JP2015203172A - Softener for sanitary paper - Google Patents
Softener for sanitary paper Download PDFInfo
- Publication number
- JP2015203172A JP2015203172A JP2014084378A JP2014084378A JP2015203172A JP 2015203172 A JP2015203172 A JP 2015203172A JP 2014084378 A JP2014084378 A JP 2014084378A JP 2014084378 A JP2014084378 A JP 2014084378A JP 2015203172 A JP2015203172 A JP 2015203172A
- Authority
- JP
- Japan
- Prior art keywords
- paper
- component
- mass
- content
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は衛生紙用柔軟剤に関し、詳細には、低湿度環境下に保管しても衛生紙に柔らかさを付与することができ、また紙力低下を抑制することができ、更に衛生紙の使用感を良好にすることができる衛生紙用柔軟剤に関する。 The present invention relates to a sanitary paper softener, and more particularly, it can impart softness to sanitary paper even when stored in a low-humidity environment, can suppress a decrease in paper strength, and further improves the feeling of use of sanitary paper. The present invention relates to a sanitary paper softener that can be improved.
衛生紙（以下、単に「紙」ともいう。）は、ティシュペーパーやトイレットペーパー、ペーパータオルなど日常において顔や手など人の肌に触れる目的にて使用されることが多く、良好な肌触りが求められている。中でもティシュペーパーは、鼻をかむなど顔に対して使用されることが多く、より良好な肌触りが求められ、例えば、薬剤をティシュペーパーに含有させて肌触りを向上させたティシュペーパー、いわゆるローションティシュが市販され人気を博している。 Sanitary paper (hereinafter, also simply referred to as “paper”) is often used for the purpose of touching human skin such as the face and hands in daily life, such as tissue paper, toilet paper, and paper towels. Yes. Among them, tissue paper is often used for the face such as biting the nose, and better touch is required. It is on the market and has gained popularity.
市販のローションティシュの多くは、良好な肌触りを付与するために、多価アルコールなどの保湿剤を含む薬剤が使用されている。日本における平均湿度は６０〜７０％ＲＨであり、保湿剤を含む薬剤を含有する紙は、空気中の水分を保湿剤が保持することによって十分な柔らかさが付与される。しかしながら、例えば冬季の暖房の効いた室内などの低湿度環境下にて薬剤を塗布した紙を保存すると、紙中の水分も減少するので徐々に紙の柔らかさが失われてしまうことがある。
即ち、柔軟剤を含んだ衛生紙は、低湿度環境下での保管においてその柔らかさが損なわれることが多い。
In many commercially available lotion tissues, a drug containing a moisturizing agent such as a polyhydric alcohol is used in order to impart a good touch. The average humidity in Japan is 60 to 70% RH, and paper containing a chemical containing a humectant is imparted with sufficient softness when the humectant retains moisture in the air. However, if the paper coated with the drug is stored in a low-humidity environment such as a heated room in winter, for example, the water in the paper also decreases and the paper may gradually lose its softness.
That is, sanitary paper containing a softening agent often loses its softness when stored in a low humidity environment.
特許文献１には、グリセリンなどの保湿剤、柔軟剤としてアルキル燐酸エステル塩などの界面活性剤、およびアラビアガムやグアーガムのような中性多糖類などの親水性高分子を混合した薬剤を紙に含ませることで、紙が水を保持する能力を高め、湿度による肌触りの変化を少なくすることが開示されている。しかしながら、この方法では、長期における低湿度環境下においては水分の維持が困難となり、柔らかさの維持も不十分となる。 In Patent Document 1, a paper containing a humectant such as glycerin, a surfactant such as an alkyl phosphate ester as a softening agent, and a hydrophilic polymer such as a neutral polysaccharide such as gum arabic or guar gum on paper. It is disclosed that the inclusion increases the ability of the paper to retain water and reduces the change in touch due to humidity. However, this method makes it difficult to maintain moisture in a long-term low-humidity environment, and the maintenance of softness is insufficient.
また、特許文献２や特許文献３では、グリセリンなどの多価アルコールを含まず、ショ糖エステルなどのエステル類とオリーブ油や高級アルコールなどの油剤を混合した薬剤を紙に含有させることが示されている。これらの方法では、多価アルコールを含まないことで水分に依存することなく紙に良好な肌触りを付与しているので、環境湿度の変化に対する肌触りの変化は少ないが、付与される柔らかさ自体が十分ではない。 Patent Document 2 and Patent Document 3 show that paper does not contain a polyhydric alcohol such as glycerin, and a paper is mixed with an ester such as sucrose ester and an oil such as olive oil or higher alcohol. Yes. In these methods, since the paper does not depend on moisture due to the absence of polyhydric alcohol, the paper has a good touch, so the change in the touch with respect to the change in environmental humidity is small, but the softness itself that is given is Not enough.
