JP2014206686A - Pattern forming method, actinic ray-sensitive or radiation-sensitive resin composition, actinic ray-sensitive or radiation-sensitive film, manufacturing method of electronic device and electronic device - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide a pattern forming method that is capable of improving resolution, dry etching resistance and depth of focus latitude(DOF) of a superfine pattern with 40 nm or less in line width, an actinic ray-sensitive or radiation-sensitive film, as well as an actinic ray-sensitive or radiation-sensitive resin composition used to form the actinic ray-sensitive or radiation-sensitive film, and to provide a manufacturing method of an electronic device including the pattern forming method and an electronic device.SOLUTION: A pattern forming method comprises the steps of: (i) forming an actinic ray-sensitive or radiation-sensitive film with 80 nm or less in film thickness by using (A) a resin that has at least one of repeating units(a) having polycyclic aromatic structure and that increases its dissolution rate to an alkali developer by the action of an acid, and (B) an actinic ray-sensitive or radiation-sensitive resin composition that contains a compound generating an acid by irradiation of an actinic ray or radiation; (ii) exposing the actinic ray-sensitive or radiation-sensitive film; and (iii) developing the exposed actinic ray-sensitive or radiation-sensitive film.

Description

  The present invention relates to an actinic ray-sensitive or radiation-sensitive resin composition and a pattern forming method using the same. More specifically, the present invention relates to an actinic ray-sensitive or radiation-sensitive resin composition suitably used for ultra-microlithography processes such as the production of VLSI and high-capacity microchips, and other photofabrication processes, and The present invention relates to the pattern forming method used. In particular, the present invention relates to an actinic ray-sensitive or radiation-sensitive resin composition particularly suitable when an ArF excimer laser or a KrF excimer laser is used as an irradiation source, and a pattern forming method using the same.

  The present invention also relates to an actinic ray-sensitive or radiation-sensitive film using the composition, an electronic device manufacturing method including the pattern forming method, and an electronic device manufactured by the method.

  Conventionally, in the manufacturing process of semiconductor devices such as IC and LSI, fine processing by lithography using a photoresist composition has been performed. In recent years, with the high integration of integrated circuits, the formation of ultrafine patterns in the submicron region and the quarter micron region has been required. Along with this, there is a tendency to shorten the exposure wavelength from g-line to i-line and further to KrF excimer laser light.

  As a resist composition for KrF exposure, a resist composition containing a resin having polyhydroxystyrene as a basic skeleton has been developed. As such a resin, for example, a copolymer of hydroxystyrene and a monomer containing an adamantyl group is known (see, for example, Patent Document 1).

  On the other hand, as a resist composition exposed mainly by an ArF light source, a composition containing a resin not containing an aromatic ring has been developed. As such a composition, for example, a composition containing a resin having a specific lactone structure is known (see, for example, Patent Document 2). Resist compositions containing a resin containing a lactone structure and an aromatic ring have also been developed (see, for example, Patent Documents 3 and 4).

  However, in the above resist composition, when an ultrafine pattern having a line width of 40 nm or less is formed, further improvement is required for resolution, dry etching resistance, and depth of focus (DOF). ing.

US Patent Application Publication No. 2007/0121390 JP 2008-031298 A JP 2012-173367 A JP 2009-035675 A

  An object of the present invention is to solve the problem of the technology for improving performance in microfabrication of a semiconductor device using actinic rays or radiation, particularly ArF excimer laser light. In particular, the object of the present invention is to provide a pattern forming method, actinic ray sensitive or radiation sensitive film capable of improving the resolution, dry etching resistance and depth of focus latitude (DOF) of ultrafine patterns having a line width of 40 nm or less. The present invention also provides an actinic ray-sensitive or radiation-sensitive resin composition used for forming the actinic ray-sensitive or radiation-sensitive film. Furthermore, the objective of this invention is providing the manufacturing method of an electronic device, and an electronic device.

  As a result of intensive studies to solve the above problems, the present inventors have completed the invention exemplified below.

[1] (i) (A) a resin containing at least one repeating unit (a) having a polycyclic aromatic structure, which increases the dissolution rate in an alkali developer by the action of an acid, and (B) active light or Forming an actinic ray-sensitive or radiation-sensitive film having a thickness of 80 nm or less using an actinic ray-sensitive or radiation-sensitive resin composition containing a compound that generates an acid upon irradiation with radiation;
(Ii) A pattern forming method including the step of exposing the actinic ray-sensitive or radiation-sensitive film, and (iii) developing the exposed actinic ray-sensitive or radiation-sensitive film.

  [2] The pattern forming method according to [1], wherein the resin (A) further contains an acid-decomposable repeating unit having a group that is decomposed by the action of an acid.

  [3] The pattern forming method according to [1] or [2], wherein the polycyclic aromatic structure of the repeating unit (a) is a naphthalene structure.

[4] The pattern forming method according to [3], wherein the repeating unit (a) is a repeating unit represented by the following general formula (Ia).

In general formula (Ia),
A ₁ represents a hydrogen atom, an alkyl group, a halogen atom, or a cyano group.
L ₁ represents a single bond or a divalent linking group.
Y represents a monovalent substituent.
n represents an integer of 0 to 7. When n is 2 or more, a plurality of Y may be the same or different.

[5] The pattern forming method according to [4], wherein the repeating unit (a) is a repeating unit represented by the following general formula (IIa).

In general formula (IIa),
A ₁ represents a hydrogen atom, an alkyl group, a halogen atom, or a cyano group.
L ₂ represents a single bond or a divalent linking group.
Y represents a monovalent substituent.
n represents an integer of 0 to 7. When n is 2 or more, a plurality of Y may be the same or different.

[6] The pattern forming method according to [5], wherein L ₂ in the general formula (IIa) is an alkylene group having 1 to 20 carbon atoms or a cycloalkylene group having 3 to 20 carbon atoms.

[7] The pattern forming method according to any one of [2] to [6], wherein the resin (A) contains a repeating unit represented by the following general formula (I) as the acid-decomposable repeating unit. .

In general formula (I),
R ₁ represents a hydrogen atom, a methyl group which may have a substituent, or a group represented by —CH ₂ —R ₁₁ . R ₁₁ represents a monovalent organic group.
R ₂ represents an alkyl group or a cycloalkyl group.
R represents an atomic group necessary for forming an alicyclic structure together with the carbon atom to which R ₂ is bonded.

  [8] The pattern forming method according to [7], wherein the alicyclic structure of the general formula (I) is a monocyclic alicyclic structure.

[9] (B) The compound that generates an acid upon irradiation with actinic rays or radiation is a compound represented by the following general formula (ZI-3) or (ZI-4): The pattern formation method of any one of Claims 1.

In general formula (ZI-3),
R _{1c to} R _5c are each independently a hydrogen atom, alkyl group, cycloalkyl group, aryl group, alkoxy group, aryloxy group, alkoxycarbonyl group, alkylcarbonyloxy group, cycloalkylcarbonyloxy group, halogen atom, hydroxyl group Represents a nitro group, an alkylthio group or an arylthio group.
R _6c and R _7c each independently represents a hydrogen atom, an alkyl group, a cycloalkyl group, a halogen atom, a cyano group or an aryl group.
R _x and R _y each independently represents an alkyl group, a cycloalkyl group, a 2-oxoalkyl group, a 2-oxocycloalkyl group, an alkoxycarbonylalkyl group, an allyl group, or a vinyl group.
Any two or more of R _{1c to} R _5c , R _5c and R _6c , R _6c and R _7c , R _5c and R _x , and R _x and R _y are bonded to each other to form a ring structure It may be formed.
Z ⁻ represents a non-nucleophilic anion.

In general formula (ZI-4),
R ₁₃ represents a hydrogen atom, a fluorine atom, a hydroxyl group, an alkyl group, a cycloalkyl group, an alkoxy group, an alkoxycarbonyl group, or a group having a cycloalkyl group.
When there are a plurality of R _{14 s,} each independently represents a group having a hydroxyl group, an alkyl group, a cycloalkyl group, an alkoxy group, an alkoxycarbonyl group, an alkylcarbonyl group, an alkylsulfonyl group, a cycloalkylsulfonyl group, or a cycloalkyl group. Represent.
R ₁₅ each independently represents an alkyl group, a cycloalkyl group or a naphthyl group. Two R ₁₅ may be bonded to each other to form a ring.
l represents an integer of 0-2.
r represents an integer of 0 to 8.
Z ⁻ represents a non-nucleophilic anion.

[10] (B) The compound that generates an acid upon irradiation with actinic rays or radiation is a compound that generates an acid represented by the following general formula (IIIB) or (IVB) upon irradiation with an actinic ray or radiation. The pattern forming method according to any one of [1] to [9].

In the general formula (IIIB),
Xf each independently represents a fluorine atom or an alkyl group substituted with at least one fluorine atom.
R ₁ and R ₂ each independently represents a hydrogen atom or an alkyl group.
When a plurality of L's are present, each independently represents a divalent linking group.
Cy represents a cyclic organic group.
x represents an integer of 1 to 20.
y represents an integer of 0 to 10.
z represents an integer of 0 to 10.

In the general formula (IVB),
Xf each independently represents a fluorine atom or an alkyl group substituted with at least one fluorine atom.
R ₁ and R ₂ each independently represents a hydrogen atom or an alkyl group.
When a plurality of L's are present, each independently represents a divalent linking group.
Cy represents a cyclic organic group.
Rf represents a group containing a fluorine atom.
x represents an integer of 1 to 20.
y represents an integer of 0 to 10.
z represents an integer of 0 to 10.

[11] The pattern forming method according to any one of [1] to [10], wherein the exposure is performed using an ArF excimer laser.
[12] The pattern forming method according to [11], wherein the exposure is performed through an immersion liquid.

[13] A method for manufacturing an electronic device, comprising the pattern forming method according to any one of [1] to [12].
[14] An electronic device manufactured by the method for manufacturing an electronic device according to [13].

  [15] (A) A resin containing at least one repeating unit (a) having a polycyclic aromatic structure, which increases the dissolution rate in an alkaline developer by the action of an acid, and (B) irradiation with actinic rays or radiation An actinic ray-sensitive or radiation-sensitive film having a film thickness of 80 nm or less, comprising an actinic ray-sensitive or radiation-sensitive resin composition containing a compound that generates an acid.

  [16] An actinic ray-sensitive or radiation-sensitive resin composition used for forming an actinic ray-sensitive or radiation-sensitive film having a thickness of 80 nm or less, and (A) a repeating unit having a polycyclic aromatic structure An actinic ray-sensitive or sensation containing a resin containing at least one kind of (a) that increases the dissolution rate in an alkaline developer by the action of an acid, and (B) a compound that generates an acid upon irradiation with active rays or radiation Radiation resin composition.

  According to the present invention, a pattern forming method, an actinic ray sensitive or radiation sensitive film capable of improving resolution, dry etching resistance, and depth of focus latitude (DOF) of an ultrafine pattern having a line width of 40 nm or less, An actinic ray-sensitive or radiation-sensitive resin composition used for forming an actinic ray-sensitive or radiation-sensitive film, an electronic device manufacturing method, and an electronic device can be provided.

Hereinafter, embodiments of the present invention will be described in detail.
In the description of the group (atomic group) in this specification, the description which does not describe substitution and non-substitution includes what does not have a substituent and what has a substituent. For example, the “alkyl group” includes not only an alkyl group having no substituent (unsubstituted alkyl group) but also an alkyl group having a substituent (substituted alkyl group).

  In the present invention, “active light” or “radiation” means, for example, an emission line spectrum of a mercury lamp, a deep ultraviolet ray represented by an excimer laser, an extreme ultraviolet ray (EUV light), an X-ray, an electron beam, an ion beam or other particle beam. Means. In the present invention, “light” means actinic rays or radiation.

  In addition, the term “exposure” in the present specification is not limited to exposure to far ultraviolet rays, X-rays, extreme ultraviolet rays (EUV light) and the like represented by mercury lamps and excimer lasers. It is also assumed that drawing by particle beams such as.

  The pattern forming method according to the present invention includes (A) a resin containing a repeating unit having a polycyclic aromatic structure and having increased solubility in an alkaline developer by the action of an acid (hereinafter also referred to as “resin (A)”). , (B) an actinic ray-sensitive or radiation-sensitive resin containing a compound that generates an acid upon irradiation with actinic rays or radiation (hereinafter also referred to as “compound (B)” or “acid generator (B)”) Applying the composition onto a substrate to form an actinic ray-sensitive or radiation-sensitive film having a thickness of 80 nm or less.

  The present inventors apply an actinic ray-sensitive or radiation-sensitive resin composition containing the resin (A) on a substrate to form an actinic ray-sensitive or radiation-sensitive film having a thickness of 80 nm or less. Thus, it has been found that the resolution and dry etching resistance of an ultrafine pattern having a line width of 40 nm or less can be improved. The mechanism of the effect is not clear, but is estimated as follows.

  When forming an ultrafine line and space pattern with a line width of 40 nm or less, the ratio of the pattern height to the length of the substrate contact portion (aspect ratio) increases, so that the pattern tends to collapse and the pattern cannot be resolved. It was. On the other hand, resolution can be ensured by reducing the film thickness, but in the case of a resist containing a resin composed of an alicyclic group not having an aromatic group, which is usually used for ArF exposure, is dry-etched. Since the resistance is insufficient and the substrate cannot be processed, it is difficult to achieve both.

  For this problem, an actinic ray-sensitive or radiation-sensitive resin composition containing a resin (A) containing a repeating unit having a polycyclic aromatic structure is used, and the film thickness of the photosensitive layer formed from this composition is 80 nm. By making it below, it is possible to sufficiently transmit 193 nm light, which is the wavelength of the ArF exposure light source, and to ensure resolution by reducing the aspect ratio of the pattern. Since it has a group ring structure, the dry etching resistance can be improved, and it is considered that the resolution and the dry etching resistance can be made compatible.

  First, the actinic ray-sensitive or radiation-sensitive resin composition (hereinafter also referred to as “the composition of the present invention”) used in the pattern forming method of the present invention will be described, and then the pattern forming method will be described.

<Actinic ray-sensitive or radiation-sensitive resin composition>
As described above, the composition of the present invention comprises (A) a resin containing at least one repeating unit (a) having a polycyclic aromatic structure, which has an increased dissolution rate in an alkaline developer by the action of an acid, and (B) The compound which generate | occur | produces an acid by irradiation of actinic light or a radiation is contained. In one form, the composition of the present invention may further contain at least one of a hydrophobic resin, a basic compound, a solvent, a surfactant, and other additives. Hereinafter, each component will be described.

[1] Resin (A) whose dissolution rate in an alkaline developer is increased by the action of an acid
<Repeating unit (a) having a polycyclic aromatic structure>
The resin (A) contains a repeating unit (a) having a polycyclic aromatic structure. The polycyclic aromatic structure of the repeating unit (a) is a condensed polycyclic aromatic structure in which at least two or more ring structures are condensed. For example, two or more single aromatic rings such as bisphenol are present. A ring assembly structure connected by a single bond or a linking group is not included. In addition, the polycyclic aromatic structure may be a structure in which an aromatic ring and a non-aromatic ring are condensed, as well as a ring in which all condensed rings are aromatic rings such as naphthalene. The polycyclic aromatic structure may be a heterocyclic system containing a heteroatom such as O, N, or S. In one embodiment of the present invention, the polycyclic aromatic structure is preferably a condensed polycyclic aromatic structure which may contain a heteroatom having 2 or 3 rings.

Examples of the polycyclic aromatic structure in the repeating unit (a) include the structures shown below.

  In one embodiment of the present invention, among the above specific examples, a naphthalene structure, a carbazole structure, and an indole structure are preferable, and a naphthalene structure is more preferable.

  The polycyclic aromatic structure in the repeating unit (a) may have a substituent, and preferred substituents include, for example, an alkyl group having 1 to 8 carbon atoms, a cycloalkyl group having 4 to 10 carbon atoms, Examples thereof include an alkoxy group having 1 to 8 carbon atoms, an alkoxycarbonyl group having 2 to 8 carbon atoms, a carboxyl group, a halogen atom, a hydroxyl group, and a cyano group. More preferably, they are a C1-C4 alkyl group and a C1-C8 alkoxy group. When there are two or more substituents, the plural substituents may be the same or different, and the plural substituents may be bonded to form a ring.

  Examples of the alkyl group having 1 to 8 carbon atoms as a substituent that the polycyclic aromatic structure may have include, for example, a methyl group, an ethyl group, a propyl group, an isopropyl group, an n-butyl group, an isobutyl group, and a t-butyl group. , A pentyl group, a hexyl group, an octyl group and the like, and these may further have a substituent. Moreover, as a C4-C10 cycloalkyl group, a cyclopentyl group, a cyclohexyl group, etc. are mentioned, for example, These may have a substituent further. Examples of the alkoxy group having 1 to 8 carbon atoms include a methoxy group and an ethoxy group, and these may further have a substituent. Examples of the alkoxy group contained in the alkoxycarbonyl group having 2 to 8 carbon atoms include a methoxy group and an ethoxy group, and these may further have a substituent. Examples of the halogen atom include a fluorine atom, a chlorine atom, a bromine atom and an iodine atom, and a fluorine atom is preferable.

  As will be described later, the resin (A) may contain a repeating unit having an acid-decomposable group. However, when the repeating unit contains a polycyclic aromatic structure and an acid-decomposable group, the repeating unit is used in the present invention. The unit is treated as a repeating unit (a) having a polycyclic aromatic structure.

In one embodiment of the present invention, a preferable structure of the repeating unit (a) having a polycyclic aromatic structure includes a structure represented by the following general formula (Ia).

In general formula (Ia),
A ₁ represents a hydrogen atom, an alkyl group, a halogen atom or a cyano group. Examples of the alkyl group include a methyl group and an ethyl group.

L ₁ represents a single bond or a divalent linking group. Examples of the divalent linking group include a group selected from the group consisting of an alkylene group, a cycloalkylene group, an ether bond, a thioether bond, a carbonyl group, an ester bond, an amide bond, a urethane bond, and a urea bond, or these two groups. And a group in which two or more are combined. As the combined linking group, for example, a linking group formed by combining an alkylene group, an ether bond and a carbonyl group is preferable.

  Y represents a monovalent substituent. Examples of the monovalent substituent include the same specific examples as those given as specific examples of the substituent that the polycyclic aromatic structure may have in the description of the polycyclic aromatic structure described above. .

  n represents an integer of 0 to 7, preferably an integer of 0 to 2. When n is 2 or more, a plurality of Y may be the same or different.

In one embodiment of the present invention, the repeating unit (a) having a polycyclic aromatic structure is more preferably a structure represented by the following general formula (IIa).

In general formula (IIa),
A _1, Y and n have the same meanings as _A 1, Y and n in the general formula (Ia).
L ₂ represents a single bond or a divalent linking group. Examples of the divalent linking group include the same specific examples as listed above as specific examples of the divalent linking group represented by L ₁ in the general formula (Ia).

In one embodiment of the present invention, L ₂ is preferably an alkylene group having 1 to 20 carbon atoms or a cycloalkylene group having 3 to 20 carbon atoms. L ₂ is more preferably an alkylene group having 1 to 5 carbon atoms.

