JP2004352747A

JP2004352747A - Adhesive film

Info

Publication number: JP2004352747A
Application number: JP2003148690A
Authority: JP
Inventors: Shingo Koda; 真吾幸田
Original assignee: Tosoh Corp
Current assignee: Tosoh Corp
Priority date: 2003-05-27
Filing date: 2003-05-27
Publication date: 2004-12-16
Anticipated expiration: 2023-05-27
Also published as: JP4539030B2

Abstract

<P>PROBLEM TO BE SOLVED: To provide an adhesive film which does not need an adhesive and has excellent film appearance and cost performance, to provide a laminate prepared by adhering the adhesive film to an adherend comprising a resin, a metal and/or a silicon oxide in an excellent adhesive force, and to provide a laminate material, used for wide industrial field materials, such as resin-coated steel plates, laminated steel plates, laminated glass, and the like used for household electric appliances, automobiles, and building materials, and the like. <P>SOLUTION: This adhesive film produced from an ethylenic resin composition comprising 98.5 to 99.99 wt. % of an ethylenic polymer having a melt mass flow rate of 0.1 to 50 g/10 min and a density of 880 to 960 kg/m<SP>3</SP>, and 0.01 to 1.5 wt. % of a silane coupling agent having an epoxy group and an alkoxy group is characterized in that at least one of the surfaces of the film is subjected to an oxidation treatment. <P>COPYRIGHT: (C)2005,JPO&NCIPI

Description

【０００１】
【発明が属する技術分野】
本発明は、エチレン系樹脂組成物を用いてなる接着性フィルムに関するものである。さらに本発明は、樹脂、金属及び／又はケイ素酸化物等からなる被着体と該接着性フィルムからなる積層体に関するものである。
【０００２】
【従来の技術】
ポリエチレン系樹脂フィルムは、低価格、成形性などに優れる理由から広い分野で使用されている。
【０００３】
しかしながら、ポリエチレン系樹脂フィルムは、その非極性構造のため、樹脂、金属及び／又はケイ素酸化物等からなる被着体と接着しにくいという欠点がある。そのため、上記被着体とポリエチレン系フィルムを積層させる場合、接着剤を接着界面に塗布する方法や、予めポリエチレン系樹脂にカルボキシル基や水酸基、酸無水物基を有するモノマーを共重合した変性エチレン系共重合体を用いたフィルムを熱圧着させる方法などが提案されている。
【０００４】
また、上記接着剤やポリエチレン系樹脂の共重合に用いられるモノマーとして、シランカップリング剤が知られており、これを利用した様々な提案がなされている。
【０００５】
接着剤を使用する例として、珪素酸化物の薄膜とポリエチレン樹脂間にアミノ基を有するシランカップリング剤を塗布する方法が提案されている（例えば、特許文献１参照）。しかしながら、本手法によれば、シランカップリング剤を塗布する設備が必要であり、設備費が負担となることや、シランカップリング剤を塗工する際に用いる有機溶剤の処理費用がかかるなどの問題点がある。
【０００６】
シランカップリング剤をポリエチレン系樹脂に予め共重合した樹脂を用いた組成物としては、５〜４０重量％のアクリル酸エステル又はメタクリル酸エステルを含む単量体成分を重合させて得られるエチレン・アクリル酸エステル共重合体又はエチレン・メタクリル酸エステル共重合体６０〜９９重量部およびエポキシ基を有するオレフィン系重合体のシラングラフト変性体１〜４０重量部よりなることを特徴とする重合体組成物が提案されている（例えば、特許文献２参照）。
【０００７】
しかしながら、本手法によれば、エポキシ基含有オレフィン系重合体へ不飽和基含有シラン化合物をグラフト変性させる際、有機過酸化物を用いているため、シラン化合物のグラフト反応と同時にエチレン・アクリル酸エステル共重合体又はエチレン・メタクリル酸エステル共重合体やエポキシ基含有オレフィン系重合体自体をも架橋させてしまうことにより、フィッシュアイと呼ばれるゲルを多発させ、積層体の外観を損ねるといった問題が発生する。また、エチレン・アクリル酸エステル共重合体又はエチレン・メタクリル酸エステル共重合体のコスト、及び該グラフト変性のコストが高い、といった問題もある。
【０００８】
【特許文献１】
特開平５−１３１５９０号公報（２頁）
【特許文献２】
特開平１−２０７３４０号公報（３頁）
【０００９】
【発明が解決しようとする課題】
本発明は、上記のような状況を鑑みなされたものであって、接着剤が不要となり、また、シランカップリング剤を共重合する際に発生するゲルによるフィルム外観の低下、カルボキシル基や酸無水物基含有モノマー共重合体を使用することによる押出機スクリュー等の腐食といった問題を避けることが可能となり、かつグラフト変性工程を経ない低コストの接着性フィルムを提供することを目的とするものである。
【００１０】
さらに、本発明は、樹脂、金属及び／又はケイ素酸化物等からなる被着体を接着させ、接着力に優れた積層体を提供することを目的とするものである。
【００１１】
【課題を解決するための手段】
本発明者らは、上記課題を解決すべく鋭意検討した結果、特定のエチレン系重合体に対し、エポキシ基及びアルコキシ基を有するシランカップリング剤を、該エチレン系重合体へのグラフト変性工程を経ることなしに、特定量配合したエチレン系樹脂組成物からなるフィルムの表面を酸化した接着性フィルムが、多様な基材に対する優れた接着性を有し、且つフィルム外観、及びコストパフォーマンスに優れることを見出し、本発明を完成させるに至った。
【００１２】
