JP2013060641A - Chemical conversion-treated plated steel sheet and method for production thereof - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide a chemical conversion-treated Al-based plated steel sheet having a chemical conversion-treated film including organic resins, and excellent in all of weatherability, water resistance, coating film adhesion and processability.SOLUTION: The chemical conversion-treated film 120' having a thickness of 0.5-10 μm is formed by coating a chemical conversion treatment liquid 120 on the surface of an Al-based alloy plated steel sheet 110 and drying. The chemical conversion treatment liquid 120 contains: a fluorine-containing olefinic resin 122 including 0.05-5 mass% hydrophilic functional group and 7-20 mass% F atom and having a number-average molecular weight within the range from 1,000 to 2,000,000; any of oxyacid salts, fluorides, hydroxides, organic acid salts, carbonates or peroxide salts of group 4A metals; and resin particles having the average grain size of 0.1-10 μm. The amount of the above salts of the group 4A metals relative to the fluorine-containing olefinic resin in the chemical conversion treatment liquid is within the range of 0.1-5 mass% in terms of metal.

Description

  The present invention relates to a chemically treated Al-based plated steel sheet having excellent weather resistance, water resistance, film adhesion and workability, and a method for producing the same.

  In order to prevent galling during the forming process, the plated steel sheet may be formed with a chemical conversion treatment film containing an organic resin (see, for example, Patent Documents 1 and 2). Patent Documents 1 and 2 describe that a chemical conversion treatment film containing an organic resin such as a urethane resin is formed on the surface of a zinc-based plated steel sheet. Thus, by covering the surface of the plated steel sheet with a chemical conversion treatment film containing an organic resin, not only galling resistance but also corrosion resistance and discoloration resistance can be improved.

  On the other hand, in order to improve the weather resistance of the chemical conversion treatment plated steel sheet, a fluororesin having excellent weather resistance may be used as an organic resin constituting the chemical conversion treatment film. Thus, when using a fluororesin for the purpose of an improvement in a weather resistance, an organic solvent type fluororesin composition is used in many cases. However, such organic solvent-based fluororesin compositions have problems such as fire hazard and harmfulness and air pollution.

  Various water-based fluororesin compositions have also been proposed (see, for example, Patent Document 3). However, all such water-based fluororesin compositions require baking at a high temperature (for example, 180 to 230 ° C., see Patent Document 3). Such high-temperature baking is practically impossible in field painting (usually using a normally dry resin), and is disadvantageous even in factory lines where heat drying is the mainstream.

  Furthermore, in order to solve the problems of the water-based fluororesin composition, a water-based fluororesin composition capable of forming a film even at a low temperature by introducing a curable site (organic functional group) has been proposed (for example, Patent Document 4). reference). However, in a film cured by reacting with an organic functional group, the weather resistance deteriorates preferentially from the cured portion, so that the film becomes porous and water resistance decreases. In addition, when the base treatment with an epoxy resin or a urethane resin is performed for improving the adhesion, the organic resin is preferentially deteriorated in weather resistance, and the film adhesion is rapidly lowered. .

JP 2005-15834 A JP 2005-206764 A JP-A-57-38845 JP-A-5-202260

  As described above, by forming a chemical conversion treatment film containing an organic resin on the surface of a plated steel sheet, it is possible to improve galling resistance, corrosion resistance, adhesion of a film (coating film) formed thereon, and the like. However, the conventional chemical conversion treatment plated steel sheet formed with the chemical conversion treatment film containing the organic resin sometimes has insufficient weather resistance when used as an exterior building material. In other words, since many organic resins such as urethane resins are deteriorated by ultraviolet rays, when a conventional chemical conversion-treated plated steel sheet is used as an exterior building material, the chemical conversion film covering the surface of the plated steel sheet is lost over time. There is a risk that. If the chemical conversion treatment film is lost in this manner, discoloration, rust, etc. may occur and the appearance may be impaired, which is not preferable as an exterior building material.

  As a means for improving the weather resistance of such a chemically treated steel sheet, it is conceivable to use a fluororesin excellent in weather resistance as an organic resin constituting the chemical conversion film. Then, this inventor performed the preliminary experiment which forms a chemical conversion treatment film on the surface of a plated steel plate using the emulsion of the water-based fluororesin which is easy to handle. As a result, it was possible to improve the ultraviolet resistance by using an emulsion of a water-based fluororesin, but on the other hand, the film forming property, water resistance and film adhesion were lowered. As a result of further studies by the present inventors, these deteriorations in quality are because an emulsifier (for example, perfluorooctanoic acid ammonium salt) used in producing an aqueous fluororesin emulsion remains in the chemical conversion film. (See the reference experiment below).

  As mentioned above, the conventional chemical conversion treatment plating steel plate in which the chemical conversion treatment film containing an organic resin was formed might have insufficient weather resistance. In addition, the use of water-based fluororesin as the organic resin can improve the weather resistance (ultraviolet light resistance) of the chemically treated steel sheet, but on the other hand, the film forming property, water resistance and film adhesion are reduced. Therefore, it was impossible to achieve both weather resistance, water resistance and film adhesion.

  This invention is made | formed in view of this point, and is a chemical conversion treatment Al type plated steel plate which has a chemical conversion treatment film containing an organic resin, and is excellent in all of weather resistance, water resistance, film adhesion, and workability. It is providing the chemical conversion treatment Al system plating steel plate.

  The present inventor uses a high molecular weight fluorine-containing resin into which a hydrophilic functional group is introduced as an organic resin, and crosslinks these fluorine-containing resins with a group 4A metal compound, thereby enabling the weather resistance and water resistance of the chemical conversion coating. The present invention has been completed through further investigations.

That is, the 1st of this invention is related with the following chemical conversion treatment Al-plated steel plates.
[1] A chemical conversion treatment Al-based steel having an Al-based alloy-plated steel sheet containing 85 to 99% by mass of Al, and a chemical conversion film having a thickness of 0.5 to 10 μm formed on the surface of the Al-based alloy-plated steel sheet It is a plated steel sheet; the chemical conversion treatment film contains 0.05 to 5 mass% of a hydrophilic functional group selected from the group consisting of a carboxyl group, a sulfonic acid group, and a salt thereof, and 7 to 20 mass% of F atoms. A fluorine-containing resin, 0.1 to 5% by mass of a 4A group metal compound in terms of metal with respect to the fluorine-containing resin, and resin particles having an average particle diameter of 0.1 to 10 μm; The area-occupancy ratio of the resin particles on the surface of the steel sheet is a chemical conversion-treated Al-based plated steel sheet that is 0.1 area% or more.
[2] The chemical conversion treatment Al-based plating according to [1], wherein the ratio of the carboxyl group and the sulfonic acid group of the fluorine-containing resin is within a range of 5 to 60 in terms of a molar ratio of carboxyl group / sulfonic acid group. steel sheet.
[3] The chemical conversion-treated Al-plated steel sheet according to [1] or [2], wherein the resin particles are polyethylene-fluororesin particles in which fluororesin fine particles are bonded to the surface of polyethylene resin particles.
[4] The chemical conversion coating further contains a polyethylene resin; the polyethylene-fluororesin particles protrude from the surface of the chemical conversion coating in a part of the surface of the chemical conversion coating; The chemical conversion treatment Al-plated steel sheet according to [3], which covers all or part of the remaining surface of the chemical conversion treatment film.
[5] The chemical conversion film further contains a phosphate; the amount of the phosphate with respect to the fluorine-containing resin is in the range of 0.05 to 3% by mass in terms of P, [1] to [4] The chemical conversion treatment Al-plated steel sheet according to any one of [4].
[6] The chemical conversion treatment film further contains a silane coupling agent; the amount of the silane coupling agent with respect to the fluorine-containing resin is in the range of 0.5 to 5% by mass. 5]. The chemical conversion treatment Al-plated steel sheet according to any one of 5).
[7] The chemical conversion treatment Al-plated steel sheet according to any one of [1] to [6], wherein the 4A group metal is selected from the group consisting of Ti, Zr, Hf, and combinations thereof.
[8] An underlayer chemical conversion film formed between the Al-based alloy-plated steel sheet and the chemical conversion film and containing a valve metal oxide or hydroxide and a valve metal fluoride, The chemical conversion treatment Al-plated steel sheet according to any one of [1] to [7].

2nd of this invention is related with the manufacturing method of the following chemical conversion treatment Al-plated steel plate.
[9] A step of preparing an Al-based alloy-plated steel sheet containing 85 to 99% by mass of Al, and a chemical conversion treatment liquid is applied to the surface of the Al-based alloy-plated steel sheet and dried to have a film thickness of 0.5 to 10 μm. The chemical conversion treatment solution is formed by adding 0.05 to 5% by mass of a hydrophilic functional group selected from the group consisting of a carboxyl group, a sulfonic acid group, and a salt thereof, and 7 to 7 F atoms. A fluorine-containing resin containing 20% by mass and having a number average molecular weight in the range of 1,000 to 2,000,000, and a group 4A metal oxyacid salt, fluoride, hydroxide, organic acid salt, carbonate or peroxide Any one of the salts and resin particles having an average particle diameter of 0.1 to 10 μm; the oxyacid salt, fluoride, hydroxide, organic acid salt, carbonate of the group 4A metal with respect to the fluorine-containing resin Or the amount of peroxide is metal equivalent The amount of the resin particles with respect to the solid content in the chemical conversion treatment liquid is in the range of 0.1 to 5% by mass; Production method.
[10] The chemical conversion treatment Al plating according to [9], wherein the ratio of the carboxyl group and the sulfonic acid group of the fluorine-containing resin is in the range of 5 to 60 in terms of a molar ratio of carboxyl group / sulfonic acid group. A method of manufacturing a steel sheet.
[11] The method for producing a chemically treated Al-based plated steel sheet according to [9] or [10], wherein the resin particles are polyethylene-fluorine resin particles in which fluororesin fine particles are bonded to the surface of polyethylene resin particles.
[12] The chemical conversion treatment liquid manufacturing method according to [11], wherein the chemical conversion treatment liquid further contains polyethylene resin particles.
[13] The chemical conversion treatment liquid further contains a phosphate; the amount of the phosphate with respect to the fluorine-containing resin is in the range of 0.05 to 3% by mass in terms of P, [9] to The manufacturing method of the chemical conversion treatment Al-plated steel plate as described in any one of [12].
[14] The chemical conversion treatment liquid further contains a silane coupling agent; the amount of the silane coupling agent with respect to the fluorine-containing resin is in the range of 0.5 to 5% by mass, [9] to [9] 13] The manufacturing method of the chemical conversion treatment Al-plated steel plate as described in any one of [13].
[15] The method for producing a chemically treated Al-based plated steel sheet according to any one of [9] to [14], wherein the 4A group metal is selected from the group consisting of Ti, Zr, Hf, and combinations thereof.
[16] Before the step of forming the chemical conversion treatment film, the method further includes the step of applying a base chemical conversion treatment solution to the surface of the Al-based alloy plated steel sheet and drying to form a base chemical conversion treatment film; A chemical conversion liquid is a manufacturing method of the chemical conversion treatment Al-plated steel plate as described in any one of [9]-[15] containing a valve metal salt and a fluoride ion.