The total content of repeating units (a) having a polycyclic aromatic structure is preferably 1 to 35 mol%, and preferably 2 to 30 mol%, based on all repeating units in the resin (A). More preferably, it is more preferably 5 to 25 mol%.
Specific examples of the repeating unit (a) are shown below, but are not limited thereto.

<Acid-decomposable repeating unit>
In addition to the repeating unit (a) having a polycyclic aromatic structure, the resin (A) preferably further contains an acid-decomposable repeating unit having a group that decomposes by the action of an acid.

The resin (A) is preferably insoluble or hardly soluble in an alkali developer.
The group that the acid-decomposable repeating unit decomposes by the action of an acid is a group that decomposes by the action of an acid to generate an alkali-soluble group (hereinafter also referred to as “acid-decomposable group”). It is preferable to have a structure protected with a group capable of decomposing and leaving an alkali-soluble group by the action of an acid.

  Alkali-soluble groups include phenolic hydroxyl groups, carboxyl groups, fluorinated alcohol groups, sulfonic acid groups, sulfonamido groups, sulfonylimide groups, (alkylsulfonyl) (alkylcarbonyl) methylene groups, (alkylsulfonyl) (alkylcarbonyl) imides. Group, bis (alkylcarbonyl) methylene group, bis (alkylcarbonyl) imide group, bis (alkylsulfonyl) methylene group, bis (alkylsulfonyl) imide group, tris (alkylcarbonyl) methylene group, tris (alkylsulfonyl) methylene group, etc. Is mentioned.

  Preferred alkali-soluble groups include carboxyl groups, fluorinated alcohol groups (preferably hexafluoroisopropanol groups), and sulfonic acid groups.

  A preferable group as the acid-decomposable group is a group obtained by substituting the hydrogen atom of these alkali-soluble groups with a group capable of leaving with an acid.

As the acid eliminable group, there can be, for _{example, -C (R 36) (R} 37) (R 38), - C (R 36) (R 37) (OR 39), - C (R 01) (R 02 ) (OR ₃₉ ) and the like.

In the formula, R _{36 to} R ₃₉ each independently represents an alkyl group, a cycloalkyl group, an aryl group, an aralkyl group, or an alkenyl group. R ₃₆ and R ₃₇ may be bonded to each other to form a ring.

R ₀₁ and R ₀₂ each independently represents a hydrogen atom, an alkyl group, a cycloalkyl group, an aryl group, an aralkyl group or an alkenyl group.

  The acid-decomposable group is preferably a cumyl ester group, an enol ester group, an acetal ester group, a tertiary alkyl ester group or the like. More preferably, it is a tertiary alkyl ester group.

The repeating unit having an acid-decomposable group that can be contained in the resin (A) is preferably a repeating unit represented by the following general formula (AI).

In general formula (AI),
Xa ₁ represents a hydrogen atom or an alkyl group which may have a substituent.
T represents a single bond or a divalent linking group.
Rx _{1 to} Rx ₃ each independently represents an alkyl group (straight or branched) or a cycloalkyl group (monocyclic or polycyclic).
Two of Rx _{1 to} Rx ₃ may combine to form a cycloalkyl group (monocyclic or polycyclic).

Examples of the alkyl group which may have a substituent represented by Xa ₁ include a group represented by a methyl group or —CH ₂ —R ₁₁ . R ₁₁ represents a halogen atom (such as a fluorine atom) hydroxyl group or a monovalent organic group, and examples thereof include an alkyl group having 5 or less carbon atoms and an acyl group having 5 or less carbon atoms, preferably 3 or less carbon atoms. An alkyl group, more preferably a methyl group. In one embodiment, Xa ₁ is preferably a hydrogen atom, a methyl group, a trifluoromethyl group, a hydroxymethyl group, or the like.

Examples of the divalent linking group for T include an alkylene group, —COO—Rt— group, —O—Rt— group, and the like. In the formula, Rt represents an alkylene group or a cycloalkylene group.
T is preferably a single bond or a —COO—Rt— group. Rt is preferably an alkylene group having 1 to 5 carbon atoms, more preferably a —CH ₂ — group, — (CH ₂ ) ₂ — group, or — (CH ₂ ) ₃ — group.

Examples of the alkyl group rx ₁ to Rx _3, methyl, ethyl, n- propyl group, an isopropyl group, n- butyl group, an isobutyl group, those having 1 to 4 carbon atoms such as t- butyl group.

Examples of the cycloalkyl group represented by Rx _{1 to} Rx ₃ include monocyclic cycloalkyl groups such as cyclopentyl group and cyclohexyl group, polycyclic cycloalkyl groups such as norbornyl group, tetracyclodecanyl group, tetracyclododecanyl group, and adamantyl group. Groups are preferred.
Examples of the cycloalkyl group formed by combining two of Rx _{1 to} Rx ₃ include a monocyclic cycloalkyl group such as a cyclopentyl group and a cyclohexyl group, a norbornyl group, a tetracyclodecanyl group, a tetracyclododecanyl group, an adamantyl group A polycyclic cycloalkyl group such as a group is preferred. A monocyclic cycloalkyl group having 5 to 6 carbon atoms is particularly preferable.

The cycloalkyl group formed by combining two of Rx _{1 to} Rx ₃ is, for example, a group in which one of the methylene groups constituting the ring has a heteroatom such as an oxygen atom or a heteroatom such as a carbonyl group It may be replaced with.

The repeating unit represented by the general formula (AI) preferably has, for example, an embodiment in which Rx ₁ is a methyl group or an ethyl group, and Rx ₂ and Rx ₃ are bonded to form the above-described cycloalkyl group.

  Each of the above groups may have a substituent. Examples of the substituent include an alkyl group (1 to 4 carbon atoms), a halogen atom, a hydroxyl group, an alkoxy group (1 to 4 carbon atoms), a carboxyl group, An alkoxycarbonyl group (C2-C6) etc. are mentioned, C8 or less is preferable.

  Specifically, specific examples disclosed in US2012 / 0135348 A1 [0265] can be used, but the present invention is not limited thereto.

Resin (A) has as a repeating unit represented by general formula (AI) at least any one of the repeating unit represented by general formula (I) and the repeating unit represented by general formula (II), for example. More preferably, it is a resin.

In formulas (I) and (II),
R ₁ and R ₃ each independently represent a hydrogen atom, a methyl group which may have a substituent, or a group represented by —CH ₂ —R ₁₁ . R ₁₁ represents a monovalent organic group.
R ₂ , R ₄ , R ₅ and R ₆ each independently represents an alkyl group or a cycloalkyl group.
R represents an atomic group necessary for forming an alicyclic structure together with the carbon atom to which R ₂ is bonded.

R ₁ and R ₃ preferably represent a hydrogen atom, a methyl group, a trifluoromethyl group or a hydroxymethyl group. Specific examples and preferred examples of the monovalent organic group in R ₁₁ are the same as those described for R ₁₁ in formula (AI).

The alkyl group in R ₂ may be linear or branched, and may have a substituent.
The cycloalkyl group in R ₂ may be monocyclic or polycyclic and may have a substituent.

R ₂ is preferably an alkyl group, more preferably an alkyl group having 1 to 10 carbon atoms, still more preferably 1 to 5 carbon atoms, and examples thereof include a methyl group and an ethyl group.

R represents an atomic group necessary for forming an alicyclic structure together with a carbon atom. The alicyclic structure formed by R together with the carbon atom is preferably a monocyclic alicyclic structure, and the carbon number thereof is preferably 3 to 7, more preferably 5 or 6.
R ₃ is preferably a hydrogen atom or a methyl group, and more preferably a methyl group.

The alkyl group in R ₄ , R ₅ , and R ₆ may be linear or branched and may have a substituent. As the alkyl group, those having 1 to 4 carbon atoms such as methyl group, ethyl group, n-propyl group, isopropyl group, n-butyl group, isobutyl group and t-butyl group are preferable.

The cycloalkyl group in R ₄ , R ₅ and R ₆ may be monocyclic or polycyclic and may have a substituent. The cycloalkyl group is preferably a monocyclic cycloalkyl group such as a cyclopentyl group or a cyclohexyl group, or a polycyclic cycloalkyl group such as a norbornyl group, a tetracyclodecanyl group, a tetracyclododecanyl group or an adamantyl group.

  Examples of the substituent that each of the above groups may have include the same groups as those described above as the substituent that each of the groups in the general formula (AI) may have.

  The acid-decomposable resin is a resin containing a repeating unit represented by the general formula (I) and a repeating unit represented by the general formula (II) as the repeating unit represented by the general formula (AI). More preferred.

  In another embodiment, a resin containing at least two kinds of repeating units represented by the general formula (I) as the repeating unit represented by the general formula (AI) is more preferable. When two or more repeating units of the general formula (I) are included, the alicyclic structure formed by R together with the carbon atom is a monocyclic alicyclic structure, and the alicyclic structure formed by R together with the carbon atom. It is preferable that both the repeating unit which is a polycyclic alicyclic structure is included. The monocyclic alicyclic structure preferably has 5 to 8 carbon atoms, more preferably 5 or 6 carbon atoms, and particularly preferably 5 carbon atoms. As the polycyclic alicyclic structure, a norbornyl group, a tetracyclodecanyl group, a tetracyclododecanyl group, and an adamantyl group are preferable.

  One type of repeating unit having an acid-decomposable group contained in the resin (A) may be used, or two or more types may be used in combination. When used in combination, specific examples disclosed in US2012 / 0135348 A1 [0287] can be used, but the present invention is not limited thereto.

  The total content of the repeating units having an acid-decomposable group is preferably 20 to 80 mol%, more preferably 25 to 75 mol%, based on all repeating units in the resin (A). More preferably, it is -70 mol%.

  In one embodiment, the resin (A) preferably contains a repeating unit having a cyclic carbonate structure. This cyclic carbonate structure is a structure having a ring including a bond represented by —O—C (═O) —O— as an atomic group constituting the ring. The ring containing a bond represented by —O—C (═O) —O— as the atomic group constituting the ring is preferably a 5- to 7-membered ring, and most preferably a 5-membered ring. Such a ring may be condensed with another ring to form a condensed ring.

  The resin (A) preferably contains a repeating unit having a lactone structure or a sultone (cyclic sulfonate ester) structure.

Any lactone group or sultone group can be used as long as it has a lactone structure or sultone structure, but a lactone structure or sultone structure having a 5- to 7-membered ring is preferable, and a lactone having a 5- to 7-membered ring is preferable. A structure in which another ring structure is condensed to form a bicyclo structure or a spiro structure in the structure or sultone structure is preferable. A lactone structure represented by any one of the general formulas (LC1-1) to (LC1-17) and the following general formulas (SL1-1) and (SL1-2) disclosed in US2012 / 0135348 A1 [0318] It is more preferable to have a repeating unit having a sultone structure. A lactone structure or a sultone structure may be directly bonded to the main chain. Preferred lactone structures or sultone structures are (LC1-1), (LC1-4), (LC1-5), (LC1-8), and more preferably (LC1-4). By using a specific lactone structure or sultone structure, LWR and development defects are improved.

The lactone structure portion or the sultone structure portion may or may not have a substituent (Rb ₂ ). When n ₂ is 2 or more, a plurality of substituents (Rb ₂ ) may be the same or different, and a plurality of substituents (Rb ₂ ) may be bonded to form a ring. .

The resin (A) preferably contains a repeating unit having a lactone structure or a sultone structure represented by the following general formula (III).

In formula (III),
A represents an ester bond (a group represented by —COO—) or an amide bond (a group represented by —CONH—).
R ₀ independently represents an alkylene group, a cycloalkylene group, or a combination thereof when there are a plurality of R ₀ .
Z is independently a single bond, an ether bond, an ester bond, an amide bond, or a urethane bond when there are a plurality of Zs.

Or urea bond

Represents. Here, R represents a hydrogen atom, an alkyl group, a cycloalkyl group, or an aryl group each independently.

R ₈ represents a monovalent organic group having a lactone structure or a sultone structure.
n _is the repetition number of the structure represented by -R 0 -Z-, represents an integer of 0 to 2.
R ₇ represents a hydrogen atom, a halogen atom or an alkyl group.

The alkylene group and cycloalkylene group represented by R ₀ may have a substituent.
Z is preferably an ether bond or an ester bond, and particularly preferably an ester bond.

The alkyl group for R ₇ is preferably an alkyl group having 1 to 4 carbon atoms, more preferably a methyl group or an ethyl group, and particularly preferably a methyl group. The alkylene group of R ₀ , the cycloalkylene group, and the alkyl group in R ₇ may each be substituted. Examples of the substituent include a halogen atom such as a fluorine atom, a chlorine atom, and a bromine atom, a mercapto group, and a hydroxy group. Group, alkoxy group such as methoxy group, ethoxy group, isopropoxy group, t-butoxy group and benzyloxy group, and acetoxy group such as acetyloxy group and propionyloxy group. R ₇ is preferably a hydrogen atom, a methyl group, a trifluoromethyl group, or a hydroxymethyl group.

A preferable chain alkylene group in R ₀ is preferably a chain alkylene group having 1 to 10 carbon atoms, more preferably 1 to 5 carbon atoms, and examples thereof include a methylene group, an ethylene group, and a propylene group. . A preferable cycloalkylene group is a cycloalkylene group having 3 to 20 carbon atoms, and examples thereof include a cyclohexylene group, a cyclopentylene group, a norbornylene group, and an adamantylene group. In order to exhibit the effect of the present invention, a chain alkylene group is more preferable, and a methylene group is particularly preferable.

The monovalent organic group having a lactone structure or a sultone structure represented by R ₈ is not limited as long as it has a lactone structure or a sultone structure, and the general formula (LC1-1) described above as a specific example A lactone structure or a sultone structure represented by ~ (LC1-17), (SL1-1) and (SL1-2) is exemplified, and a structure represented by (LC1-4) is particularly preferable. Further, n ₂ in (LC1-1) to (LC1-17), (SL1-1) and (SL1-2) is more preferably 2 or less.
R ₈ is preferably a monovalent organic group having an unsubstituted lactone structure or sultone structure, or a monovalent organic group having a lactone structure or sultone structure having a methyl group, a cyano group or an alkoxycarbonyl group as a substituent. A monovalent organic group having a lactone structure (cyanolactone) or a sultone structure (cyanosultone) having a cyano group as a substituent is more preferable.

In general formula (III), it is preferable that n is 1 or 2.
A is preferably an ester bond.
Z is preferably a single bond.

  Specific examples of the repeating unit having a group having a lactone structure or a sultone structure represented by the general formula (III) include the repeating units disclosed in US2012 / 0135348 A1 [0305]. It is not limited to this.

  The content of the repeating unit represented by the general formula (III) is preferably 15 to 60 mol%, more preferably 20 to 60 mol in total with respect to all repeating units in the resin (A) when plural types are contained. %, More preferably 30 to 50 mol%.

  The resin (A) may also contain a repeating unit having the above-mentioned lactone structure or sultone structure in addition to the unit represented by the general formula (III).

  Specific examples of the repeating unit having a lactone group or a sultone group include the repeating units disclosed in US2012 / 0135348 A1 [0325] to [0328] in addition to the specific examples given above. It is not limited to these.

  In order to enhance the effect of the present invention, two or more kinds of lactone or sultone repeating units selected from general formula (III) can be used in combination. When using together, it is preferable to select and use 2 or more types from the lactone or sultone repeating unit in which n is 1 in general formula (III).

The resin (A) preferably has a repeating unit having a hydroxyl group or a cyano group other than the general formulas (AI) and (III). This improves the substrate adhesion and developer compatibility. The repeating unit having a hydroxyl group or a cyano group is preferably a repeating unit having an alicyclic hydrocarbon structure substituted with a hydroxyl group or a cyano group, and preferably has no acid-decomposable group. The alicyclic hydrocarbon structure in the alicyclic hydrocarbon structure substituted with a hydroxyl group or a cyano group is preferably an adamantyl group, a diamantyl group, or a norbornane group. As the alicyclic hydrocarbon structure substituted with a preferred hydroxyl group or cyano group, partial structures represented by the following general formulas (VIIa) to (VIId) are preferred.

In general formulas (VIIa) to (VIIc),
R ₂ c to R ₄ c each independently represents a hydrogen atom, a hydroxyl group, or a cyano group. However, at least one of R ₂ c to R ₄ c represents a hydroxyl group or a cyano group. Preferably, one or two of R ₂ c to R ₄ c are a hydroxyl group and the rest are hydrogen atoms. In general formula (VIIa), more preferably, _two of R ₂ c to R ₄ c are a hydroxyl group and the rest are hydrogen atoms.

Examples of the repeating unit having a partial structure represented by the general formulas (VIIa) to (VIId) include the repeating units represented by the following general formulas (AIIa) to (AIId).

In the general formulas (AIIa) to (AIId),
R ₁ c represents a hydrogen atom, a methyl group, a trifluoromethyl group, or a hydroxymethyl group.

R ₂ c to R ₄ c are in the general formula (VIIa) ~ _(VIIc), same meanings as R 2 c~R ₄ c.

  The content of the repeating unit having a hydroxyl group or a cyano group is preferably from 5 to 40 mol%, more preferably from 5 to 30 mol%, still more preferably from 10 to 25 mol%, based on all repeating units in the resin (A).

  Specific examples of the repeating unit having a hydroxyl group or a cyano group include the repeating units disclosed in US2012 / 0135348 A1 [0340], but the present invention is not limited thereto.

  The resin (A) used in the actinic ray-sensitive or radiation-sensitive resin composition of the present invention may have a repeating unit having an alkali-soluble group. Examples of the alkali-soluble group include a carboxyl group, a sulfonamide group, a sulfonylimide group, a bissulfonylimide group, and an aliphatic alcohol (for example, hexafluoroisopropanol group) substituted with an electron-withdrawing group at the α-position. It is more preferable to have a repeating unit. By containing the repeating unit having an alkali-soluble group, the resolution in contact hole applications is increased. The repeating unit having an alkali-soluble group includes a repeating unit in which an alkali-soluble group is directly bonded to the main chain of the resin, such as a repeating unit of acrylic acid or methacrylic acid, or an alkali in the main chain of the resin through a linking group. Either a repeating unit to which a soluble group is bonded, or a polymerization initiator or chain transfer agent having an alkali-soluble group is used at the time of polymerization and introduced at the end of the polymer chain. Both are preferable, and the linking group is monocyclic or polycyclic. It may have a cyclic hydrocarbon structure. Particularly preferred are repeating units of acrylic acid or methacrylic acid.

  As for content of the repeating unit which has an alkali-soluble group, 0-20 mol% is preferable with respect to all the repeating units in resin (A), More preferably, it is 3-15 mol%, More preferably, it is 5-10 mol%.

Specific examples of the repeating unit having an alkali-soluble group include the repeating unit disclosed in US2012 / 0135348 A1 [0344], but the present invention is not limited thereto.
The resin (A) of the present invention further has an alicyclic hydrocarbon structure that does not have a polar group (for example, the alkali-soluble group, hydroxyl group, cyano group, etc.) and has a repeating unit that does not exhibit acid decomposability. it can. Examples of such a repeating unit include a repeating unit represented by the general formula (IV).