すなわち、本発明は、ＪＩＳＫ６９２２−１（１９９８年）で測定したメルトマスフローレイトが０．１〜５０ｇ／１０分、ＪＩＳＫ６９２２−１（１９９８年）で測定した密度が８８０〜９６０ｋｇ／ｍ^３であるエチレン系重合体９８．５〜９９．９９重量％、及びエポキシ基及びアルコキシ基を有するシランカップリング剤０．０１〜１．５重量％とからなるエチレン系樹脂組成物を用いてなるフィルムであって、そのフィルム表面の少なくとも片面が酸化処理されていることを特徴とする接着性フィルムに関するものである。
【００１３】
また、本発明は、エチレン系樹脂組成物を用いてなるフィルム表面の少なくとも片面がコロナ放電処理、フレーム処理、プラズマ処理から選ばれるいずれかの方法で酸化されていることを特徴とする接着性フィルムに関するものである。
【００１４】
さらに、本発明は、本発明の接着性フィルムが、（ａ）熱可塑性樹脂からなるフィルムもしくはシート、（ｂ）金属板、金属箔もしくは金属及び／又は金属酸化物蒸着膜、（ｃ）ガラス板、ガラス箔もしくはケイ素酸化物蒸着膜、及び（ｄ）紙からなる群より選ばれる少なくとも１種以上の基材を被着体とし、少なくとも１以上の被着体と少なくとも１以上の該接着性フィルムが熱圧着されてなることを特徴とする積層体に関するものである。
【００１５】
以下に、本発明について詳細に説明する。
【００１６】
本発明にて用いられるエチレン系重合体は、ＪＩＳＫ６９２２−１（１９９８年）によるＭＦＲが０．１〜５０ｇ／１０分の物性を示すものである。
【００１７】
ＭＦＲが０．１ｇ／１０分未満である場合、エチレン系樹脂組成物をフィルム成形加工に供した際の押出負荷が高いことや製膜時の延展性が悪いため好ましくなく、また５０ｇ／１０分を超える場合、エチレン系樹脂組成物をフィルム成形加工に供した際に必要な溶融粘度が低く、フィルム成形加工性に劣るものとなるため好ましくない。
【００１８】
さらに、本発明にて用いられるエチレン系重合体は、ＪＩＳＫ６９２２−１（１９９８年）で測定した密度が８８０〜９６０ｋｇ／ｍ^３を示すものである。
【００１９】
密度が８８０ｋｇ／ｍ^３未満である場合、積層体の耐熱性が劣り、５０℃以上の雰囲気下での接着性が低下するため好ましくなく、９６０ｋｇ／ｍ^３を超える場合、被着体との接着性が劣り、好ましくない。
【００２０】
本発明にて用いられるエチレン系重合体は特に限定するものではなく、エチレン単独重合体、エチレンと炭素数３〜１２のα−オレフィンとの共重合体、エチレンとビニルエステルとの共重合体等が例示される。さらにこれら重合体として、高圧法低密度ポリエチレン（以下、ＬＤＰＥと記す。）、直鎖状低密度ポリエチレン（以下、ＬＬＤＰＥと記す。）、中密度ポリエチレン（以下、ＭＤＰＥと記す。）、高密度ポリエチレン（以下、ＨＤＰＥと記す。）、エチレン−酢酸ビニル共重合体（以下、ＥＶＡと記す。）、エチレン−アクリル酸エチルエステル共重合体（以下、ＥＥＡと記す。）等が例示される。また、これらエチレン系重合体は単独で使用してもよいし、２種以上混合して使用してもよい。
【００２１】
ここで、エチレン系重合体の重合方法は、特に限定するものではなく、ＬＤＰＥやＥＶＡ，ＥＥＡ等の場合、例えば高圧法によるラジカル重合法を挙げることができ、ＬＬＤＰＥやＭＤＰＥ，ＨＤＰＥの場合、チーグラーナッタ触媒やメタロセン触媒を用いた気相法、溶液法、高圧法等の重合法を挙げることができる。
【００２２】
本発明で用いられるエポキシ基及びアルコキシ基を有するシランカップリング剤は、分子中に少なくとも１以上のエポキシ基及びアルコキシ基を有するシラン化合物を示す。
【００２３】
このようなエポキシ基及びアルコキシ基を有するシランカップリング剤は特に限定されるものではなく、β−（３，４−エポキシシクロヘキシル）エチルトリメトキシシラン、γ−グリシドキシプロピルトリメトキシシラン、γ−グリシドキシプロピルトリエトキシシラン、γ−グリシドキシプロピルメチルジメトキシシラン、γ−グリシドキシプロピルメチルジエトキシシラン等が例示される。
【００２４】
また、これらエポキシ基及びアルコキシ基を有するシランカップリング剤は、単独もしくは２種以上混合して使用してもよく、さらに他のシランカップリング剤やチタン系カップリング剤と併用してもかまわない。
【００２５】
本発明に用いられるエポキシ基及びアルコキシ基を有するシランカップリング剤は公知のものを使用することができる（例えば、チッソ株式会社製、商品名：サイラエースＳ５１０、Ｓ５２０，Ｓ５３０、信越化学工業株式会社製、商品名：信越シリコーンＫＢＭ３０３，ＫＢＭ４０３，ＫＢＥ４０２，ＫＢＥ４０３）。
【００２６】
本発明におけるエチレン系重合体とエポキシ基及びアルコキシ基を有するシランカップリング剤からなる樹脂組成物におけるエチレン系重合体とエポキシ基及びアルコキシ基を有するシランカップリング剤の配合割合は、エチレン系重合体が９８．５〜９９．９９重量％、エポキシ基及びアルコキシ基を有するシランカップリング剤が０．０１〜１．５重量％である。
【００２７】
エポキシ基及びアルコキシ基を有するシランカップリング剤の配合割合が０．０１重量％未満の場合は、該シランカップリング剤のフィルム表面への滲出量が少なく、接着性フィルムを被着体に熱接着することにより得られる積層体の接着性が劣り好ましくない。特に被着体がガラス等の珪素酸化物の場合の接着性、及び被着体がアルミニウム等の金属の場合における高湿度雰囲気下での接着性が劣り好ましくない。また、１．５重量％を超える場合は、該シランカップリング剤のフィルム表面への滲出量が過剰となり接着性フィルムを被着体に熱圧着することにより得られる積層体の接着性が劣り、またコストパフォーマンスも悪化するため好ましくない。
【００２８】
さらに、本発明におけるエチレン系樹脂組成物の製造方法は特に限定するものではなく、エチレン系重合体とエポキシ基及びアルコキシ基を有するシランカップリング剤とを押出機等で溶融混合する方法、エチレン系重合体ペレットと、エポキシ基及びアルコキシ基を有するシランカップリング剤を予めポリオレフィン樹脂に練り込んだマスターバッチとをドライブレンドする方法等が例示される。
【００２９】
また、係るエチレン系樹脂組成物は、必要に応じて酸化防止剤、滑剤、中和剤、ブロッキング防止剤、界面活性剤、スリップ剤等、通常エチレン系樹脂に使用される添加剤を添加したものでもかまわない。
【００３０】
本発明におけるエチレン系樹脂組成物を用いてなるフィルムの製造方法は特に限定するものではなく、インフレーション成形機、Ｔダイキャスト成形機、カレンダー成形機、プレス成形機等を用いて得ることが可能である。さらに、インフレーション成形やＴダイキャスト成形においては共押出法により多層フィルムを得ることも可能である。
【００３１】
本発明の接着性フィルムは、フィルム表面の接着性を発現させるために、その表面の少なくとも片面が酸化処理されているものである。該酸化処理による接着性効果の発現機構は明確ではないが、エチレン系樹脂組成物を用いてなるフィルム表面上に酸化処理により形成したカルボキシル基と、シランカップリング剤のエポキシ基が反応することにより、シランカップリング剤がフィルム表面に固定化し、その後のアルコキシ基の加水分解により生成するシラノール基が接着性を発現させるものと考えられる。
【００３２】
フィルム表面を酸化する際の酸化処理方法としては特に限定はなく、クロム酸処理、硫酸処理、空気酸化、オゾン処理、コロナ放電処理、フレーム処理、プラズマ処理等が例示される。中でも、エチレン系樹脂組成物を用いてなるフィルム表面上に酸化物を効果的に形成させる上で、コロナ放電処理、フレーム処理、プラズマ処理から選ばれる、少なくとも１種以上の酸化方法が特に好ましい。