肌触りを更に向上させる方法として、紙に塗布する柔軟剤の量を増やすことが挙げられる。塗布する柔軟剤量を増やすことによって柔らかさをはじめとした肌触りは向上するものの、紙の強度、即ち紙力が低下してしまう。紙力が低下すると、例えば箱から取り出す際に破れ易くなることがあり、また、鼻をかんだり、クレンジングのふき取りを行なったりした際に紙片が破れて一部が肌に付着することがあるので、紙を使用する際に不具合が生じることがある。更に、ローションティシュの製造時において、柔軟剤を塗布した後の工程で紙切れが起こるなどの不具合が生じることがある。
そこで、紙力を上げる方法として、紙力増強剤を使用する方法や紙の坪量を上げて紙自体を厚くする方法が考えられる。しかしながら、これらの方法では、紙力を上げることはできるものの、紙が硬くなり、求める柔らかさが不十分となる。
One way to further improve the touch is to increase the amount of softening agent applied to the paper. By increasing the amount of the softening agent applied, the softness and other soft touches are improved, but the strength of the paper, that is, the paper strength is reduced. When paper strength decreases, for example, it may be easily torn when taken out from the box, and when you bite the nose or wipe cleansing, the piece of paper may tear and part of it may adhere to the skin. When using paper, problems may occur. Further, when manufacturing the lotion tissue, there may be a problem such as paper breakage in the process after applying the softening agent.
Therefore, as a method for increasing the paper strength, a method using a paper strength enhancer or a method of increasing the paper basis weight to thicken the paper itself can be considered. However, these methods can increase the paper strength, but the paper becomes hard and the required softness is insufficient.
特許文献４には、グリセリン、ポリオキシアルキレンメチルグルコシド、ジグリセリンを含有する柔軟剤を紙に塗布することにより、紙力低下を抑制しながら肌触りを向上させ得ることが開示されている。特許文献５には、グリセリン、ポリオキシアルキレンメチルグルコシド、ジグリセリンに加えて、ポリエチレングリコールを含有する柔軟剤を紙に塗布することにより、高湿度環境下でも紙力低下を抑制し得ることが開示されている。しかしながら、これらの方法では、低湿度で長期保存した場合に柔らかさが低下するおそれがある。
即ち、肌触りを更に向上させるために、衛生紙に塗布する柔軟剤の量を増やすことによって低湿度環境下で紙を保管しても肌触りを維持向上させることができても、紙力を維持することが難しいので、衛生紙の製造時に不具合が生じることがあり、また使用時に破れたり衛生紙片が肌に付着したりするなど、不快な使用感となることがある。
Patent Document 4 discloses that a softening agent containing glycerin, polyoxyalkylene methyl glucoside and diglycerin can be applied to paper to improve the touch while suppressing a decrease in paper strength. Patent Document 5 discloses that in addition to glycerin, polyoxyalkylene methyl glucoside and diglycerin, a softening agent containing polyethylene glycol can be applied to paper to suppress a decrease in paper strength even in a high humidity environment. Has been. However, in these methods, there is a risk that the softness is lowered when stored for a long time at low humidity.
That is, in order to further improve the touch, even if the paper can be stored and maintained in a low humidity environment by increasing the amount of the softening agent applied to the sanitary paper, the paper strength can be maintained. However, it may cause problems during the manufacture of sanitary paper, and may cause an unpleasant feeling of use, such as tearing during use or sanitary paper pieces adhering to the skin.
本発明は、低湿度環境下に保管しても衛生紙に柔らかさを付与することができ、また紙力低下を抑制することができ、更に衛生紙の使用感を良好にすることができる衛生紙用柔軟剤の提供を目的とする。 The present invention can provide softness to sanitary paper even when stored in a low-humidity environment, can suppress a decrease in paper strength, and can further improve the feeling of use of sanitary paper. The purpose is to provide an agent.
本発明者らは、鋭意検討した結果、（Ａ）グリセリン、（Ｂ）特定のポリオキシアルキレン多価アルコール、および（Ｃ）特定のショ糖脂肪酸エステルを所定量で含有する組成物を衛生紙に含ませることによって、低湿度環境下でも柔らかさを有し、また紙力低下が抑制され、更に使用感が良好な衛生紙が得られることを見出した。 As a result of intensive studies, the present inventors have included in sanitary paper a composition containing (A) glycerin, (B) a specific polyoxyalkylene polyhydric alcohol, and (C) a specific sucrose fatty acid ester in a predetermined amount. As a result, it was found that sanitary paper that has softness even in a low-humidity environment, that suppresses a decrease in paper strength, and that has a good usability can be obtained.