In the general formula (IV), R ₅ represents a hydrocarbon group having at least one cyclic structure and having no polar group.
Ra represents a hydrogen atom, an alkyl group, or a —CH ₂ —O—Ra ₂ group. In the formula, Ra ₂ represents a hydrogen atom, an alkyl group, or an acyl group. Ra is preferably a hydrogen atom, a methyl group, a hydroxymethyl group or a trifluoromethyl group, particularly preferably a hydrogen atom or a methyl group.

The cyclic structure possessed by R ₅ includes a monocyclic hydrocarbon group and a polycyclic hydrocarbon group. Examples of the monocyclic hydrocarbon group include a cycloalkenyl group having 3 to 12 carbon atoms such as a cyclopentyl group, a cyclohexyl group, a cycloheptyl group, a cyclooctyl group, and the like, and a cyclohexenyl group. Groups. The preferred monocyclic hydrocarbon group is a monocyclic hydrocarbon group having 3 to 7 carbon atoms, more preferably a cyclopentyl group or a cyclohexyl group.

The polycyclic hydrocarbon group includes a ring assembly hydrocarbon group and a bridged cyclic hydrocarbon group, and examples of the ring assembly hydrocarbon group include a bicyclohexyl group and a perhydronaphthalenyl group. As the bridged cyclic hydrocarbon ring, for example, bicyclic such as pinane, bornane, norpinane, norbornane, bicyclooctane ring (bicyclo [2.2.2] octane ring, bicyclo [3.2.1] octane ring, etc.) And hydrocarbon rings and tricyclic hydrocarbon rings such as adamantane, tricyclo [5.2.1.0 ^2,6 ] decane, tricyclo [4.3.1.1 ^2,5 ] undecane ring, and the like.

Preferred examples of the bridged cyclic hydrocarbon ring include a norbornyl group, an adamantyl group, a bicyclooctanyl group, a tricyclo [5,2,1,0 ^2,6 ] decanyl group, and the like. More preferable examples of the bridged cyclic hydrocarbon ring include a norbornyl group and an adamantyl group.

  These alicyclic hydrocarbon groups may have a substituent. Preferred examples of the substituent include a halogen atom, an alkyl group, a hydroxyl group substituted with a hydrogen atom, and an amino group substituted with a hydrogen atom. It is done.

  The resin (A) has an alicyclic hydrocarbon structure having no polar group, and may or may not contain a repeating unit that does not exhibit acid decomposability. The content of is preferably from 1 to 40 mol%, more preferably from 2 to 20 mol%, based on all repeating units in the resin (A).

Specific examples of the repeating unit having an alicyclic hydrocarbon structure having no polar group and not exhibiting acid decomposability include the repeating units disclosed in US2012 / 0135348 A1 [0354]. Is not limited to these.
The resin (A) used in the composition of the present invention has a resolving power that is a general necessary characteristic of a resist, in addition to the above repeating structural unit, dry etching resistance, standard developer suitability, substrate adhesion, resist profile, and the like. It can have various repeating structural units for the purpose of adjusting heat resistance, sensitivity and the like.

  Examples of such repeating structural units include, but are not limited to, repeating structural units corresponding to the following monomers.

  Thereby, performance required for the resin used in the composition of the present invention, in particular, (1) solubility in coating solvent, (2) film-forming property (glass transition point), (3) alkali developability, (4 Fine adjustments such as () film slippage (selection of hydrophilicity / hydrophobicity, alkali-soluble group), (5) adhesion of unexposed part to substrate, (6) dry etching resistance, etc. are possible.

  As such a monomer, for example, a compound having one addition polymerizable unsaturated bond selected from acrylic acid esters, methacrylic acid esters, acrylamides, methacrylamides, allyl compounds, vinyl ethers, vinyl esters, etc. Etc.

  In addition, any addition-polymerizable unsaturated compound that can be copolymerized with monomers corresponding to the above various repeating structural units may be copolymerized.

  In the resin (A) used in the composition of the present invention, the molar ratio of each repeating structural unit is the resist dry etching resistance, standard developer suitability, substrate adhesion, resist profile, and general required performance of the resist. It is appropriately set to adjust the resolving power, heat resistance, sensitivity and the like.

  When the composition of the present invention is for ArF exposure, it is preferable that the resin (A) used in the composition of the present invention has substantially no aromatic group from the viewpoint of transparency to ArF light. . More specifically, the repeating unit having an aromatic group is preferably 5% by mole or less, more preferably 3% by mole or less, and more ideally, during the entire repetition of the resin (A). More preferably, it is 0 mol%, that is, it does not have a repeating unit having an aromatic group. The resin (A) preferably has a monocyclic or polycyclic alicyclic hydrocarbon structure.

  In addition, it is preferable that resin (A) does not contain a fluorine atom and a silicon atom from a compatible viewpoint with the hydrophobic resin mentioned later.

  The resin (A) used in the composition of the present invention is preferably one in which all of the repeating units are composed of (meth) acrylate-based repeating units. In this case, all of the repeating units are methacrylate repeating units, all of the repeating units are acrylate repeating units, or all of the repeating units are methacrylate repeating units and acrylate repeating units. Although it can be used, the acrylate-based repeating unit is preferably 50 mol% or less of the total repeating units. Moreover, the alicyclic hydrocarbon substituted by the (meth) acrylate type repeating unit 20-50 mol% which has an acid-decomposable group, the (meth) acrylate type repeating unit 20-50 mol% which has a lactone group, and a hydroxyl group or a cyano group. A copolymer containing 5 to 30 mol% of a (meth) acrylate-based repeating unit having a structure and further containing 0 to 20 mol% of another (meth) acrylate-based repeating unit is also preferred.

  The resin (A) in the present invention can be synthesized according to a conventional method (for example, radical polymerization). Specifically, the synthesis method disclosed in US2012 / 0164573 A1 [0126] to [0128] can be used.

  The weight average molecular weight of the resin (A) of the present invention is preferably 1,000 to 200,000, more preferably 2,000 to 20,000, still more preferably 3, as a polystyrene conversion value by GPC method. 000 to 15,000, particularly preferably 3,000 to 11,000. By setting the weight average molecular weight to 1,000 to 200,000, deterioration of heat resistance and dry etching resistance can be prevented, developability is deteriorated, and viscosity is increased, resulting in deterioration of film forming property. Can be prevented.

  The dispersity (molecular weight distribution) is usually 1.0 to 3.0, preferably 1.0 to 2.6, more preferably 1.0 to 2.0, and particularly preferably 1.4 to 2.0. Those in the range are used. The smaller the molecular weight distribution, the better the resolution and the resist shape, and the smoother the side wall of the resist pattern, the better the roughness.

In the present invention, the content of the resin (A) in the entire composition is preferably from 30 to 99 mass%, more preferably from 55 to 95 mass%, based on the total solid content.
In addition, the resins of the present invention may be used alone or in combination.

[2] Compound (B) that generates an acid upon irradiation with an actinic ray or radiation
The composition of the present invention contains a compound (B) that generates an acid upon irradiation with actinic rays or radiation (hereinafter also referred to as “acid generator” or “compound (B)”). The compound (B) is preferably a compound that generates an organic acid upon irradiation with actinic rays or radiation.

  The compound (B) may be in the form of a low molecular compound or may be in a form incorporated in a part of the polymer. Moreover, you may use together the form incorporated in a part of polymer and the form of a low molecular compound.

  When the compound (B) is in the form of a low molecular compound, the molecular weight is preferably 3000 or less, more preferably 2000 or less, and even more preferably 1000 or less.

  When the compound (B) is in a form incorporated in a part of the polymer, it may be incorporated in a part of the resin (A) described above or may be incorporated in a resin different from the resin (A). .

In the present invention, the compound (B) is preferably in the form of a low molecular compound.
Examples of the acid generator (B) include a photoinitiator for photocationic polymerization, a photoinitiator for photoradical polymerization, a photodecoloring agent for dyes, a photochromic agent, an actinic ray or Known compounds that generate an acid upon irradiation with radiation and mixtures thereof can be appropriately selected and used.
Examples thereof include diazonium salts, phosphonium salts, sulfonium salts, iodonium salts, imide sulfonates, oxime sulfonates, diazodisulfones, disulfones, and o-nitrobenzyl sulfonates.

Preferred examples of the acid generator (B) include compounds represented by the following general formulas (ZI), (ZII), and (ZIII).

In the general formula (ZI),
R ₂₀₁ , R ₂₀₂ and R ₂₀₃ each independently represents an organic group.
The carbon number of the organic group as R ₂₀₁ , R ₂₀₂ and R ₂₀₃ is generally 1 to 30, preferably 1 to 20.
Two of R _{201 to} R ₂₀₃ may be bonded to form a ring structure, and the ring may contain an oxygen atom, a sulfur atom, an ester bond, an amide bond, or a carbonyl group. Examples of the group formed by combining two of R _{201 to} R ₂₀₃ include an alkylene group (eg, butylene group, pentylene group).
Z ⁻ represents a non-nucleophilic anion.
Examples of the non-nucleophilic anion as Z ⁻ include a sulfonate anion, a carboxylate anion, a sulfonylimide anion, a bis (alkylsulfonyl) imide anion, and a tris (alkylsulfonyl) methyl anion.

  A non-nucleophilic anion is an anion that has an extremely low ability to cause a nucleophilic reaction, and is an anion that can suppress degradation over time due to an intramolecular nucleophilic reaction. Thereby, the temporal stability of the actinic ray-sensitive or radiation-sensitive resin composition is improved.

Examples of the sulfonate anion include an aliphatic sulfonate anion, an aromatic sulfonate anion, and a camphor sulfonate anion.
Examples of the carboxylate anion include an aliphatic carboxylate anion, an aromatic carboxylate anion, and an aralkylcarboxylate anion.

The aliphatic moiety in the aliphatic sulfonate anion and aliphatic carboxylate anion may be an alkyl group or a cycloalkyl group, preferably an alkyl group having 1 to 30 carbon atoms and a cyclohexane having 3 to 30 carbon atoms. An alkyl group,
The aromatic group in the aromatic sulfonate anion and aromatic carboxylate anion is preferably an aryl group having 6 to 14 carbon atoms such as a phenyl group, a tolyl group, and a naphthyl group.

  The alkyl group, cycloalkyl group and aryl group in the aliphatic sulfonate anion and aromatic sulfonate anion may have a substituent.

Examples of other non-nucleophilic anions include fluorinated phosphorus (for example, PF ₆ ⁻ ), fluorinated boron (for example, BF ₄ ⁻ ), fluorinated antimony and the like (for example, SbF ₆ ⁻ ). .

Examples of the non-nucleophilic anion of Z ⁻ include an aliphatic sulfonate anion in which at least α position of the sulfonic acid is substituted with a fluorine atom, an aromatic sulfonate anion substituted with a fluorine atom or a group having a fluorine atom, an alkyl group Is preferably a bis (alkylsulfonyl) imide anion substituted with a fluorine atom, or a tris (alkylsulfonyl) methide anion wherein an alkyl group is substituted with a fluorine atom. The non-nucleophilic anion is more preferably a perfluoroaliphatic sulfonic acid anion having 4 to 8 carbon atoms, a benzenesulfonic acid anion having a fluorine atom, still more preferably a nonafluorobutanesulfonic acid anion, a perfluorooctanesulfonic acid anion, It is a pentafluorobenzenesulfonic acid anion and 3,5-bis (trifluoromethyl) benzenesulfonic acid anion.

The acid generator (B) is preferably a compound that generates an acid represented by the following general formula (IIIB) or (IVB) upon irradiation with actinic rays or radiation. Since it is a compound that generates an acid represented by the following general formula (IIIB) or (IVB) and has a cyclic organic group, the resolution and roughness performance can be further improved.
The non-nucleophilic anion may be an anion that generates an organic acid represented by the following general formula (IIIB) or (IVB).

In the general formulas (IIIB) and (IVB),
Xf each independently represents a fluorine atom or an alkyl group substituted with at least one fluorine atom.
R ₁ and R ₂ each independently represents a hydrogen atom or an alkyl group.
When a plurality of L's are present, each independently represents a divalent linking group.
Cy represents a cyclic organic group.
Rf represents a group containing a fluorine atom.
x represents an integer of 1 to 20.
y represents an integer of 0 to 10.
z represents an integer of 0 to 10.

General formulas (IIIB) and (IVB) will be described in more detail.
Xf represents a fluorine atom or an alkyl group substituted with at least one fluorine atom. The alkyl group preferably has 1 to 10 carbon atoms, more preferably 1 to 4 carbon atoms. The alkyl group substituted with at least one fluorine atom is preferably a perfluoroalkyl group.
Xf is preferably a fluorine atom or a perfluoroalkyl group having 1 to 4 carbon atoms. Xf is more preferably a fluorine atom or CF ₃ . In particular, it is preferable that both Xf are fluorine atoms.

R ₁ and R ₂ are each independently a hydrogen atom or an alkyl group. The alkyl group as R ₁ and R ₂ may have a substituent, and preferably has 1 to 4 carbon atoms. R ₁ and R ₂ are preferably a hydrogen atom.

L represents a divalent linking group. Examples of the divalent linking group include —COO—, —OCO—, —CONH—, —NHCO—, —CO—, —O—, —S—, —SO—, —SO ₂ —, and an alkylene group. (Preferably having 1 to 6 carbon atoms), cycloalkylene group (preferably having 3 to 10 carbon atoms), alkenylene group (preferably having 2 to 6 carbon atoms) or a divalent linking group in which a plurality of these are combined. . Among them, -COO -, - OCO -, - CONH -, - NHCO -, - CO -, - O -, - SO 2 -, - COO- alkylene group -, - OCO- alkylene group -, - CONH- alkylene group - or -NHCO- alkylene group - are preferred, -COO -, - OCO -, - CONH -, - SO 2 -, - COO- alkylene group - or -OCO- alkylene group - is more preferable.

Cy represents a cyclic organic group. Examples of the cyclic organic group include an alicyclic group, an aryl group, and a heterocyclic group.
The alicyclic group may be monocyclic or polycyclic. Examples of the monocyclic alicyclic group include monocyclic cycloalkyl groups such as a cyclopentyl group, a cyclohexyl group, and a cyclooctyl group. Examples of the polycyclic alicyclic group include polycyclic cycloalkyl groups such as a norbornyl group, a tricyclodecanyl group, a tetracyclodecanyl group, a tetracyclododecanyl group, and an adamantyl group. Among these, an alicyclic group having a bulky structure having 7 or more carbon atoms, such as a norbornyl group, a tricyclodecanyl group, a tetracyclodecanyl group, a tetracyclododecanyl group, and an adamantyl group, is a PEB (heating after exposure) step. From the viewpoints of suppressing diffusibility in the film and improving MEEF (Mask Error Enhancement Factor).

The aryl group may be monocyclic or polycyclic. Examples of the aryl group include a phenyl group, a naphthyl group, a phenanthryl group, and an anthryl group. Among these, a naphthyl group having a relatively low light absorbance at 193 nm is preferable.
The heterocyclic group may be monocyclic or polycyclic, but the polycyclic group can suppress acid diffusion more. Moreover, the heterocyclic group may have aromaticity or may not have aromaticity. Examples of the heterocyclic ring having aromaticity include a furan ring, a thiophene ring, a benzofuran ring, a benzothiophene ring, a dibenzofuran ring, a dibenzothiophene ring, and a pyridine ring. Examples of the heterocyclic ring that does not have aromaticity include a tetrahydropyran ring, a lactone ring, a sultone ring, and a decahydroisoquinoline ring. As the heterocyclic ring in the heterocyclic group, a furan ring, a thiophene ring, a pyridine ring, or a decahydroisoquinoline ring is particularly preferable. Examples of the lactone ring and sultone ring include the lactone structure and sultone structure exemplified in the aforementioned resin (P).

  The cyclic organic group may have a substituent. Examples of the substituent include an alkyl group (which may be linear or branched, preferably 1 to 12 carbon atoms), and a cycloalkyl group (monocyclic, polycyclic or spirocyclic). Well, preferably having 3 to 20 carbon atoms), aryl group (preferably having 6 to 14 carbon atoms), hydroxyl group, alkoxy group, ester group, amide group, urethane group, ureido group, thioether group, sulfonamide group, and sulfonic acid An ester group is mentioned. The carbon constituting the cyclic organic group (carbon contributing to ring formation) may be a carbonyl carbon.

x is preferably 1 to 8, more preferably 1 to 4, and particularly preferably 1. y is preferably 0 to 4, and more preferably 0. z is preferably 0 to 8, more preferably 0 to 4, and still more preferably 1.
Examples of the group containing a fluorine atom represented by Rf include an alkyl group having at least one fluorine atom, a cycloalkyl group having at least one fluorine atom, and an aryl group having at least one fluorine atom. .

These alkyl group, cycloalkyl group and aryl group may be substituted with a fluorine atom, or may be substituted with another substituent containing a fluorine atom. When Rf is a cycloalkyl group having at least one fluorine atom or an aryl group having at least one fluorine atom, other substituents containing a fluorine atom include, for example, alkyl substituted with at least one fluorine atom. Groups.
Further, these alkyl group, cycloalkyl group and aryl group may be further substituted with a substituent not containing a fluorine atom. As this substituent, the thing which does not contain a fluorine atom among what was demonstrated about Cy previously can be mentioned, for example.

  Examples of the alkyl group having at least one fluorine atom represented by Rf include those described above as the alkyl group substituted with at least one fluorine atom represented by Xf. Examples of the cycloalkyl group having at least one fluorine atom represented by Rf include a perfluorocyclopentyl group and a perfluorocyclohexyl group. Examples of the aryl group having at least one fluorine atom represented by Rf include a perfluorophenyl group.

In the above general formula, a particularly preferred embodiment is an embodiment in which x is 1, 2 and Xf is a fluorine atom, y is 0 to 4, all R ₁ and R ₂ are hydrogen atoms, and z is 1. In such an embodiment, there are few fluorine atoms, it is difficult to be unevenly distributed on the surface when the resist film is formed, and it is easy to disperse uniformly in the resist film.

Examples of the organic group represented by R ₂₀₁ , R ₂₀₂ and R ₂₀₃ include the corresponding groups in the compounds (ZI-1), (ZI-2), (ZI-3) and (ZI-4) described later. Can be mentioned.
In addition, the compound which has two or more structures represented by general formula (ZI) may be sufficient. For example, at least one of R _{201 to} R ₂₀₃ of the compound represented by the general formula (ZI) is a single bond or at least one of R _{201 to} R ₂₀₃ of another compound represented by the general formula (ZI) It may be a compound having a structure bonded through a linking group.

Further preferred examples of the (ZI) component include compounds (ZI-1), (ZI-2), (ZI-3) and (ZI-4) described below.
The compound (ZI-1) is an arylsulfonium compound in which at least one of R _{201 to} R _{203 in} the general formula (ZI) is an aryl group, that is, a compound having arylsulfonium as a cation.

