethylene glycol monoethyl ether acetate, diethylene glycol monobutyl ether acetate, diethylene glycol monoethyl. Ether acetate, ethyl-3-ethoxypropionate, 3-methoxybutyl acetate, 3-methyl-3-methoxybutyl acetate, methyl formate, ethyl formate, butyl formate, propyl formate, ethyl lactate, butyl lactate, propyl lactate, etc. Can be mentioned.
Examples of the alcohol solvent include methyl alcohol, ethyl alcohol, n-propyl alcohol, isopropyl alcohol, n-butyl alcohol, sec-butyl alcohol, 4-methyl-2-pentanol, tert-butyl alcohol, isobutyl alcohol, n -Alcohols such as hexyl alcohol, n-heptyl alcohol, n-octyl alcohol, n-decanol, glycol solvents such as ethylene glycol, diethylene glycol, triethylene glycol, ethylene glycol monomethyl ether, propylene glycol monomethyl ether, ethylene glycol mono Ethyl ether, propylene glycol monoethyl ether, diethylene glycol monomethyl ether, triethylene glycol monoethyl Ether, may be mentioned glycol monoethyl ether and methoxymethyl butanol.
Examples of the ether solvent include anisole, dioxane, tetrahydrofuran and the like in addition to the glycol ether solvent.
Examples of the amide solvent include N-methyl-2-pyrrolidone, N, N-dimethylacetamide, N, N-dimethylformamide, hexamethylphosphoric triamide, 1,3-dimethyl-2-imidazolidinone and the like. Can be used.
Examples of the hydrocarbon solvent include aromatic hydrocarbon solvents such as toluene and xylene, and aliphatic hydrocarbon solvents such as pentane, hexane, octane and decane.
A plurality of the above solvents may be mixed, or may be used by mixing with a solvent other than those described above or water. However, in order to fully exhibit the effects of the present invention, the water content of the developer as a whole is preferably less than 10% by mass, and more preferably substantially free of moisture.
That is, the amount of the organic solvent used in the organic developer is preferably 90% by mass or more and 100% by mass or less, and more preferably 95% by mass or more and 100% by mass or less, with respect to the total amount of the developer.
In particular, the organic developer is preferably a developer containing at least one organic solvent selected from the group consisting of ketone solvents, ester solvents, alcohol solvents, amide solvents and ether solvents. .