すなわち、本発明は、（Ａ）グリセリン、（Ｂ）オキシアルキレン基の炭素数が２〜３であり、アルキレンオキシドの平均付加モル数が５〜３０であり、かつ価数が３〜６の多価アルコールから形成されたポリオキシアルキレン多価アルコール、および（Ｃ）炭素数１０〜２２のアシル基を有するショ糖脂肪酸エステルを含有し、（Ａ）成分と（Ｂ）成分と（Ｃ）成分の合計含有量を１００質量部としたとき、（Ａ）成分の含有量が９０〜９９．７質量部、（Ｂ）成分の含有量が０．２〜５質量部、（Ｃ）成分の含有量が０．１〜５質量部である衛生紙用柔軟剤に関する。
また、本発明の衛生紙用柔軟剤は、更に（Ｄ）炭化水素油を含有し、（Ａ）成分と（Ｂ）成分と（Ｃ）成分の合計を１００質量部としたとき、（Ｄ）成分の含有量が０．２〜２．５質量部であってもよい。
なお、本発明における「衛生紙」には、日常において顔や手など人の肌に触れる目的にて使用される紙が包含され、例えば、ティシュペーパー、トイレットペーパー、ペーパータオルなどが包含される。
That is, in the present invention, (A) glycerin, (B) an oxyalkylene group having 2 to 3 carbon atoms, an alkylene oxide having an average added mole number of 5 to 30, and a valence of 3 to 6 A polyoxyalkylene polyhydric alcohol formed from a monohydric alcohol, and (C) a sucrose fatty acid ester having an acyl group having 10 to 22 carbon atoms, comprising (A) component, (B) component, and (C) component When the total content is 100 parts by mass, the content of component (A) is 90 to 99.7 parts by mass, the content of component (B) is 0.2 to 5 parts by mass, and the content of component (C) Relates to a softener for sanitary paper, wherein is 0.1 to 5 parts by mass.
The sanitary paper softener of the present invention further contains (D) a hydrocarbon oil, and when the total of (A), (B) and (C) is 100 parts by mass, (D) The content of may be 0.2 to 2.5 parts by mass.
The “sanitary paper” in the present invention includes paper used for daily contact with human skin such as face and hand, and includes, for example, tissue paper, toilet paper, paper towel and the like.
本発明の衛生紙用柔軟剤によれば、低湿度環境下に保管しても衛生紙に柔らかさを付与することができ、また紙力低下を抑制することができ、更に衛生紙の使用感を良好にすることができる。 According to the sanitary paper softener of the present invention, softness can be imparted to sanitary paper even when stored in a low-humidity environment, and a decrease in paper strength can be suppressed. can do.
以下、本発明の実施形態を説明する。本発明の衛生紙用柔軟剤は、（Ａ）グリセリン、（Ｂ）特定のポリオキシアルキレン多価アルコール、および（Ｃ）特定のショ糖脂肪酸エステルを含有する。 Embodiments of the present invention will be described below. The sanitary paper softener of the present invention contains (A) glycerin, (B) a specific polyoxyalkylene polyhydric alcohol, and (C) a specific sucrose fatty acid ester.
（Ａ）成分のグリセリンとしては、化粧品、医薬品等の原料として使用されているグリセリンが好適に使用される。 (A) As glycerin of a component, the glycerin currently used as raw materials, such as cosmetics and a pharmaceutical, is used suitably.
（Ｂ）成分のポリオキシアルキレン多価アルコールは、紙のしっとり感向上と共に紙力低下の抑制に寄与するものである。
ポリオキシアルキレン多価アルコールのオキシアルキレン基は、炭素数が２〜３であり、具体的にはオキシエチレン基またはオキシプロピレン基であり、好ましくはオキシエチレン基である。
アルキレンオキシドの平均付加モル数は５〜３０であり、好ましくは７〜２０、更に好ましくは９〜１２である。平均付加モル数が５未満の場合には紙力低下の抑制が不十分となることがあり、３０モルを超える場合には柔らかさの向上が不十分となることがある。
ポリオキシアルキレン多価アルコールの構成成分である多価アルコールは価数が３〜６であり、具体的にはグリセリン、ジグリセリン、トリグリセリン、テトラグリセリン、ペンタエリスリトール、グルコース、メチルグルコシド、ソルビタン、キシリトール、ソルビトールなどが挙げられる。特に、多価アルコールの価数は３〜４が好ましく、例えばグリセリン、メチルグルコシドなどが好ましい。
The (B) component polyoxyalkylene polyhydric alcohol contributes to the improvement of the moist feeling of paper and the suppression of paper strength reduction.
The oxyalkylene group of the polyoxyalkylene polyhydric alcohol has 2 to 3 carbon atoms, specifically an oxyethylene group or an oxypropylene group, preferably an oxyethylene group.
The average added mole number of alkylene oxide is 5 to 30, preferably 7 to 20, and more preferably 9 to 12. When the average number of added moles is less than 5, suppression of reduction in paper strength may be insufficient, and when it exceeds 30 moles, improvement in softness may be insufficient.
The polyhydric alcohol that is a constituent of the polyoxyalkylene polyhydric alcohol has a valence of 3 to 6, and specifically glycerin, diglycerin, triglycerin, tetraglycerin, pentaerythritol, glucose, methyl glucoside, sorbitan, xylitol. And sorbitol. In particular, the valence of the polyhydric alcohol is preferably 3 to 4, and for example, glycerin, methyl glucoside and the like are preferable.