In the arylsulfonium compound, all of R _{201 to} R ₂₀₃ may be an aryl group, or a part of R _{201 to} R ₂₀₃ may be an aryl group, and the rest may be an alkyl group or a cycloalkyl group.
Examples of the arylsulfonium compound include triarylsulfonium compounds, diarylalkylsulfonium compounds, aryldialkylsulfonium compounds, diarylcycloalkylsulfonium compounds, and aryldicycloalkylsulfonium compounds.

The aryl group of the arylsulfonium compound is preferably a phenyl group or a naphthyl group, and more preferably a phenyl group. The aryl group may be an aryl group having a heterocyclic structure having an oxygen atom, a nitrogen atom, a sulfur atom or the like. Examples of the heterocyclic structure include a pyrrole residue, a furan residue, a thiophene residue, an indole residue, a benzofuran residue, and a benzothiophene residue. When the arylsulfonium compound has two or more aryl groups, the two or more aryl groups may be the same or different.
The alkyl group or cycloalkyl group that the arylsulfonium compound has as necessary is preferably a linear or branched alkyl group having 1 to 15 carbon atoms and a cycloalkyl group having 3 to 15 carbon atoms, such as a methyl group, Examples thereof include an ethyl group, a propyl group, an n-butyl group, a sec-butyl group, a t-butyl group, a cyclopropyl group, a cyclobutyl group, and a cyclohexyl group.

The aryl group, alkyl group and cycloalkyl group of R _{201 to} R ₂₀₃ are an alkyl group (for example, 1 to 15 carbon atoms), a cycloalkyl group (for example, 3 to 15 carbon atoms), an aryl group (for example, 6 to 14 carbon atoms). , An alkoxy group (for example, having 1 to 15 carbon atoms), a halogen atom, a hydroxyl group, or a phenylthio group may be substituted.

Next, the compound (ZI-2) will be described.
Compound (ZI-2) is a compound in which R _{201 to} R ₂₀₃ in formula (ZI) each independently represents an organic group having no aromatic ring. Here, the aromatic ring includes an aromatic ring containing a hetero atom.
The organic group not containing an aromatic ring as R _{201 to} R ₂₀₃ generally has 1 to 30 carbon atoms, preferably 1 to 20 carbon atoms.
R _{201 to} R ₂₀₃ are each independently preferably an alkyl group, a cycloalkyl group, an allyl group, or a vinyl group, more preferably a linear or branched 2-oxoalkyl group, 2-oxocycloalkyl group, alkoxy group. A carbonylmethyl group, particularly preferably a linear or branched 2-oxoalkyl group.

As the alkyl group and cycloalkyl group of R _{201 to} R ₂₀₃ , a linear or branched alkyl group having 1 to 10 carbon atoms (for example, a methyl group, an ethyl group, a propyl group, a butyl group, a pentyl group), carbon Examples thereof include cycloalkyl groups of several 3 to 10 (cyclopentyl group, cyclohexyl group, norbornyl group).

R _{201 to} R ₂₀₃ may be further substituted with a halogen atom, an alkoxy group (eg, having 1 to 5 carbon atoms), a hydroxyl group, a cyano group, or a nitro group.

Next, the compound (ZI-3) will be described.
The compound (ZI-3) is a compound represented by the following general formula (ZI-3), and is a compound having a phenacylsulfonium salt structure.

In general formula (ZI-3),
R _{1c to} R _5c are each independently a hydrogen atom, alkyl group, cycloalkyl group, aryl group, alkoxy group, aryloxy group, alkoxycarbonyl group, alkylcarbonyloxy group, cycloalkylcarbonyloxy group, halogen atom, hydroxyl group Represents a nitro group, an alkylthio group or an arylthio group.
R _6c and R _7c each independently represents a hydrogen atom, an alkyl group, a cycloalkyl group, a halogen atom, a cyano group or an aryl group.
R _x and R _y each independently represents an alkyl group, a cycloalkyl group, a 2-oxoalkyl group, a 2-oxocycloalkyl group, an alkoxycarbonylalkyl group, an allyl group, or a vinyl group.

Any two or more of R _{1c to} R _5c , R _5c and R _6c , R _6c and R _7c , R _5c and R _x , and R _x and R _y may be bonded to form a ring structure. The ring structure may include an oxygen atom, a sulfur atom, a ketone group, an ester bond, and an amide bond.

  Examples of the ring structure include an aromatic or non-aromatic hydrocarbon ring, an aromatic or non-aromatic heterocycle, or a polycyclic fused ring formed by combining two or more of these rings. Examples of the ring structure include 3- to 10-membered rings, preferably 4- to 8-membered rings, and more preferably 5- or 6-membered rings.

Examples of the group formed by combining any two or more of R _{1c to} R _5c , R _6c and R _7c , and R _x and R _y include a butylene group and a pentylene group.
The group formed by combining R _5c and R _6c and R _5c and R _x is preferably a single bond or an alkylene group, and examples of the alkylene group include a methylene group and an ethylene group. .
Z ^- represents a non-nucleophilic anion, in the general formula (ZI) Z ^- and include the same non-nucleophilic anion.

Specific examples of the alkoxy group in the alkoxycarbonyl group as R _1c to R _5c are the same as specific examples of the alkoxy group of _R 1c _{to R 5c.}
Specific examples of the alkyl group in the alkylcarbonyloxy group and alkylthio group as R _1c to R _5c are the same as specific examples of the alkyl group of _R 1c _{to R 5c.}
Specific examples of the cycloalkyl group in the cycloalkyl carbonyl group as R _1c to R _5c are the same as specific examples of the cycloalkyl group of _R 1c _{to R 5c.}
Specific examples of the aryl group in the aryloxy group and arylthio group as R _1c to R _5c are the same as specific examples of the aryl group of _R 1c _{to R 5c.}

  Examples of the cation in the compound (ZI-2) or (ZI-3) in the present invention include cations described in paragraph [0036] and thereafter of US Patent Application Publication No. 2012/0076996.

Next, the compound (ZI-4) will be described.
The compound (ZI-4) is represented by the following general formula (ZI-4).

In general formula (ZI-4),
R ₁₃ represents a hydrogen atom, a fluorine atom, a hydroxyl group, an alkyl group, a cycloalkyl group, an alkoxy group, an alkoxycarbonyl group, or a group having a cycloalkyl group. These groups may have a substituent.
When there are a plurality of R _{14 s,} each independently represents a group having a hydroxyl group, an alkyl group, a cycloalkyl group, an alkoxy group, an alkoxycarbonyl group, an alkylcarbonyl group, an alkylsulfonyl group, a cycloalkylsulfonyl group, or a cycloalkyl group. Represent. These groups may have a substituent.
R ₁₅ each independently represents an alkyl group, a cycloalkyl group or a naphthyl group. These groups may have a substituent. Two R ₁₅ may be bonded to each other to form a ring. When two R ₁₅ are bonded to each other to form a ring, the ring skeleton may contain a hetero atom such as an oxygen atom or a nitrogen atom. In one embodiment, it is preferred that two R ₁₅ are alkylene groups and are bonded to each other to form a ring structure.

l represents an integer of 0-2.
r represents an integer of 0 to 8.
Z ^- represents a non-nucleophilic anion, in the general formula (ZI) Z ^- and include the same non-nucleophilic anion.

In the general formula (ZI-4), the alkyl group of R ₁₃ , R ₁₄ and R ₁₅ is linear or branched and preferably has 1 to 10 carbon atoms, and is preferably a methyl group, an ethyl group, n -A butyl group, a t-butyl group, etc. are preferable.

  Examples of the cation of the compound represented by the general formula (ZI-4) in the present invention include paragraphs [0121], [0123], [0124] of JP2010-256842A, and JP2011-76056A. The cations described in paragraphs [0127], [0129], and [0130] of the above.

Next, general formulas (ZII) and (ZIII) will be described.
In general formulas (ZII) and (ZIII),
R ₂₀₄ to R ₂₀₇ each independently represents an aryl group, an alkyl group or a cycloalkyl group.
The aryl group for R _{204 to} R ₂₀₇ is preferably a phenyl group or a naphthyl group, and more preferably a phenyl group. The aryl group of R _{204 to} R ₂₀₇ may be an aryl group having a heterocyclic structure having an oxygen atom, a nitrogen atom, a sulfur atom, or the like. Examples of the skeleton of the aryl group having a heterocyclic structure include pyrrole, furan, thiophene, indole, benzofuran, and benzothiophene.
The alkyl group and cycloalkyl group in R _{204 to} R ₂₀₇ are preferably a linear or branched alkyl group having 1 to 10 carbon atoms (for example, methyl group, ethyl group, propyl group, butyl group, pentyl group), carbon Examples thereof include cycloalkyl groups of several 3 to 10 (cyclopentyl group, cyclohexyl group, norbornyl group).

The aryl group, alkyl group, and cycloalkyl group of R _{204 to} R ₂₀₇ may have a substituent. Aryl group, alkyl group of R ₂₀₄ to R _207, the cycloalkyl group substituent which may be possessed by, for example, an alkyl group (for example, 1 to 15 carbon atoms), a cycloalkyl group (for example, 3 to 15 carbon atoms ), An aryl group (for example, having 6 to 15 carbon atoms), an alkoxy group (for example, having 1 to 15 carbon atoms), a halogen atom, a hydroxyl group, and a phenylthio group.

Z ⁻ represents a non-nucleophilic anion, and examples thereof include the same as the non-nucleophilic anion of Z ^{− in} formula (ZI).
Examples of the acid generator (B) further include compounds represented by the following general formulas (ZIV), (ZV), and (ZVI).

In general formulas (ZIV) to (ZVI),
Ar ₃ and Ar ₄ each independently represents an aryl group.
R ₂₀₈ , R ₂₀₉ and R ₂₁₀ each independently represents an alkyl group, a cycloalkyl group or an aryl group.
A represents an alkylene group, an alkenylene group or an arylene group.

Specific examples of the aryl group of Ar ₃ , Ar ₄ , R ₂₀₈ , R ₂₀₉ and R ₂₁₀ are the same as the specific examples of the aryl group as R ₂₀₁ , R ₂₀₂ and R ₂₀₃ in the general formula (ZI-1). Things can be mentioned.
Specific examples of the alkyl group and cycloalkyl group represented by R ₂₀₈ , R _209, and R ₂₁₀ include specific examples of the alkyl group and cycloalkyl group represented by R ₂₀₁ , R _202, and R ₂₀₃ in the general formula (ZI-2), respectively. The same thing as an example can be mentioned.

  The alkylene group of A is alkylene having 1 to 12 carbon atoms (for example, methylene group, ethylene group, propylene group, isopropylene group, butylene group, isobutylene group, etc.), and the alkenylene group of A is 2 to 2 carbon atoms. 12 alkenylene groups (for example, ethenylene group, propenylene group, butenylene group, etc.), and as the arylene group for A, arylene groups having 6 to 10 carbon atoms (for example, phenylene group, tolylene group, naphthylene group, etc.) Can be mentioned.

  Among the acid generators (B), particularly preferred examples include compounds exemplified in US2012 / 0207978A1 [0143].

The acid generator (B) can be synthesized by a known method, for example, according to the method described in JP-A No. 2007-161707.
An acid generator (B) can be used individually by 1 type or in combination of 2 or more types.

The content of the compound (B) that generates an acid upon irradiation with actinic rays or radiation is 0.1 to 30% by mass based on the total solid content of the actinic ray-sensitive or radiation-sensitive resin composition. More preferably, it is 0.5-25 mass%, More preferably, it is 3-20 mass%, Most preferably, it is 3-15 mass%.
Moreover, when an acid generator (B) is represented by the said general formula (ZI-3) or (ZI-4), the content rate is 5-35 mass on the basis of the total solid of a composition. % Is preferable, 8 to 30% by mass is more preferable, 9 to 30% by mass is further preferable, and 9 to 25% by mass is particularly preferable.

[3] Acid Diffusion Control Agent The actinic ray-sensitive or radiation-sensitive resin composition of the present invention preferably contains an acid diffusion control agent. The acid diffusion controller acts as a quencher that traps the acid generated from the acid generator or the like. Examples of the acid diffusion controller include a basic compound, a low molecular compound having a nitrogen atom and having a group capable of leaving by the action of an acid, a basic compound whose basicity is reduced or disappeared by irradiation with actinic rays or radiation, and an acid. An onium salt that is a weak acid relative to the generator can be used. These acid diffusion control agents may be used alone or in combination of two or more. For example, different types of acid diffusion control agents may be used in combination, such as a basic compound and an onium salt that is a weak acid relative to the acid generator.

[3-1] Basic compound The basic compound is preferably a compound having a structure represented by the following formulas (A) to (E).

In general formulas (A) and (E),
R ²⁰⁰ , R ²⁰¹ and R ²⁰² may be the same or different and are a hydrogen atom, an alkyl group (preferably having 1 to 20 carbon atoms), a cycloalkyl group (preferably having 3 to 20 carbon atoms) or an aryl group (having a carbon number). 6-20), wherein R ²⁰¹ and R ²⁰² may combine with each other to form a ring.

R ²⁰³ , R ²⁰⁴ , R ²⁰⁵ and R ²⁰⁶ may be the same or different and each represents an alkyl group having 1 to 20 carbon atoms.
About the said alkyl group, as an alkyl group which has a substituent, a C1-C20 aminoalkyl group, a C1-C20 hydroxyalkyl group, or a C1-C20 cyanoalkyl group is preferable.
The alkyl groups in the general formulas (A) and (E) are more preferably unsubstituted.

  Preferable basic compounds include guanidine, aminopyrrolidine, pyrazole, pyrazoline, piperazine, aminomorpholine, aminoalkylmorpholine, piperidine, and more preferable compounds include imidazole structure, diazabicyclo structure, onium hydroxide structure, onium Examples thereof include a compound having a carboxylate structure, a trialkylamine structure, an aniline structure or a pyridine structure, an alkylamine derivative having a hydroxyl group and / or an ether bond, and an aniline derivative having a hydroxyl group and / or an ether bond.

  Specific examples of preferable basic compounds include compounds exemplified in US2012 / 0219913A1 [0379].

  Preferred examples of the basic compound further include an amine compound having a phenoxy group, an ammonium salt compound having a phenoxy group, an amine compound having a sulfonic acid ester group, and an ammonium salt compound having a sulfonic acid ester group.

As the amine compound, a primary, secondary or tertiary amine compound can be used, and an amine compound in which at least one alkyl group is bonded to a nitrogen atom is preferable. The amine compound is more preferably a tertiary amine compound. As long as at least one alkyl group (preferably having 1 to 20 carbon atoms) is bonded to a nitrogen atom, the amine compound has an cycloalkyl group (preferably having 3 to 20 carbon atoms) or an aryl group (preferably having 3 to 20 carbon atoms). Preferably C6-C12) may be bonded to a nitrogen atom. The amine compound preferably has an oxygen atom in the alkyl chain and an oxyalkylene group is formed. The number of oxyalkylene groups is 1 or more, preferably 3 to 9, more preferably 4 to 6 in the molecule. Among the oxyalkylene groups, an oxyethylene group (—CH ₂ CH ₂ O—) or an oxypropylene group (—CH (CH ₃ ) CH ₂ O— or —CH ₂ CH ₂ CH ₂ O—) is preferable, and more preferably oxy Ethylene group.

As the ammonium salt compound, a primary, secondary, tertiary, or quaternary ammonium salt compound can be used, and an ammonium salt compound in which at least one alkyl group is bonded to a nitrogen atom is preferable. As long as at least one alkyl group (preferably having 1 to 20 carbon atoms) is bonded to a nitrogen atom, the ammonium salt compound has a cycloalkyl group (preferably having 3 to 20 carbon atoms) or an aryl group in addition to the alkyl group. (Preferably having 6 to 12 carbon atoms) may be bonded to a nitrogen atom. The ammonium salt compound preferably has an oxygen atom in the alkyl chain and an oxyalkylene group is formed. The number of oxyalkylene groups is 1 or more, preferably 3 to 9, more preferably 4 to 6 in the molecule. Among the oxyalkylene groups, an oxyethylene group (—CH ₂ CH ₂ O—) or an oxypropylene group (—CH (CH ₃ ) CH ₂ O— or —CH ₂ CH ₂ CH ₂ O—) is preferable, and more preferably oxy Ethylene group.

  Examples of the anion of the ammonium salt compound include halogen atoms, sulfonates, borates, and phosphates. Among them, halogen atoms and sulfonates are preferable.

The following compounds are also preferable as the basic compound.

  As basic compounds, in addition to the above-mentioned compounds, JP 2011-22560 A [0180] to [0225], JP 2012-137735 A [0218] to [0219], International Publication Pamphlet WO 2011/158687 A1 [ [0416] to [0438] can also be used.

  These basic compounds may be used individually by 1 type, and may be used in combination of 2 or more types.

  The composition of the present invention may or may not contain a basic compound, but when it is contained, the content of the basic compound is based on the solid content of the actinic ray-sensitive or radiation-sensitive resin composition. Usually, it is 0.001-10 mass%, Preferably it is 0.01-5 mass%.

  The use ratio of the acid generator (including the acid generator (A ′)) and the basic compound in the composition is preferably acid generator / basic compound (molar ratio) = 2.5 to 300. That is, the molar ratio is preferably 2.5 or more from the viewpoint of sensitivity and resolution, and is preferably 300 or less from the viewpoint of suppressing resolution from being reduced due to the thickening of the resist pattern over time until post-exposure heat treatment. The acid generator / basic compound (molar ratio) is more preferably 5.0 to 200, still more preferably 7.0 to 150.

[3-2] A low molecular compound having a nitrogen atom and having a group capable of leaving by the action of an acid A low molecular compound having a nitrogen atom and having a group capable of leaving by the action of an acid (hereinafter referred to as “compound (C ) ”Is preferably an acetal group, a carbonate group, a carbamate group, a tertiary ester group, a tertiary hydroxyl group or a hemiaminal ether group as the group capable of leaving by the action of an acid. Particularly preferred is an ether group.

  The molecular weight of the compound (C) having a group capable of leaving by the action of an acid is preferably 100 to 1000, more preferably 100 to 700, and particularly preferably 100 to 500.

  As the compound (C), an amine derivative having a group capable of leaving by the action of an acid on the nitrogen atom is preferable.

Compound (C) may have a carbamate group having a protecting group on the nitrogen atom. The protecting group constituting the carbamate group can be represented by the following general formula (d-1).

In general formula (d-1),
Rb each independently represents a hydrogen atom, an alkyl group (preferably 1 to 10 carbon atoms), a cycloalkyl group (preferably 3 to 30 carbon atoms), an aryl group (preferably 3 to 30 carbon atoms), an aralkyl group ( Preferably it represents C1-C10) or an alkoxyalkyl group (preferably C1-C10). Rb may be connected to each other to form a ring.

  The alkyl group, cycloalkyl group, aryl group, and aralkyl group represented by Rb are substituted with a functional group such as hydroxyl group, cyano group, amino group, pyrrolidino group, piperidino group, morpholino group, oxo group, alkoxy group, or halogen atom. It may be. The same applies to the alkoxyalkyl group represented by Rb.

  Rb is preferably a linear or branched alkyl group, cycloalkyl group, or aryl group. More preferably, it is a linear or branched alkyl group or cycloalkyl group.