The vapor pressure of the organic developer is preferably 5 kPa or less, more preferably 3 kPa or less, and particularly preferably 2 kPa or less at 20 ° C. By setting the vapor pressure of the organic developer to 5 kPa or less, evaporation of the developer on the substrate or in the developing cup is suppressed, and the temperature uniformity in the wafer surface is improved. As a result, the dimensions in the wafer surface are uniform. Sexuality improves.
Specific examples having a vapor pressure of 5 kPa or less include 1-octanone, 2-octanone, 1-nonanone, 2-nonanone, 2-heptanone (methyl amyl ketone), 4-heptanone, 2-hexanone, diisobutyl ketone, Ketone solvents such as cyclohexanone, methylcyclohexanone, phenylacetone, methyl isobutyl ketone, butyl acetate, pentyl acetate, isopentyl acetate, amyl acetate, propylene glycol monomethyl ether acetate, ethylene glycol monoethyl ether acetate, diethylene glycol monobutyl ether acetate, diethylene glycol monoethyl Ether acetate, ethyl-3-ethoxypropionate, 3-methoxybutyl acetate, 3-methyl-3-methoxybutyl acetate, formate , Ester solvents such as propyl formate, ethyl lactate, butyl lactate, propyl lactate, n-propyl alcohol, isopropyl alcohol, n-butyl alcohol, sec-butyl alcohol, tert-butyl alcohol, isobutyl alcohol, n-hexyl alcohol, alcohol solvents such as n-heptyl alcohol, n-octyl alcohol and n-decanol, glycol solvents such as ethylene glycol, diethylene glycol and triethylene glycol, ethylene glycol monomethyl ether, propylene glycol monomethyl ether, ethylene glycol monoethyl ether, Propylene glycol monoethyl ether, diethylene glycol monomethyl ether, triethylene glycol monoethyl ether, methoxyme Glycol ether solvents such as rubutanol, ether solvents such as tetrahydrofuran, amide solvents such as N-methyl-2-pyrrolidone, N, N-dimethylacetamide, N, N-dimethylformamide, aromatic carbonization such as toluene and xylene Examples thereof include aliphatic hydrocarbon solvents such as hydrogen solvents, octane, and decane.
Specific examples having a vapor pressure of 2 kPa or less, which is a particularly preferable range, include 1-octanone, 2-octanone, 1-nonanone, 2-nonanone, 2-heptanone, 4-heptanone, 2-hexanone, diisobutyl ketone, Ketone solvents such as cyclohexanone, methylcyclohexanone, phenylacetone, butyl acetate, amyl acetate, propylene glycol monomethyl ether acetate, ethylene glycol monoethyl ether acetate, diethylene glycol monobutyl ether acetate, diethylene glycol monoethyl ether acetate, ethyl-3-ethoxypropio , Ester solvents such as 3-methoxybutyl acetate, 3-methyl-3-methoxybutyl acetate, ethyl lactate, butyl lactate, propyl lactate, Alcohol solvents such as alcohol, sec-butyl alcohol, tert-butyl alcohol, isobutyl alcohol, n-hexyl alcohol, n-heptyl alcohol, n-octyl alcohol, n-decanol, ethylene glycol, diethylene glycol, triethylene glycol, etc. Glycol solvents, ethylene glycol monomethyl ether, propylene glycol monomethyl ether, ethylene glycol monoethyl ether, propylene glycol monoethyl ether, diethylene glycol monomethyl ether, triethylene glycol monoethyl ether, glycol ether solvents such as methoxymethyl butanol, N- Methyl-2-pyrrolidone, N, N-dimethylacetamide, N, N-dimethylformamide Amide solvents, aromatic hydrocarbon solvents such as xylene, octane, aliphatic hydrocarbon solvents decane.

  The organic developer may contain a basic compound. Specific examples and preferred examples of the basic compound that can be contained in the developer used in the present invention are the same as those in the basic compound that can be contained in the actinic ray-sensitive or radiation-sensitive resin composition described above.

An appropriate amount of a surfactant can be added to the organic developer as required.
The surfactant is not particularly limited, and for example, ionic or nonionic fluorine-based and / or silicon-based surfactants can be used. Examples of these fluorine and / or silicon surfactants include, for example, JP-A No. 62-36663, JP-A No. 61-226746, JP-A No. 61-226745, JP-A No. 62-170950, JP 63-34540 A, JP 7-230165 A, JP 8-62834 A, JP 9-54432 A, JP 9-5988 A, US Pat. No. 5,405,720, etc. The surfactants described in US Pat. Nos. 5,360,692, 5,298,881, 5,296,330, 5,346,098, 5,576,143, 5,294,511, and 5,824,451 can be mentioned. Preferably, it is a nonionic surfactant. Although it does not specifically limit as a nonionic surfactant, It is still more preferable to use a fluorochemical surfactant or a silicon-type surfactant.
The amount of the surfactant used is preferably 0 to 2% by mass, more preferably 0.0001 to 2% by mass, and particularly preferably 0.0005 to 1% by mass with respect to the total amount of the developer.

As a developing method, for example, a method in which a substrate is immersed in a tank filled with a developer for a certain period of time (dip method), a method in which the developer is raised on the surface of the substrate by surface tension and is left stationary for a certain time (paddle) Method), a method of spraying the developer on the substrate surface (spray method), a method of continuously discharging the developer while scanning the developer discharge nozzle on the substrate rotating at a constant speed (dynamic dispensing method) Etc. can be applied.
When the various development methods described above include a step of discharging the developer from the developing nozzle of the developing device toward the resist film, the discharge pressure of the discharged developer (the flow rate per unit area of the discharged developer) is Preferably it is 2 mL / sec / mm ² or less, More preferably, it is 1.5 mL / sec / mm ² or less, More preferably, it is 1 mL / sec / mm ² or less. There is no particular lower limit on the flow rate, but 0.2 mL / sec / mm ² or more is preferable in consideration of throughput.
By setting the discharge pressure of the discharged developer to be in the above range, pattern defects derived from the resist residue after development can be remarkably reduced.
The details of this mechanism are not clear, but perhaps by setting the discharge pressure within the above range, the pressure applied by the developer to the resist film will decrease, and the resist film / resist pattern may be inadvertently cut or collapsed. This is considered to be suppressed.
The developer discharge pressure (mL / sec / mm ² ) is a value at the developing nozzle outlet in the developing device.