（Ｃ）成分のショ糖脂肪酸エステルは、炭素数１０〜２２のアシル基を有する。炭素数１０〜２２のアシル基としては、具体的に脂肪酸名で表記すると、例えばカプリン酸、ラウリン酸、ミリスチン酸、パルミチン酸、ステアリン酸、イソステアリン酸、オレイン酸、リノール酸、リノレン酸等の脂肪酸が挙げられる。また、混合脂肪酸由来のアシル基を用いることができ、かかる混合脂肪酸としては、ヤシ油脂肪酸、パーム油脂肪酸等が挙げられる。
特に、炭素数１４〜２２のアシル基が好ましく、炭素数１６〜１８の直鎖で飽和のアシル基が更に好ましい。ショ糖脂肪酸エステルが炭素数１０〜２２のアシル基を有することにより、良好な柔らかさを衛生紙に付与することができる。
また、ショ糖脂肪酸エステルは親水性が高い方が好ましく、特にモノエステル含量が５０％以上である場合に更に良好な効果を示す。
The sucrose fatty acid ester as the component (C) has an acyl group having 10 to 22 carbon atoms. Examples of the acyl group having 10 to 22 carbon atoms include fatty acids such as capric acid, lauric acid, myristic acid, palmitic acid, stearic acid, isostearic acid, oleic acid, linoleic acid, and linolenic acid. Is mentioned. Moreover, the acyl group derived from a mixed fatty acid can be used, and examples of the mixed fatty acid include coconut oil fatty acid and palm oil fatty acid.
In particular, an acyl group having 14 to 22 carbon atoms is preferable, and a linear and saturated acyl group having 16 to 18 carbon atoms is more preferable. When the sucrose fatty acid ester has an acyl group having 10 to 22 carbon atoms, good softness can be imparted to the sanitary paper.
In addition, the sucrose fatty acid ester preferably has a high hydrophilicity, and particularly exhibits a better effect when the monoester content is 50% or more.
本発明の衛生紙用柔軟剤は、（Ａ）成分と（Ｂ）成分と（Ｃ）成分の合計含有量を１００質量部としたとき、（Ａ）成分の含有量が９０〜９９．７質量部、好ましくは９２〜９９質量部である。（Ａ）成分の含有量が９０質量部未満の場合は、６０％ＲＨ以上の湿度環境においてしっとり感の向上が不十分となることがあり、（Ａ）成分の含有量が９９．７質量部を超える場合は、低湿度環境下における柔らかさの向上が不十分となることがある。 The sanitary paper softener of the present invention has a component (A) content of 90 to 99.7 parts by mass when the total content of the component (A), the component (B), and the component (C) is 100 parts by mass. , Preferably it is 92-99 mass parts. When the content of the component (A) is less than 90 parts by mass, the moist feeling may be insufficiently improved in a humidity environment of 60% RH or more, and the content of the component (A) is 99.7 parts by mass. In the case of exceeding, the improvement of softness in a low humidity environment may be insufficient.
（Ｂ）成分の含有量は、（Ａ）成分と（Ｂ）成分と（Ｃ）成分の合計含有量を１００質量部としたとき、０．２〜５質量部である。（Ｂ）成分の含有量が０．２質量部未満の場合は、紙力低下を抑制することが困難となることがあり、５質量部を超える場合は、湿度６０％ＲＨ以上の環境において、きしみ感が感じられることがある。中でも、（Ｂ）成分の含有量が１〜２質量部の場合、紙力低下を抑制しながらしっとり感を衛生紙に与えることができる。 The content of the component (B) is 0.2 to 5 parts by mass when the total content of the component (A), the component (B) and the component (C) is 100 parts by mass. When the content of the component (B) is less than 0.2 parts by mass, it may be difficult to suppress a decrease in paper strength. When the content exceeds 5 parts by mass, in an environment with a humidity of 60% RH or more, A squeaky sensation may be felt. Especially, when content of (B) component is 1-2 mass parts, a moist feeling can be given to sanitary paper, suppressing paper strength fall.
（Ｃ）成分の含有量は、（Ａ）成分と（Ｂ）成分と（Ｃ）成分の合計含有量を１００質量部としたとき、０．１〜５質量部である。（Ｃ）成分の含有量が０．１質量部未満の場合は紙の柔らかさが不十分となることがあり、５質量部を超える場合は紙のしっとり感が不十分となることがある。中でも、（Ｃ）成分の含有量が０．５〜２質量部であることが好ましく、良好な柔らかさやしっとり感を衛生紙に与えることができる。 The content of the component (C) is 0.1 to 5 parts by mass when the total content of the component (A), the component (B), and the component (C) is 100 parts by mass. When the content of the component (C) is less than 0.1 parts by mass, the paper may have insufficient softness, and when it exceeds 5 parts by mass, the paper may have a moist feeling. Especially, it is preferable that content of (C) component is 0.5-2 mass parts, Good softness and moist feeling can be given to sanitary paper.