  ADVANTAGE OF THE INVENTION According to this invention, the chemical conversion treatment Al type plated steel plate which is excellent in all of a weather resistance, water resistance, film | membrane adhesiveness, and workability can be provided. The chemical conversion treated Al-based plated steel sheet of the present invention is useful as, for example, a plated steel sheet for exterior building materials because it is excellent in weather resistance, water resistance, corrosion resistance, discoloration resistance and workability.

1A to 1D are SEM images of a chemical conversion film containing polyethylene resin particles or polyethylene-fluorine resin particles heated at a predetermined temperature. 2A to 2C are schematic cross-sectional views showing the formation process of the chemical conversion coating. 3A to 3C are SEM images showing the formation process of the chemical conversion film. It is a fluorescence X-ray spectrum of the polyethylene- fluorine resin particle in a chemical conversion treatment film. It is a graph which shows the relationship between the quantity of the 4A group metal in a fluororesin membrane | film | coat, and moisture permeability. It is a graph which shows the relationship between the density | concentration of the emulsifier in the emulsion of fluorine-containing resin, and the water vapor transmission rate of a fluorine resin film.

1. Chemical conversion treatment Al-plated steel sheet The chemical conversion treatment Al-plated steel sheet of the present invention has an Al-based alloy-plated steel sheet (chemical conversion-treated original sheet) and a chemical conversion-treated film formed on the surface of the Al-based alloy-plated steel sheet. The chemical conversion treatment Al-plated steel sheet of the present invention comprises a high molecular weight fluorine-containing resin, a group 4A metal compound and a resin particle (lubricant) in which a chemical conversion treatment film has introduced a hydrophilic functional group (such as a carboxyl group or a sulfonic acid group). Inclusion is a feature.

  Hereafter, each component of the chemical conversion treatment Al-plated steel plate of this invention is demonstrated.

[Chemical conversion treatment master]
As the chemical conversion treatment original plate, an Al-based alloy plated steel plate having excellent corrosion resistance and design properties is used. Here, the “Al-based alloy-plated steel sheet” means a steel sheet that contains 85 to 99% by mass of Al and the balance is substantially an Si-based alloy-plated layer of Si. Examples of the Al-based alloy-plated steel sheet include a molten Al-9% Si-plated steel sheet.

  Low carbon steel, medium carbon steel, high carbon steel, alloy steel, etc. are used as the base steel of the Al-based alloy plated steel sheet. When workability is required, steel sheets for deep drawing such as low carbon Ti-added steel and low carbon Nb-added steel are preferred as the base steel.

[Base chemical conversion coating]
On the surface of an Al-based alloy-plated steel sheet used as a chemical conversion treatment original plate, an underlying chemical conversion treatment film containing a valve metal oxide or hydroxide and a valve metal fluoride may be formed. Thus, when the foundation | substrate chemical conversion treatment film is formed in the surface of an Al type alloy plating steel plate, a chemical conversion treatment film is formed in the surface of an Al type alloy plating steel plate through a foundation | substrate chemical conversion treatment film.

  Valve metal oxides and hydroxides exhibit high insulation resistance. For this reason, the foundation | substrate chemical conversion treatment film containing the oxide or hydroxide of valve metal acts as a resistor with respect to the movement of an electron. Therefore, the reduction reaction of dissolved oxygen contained in the moisture in the atmosphere is suppressed, and the oxidation reaction of the paired Al-based alloy plated steel sheet is also suppressed. As a result, elution (corrosion) of metal components from the Al-based alloy-plated steel sheet as the base material is suppressed. Especially, the tetravalent compound of IV group A element, such as Ti, Zr, and Hf, is a stable compound, and forms the outstanding highly insulating film.

  In addition, a film defect is inevitably generated in a chemical conversion treatment film at the time of chemical conversion treatment or molding. Since the base material is exposed at the film defect portion, a corrosion inhibiting action cannot be expected even if chemical conversion treatment is performed. On the other hand, since the above-mentioned base chemical conversion treatment film also contains a fluoride of valve metal, it has a self-repairing action. That is, the fluoride of the valve metal dissolves in moisture in the atmosphere and then re-deposits as a hardly soluble oxide or hydroxide on the surface of the base steel exposed from the film defect portion. As a result, since the film defect portion is filled, a self-repairing action is exhibited.

  Although the chemical conversion treatment Al-plated steel plate of this invention is manufactured by performing chemical conversion treatment to the Al alloy-plated steel plate, the Al-based alloy plated steel plate before chemical conversion treatment has insufficient corrosion resistance. Therefore, corrosion may occur during storage or transportation of the Al-based alloy-plated steel sheet before chemical conversion treatment or during forming. Therefore, by forming a base chemical conversion coating on the Al-based alloy plated steel sheet before chemical conversion, it is possible to reliably prevent the occurrence of corrosion in the Al-based alloy plated steel sheet before chemical conversion.

  When the Al-based alloy-plated steel sheet on which the base chemical conversion treatment film is formed is stored, transported, or formed (including welding), some of the base chemical conversion treatment film may be peeled off, missing, or missing. As a result, the surface of the Al-based alloy-plated steel sheet is exposed, and the chemical conversion treatment film containing the fluorine-containing resin and the 4A group metal compound is in direct contact with the exposed surface.

  The base chemical conversion treatment film has an effect of improving the adhesion between the Al-based alloy plated steel sheet and the chemical conversion treatment film. For this reason, the chemical conversion treatment film formed at the place where the base chemical conversion treatment film is peeled is generally considered to have a reduced film adhesion. However, in the chemical conversion treatment film, Al eluted from the plating layer in direct contact exists. And the presence of this Al improves the corrosion resistance and film adhesion of the chemical conversion film. In other words, the corrosion resistance and adhesion of the chemical conversion coating are hardly reduced even at the location where the base chemical conversion coating peels off and exhibits the effect of improving the adhesion between the Al-based alloy plated steel sheet and the chemical conversion coating. The The mechanism by which the presence of Al in the chemical conversion film improves the corrosion resistance and film adhesion of the chemical conversion film will be described later.

  The base chemical conversion treatment film can be formed by drying a coating film of the base chemical conversion treatment liquid formed on the surface of the Al-based alloy-plated steel sheet as the base material. The base chemical conversion treatment solution contains valve metal salt, fluoride ions, and water as a solvent. By drying the coating film of the base chemical conversion treatment solution, the valve metal salt becomes an oxide or hydroxide or a fluoride of valve metal contained in the base chemical conversion coating film.

  Examples of the valve metal include Ti, Zr, Hf, V, Nb, Ta, Mo, and W. The valve metal salt added to the base chemical conversion treatment liquid may be a valve metal halide or oxyacid salt. If the added valve metal salt is fluoride, it also acts as a fluoride ion source.

Examples of titanium salts include K _n TiF ₆ (K: alkali metal or alkaline earth metal, n: 1 or 2), K ₂ [TiO (COO) ₂ ], (NH ₄ ) ₂ TiF ₆ , TiCl ₄ , TiOSO ₄ , Ti (SO ₄ ) ₂ , Ti (OH) _{4 and the} like are included. On the other hand, the fluoride ion source contained in the base chemical conversion treatment liquid may be a valve metal salt containing fluorine atoms, or may be a separate soluble fluoride (for example, (NH ₄ ) F).

  It is preferable that an organic acid having a chelating action is added to the base chemical conversion treatment solution in order to stabilize the valve metal salt. The organic acid can chelate metal ions and stabilize the chemical conversion solution. Therefore, the addition amount of the organic acid is set so that the molar ratio of organic acid / metal ion is 0.02 or more. Examples of the organic acid include tartaric acid, tannic acid, citric acid, succinic acid, malonic acid, lactic acid, acetic acid, ascorbic acid and the like. Among them, oxycarboxylic acids such as tartaric acid and polyhydric phenols such as tannic acid stabilize the base chemical conversion solution and also complement the fluoride's self-healing action, improving adhesion. It is valid.

  Various chemical orthophosphates or polyphosphates may be added to the base chemical conversion treatment solution. This is because the chemical conversion film contains a soluble or hardly soluble metal phosphate or composite phosphate.

  Soluble metal phosphate or composite phosphate elutes from the base chemical conversion coating to the film defects and reacts with the plating components (such as Al) of the Al-based alloy-plated steel sheet as the base material, resulting in insoluble phosphoric acid. Precipitate the salt. In this way, the self-healing action of titanium fluoride is complemented. Further, since the atmosphere is slightly acidified when the soluble phosphate is dissociated, the hydrolysis of titanium fluoride, and hence the generation of hardly soluble titanium oxide or hydroxide, is promoted.

  The metal of the soluble phosphate or composite phosphate can be an alkali metal, an alkaline earth metal, Mn, and the like. The soluble phosphate or composite phosphate may be added to the base chemical conversion treatment liquid in the form of various metal phosphates, or various metal salts may be combined with phosphoric acid, polyphosphoric acid, or phosphate. You may add to a chemical conversion liquid.