【００３３】
コロナ放電処理は、プラスチックフィルムやシート表面の連続処理技術として広く使用されているものであり、コロナ放電処理機により発生したコロナ雰囲気にフィルムを通過させることにより行われる。本発明においては、コロナ放電密度１〜１００Ｗ・分／ｍ^２の放電処理を施すことが、被着体との接着性に優れた接着性フィルムを得る上で好ましい。
【００３４】
フレーム処理は、天然ガスやプロパン等を燃焼させたときに生じる火炎にフィルム表面を接することで処理が行われる。
【００３５】
プラズマ処理は、アルゴン、ヘリウム、ネオン、水素、酸素、空気等の単体又は混合気体をプラズマジェットで電子的に励起せしめた後、帯電粒子を除去し、電気的に中性とした励起不活性ガスをフィルム表面に吹き付けることにより行われる。
【００３６】
本発明においては、酸化処理されたフィルム表面のＪＩＳＫ６７６８（１９９８年）で測定される濡れ指数が３３０〜７００μＮ／ｃｍ、特に３７０〜６００μＮ／ｃｍとなる酸化処理を施すことが、被着体との接着性に優れた接着性フィルムを得る上で好ましい。
【００３７】
本発明の接着性フィルムの厚みは、本発明の目的が達成される限りにおいて特に限定はなく、柔軟性に優れ、破損などの問題が小さいことから、１μｍ〜５ｍｍの厚みであることが好ましい。
【００３８】
本発明の積層体は、（ａ）熱可塑性樹脂からなるフィルムもしくはシート、（ｂ）金属板、金属箔もしくは金属及び／又は金属酸化物蒸着膜、（ｃ）ガラス板、ガラス箔もしくはケイ素酸化物蒸着膜、（ｄ）紙からなる群より選ばれる少なくとも１種以上の基材を被着体とし、少なくとも１以上の被着体と少なくとも１以上の該接着性フィルムの酸化処理面とを熱圧着することにより得ることができる。
【００３９】
本発明の積層体を構成する被着体として用いる熱可塑性樹脂からなるフィルムもしくはシートに特に限定はなく、ポリエチレンテレフタレート等のポリエステル、ポリアミド、ポリビニルアルコール、エチレン−酢酸ビニル共重合体鹸化物、ポリカーボネート、ポリエチレン、ポリプロピレン等の合成高分子重合体からなるフィルム又はシート等が例示される。また、これら高分子重合体フィルム又はシートがウレタン系インキ等を用い印刷されたものも例示される。中でも、ポリエステル、ポリアミド、エチレン−酢酸ビニル共重合体鹸化物及びポリビニルアルコールからなるフィルム又はシートは、得られた積層体の接着強度が高く、好ましい。
【００４０】
本発明の積層体を構成する被着体として用いる金属板、金属箔もしくは金属及び／又は金属酸化物蒸着膜に特に限定はなく、鋼鈑としては鉄鋼鈑、銅鈑等が、金属箔としてはアルミ箔、銅箔等が、金属及び／又は金属酸化物蒸着膜としては高分子重合体フィルム又はシートにアルミ蒸着及び／又はアルミナ蒸着されたもの等が例示できる。
【００４１】
本発明の積層体を構成する被着体として用いるガラス板、ガラス箔もしくはケイ素酸化物蒸着膜に特に限定はなく、さらにケイ素酸化物蒸着膜としては高分子重合体フィルム又はシートに二酸化珪素等を蒸着したもの等が例示できる。
【００４２】
本発明の積層体を構成する被着体として用いる紙に特に限定はなく、クラフト紙、上質紙、グラシン紙等が例示できる。
【００４３】
熱圧着の方法としては、公知の方法を用いることができ、特に限定はない。例えば、サーマルラミネート法、ヒートシール等の方法を挙げることができる。また、上記加工により得られた積層体は、接着性を向上させるため、３０℃以上の温度で１０時間以上熱処理すると、さらに接着強度が上昇し好ましい。
【００４４】
さらに、被着体と接着性フィルムとの接着性を高めるため、被着体の接着面に対してコロナ処理、フレーム処理、プラズマ処理などの表面処理を施してもよい。また、もし必要であれば被着体の接着面に接着剤を塗布してもよい。
【００４５】
本発明に係る積層体の積層状態は、少なくとも１以上の被着体と少なくとも１以上の接着性フィルムを組合せて熱圧着されていればよく、特に制限はない。例えば積層状態の組合せとして、１枚の被着体と１枚の接着性フィルムの組合せ、２枚の被着体の間に１枚の接着性フィルムを挟んだ組合せ、また、被着体及び／又は接着性フィルムが複数の場合はそれらが異なる被着体及び／又は接着性フィルムである組合せ等が挙げられる。
【００４６】
本発明の接着性フィルムは、家電製品や自動車、その他建材用シートに用いられる樹脂被覆又は積層鋼鈑、合わせガラス等、広範囲にわたる産業用資材を供するための接着性フィルムとして極めて有用である。
【００４７】
【実施例】
以下、実施例により本発明をさらに詳細に説明するが、本発明はこれら実施例に限定されるものではない。
【００４８】
以下に、物性、加工性の測定方法と評価方法を示す。
【００４９】
（１）メルトマスフローレート（ＭＦＲ）
ＪＩＳＫ６９２２−１（１９９８年）に準拠。
【００５０】
（２）密度
ＪＩＳＫ６９２２−１（１９９８年）に準拠。
【００５１】
（３）被着体との接着性
ヒートシーラー（東洋精機（株）製）を用い、温度１５０℃、時間３秒、圧力２ＭＰａの条件で、被着体と接着性フィルムを熱圧着させた。被着体には、アルミニウム板（東洋アルミニウム（株）製商品名：Ａ１Ｎ３０Ｈ−Ｈ１８）、及びガラス板（北陸板硝子製）の２種類を用いた。
【００５２】
剥離試験は、引張試験機（島津製作所（株）製、商品名：オートグラフＤＣＳ５００）を用い、サンプル巾１５ｍｍ、剥離速度３００ｍｍ／分の条件で被着体と接着性フィルム層間を１８０°剥離した際の剥離強度を測定し、該剥離強度を接着強度とした。
【００５３】
（４）濡れ指数
ＪＩＳＫ６７６８（１９９８年）に準拠。
【００５４】
実施例１
エチレン系重合体として、ＭＦＲが８ｇ／１０分、密度が９１８ｋｇ／ｍ^３であるＬＤＰＥ（東ソー（株）製商品名：ペトロセン２１３）９９．５重量％、エポキシ基及びアルコキシ基を有するシランカップリング剤として、γ−グリシドキシプロピルトリエトキシシラン（信越化学工業（株）製商品名：信越シリコーンＫＢＥ４０３）を０．５重量％になるよう配合し、単軸押出機にて溶融混練しペレットを得た。
【００５５】
得られたペレットを２５ｍｍΦのスクリューを有するキャストフィルム成形機の押出機へ供給し、２８０℃の温度でＴダイよりフィルム厚みが３０μｍになるよう押出した後、該フィルムの片面を５０Ｗ・分／ｍ^２の条件でコロナ放電処理し接着性フィルムを得た。
【００５６】
その後、厚み２５μｍのニ軸延伸ポリエステルフィルム（東洋紡績（株）製商品名：東洋紡エステルフィルムＥ５１００、以下「ＰＥＴ」と記す。）を基材として用い、その片面にコロナ処理を施した。該ＰＥＴフィルムのコロナ処理面にアンカーコート剤（日本曹達（株）製商品名：チタボンドＴ−１２０）を塗布した面と上記の接着性フィルムの非コロナ処理面とを、低密度ポリエチレン（東ソー（株）製商品名：ペトロセン２０３）を用いサンドイッチラミネ−ションし、接着性評価用の接着性フィルム支持体を得た。なお、係るサンドイッチラミネ−ションは、２５ｍｍφの押出機を有する押出ラミネーターを用い、押出温度３００℃、低密度ポリエチレン厚み２５μｍにて行った。得られた接着性評価用の接着性フィルム支持体（厚み０．０８ｍｍ、長さ１０ｃｍ、巾１０ｃｍ）の構成は以下の通りであり、接着性フィルムのコロナ放電処理面が表面となる様に構成した。
