JP5046380B2 - Container lid with excellent straw piercing properties - Google Patents

Description

  The present invention is used for sealing containers such as composite materials and plastic resins used in the beverage field such as liquids and jellies, and is preferably used by piercing a straw used for drinking the contents of the container. It relates to materials.

As a lid material for sealing the opening of a container containing a beverage such as liquid or jelly, a material using a resin film or the like on the outermost surface so that it can be easily peeled off and opened is well known.
However, in addition to the usage in which the container can be easily peeled off and opened by the container, it is required to allow the contents to be drunk by piercing the lid with a straw or the like while the container is sealed.
Therefore, such a lid member is required to have good straw piercing property, but the lid member using the above resin film does not have good straw piercing property. By providing an aluminum foil layer in the lower layer of this resin film, the piercing property can be improved. However, in order to obtain a significant effect, the aluminum foil layer needs to have a thickness exceeding 20 μm, and the improvement effect is not sufficient. In addition, the cover material using aluminum foil as the outermost surface has good piercing ability of the straw, but when gravure printing is performed on the surface of the cover material, the ink becomes dull due to the metallic luster of the aluminum, and the color of the ink ( Since it becomes a cover material inferior to (decoration property), it is excellent in piercing property and the cover material with favorable decorating property is calculated | required.

Several proposals have already been made for a lid material with improved straw piercing properties. For example, Patent Document 1 proposes a lid material using a thin PET film on the outermost surface. Moreover, in patent document 2 grade | etc., The lid | cover material which gave the easy piercing process to the straw piercing part is proposed. Furthermore, Patent Document 3 proposes a lid material in which a uniaxially stretched film is combined to improve the piercing property.
Japanese Utility Model Publication No. 07-28866 Japanese Patent Application Laid-Open No. 07-061469 JP 09-323377 A

However, the lid material using a thin PET film on the outermost surface shown in Patent Document 1 has a problem that pitch printing is very difficult because the film is too thin. Moreover, a thin film has a strong record wrinkle in a coil state, and a strong tension is applied at the time of laminating to correct it. Therefore, there is a problem that a curl is strong and a handling problem often occurs. In addition, the lid material of Patent Document 2 and the like in which the pierced portion of the straw is pierced easily requires secondary processing and tertiary processing, and is designed to guide the consumer to the processing portion that pierces the straw. However, there is a problem that the cost is increased.
Moreover, in the cover material which compounded the uniaxially stretched film shown by patent document 3, since these films differ greatly in the vertical and horizontal thermal contraction rate, a curl is strong and a problem arises in handling in many cases. In addition, the beverage container in the field of the present invention may be used by opening the lid without piercing the straw, but there is a problem that the base material is easily broken during the opening operation.

  The present invention has been made against the background of the above circumstances, and does not impair printability, handling properties, etc., and is excellent in straw piercing properties without increasing the burden of the manufacturing process, and further in strength as a lid material. It is another object of the present invention to provide a container lid material excellent in straw piercing property.

That is, of the straw piercing property excellent container lid of the present invention, according to claim 1 the invention described has a thickness in the. 12 to 2 5 [mu] m, and burst strength is 188 ～240KPa, tear strength 20 gf / 32 A polyester film that is not more than one sheet is used as the outermost surface, a sealant layer is provided at least on the surface in contact with the container opening, and an intermediate layer composed of one or more layers is provided between the polyester film and the sealant layer. And at least one of the intermediate layers is made of an aluminum foil having a thickness of 9 μm or more and less than 20 μm .

That is, according to the present invention, the outermost polyester film has an appropriate burst strength, so that a good lid strength is ensured, the burst strength is suppressed to a predetermined value or less, and a tear strength is obtained. By keeping the value below a predetermined value, the straw can be easily pierced. For the polyester film, a material having excellent printability can be selected after selecting the above-mentioned burst strength and tear strength, which makes it easy to ensure good printability. Moreover, the purpose can be achieved by selecting the material, and the easy piercing property of the straw can be obtained without requiring special processing.
The reason for setting specific conditions in the present invention will be described below.