  Examples of the ring formed by connecting two Rb to each other include an alicyclic hydrocarbon group, an aromatic hydrocarbon group, a heterocyclic hydrocarbon group, or a derivative thereof.

  Specific examples of the structure represented by the general formula (d-1) include, but are not limited to, the structures disclosed in US2012 / 0135348 A1 [0466].

It is particularly preferable that the compound (C) has a structure represented by the following general formula (6).

  In the general formula (6), Ra represents a hydrogen atom, an alkyl group, a cycloalkyl group, an aryl group, or an aralkyl group. When l is 2, two Ras may be the same or different, and two Ras may be connected to each other to form a heterocyclic ring together with the nitrogen atom in the formula. The heterocyclic ring may contain a hetero atom other than the nitrogen atom in the formula.

Rb has the same meaning as Rb in formula (d-1), and preferred examples are also the same.
l represents an integer of 0 to 2, m represents an integer of 1 to 3, and satisfies l + m = 3.

  In the general formula (6), the alkyl group, cycloalkyl group, aryl group and aralkyl group as Ra are described above as the groups in which the alkyl group, cycloalkyl group, aryl group and aralkyl group as Rb may be substituted. It may be substituted with a group similar to the group.

  Specific examples of the alkyl group, cycloalkyl group, aryl group, and aralkyl group of Ra (these alkyl group, cycloalkyl group, aryl group, and aralkyl group may be substituted with the above groups) include: The same group as the specific example mentioned above about Rb is mentioned.

  Specific examples of the particularly preferred compound (C) in the present invention include, but are not limited to, compounds disclosed in US2012 / 0135348 A1 [0475].

  The compound represented by the general formula (6) can be synthesized based on JP2007-298869A, JP2009-199021A, and the like.

  In the present invention, the low molecular compound (C) having a group capable of leaving by the action of an acid on the nitrogen atom can be used singly or in combination of two or more.

  The content of the compound (C) in the actinic ray-sensitive or radiation-sensitive resin composition of the present invention is preferably 0.001 to 20% by mass, more preferably based on the total solid content of the composition. It is 0.001-10 mass%, More preferably, it is 0.01-5 mass%.

[3-3] Basic compounds whose basicity decreases or disappears upon irradiation with actinic rays or radiation Basic compounds whose basicity decreases or disappears upon irradiation with actinic rays or radiation have a proton acceptor functional group In addition, the compound is decomposed by irradiation with actinic rays or radiation, and the proton acceptor property is lowered, disappears, or changes from proton acceptor property to acidity. Hereinafter, it is also referred to as compound (PA).

The proton acceptor functional group is a group that can interact electrostatically with a proton or a functional group having an electron. For example, a functional group having a macrocyclic structure such as a cyclic polyether or a π-conjugated group. It means a functional group having a nitrogen atom with an unshared electron pair that does not contribute. The nitrogen atom having an unshared electron pair that does not contribute to π conjugation is, for example, a nitrogen atom having a partial structure represented by the following general formula.

  Examples of a preferable partial structure of the proton acceptor functional group include a crown ether, an azacrown ether, a primary to tertiary amine, a pyridine, an imidazole, and a pyrazine structure.

  The compound (PA) is decomposed by irradiation with an actinic ray or radiation to generate a compound in which the proton acceptor property is lowered, disappeared, or changed from proton acceptor property to acidity. Here, the decrease or disappearance of the proton acceptor property or the change from the proton acceptor property to the acid is a change in the proton acceptor property caused by the addition of a proton to the proton acceptor functional group. Means that when a proton adduct is formed from a compound having a proton acceptor functional group (PA) and a proton, the equilibrium constant in the chemical equilibrium is reduced.

  Proton acceptor property can be confirmed by measuring pH.

  In the present invention, the acid dissociation constant pKa of the compound generated by decomposition of the compound (PA) upon irradiation with actinic rays or radiation preferably satisfies pKa <−1, more preferably −13 <pKa <−1. And more preferably −13 <pKa <−3.

  In the present invention, the acid dissociation constant pKa represents the acid dissociation constant pKa in an aqueous solution. For example, Chemical Handbook (II) (4th revised edition, 1993, edited by the Chemical Society of Japan, Maruzen Co., Ltd.) It shows that acid strength is so large that this value is low. Specifically, the acid dissociation constant pKa in an aqueous solution can be measured by measuring an acid dissociation constant at 25 ° C. using an infinitely diluted aqueous solution, and using the following software package 1, Hammett The values based on the substituent constants and the database of known literature values can also be obtained by calculation. The values of pKa described in this specification all indicate values obtained by calculation using this software package.

  Software package 1: Advanced Chemistry Development (ACD / Labs) Software V8.14 for Solaris (1994-2007 ACD / Labs).

The compound (PA) generates, for example, a compound represented by the following general formula (PA-1) as the proton adduct generated by decomposition upon irradiation with actinic rays or radiation. The compound represented by the general formula (PA-1) has an acidic group as well as a proton acceptor functional group, so that the proton acceptor property is reduced or disappeared compared to the compound (PA), or from the proton acceptor property. It is a compound that has changed to acidic.

In general formula (PA-1),
Q _represents -SO 3 H, _-CO 2 H, or _-W 1 _NHW 2 _{R f.} Here, R _f represents an alkyl group, a cycloalkyl group, or an aryl group, and W ₁ and W ₂ each independently represent —SO ₂ — or —CO—.
A represents a single bond or a divalent linking group.
X represents —SO ₂ — or —CO—.
n represents 0 or 1.
B represents a single bond, an oxygen atom, or —N (R _x ) R _y —. Here, R _x represents a hydrogen atom or a monovalent organic group, and R _y represents a single bond or a divalent organic group. R _x may be bonded to R _y to form a ring, or R _x may be bonded to R to form a ring.
R represents a monovalent organic group having a proton acceptor functional group.

General formula (PA-1) is demonstrated still in detail.
The divalent linking group in A is preferably a divalent linking group having 2 to 12 carbon atoms, and examples thereof include an alkylene group and a phenylene group. More preferably, it is an alkylene group having at least one fluorine atom, and a preferable carbon number is 2 to 6, more preferably 2 to 4. The alkylene chain may have a linking group such as an oxygen atom or a sulfur atom. The alkylene group is particularly preferably an alkylene group in which 30 to 100% of the number of hydrogen atoms are substituted with fluorine atoms, and more preferably, the carbon atom bonded to the Q site has a fluorine atom. Further, a perfluoroalkylene group is preferable, and a perfluoroethylene group, a perfluoropropylene group, and a perfluorobutylene group are more preferable.

  The monovalent organic group in Rx preferably has 1 to 30 carbon atoms, and examples thereof include an alkyl group, a cycloalkyl group, an aryl group, an aralkyl group, and an alkenyl group. These groups may further have a substituent.

  The alkyl group in Rx may have a substituent, preferably a linear or branched alkyl group having 1 to 20 carbon atoms, and has an oxygen atom, a sulfur atom, or a nitrogen atom in the alkyl chain. May be.

  Preferred examples of the divalent organic group for Ry include an alkylene group.

  Examples of the ring structure which Rx and Ry may be bonded to each other include a 5- to 10-membered ring containing a nitrogen atom, particularly preferably a 6-membered ring.

  The proton acceptor functional group in R is as described above, and examples thereof include azacrown ether, primary to tertiary amines, groups having a heterocyclic aromatic structure containing nitrogen such as pyridine and imidazole.

  As the organic group having such a structure, a preferable carbon number is 4 to 30, and examples thereof include an alkyl group, a cycloalkyl group, an aryl group, an aralkyl group, and an alkenyl group.

  The alkyl group, the cycloalkyl group, the aryl group, the aralkyl group, the alkyl group in the alkenyl group, the cycloalkyl group, the aryl group, the aralkyl group, and the alkenyl group in R include a proton acceptor functional group or an ammonium group. Are the same as the alkyl group, cycloalkyl group, aryl group, aralkyl group and alkenyl group mentioned above.

  When B is -N (Rx) Ry-, R and Rx are preferably bonded to each other to form a ring. By forming the ring structure, the stability is improved, and the storage stability of the composition using the ring structure is improved. The number of carbon atoms forming the ring is preferably 4 to 20, and may be monocyclic or polycyclic, and may contain an oxygen atom, a sulfur atom, or a nitrogen atom in the ring.

  Examples of the monocyclic structure include a 4-membered ring, a 5-membered ring, a 6-membered ring, a 7-membered ring, and an 8-membered ring containing a nitrogen atom. Examples of the polycyclic structure include a structure composed of a combination of two or three or more monocyclic structures.

As _{R f} in _-X 1 NHX ₂ R _f represented by Q, preferred is an alkyl group which may have a fluorine atom having 1 to 6 carbon atoms, more preferably perfluoroalkyl of 1 to 6 carbon atoms It is a group. Further, as X ₁ and X ₂ , at least one is preferably —SO ₂ —, and more preferably, both X ₁ and X ₂ are —SO ₂ —.

Q is particularly preferably —SO ₃ H or —CO ₂ H from the viewpoint of the hydrophilicity of the acid group.
Among the compounds represented by the general formula (PA-1), a compound in which the Q site is a sulfonic acid can be synthesized by using a general sulfonamidation reaction. For example, a method in which one sulfonyl halide part of a bissulfonyl halide compound is selectively reacted with an amine compound to form a sulfonamide bond, and then the other sulfonyl halide part is hydrolyzed, or a cyclic sulfonic acid anhydride is used. It can be obtained by a method of ring-opening by reacting with an amine compound.

The compound (PA) is preferably an ionic compound. The proton acceptor functional group may be contained in either the anion portion or the cation portion, but is preferably contained in the anion portion.
Preferred examples of the compound (PA) include compounds represented by the following general formulas (4) to (6).

In the general formulas (4) to (6), A, X, n, B, R, Rf, X ₁ and X ₂ have the same meanings as those in the general formula (PA-1).
C ⁺ represents a counter cation.
The counter cation is preferably an onium cation. More specifically, the sulfonium cation described as S ⁺ (R ₂₀₁ ) (R ₂₀₂ ) (R ₂₀₃ ) in general formula (ZI) in the acid generator described later, I ⁺ (R ₂₀₄ in general formula (ZII)) ) The iodonium cation described as (R ₂₀₅ ) is a preferred example.
Hereinafter, specific examples of the compound (PA) include compounds exemplified in US2011 / 0269072A1 [0280].

Moreover, in this invention, compounds (PA) other than the compound which generate | occur | produces the compound represented by general formula (PA-1) can also be selected suitably. For example, an ionic compound that has a proton acceptor moiety in the cation moiety may be used. More specifically, a compound represented by the following general formula (7) is exemplified.

In the formula, A represents a sulfur atom or an iodine atom.
m represents 1 or 2, and n represents 1 or 2. However, when A is a sulfur atom, m + n = 3, and when A is an iodine atom, m + n = 2.
R represents an aryl group.
R _N represents an aryl group substituted with a proton acceptor functional group.
X ⁻ represents a counter anion.
X ^- it includes specific examples of can be the same as the anion moiety of the acid generator.

Specific examples of the aryl group of R and R _N is a phenyl group are preferably exemplified.

Specific examples of the proton acceptor functional group R _N are the same as those of the proton acceptor functional group described in the foregoing formula (PA-1).
Specific examples of the ionic compound having a proton acceptor site in the cation moiety include compounds exemplified in US2011 / 0269072A1 [0291].

  Such a compound can be synthesized with reference to methods described in, for example, JP-A-2007-230913 and JP-A-2009-122623.

A compound (PA) may be used individually by 1 type, and may be used in combination of 2 or more type.
The content of the compound (PA) is preferably 0.1 to 10% by mass and more preferably 1 to 8% by mass based on the total solid content of the composition.

[3-4] Onium salt that is relatively weak acid to acid generator In the actinic ray-sensitive or radiation-sensitive resin composition of the present invention, an onium salt that is relatively weak acid to the acid generator ( Hereinafter, “compound (D)”) can also be used as an acid diffusion controller.

  When an acid generator and an onium salt that generates an acid that is a relatively weak acid with respect to the acid generated from the acid generator are mixed and used, the acid generated from the acid generator by irradiation with actinic rays or radiation When it collides with an onium salt having an unreacted weak acid anion, a weak acid is released by salt exchange to produce an onium salt having a strong acid anion. In this process, the strong acid is exchanged with a weak acid having a lower catalytic ability, so that the acid is apparently deactivated and the acid diffusion can be controlled.

The compound (D) is preferably a compound represented by the following general formulas (d1-1) to (d1-3).

In the formula, R ⁵¹ represents a hydrocarbon group which may have a substituent, and Z ^2c represents a hydrocarbon group having 1 to 30 carbon atoms which may have a substituent (however, a carbon adjacent to S). R ⁵² is an organic group, Y ³ is a linear, branched or cyclic alkylene group or an arylene group, and Rf is a fluorine atom. Each of the M ⁺ is independently a sulfonium or iodonium cation.

Preferable examples of the sulfonium cation or iodonium cation represented by M ⁺ include the sulfonium cation exemplified for the acid generator (ZI) and the iodonium cation exemplified for (ZII).

Preferable examples of the anion moiety of the compound represented by the general formula (d1-1) include the structure exemplified in paragraph [0198] of JP2012-242799A.
Preferable examples of the anion moiety of the compound represented by the general formula (d1-2) include a structure exemplified in paragraph [0201] of JP2012-242799A.
Preferable examples of the anion moiety of the compound represented by the general formula (d1-3) include the structures exemplified in paragraphs [0209] and [0210] of JP2012-242799A.

  The onium salt (D) which is a weak acid relative to the acid generator has a cation moiety and an anion moiety in the same molecule, and the cation moiety and the anion moiety are linked by a covalent bond ( Hereinafter, it may be expressed as a compound (D1).

The compound (D1) is preferably a compound represented by any one of the following general formulas (D1-1), (D1-2), and (D1-3).

In general formulas (D1-1), (D1-2) and (D1-3),
R ₁ , R ₂ and R ₃ represent a substituent having 1 or more carbon atoms.
L ₁ represents a divalent linking group or a single bond linking the cation moiety and the anion moiety.
-X ^- it ^is, -COO _^-, -SO 3 _- represents an anion portion selected from ^{_{-R 4 -, -SO 2 -,}} -N. R ₄ has 1 having a carbonyl group: —C (═O) —, a sulfonyl group: —S (═O) ₂ —, and a sulfinyl group: —S (═O) — at the site of connection with the adjacent N atom. Represents a valent substituent.

R ₁ , R ₂ , R ₃ , R ₄ and L ₁ may be bonded to each other to form a ring structure. In (C-3), two of R1 to R3 may be combined to form a double bond with the N atom.

Examples of the substituent having 1 or more carbon atoms in R _{1 to} R ₃ include an alkyl group, a cycloalkyl group, an aryl group, an alkyloxycarbonyl group, a cycloalkyloxycarbonyl group, an aryloxycarbonyl group, an alkylaminocarbonyl group, and a cycloalkylamino. A carbonyl group, an arylaminocarbonyl group, etc. are mentioned. Preferably, they are an alkyl group, a cycloalkyl group, and an aryl group.

L ₁ as the divalent linking group is a linear or branched alkylene group, cycloalkylene group, arylene group, carbonyl group, ether bond, ester bond, amide bond, urethane bond, urea bond, and two types thereof. Examples include groups formed by combining the above. L ₁ is more preferably an alkylene group, an arylene group, an ether bond, an ester bond, or a group formed by combining two or more of these.

  Preferable examples of the compound represented by the general formula (D1-1) include paragraphs [0037] to [0039] of JP2013-6827A and paragraphs [0027] to [0029] of JP2013-8020A. ] Can be mentioned.

  Preferable examples of the compound represented by the general formula (D1-2) include compounds exemplified in paragraphs [0012] to [0013] of JP2012-189977A.

  Preferable examples of the compound represented by the general formula (D1-3) include compounds exemplified in paragraphs [0029] to [0031] of JP 2012-252124 A.

  The content of the onium salt (D) that is a weak acid relative to the acid generator is preferably 0.5 to 10.0% by mass, based on the solid content of the composition, and is 0.5 to 8%. More preferably, it is 0.0 mass%, and it is further more preferable that it is 1.0-8.0 mass%.

[4] Hydrophobic resin (HR)
The actinic ray-sensitive or radiation-sensitive resin composition according to the present invention is also referred to as a hydrophobic resin (hereinafter referred to as “hydrophobic resin (HR)” or simply “resin (HR)”), particularly when applied to immersion exposure. ) May be contained. The hydrophobic resin (HR) is preferably different from the resin (A).

  As a result, the hydrophobic resin (HR) is unevenly distributed on the surface layer of the film, and when the immersion medium is water, the static / dynamic contact angle of the resist film surface with water is improved, and the immersion liquid followability is improved. be able to.

  The hydrophobic resin (HR) is preferably designed to be unevenly distributed at the interface as described above. However, unlike the surfactant, the hydrophobic resin (HR) is not necessarily required to have a hydrophilic group in the molecule. There is no need to contribute to uniform mixing.

Hydrophobic resin (HR) is any one of “fluorine atom”, “silicon atom”, and “CH ₃ partial structure contained in side chain portion of resin” from the viewpoint of uneven distribution in the surface layer of the film It is preferable to have the above, and it is more preferable to have two or more.

  When the hydrophobic resin (HR) contains a fluorine atom and / or a silicon atom, the fluorine atom and / or silicon atom in the hydrophobic resin (HR) may be contained in the main chain of the resin. , May be contained in the side chain.

  When the hydrophobic resin (HR) contains a fluorine atom, it is a resin having an alkyl group having a fluorine atom, a cycloalkyl group having a fluorine atom, or an aryl group having a fluorine atom as a partial structure having a fluorine atom. Preferably there is.

  The alkyl group having a fluorine atom (preferably having 1 to 10 carbon atoms, more preferably 1 to 4 carbon atoms) is a linear or branched alkyl group in which at least one hydrogen atom is substituted with a fluorine atom, and further a fluorine atom It may have a substituent other than.

  The cycloalkyl group having a fluorine atom is a monocyclic or polycyclic cycloalkyl group in which at least one hydrogen atom is substituted with a fluorine atom, and may further have a substituent other than a fluorine atom.

  Examples of the aryl group having a fluorine atom include those in which at least one hydrogen atom of an aryl group such as a phenyl group or a naphthyl group is substituted with a fluorine atom, and may further have a substituent other than a fluorine atom. .

Preferred examples of the alkyl group having a fluorine atom, the cycloalkyl group having a fluorine atom, and the aryl group having a fluorine atom include groups represented by the following general formulas (F2) to (F4). The invention is not limited to this.

In general formulas (F2) to (F4),
R _{57 to} R ₆₈ each independently represent a hydrogen atom, a fluorine atom or an alkyl group (straight or branched). However, at least one of R _{57 to} R ₆₁ , at least one of R _{62 to} R ₆₄ , and at least one of R _{65 to} R ₆₈ are each independently a fluorine atom or at least one hydrogen atom is a fluorine atom. It represents a substituted alkyl group (preferably having 1 to 4 carbon atoms).