【００５７】
（接着性評価用の接着性フィルム支持体の構成）
［ＰＥＴ（基材）／低密度ポリエチレン／接着性フィルム（コロナ放電処理面）］
得られた接着性評価用の接着性フィルム支持体を温度２３℃、相対湿度（以下、「ＲＨ」と記す。）５０％の環境に３日間放置した。
【００５８】
その後、接着性フィルム支持体の接着性フィルム面、即ちコロナ放電処理面と、被着体、即ちアルミニウム板（厚み０．１ｍｍ、長さ１０ｃｍ、巾１０ｃｍ）及びガラス板（厚み０．１ｍｍ、長さ１０ｃｍ、巾１０ｃｍ）とを、ヒートシーラーを用いて上記の被着体接着性評価条件にて熱接着させ積層体を得た。
【００５９】
係る積層体を、その後、温度２３℃、湿度５０％ＲＨの環境、及び温度４０℃、湿度９０％ＲＨの環境に７日間放置し、接着性を評価した。その評価結果を表１に示した。
【００６０】
実施例２
エチレン系重合体として、ＬＤＰＥを９９．５重量％、エポキシ基及びアルコキシ基を有するシランカップリング剤として、γ−グリシドキシプロピルトリエトキシシランを０．５重量部の代わりに、ＬＤＰＥ（東ソー（株）製商品名：ペトロセン２１３）９９重量％、γ−グリシドキシプロピルトリエトキシシラン（信越化学工業（株）製商品名：信越シリコーンＫＢＥ４０３）を１重量％とした以外は実施例１と同様にして接着性フィルム及び積層体を得た。評価結果は表１に示した。
【００６１】
実施例３
接着性フィルム表面のコロナ放電処理条件が５０Ｗ・分／ｍ^２である代わりに、１００Ｗ・分／ｍ^２とした以外は実施例１と同様にして接着性フィルム及び積層体を得た。評価結果は表１に示した。
【００６２】
実施例４
エチレン系重合体として、ＬＤＰＥを９９．５重量％、エポキシ基及びアルコキシ基を有するシランカップリング剤として、γ−グリシドキシプロピルトリエトキシシランを０．５重量部の代わりに、ＬＤＰＥ（東ソー（株）製商品名：ペトロセン２１３）９９．５重量％、γ−グリシドキシプロピルトリメトキシシラン（信越化学工業（株）製商品名：信越シリコーンＫＢＭ４０３）を０．５重量％とした以外は実施例１と同様にして積層体を得た。評価結果は表１に示した。
【００６３】
実施例５
エチレン系重合体として、ＬＤＰＥを９９．５重量％、エポキシ基及びアルコキシ基を有するシランカップリング剤として、γ−グリシドキシプロピルトリエトキシシランを０．５重量部の代わりに、ＭＦＲが１０ｇ／１０分、密度が９１３ｋｇ／ｍ^３であるＬＬＤＰＥ（東ソー（株）製商品名：ニポロン−ＺＴＺ４２０）９９．５重量％、γ−グリシドキシプロピルトリエトキシシラン（信越化学工業（株）製商品名：信越シリコーンＫＢＥ４０３）を０．５重量％とした以外は実施例１と同様にして積層体を得た。評価結果は表１に示した。
【００６４】
【表１】

比較例１
エチレン系重合体として、ＬＤＰＥ（東ソー（株）製商品名：ペトロセン２１３）を９９．５重量％、エポキシ基及びアルコキシ基を有するシランカップリング剤として、γ−グリシドキシプロピルトリエトキシシラン（信越化学工業（株）製商品名：信越シリコーンＫＢＥ４０３）を０．５重量部の代わりに、ＬＤＰＥ（東ソー（株）製商品名：ペトロセン２１３）１００重量％とし、エポキシ基を有するシランカップリング剤を用いなかったこと以外は実施例１と同様にして積層体を得た。評価結果は表２に示したが、アルミニウム板に対する高湿度雰囲気での接着性、及びガラス板に対する接着性が劣っていた。
【００６５】
比較例２
接着性フィルム表面のコロナ放電処理条件が５０Ｗ・分／ｍ^２である代わりに、コロナ放電処理を施さなかったこと以外は実施例１と同様にして接着性フィルム及び積層体を得た。評価結果は表２に示したが、アルミニウム板及びガラス板への接着性が劣っていた。
【００６６】
比較例３
エチレン系重合体として、ＬＤＰＥを９９．５重量％、エポキシ基及びアルコキシ基を有するシランカップリング剤として、γ−グリシドキシプロピルトリエトキシシランを０．５重量部の代わりに、ＬＤＰＥ（東ソー（株）製商品名：ペトロセン２１３）９５．０重量％、エポキシ基及びアルコキシ基を有するシランカップリング剤として、γ−グリシドキシプロピルトリエトキシシラン（信越化学工業（株）製商品名：信越シリコーンＫＢＥ４０３）を５．０重量％とした以外は実施例１と同様にしてフィルム成形加工を試みたが、押出機内において樹脂が滑り、フィルム化することができなかった。評価結果は表２に示した。
【００６７】
【表２】

【発明の効果】
本発明は、接着剤が不要であり、フィルム外観及びコストパーフォーマンスに優れる接着性フィルムを提供する。
【００６８】
さらに、本発明は、樹脂、金属及び／又はケイ素酸化物等からなる被着体を接着させ、接着力に優れた積層体を提供する。[0001]
TECHNICAL FIELD OF THE INVENTION
The present invention relates to an adhesive film using an ethylene-based resin composition. Furthermore, the present invention relates to a laminate comprising an adherend made of a resin, a metal, and / or a silicon oxide, and the adhesive film.
[0002]
[Prior art]
Polyethylene resin films are used in a wide range of fields because of their low cost and excellent moldability.
[0003]
However, the polyethylene-based resin film has a disadvantage that it is difficult to adhere to an adherend made of resin, metal, and / or silicon oxide due to its nonpolar structure. Therefore, when laminating the adherend and the polyethylene-based film, a method of applying an adhesive to the bonding interface, or a modified ethylene-based resin in which a monomer having a carboxyl group, a hydroxyl group, or an acid anhydride group is previously copolymerized with a polyethylene-based resin. A method of thermocompression bonding a film using a copolymer has been proposed.
[0004]
Further, a silane coupling agent is known as a monomer used for copolymerization of the adhesive and the polyethylene resin, and various proposals using the silane coupling agent have been made.