  Examples of the method for adjusting the discharge pressure of the developer include a method of adjusting the discharge pressure with a pump or the like, and a method of changing the pressure by adjusting the pressure by supply from a pressurized tank.

  Moreover, you may implement the process of stopping image development, after substituting with another solvent after the process developed using the developing solution containing an organic solvent.

  After the step of developing with a developer containing an organic solvent, a step of washing with a rinse solution may be included. From the viewpoint of throughput (productivity), the amount of rinse solution used, etc. It is not necessary to include the step of using and washing.

The rinsing solution used in the rinsing step after the step of developing with a developer containing an organic solvent is not particularly limited as long as the resist pattern is not dissolved, and a solution containing a general organic solvent can be used. . The rinsing liquid contains at least one organic solvent selected from the group consisting of hydrocarbon solvents (preferably decane), ketone solvents, ester solvents, alcohol solvents, amide solvents and ether solvents. It is preferable to use a rinse solution.
Specific examples of the hydrocarbon solvent, the ketone solvent, the ester solvent, the alcohol solvent, the amide solvent, and the ether solvent are the same as those described in the developer containing an organic solvent.
More preferably, it contains at least one organic solvent selected from the group consisting of ketone solvents, ester solvents, alcohol solvents, and amide solvents after the step of developing using a developer containing an organic solvent. A step of washing with a rinsing liquid is performed, more preferably, a step of washing with a rinsing liquid containing an alcohol solvent or an ester solvent is carried out, and particularly preferably, a rinsing liquid containing a monohydric alcohol is used. And, most preferably, the step of cleaning with a rinse solution containing a monohydric alcohol having 5 or more carbon atoms is performed.
Here, examples of the monohydric alcohol used in the rinsing step include linear, branched, and cyclic monohydric alcohols, and specifically, 1-butanol, 2-butanol, and 3-methyl-1-butanol. Tert-butyl alcohol, 1-pentanol, 2-pentanol, 1-hexanol, 4-methyl-2-pentanol, 1-heptanol, 1-octanol, 2-hexanol, cyclopentanol, 2-heptanol, 2 -Octanol, 3-hexanol, 3-heptanol, 3-octanol, 4-octanol and the like can be used, and particularly preferable monohydric alcohols having 5 or more carbon atoms include 1-hexanol, 2-hexanol, 4-methyl- Use 2-pentanol, 1-pentanol, 3-methyl-1-butanol, etc. It can be.

  A plurality of these components may be mixed, or may be used by mixing with an organic solvent other than the above.

  The water content in the rinse liquid is preferably 10% by mass or less, more preferably 5% by mass or less, and particularly preferably 3% by mass or less. By setting the water content to 10% by mass or less, good development characteristics can be obtained.

  The vapor pressure of the rinsing solution used after the step of developing with a developer containing an organic solvent is preferably 0.05 kPa or more and 5 kPa or less, more preferably 0.1 kPa or more and 5 kPa or less at 20 ° C. 12 kPa or more and 3 kPa or less are the most preferable. By setting the vapor pressure of the rinse liquid to 0.05 kPa or more and 5 kPa or less, the temperature uniformity in the wafer surface is improved, and further, the swelling due to the penetration of the rinse solution is suppressed, and the dimensional uniformity in the wafer surface. Improves.

  An appropriate amount of a surfactant can be added to the rinse solution.