Burst strength: 188 ~240kPa
For straw breaks through the polyester film (base material) is, of course the strength of the polyester film substrate itself, and elongation of the polyester film, stickiness, etc. of the polyester film resin, the plurality of elements are involved. These characteristics can be discriminated by evaluating the bursting strength, and the lower the bursting strength, the easier it is for the substrate to break (hole) due to the straw pressure. However, if it is less than 188 kPa, the substrate strength is insufficient and the composite (printing / bonding) process cannot be endured. On the other hand, if it exceeds 240 kPa, the piercing property is not different from that of a general packaging polyester film. Therefore, the breaking strength is set in the above range. Incidentally, it is desirable to the upper limit and 200kPa for the same reason.

Tear strength: 20 gf / 32 sheets or less
Once a cut (hole) is formed in the polyester film (base material) with a straw, the one having a lower tear strength is easier to enter the straw after the cut (hole) is expanded.
If it exceeds 20 gf / 32 sheets, the strength of the straw is lost, making it difficult to spread the cut (hole). For the same reason, the upper limit is desirably 15 gf / 32 sheets. Further, if the tear strength of the polyester film is weak, the lower limit is desirably 5 gf / 32 sheets for the reason that the lid material bursts when the contents are filled or the product is transported.

Polyester film thickness: 12-25 μm
The thickness of the polyester film is limited to 12 to 25 μm. If it is less than 12 μm, pitch printing is difficult, and quality defects due to record defects are likely to occur. On the other hand, if it exceeds 25 μm, good piercing property cannot be obtained. Therefore, the thickness of the polyester film is set within the above range. For the same reason, it is desirable that the lower limit is 12 μm and the upper limit is 20 μm.

The polyester (PET) film present invention, as described above, the material of the film is Ru with port re ester film. In addition to PET, typical films used for packaging materials with printing include OPP films and cellophane (PT) films. OPP cannot secure transparency and smoothness of the film unless the film is stretched more than a certain level, so that it is difficult to produce a film having a desired burst strength. Cellophane is difficult to form into a thickness of 20 μm or less, and if a certain thickness is secured, the burst strength increases. PET film, on the other hand, is biaxially stretched during film formation, so there is little difference in longitudinal and lateral strength and elongation. By adjusting the degree of stretching, the bursting strength is relatively easy compared to other films, and tearing Films with good characteristics can be manufactured.

At least one of the intermediate layers is an aluminum foil. The lid material of the present invention has a sealant layer that has a sealing property between the outermost polyester film and the container opening and is thermally bonded to the end of the opening. and which, Ru der having an intermediate layer of one or more layers between these. Then, in the intermediate layer, that make up at least one layer of aluminum foil. This aluminum foil further improves the piercing property of the straw. The aluminum foil means pure aluminum foil or aluminum alloy foil, and the present invention is not limited to a specific composition.

Incidentally, the aluminum foil is of a thickness of less than 9Myuemu～20myuemu. When the thickness is less than 9 μm, the contribution to the piercing property is insufficient, and when the thickness is 20 μm or more, the effect of improving the piercing property is saturated and the cost is increased.
In addition, when a general PET film for packaging is used as the outermost layer, when an aluminum foil layer is provided in the lower layer in order to improve the piercing property, an aluminum foil having a thickness exceeding 20 μm is required, and the increase in foil thickness Although an increase in cost is unavoidable, in the present invention, since the thickness of the aluminum foil can be made less than 20 μm, an increase in cost can be suppressed as much as possible to improve the straw piercing property.