  On the other hand, the hardly soluble metal phosphate or composite phosphate is dispersed in the base chemical conversion treatment film to eliminate film defects and improve the film strength. The metal of the poorly soluble phosphate or the composite phosphate may be Al, Ti, Zr, Hf, Zn or the like. The hardly soluble phosphate or the composite phosphate may be added to the chemical conversion treatment liquid in the form of various metal phosphates, or a chemical conversion treatment by combining various metal salts with phosphoric acid, polyphosphoric acid or phosphate. It may be added to the liquid.

  Organic chemical waxes such as fluorine, polyethylene, and styrene, inorganic lubricants such as silica, molybdenum disulfide, and talc can be added to the base chemical conversion treatment liquid. By adding these, the lubricity of the base chemical conversion coating can be improved. It is considered that the low melting point organic wax bleeds on the film surface and develops lubricity when the coating film of the base chemical conversion treatment liquid is dried. On the other hand, high-melting organic waxes and inorganic lubricants are present in a dispersed state in the film, but it is considered that the outermost surface layer of the film is exposed to the surface of the film in an island-like distribution to exhibit lubricity.

  When the base chemical conversion film obtained by drying the coating film of the base chemical conversion liquid is subjected to elemental analysis using fluorescent X-ray, ESCA, or the like, the concentrations of O and F contained in the base chemical conversion film are measured. The element concentration ratio F / O (atomic ratio) is preferably 1/100 or more. It is for suppressing the corrosion of the obtained chemical conversion treatment steel plate. In particular, when the element concentration ratio F / O (atomic ratio) is 1/100 or more, the occurrence of corrosion starting from a film defect portion is significantly reduced. This is presumably because a sufficient amount of titanium fluoride is contained in the base chemical conversion treatment film and exhibits a self-repairing action.

[Chemical conversion coating]
The chemical conversion treatment film is formed on the surface of the above-described Al-based alloy plated steel plate (chemical conversion treatment original plate). The surface of the chemical conversion treatment original plate may be subjected to a base chemical conversion treatment such as forming a coating as a base, but the base chemical conversion treatment may not be performed. In addition, when the surface chemical conversion treatment is not performed on the surface of the chemical conversion treatment original plate, a chemical conversion treatment film is directly formed on the surface of the chemical conversion treatment original plate. This chemical conversion film improves the weather resistance, water resistance, workability (lubricity), and the like of the Al-based alloy plated steel sheet.

  The object of the present invention is to improve all of the weather resistance, water resistance, film adhesion and workability of the chemical conversion treated Al-plated steel sheet. As described above, in order to improve the weather resistance (ultraviolet light resistance) of the chemical conversion coating, a fluorine-containing resin may be used as the organic resin. Fluorine-containing resins are roughly classified into solvent-based fluorine-containing resins and water-based fluorine-containing resins. When a chemical conversion film is formed using a solvent-based fluorine-containing resin, recovery of the volatilized solvent becomes a problem, but when a water-based fluorine-containing resin is used, such a problem does not occur. Then, this inventor tried to form the chemical conversion treatment Al-plated steel plate excellent in all of weather resistance, water resistance, film | membrane adhesiveness, and workability using the water-type fluorine-containing resin which is easy to handle.

  As described above, according to the preliminary experiment of the present inventor, when a chemical conversion film is formed using an emulsion of a water-based fluorine-containing resin, the water resistance decreases when an emulsion of a water-based fluorine-containing resin is produced. It was considered that the emulsifier used remained in the chemical conversion film (see the reference experiment described later). Then, this inventor thought that the fall of the water resistance of a chemical conversion treatment film could be suppressed if the emulsion of water-type fluorine-containing resin could be manufactured, using few emulsifiers. And as a result of studying various water-based fluorine-containing resins, the present inventor is able to produce water-based emulsions with little use of emulsifiers. It has been found that a chemical conversion treatment film containing almost no can be easily formed.

  Moreover, this inventor examined not only suppressing the fall of the water resistance of a chemical conversion treatment film but improving water resistance. As a result of studying from various viewpoints, it was found that the water resistance of the chemical conversion coating can be remarkably improved by increasing the molecular weight of the aqueous fluorine-containing resin and crosslinking the aqueous fluorine resin with a group 4A metal compound. It was.

  And this inventor is adding weather resistance, water resistance, and film | membrane adhesiveness by mix | blending a 4A group metal compound further with the chemical conversion liquid based on the high molecular weight fluorine-containing resin which introduce | transduced the hydrophilic functional group. It was found that a chemical conversion treatment film compatible with the above can be formed.

  Furthermore, this inventor examined improving the workability (lubricity) of a chemical conversion treatment Al-plated steel plate. And as a result of studying various means, the present inventor dispersed resin particles having an average particle diameter of 0.1 to 10 μm in the chemical conversion film, in addition to weather resistance, water resistance and film adhesion. Furthermore, they have found that a chemical conversion film excellent in workability (lubricity) can be formed.

  In the chemical conversion coating of the chemical conversion treated Al-plated steel sheet of the present invention, 1) Weather resistance (ultraviolet resistance) is improved by blending a fluorine-containing resin (preferably a fluorine-containing olefin resin). In addition, 2) the use of a fluorine-containing resin into which a hydrophilic functional group has been introduced reduces the use of an emulsifier during emulsion production, 3) the molecular weight of the fluorine-containing resin is increased, and 4) the fluorine-containing resin is 4A. By cross-linking with a group metal compound, weather resistance (ultraviolet light resistance) and water resistance are improved. 5) Workability (lubricity) is improved by dispersing resin particles having an average particle diameter of 0.1 to 10 μm.

  Hereinafter, each component contained in the chemical conversion treatment film will be described.

1) Water-based fluorine-containing resin The chemical conversion film contains a fluorine-containing resin, more specifically, a fluorine-containing olefin resin as a main component. The amount of the fluorine-containing resin contained as a main component in the chemical conversion film is preferably in the range of 70 to 99% by mass. As described above, by using a fluorine-containing resin as the organic resin constituting the chemical conversion coating, the weather resistance (ultraviolet resistance) of the chemical conversion coating can be improved.

  The fluorine-containing resin is preferably a water-based fluorine-containing resin that is easier to handle than the organic solvent-based fluorine resin. “Aqueous fluorine-containing resin” refers to a fluorine-containing resin having a hydrophilic functional group. Preferred examples of the hydrophilic functional group include a carboxyl group, a sulfonic acid group, and salts thereof. Examples of the salt of the carboxyl group or sulfonic acid group include ammonium salt, amine salt, alkali metal salt and the like.

  Preferred aqueous fluorine-containing resins (preferably fluorine-containing olefin resins) have a hydrophilic functional group of 0.05 to 5% by mass. A fluorine-containing resin having 0.05 to 5% by mass of a hydrophilic functional group can be made into an aqueous emulsion without using an emulsifier. The chemical conversion film containing almost no emulsifier can be a chemical conversion film excellent in water resistance.

  The content of the hydrophilic functional group in the aqueous fluorine-containing resin may be obtained by dividing the total molar mass of the hydrophilic functional group contained in the aqueous fluorine-containing resin by the number average molecular weight of the aqueous fluorine-containing resin. Since the molar mass of the carboxyl group is 45 and the molar mass of the sulfonic acid group is 81, the number of each of the carboxyl group and sulfonic acid group contained in the aqueous fluorine-containing resin is determined, and each is multiplied by the molar mass. The total molar mass of the hydrophilic functional group contained in the aqueous fluorine-containing resin is obtained. The number average molecular weight of the water-based fluorine-containing resin is measured by GPC.

The carboxyl group in the water-based fluorine-containing resin forms a hydrogen bond with the plating layer surface and contributes to improving the adhesion between the chemical conversion film and the plating layer surface. However, since H ⁺ is difficult to dissociate, The cross-linking reaction is unlikely to occur. On the other hand, the sulfonic acid group in the water-based fluorine-containing resin tends to dissociate H ^+, but if it remains unreacted in the film without cross-linking reaction with the group 4A metal compound, the water molecule adsorbing action is strong, so There is a risk that the water resistance will be significantly reduced. Therefore, it is preferable that the water-based fluorine-containing resin includes both a carboxyl group and a sulfonic acid group in order to make use of each feature. In this case, the ratio of the carboxyl group to the sulfonic acid group is preferably in the range of 5 to 60 in terms of the molar ratio of carboxyl group / sulfonic acid group.

  The number average molecular weight of the water-based fluorine-containing resin (preferably fluorine-containing olefin resin) contained in the chemical conversion coating is preferably 1000 or more, more preferably 10,000 or more, and particularly preferably 200,000 or more.

  If the molecular weight of the water-based fluorine-containing resin contained in the chemical conversion coating is too small, the water permeability and water resistance of the chemical conversion coating cannot be sufficiently improved. In such a case, moisture or corrosive gas easily penetrates the chemical conversion coating and reaches the plated steel sheet, so that the plated steel sheet may be easily corroded. In addition, when an aqueous fluorine-containing resin with a low molecular weight is used, radicals generated by the action of light energy or the like are likely to act on the end of the polymer chain, so the aqueous fluorine-containing resin is easily hydrolyzed by a synergistic action such as water. There is a risk of being. In order to prevent these problems, the molecular weight of the aqueous fluorine-containing resin contained in the chemical conversion coating may be increased to some extent, or a crosslinked structure may be formed between the aqueous fluorine-containing resins. By increasing the molecular weight of the water-based fluorine-containing resin, the intermolecular force increases and the cohesive strength of the chemical conversion coating increases, so that the water resistance is improved. Moreover, since the bond between atoms in the main chain of the water-based fluorine-containing resin is stabilized, hydrolysis is less likely to occur.

  On the other hand, the number average molecular weight of the water-based fluorine-containing resin contained in the chemical conversion coating is preferably 2 million or less. When the number average molecular weight exceeds 2 million, there is a possibility that a problem may occur in the stability of the treatment liquid such as gelation.

  The content of F atoms in the aqueous fluorine-containing resin contained in the chemical conversion film is preferably in the range of 7 to 20% by mass. When content of F atom is less than 7 mass%, the weather resistance of a chemical conversion treatment film cannot fully be improved. On the other hand, when the content of F atoms is more than 20% by mass, it is difficult to form a paint and the adhesion and drying properties may be reduced. The content of F atoms in the aqueous fluorine-containing resin can be measured by using a fluorescent X-ray analyzer.