R _{57 to} R ₆₁ and R _{65 to} R ₆₇ are preferably all fluorine atoms. R ₆₂ , R ₆₃ and R ₆₈ are preferably an alkyl group (preferably having 1 to 4 carbon atoms) in which at least one hydrogen atom is substituted with a fluorine atom, and preferably a perfluoroalkyl group having 1 to 4 carbon atoms. Further preferred. R ₆₂ and R ₆₃ may be connected to each other to form a ring.

  Specific examples of the group represented by the general formula (F2) include a p-fluorophenyl group, a pentafluorophenyl group, and a 3,5-di (trifluoromethyl) phenyl group.

  Specific examples of the group represented by the general formula (F3) include those exemplified in [0500] of US2012 / 0251948A1.

Specific examples of the group represented by the general formula (F4) include, for example, —C (CF ₃ ) ₂ OH, —C (C ₂ F ₅ ) ₂ OH, —C (CF ₃ ) (CH ₃ ) OH, -CH _(CF 3) OH and the like, -C _{(CF 3)} 2 OH is preferred.

  The partial structure containing a fluorine atom may be directly bonded to the main chain, and further from the group consisting of an alkylene group, a phenylene group, an ether bond, a thioether bond, a carbonyl group, an ester bond, an amide bond, a urethane bond and a ureylene bond. You may couple | bond with a principal chain through the group selected or the group which combined these 2 or more.

  The hydrophobic resin (HR) may contain a silicon atom. The partial structure having a silicon atom is preferably a resin having an alkylsilyl structure (preferably a trialkylsilyl group) or a cyclic siloxane structure.

Specific examples of the alkylsilyl structure or the cyclic siloxane structure include groups represented by the following general formulas (CS-1) to (CS-3).

In general formulas (CS-1) to (CS-3),
R _{12 to} R ₂₆ each independently represent a linear or branched alkyl group (preferably having 1 to 20 carbon atoms) or a cycloalkyl group (preferably having 3 to 20 carbon atoms).

L < ₃ > -L < ₅ > represents a single bond or a bivalent coupling group. Examples of the divalent linking group include an alkylene group, a phenylene group, an ether bond, a thioether bond, a carbonyl group, an ester bond, an amide bond, a urethane bond, and a urea bond, or a combination of two or more ( Preferably, the total carbon number is 12 or less).

  n represents an integer of 1 to 5. n is preferably an integer of 2 to 4.

  Examples of the repeating unit having a fluorine atom or a silicon atom include those exemplified in [0519] of US2012 / 0251948A1.

Further, as described above, the hydrophobic resin (HR) also preferably includes a CH ₃ partial structure in the side chain portion.
Here, the CH ₃ partial structure possessed by the side chain moiety in the resin (HR) (hereinafter also simply referred to as “side chain CH ₃ partial structure”) has a CH ₃ partial structure possessed by an ethyl group, a propyl group, or the like. It is included.

On the other hand, a methyl group directly bonded to the main chain of the resin (HR) (for example, an α-methyl group of a repeating unit having a methacrylic acid structure) causes the surface uneven distribution of the resin (HR) due to the influence of the main chain. Since the contribution is small, it is not included in the CH ₃ partial structure in the present invention.

More specifically, the resin (HR) includes a repeating unit derived from a monomer having a polymerizable moiety having a carbon-carbon double bond, such as a repeating unit represented by the following general formula (M). In the case where R _{11 to} R ₁₄ are CH ₃ “as is”, the CH ₃ is not included in the CH ₃ partial structure of the side chain moiety in the present invention.

Meanwhile, CH ₃ partial structure exists through some atoms from C-C backbone, and those falling under CH ₃ partial structures in the present invention. For example, when R ₁₁ is an ethyl group (CH ₂ CH ₃ ), it is assumed that it has “one” CH ₃ partial structure in the present invention.

In the general formula (M),
R < ₁₁ > -R < ₁₄ > represents a side chain part each independently.
Examples of R _{11 to} R _{14 in the} side chain portion include a hydrogen atom and a monovalent organic group.

Examples of the monovalent organic group for R _{11 to} R ₁₄ include an alkyl group, a cycloalkyl group, an aryl group, an alkyloxycarbonyl group, a cycloalkyloxycarbonyl group, an aryloxycarbonyl group, an alkylaminocarbonyl group, and a cycloalkylaminocarbonyl. Group, an arylaminocarbonyl group, and the like, and these groups may further have a substituent.

The hydrophobic resin (HR) is preferably a resin having a repeating unit having a CH ₃ partial structure in the side chain portion. As such a repeating unit, a repeating unit represented by the following general formula (V), and It is more preferable to have at least one repeating unit (x) among repeating units represented by the following general formula (VI).
Hereinafter, the repeating unit represented by formula (V) will be described in detail.

In the general formula (V), X _b1 represents a hydrogen atom, an alkyl group, a cyano group or a halogen atom, R ₂ has one or more CH ₃ partial structure represents a stable organic radical to acid. Here, the organic group that is stable to acid is more preferably an organic group that does not have the “acid-decomposable group” described in the resin (A).

The alkyl group of _Xb1 preferably has 1 to 4 carbon atoms, and examples thereof include a methyl group, an ethyl group, a propyl group, a hydroxymethyl group, and a trifluoromethyl group, and a methyl group is preferable.

X _b1 is preferably a hydrogen atom or a methyl group.

Examples of R ₂ include an alkyl group, a cycloalkyl group, an alkenyl group, a cycloalkenyl group, an aryl group, and an aralkyl group having one or more CH ₃ partial structures. The above cycloalkyl group, alkenyl group, cycloalkenyl group, aryl group, and aralkyl group may further have an alkyl group as a substituent.

R ₂ is preferably an alkyl group or an alkyl-substituted cycloalkyl group having one or more CH ₃ partial structures.

The acid-stable organic group having one or more CH ₃ partial structures as R ₂ preferably has 2 or more and 10 or less CH ₃ partial structures, and more preferably 2 or more and 8 or less.

Preferred specific examples of the repeating unit represented by the general formula (V) are shown below. Note that the present invention is not limited to this.

The repeating unit represented by the general formula (V) is preferably an acid-stable (non-acid-decomposable) repeating unit, and specifically, a group that decomposes by the action of an acid to generate a polar group. It is preferable that it is a repeating unit which does not have.
Hereinafter, the repeating unit represented by formula (VI) will be described in detail.

In the general formula (VI), X _b2 represents a hydrogen atom, an alkyl group, a cyano group or a halogen atom, R ₃ has one or more CH ₃ partial structure represents a stable organic radical to acid, n represents an integer of 1 to 5.

The alkyl group of _Xb2 preferably has 1 to 4 carbon atoms, and examples thereof include a methyl group, an ethyl group, a propyl group, a hydroxymethyl group, and a trifluoromethyl group, and a hydrogen atom is preferable.

X _b2 is preferably a hydrogen atom.

Since R ₃ is an organic group that is stable against an acid, more specifically, R ₃ is preferably an organic group that does not have the “acid-decomposable group” described in the resin (A).

R ₃ includes an alkyl group having one or more CH ₃ partial structures.

The acid-stable organic group having one or more CH ₃ partial structures as R ₃ preferably has 1 or more and 10 or less CH ₃ partial structures, more preferably 1 or more and 8 or less, More preferably, it is 1 or more and 4 or less.

  n represents an integer of 1 to 5, more preferably an integer of 1 to 3, and still more preferably 1 or 2.

Preferred specific examples of the repeating unit represented by the general formula (VI) are shown below. Note that the present invention is not limited to this.

  The repeating unit represented by the general formula (VI) is preferably an acid-stable (non-acid-decomposable) repeating unit, and specifically, a group that decomposes by the action of an acid to generate a polar group. It is preferable that it is a repeating unit which does not have.

In the case where the resin (HR) contains a CH ₃ partial structure in the side chain portion, and particularly when it does not have a fluorine atom and a silicon atom, the repeating unit represented by the general formula (V) and the general formula The content of at least one repeating unit (x) among the repeating units represented by (VI) is preferably 90 mol% or more, and 95 mol% or more with respect to all the repeating units of the resin (C). It is more preferable that The content is usually 100 mol% or less with respect to all repeating units of the resin (C).

  The resin (HR) is a repeating unit represented by the general formula (V), and at least one repeating unit (x) among the repeating units represented by the general formula (VI) is all repeated of the resin (HR). By containing 90 mol% or more with respect to the unit, the surface free energy of the resin (C) increases. As a result, the resin (HR) is less likely to be unevenly distributed on the surface of the resist film, so that the static / dynamic contact angle of the resist film with respect to water can be reliably improved and the immersion liquid followability can be improved.

In addition, the hydrophobic resin (HR) includes the following (x) to (z) even when (i) contains a fluorine atom and / or a silicon atom, and (ii) contains a CH ₃ partial structure in the side chain portion. ) May have at least one group selected from the group of

(X) an acid group,
(Y) a group having a lactone structure, an acid anhydride group, or an acid imide group,
(Z) A group that decomposes by the action of an acid.

  Examples of the acid group (x) include a phenolic hydroxyl group, a carboxylic acid group, a fluorinated alcohol group, a sulfonic acid group, a sulfonamide group, a sulfonylimide group, an (alkylsulfonyl) (alkylcarbonyl) methylene group, and an (alkylsulfonyl) (alkyl Carbonyl) imide group, bis (alkylcarbonyl) methylene group, bis (alkylcarbonyl) imide group, bis (alkylsulfonyl) methylene group, bis (alkylsulfonyl) imide group, tris (alkylcarbonyl) methylene group, tris (alkylsulfonyl) A methylene group etc. are mentioned.

  Preferred acid groups include fluorinated alcohol groups (preferably hexafluoroisopropanol), sulfonimide groups, and bis (alkylcarbonyl) methylene groups.

  The repeating unit having an acid group (x) includes a repeating unit in which an acid group is directly bonded to the main chain of the resin, such as a repeating unit of acrylic acid or methacrylic acid, or a resin having a linking group. Examples include a repeating unit in which an acid group is bonded to the main chain, and a polymerization initiator or chain transfer agent having an acid group can be introduced at the end of the polymer chain at the time of polymerization. preferable. The repeating unit having an acid group (x) may have at least one of a fluorine atom and a silicon atom.

  The content of the repeating unit having an acid group (x) is preferably 1 to 50 mol%, more preferably 3 to 35 mol%, still more preferably 5 to 5 mol% with respect to all repeating units in the hydrophobic resin (HR). 20 mol%.

Specific examples of the repeating unit having an acid group (x) are shown below, but the present invention is not limited thereto. In the formula, Rx represents a hydrogen atom, CH ₃ , CF ₃ , or CH ₂ OH.

  As the group having a lactone structure, the acid anhydride group, or the acid imide group (y), a group having a lactone structure is particularly preferable.

  The repeating unit containing these groups is a repeating unit in which this group is directly bonded to the main chain of the resin, such as a repeating unit of acrylic acid ester and methacrylic acid ester. Alternatively, this repeating unit may be a repeating unit in which this group is bonded to the main chain of the resin via a linking group. Or this repeating unit may be introduce | transduced into the terminal of resin using the polymerization initiator or chain transfer agent which has this group at the time of superposition | polymerization.

  Examples of the repeating unit having a group having a lactone structure include those similar to the repeating unit having a lactone structure described above in the section of the acid-decomposable resin (A).

  The content of the repeating unit having a group having a lactone structure, an acid anhydride group, or an acid imide group is preferably 1 to 100 mol% based on all repeating units in the hydrophobic resin (HR), It is more preferably 3 to 98 mol%, and further preferably 5 to 95 mol%.

  In the hydrophobic resin (HR), examples of the repeating unit having a group (z) that is decomposed by the action of an acid are the same as the repeating unit having an acid-decomposable group listed for the resin (A). The repeating unit having a group (z) that is decomposed by the action of an acid may have at least one of a fluorine atom and a silicon atom. In the hydrophobic resin (HR), the content of the repeating unit having a group (z) that is decomposed by the action of an acid is preferably 1 to 80 mol% with respect to all repeating units in the resin (HR). Preferably it is 10-80 mol%, More preferably, it is 20-60 mol%.

The hydrophobic resin (HR) may further have a repeating unit represented by the following general formula (VII).

In general formula (VII):
R _c31 represents a hydrogen atom, an alkyl group (which may be substituted with a fluorine atom or the like), a cyano group, or a —CH ₂ —O—Rac ₂ group. In the formula, Rac ₂ represents a hydrogen atom, an alkyl group or an acyl group. R _c31 is preferably a hydrogen atom, a methyl group, a hydroxymethyl group or a trifluoromethyl group, particularly preferably a hydrogen atom or a methyl group.

R _c32 represents a group having an alkyl group, a cycloalkyl group, an alkenyl group, a cycloalkenyl group or an aryl group. These groups may be substituted with a group containing a fluorine atom or a silicon atom.

L _c3 represents a single bond or a divalent linking group.

In general formula (VII), the alkyl group represented by R _c32 is preferably a linear or branched alkyl group having 3 to 20 carbon atoms.

  The cycloalkyl group is preferably a cycloalkyl group having 3 to 20 carbon atoms.

  The alkenyl group is preferably an alkenyl group having 3 to 20 carbon atoms.

  The cycloalkenyl group is preferably a cycloalkenyl group having 3 to 20 carbon atoms.

  The aryl group is preferably an aryl group having 6 to 20 carbon atoms, more preferably a phenyl group or a naphthyl group, and these may have a substituent.

R _c32 is preferably an unsubstituted alkyl group or an alkyl group substituted with a fluorine atom.

The divalent linking group of L _c3 is preferably an alkylene group (preferably having 1 to 5 carbon atoms), an ether bond, a phenylene group, or an ester bond (a group represented by —COO—).

  The content of the repeating unit represented by the general formula (VII) is preferably 1 to 100 mol%, more preferably 10 to 90 mol%, based on all repeating units in the hydrophobic resin. 30 to 70 mol% is more preferable.

It is also preferable that the hydrophobic resin (HR) further has a repeating unit represented by the following general formula (CII-AB).

In the formula (CII-AB),
R _c11 ′ and R _c12 ′ each independently represents a hydrogen atom, a cyano group, a halogen atom or an alkyl group.

  Zc 'represents an atomic group for forming an alicyclic structure containing two bonded carbon atoms (C-C).

  The content of the repeating unit represented by the general formula (CII-AB) is preferably 1 to 100 mol%, and preferably 10 to 90 mol%, based on all repeating units in the hydrophobic resin. More preferably, it is more preferably 30 to 70 mol%.

Specific examples of the repeating unit represented by the general formulas (VII) and (CII-AB) are shown below, but the present invention is not limited thereto. In the formula, Ra represents H, CH ₃ , CH ₂ OH, CF ₃ or CN.

  When the hydrophobic resin (HR) has a fluorine atom, the content of the fluorine atom is preferably 5 to 80% by mass with respect to the weight average molecular weight of the hydrophobic resin (HR), and is 10 to 80% by mass. More preferably. Moreover, it is preferable that the repeating unit containing a fluorine atom is 10-100 mol% in all the repeating units contained in hydrophobic resin (HR), and it is more preferable that it is 30-100 mol%.

  When the hydrophobic resin (HR) has a silicon atom, the content of the silicon atom is preferably 2 to 50% by mass with respect to the weight average molecular weight of the hydrophobic resin (HR), and is 2 to 30% by mass. More preferably. Moreover, it is preferable that it is 10-100 mol% in the repeating unit containing a silicon atom among all the repeating units contained in hydrophobic resin (HR), and it is more preferable that it is 20-100 mol%.

On the other hand, particularly when the resin (HR) includes a CH ₃ partial structure in the side chain portion, it is also preferable that the resin (HR) does not substantially contain a fluorine atom and a silicon atom. In this case, specifically, The content of the repeating unit having a fluorine atom or a silicon atom is preferably 5 mol% or less, more preferably 3 mol% or less, more preferably 1 mol based on all repeating units in the resin (HR). % Or less, ideally 0 mol%, that is, no fluorine atom and no silicon atom. Moreover, it is preferable that resin (HR) is substantially comprised only by the repeating unit comprised only by the atom chosen from a carbon atom, an oxygen atom, a hydrogen atom, a nitrogen atom, and a sulfur atom. More specifically, the repeating unit composed only of atoms selected from a carbon atom, an oxygen atom, a hydrogen atom, a nitrogen atom and a sulfur atom may be 95 mol% or more in all the repeating units of the resin (HR). Preferably, it is 97 mol% or more, more preferably 99 mol% or more, and ideally 100 mol%.

  The weight average molecular weight of the hydrophobic resin (HR) in terms of standard polystyrene is preferably 1,000 to 100,000, more preferably 1,000 to 50,000, and even more preferably 2,000 to 15,000. is there.

  Moreover, the hydrophobic resin (HR) may be used alone or in combination.

  The content of the hydrophobic resin (HR) in the composition is preferably 0.01 to 10% by mass, more preferably 0.05 to 8% by mass, based on the total solid content in the composition of the present invention. More preferably, it is 1-7 mass%.

  The hydrophobic resin (HR), like the resin (A), naturally has few impurities such as metals, and the residual monomer and oligomer components are preferably 0.01 to 5% by mass, more preferably. Is more preferably 0.01 to 3% by mass and 0.05 to 1% by mass. As a result, an actinic ray-sensitive or radiation-sensitive resin composition that does not change over time such as foreign matter in liquid or sensitivity can be obtained. The molecular weight distribution (Mw / Mn, also referred to as dispersity) is preferably in the range of 1 to 5, more preferably 1 to 3, and still more preferably from the viewpoints of resolution, resist shape, resist pattern sidewall, roughness, and the like. It is the range of 1-2.

  As the hydrophobic resin (HR), various commercially available products can be used, or they can be synthesized according to a conventional method (for example, radical polymerization). For example, as a general synthesis method, a monomer polymerization method in which a monomer species and an initiator are dissolved in a solvent and heating is performed, and a solution of the monomer species and the initiator is dropped into the heating solvent over 1 to 10 hours. The dropping polymerization method is added, and the dropping polymerization method is preferable.

  The reaction solvent, the polymerization initiator, the reaction conditions (temperature, concentration, etc.) and the purification method after the reaction are the same as described in the resin (A), but in the synthesis of the hydrophobic resin (HR), The reaction concentration is preferably 30 to 50% by mass.

Specific examples of the hydrophobic resin (HR) are shown below. The following table shows the molar ratio of repeating units in each resin (corresponding to each repeating unit in order from the left), the weight average molecular weight, and the degree of dispersion.

[5] Solvent The actinic ray-sensitive or radiation-sensitive resin composition of the present invention usually contains a solvent.
Solvents that can be used in preparing the actinic ray-sensitive or radiation-sensitive resin composition include, for example, alkylene glycol monoalkyl ether carboxylates, alkylene glycol monoalkyl ethers, alkyl lactate esters, alkyl alkoxypropionates, Examples thereof include organic solvents such as cyclic lactones (preferably having 4 to 10 carbon atoms), monoketone compounds which may have a ring (preferably having 4 to 10 carbon atoms), alkylene carbonates, alkyl alkoxyacetates and alkyl pyruvates. .
Specific examples of these solvents can include those described in US Patent Application Publication No. 2008/0187860 [0441] to [0455].