  In the rinsing step, the wafer that has been developed using the developer containing the organic solvent is washed using the rinse solution containing the organic solvent. The cleaning method is not particularly limited. For example, a method of continuing to discharge the rinse liquid onto the substrate rotating at a constant speed (rotary coating method), or immersing the substrate in a tank filled with the rinse liquid for a certain period of time. A method (dip method), a method of spraying a rinsing liquid on the substrate surface (spray method), and the like can be applied. Among them, a cleaning treatment is performed by a spin coating method, and after cleaning, the substrate is rotated at a speed of 2000 rpm to 4000 rpm. It is preferable to rotate and remove the rinse liquid from the substrate. It is also preferable to include a heating step (Post Bake) after the rinsing step. The developing solution and the rinsing solution remaining between the patterns and inside the patterns are removed by baking. The heating step after the rinsing step is usually 40 to 160 ° C., preferably 70 to 95 ° C., and usually 10 seconds to 3 minutes, preferably 30 seconds to 90 seconds.

In addition, you may produce the mold for imprint using the composition which concerns on this invention, For the details, please refer to patent 4109085 and Unexamined-Japanese-Patent No. 2008-162101, for example.
The pattern forming method of the present invention can also be used for guide pattern formation in DSA (Directed Self-Assembly) (see, for example, ACS Nano Vol. 4 No. 8 Pages 4815-4823).
Further, the resist pattern formed by the above method can be used as a core material (core) of a spacer process disclosed in, for example, JP-A-3-270227 and JP-A-2013-164509.

The present invention also relates to an electronic device manufacturing method including the above-described pattern forming method of the present invention, and an electronic device manufactured by this manufacturing method.
The electronic device of the present invention is suitably mounted on electrical and electronic equipment (home appliances, OA / media related equipment, optical equipment, communication equipment, etc.).

[Usage]
The pattern forming method of the present invention is suitably used for the production of semiconductor microcircuits such as the manufacture of VLSI and high-capacity microchips. When creating a semiconductor microcircuit, the patterned resist film is used for circuit formation and etching, and the remaining resist film portion is finally removed with a solvent or the like. Unlike so-called permanent resists, the resist film derived from the actinic ray-sensitive or radiation-sensitive resin composition described in the present invention does not remain in the final product such as a microchip.

The present invention also relates to an electronic device manufacturing method including the above-described pattern forming method of the present invention, and an electronic device manufactured by this manufacturing method.
The electronic device of the present invention is suitably mounted on electrical and electronic equipment (home appliances, OA / media related equipment, optical equipment, communication equipment, etc.).

  EXAMPLES Hereinafter, although an Example demonstrates this invention further more concretely, this invention is not limited to a following example.

<Synthesis Example 1: Synthesis of Resin (P-1)>
11.4 g of a compound represented by the following formula (2), 3.3 g of a compound represented by the following formula (1), 20.0 g of a 50 mass% ethyl acetate solution of p-hydroxystyrene (3) (p-hydroxystyrene) 10.0 g of (3) was contained) and 3.2 g of polymerization initiator V-601 (manufactured by Wako Pure Chemical Industries, Ltd.) were dissolved in 59.4 g of cyclohexanone. 11.8 g of cyclohexanone was placed in the reaction vessel, and the solution prepared previously at 85 ° C. was added dropwise over 4 hours under a nitrogen gas atmosphere. The reaction solution was heated and stirred for 2 hours and then allowed to cool to room temperature. The obtained reaction solution was dropped and reprecipitated into 494 g of a mixed solution of heptane / ethyl acetate (9/1 (mass ratio)), and 20.3 g of (P-1) was obtained by filtering the precipitate.

  Hereinafter, resins (P-2) to (P-20) and (PR-1) to (PR-4) were synthesized using the same method as for resin (P-1). The synthesized polymer structure, weight average molecular weight (Mw) and dispersity (Mw / Mn) are described below. Moreover, the composition ratio of each repeating unit of the following polymer structure was shown by molar ratio.

  Hereafter, the structure and volume value of the acid generator used in the Example are shown. The calculated value is the volume value of the acid in which protons are bonded to the anion portion.