  Examples of the aqueous fluorine-containing resin include a copolymer of a fluoroolefin and a hydrophilic functional group-containing monomer. The hydrophilic functional group-containing monomer is a carboxyl group-containing monomer or a sulfonic acid group-containing monomer.

  Examples of fluoroolefins include tetrafluoroethylene, trifluoroethylene, chlorotrifluoroethylene, hexafluoropropylene, vinyl fluoride, vinylidene fluoride, pentafluoropropylene, 2,2,3,3-tetrafluoropropylene, 3, 3,3-trifluoropropylene, bromotrifluoroethylene, 1-chloro-1,2-difluoroethylene, 1,1-dichloro-2,2-difluoroethylene and the like are included. These fluoroolefins may be used alone or in combination of two or more. From the viewpoint of weather resistance (ultraviolet light resistance), among these fluoroolefins, perfluoroolefins such as tetrafluoroethylene and hexafluoropropylene, and vinylidene fluoride are preferable. Fluoroolefins containing chlorine such as chlorotrifluoroethylene are not preferred because corrosion due to chlorine ions may occur.

Examples of the carboxyl group-containing monomer include unsaturated carboxylic acids represented by the following formula (1) and unsaturated carboxylic acids such as esters or acid anhydrides thereof.
(In formula, R < ¹ >, R < ² > and R < ³ > are the same or different, and all are a hydrogen atom, an alkyl group, a carboxyl group, or an ester group. N is in the range of 0-20.)

  Examples of the unsaturated carboxylic acid represented by the above formula (1) include acrylic acid, methacrylic acid, vinyl acetic acid, crotonic acid, cinnamic acid, itaconic acid, itaconic acid monoester, maleic acid, maleic acid monoester, fumaric acid , Fumaric acid monoester, 5-hexenoic acid, 5-heptenoic acid, 6-heptenoic acid, 7-octenoic acid, 8-nonenoic acid, 9-decenoic acid, 10-undecylene acid, 11-dodecylene acid, 17-octadecylenic acid Oleic acid and the like.

Another example of the carboxyl group-containing monomer is a carboxyl group-containing vinyl ether monomer represented by the following formula (2).
(Wherein R ⁴ and R ⁵ are the same or different, and each is a saturated or unsaturated linear or cyclic alkyl group. N is 0 or 1. m is 0 or 1.)

  Examples of the carboxyl group-containing vinyl ether monomer represented by the above formula (2) include 3- (2-allyloxyethoxycarbonyl) propionic acid, 3- (2-allyloxybutoxycarbonyl) propionic acid, 3- (2-vinylidene). Roxyethoxycarbonyl) propionic acid, 3- (2-vinyloxybutoxycarbonyl) propionic acid and the like.

  Examples of sulfonic acid group-containing monomers include vinyl sulfonic acid, allyl sulfonic acid, methallyl sulfonic acid, styrene sulfonic acid, 2-acrylamido-2-methylpropane sulfonic acid, 2-methacryloyloxyethane sulfonic acid, and 3-methacryloyloxy. Propanesulfonic acid, 4-methacryloyloxybutanesulfonic acid, 3-methacryloyloxy-2-hydroxypropanesulfonic acid, 3-acryloyloxypropanesulfonic acid, allyloxybenzenesulfonic acid, methallyloxybenzenesulfonic acid, isoprenesulfonic acid, Examples include 3-allyloxy-2-hydroxypropanesulfonic acid.

  The copolymer of the fluoroolefin and the hydrophilic functional group-containing monomer may be further copolymerized with another copolymerizable monomer as necessary. Examples of other copolymerizable monomers include carboxylic acid vinyl esters, alkyl vinyl ethers, and non-fluorinated olefins.

  Carboxylic acid vinyl esters can improve compatibility and gloss and increase the glass transition temperature. Examples of vinyl carboxylates include vinyl acetate, vinyl propionate, vinyl butyrate, vinyl isobutyrate, vinyl pivalate, vinyl caproate, vinyl versatate, vinyl laurate, vinyl stearate, vinyl cyclohexylcarboxylate, benzoate Vinyl acid, vinyl para-t-butyl benzoate and the like are included.

  Alkyl vinyl ethers can improve gloss and flexibility. Examples of the alkyl vinyl ethers include methyl vinyl ether, ethyl vinyl ether, butyl vinyl ether and the like.

  Non-fluorinated olefins can improve flexibility. Examples of non-fluorinated olefins include ethylene, propylene, n-butene, isobutene and the like.

  A fluoroolefin copolymer having a hydrophilic functional group can be obtained by copolymerizing the above monomers by a known polymerization method. At this time, by adjusting the amount of the fluoroolefin in the raw material monomer composition so that the fluoroolefin copolymer has 0.05 to 5% by mass of the hydrophilic functional group, the fluoroolefin copolymer can be used with almost no emulsifier. An aqueous emulsion of the polymer can be produced. The chemical conversion film formed using an emulsion of a fluoroolefin copolymer containing almost no emulsifier (1% by mass or less) contains almost no emulsifier.

  Thus, the chemical conversion treatment film which hardly contains an emulsifier can be easily formed by using the fluorine-containing resin having a hydrophilic functional group as the aqueous fluorine-containing resin constituting the chemical conversion treatment film. The chemical conversion film thus formed exhibits excellent water resistance with little deterioration in water resistance due to the residual emulsifier.

2) Group 4A metal compound The chemical conversion film contains a group 4A metal compound. The 4A group metal compound easily reacts with a functional group such as a carboxyl group or a sulfonic acid group in the aqueous fluorine-containing resin, and accelerates the curing or crosslinking reaction of the aqueous fluorine-containing resin. Therefore, the water resistance of the chemical conversion film can be improved even by low-temperature drying.

  When a melamine resin or an isocyanate resin is used for cross-linking of the fluorine-containing resin, there is a problem that the weather resistance is easily deteriorated. For example, in a chemical conversion treatment film cured using a melamine resin, weather resistance deterioration is immediately caused by oxidation and hydrolysis of ester bonds and form ether bonds. In addition, weathering deterioration also proceeds when the crosslinked structure is cut by an acidic substance such as sulfate ion or nitrate ion contained in acid rain. In a chemical conversion film cured using an isocyanate resin, the urethane bond formed at the cross-linked portion is weaker than the F bond, so that the cross-linked structure is preferentially cut, and the weather resistance deteriorates.

  On the other hand, by using a group 4A metal compound for crosslinking of the fluorine-containing resin, such a problem can be avoided and weather resistance can be improved.

  In addition, the group 4A metal compound also improves film adhesion and water resistance. That is, the strong Al oxide present on the surface of the Al-based alloy-plated steel sheet reduces the adhesion of the chemical conversion coating, but by adding a 4A group metal compound to the chemical conversion coating, this Al oxide coating A decrease in adhesion can be suppressed. The group 4A metal compound also serves as a supply source of group 4A metal ions that react with Al ions eluted by the etching reaction. The reaction product is concentrated at the interface between the plating layer and the chemical conversion film to improve the initial corrosion resistance. Examples of Group 4A metals include Ti, Zr, Hf, and the like.

  The content of the group 4A metal compound in the chemical conversion coating is preferably in the range of 0.1 to 5 mass% in terms of metal relative to the fluorine-containing resin. When the content is less than 0.1% by mass in terms of metal, the adverse effect due to the concentration of Al oxide cannot be sufficiently suppressed, and the aqueous fluorine-containing resin fat cannot be sufficiently crosslinked. As a result, the water resistance of the chemical conversion coating cannot be sufficiently improved. On the other hand, when the content is more than 5% by mass in terms of metal, the chemical conversion film becomes porous, and the workability and weather resistance may be reduced.

  The metal conversion amount of the group 4A metal compound in the chemical conversion coating can be measured by using a fluorescent X-ray analyzer.

As described above, Al eluted from the plating layer is present in the chemical conversion film. This Al contributes to improvement of corrosion resistance. It is presumed that the corrosion resistance is improved by the presence of Al due to the following mechanism. That is, 1) Since the chemical conversion treatment solution is weakly alkaline, when the chemical conversion treatment solution is applied, Al oxide and metal Al contained in the plating layer are selectively eluted into the chemical conversion treatment solution. 2) In the pH range of the chemical conversion treatment solution, Al dissolves in the chemical conversion treatment solution in the state of Al (OH) ₄ ⁻ . 3) When forming the chemical conversion film by drying the chemical conversion liquid, Al in the chemical conversion liquid is taken into the chemical conversion film by dehydration condensation or the like. 4) As a result, the insulating properties and density of the chemical conversion coating are improved, and the corrosion resistance is improved.

3) Resin particle The chemical conversion film contains resin particles. The resin particles are dispersed in the chemical conversion treatment film, and at least a part thereof is exposed (protruded) on the surface of the chemical conversion treatment film (see FIG. 3C). The resin particles protruding on the surface of the chemical conversion treatment film function like a “roller” during the molding process, thereby improving the lubricity of the chemical conversion treatment film surface. As a result, the workability of the chemical conversion treated Al-plated steel sheet can be improved.

  The average particle diameter of the resin particles is preferably within the range of 0.1 to 10 μm. When the average particle diameter of the resin particles is less than 0.1 μm, most of the resin particles are buried in the chemical conversion coating, so that the lubricity of the chemical conversion coating surface cannot be improved efficiently. On the other hand, when the average particle diameter of the resin particles exceeds 10 μm, the resin particles may be easily dropped during the molding process. If the resin particles fall off in this way, defects will occur in the chemical conversion film, and the corrosion resistance will be reduced. In the present specification, the average particle diameter of the resin particles means a particle diameter (median diameter) at an integrated value of 50% in a particle diameter distribution measured by a laser diffraction scattering method.