  In this invention, you may use the mixed solvent which mixed the solvent which contains a hydroxyl group in a structure, and the solvent which does not contain a hydroxyl group as an organic solvent.

  As the solvent containing a hydroxyl group and the solvent not containing a hydroxyl group, the above-mentioned exemplary compounds can be selected as appropriate. As the solvent containing a hydroxyl group, alkylene glycol monoalkyl ether, alkyl lactate and the like are preferable, and propylene glycol monomethyl ether ( PGME, also known as 1-methoxy-2-propanol), ethyl lactate is more preferred. Further, as the solvent not containing a hydroxyl group, alkylene glycol monoalkyl ether acetate, alkyl alkoxypropionate, monoketone compound which may contain a ring, cyclic lactone, alkyl acetate and the like are preferable, and among these, propylene glycol monomethyl ether Acetate (PGMEA, also known as 1-methoxy-2-acetoxypropane), ethyl ethoxypropionate, 2-heptanone, γ-butyrolactone, cyclohexanone, butyl acetate are particularly preferred, propylene glycol monomethyl ether acetate, ethyl ethoxypropionate, 2 -Heptanone is most preferred.

  The mixing ratio (mass) of the solvent containing a hydroxyl group and the solvent not containing a hydroxyl group is 1/99 to 99/1, preferably 10/90 to 90/10, more preferably 20/80 to 60/40. . A mixed solvent containing 50% by mass or more of a solvent not containing a hydroxyl group is particularly preferred from the viewpoint of coating uniformity.

  The solvent preferably contains propylene glycol monomethyl ether acetate, and is preferably a propylene glycol monomethyl ether acetate single solvent or a mixed solvent of two or more containing propylene glycol monomethyl ether acetate.

[6] Surfactant The composition may or may not further contain a surfactant. When it is contained, fluorine and / or silicon surfactant (fluorine surfactant, silicon surfactant, It is more preferable to contain any one or two or more of surfactants having both a fluorine atom and a silicon atom.

  When the composition contains a surfactant, it is possible to provide a resist pattern with less adhesion and development defects with good sensitivity and resolution when using an exposure light source of 250 nm or less, particularly 220 nm or less.

  Examples of the fluorine-based and / or silicon-based surfactant include surfactants described in [0276] of US Patent Application Publication No. 2008/0248425. For example, F-top EF301, EF303, (Shin-Akita Kasei Co., Ltd.) )), Florard FC430, 431, 4430 (manufactured by Sumitomo 3M Co., Ltd.), Megafac F171, F173, F176, F189, F113, F110, F177, F120, R08 (manufactured by DIC Corporation), Surflon S-382 SC101, 102, 103, 104, 105, 106, KH-20 (manufactured by Asahi Glass Co., Ltd.), Troisol S-366 (manufactured by Troy Chemical Co., Ltd.), GF-300, GF-150 (Toagosei Chemical Co., Ltd.) ), Surflon S-393 (Seimi Chemical Co., Ltd.), Ftop EF121, EF 22A, EF122B, RF122C, EF125M, EF135M, EF351, EF352, EF801, EF802, EF601 (manufactured by Gemco), PF636, PF656, PF6320, PF6520 (manufactured by OMNOVA), FTX-204G, 230G, 218G 204D, 208D, 212D, 218D, 222D (manufactured by Neos Co., Ltd.) and the like. Polysiloxane polymer KP-341 (manufactured by Shin-Etsu Chemical Co., Ltd.) can also be used as a silicon-based surfactant.

  In addition to the known surfactants described above, surfactants are derived from fluoroaliphatic compounds produced by the telomerization method (also referred to as the telomer method) or the oligomerization method (also referred to as the oligomer method). A surfactant using a polymer having a fluoroaliphatic group can be used. The fluoroaliphatic compound can be synthesized by the method described in JP-A-2002-90991.

As the surfactant corresponding to the above, Megafac F178, F-470, F-473, F-475, F-476, F-472 (manufactured by DIC Corporation), acrylate having C ₆ F ₁₃ group (or methacrylate) and (poly (oxyalkylene)) acrylate (copolymer of or methacrylate), and acrylate having a C ₃ F ₇ group (or methacrylate) (poly (oxyethylene) and) acrylate (or methacrylate) (poly ( And a copolymer with oxypropylene)) acrylate (or methacrylate).

  In the present invention, surfactants other than fluorine-based and / or silicon-based surfactants described in [0280] of US Patent Application Publication No. 2008/0248425 can also be used.

  These surfactants may be used alone or in several combinations.

  When the composition contains a surfactant, the amount of the surfactant used is preferably 0.0001 to 2% by mass, more preferably 0.0005 to 1% by mass, based on the total solid content of the composition. It is.

  On the other hand, by making the addition amount of the surfactant 10 ppm or less with respect to the total amount of the composition (excluding the solvent), the surface unevenness of the hydrophobic resin is increased, thereby making the resist film surface more hydrophobic. It is possible to improve water followability at the time of immersion exposure.

[7] Other additives The actinic ray-sensitive or radiation-sensitive resin composition of the present invention may or may not contain a carboxylic acid onium salt. Examples of such carboxylic acid onium salts include those described in US Patent Application Publication No. 2008/0187860 [0605] to [0606].

  These carboxylic acid onium salts can be synthesized by reacting sulfonium hydroxide, iodonium hydroxide, ammonium hydroxide and carboxylic acid with silver oxide in a suitable solvent.

  When the actinic ray-sensitive or radiation-sensitive resin composition contains a carboxylic acid onium salt, the content thereof is generally 0.1 to 20% by mass, preferably 0, based on the total solid content of the composition. It is 5-10 mass%, More preferably, it is 1-7 mass%.

  If necessary, the actinic ray-sensitive or radiation-sensitive resin composition of the present invention may further include an acid proliferator, a dye, a plasticizer, a photosensitizer, a light absorber, an alkali-soluble resin, a dissolution inhibitor, and a development. A compound (for example, a phenol compound having a molecular weight of 1000 or less, an alicyclic group having a carboxyl group, or an aliphatic compound) that promotes solubility in a liquid can be contained.

  Such phenolic compounds having a molecular weight of 1000 or less can be obtained by referring to, for example, the methods described in JP-A-4-1222938, JP-A-2-28531, US Pat. No. 4,916,210, European Patent 219294, etc. It can be easily synthesized by those skilled in the art.

  Specific examples of alicyclic or aliphatic compounds having a carboxyl group include carboxylic acid derivatives having a steroid structure such as cholic acid, deoxycholic acid, lithocholic acid, adamantane carboxylic acid derivatives, adamantane dicarboxylic acid, cyclohexane carboxylic acid, cyclohexane Examples thereof include, but are not limited to, dicarboxylic acids.

  As described later in the pattern forming method, from the viewpoint of improving resolution, the actinic ray-sensitive or radiation-sensitive film having a film thickness of 80 nm or less using the actinic ray-sensitive or radiation-sensitive resin composition of the present invention. Is formed. Such a film thickness can be obtained by setting the solid content concentration in the composition to an appropriate range to give an appropriate viscosity and improving the coating property and film forming property.

  The solid content concentration of the actinic ray-sensitive or radiation-sensitive resin composition in the present invention is usually 1.0 to 10% by mass, preferably 2.0 to 5.7% by mass, and more preferably 2.0. It is -5.3 mass%. By setting the solid content concentration within the above range, it is possible to uniformly apply the resist solution on the substrate, and it is possible to form a resist pattern having excellent line width roughness. The reason for this is not clear, but perhaps the solid content concentration is 10% by mass or less, preferably 5.7% by mass or less, which suppresses aggregation of the material in the resist solution, particularly the photoacid generator. As a result, it is considered that a uniform resist film was formed.

  The solid content concentration is a weight percentage of the weight of other resist components excluding the solvent with respect to the total weight of the actinic ray-sensitive or radiation-sensitive resin composition.

  In the actinic ray-sensitive or radiation-sensitive resin composition of the present invention, the above components are dissolved in a predetermined organic solvent, preferably the mixed solvent, filtered, and then applied onto a predetermined support (substrate). Use. The pore size of the filter used for filter filtration is preferably 0.1 μm or less, more preferably 0.05 μm or less, and still more preferably 0.03 μm or less made of polytetrafluoroethylene, polyethylene, or nylon. In filter filtration, for example, as in JP-A-2002-62667, circulation filtration may be performed, or filtration may be performed by connecting a plurality of types of filters in series or in parallel. The composition may be filtered multiple times. Furthermore, you may perform a deaeration process etc. with respect to a composition before and behind filter filtration.

<Pattern formation method>
Next, the pattern forming method according to the present invention will be described.
The pattern forming method of the present invention comprises:
(I) forming an actinic ray-sensitive or radiation-sensitive film having a thickness of 80 nm or less using the actinic ray-sensitive or radiation-sensitive resin composition of the present invention;
(Ii) at least a step of exposing the actinic ray-sensitive or radiation-sensitive film; and (iii) a step of developing the exposed actinic-ray-sensitive or radiation-sensitive film.

In the pattern forming method of the present invention, the exposure may be immersion exposure.
The pattern forming method of the present invention may include an exposure step a plurality of times.
Moreover, the pattern formation method of this invention may include the heating process in multiple times.
Moreover, the pattern formation method of this invention may include the image development process in multiple times.

  The actinic ray-sensitive or radiation-sensitive film of the present invention is formed from the above-described actinic ray-sensitive or radiation-sensitive resin composition of the present invention, and more specifically, the substrate is active. A film formed by applying a light-sensitive or radiation-sensitive resin composition is preferable.

  As described above, from the viewpoint of improving the resolution, the film thickness of the actinic ray-sensitive or radiation-sensitive film formed using the actinic ray-sensitive or radiation-sensitive resin composition of the present invention is 80 nm or less, and more Preferably it is 70 nm or less, More preferably, it is 60 nm or less.

  In the pattern forming method of the present invention, a step of forming a film of an actinic ray-sensitive or radiation-sensitive resin composition on a substrate, a step of exposing the film, and a developing step are generally known methods. Can be performed.

It is also preferable to include a preheating step (PB; Prebake) after the film formation and before the exposure step.
It is also preferable to include a post-exposure heating step (PEB; Post Exposure Bake) after the exposure step and before the development step.

The heating temperature is preferably 70 to 130 ° C., more preferably 80 to 120 ° C. for both PB and PEB.
The heating time is preferably 30 to 300 seconds, more preferably 30 to 180 seconds, and still more preferably 30 to 90 seconds.
Heating can be performed by means provided in a normal exposure / developing machine, and may be performed using a hot plate or the like.
The reaction of the exposed part is promoted by baking, and the sensitivity and pattern profile are improved.

Although there is no restriction | limiting in the light source wavelength used for the exposure apparatus in this invention, Infrared light, visible light, ultraviolet light, far ultraviolet light, extreme ultraviolet light, X-rays, an electron beam, etc. can be mentioned, Preferably it is 250 nm or less. More preferably 220 nm or less, particularly preferably far ultraviolet light having a wavelength of 1 to ₂₀₀ nm, specifically, KrF excimer laser (248 nm), ArF excimer laser (193 nm), F ₂ excimer laser (157 nm), X-ray, EUV (13 nm), electron beam, etc., KrF excimer laser, ArF excimer laser, EUV or electron beam are preferable, and ArF excimer laser is more preferable.

  Moreover, the immersion exposure method can be applied in the step of performing exposure according to the present invention. The immersion exposure method can be combined with a super-resolution technique such as a phase shift method or a modified illumination method.

  When performing immersion exposure, (1) after forming the film on the substrate, before the exposure step and / or (2) after exposing the film via the immersion liquid, Prior to the heating step, a step of washing the surface of the membrane with an aqueous chemical may be performed.

  The immersion liquid is preferably a liquid that is transparent to the exposure wavelength and has a refractive index temperature coefficient as small as possible so as to minimize distortion of the optical image projected onto the film. In the case of an ArF excimer laser (wavelength: 193 nm), it is preferable to use water from the viewpoints of availability and ease of handling in addition to the above-described viewpoints.

When water is used, an additive (liquid) that decreases the surface tension of water and increases the surface activity may be added in a small proportion. This additive is preferably one that does not dissolve the resist layer on the wafer and can ignore the influence on the optical coating on the lower surface of the lens element.
As such an additive, for example, an aliphatic alcohol having a refractive index substantially equal to that of water is preferable, and specific examples include methyl alcohol, ethyl alcohol, isopropyl alcohol and the like. By adding an alcohol having a refractive index substantially equal to that of water, even if the alcohol component in water evaporates and the content concentration changes, an advantage that the change in the refractive index of the entire liquid can be made extremely small can be obtained.

On the other hand, when an opaque substance or impurities whose refractive index is significantly different from that of water are mixed with respect to 193 nm light, the optical image projected on the resist is distorted. Therefore, distilled water is preferable as the water to be used. Further, pure water filtered through an ion exchange filter or the like may be used.
The electrical resistance of water used as the immersion liquid is preferably 18.3 MQcm or more, the TOC (organic substance concentration) is preferably 20 ppb or less, and deaeration treatment is preferably performed.

Moreover, it is possible to improve lithography performance by increasing the refractive index of the immersion liquid. From such a viewpoint, an additive that increases the refractive index may be added to water, or heavy water (D ₂ O) may be used instead of water.

The receding contact angle of the resist film formed by using the actinic ray-sensitive or radiation-sensitive resin composition in the present invention is 70 ° or more at a temperature of 23 ± 3 ° C. and a humidity of 45 ± 5%, and through the immersion medium. It is suitable for exposure, preferably 75 ° or more, and more preferably 75 to 85 °.
If the receding contact angle is too small, it cannot be suitably used for exposure through an immersion medium, and the effect of reducing water residue (watermark) defects cannot be sufficiently exhibited. In order to realize a preferable receding contact angle, it is preferable to include the hydrophobic resin (HR) in the actinic ray-sensitive or radiation-sensitive composition. Alternatively, the receding contact angle may be improved by forming a coating layer (so-called “topcoat”) of a hydrophobic resin composition on the resist film.

  In the immersion exposure process, the immersion head needs to move on the wafer following the movement of the exposure head to scan the wafer at high speed to form the exposure pattern. In this case, the contact angle of the immersion liquid with respect to the resist film is important, and the resist is required to follow the high-speed scanning of the exposure head without remaining droplets.

In the present invention, the substrate on which the film is formed is not particularly limited, and silicon, SiN, inorganic substrates such as SiO ₂ and SiN, coated inorganic substrates such as SOG, semiconductor manufacturing processes such as IC, liquid crystal, and thermal head For example, a substrate generally used in a circuit board manufacturing process or other photofabrication lithography process can be used. Furthermore, if necessary, an antireflection film may be formed between the resist film and the substrate. As the antireflection film, a known organic or inorganic antireflection film can be appropriately used.

  The developer used in the step of developing the resist film formed using the actinic ray-sensitive or radiation-sensitive resin composition of the present invention is not particularly limited, but for example, a developer containing an alkali developer or an organic solvent (Hereinafter also referred to as an organic developer) can be used. Moreover, when the pattern formation method of this invention includes the image development process of multiple times, you may combine the process developed using an alkaline developing solution, and the process developed using an organic type developing solution.

When the pattern forming method of the present invention includes a step of developing using an alkali developer, usable alkali developers are not particularly limited, but generally, 2.38% by mass of tetramethylammonium hydroxide. An aqueous solution is desirable. In addition, an appropriate amount of alcohol or surfactant may be added to the alkaline aqueous solution.
The alkali concentration of the alkali developer is usually from 0.1 to 20% by mass.
The pH of the alkali developer is usually from 10.0 to 15.0.
As a rinsing solution in the rinsing treatment performed after alkali development, pure water can be used, and an appropriate amount of a surfactant can be added.
In addition, after the developing process or the rinsing process, a process of removing the developing solution or the rinsing liquid adhering to the pattern with a supercritical fluid can be performed.

  When the pattern forming method of the present invention includes a step of developing using an organic developer, examples of the organic developer include ketone solvents, ester solvents, alcohol solvents, amide solvents, ether solvents, and the like. These polar solvents and hydrocarbon solvents can be used.

  Examples of the ketone solvent include 1-octanone, 2-octanone, 1-nonanone, 2-nonanone, acetone, 2-heptanone (methyl amyl ketone), 4-heptanone, 1-hexanone, 2-hexanone, diisobutyl ketone, Examples include cyclohexanone, methylcyclohexanone, phenylacetone, methylethylketone, methylisobutylketone, acetylacetone, acetonylacetone, ionone, diacetylalcohol, acetylcarbinol, acetophenone, methylnaphthylketone, isophorone, and propylene carbonate.

  Examples of ester solvents include methyl acetate, butyl acetate, ethyl acetate, isopropyl acetate, pentyl acetate, isopentyl acetate, amyl acetate, propylene glycol monomethyl ether acetate, ethylene glycol monoethyl ether acetate, diethylene glycol monobutyl ether acetate, diethylene glycol monoethyl. Examples include ether acetate, ethyl-3-ethoxypropionate, 3-methoxybutyl acetate, 3-methyl-3-methoxybutyl acetate, methyl formate, ethyl formate, butyl formate, propyl formate, ethyl lactate, butyl lactate, and propyl lactate. be able to.

  Examples of the alcohol solvent include methyl alcohol, ethyl alcohol, n-propyl alcohol, isopropyl alcohol, n-butyl alcohol, sec-butyl alcohol, tert-butyl alcohol, isobutyl alcohol, n-hexyl alcohol, n-heptyl alcohol, alcohols such as n-octyl alcohol and n-decanol, glycol solvents such as ethylene glycol, diethylene glycol and triethylene glycol, ethylene glycol monomethyl ether, propylene glycol monomethyl ether, ethylene glycol monoethyl ether, propylene glycol monoethyl ether, Diethylene glycol monomethyl ether, triethylene glycol monoethyl ether, methoxymethyl butano It can be mentioned glycol ether solvents such as Le.

Examples of the ether solvent include dioxane, tetrahydrofuran and the like in addition to the glycol ether solvent.
Examples of the amide solvent include N-methyl-2-pyrrolidone, N, N-dimethylacetamide, N, N-dimethylformamide, hexamethylphosphoric triamide, 1,3-dimethyl-2-imidazolidinone and the like. Can be used.
Examples of the hydrocarbon solvent include aromatic hydrocarbon solvents such as toluene and xylene, and aliphatic hydrocarbon solvents such as pentane, hexane, octane and decane.

A plurality of the above solvents may be mixed, or may be used by mixing with a solvent other than those described above or water. However, in order to fully exhibit the effects of the present invention, the water content of the developer as a whole is preferably less than 10% by mass, and more preferably substantially free of moisture.
That is, the amount of the organic solvent used in the organic developer is preferably 90% by mass or more and 100% by mass or less, and more preferably 95% by mass or more and 100% by mass or less, with respect to the total amount of the developer.

  In particular, the organic developer is preferably a developer containing at least one organic solvent selected from the group consisting of ketone solvents, ester solvents, alcohol solvents, amide solvents and ether solvents. .