（Ｂ）成分と（Ｃ）成分の質量比〔（Ｂ）／（Ｃ）〕は、３０／７０〜７５／２５であることが低湿度環境下における柔らかさの維持の点で好適であり、中でも５０／５０〜７０／３０であることが更に好ましい。 The mass ratio of the component (B) to the component (C) [(B) / (C)] is preferably 30/70 to 75/25 from the viewpoint of maintaining softness in a low humidity environment. Among these, 50/50 to 70/30 is more preferable.
本発明の衛生紙用柔軟剤は、（Ａ）成分、（Ｂ）成分および（Ｃ）成分に加えて、更に（Ｄ）炭化水素油を含有していてもよく、（Ｄ）成分を含有することにより、低湿度下における紙の保水性を更に向上させることができる。
炭化水素油としては、例えば、水添ポリイソブテン、流動パラフィン、スクワラン、ワセリン等が挙げられる。好ましくは水添ポリイソブテン等の分岐を有するものであり、このような炭化水素油は、低温低湿度環境下でも衛生紙を硬くさせ難く、保水性を維持させることができる。
炭化水素油の中でも４０℃における動粘度が４〜１００ｍｍ２／ｓであるものが好ましく、更に４０℃における動粘度が１０〜５０ｍｍ２／ｓであるものがより好ましい。なお、炭化水素油の動粘度は、JIS K 2283記載の方法に従って測定することができる。
The sanitary paper softener of the present invention may further contain (D) hydrocarbon oil in addition to (A) component, (B) component and (C) component, and contain (D) component. As a result, the water retention of the paper under low humidity can be further improved.
Examples of the hydrocarbon oil include hydrogenated polyisobutene, liquid paraffin, squalane, and petroleum jelly. Preferably, it has a branch such as hydrogenated polyisobutene, and such a hydrocarbon oil can keep the sanitary paper hard even under a low temperature and low humidity environment, and can maintain water retention.
Among the hydrocarbon oils, those having a kinematic viscosity at 40 ° C. of 4 to 100 mm 2 / s are preferred, and those having a kinematic viscosity at 40 ° C. of 10 to 50 mm 2 / s are more preferred. The kinematic viscosity of the hydrocarbon oil can be measured according to the method described in JIS K 2283.
（Ｄ）成分の含有量は、（Ａ）成分と（Ｂ）成分と（Ｃ）成分の合計を１００質量部としたとき、好ましくは０．２〜２．５質量部であり、更に好ましくは０．５〜２質量部、特に好ましくは１〜１．５質量部である。（Ｄ）成分を上記の範囲で含有することにより、低湿度下における紙の保水性を更に向上させることができる。 The content of component (D) is preferably 0.2 to 2.5 parts by mass, more preferably 100 parts by mass when the total of components (A), (B) and (C) is 100 parts by mass. 0.5 to 2 parts by mass, particularly preferably 1 to 1.5 parts by mass. By containing the component (D) in the above range, the water retention of the paper under low humidity can be further improved.
本発明の衛生紙用柔軟剤は、ミリスチン酸イソプロピルやパルミチン酸エチルヘキシルなどのエステル油、高級アルコール、オリーブ油や大豆油などの油脂類、メチルポリシロキサンやその誘導体などのシリコーン油といった油性成分；アルキルリン酸エステル、アルキル硫酸エステル、アルキルスルホコハク酸塩などの陰イオン界面活性剤、四級アンモニウム塩やアルキルアミン塩などのカチオン性界面活性剤、アルキルベタインなどの両性界面活性剤、ソルビタン脂肪酸エステルやアルキルアルカノールアミドなどの非イオン性界面活性剤といった界面活性剤；ジグリセリン、プロピレングリコール、１, ３−ブチレングリコール、ソルビトールなどの多価アルコール、ポリエチレングリコールなどの保湿剤；セルロース誘導体、デンプン誘導体、ポリビニルアルコール、カルボキシビニルポリマー、キサンタンガム、ゲランガム、グアーガム、カードラン、水溶性コラーゲンなどの水溶性高分子；安息香酸、フェノキシエタノール、塩化ベンザルコニウム、メチルイソチアゾリノン、ブチルカルバミン酸ヨウ化イソプロピルといった防腐剤などを他の成分としてさらに含有してもよい。
他の成分として、中でもポリエチレングリコールを含有することが好ましく、例えば、数平均分子量が２００〜１０００、さらに好ましくは数平均分子量が３００〜６００のポリエチレングリコールが、（Ａ）成分と（Ｂ）成分と（Ｃ）成分の合計含有量を１００質量部としたとき、０．５〜５質量部含まれていることが好ましい。なお、ポリエチレングリコールの数平均分子量は、通常、水酸基価より算出することができる。
The sanitary paper softener of the present invention comprises oil components such as ester oils such as isopropyl myristate and ethylhexyl palmitate, higher alcohols, oils such as olive oil and soybean oil, and silicone oils such as methylpolysiloxane and derivatives thereof; Anionic surfactants such as esters, alkyl sulfates and alkylsulfosuccinates, cationic surfactants such as quaternary ammonium salts and alkylamine salts, amphoteric surfactants such as alkylbetaines, sorbitan fatty acid esters and alkylalkanolamides Surfactants such as nonionic surfactants such as diglycerin, propylene glycol, polyhydric alcohols such as 1,3-butylene glycol and sorbitol, moisturizers such as polyethylene glycol, cellulose derivatives and denps Water-soluble polymers such as derivatives, polyvinyl alcohol, carboxyvinyl polymer, xanthan gum, gellan gum, guar gum, curdlan, water-soluble collagen; benzoic acid, phenoxyethanol, benzalkonium chloride, methylisothiazolinone, isopropyl butylcarbamate, etc. You may further contain antiseptic | preservative etc. as another component.