As described above, according to the container lid material excellent in the piercing property of the straw of the present invention, the thickness is 12 to 25 μm, the burst strength is 188 to 240 kPa, and the tear strength is 20 gf / 32 sheets or less. A certain polyester film is used as the outermost surface, a sealant layer is provided at least on the surface in contact with the container opening, and an intermediate layer composed of one or more layers is provided between the polyester film and the sealant layer, Since at least one of the intermediate layers is made of an aluminum foil having a thickness of 9 μm or more and less than 20 μm, it is possible to improve the piercing property of the straw while ensuring the strength as a lid. Moreover, it can be set as the cover material excellent also in printability by using a raw material with favorable printability for the said polyester film.

Below, one Embodiment of this invention is described based on FIG.
Lid 10 of the present invention, Thickness the outermost layer has a more composed film layer 11 to the polyester film arm of 12～25Myuemu, sealant to the opening 21 side of the container 20 lid member 10 is bonded It has a layer 13. The film layer 11 has the characteristics that the thickness is 12 to 25 μm, the burst strength is 188 to 240 kPa, and the tear strength is 20 gf / 32 or less.
The burst strength can be measured by a method defined in JIS P8112-1994. The tear strength can be measured by a method defined in JIS K7127-2: 1998.

The said polyester film can be manufactured by a conventional method, and especially a manufacturing method is not limited as this invention. The polyester film can be printed as desired to form a printed layer.
Moreover, a known material can be adopted for the sealant layer 13, and the present invention is not limited to a specific material, and the thickness thereof is not specified.
In the present invention, between the film layer 11 and the sealant layer 13, Ru an intermediate layer or layers. The intermediate layer, you more configuration to the aluminum foil. In this embodiment, description will be made assuming that the aluminum foil layer 12 is provided as an intermediate layer. Although the composition of this aluminum foil is not specifically limited, For example, 1N30 is mentioned. The thickness of the aluminum foil layer 12 is less than 9～20Myuemu.
Lamination of each of the above layers can be performed by a known method such as dry lamination or extruded polyethylene lamination, and the lamination method is not particularly limited as the present invention.

The lid 10 covers the opening 21 of the container 20 in which the beverage contents are stored, is thermally bonded to the flange 21a at the periphery of the opening 21 via the sealant layer 13, and is provided for distribution. At this time, the lid member 10 has sufficient strength and there is no leakage of the contents.
In the container 20, a straw 30 is stored in a plastic film on the side wall of the container 20. When a purchaser or the like tries to drink the contents in the container 20, the straw 30 is removed from the plastic film. Remove and stab from above the lid 10. At this time, a cut is easily formed in the lid member 10 by the straw 30, and the cut is further expanded by pushing the straw 30, so that the straw 30 can be easily inserted into the container 20. A purchaser or the like can drink the contents through the pierced straw 30.

The laminated structure of the lid material is not limited to the above, and various structures can be adopted as long as it has the film characteristics of the outermost layer and the sealant layer of the lowermost layer.
FIG. 3 shows some examples of laminated structures. In addition, about the structure which is common in the said embodiment, the same code | symbol is attached | subjected and demonstrated. Moreover, among the examples of the laminated structure shown in FIG. 3, the lid members 10 e to 10 h shown in FIGS. (E) to (h) are reference examples that do not have the aluminum foil layer 12.

(A) The lid member 10a shown in the figure has a printing layer 11a on the back side of the film layer 11, and the film layer 11 is interposed via an aluminum foil layer 12 and an adhesive layer 14a by dry lamination or the like. Are stacked. Further, a sealant film 13a is laminated on the back side of the aluminum foil layer 12 via an adhesive layer 14b by dry lamination or the like.
(B) The lid 10b shown in the figure has a film layer 11, a printing layer 11a, an adhesive layer 14a, and an aluminum foil layer 12 laminated in the same manner as described above. Polyethylene) layer 15 and hot melt sealant layer 13b are laminated.