  The content of the resin particles in the chemical conversion coating is adjusted so that the area occupancy of the resin particles on the surface of the chemical conversion coating is 0.1 area% or more. If the area occupancy of the resin particles is less than 0.1 area%, the lubricity of the chemical conversion coating cannot be sufficiently improved. The area occupancy ratio of the resin particles on the surface of the chemical conversion coating can be determined by observing the surface of the chemical conversion coating with a scanning electron microscope (SEM).

  The type of resin particles is not particularly limited, but polyethylene-fluorine resin particles are preferable from the viewpoint of heat resistance and dispersibility.

  Polyethylene resin particles are excellent in dispersibility in the chemical conversion treatment liquid because of low specific gravity (for example, 0.95), but poor in heat resistance because of low melting point (for example, 123 ° C.). When resin particles having low heat resistance are used as described above, the shape of the particles may not be maintained when the chemical conversion solution is heated and dried to form a chemical conversion coating. Specifically, when the chemical conversion treatment liquid is heated and dried at about 140 to 180 ° C., the polyethylene resin particles are melted. When the resin particles are thus melted, the resin particles cannot function as “rollers” and cannot contribute to improvement of lubricity.

  On the other hand, the fluororesin particles have a high melting point (for example, 330 ° C.) and excellent heat resistance, but have a large specific gravity (for example, 2.2) and are inferior in dispersibility in the chemical conversion treatment liquid. Thus, when resin particles with low dispersibility in the chemical conversion treatment liquid are used, it becomes difficult to uniformly disperse the resin particles in the chemical conversion treatment film.

  The polyethylene-fluorine resin particles are obtained by bonding (adsorbing) fluororesin fine particles to the surface of the polyethylene resin particles by bringing the fluororesin fine particles into contact with the polyethylene resin particles softened by heating. By bonding fluororesin fine particles to the surface of the polyethylene resin particles, heat resistance to such an extent that the shape of the particles can be maintained even when heated at about 140 to 180 ° C. and dispersibility in the chemical conversion treatment liquid (specific gravity: For example, 1.1) can be made compatible. Moreover, a weather resistance can also be improved by couple | bonding a fluororesin fine particle with the surface of a polyethylene resin particle.

  FIG. 1 is an SEM image (plan view) of a chemical conversion film containing polyethylene resin particles or polyethylene-fluorine resin particles heated to 50 ° C. or 150 ° C. FIG. 1A is an SEM image of a chemical conversion coating formed by applying a chemical conversion treatment liquid containing polyethylene resin particles to the surface of a plated steel sheet and drying at 50 ° C. FIG. FIG. 1B is an SEM image of a chemical conversion film formed by applying a chemical conversion treatment liquid containing polyethylene resin particles to the surface of a plated steel sheet and drying at 150 ° C. FIG. 1C is an SEM image of a chemical conversion coating formed by applying a chemical conversion treatment liquid containing polyethylene-fluororesin particles to the surface of a plated steel sheet and drying at 50 ° C. FIG. 1D is an SEM image of a chemical conversion coating formed by applying a chemical conversion treatment liquid containing polyethylene-fluororesin particles to the surface of a plated steel sheet and drying at 150 ° C.

  As shown in FIG. 1A, when the chemical conversion treatment liquid containing polyethylene resin particles was dried at 50 ° C., the shape of the polyethylene resin particles was maintained, and the polyethylene resin particles protruded from the surface of the chemical conversion treatment film (in the figure). (See “PE”). On the other hand, as shown in FIG. 1B, when the chemical conversion treatment liquid containing polyethylene resin particles is dried at 150 ° C., the polyethylene resin particles are melted, and the polyethylene resin is uniformly distributed on the surface of the chemical conversion treatment film. (See “PE” in the figure).

  As shown in FIG. 1C, when the chemical conversion treatment liquid containing polyethylene-fluororesin particles is dried at 50 ° C., the shape of the polyethylene-fluororesin particles is maintained, and the polyethylene-fluororesin particles are removed from the surface of the chemical conversion coating. It protruded (see “PE-F” in the figure). In addition, as shown in FIG. 1D, when the chemical conversion treatment liquid containing polyethylene-fluororesin particles is dried at 150 ° C., some polyethylene-fluororesin particles (those with a small amount of fluororesin fine particles attached) are melted. However, the remaining polyethylene-fluororesin (those with a large amount of fluororesin fine particles attached) did not melt (see “PE-F” in the figure).

  Thus, when the drying temperature is low, there is no problem even with polyethylene resin particles, but when the drying temperature is high, it is preferable to use polyethylene-fluororesin particles. From the viewpoint of weather resistance, it is preferable to use polyethylene-fluororesin particles.

  The average particle diameter of the polyethylene resin particles constituting the polyethylene-fluororesin particles is not particularly limited as long as the average particle diameter of the polyethylene-fluororesin particles is within a range of 0.1 to 10 μm. Examples of commercially available polyethylene resin particles that can be used include HYTEC E-9016, HYTEC E-1000 (all are Toho Chemical Co., Ltd.), CJ-172B, CJ-137 (all are Koyo Chemical Co., Ltd.), and Permarin KUE-4. Permarin KUE-5 (both are Sanyo Chemical Industries, Ltd.). On the other hand, the average particle diameter of the fluororesin fine particles constituting the polyethylene-fluororesin particles may be appropriately set according to the average particle diameter of the polyethylene resin particles. For example, the average particle diameter of the fluororesin fine particles is preferably 0.3 μm or less.

  The ratio of the fluororesin in the polyethylene-fluororesin particles is preferably in the range of 5 to 40% by mass. When the ratio of a fluororesin is less than 5 mass%, there exists a possibility that the effect by making a fluororesin adhere cannot fully be exhibited. On the other hand, when the ratio of the fluororesin is more than 40% by mass, the polyethylene-fluororesin particles may be easily removed from the chemical conversion film. The ratio of the fluororesin in the polyethylene-fluororesin particles can be measured by using a fluorescent X-ray analyzer.

4) Polyethylene resin When the chemical conversion film contains polyethylene-fluororesin particles, the chemical conversion film preferably further contains a polyethylene resin. Usually, the polyethylene resin coats all or part of the region of the surface of the chemical conversion coating where the polyethylene-fluororesin particles do not protrude (see FIG. 2C). The polyethylene resin that coats the surface of the chemical conversion coating is a polyethylene resin that bleeds on the surface of the chemical conversion coating in the manufacturing process. A polyethylene resin particle improves the workability of a chemical conversion treatment Al-plated steel plate further by improving the lubricity of the chemical conversion treatment film surface with a polyethylene-fluorine resin particle.

  The content of the polyethylene resin in the chemical conversion coating is preferably in the range of 0.1 to 16% by mass with respect to the chemical conversion coating. When the content of the polyethylene resin is less than 0.1% by mass, the effect of the polyethylene resin cannot be exhibited sufficiently. On the other hand, when the content of the polyethylene resin is more than 16% by mass, the weather resistance may be lowered.

5) Phosphate The chemical conversion treatment film preferably further contains a phosphate. Phosphate reacts with the plating layer surface of the Al-based alloy plated steel sheet to improve the adhesion of the chemical conversion coating to the Al-based alloy plated steel sheet.

  The type of phosphate is not particularly limited as long as it is a compound having a phosphate anion and is water-soluble. Examples of phosphates include sodium phosphate, ammonium phosphate, magnesium phosphate, potassium phosphate, manganese phosphate, zinc phosphate, orthophosphoric acid, metaphosphoric acid, pyrophosphoric acid (diphosphoric acid), triphosphoric acid, Tetraphosphate etc. are included. These phosphates may be used alone or in combination of two or more.

  The content of the phosphate in the chemical conversion coating is preferably in the range of 0.05 to 3% by mass in terms of P with respect to the fluorine-containing resin. When the P conversion amount is less than 0.05% by mass, the reaction with the plating layer surface is insufficient, and the adhesion of the chemical conversion film cannot be sufficiently improved. On the other hand, when P conversion amount exceeds 3 mass%, reaction with 4A group metal compound will advance excessively, and the crosslinking effect by 4A group metal compound will be impaired.

  The P equivalent amount of phosphate in the chemical conversion coating can be measured by using a fluorescent X-ray analyzer.

6) Silane coupling agent It is preferable that a chemical conversion treatment film contains a silane coupling agent further. By mix | blending a silane coupling agent, the adhesiveness of a chemical conversion treatment film can be improved more. Silane coupling agents include silanes containing one or more functional groups such as amino, epoxy, mercapto, acryloxy, methacryloxy, alkoxy, vinyl, styryl, isocyanate, and chloropropyl groups. A compound is used.

  The content of the silane coupling agent in the chemical conversion film is preferably in the range of 0.5 to 5 mass% with respect to the fluorine-containing resin. When content of a silane coupling agent is less than 0.5 mass%, the adhesiveness of a chemical conversion treatment film cannot fully be improved. On the other hand, when the content of the silane coupling agent exceeds 5% by mass, the film adhesion is saturated and no further improvement is observed.

  The content of the silane coupling agent in the chemical conversion coating can be measured by using a fluorescent X-ray analyzer.

  The film thickness of the chemical conversion coating is preferably in the range of 0.5 to 10 μm. When the film thickness is less than 0.5 μm, sufficient corrosion resistance and discoloration resistance cannot be imparted. On the other hand, even if the film thickness exceeds 10 μm, it cannot be expected to improve the performance with the increase in film thickness.

2. The manufacturing method of the chemical conversion treatment Al-plated steel plate Although the manufacturing method of the chemical conversion treatment Al-plated steel plate of this invention is not specifically limited, For example, it can manufacture by the following method.

  The manufacturing method of the chemical conversion treatment Al-plated steel sheet of the present invention includes 1) a first step of preparing an Al-based alloy plated steel sheet (chemical conversion treatment original plate), 2) a second step of preparing a chemical conversion treatment liquid, and 3 And a third step of forming a chemical conversion film on the surface of the Al-based alloy-plated steel sheet. In addition, when forming a chemical conversion treatment film on the surface of the Al-based alloy plated steel sheet via the base chemical conversion treatment film, the surface of the Al-based alloy plated steel sheet is ground before the third step of forming the chemical conversion treatment film. The method further includes the step of forming a chemical conversion film.