Among other components, it is preferable to contain polyethylene glycol, for example, polyethylene glycol having a number average molecular weight of 200 to 1000, more preferably a number average molecular weight of 300 to 600 is (A) component and (B) component. When the total content of component (C) is 100 parts by mass, 0.5 to 5 parts by mass is preferably included. The number average molecular weight of polyethylene glycol can be usually calculated from the hydroxyl value.
本発明の衛生紙用柔軟剤は、取扱いを良くするために、水などの溶媒で希釈し粘度を低減させて使用することが好ましく、例えば、水で１〜１．５倍に希釈して使用することができる。 In order to improve handling, the sanitary paper softener of the present invention is preferably used after being diluted with a solvent such as water to reduce the viscosity, for example, diluted 1 to 1.5 times with water. be able to.
本発明の衛生紙用柔軟剤を含ませる衛生紙としては、ティシュペーパー、トイレットペーパー、キッチンペーパー等が挙げられる。衛生紙用柔軟剤を含ませる方法としては、塗布、含浸、流延などが挙げられる。例えば、水にて１．０５〜１．２５倍に希釈した衛生紙用柔軟剤をコーターまたは印刷機による塗布法、スプレー塗布法、浸漬法等により衛生紙に含ませることができる。これらの方法の中でも、グラビア印刷やフレキソ印刷等の印刷方式による塗布法が衛生紙への柔軟剤の付着のムラが少なくなる面で好ましい。
さらに、本発明の衛生紙用柔軟剤を衛生紙に含ませる工程において、衛生紙用柔軟剤を加温するなどして粘度を５０〜３００ｍＰａ・ｓｅｃ、好ましくは７０〜１５０ｍＰａ・ｓｅｃに調整することにより衛生紙への付着のムラを低減することができる。
なお、上記の粘度は、４０℃における粘度であり、Ｂ型粘度計にて測定することができる。
本発明の衛生紙用柔軟剤は、充分な効果を発揮するために、衛生紙１００質量部に対して、１５〜３５質量部を衛生紙に含ませることができ、好ましくは２３〜３５質量部を含ませることにより本発明の効果がより顕著に発揮される。
Examples of the sanitary paper containing the sanitary paper softener of the present invention include tissue paper, toilet paper, and kitchen paper. Examples of the method for including the sanitizing paper softener include coating, impregnation, and casting. For example, the sanitary paper softener diluted 1.05 to 1.25 times with water can be included in the sanitary paper by a coating method using a coater or a printing machine, a spray coating method, a dipping method, or the like. Among these methods, a coating method using a printing method such as gravure printing or flexographic printing is preferable in terms of reducing unevenness in the adhesion of the softener to the sanitary paper.
Furthermore, in the step of including the sanitary paper softener of the present invention in the sanitary paper, the sanitary paper softener is heated to a sanitary paper by adjusting the viscosity to 50 to 300 mPa · sec, preferably 70 to 150 mPa · sec. Unevenness of adhesion can be reduced.
In addition, said viscosity is a viscosity in 40 degreeC and can be measured with a B-type viscometer.
The sanitary paper softener of the present invention can contain 15 to 35 parts by mass, preferably 23 to 35 parts by mass, with respect to 100 parts by mass of sanitary paper in order to exert a sufficient effect. As a result, the effect of the present invention is more remarkably exhibited.
以下、本発明を実施例および比較例により具体的に説明する。 Hereinafter, the present invention will be specifically described with reference to Examples and Comparative Examples.