(C) The cover material 10c shown in the figure has a film layer 11, a printing layer 11a, an adhesive layer 14a, and an aluminum foil layer 12 laminated in the same manner as described above, and an extruded sealant resin under the aluminum foil layer 12 A sealant layer 13c having a single layer or multiple layers is laminated.
(D) The lid 10d shown in the figure has a film layer 11, a printing layer 11a, an adhesive layer 14a, and an aluminum foil layer 12 laminated in the same manner as described above. The paper layer 16 is laminated via the adhesive layer 14 b by wet lamination, and the sealant layer 13 c is laminated below the paper layer 16.

  (E) The lid member 10e shown in the figure has a paper layer 16 laminated on a film layer 11 having a printed layer 11a on the back side through an adhesive layer 14a by dry lamination or wet lamination. An extruded PE (polyethylene) layer 15 and a sealant layer 13b are laminated on the lower layer side.

(F) The cover material 10f shown in the figure has a paper layer 16 laminated on a film layer 11 having a printed layer 11a on the back side through an adhesive layer 14a by dry lamination or wet lamination. A sealant layer 13c is laminated on the lower layer side.
(G) In the lid 10g shown in the figure, a sealant film 13a is laminated on a film layer 11 having a printed layer 11a on the back side through an adhesive layer 14a by dry lamination.
(H) The lid member 10h shown in the figure has an extruded PE layer 15 and a sealant layer 13b laminated on a film layer 11 having a printed layer 11a on the back side.

  In addition, the lid | cover materials 10 and 10a-10h demonstrated by the said embodiment are shown as an example, and the structure of this invention is not limited to these laminated structures, It is suitably within the scope of this invention. It is possible to adopt the form.

Examples of the present invention will be described below.
A polyester film (PET) was used as the outermost layer, and a lid material was configured according to the following configuration.
Cover material composition Polyester film / aluminum foil / sealant layer However, PE-EVA film 30 μm is used for the sealant layer, the thickness of the polyester film and the aluminum foil layer is changed, and each material is thermoset urethane adhesive 3 g / m ² Samples laminated by the dry lamination method used were prepared. The composition of the aluminum foil was 1N30.
For comparison, a film using a moisture-proof cellophane film (PT) as the outermost layer and a film using a polypropylene biaxially stretched film (OPP) were prepared.

For each film, the burst strength and tear strength were measured. The burst strength was measured by JIS-P-8112 Murren method, and the tear strength was measured by JIS-K-7128-2 Elmendorf tester.
Each specimen was measured for piercing strength and curl degree.
The puncture strength conforms to the test method stipulated in the Food Sanitation Law, and a commercially available straw (tip angle 45 degrees, diameter 4.84 mm) is used instead of the measuring needle, and the puncture angle is the standard vertical direction (90 In addition to (°), measurement was also performed from an oblique direction (60 °).
The curl degree is measured by measuring the height of warpage when a specimen cut into a square of 10 cm on a side is placed on a horizontal table surface. ○: Warpage height is less than 5 mm, Δ: Warpage height The thickness was evaluated to be less than 5 to 20 mm, x: warped height of 20 mm or more.
The test results are shown in Table 1.

It is an expanded sectional view showing a lid material of one embodiment of the present invention. Similarly, it is sectional drawing which shows the container which welded the cover material. It is an expanded sectional view which shows the example of a change of the cover material of this invention.

Explanation of symbols

DESCRIPTION OF SYMBOLS 10 Cover material 11 Film 12 Aluminum foil layer 13 Sealant layer 20 Container 21 Opening part 30 Straw

Claims (1)

A polyester film having a thickness of 12 to 25 μm, a burst strength of 188 to 240 kPa, and a tear strength of 20 gf / 32 or less is used as the outermost surface, and a sealant layer is provided at least on the surface in contact with the container opening , An intermediate layer composed of one or more layers is provided between the sealant layer and at least one of the intermediate layers is made of an aluminum foil having a thickness of 9 μm or more and less than 20 μm. A container lid with excellent straw piercing characteristics .