[0005]
As an example of using an adhesive, there has been proposed a method of applying a silane coupling agent having an amino group between a silicon oxide thin film and a polyethylene resin (for example, see Patent Document 1). However, according to this method, equipment for applying the silane coupling agent is required, and equipment costs are burdened, and processing costs for the organic solvent used when applying the silane coupling agent are increased. There is a problem.
[0006]
Examples of the composition using a resin obtained by previously copolymerizing a silane coupling agent with a polyethylene resin include ethylene-acrylic resin obtained by polymerizing a monomer component containing 5 to 40% by weight of an acrylate or a methacrylate. A polymer composition comprising 60 to 99 parts by weight of an acid ester copolymer or an ethylene / methacrylic acid ester copolymer and 1 to 40 parts by weight of a silane graft modified olefin polymer having an epoxy group. It has been proposed (for example, see Patent Document 2).
[0007]
However, according to this method, when the unsaturated group-containing silane compound is graft-modified to the epoxy group-containing olefin polymer, an organic peroxide is used. By cross-linking the copolymer or the ethylene / methacrylic acid ester copolymer or the epoxy group-containing olefin-based polymer itself, a gel called fisheye occurs frequently, and a problem such as impairing the appearance of the laminate occurs. . There is also a problem that the cost of the ethylene / acrylate copolymer or the ethylene / methacrylate copolymer and the cost of the graft modification are high.
[0008]
[Patent Document 1]
JP-A-5-131590 (page 2)
[Patent Document 2]
JP-A-1-207340 (p. 3)
[0009]
[Problems to be solved by the invention]
The present invention has been made in view of the above situation, and eliminates the need for an adhesive, reduces the appearance of a film due to a gel generated when copolymerizing a silane coupling agent, and reduces carboxyl groups and acid anhydrides. It is an object of the present invention to provide a low-cost adhesive film that can avoid problems such as corrosion of an extruder screw and the like due to the use of a monomer-containing monomer copolymer, and does not go through a graft modification step. is there.
[0010]
Another object of the present invention is to provide a laminate having excellent adhesive strength by bonding an adherend made of a resin, a metal, and / or a silicon oxide.
[0011]
[Means for Solving the Problems]
The present inventors have conducted intensive studies to solve the above-mentioned problems, and as a result, for a specific ethylene polymer, a silane coupling agent having an epoxy group and an alkoxy group was subjected to a graft modification step on the ethylene polymer. An adhesive film obtained by oxidizing the surface of a film composed of a specific amount of an ethylene-based resin composition without passing through, has excellent adhesiveness to various substrates, and is excellent in film appearance and cost performance. And completed the present invention.