〔衛生紙用柔軟剤の調製例〕
（Ａ）成分のグリセリンを９７．８質量部、（Ｂ）成分のポリオキシエチレン（１０）メチルグルコシドを１．２質量部、（Ｃ）成分のショ糖ラウリン酸エステルを１質量部、それぞれ混合して、組成物１（実施例１）を得た。
また、実施例１と同様に、表２および表３に示すとおり、各成分を所定の割合で混合し、組成物２〜組成物１７（実施例２〜１３、比較例１〜４）を調製した。
（Ｃ）成分として用いたショ糖脂肪酸エステルは、表１に示すＣ−１、Ｃ−２、Ｃ−３であり、モノエステル含量は以下の方法にて測定した。
[Example of preparation of softener for sanitary paper]
(A) 97.8 parts by mass of component glycerin, (B) component polyoxyethylene (10) methyl glucoside 1.2 parts by mass, (C) component 1 part by mass of sucrose laurate Thus, composition 1 (Example 1) was obtained.
Further, as in Example 1, as shown in Tables 2 and 3, the respective components were mixed at a predetermined ratio to prepare compositions 2 to 17 (Examples 2 to 13 and Comparative Examples 1 to 4). did.
(C) Sucrose fatty acid ester used as a component is C-1, C-2, and C-3 shown in Table 1, and the monoester content was measured by the following method.
（モノエステル含量測定）
ゲル浸透クロマトグラフィー（ＧＰＣ）を用いて以下の条件にて測定し、モノエステルのピークの面積百分率比をモノエステルの成分含有量とした。
装置：東ソー株式会社製、ＨＬＣ−８２２０
カラム：TSKgel Super H1000、Super H2000 、Super H4000
溶離液：ＴＨＦ
流速：０．２ｍＬ／ｍｉｎ
検出器：ＲＩ
(Monoester content measurement)
Measurement was performed using gel permeation chromatography (GPC) under the following conditions, and the area percentage ratio of the monoester peak was defined as the monoester component content.
Apparatus: Tosoh Corporation, HLC-8220
Column: TSKgel Super H1000, Super H2000, Super H4000
Eluent: THF
Flow rate: 0.2 mL / min
Detector: RI
〔衛生紙用柔軟剤塗布ティシュペーパーの調製例〕
調製した衛生紙用柔軟剤を水にて１．１倍に希釈した後、４０℃に加温して動粘度を７０〜１００ｍＰａ・ｓｅｃに調整し、ティシュペーパーに柔軟剤を印刷方式にて転写塗布した。塗布前後のティシュペーパーの重量差から、塗布前のティシュペーパー１００質量部に対する塗布量を算出し、２４〜２６質量部となるように塗布した。
[Preparation example of tissue paper coated with softener for sanitary paper]
The prepared sanitary paper softener is diluted 1.1 times with water, heated to 40 ° C to adjust the kinematic viscosity to 70-100 mPa · sec, and the softener is transferred onto tissue paper by printing. did. From the weight difference of the tissue paper before and after application, the amount of application to 100 parts by mass of tissue paper before application was calculated, and the application was made to be 24 to 26 parts by mass.
〔柔らかさの評価〕
調製したティシュペーパーを温度２３℃、湿度６０％ＲＨの恒温恒湿環境、および温度２３℃、湿度３０％ＲＨの恒温恒湿環境に、それぞれ７日間保管した後に、２枚１組としてJAPAN TAPPI No.34 に準拠した方法にて柔軟度（ｍＮ／１００ｍｍ）の評価を行なった。各湿度条件での柔軟度から以下のとおりに評価した。
[Evaluation of softness]
The prepared tissue paper is stored in a constant temperature and humidity environment at a temperature of 23 ° C. and a humidity of 60% RH, and a constant temperature and humidity environment of a temperature of 23 ° C. and a humidity of 30% RH for 7 days, respectively. The degree of flexibility (mN / 100 mm) was evaluated by a method based on .34. It evaluated as follows from the softness | flexibility in each humidity condition.
（６０％ＲＨ）
１６ｍＮ／１００ｍｍ以下：◎（極めて良好）
１６ｍＮ／１００ｍｍ超、１８ｍＮ／１００ｍｍ未満：○（良好）
１８ｍＮ／１００ｍｍ以上：×（不良）
（３０％ＲＨ）
２１ｍＮ／１００ｍｍ以下：◎（極めて良好）
２１ｍＮ／１００ｍｍ超、２３ｍＮ／１００ｍｍ未満：○（良好）
２３ｍＮ／１００ｍｍ以上：×（不良）
(60% RH)
16 mN / 100 mm or less: ◎ (very good)
More than 16mN / 100mm, less than 18mN / 100mm: ○ (good)
18 mN / 100 mm or more: x (defect)
(30% RH)
21 mN / 100 mm or less: ◎ (very good)
More than 21 mN / 100 mm, less than 23 mN / 100 mm: ○ (good)
23 mN / 100 mm or more: x (defect)
〔紙力の測定〕
調製したティシュペーパーを温度２３℃、湿度６０％ＲＨの恒温恒湿環境にて２日間保管した後、ティシュペーパーを１２０×１５ｍｍに切り、引張圧縮試験機（株式会社今田製作所製、ＳＶ−２０１−０−ＳＨ）を用いて紙の引張強度を測定した。得られた引張強度から以下のとおりに評価した。
０．５Ｎ以上：○（良好）
０．５Ｎ未満：×（不良）
[Measurement of paper strength]
The prepared tissue paper was stored in a constant temperature and humidity environment at a temperature of 23 ° C. and a humidity of 60% RH for 2 days, and then the tissue paper was cut into 120 × 15 mm, and a tensile and compression tester (manufactured by Imada Manufacturing Co., Ltd., SV-201-). The tensile strength of the paper was measured using 0-SH). Evaluation was performed as follows from the obtained tensile strength.