[Preparation of raw material for chemical conversion treatment]
In the first step, the aforementioned Al-based alloy plated steel sheet is prepared as a chemical conversion treatment original sheet.

[Preparation of chemical conversion solution]
In the second step, a chemical conversion liquid containing a fluorine-containing resin having a hydrophilic functional group (preferably a fluorine-containing olefin resin), a group 4A metal compound, and resin particles is prepared.

  In the chemical conversion treatment liquid, a group 4A metal compound and resin particles (for example, polyethylene-fluorine resin particles) are added to an aqueous emulsion of the fluorine-containing resin (preferably fluorine-containing olefin resin) having the hydrophilic functional group described above. Can be prepared. As the group 4A metal compound to be added to the chemical conversion treatment liquid, a group 4A metal oxyacid salt, fluoride, hydroxide, organic acid salt, carbonate, peroxide salt, or the like is used. Examples of oxyacid salts include hydrates, ammonium salts, alkali metal salts, alkaline earth metal salts, and the like. You may add a polyethylene resin particle, a phosphate, a silane coupling agent, etc. to a chemical conversion liquid as needed.

  The number average molecular weight of the fluorine-containing resin contained in the aqueous emulsion is preferably 1000 or more, more preferably 10,000 or more, and particularly preferably 200,000 or more. As described above, this is to impart water resistance to the chemical conversion coating. On the other hand, from the viewpoint of the stability of the treatment liquid, the number average molecular weight of the fluorine-containing resin is preferably 2 million or less.

  The fluorine-containing resin preferably has a hydrophilic functional group of 0.05 to 5% by mass from the viewpoint of preparing an aqueous emulsion without using an emulsifier.

  The content of the emulsifier in the aqueous emulsion of the fluorine-containing resin is preferably 1% by mass or less. When the emulsifier exceeds 1% by mass, the emulsifier may remain in the chemical conversion film depending on the drying temperature when the chemical conversion film is formed in the third step. If the emulsifier remains in the chemical conversion coating as described above, the water resistance of the chemical conversion coating is remarkably lowered, which is not preferable. As described above, an aqueous emulsion can be prepared even if the amount of the emulsifier is 1% by mass or less as long as it is a fluorine-containing resin having a hydrophilic functional group.

  The emulsifier that may be contained in the aqueous emulsion of the fluorine-containing resin is preferably a fluorine-based emulsifier such as an ammonium salt of perfluorooctanoic acid or an ammonium salt of perfluorononanoic acid from the viewpoint of weather resistance and water resistance. In addition, a known fluorosurfactant can also be used as an emulsifier.

  The content of the fluorine-containing resin in the chemical conversion treatment liquid is preferably in the range of 10 to 70 parts by mass with respect to 100 parts by mass of water. When the content of the fluorine-containing resin is less than 10 parts by mass, the amount of water evaporation increases in the drying process, and the film formability and denseness of the chemical conversion film may be reduced. On the other hand, when content of fluorine-containing resin is more than 70 mass parts, there exists a possibility that the storage stability of a chemical conversion liquid may fall.

  The content of group 4A metal oxyacid salt, fluoride, hydroxide, organic acid salt, carbonate or peroxide in the chemical conversion solution is 0. A range of 1 to 5 parts by mass is preferable. When the content of these salts is less than 0.1 part by mass, the crosslinking reaction and the reaction with the plating layer surface are insufficient, and the water resistance and film adhesion of the chemical conversion film cannot be sufficiently improved. On the other hand, when the content of these salts exceeds 5 parts by mass, the cross-linking reaction proceeds and the storage stability of the chemical conversion solution may be reduced.

  The content of the resin particles (for example, polyethylene-fluorine resin particles) in the chemical conversion liquid is in the range of 0.5 to 20 parts by mass with respect to 100 parts by mass of the solid content (fluorine-containing resin, 4A group metal compound, etc.). The inside is preferable. As described above, when the resin particle content is less than 0.5% by mass, the lubricity of the chemical conversion coating cannot be sufficiently improved. On the other hand, when the content of the resin particles is more than 20% by mass, the weather resistance of the chemical conversion film may be deteriorated.

  When polyethylene resin particles are further added to the chemical conversion treatment liquid in addition to the polyethylene-fluorine resin particles, the content of the polyethylene resin particles in the chemical conversion treatment liquid is 0.1 to 16 masses per 100 parts by mass of the solid content. Within the range of parts is preferred. As described above, when the content of the polyethylene resin particles is less than 0.1% by mass, the effect of the polyethylene resin cannot be exhibited sufficiently. On the other hand, when the addition amount exceeds 16% by mass, the weather resistance of the chemical conversion coating may be lowered. Moreover, the average particle diameter of the polyethylene resin particles is preferably within a range of 0.1 to 10 μm. When the average particle diameter is less than 0.1 μm, most of the polyethylene resin particles are buried in the chemical conversion film, and the polyethylene resin cannot be bleed on the surface of the chemical conversion film. On the other hand, when the average particle size is more than 10 μm, the polyethylene resin particles may fall off while the chemical conversion solution is being dried.

  When adding a phosphate to a chemical conversion liquid, the phosphate content in the chemical conversion liquid is preferably in the range of 0.05 to 3 parts by mass in terms of P with respect to 100 parts by mass of the fluorine-containing resin. . When the phosphate content is less than 0.05 parts by mass, the adhesion of the chemical conversion film cannot be sufficiently improved. On the other hand, when the content of the phosphate is more than 3 parts by mass, the reaction with the 4A group metal compound may proceed excessively and the crosslinking effect by the 4A group metal compound may be impaired.

  When adding a silane coupling agent to a chemical conversion liquid, content of the silane coupling agent in a chemical conversion liquid has the preferable range of 0.5-5 mass parts with respect to 100 mass parts of fluorine-containing resin. When content of a silane coupling agent is less than 0.5 mass part, the adhesiveness of a chemical conversion treatment film cannot fully be improved. On the other hand, when the content of the silane coupling agent exceeds 5 parts by mass, the film adhesion is saturated and no further improvement is observed. In addition, the stability of the chemical conversion liquid may be reduced.

  Etching agents, inorganic compounds, inorganic lubricants, color pigments, dyes, and the like may be added to the chemical conversion liquid as necessary as other components. Fluoride etc. are used as an etching agent. An etching agent improves the adhesiveness of a chemical conversion treatment film more by activating the plating layer surface. Inorganic compounds (oxides, phosphates, etc.) such as Mg, Ca, Sr, V, W, Mn, B, Si, and Sn improve the water resistance by densifying the chemical conversion film. Inorganic lubricants such as molybdenum disulfide and talc are brought into the film from the chemical conversion treatment liquid, and further improve the lubricity of the chemical conversion treatment film and further the workability of the chemical conversion treatment Al-plated steel sheet. Moreover, predetermined | prescribed color tone can be provided to a chemical conversion treatment film by mix | blending an inorganic pigment, an organic pigment, organic dye, etc.

[Formation of chemical conversion coating]
In the third step, a chemical conversion treatment film is formed on the surface of the Al-based alloy plated steel sheet prepared in the first step. In order to form the chemical conversion film, the chemical conversion solution prepared in the second step may be applied to the surface of the Al-based alloy plated steel sheet prepared in the first step and dried.

  The method for applying the chemical conversion liquid is not particularly limited, and may be appropriately selected from known methods. Examples of such a coating method include a roll coating method, a curtain flow method, a spin coating method, a spray method, and a dip pulling method.

  The chemical conversion solution may be dried at room temperature, but considering continuous operation, it is preferable to keep the temperature at 50 ° C. or higher to shorten the drying time. However, when the temperature is kept above 300 ° C., the organic component may be thermally decomposed to deteriorate the performance of the chemical conversion coating. In the production method of the present invention, since the content of the emulsifier contained in the chemical conversion treatment liquid is small, even if the drying temperature is about 50 ° C., the emulsifier is hardly contained, and a chemical conversion treatment film having excellent water resistance can be formed. .

  FIG. 2 is a schematic cross-sectional view showing the formation process of the chemical conversion coating. FIG. 2 shows a state in which a chemical conversion treatment liquid to which polyethylene-fluorine resin particles and polyethylene resin particles are added is applied.

  First, a chemical conversion treatment liquid is applied to the surface of the Al-based alloy plated steel sheet 110 to form a coating film 120 of the chemical conversion treatment liquid (see FIG. 2A). Polyethylene-fluorine resin particles 122 and polyethylene resin particles 124 are dispersed in the coating film 120 of the chemical conversion treatment liquid.

  Next, when the temperature is raised to about 50 ° C., the moisture evaporates and a chemical conversion film 120 ′ is formed (see FIG. 2B). At this time, most of the polyethylene-fluorine resin particles 122 and the polyethylene resin particles 124 protrude from the surface of the chemical conversion coating 120 ′. FIG. 3A is an SEM image (plan view) of the chemical conversion coating after the chemical conversion coating is dried at 50 ° C. FIG. Although it is not possible to distinguish between the polyethylene-fluororesin particles and the polyethylene resin particles, it can be seen that these particles protrude from the surface of the chemical conversion coating (see “PE-F or PE” in the figure).

  When the temperature is further increased to about 150 ° C., the polyethylene resin particles 124 are melted and the polyethylene resin is bleed on the surface (see FIG. 2C). The bleed polyethylene resin 124 ′ covers the whole or part of the surface of the chemical conversion coating 120 ′. On the other hand, the polyethylene-fluorine resin particles 122 are maintained as they are without melting. FIG. 3B is an SEM image (plan view) of the chemical conversion coating after the coating of the chemical conversion solution is dried at 150 ° C. It can be seen that only the polyethylene-fluororesin particles protrude from the surface of the chemical conversion coating (see “PE-F” in the figure). FIG. 3C is an SEM image (cross-sectional view) of polyethylene-fluororesin particles protruding from the surface of the chemical conversion coating. It can be confirmed by fluorescent X-ray analysis that the particles protruding from the surface of the chemical conversion coating are polyethylene-fluororesin particles. FIG. 4 is a fluorescent X-ray spectrum of polyethylene-fluororesin particles protruding from the surface of the chemical conversion coating.