Basic compound TBAH: Tetrabutylammonium hydroxide TBAB: Tetrabutylammonium benzoate TOA: Tri (n-octyl) amine TPI: 2,4,5-triphenylimidazole

Solvent S1: PGMEA
S2: PGME
S3: Cyclohexanone S4: γ-Butyrolactone

Surfactant W-1: Megafac R08 (manufactured by DIC Corporation; fluorine and silicon-based)
W-2: Polysiloxane polymer KP-341 (manufactured by Shin-Etsu Chemical Co., Ltd .; silicon-based)
W-3: Troisol S-366 (manufactured by Troy Chemical Co .; fluorine type)
W-4: PF6320 (manufactured by OMNOVA; fluorine-based)

Developer / Rinse Solution G-1: Butyl acetate G-2: 2-Heptanone G-3: Anisole G-4: 4-Methyl-2-pentanol G-5: 1-Hexanol G-6: Decane

[Examples 1-1 to 1-20, Comparative Examples 1-1 to 1-4 (electron beam EB exposure (alkali development positive))]
(1) Preparation and application of coating solution of actinic ray-sensitive or radiation-sensitive resin composition A coating solution having the composition shown in the table below is precisely filtered with a membrane filter having a pore size of 0.1 μm, and actinic ray Or radiation sensitive resin composition (resist composition) solution (solid content concentration: 1.5 mass%) was obtained.
This actinic ray-sensitive or radiation-sensitive resin composition solution was applied onto a 6-inch Si wafer that had been previously treated with hexamethyldisilazane (HMDS) using a spin coater Mark8 manufactured by Tokyo Electron, and 100 ° C. for 60 seconds. It dried on the hotplate and obtained the resist film with a film thickness of 100 nm.

(2) EB exposure and development The wafer coated with the resist film obtained in (1) above was subjected to pattern irradiation using an electron beam drawing apparatus (HL750 manufactured by Hitachi, Ltd., acceleration voltage 50 KeV). . At this time, drawing was performed so that a 1: 1 line and space was formed. After electron beam drawing, after heating at 110 ° C. for 60 seconds on a hot plate, immersing in an aqueous 2.38 mass% tetramethylammonium hydroxide (TMAH) solution for 60 seconds, and then rinsing with water for 30 seconds. Dried.

(3) Evaluation of resist pattern Using the scanning electron microscope (S-9220 by Hitachi, Ltd.), the obtained resist pattern was evaluated about the sensitivity, the resolution, and the scum by the following method. The results are shown in the table below.

(3-1) Sensitivity Irradiation energy when resolving a 1: 1 line and space pattern with a line width of 100 nm was defined as sensitivity (Eop). The smaller this value, the better the performance.

(3-2) Resolution In the above Eop, the minimum line width of the separated (1: 1) line and space pattern was defined as the resolution. The smaller this value, the better the performance.

(3-3) Scum evaluation A cross section of a 1: 1 line and space pattern with a line width of 100 nm at the irradiation dose showing the above sensitivity was observed using a scanning electron microscope (S-4300, manufactured by Hitachi, Ltd.), Two-stage evaluation of A and B was performed for the presence or absence of scum. The evaluation criteria are shown below.
A: When scum is not visually observed B: When scum is visually observed

  The evaluation results are shown in Table 1 below.

  As can be seen from Table 1 above, Examples 1-1 to 1-20 use a resin having no repeating unit represented by General Formula (3) and General Formula (4) according to the present invention. Compared with Comparative Examples 1-1 to 1-4, high sensitivity, high resolution, and reduction of scum were simultaneously satisfied.

[Examples 2-1 to 2-20, Comparative Examples 2-1 to 2-4 (electron beam EB exposure (organic solvent developing negative))]
The composition was changed as shown in the following table, and development was carried out with an organic aqueous developer described in the following table instead of an aqueous alkali solution (TMAH; 2.38 mass% tetramethylammonium hydroxide aqueous solution). The actinic ray-sensitive or radiation-sensitive resin composition was prepared and the pattern was formed in the same manner as in Example 1-1 except that the rinse solution described in the following table was used. In the example described as “None” in the column, no rinsing is performed.