[0012]
That is, according to the present invention, the melt mass flow rate measured according to JIS K 6922-1 (1998) is 0.1 to 50 g / 10 min, and the density measured according to JIS K 6922-1 (1998) is 880 to 960 kg / m ³ . A film using an ethylene-based resin composition comprising 98.5 to 99.99% by weight of a certain ethylene-based polymer and 0.01 to 1.5% by weight of a silane coupling agent having an epoxy group and an alkoxy group. Further, the present invention relates to an adhesive film characterized in that at least one surface of the film surface is oxidized.
[0013]
Further, the present invention provides an adhesive film characterized in that at least one surface of the film surface using the ethylene-based resin composition is oxidized by any method selected from corona discharge treatment, flame treatment, and plasma treatment. It is about.
[0014]
Further, the present invention provides the adhesive film of the present invention, wherein (a) a film or sheet made of a thermoplastic resin, (b) a metal plate, a metal foil or a metal and / or metal oxide vapor-deposited film, and (c) a glass plate. , A glass foil or a silicon oxide vapor-deposited film, and (d) at least one substrate selected from the group consisting of paper as an adherend, at least one adherent and at least one adhesive film. Are laminated by thermocompression bonding.
[0015]
Hereinafter, the present invention will be described in detail.
[0016]
The ethylene polymer used in the present invention has an MFR of 0.1 to 50 g / 10 min according to JIS K692-1 (1998).
[0017]
If the MFR is less than 0.1 g / 10 min, it is not preferable because the extrusion load is high when the ethylene-based resin composition is subjected to film forming and the spreadability during film formation is poor. It is not preferable that the viscosity exceeds the above range because the melt viscosity required when the ethylene-based resin composition is subjected to film forming processing is low and the film forming processability is poor.
[0018]
Further, the ethylene polymer used in the present invention has a density of 880 to 960 kg / m ³ measured according to JIS K6922-1 (1998).
[0019]
When the density is less than 880 kg / m ³ , the heat resistance of the laminate is inferior, and the adhesiveness in an atmosphere of 50 ° C. or more is unfavorably reduced. When the density exceeds 960 kg / m ³ , the adhesion to the adherend is made. Poor properties are not preferred.
[0020]
The ethylene polymer used in the present invention is not particularly limited, and may be ethylene homopolymer, a copolymer of ethylene and an α-olefin having 3 to 12 carbon atoms, a copolymer of ethylene and a vinyl ester, or the like. Is exemplified. Further, as these polymers, high-pressure low-density polyethylene (hereinafter referred to as LDPE), linear low-density polyethylene (hereinafter referred to as LLDPE), medium-density polyethylene (hereinafter referred to as MDPE), and high-density polyethylene. (Hereinafter referred to as HDPE), an ethylene-vinyl acetate copolymer (hereinafter referred to as EVA), an ethylene-acrylic acid ethyl ester copolymer (hereinafter referred to as EEA), and the like. These ethylene polymers may be used alone or in combination of two or more.
[0021]
Here, the polymerization method of the ethylene polymer is not particularly limited. In the case of LDPE, EVA, EEA, etc., for example, a radical polymerization method by a high pressure method can be mentioned. In the case of LLDPE, MDPE, HDPE, Ziegler Polymerization methods such as a gas phase method, a solution method, and a high pressure method using a Natta catalyst or a metallocene catalyst can be given.
[0022]
The silane coupling agent having an epoxy group and an alkoxy group used in the present invention is a silane compound having at least one epoxy group and an alkoxy group in a molecule.
[0023]
The silane coupling agent having such an epoxy group and an alkoxy group is not particularly limited, and β- (3,4-epoxycyclohexyl) ethyltrimethoxysilane, γ-glycidoxypropyltrimethoxysilane, γ- Glycidoxypropyltriethoxysilane, γ-glycidoxypropylmethyldimethoxysilane, γ-glycidoxypropylmethyldiethoxysilane and the like are exemplified.
[0024]
These silane coupling agents having an epoxy group and an alkoxy group may be used alone or as a mixture of two or more kinds, and may be used in combination with another silane coupling agent or a titanium-based coupling agent. .
[0025]
As the silane coupling agent having an epoxy group and an alkoxy group used in the present invention, a known silane coupling agent can be used (for example, manufactured by Chisso Corporation, trade names: SILAACE S510, S520, S530, manufactured by Shin-Etsu Chemical Co., Ltd.). (Trade names: Shin-Etsu Silicone KBM303, KBM403, KBE402, KBE403).
[0026]
In the resin composition comprising an ethylene polymer and a silane coupling agent having an epoxy group and an alkoxy group in the present invention, the blending ratio of the ethylene polymer and the silane coupling agent having an epoxy group and an alkoxy group is an ethylene polymer. 98.5 to 99.99% by weight, and 0.01 to 1.5% by weight of the silane coupling agent having an epoxy group and an alkoxy group.
[0027]
When the blending ratio of the silane coupling agent having an epoxy group and an alkoxy group is less than 0.01% by weight, the amount of the silane coupling agent exuding to the film surface is small, and the adhesive film is thermally bonded to the adherend. In this case, the adhesiveness of the resulting laminate is poor, which is not preferable. In particular, the adhesiveness when the adherend is made of silicon oxide such as glass and the adhesiveness in a high-humidity atmosphere when the adherend is made of metal such as aluminum are inferior. On the other hand, when the amount exceeds 1.5% by weight, the amount of the silane coupling agent seeping out to the film surface becomes excessive, and the adhesiveness of the laminate obtained by thermocompression bonding the adhesive film to the adherend is inferior. In addition, cost performance deteriorates, which is not preferable.
[0028]
Further, the method for producing the ethylene-based resin composition in the present invention is not particularly limited, and a method of melt-mixing an ethylene-based polymer and a silane coupling agent having an epoxy group and an alkoxy group with an extruder or the like, For example, a method of dry blending a polymer pellet and a master batch in which a silane coupling agent having an epoxy group and an alkoxy group is kneaded in a polyolefin resin in advance is exemplified.
[0029]
In addition, the ethylene-based resin composition contains, if necessary, additives commonly used in ethylene-based resins, such as an antioxidant, a lubricant, a neutralizing agent, an anti-blocking agent, a surfactant, and a slipping agent. But it doesn't matter.