  By the above procedure, the chemical conversion treatment Al-plated steel sheet of this invention which is excellent in all of weather resistance, water resistance, film | membrane adhesiveness, and workability can be manufactured.

[Formation of base chemical conversion coating]
In the step of forming the base chemical conversion treatment film, before forming the chemical conversion treatment film, the base chemical conversion treatment liquid is applied to the surface of the Al-based alloy plated steel sheet prepared in the first step to form a coating film. The base chemical conversion treatment liquid can be applied by, for example, a roll coating method, a spin coating method, a spray method, or the like. The coating amount of the base chemical conversion treatment liquid is preferably adjusted so that the valve metal adhesion amount is 1 mg / m ² or more. It is for providing sufficient corrosion resistance to the chemical conversion treatment steel plate obtained. Moreover, it is preferable to adjust the application quantity of a foundation | substrate chemical conversion liquid so that the thickness of the foundation | substrate chemical conversion treatment film formed may be 3 nm or more and 1000 nm or less. Sufficient corrosion resistance is exhibited at 3 nm or more, and when it exceeds 1000 nm, cracks may occur due to stress when forming a steel sheet.

  A base chemical conversion treatment film can be formed by drying the coating film formed on the surface of the Al-based alloy-plated steel sheet without washing with water. Although it can dry at normal temperature, when continuous operation is considered, it is preferable to hold at 50 degreeC or more and to shorten drying time. However, when the drying temperature exceeds 200 ° C., the organic component contained in the chemical conversion coating film is thermally decomposed, and the properties imparted with the organic component may be impaired.

  EXAMPLES Hereinafter, although this invention is demonstrated in detail with reference to an Example, this invention is not limited by these Examples.

[Example]
1. Preparation of chemical conversion treatment Al-plated steel sheet Using SPCC having a plate thickness of 0.8 mm as a base material, a molten Al-9 mass% Si alloy-plated steel sheet (plating adhesion amount 45 g / m ² ) was prepared. In this example, this plated steel sheet was used as a chemical conversion treatment original sheet.

  A chemical conversion treatment liquid having the composition shown in Table 1 was applied to the surface of the molten Al-9 mass% Si alloy-plated steel sheet, and dried by heating at a final plate temperature of 140 ° C. to form a chemical conversion treatment film having a thickness of 2.0 μm.

  The chemical conversion treatment liquids of treatment liquids No. 1 to 12 shown in Table 1 are aqueous emulsions containing a predetermined amount of a fluorine-containing resin containing a carboxyl group and a sulfonic acid group and an emulsifier (nonvolatile content: 25% by mass; see Table 2). 4A group metal compound, polyethylene-fluorine resin particles (resin particles) and the like. The chemical conversion treatment liquid of treatment liquid No. 13 is the addition of a group 4A metal compound, polyethylene-fluororesin particles (resin particles), etc., to an aqueous emulsion containing a urethane resin and an emulsifier (nonvolatile content: 25% by mass; see Table 2). Prepared.

  An aqueous emulsion containing a fluorine-containing resin was obtained by adding a predetermined amount of a fluoroolefin, a carboxyl group-containing monomer, a sulfonic acid group-containing monomer and an emulsifier to an aqueous solvent and copolymerizing them. PR135 (Sumika Bayern Urethane Co., Ltd.) was used as an aqueous emulsion containing a urethane resin. A-1891 (Momentive Performance Materials Japan GK) was used as the silane coupling agent.

  The amounts of group 4A metal, phosphate and silane coupling agent relative to the organic resin in the chemical conversion coating of each chemical conversion Al-plated steel sheet were measured using a fluorescent X-ray analyzer. The contents of phosphate and silane coupling agent were calculated from the measured values of P and Si. Moreover, the area occupation rate of the polyethylene-fluororesin particle | grains in the surface of the chemical conversion treatment film of each chemical conversion treatment Al-plated steel plate was measured using the scanning electron microscope. Table 3 shows the amounts of Group 4A metal, phosphate, and silane coupling agent relative to the organic resin in the chemical conversion coating formed, and the area occupancy ratio of the polyethylene-fluororesin particles on the surface of the chemical conversion coating for each chemical conversion coating. Shown in

2. Evaluation of chemical conversion treatment Al-plated steel sheet (1) Accelerated weather resistance test A test piece was cut out from each chemical conversion treatment Al-plated steel sheet, and an accelerated weather resistance test (xenon lamp method) was conducted in accordance with JIS K5600-7-7: 2008. Carried out. In this test, the process of spraying water for 18 minutes while irradiating the light of a xenon arc lamp for 120 minutes was defined as 1 cycle (2 hours), and this process was repeated 0 to 1000 cycles (0, 500, 1000 cycles).

(2) Evaluation of weather resistance About each chemical conversion treatment Al-plated steel sheet, the thickness of the chemical conversion treatment film before and after the accelerated weathering test was measured by a cross-sectional microscope, and the coating film residual ratio was obtained. About each chemical conversion treatment Al-plated steel sheet, “◎” when the coating film remaining rate is 95% or more, “◯” when 80% or more and less than 95%, “△” when 60% or more and less than 80%. When it was 30% or more and less than 60%, it was evaluated as “▲”, and when it was less than 30%, it was evaluated as “x”.

(3) Evaluation of film adhesion About each chemical conversion treatment Al-plated steel sheet, using a test piece (size: 30 mm × 150 mm) before and after the accelerated weathering test, a draw bead test (die bead height: 4 mm, pressure: 1.0 kN), the remaining film ratio of the portion where the mold slid was measured. About each chemical conversion treatment Al-plated steel sheet, “◎” when the film remaining rate is 95% or more, “◯” when 80% or more and less than 95%, “△” when 60% or more and less than 80%, 30 % Or more and less than 60% were evaluated as “▲”, and less than 30% were evaluated as “×”.

(4) Corrosion resistance evaluation of flat part About each chemical conversion treatment Al-plated steel sheet, a salt spray test (according to JIS Z2371; 120 hours) is performed using the test piece after the accelerated weathering test, and the area where white rust occurs in the flat part Rate was evaluated. About each chemical conversion treatment Al-plated steel sheet, when the white rust occurrence area ratio is 5% or less, “◎”, when it exceeds 5% and 10% or less, “◯”, and when it exceeds 10% and 30% or less, “ “△” was evaluated as “▲” when 30% was exceeded and 50% or less, and “X” was evaluated when 50% was exceeded.

(5) Evaluation of lubricity A test piece having a width of 30 mm and a length of 300 mm was cut out from each chemically treated Al-based plated steel sheet. A mold made of SKD11 was brought into contact with both surfaces of each test piece, and the test piece was pulled out at a speed of 100 mm / min while applying a load of 600 kgf through the mold. The pulling force at this time was measured to evaluate the lubricity. For each chemical conversion treated Al-plated steel sheet, “◎” when the pulling force is 200 kgf or less, “◯” when it exceeds 200 kgf and 250 kgf or less, “Δ” when it exceeds 250 kgf and 300 kgf or less, “Δ”, and exceeds 300 kgf and 400 kgf or less. In the case of, “「 ”was evaluated, and in the case of exceeding 400 kgf,“ × ”was evaluated.

(6) Evaluation result About each chemical conversion treatment Al type plated steel sheet (Examples 1-7, Comparative Examples 1-6), the kind of used processing liquid, a weather resistance test, a film | membrane adhesiveness test, a flat part corrosion resistance test, and Table 4 shows the evaluation results of the lubricity test.

  The weather resistance was evaluated by the coating film remaining rate of the chemical conversion coating after the accelerated weather resistance test. In the chemical conversion treatment Al-plated steel sheet of Comparative Example 6 in which the chemical conversion treatment film containing the urethane resin was formed, the chemical conversion treatment film disappeared after 500 cycles (equivalent to outdoor exposure of 5 years). Further, even in the chemical conversion treatment Al-plated steel sheet of Comparative Example 4 in which a chemical conversion treatment film containing excessively large polyethylene-fluorine resin particles was formed, the polyethylene-fluororesin particles were dropped from the chemical conversion treatment film, so that the weather resistance was poor. It was. On the other hand, in the chemical conversion treatment Al-plated steel sheet of Examples 1-7 in which a chemical conversion treatment film containing a fluorine-containing resin having a predetermined amount of a hydrophilic functional group and a group 4A metal compound is formed, 1000 cycles (equivalent to 10 years of outdoor exposure) Even after repeating, the film thickness of the chemical conversion film hardly changed.

  The film adhesion was evaluated by the film remaining rate after the draw bead test. In the chemical conversion treatment Al-plated steel sheet of Comparative Example 6 in which a chemical conversion treatment film containing a urethane resin was formed, the chemical conversion treatment film almost disappeared after 500 cycles (equivalent to 5 years of outdoor exposure), so the film still exists after the draw bead test. do not do. On the other hand, in the chemical conversion treatment Al-plated steel sheets of Examples 1 to 7 in which a chemical conversion treatment film containing a fluorine-containing resin having a predetermined amount of hydrophilic functional group, a group 4A metal compound, and polyethylene-fluorine resin particles is formed, 1000 cycles ( The film adhesion was good even after repeated exposure for 10 years.

  Corrosion resistance was evaluated based on the white rust generation area ratio after the salt spray test. In the chemical conversion treatment Al-plated steel sheet of Comparative Example 6 in which a chemical conversion treatment film containing a urethane resin was formed, although the corrosion resistance was good before the accelerated weather resistance test, the corrosion resistance was remarkably lowered with the disappearance of the film. Moreover, the chemical conversion treatment Al-plated steel sheet of Comparative Example 1 and Comparative Example 2 in which a chemical conversion treatment film containing a fluorine-containing resin having an excessive or excessive amount of a hydrophilic functional group is formed, and a chemical conversion treatment not containing a group 4A metal compound In the chemical conversion treatment Al-plated steel sheet of Comparative Example 3 and Comparative Example 5 in which the film was formed, the corrosion resistance was inferior before the accelerated weather resistance test. On the other hand, in the chemical conversion treatment Al-plated steel sheet of Examples 1-7 in which a chemical conversion treatment film containing a fluorine-containing resin having a predetermined amount of a hydrophilic functional group and a group 4A metal compound is formed, 1000 cycles (equivalent to 10 years of outdoor exposure) Even after repetition, the corrosion resistance was good.