0.5N or more: ○ (good)
Less than 0.5N: x (defect)
〔使用感の評価〕
温度２３℃、湿度６０％ＲＨの恒温恒湿環境にて２日間保管した衛生紙用柔軟剤塗布ティシュペーパーを用いて、水で濡らした手を拭いた際の使用感について評価した。パネラー１０名に対して、肌触りに加えて、手の上に水１ｍｌを広げ、そのティシュペーパーで拭いたときの状態を評価した。ティシュペーパーが手に張り付き、破れるなどして拭きにくいと感じた場合は「不合格」、拭きにくいと感じなかった場合は「合格」の評価を行なった。この結果、「合格」と評価したパネラーが８人以上の場合は「◎」（極めて良好）、６人以上７人以下の場合は「○」（良好）、５人以下の場合は「×」（不良）と判定した。
[Evaluation of feeling of use]
Using tissue paper coated with a softening agent for sanitary paper stored for 2 days in a constant temperature and humidity environment at a temperature of 23 ° C. and a humidity of 60% RH, the usability when wiping hands wet with water was evaluated. For 10 panelists, in addition to the touch, 1 ml of water was spread on the hand and the condition when wiped with tissue paper was evaluated. The tissue paper was evaluated as “Fail” when it felt that it was difficult to wipe because it was stuck or torn, and “Pass” when it did not feel difficult to wipe. As a result, when the number of panelists evaluated as “pass” is 8 or more, “◎” (very good), when 6 or more and 7 or less, “◯” (good), and when 5 or less, “×” (Defect) was determined.
実施例１〜１３の衛生紙用柔軟剤である組成物１〜１３が塗布されたティシュペーパーは、いずれも高湿度および低湿度環境での柔らかさ、紙力低下の抑制、使用感の点で優れていた。
一方、比較例１および２では（Ｃ）成分が含まれていないので、低湿度環境下での柔軟性および使用感が不十分であった。比較例３では（Ｂ）成分に代えてアルキレンオキシドの付加されていない多価アルコールが用いられているので、紙力低下抑制が不十分であった。比較例４では（Ａ）成分および（Ｃ）成分の配合量が本発明規定の範囲から外れているので、高湿度および低湿度環境での柔軟性が不十分であった。
The tissue papers coated with the compositions 1 to 13, which are sanitary paper softeners of Examples 1 to 13, are all excellent in terms of softness in high-humidity and low-humidity environments, suppression of paper strength reduction, and usability. It was.
On the other hand, since the component (C) was not contained in Comparative Examples 1 and 2, flexibility and usability in a low humidity environment were insufficient. In Comparative Example 3, since the polyhydric alcohol to which no alkylene oxide was added was used in place of the component (B), the reduction in paper strength was insufficient. In Comparative Example 4, since the blending amounts of the component (A) and the component (C) are out of the range defined in the present invention, the flexibility in high and low humidity environments was insufficient.
Claims (2)
（Ｂ）オキシアルキレン基の炭素数が２〜３であり、アルキレンオキシドの平均付加モル数が５〜３０であり、かつ価数が３〜６の多価アルコールから形成されたポリオキシアルキレン多価アルコール、および
（Ｃ）炭素数１０〜２２のアシル基を有するショ糖脂肪酸エステルを含有し、
（Ａ）成分と（Ｂ）成分と（Ｃ）成分の合計含有量を１００質量部としたとき、（Ａ）成分の含有量が９０〜９９．７質量部、（Ｂ）成分の含有量が０．２〜５質量部、（Ｃ）成分の含有量が０．１〜５質量部である衛生紙用柔軟剤。 (A) glycerin,
(B) The polyoxyalkylene polyvalent formed from a polyhydric alcohol having 2 to 3 carbon atoms in the oxyalkylene group, an average added mole number of alkylene oxide of 5 to 30, and a valence of 3 to 6 An alcohol, and (C) a sucrose fatty acid ester having an acyl group having 10 to 22 carbon atoms,
When the total content of the component (A), the component (B), and the component (C) is 100 parts by mass, the content of the component (A) is 90 to 99.7 parts by mass, and the content of the component (B) is A softener for sanitary paper, having a content of 0.2 to 5 parts by mass and a component (C) of 0.1 to 5 parts by mass.