[0030]
The method for producing a film using the ethylene-based resin composition of the present invention is not particularly limited, and can be obtained using an inflation molding machine, a T-die casting molding machine, a calendar molding machine, a press molding machine, or the like. is there. Further, in inflation molding or T-die casting, a multilayer film can be obtained by a co-extrusion method.
[0031]
The adhesive film of the present invention is one in which at least one surface is oxidized in order to express the adhesiveness of the film surface. Although the mechanism of the adhesion effect by the oxidation treatment is not clear, the carboxyl group formed by the oxidation treatment on the film surface using the ethylene-based resin composition and the epoxy group of the silane coupling agent react with each other. It is considered that the silane coupling agent is immobilized on the film surface, and the silanol group generated by the subsequent hydrolysis of the alkoxy group develops adhesiveness.
[0032]
The oxidation treatment method for oxidizing the film surface is not particularly limited, and examples thereof include chromic acid treatment, sulfuric acid treatment, air oxidation, ozone treatment, corona discharge treatment, flame treatment, and plasma treatment. Among these, at least one or more oxidation methods selected from corona discharge treatment, flame treatment, and plasma treatment are particularly preferable for effectively forming an oxide on the film surface using the ethylene-based resin composition.
[0033]
The corona discharge treatment is widely used as a continuous treatment technique for a plastic film or sheet surface, and is performed by passing the film through a corona atmosphere generated by a corona discharge treatment machine. In the present invention, it is preferable to perform a discharge treatment at a corona discharge density of 1 to 100 W · min / m ² in order to obtain an adhesive film having excellent adhesion to an adherend.
[0034]
The flame treatment is performed by bringing the film surface into contact with a flame generated when natural gas, propane, or the like is burned.
[0035]
Plasma treatment is an excited inert gas that is made neutral by electrically exciting a single or mixed gas such as argon, helium, neon, hydrogen, oxygen, and air with a plasma jet, then removing charged particles and electrically neutralizing. Is sprayed onto the film surface.
[0036]
In the present invention, the oxidized film surface is subjected to an oxidizing treatment having a wetting index of 330 to 700 μN / cm, particularly 370 to 600 μN / cm, as measured according to JIS K6768 (1998), whereby the adherend and It is preferable to obtain an adhesive film having excellent adhesiveness.
[0037]
The thickness of the adhesive film of the present invention is not particularly limited as long as the object of the present invention is achieved, and is preferably 1 μm to 5 mm because of excellent flexibility and small problems such as breakage.
[0038]
The laminate of the present invention comprises (a) a film or sheet made of a thermoplastic resin, (b) a metal plate, a metal foil or a metal and / or metal oxide deposited film, (c) a glass plate, a glass foil or a silicon oxide. At least one or more substrates selected from the group consisting of a vapor-deposited film and (d) paper are used as adherends, and at least one or more adherends and at least one or more oxidized surfaces of the adhesive film are thermocompression-bonded. Can be obtained.
[0039]
The film or sheet made of a thermoplastic resin used as the adherend constituting the laminate of the present invention is not particularly limited, and polyesters such as polyethylene terephthalate, polyamide, polyvinyl alcohol, ethylene-vinyl acetate copolymer saponified, polycarbonate, Examples thereof include films or sheets made of a synthetic polymer such as polyethylene and polypropylene. Further, those obtained by printing these polymer films or sheets using urethane-based ink or the like are also exemplified. Above all, a film or sheet made of polyester, polyamide, saponified ethylene-vinyl acetate copolymer and polyvinyl alcohol is preferable since the obtained laminate has high adhesive strength.
[0040]
The metal plate, metal foil or metal and / or metal oxide vapor-deposited film used as an adherend constituting the laminate of the present invention is not particularly limited. Examples of an aluminum foil, a copper foil, and the like, and a metal and / or metal oxide deposited film obtained by depositing aluminum and / or alumina on a polymer film or sheet can be exemplified.
[0041]
There is no particular limitation on the glass plate, glass foil or silicon oxide vapor-deposited film used as the adherend constituting the laminate of the present invention. Further, as the silicon oxide vapor-deposited film, silicon dioxide or the like is used as a polymer film or sheet. Examples thereof include those obtained by vapor deposition.
[0042]
The paper used as the adherend constituting the laminate of the present invention is not particularly limited, and examples thereof include kraft paper, woodfree paper, and glassine paper.
[0043]
As the method of thermocompression bonding, a known method can be used, and there is no particular limitation. For example, a method such as a thermal laminating method or a heat sealing method can be used. Further, the laminate obtained by the above processing is preferably heat-treated at a temperature of 30 ° C. or more for 10 hours or more in order to improve the adhesiveness, because the adhesive strength further increases.
[0044]
Furthermore, in order to enhance the adhesiveness between the adherend and the adhesive film, a surface treatment such as a corona treatment, a frame treatment, and a plasma treatment may be performed on the adhesion surface of the adherend. If necessary, an adhesive may be applied to the bonding surface of the adherend.
[0045]
The laminated state of the laminate according to the present invention is not particularly limited as long as it is thermocompression-bonded by combining at least one or more adherends and at least one or more adhesive films. For example, as a combination of lamination states, a combination of one adherend and one adhesive film, a combination in which one adhesive film is sandwiched between two adherends, and a combination of the adherend and / or Alternatively, when there are a plurality of adhesive films, examples thereof include a combination of different adherends and / or adhesive films.
[0046]
INDUSTRIAL APPLICABILITY The adhesive film of the present invention is extremely useful as an adhesive film for providing a wide range of industrial materials such as resin-coated or laminated steel sheets and laminated glass used for home electric appliances, automobiles, and other building material sheets.
[0047]
【Example】
Hereinafter, the present invention will be described in more detail with reference to Examples, but the present invention is not limited to these Examples.
[0048]
The methods for measuring and evaluating the physical properties and workability are described below.
[0049]
(1) Melt mass flow rate (MFR)
Conforms to JIS K6922-1 (1998).
[0050]
(2) Density Conforms to JIS K6822-1 (1998).
[0051]
(3) Adhesive to Adherend The adherend and the adhesive film were thermocompression bonded using a heat sealer (manufactured by Toyo Seiki Co., Ltd.) under the conditions of a temperature of 150 ° C., a time of 3 seconds, and a pressure of 2 MPa. As the adherend, two types of an aluminum plate (trade name: A1N30H-H18 manufactured by Toyo Aluminum Co., Ltd.) and a glass plate (manufactured by Hokuriku Sheet Glass) were used.