  The lubricity was evaluated by the pulling force required when pulling out a test piece to which a load was applied. Since the chemical conversion treatment Al-plated steel sheet of Comparative Example 1 had a small amount of polyethylene-fluororesin particles in the chemical conversion treatment film, the lubricity was inferior. Similarly, the chemical conversion treatment Al-plated steel sheet of Comparative Example 5 that does not contain polyethylene-fluororesin particles also had poor lubricity. Moreover, since the chemical conversion treatment Al-plated steel plate of Comparative Example 6 had a small average particle diameter of the polyethylene-fluorine resin particles and was buried in the chemical conversion treatment film, the lubricity was inferior. On the other hand, in the chemical conversion treatment Al-plated steel sheets of Examples 1 to 7 in which a chemical conversion treatment film containing a predetermined amount of polyethylene-fluororesin particles having an average particle diameter within a predetermined range was formed, the lubricity was good.

  From the above results, it can be seen that the chemically treated Al-based plated steel sheet of the present invention is excellent in weather resistance, corrosion resistance, film adhesion, and workability (lubricity).

[Reference experiment]
As a reference experiment, the results of examining the relationship between the moisture permeability and the amount of the group 4A metal compound and the amount of the emulsifier in the fluororesin film are shown.

  A predetermined amount of group 4A was added to an aqueous emulsion of a fluorine-containing resin having a hydrophilic functional group prepared by adding a hydrophilic functional group-containing monomer to 1% by mass and adding an emulsifier to 1% by mass. The chemical conversion treatment solution prepared by adding the metal compound was applied to the surface of the plated steel plate with a bar coater and dried by heating at a final plate temperature of 140 ° C. to form a fluororesin film having a thickness of 30 μm. This fluororesin film was peeled off from the plated steel sheet and cut into a predetermined size to obtain a test piece. About each test piece (free fluororesin film | membrane), the water vapor transmission rate was measured based on JISZ0208 (measurement conditions, temperature 40 ± 0.5 degreeC, relative humidity 90 ± 2%, 24 hours).

  FIG. 5 is a graph showing the relationship between the amount of group 4A metal in the fluororesin coating and the moisture permeability. From this graph, it is understood that the moisture permeability of the fluororesin film can be remarkably lowered by setting the amount of the group 4A metal in the fluororesin film to 0.1 mass% or more.

  Add a hydrophilic functional group-containing monomer to 1% by mass and add a predetermined amount of emulsifier to an aqueous emulsion of a fluorine-containing resin having a hydrophilic functional group. A chemical conversion treatment solution prepared by adding 1% by mass in terms of conversion is applied to the surface of the plated steel plate with a bar coater and dried by heating at a final plate temperature of 140 ° C. to form a fluororesin film having a thickness of 30 μm. did. This fluororesin film was peeled off from the plated steel sheet and cut into a predetermined size to obtain a test piece. About each test piece (free fluororesin film | membrane), the water vapor transmission rate was measured based on JISZ0208 (measurement conditions, temperature 40 ± 0.5 degreeC, relative humidity 90 ± 2%, 24 hours).

  FIG. 6 is a graph showing the relationship between the concentration of the emulsifier in the aqueous emulsion of the fluorine-containing resin and the moisture permeability of the fluorine resin film. From this graph, it is understood that the moisture permeability of the fluororesin film can be remarkably reduced by setting the concentration of the emulsifier in the emulsion to 1% by mass or less.

  From the above results, it can be seen that the fluororesin film having a large amount of the group 4A metal compound and a small amount of the remaining emulsifier has excellent water resistance.

  Since the chemical conversion treatment Al-plated steel sheet of the present invention is excellent in weather resistance, water resistance, film adhesion, corrosion resistance and workability, it is useful in various applications such as exterior building materials. For example, the chemical conversion treatment Al-based plated steel sheet of the present invention includes: 1) steel pipe, shape steel, support, beam, conveying member for vinyl house or agricultural house, 2) sound insulation wall, sound insulation wall, sound absorption wall, snow insulation wall, guardrail, It can be suitably used for applications such as railings, protective fences, columns, 3) railway vehicle members, overhead wire members, electrical equipment members, safety environment members, structural members, and solar mounts.

  The Al-based alloy-plated steel sheet sufficiently adheres to the coating film under high temperature and high humidity and is excellent in corrosion resistance. Therefore, the chemical conversion treatment Al-plated steel sheet of the present invention is particularly suitable as an exterior material used in a high temperature and high humidity environment.

DESCRIPTION OF SYMBOLS 110 Al type alloy plating steel plate 120 Chemical conversion liquid coating film 120 'Chemical conversion coating film 122 Polyethylene-fluorine resin particle 124 Polyethylene resin particle 124' Bleed polyethylene resin

Claims (16)

An Al-based alloy-plated steel sheet containing 85 to 99% by mass of Al;
A chemical conversion treatment Al-plated steel sheet having a film thickness of 0.5 to 10 μm formed on the surface of the Al alloy-plated steel sheet,
The chemical conversion film is a fluorine-containing resin containing 0.05 to 5% by mass of a hydrophilic functional group selected from the group consisting of a carboxyl group, a sulfonic acid group and a salt thereof and 7 to 20% by mass of F atoms, Containing 0.1 to 5% by mass of a Group 4A metal compound in terms of metal with respect to the fluorine-containing resin, and resin particles having an average particle size of 0.1 to 10 μm,
The area occupation ratio of the resin particles on the surface of the chemical conversion film is 0.1 area% or more.
Chemical conversion treatment Al-plated steel sheet.   The chemical conversion treatment Al-plated steel plate of Claim 1 whose ratio of the carboxyl group and sulfonic acid group which the said fluorine-containing resin has is in the range of 5-60 in the molar ratio of a carboxyl group / sulfonic acid group.   The said resin particle is a chemical conversion treatment Al-plated steel plate of Claim 1 which is the polyethylene- fluorine resin particle by which the fluororesin fine particle is couple | bonded with the surface of the polyethylene resin particle. The chemical conversion film further contains a polyethylene resin,
The polyethylene-fluororesin particles protrude from the surface of the chemical conversion coating on a part of the surface of the chemical conversion coating,
The polyethylene resin covers all or part of the remaining part of the surface of the chemical conversion film,
The chemical conversion treatment Al-plated steel sheet according to claim 3. The chemical conversion film further contains a phosphate,
The amount of the phosphate with respect to the fluorine-containing resin is in the range of 0.05 to 3% by mass in terms of P.
The chemical conversion treatment Al-plated steel plate according to claim 1. The chemical conversion film further contains a silane coupling agent,
The amount of the silane coupling agent relative to the fluorine-containing resin is in the range of 0.5 to 5% by mass.
The chemical conversion treatment Al-plated steel plate according to claim 1.   The said 4A group metal is a chemical conversion treatment Al-plated steel plate of Claim 1 chosen from the group which consists of Ti, Zr, Hf, and these combination. Formed between the Al-based alloy-plated steel sheet and the chemical conversion film,
The chemical conversion treatment Al-plated steel sheet of Claim 1 which further has the foundation | substrate chemical conversion treatment film containing the oxide or hydroxide of valve metal, and the fluoride of valve metal. Preparing an Al-based alloy-plated steel sheet containing 85 to 99% by mass of Al;
Applying a chemical conversion treatment liquid to the surface of the Al-based alloy-plated steel sheet and drying to form a chemical conversion treatment film having a thickness of 0.5 to 10 μm,
The said chemical conversion liquid contains 0.05-5 mass% of hydrophilic functional groups chosen from the group which consists of a carboxyl group, a sulfonic acid group, and these salts, and 7-20 mass% of F atoms, and a number average molecular weight. Fluorine-containing resin in the range of 1,000 to 2,000,000, oxyacid salt, fluoride, hydroxide, organic acid salt, carbonate or peroxide salt of group 4A metal, and an average particle size of 0.1 Containing 10 to 10 μm resin particles,
The amount of the oxyacid salt, fluoride, hydroxide, organic acid salt, carbonate or peroxide of the group 4A metal in the fluorine-containing resin is within a range of 0.1 to 5% by mass in terms of metal. Yes,
The amount of the resin particles relative to the solid content in the chemical conversion treatment liquid is in the range of 0.5 to 20% by mass.
The manufacturing method of a chemical conversion treatment Al-plated steel plate.   The ratio of the carboxyl group and sulfonic acid group which the said fluorine-containing resin has is in the range of 5-60 in the molar ratio of a carboxyl group / sulfonic acid group, Manufacture of the chemical conversion treatment Al-plated steel plate of Claim 9 Method.   The said resin particle is a manufacturing method of the chemical conversion treatment Al-plated steel plate of Claim 9 which is a polyethylene- fluorine resin particle by which the fluororesin fine particle is couple | bonded with the surface of the polyethylene resin particle.   The said chemical conversion treatment liquid is a manufacturing method of the chemical conversion treatment Al-plated steel plate of Claim 11 which contains a polyethylene resin particle further. The chemical conversion treatment liquid further contains a phosphate,
The amount of the phosphate with respect to the fluorine-containing resin is in the range of 0.05 to 3% by mass in terms of P.
The manufacturing method of the chemical conversion treatment Al-plated steel plate of Claim 9. The chemical conversion treatment liquid further contains a silane coupling agent,
The amount of the silane coupling agent relative to the fluorine-containing resin is in the range of 0.5 to 5% by mass.
The manufacturing method of the chemical conversion treatment Al-plated steel plate of Claim 9.   The said 4A group metal is a manufacturing method of the chemical conversion treatment Al-plated steel plate of Claim 9 chosen from the group which consists of Ti, Zr, Hf, and these combination. Before the step of forming the chemical conversion coating, further comprising the step of applying a base chemical conversion treatment liquid on the surface of the Al-based alloy plated steel sheet and drying to form a base chemical conversion coating;
The base chemical conversion treatment solution contains a valve metal salt and fluoride ions.
The manufacturing method of the chemical conversion treatment Al-plated steel plate of Claim 9.