Evaluation of Resist Pattern Using a scanning electron microscope (S-9220, manufactured by Hitachi, Ltd.), the obtained resist patterns were designated as Examples 1-1 to 1-20 and Comparative Examples 1-1 to 1-4. The sensitivity, resolving power, and scum were evaluated in the same manner. The results are shown in Table 2 below.

  As can be seen from Table 2 above, Examples 2-1 to 2-20 use a resin having no repeating unit represented by General Formula (3) and General Formula (4) according to the present invention. Compared with Comparative Examples 2-1 to 2-4, high sensitivity, high resolution, and reduction of scum were simultaneously satisfied.

[Examples 3-1 to 3-20, Comparative examples 3-1 to 3-4 (EUV exposure (alkali development positive))]
(1) Preparation and application of coating solution of actinic ray-sensitive or radiation-sensitive resin composition A coating solution having the composition shown in the table below is precisely filtered with a membrane filter having a pore size of 0.05 μm, and actinic ray Or radiation sensitive resin composition (resist composition) solution (solid content concentration: 1.5 mass%) was obtained.
This actinic ray-sensitive or radiation-sensitive resin composition solution was applied onto a 6-inch Si wafer that had been previously treated with hexamethyldisilazane (HMDS) using a spin coater Mark8 manufactured by Tokyo Electron, and 100 ° C. for 60 seconds. It dried on the hotplate and obtained the resist film with a film thickness of 50 nm.

(2) EUV exposure and development The wafer coated with the resist film obtained in the above (1) is subjected to an EUV exposure apparatus (Micro Exposure Tool, NA 0.3, Quadrupole, outer sigma 0.68, inner sigma 0, manufactured by Exitech) .36) and pattern exposure was performed using an exposure mask (line / space = 1/1). After irradiation, heated on a hot plate at 110 ° C. for 60 seconds, immersed in an aqueous 2.38 mass% tetramethylammonium hydroxide (TMAH) solution for 60 seconds, rinsed with water for 30 seconds, and dried. A resist pattern having a 1: 1 line and space pattern with a line width of 50 nm was obtained.

(3) Evaluation of resist pattern Using a scanning electron microscope (S-9380II, manufactured by Hitachi, Ltd.), the obtained resist pattern was evaluated for sensitivity, resolution, pattern shape, and scum by the following methods. The results are shown in the table below.

(3-1) Sensitivity Irradiation energy when resolving a 1: 1 line and space pattern with a line width of 50 nm was defined as sensitivity (Eop). The smaller this value, the better the performance.

(3-2) Resolution In Eop, the minimum line width of the separated (1: 1) line and space pattern was defined as the resolution. The smaller this value, the better the performance.

(3-3) Scum evaluation A cross section of a 1: 1 line and space pattern with a line width of 50 nm at the irradiation dose showing the above sensitivity was observed using a scanning electron microscope (S-4300, manufactured by Hitachi, Ltd.), Two-stage evaluation of A and B was performed for the presence or absence of scum.
A: When scum is not visually observed B: When scum is visually observed

  The evaluation results are shown in Table 3 below.

  As can be seen from Table 3 above, Examples 3-1 to 3-20 use a resin having no repeating unit represented by General Formula (3) and General Formula (4) according to the present invention. Compared with Comparative Examples 3-1 to 3-4, high sensitivity, high resolution, and reduction in scum were simultaneously satisfied.

[Examples 4-1 to 4-20, Comparative Examples 4-1 to 4-4 (EUV exposure (organic solvent developing negative))]
The composition is changed as shown in the table below, and development is performed with the organic developer described in the table below instead of the alkaline aqueous solution (TMAH; 2.38 mass% tetramethylammonium hydroxide aqueous solution), and the water is replaced with water. The actinic ray-sensitive or radiation-sensitive resin composition was prepared and the pattern was formed in the same manner as in Example 3-1, except that rinsing was performed using the rinsing liquid described in the following table. In the table below, rinsing is not performed in the examples where “None” is described in the column of the rinsing liquid.

Evaluation of Resist Pattern Using a scanning electron microscope (S-9380II manufactured by Hitachi, Ltd.), the obtained resist pattern was the same as in Examples 3-1 to 3-20 and Comparative Examples 3-1 to 3-4. In this method, the sensitivity, resolution, and scum were evaluated. The results are shown in Table 4 below.