  The vapor pressure of the organic developer is preferably 5 kPa or less, more preferably 3 kPa or less, and particularly preferably 2 kPa or less at 20 ° C. By setting the vapor pressure of the organic developer to 5 kPa or less, evaporation of the developer on the substrate or in the developing cup is suppressed, and the temperature uniformity in the wafer surface is improved. As a result, the dimensions in the wafer surface are uniform. Sexuality improves.

An appropriate amount of a surfactant can be added to the organic developer as required.
The surfactant is not particularly limited, and for example, ionic or nonionic fluorine-based and / or silicon-based surfactants can be used. Examples of these fluorine and / or silicon surfactants include, for example, JP-A No. 62-36663, JP-A No. 61-226746, JP-A No. 61-226745, JP-A No. 62-170950, JP 63-34540 A, JP 7-230165 A, JP 8-62834 A, JP 9-54432 A, JP 9-5988 A, US Pat. No. 5,405,720, etc. The surfactants described in the specifications of US Pat. Preferably, it is a nonionic surfactant. Although it does not specifically limit as a nonionic surfactant, It is still more preferable to use a fluorochemical surfactant or a silicon-type surfactant.

  The amount of the surfactant used is usually 0.001 to 5% by mass, preferably 0.005 to 2% by mass, and more preferably 0.01 to 0.5% by mass with respect to the total amount of the developer.

  The organic developer may contain a basic compound. As a basic compound, the above-mentioned compound illustrated as an acid diffusion controlling agent can be mentioned, for example.

  As a developing method, for example, a method in which a substrate is immersed in a tank filled with a developer for a certain period of time (dip method), a method in which the developer is raised on the surface of the substrate by surface tension and is left stationary for a certain time (paddle) Method), a method of spraying the developer on the substrate surface (spray method), a method of continuously discharging the developer while scanning the developer discharge nozzle on the substrate rotating at a constant speed (dynamic dispensing method) Etc. can be applied.

When the various development methods described above include a step of discharging the developer from the developing nozzle of the developing device toward the resist film, the discharge pressure of the discharged developer (the flow rate per unit area of the discharged developer) is Preferably it is 2 mL / sec / mm ² or less, More preferably, it is 1.5 mL / sec / mm ² or less, More preferably, it is 1 mL / sec / mm ² or less. There is no particular lower limit on the flow rate, but 0.2 mL / sec / mm ² or more is preferable in consideration of throughput.

By setting the discharge pressure of the discharged developer to be in the above range, pattern defects derived from the resist residue after development can be remarkably reduced.
The details of this mechanism are not clear, but perhaps by setting the discharge pressure within the above range, the pressure applied by the developer to the resist film will decrease, and the resist film / resist pattern may be inadvertently cut or collapsed. This is considered to be suppressed.

The developer discharge pressure (mL / sec / mm ² ) is a value at the developing nozzle outlet in the developing device.
Examples of the method for adjusting the discharge pressure of the developer include a method of adjusting the discharge pressure with a pump or the like, and a method of changing the pressure by adjusting the pressure by supply from a pressurized tank.

Moreover, you may implement the process of stopping image development, after substituting with another solvent after the process developed using the developing solution containing an organic solvent.
It is preferable to include the process of wash | cleaning using a rinse liquid after the process developed using the developing solution containing an organic solvent.

  The rinsing solution used in the rinsing step after the step of developing with a developer containing an organic solvent is not particularly limited as long as the resist pattern is not dissolved, and a solution containing a general organic solvent can be used. . As the rinsing liquid, a rinsing liquid containing at least one organic solvent selected from the group consisting of hydrocarbon solvents, ketone solvents, ester solvents, alcohol solvents, amide solvents and ether solvents is used. It is preferable.

  Specific examples of the hydrocarbon solvent, the ketone solvent, the ester solvent, the alcohol solvent, the amide solvent, and the ether solvent are the same as those described in the developer containing an organic solvent.

  More preferably, it contains at least one organic solvent selected from the group consisting of ketone solvents, ester solvents, alcohol solvents, and amide solvents after the step of developing using a developer containing an organic solvent. A step of washing with a rinsing liquid is performed, more preferably, a step of washing with a rinsing liquid containing an alcohol solvent or an ester solvent is carried out, and particularly preferably, a rinsing liquid containing a monohydric alcohol is used. And, most preferably, the step of cleaning with a rinse solution containing a monohydric alcohol having 5 or more carbon atoms is performed.

Here, examples of the monohydric alcohol used in the rinsing step include linear, branched, and cyclic monohydric alcohols, and specifically, 1-butanol, 2-butanol, and 3-methyl-1-butanol. Tert-butyl alcohol, 1-pentanol, 2-pentanol, 1-hexanol, 4-methyl-2-pentanol, 1-heptanol, 1-octanol, 2-hexanol, cyclopentanol, 2-heptanol, 2 -Octanol, 3-hexanol, 3-heptanol, 3-octanol, 4-octanol and the like can be used, and particularly preferable monohydric alcohols having 5 or more carbon atoms include 1-hexanol, 2-hexanol, 4-methyl- Use 2-pentanol, 1-pentanol, 3-methyl-1-butanol, etc. It can be.
A plurality of these components may be mixed, or may be used by mixing with an organic solvent other than the above.

  The water content in the rinse liquid is preferably 10% by mass or less, more preferably 5% by mass or less, and particularly preferably 3% by mass or less. By setting the water content to 10% by mass or less, good development characteristics can be obtained.

  The vapor pressure of the rinsing solution used after the step of developing with a developer containing an organic solvent is preferably 0.05 kPa or more and 5 kPa or less, more preferably 0.1 kPa or more and 5 kPa or less at 20 ° C. 12 kPa or more and 3 kPa or less are the most preferable. By setting the vapor pressure of the rinse liquid to 0.05 kPa or more and 5 kPa or less, the temperature uniformity in the wafer surface is improved, and further, the swelling due to the penetration of the rinse solution is suppressed, and the dimensional uniformity in the wafer surface. Improves.

An appropriate amount of a surfactant can be added to the rinse solution.
In the rinsing step, the wafer that has been developed using the developer containing the organic solvent is washed using the rinse solution containing the organic solvent. The cleaning method is not particularly limited. For example, a method of continuing to discharge the rinse liquid onto the substrate rotating at a constant speed (rotary coating method), or immersing the substrate in a tank filled with the rinse liquid for a certain period of time. A method (dip method), a method of spraying a rinsing liquid on the substrate surface (spray method), and the like can be applied. Among them, a cleaning treatment is performed by a spin coating method, and after cleaning, the substrate is rotated at a speed of 2000 rpm to 4000 rpm. It is preferable to rotate and remove the rinse liquid from the substrate. It is also preferable to include a heating step (Post Bake) after the rinsing step. The developing solution and the rinsing solution remaining between the patterns and inside the patterns are removed by baking. The heating step after the rinsing step is usually 40 to 160 ° C., preferably 70 to 95 ° C., and usually 10 seconds to 3 minutes, preferably 30 seconds to 90 seconds.

The present invention also relates to an electronic device manufacturing method including the above-described negative pattern forming method of the present invention, and an electronic device manufactured by this manufacturing method.
The electronic device of the present invention is suitably mounted on electrical and electronic equipment (home appliances, OA / media related equipment, optical equipment, communication equipment, etc.).

EXAMPLES Hereinafter, although an Example demonstrates this invention further in detail, the content of this invention is not limited by this.
<Synthesis of Resin A-1>
Under a nitrogen stream, 17.0 g of cyclohexanone was placed in a three-necked flask and heated to 85 ° C. In this way, solvent 1 was obtained. Next, the following monomer 1 (8.89 g), the following monomer 2 (3.55 g), the following monomer 3 (6.38 g), and the following monomer 4 (2.40 g) were added to cyclohexanone (67.9 g). Dissolved to prepare a monomer solution. Furthermore, 6.5 mol% of polymerization initiator V-601 (manufactured by Wako Pure Chemical Industries, Ltd.) was added to the total amount of monomers, and the dissolved solution was added dropwise to the solvent 1 over 6 hours. After completion of dropping, the reaction was further continued at 85 ° C. for 2 hours. The reaction solution was allowed to cool and then added dropwise to a mixed solvent of 506 g of heptane / 217 g of ethyl acetate, and the precipitated powder was collected by filtration and dried to obtain 18.6 g of Resin (A-1). About the obtained resin (A-1), the weight average molecular weight (Mw: polystyrene conversion), the number average molecular weight (Mn: polystyrene conversion), and dispersity (Mw / Mn) were calculated by GPC (solvent: THF) measurement. . Moreover, the composition ratio (molar ratio) of the resin (A-1) was calculated by ¹³ C-NMR. The weight average molecular weight (Mw) of the resin (A-1) was 8600, and the dispersity (Mw / Mn) was 1.56.

  Resins (A-2) to (A-5), (AX), and (AY) described later were synthesized in the same manner as the resin (A-1).

<Resist preparation>
The components shown in Table 3 below are dissolved in a solvent, and a solution with a solid content of 4% by mass is prepared for each, and this is filtered through a polyethylene filter having a pore size of 0.05 μm. A resin composition (hereinafter also referred to as a resist composition) was prepared. The actinic ray-sensitive or radiation-sensitive resin composition was evaluated by the following method, and the results are shown in Table 2.
<Resist evaluation>
(ArF immersion exposure)
An organic antireflection film ARC29SR (manufactured by Nissan Chemical Industries, Ltd.) was applied onto a 12-inch silicon wafer and baked at 205 ° C. for 60 seconds to form an antireflection film having a thickness of 98 nm. On top of that, the actinic ray-sensitive or radiation-sensitive resin composition prepared above was applied and baked at 95 ° C. for 60 seconds to form a resist film having a thickness shown in Table 3 below. In contrast, using an ArF excimer laser immersion scanner (XTML1700i, NA1.20, C-Quad, outer sigma 0.981, inner sigma 0.895, XY deflection manufactured by ASML), a 1: 1 line with a line width of 48 nm Exposure was through a 6% halftone mask with andspace pattern. Ultra pure water was used as the immersion liquid. Then, after heating at 90 ° C. for 60 seconds, paddle development with an aqueous tetramethylammonium hydroxide solution (2.38 mass%) for 30 seconds, paddle with pure water, rinse, and spin dry to form a pattern. did.

(Pattern resolution)
When the exposure amount for reproducing a mask pattern with a line width of 48 nm is set as the optimum exposure amount, and the line width of the line pattern formed by further increasing the exposure amount from the optimum exposure amount is reduced. In addition, the line width (nm) was determined so that the pattern could be resolved without falling down. A smaller value indicates that a finer pattern is resolved without falling down, and indicates that the resolution of the ultrafine pattern is excellent.

[Dry etching rate]
For the 1: 1 line and space pattern with a line width of 48 nm obtained above, dry etching was performed for 30 seconds in the pattern portion under the atmosphere of argon, C4F6, and O2, and the dry etching rate was calculated from the change in film thickness before and after that. Asked. Smaller values indicate higher dry etching resistance and better performance.

[Evaluation of depth of focus latitude (DOF)]
The exposure amount and depth of focus for reproducing a resist pattern of 1: 1 line and space pattern with a line width of 48 nm are set as the optimum exposure amount and the optimum depth of focus, respectively, and the depth of focus is set to the optimum depth of focus while keeping the exposure amount as the optimum exposure amount. The depth of focus allowing a line width of ± 10% (that is, 48 nm ± 10%) of the line width was observed. A larger value is desirable because the tolerance for defocus is large.

  The abbreviations in the table represent the following.

[Photoacid generator (B)]

[Resin (A)]
For each of the following resins, the composition ratio of repeating units is a molar ratio.

[Basic compounds]

[Hydrophobic resin]
The hydrophobic resin was appropriately selected from (B-1) to (B-56) listed as specific examples above.

〔solvent〕
A1: Propylene glycol monomethyl ether acetate (PGMEA)
A2: Cyclohexanone A3: γ-Butyrolactone B1: Propylene glycol monomethyl ether (PGME)
B2: Ethyl lactate [Surfactant]
W-1: Megafuck F176 (manufactured by DIC Corporation) (fluorine-based)
W-2: Troisol S-366 (manufactured by Troy Chemical Co., Ltd.) (fluorine type)
W-3: PF656 (manufactured by OMNOVA) (fluorine-based)
From Table 3 above, it can be seen that the pattern created by the pattern forming method of the present invention is excellent in pattern resolution, dry etching resistance and depth of focus latitude.

Claims (16)

(I) (A) a resin containing at least one repeating unit (a) having a polycyclic aromatic structure, which increases the dissolution rate in an alkaline developer by the action of an acid, and (B) irradiation with actinic rays or radiation Forming an actinic ray-sensitive or radiation-sensitive film having a film thickness of 80 nm or less using an actinic ray-sensitive or radiation-sensitive resin composition containing a compound that generates an acid by
(Ii) A pattern forming method including the step of exposing the actinic ray-sensitive or radiation-sensitive film, and (iii) developing the exposed actinic ray-sensitive or radiation-sensitive film.   The pattern formation method according to claim 1, wherein the resin (A) further contains an acid-decomposable repeating unit having a group that is decomposed by the action of an acid.   The pattern formation method of Claim 1 or 2 whose said polycyclic aromatic structure which a repeating unit (a) has is a naphthalene structure. The pattern formation method of Claim 3 whose repeating unit (a) is a repeating unit represented by the following general formula (Ia).

In general formula (Ia),
A ₁ represents a hydrogen atom, an alkyl group, a halogen atom, or a cyano group.
L ₁ represents a single bond or a divalent linking group.
Y represents a monovalent substituent.
n represents an integer of 0 to 7. When n is 2 or more, a plurality of Y may be the same or different. The pattern formation method of Claim 4 whose repeating unit (a) is a repeating unit represented by the following general formula (IIa).

In general formula (IIa),
A ₁ represents a hydrogen atom, an alkyl group, a halogen atom, or a cyano group.
L ₂ represents a single bond or a divalent linking group.
Y represents a monovalent substituent.
n represents an integer of 0 to 7. When n is 2 or more, a plurality of Y may be the same or different. _{L 2} in the general formula (IIa) is a cycloalkylene group alkylene or 3 to 20 carbon atoms, having 1 to 20 carbon atoms, a pattern forming method according to claim 5. The pattern formation method of any one of Claims 2-6 in which resin (A) contains the repeating unit represented by the following general formula (I) as said acid-decomposable repeating unit.

In general formula (I),
R ₁ represents a hydrogen atom, a methyl group which may have a substituent, or a group represented by —CH ₂ —R ₁₁ . R ₁₁ represents a monovalent organic group.
R ₂ represents an alkyl group or a cycloalkyl group.
R represents an atomic group necessary for forming an alicyclic structure together with the carbon atom to which R ₂ is bonded.   The pattern formation method of Claim 7 whose said alicyclic structure which general formula (I) has is a monocyclic alicyclic structure. (B) The compound which generate | occur | produces an acid by irradiation of actinic light or a radiation is a compound represented by the following general formula (ZI-3) or (ZI-4) in any one of Claims 1-8. The pattern formation method as described.

In general formula (ZI-3),
R _{1c to} R _5c are each independently a hydrogen atom, alkyl group, cycloalkyl group, aryl group, alkoxy group, aryloxy group, alkoxycarbonyl group, alkylcarbonyloxy group, cycloalkylcarbonyloxy group, halogen atom, hydroxyl group Represents a nitro group, an alkylthio group or an arylthio group.
R _6c and R _7c each independently represents a hydrogen atom, an alkyl group, a cycloalkyl group, a halogen atom, a cyano group or an aryl group.
R _x and R _y each independently represents an alkyl group, a cycloalkyl group, a 2-oxoalkyl group, a 2-oxocycloalkyl group, an alkoxycarbonylalkyl group, an allyl group, or a vinyl group.
Any two or more of R _{1c to} R _5c , R _5c and R _6c , R _6c and R _7c , R _5c and R _x , and R _x and R _y are bonded to each other to form a ring structure It may be formed.
Z ⁻ represents a non-nucleophilic anion.
In general formula (ZI-4),
R ₁₃ represents a hydrogen atom, a fluorine atom, a hydroxyl group, an alkyl group, a cycloalkyl group, an alkoxy group, an alkoxycarbonyl group, or a group having a cycloalkyl group.
When there are a plurality of R _{14 s,} each independently represents a group having a hydroxyl group, an alkyl group, a cycloalkyl group, an alkoxy group, an alkoxycarbonyl group, an alkylcarbonyl group, an alkylsulfonyl group, a cycloalkylsulfonyl group, or a cycloalkyl group. Represent.
R ₁₅ each independently represents an alkyl group, a cycloalkyl group or a naphthyl group. Two R ₁₅ may be bonded to each other to form a ring.
l represents an integer of 0-2.
r represents an integer of 0 to 8.
Z ⁻ represents a non-nucleophilic anion. (B) The compound which generate | occur | produces an acid by irradiation of actinic light or a radiation is a compound which generate | occur | produces the acid represented by the following general formula (IIIB) or (IVB) by irradiation of actinic light or a radiation. 10. The pattern forming method according to any one of 9 above.

In the general formula (IIIB),
Xf each independently represents a fluorine atom or an alkyl group substituted with at least one fluorine atom.
R ₁ and R ₂ each independently represents a hydrogen atom or an alkyl group.
When a plurality of L's are present, each independently represents a divalent linking group.
Cy represents a cyclic organic group.
x represents an integer of 1 to 20.
y represents an integer of 0 to 10.
z represents an integer of 0 to 10.
In the general formula (IVB),
Xf each independently represents a fluorine atom or an alkyl group substituted with at least one fluorine atom.
R ₁ and R ₂ each independently represents a hydrogen atom or an alkyl group.
When a plurality of L's are present, each independently represents a divalent linking group.
Cy represents a cyclic organic group.
Rf represents a group containing a fluorine atom.
x represents an integer of 1 to 20.
y represents an integer of 0 to 10.
z represents an integer of 0 to 10.   The pattern forming method according to claim 1, wherein the exposure is performed using an ArF excimer laser.   The pattern forming method according to claim 11, wherein the exposure is performed through an immersion liquid.   The manufacturing method of an electronic device containing the pattern formation method of any one of Claims 1-12.   An electronic device manufactured by the method for manufacturing an electronic device according to claim 13.   (A) a resin containing at least one repeating unit (a) having a polycyclic aromatic structure, a resin whose dissolution rate in an alkaline developer is increased by the action of an acid, and (B) an acid by irradiation with actinic rays or radiation. An actinic ray-sensitive or radiation-sensitive film having a film thickness of 80 nm or less comprising an actinic ray-sensitive or radiation-sensitive resin composition containing a generated compound.   An actinic ray-sensitive or radiation-sensitive resin composition used for forming an actinic ray-sensitive or radiation-sensitive film having a thickness of 80 nm or less, wherein (A) a repeating unit having a polycyclic aromatic structure (a) An actinic ray-sensitive or radiation-sensitive resin containing a compound that increases the dissolution rate in an alkaline developer by the action of an acid, and (B) a compound that generates an acid upon irradiation with an actinic ray or radiation Composition.