  As can be seen from Table 4 above, Examples 4-1 to 4-20 use a resin having no repeating unit represented by General Formula (3) and General Formula (4) according to the present invention. Compared with Comparative Examples 4-1 to 4-4, high sensitivity, high resolution, and reduction of scum were simultaneously satisfied.

Claims (11)

An actinic ray-sensitive or sensitive material containing a resin (A) having a partial structure in which acetal is decomposed by the action of an acid to produce a phenolic hydroxyl group and a partial structure in which the acetal is decomposed by the action of an acid to produce a carboxylic acid group a radiation-sensitive resin composition,
The resin (A) is a resin having a repeating unit represented by the general formula (3) and a repeating unit represented by the general formula (4),
(In general formula (3),
R ₃₁ , R ₃₂ and R ₃₃ each independently represents a hydrogen atom, an alkyl group, a cycloalkyl group, a halogen atom, a cyano group or an alkoxycarbonyl group. R ₃₂ may be bonded to L ₃ to form a ring, in which case R ₃₂ represents an alkylene group.
L ₃ represents a single bond or a divalent linking group, and in the case of forming a ring with R ₃₂ , represents a trivalent linking group.
Ar ₃ represents an aromatic ring group.
R ₃₄ represents a hydrogen atom, an alkyl group, a cycloalkyl group, an aryl group, an aralkyl group, an alkoxy group, an acyl group, or a heterocyclic group.
R ₃₅ represents a hydrogen atom, an alkyl group, a cycloalkyl group, an aryl group, an aralkyl group, an alkoxy group, an acyl group, or a heterocyclic group.
M ₃ represents a single bond or a divalent linking group.
Q ₃ represents an alkyl group, a cycloalkyl group, an aryl group or a heterocyclic group.
At least two of Q ₃ , M ₃ and R ₃₄ may be bonded to form a ring.
In general formula (4),
R ₄₁ , R ₄₂ and R ₄₃ each independently represents a hydrogen atom, an alkyl group, a cycloalkyl group, a halogen atom, a cyano group or an alkoxycarbonyl group. R ₄₂ may be bonded to L ₄ to form a ring, and R ₄₂ in this case represents an alkylene group.
L ₄ represents a single bond or a divalent linking group, and in the case of forming a ring with R ₄₂ , represents a trivalent linking group.
R ₄₄ represents a hydrogen atom, an alkyl group, a cycloalkyl group, an aryl group, an aralkyl group, an alkoxy group, an acyl group, or a heterocyclic group.
R ₄₅ represents a hydrogen atom, an alkyl group, a cycloalkyl group, an aryl group, an aralkyl group, an alkoxy group, an acyl group, or a heterocyclic group.
M ₄ represents a single bond or a divalent linking group.
Q ₄ represents an alkyl group, a cycloalkyl group, an aryl group, or a heterocyclic group.
At least two of Q ₄ , M ₄ and R ₄₄ may be bonded to form a ring. )
In Formula (3), a group R ₃₄ is represented by the general formula (3-1), actinic ray-sensitive or radiation-sensitive resin composition.

(In general formula (3-1),
R _3a , R _3b and R _3c each independently represent a substituent other than a hydrogen atom, and each may be bonded to form a ring. ) An actinic ray-sensitive or sensitive material containing a resin (A) having a partial structure in which acetal is decomposed by the action of an acid to produce a phenolic hydroxyl group and a partial structure in which the acetal is decomposed by the action of an acid to produce a carboxylic acid group a radiation-sensitive resin composition,
The resin (A) is a resin having a repeating unit represented by the general formula (3) and a repeating unit represented by the general formula (4),
(In general formula (3),
R ₃₁ , R ₃₂ and R ₃₃ each independently represents a hydrogen atom, an alkyl group, a cycloalkyl group, a halogen atom, a cyano group or an alkoxycarbonyl group. R ₃₂ may be bonded to L ₃ to form a ring, in which case R ₃₂ represents an alkylene group.
L ₃ represents a single bond or a divalent linking group, and in the case of forming a ring with R ₃₂ , represents a trivalent linking group.
Ar ₃ represents an aromatic ring group.
R ₃₄ represents a hydrogen atom, an alkyl group, a cycloalkyl group, an aryl group, an aralkyl group, an alkoxy group, an acyl group, or a heterocyclic group.
R ₃₅ represents a hydrogen atom, an alkyl group, a cycloalkyl group, an aryl group, an aralkyl group, an alkoxy group, an acyl group, or a heterocyclic group.
M ₃ represents a single bond or a divalent linking group.
Q ₃ represents an alkyl group, a cycloalkyl group, an aryl group or a heterocyclic group.
At least two of Q ₃ , M ₃ and R ₃₄ may be bonded to form a ring.
In general formula (4),
R ₄₁ , R ₄₂ and R ₄₃ each independently represents a hydrogen atom, an alkyl group, a cycloalkyl group, a halogen atom, a cyano group or an alkoxycarbonyl group. R ₄₂ may be bonded to L ₄ to form a ring, and R ₄₂ in this case represents an alkylene group.
L ₄ represents a single bond or a divalent linking group, and in the case of forming a ring with R ₄₂ , represents a trivalent linking group.
R ₄₄ represents a hydrogen atom, an alkyl group, a cycloalkyl group, an aryl group, an aralkyl group, an alkoxy group, an acyl group, or a heterocyclic group.
R ₄₅ represents a hydrogen atom, an alkyl group, a cycloalkyl group, an aryl group, an aralkyl group, an alkoxy group, an acyl group, or a heterocyclic group.
M ₄ represents a single bond or a divalent linking group.
Q ₄ represents an alkyl group, a cycloalkyl group, an aryl group, or a heterocyclic group.
At least two of Q ₄ , M ₄ and R ₄₄ may be bonded to form a ring. )
The actinic ray-sensitive or radiation-sensitive resin composition in which R ₄₄ is a group represented by the general formula (4-1) in the general formula (4) .
(In general formula (4-1),
R _4a , R _4b and R _4c each independently represent a substituent other than a hydrogen atom, and each may be bonded to form a ring. ) The resin (A) further comprises the general formula (1) is a resin having a repeating unit represented by claim 1 or 2 actinic ray-sensitive or radiation-sensitive resin composition according to.
(In general formula (1),
R ₁₁ , R ₁₂ and R ₁₃ each independently represents a hydrogen atom, an alkyl group, a cycloalkyl group, a halogen atom, a cyano group or an alkoxycarbonyl group. R ₁₃ may be bonded to Ar ₁ to form a ring, in which case R ₁₃ represents an alkylene group.
X ₁ represents a single bond or a divalent linking group.
Ar ₁ represents an (n + 1) -valent aromatic ring group, and when bonded to R ₁₃ to form a ring, represents an (n + 2) -valent aromatic ring group.
n represents an integer of 1 to 4. ) In the general formula _(3), L 3 is a single bond, Ar ₃ is actinic ray-sensitive or radiation-sensitive resin composition according to any one of claims 1 to 3 is a phenylene group. In the general formula (4), L ₄ is a single bond, a group having an aromatic ring, the actinic ray-sensitive according to any one of claims 1 to 4, a group having a group or adamantyl structure having a norbornyl structure Or a radiation sensitive resin composition. The actinic ray-sensitive or radiation-sensitive resin composition according to any one of claims 1 to 5 , further comprising a compound capable of generating an acid having a volume of 240 to ³ or more upon irradiation with an actinic ray or radiation. The actinic ray-sensitive or resist film made of the radiation-sensitive resin composition according to any one of claims 1-6. (A) forming the resist film according to claim 7 ;
(A) A pattern forming method comprising a step of exposing the film, and (c) a step of developing the exposed film using a developer to form a pattern. The pattern forming method according to claim 8 , wherein the step (c) is a step of forming a negative pattern by developing the exposed film with a developer containing an organic solvent. The pattern formation method of Claim 8 or 9 with which the said exposure is performed using an X-ray, an electron beam, or EUV light. To any one of claims 8 to 10 including the pattern forming method described method for manufacturing an electronic device.