[0052]
The peeling test was performed using a tensile tester (trade name: Autograph DCS500, manufactured by Shimadzu Corporation), and the adherend and the adhesive film layer were peeled by 180 ° under the conditions of a sample width of 15 mm and a peeling speed of 300 mm / min. The peel strength at that time was measured, and the peel strength was defined as the adhesive strength.
[0053]
(4) Wetting index Complies with JIS K6768 (1998).
[0054]
Example 1
As an ethylene polymer, 99.5% by weight of LDPE (trade name: Petrocene 213 manufactured by Tosoh Corporation) having an MFR of 8 g / 10 min and a density of 918 kg / m ³ , a silane coupling having an epoxy group and an alkoxy group As an agent, γ-glycidoxypropyltriethoxysilane (trade name: Shin-Etsu Silicone KBE403, manufactured by Shin-Etsu Chemical Co., Ltd.) was blended in an amount of 0.5% by weight, and melt-kneaded with a single screw extruder to obtain pellets. Obtained.
[0055]
The obtained pellets are supplied to an extruder of a cast film forming machine having a screw of 25 mmφ, and extruded at a temperature of 280 ° C. from a T-die so as to have a film thickness of 30 μm. ^Under the conditions of ² , a corona discharge treatment was performed to obtain an adhesive film.
[0056]
Thereafter, a biaxially stretched polyester film having a thickness of 25 μm (manufactured by Toyobo Co., Ltd., trade name: Toyobo ester film E5100, hereinafter referred to as “PET”) was used as a base material, and one surface thereof was subjected to corona treatment. The surface of the PET film on which a corona-treated surface was coated with an anchor coat agent (trade name: Titabond T-120, manufactured by Nippon Soda Co., Ltd.) and the non-corona-treated surface of the above adhesive film were coated with a low-density polyethylene (Tosoh Corporation) The product was subjected to sandwich lamination using Petrocene 203) (trade name) to obtain an adhesive film support for evaluation of adhesiveness. The sandwich lamination was performed at an extrusion temperature of 300 ° C. and a low-density polyethylene thickness of 25 μm using an extrusion laminator having an extruder of 25 mmφ. The structure of the obtained adhesive film support (thickness: 0.08 mm, length: 10 cm, width: 10 cm) for evaluation of adhesiveness is as follows, and is configured so that the corona discharge-treated surface of the adhesive film becomes the surface. did.
[0057]
(Configuration of adhesive film support for evaluation of adhesiveness)
[PET (base material) / low density polyethylene / adhesive film (corona discharge treated surface)]
The obtained adhesive film support for adhesive evaluation was left for 3 days in an environment at a temperature of 23 ° C. and a relative humidity (hereinafter referred to as “RH”) of 50%.
[0058]
Thereafter, the adhesive film surface of the adhesive film support, ie, the corona discharge treated surface, and the adherends, ie, an aluminum plate (thickness 0.1 mm, length 10 cm, width 10 cm) and a glass plate (thickness 0.1 mm, length 10 cm and a width of 10 cm) were thermally bonded using a heat sealer under the above conditions for evaluating the adherence of the adherend.
[0059]
The laminate was then left in an environment of a temperature of 23 ° C. and a humidity of 50% RH and an environment of a temperature of 40 ° C. and a humidity of 90% RH for 7 days to evaluate the adhesiveness. Table 1 shows the evaluation results.
[0060]
Example 2
Instead of 99.5% by weight of LDPE as an ethylene polymer and 0.5 part by weight of γ-glycidoxypropyltriethoxysilane as a silane coupling agent having an epoxy group and an alkoxy group, LDPE (Tosoh ( Product name: Petrocene 213) 99% by weight, γ-glycidoxypropyltriethoxysilane (Shin-Etsu Chemical Co., Ltd. product name: Shin-Etsu Silicone KBE403) is the same as Example 1 except that it is 1% by weight. To obtain an adhesive film and a laminate. The evaluation results are shown in Table 1.
[0061]
Example 3
An adhesive film and a laminate were obtained in the same manner as in Example 1 except that the corona discharge treatment condition on the surface of the adhesive film was changed to 100 W · min / m ² instead of 50 W · min / m ² . The evaluation results are shown in Table 1.
[0062]
Example 4
Instead of 99.5% by weight of LDPE as an ethylene polymer and 0.5 part by weight of γ-glycidoxypropyltriethoxysilane as a silane coupling agent having an epoxy group and an alkoxy group, LDPE (Tosoh ( Product name: Petrocene 213) 99.5% by weight, γ-glycidoxypropyltrimethoxysilane (Shin-Etsu Chemical Co., Ltd. product name: Shin-Etsu Silicone KBM403) was implemented except for 0.5% by weight. A laminate was obtained in the same manner as in Example 1. The evaluation results are shown in Table 1.
[0063]
Example 5
As an ethylene-based polymer, LDPE was 99.5% by weight, and as a silane coupling agent having an epoxy group and an alkoxy group, γ-glycidoxypropyltriethoxysilane was 0.5 parts by weight. 10 minutes, 99.5% by weight of LLDPE (trade name: Nipolon-Z TZ420, manufactured by Tosoh Corporation) having a density of 913 kg / m ³ , γ-glycidoxypropyltriethoxysilane (manufactured by Shin-Etsu Chemical Co., Ltd.) A laminate was obtained in the same manner as in Example 1 except that 0.5% by weight (name: Shin-Etsu Silicone KBE403) was used. The evaluation results are shown in Table 1.
[0064]
[Table 1]

Comparative Example 1
99.5% by weight of LDPE (trade name: Petrocene 213 manufactured by Tosoh Corporation) as an ethylene polymer, and γ-glycidoxypropyltriethoxysilane (Shin-Etsu) as a silane coupling agent having an epoxy group and an alkoxy group 100% by weight of LDPE (trade name: Petrocene 213, manufactured by Tosoh Corporation) instead of 0.5 part by weight of Shin-Etsu Silicone KBE403 manufactured by Chemical Industry Co., Ltd., and a silane coupling agent having an epoxy group is used. A laminate was obtained in the same manner as in Example 1 except that the laminate was not used. The evaluation results are shown in Table 2, and the adhesion to the aluminum plate in a high humidity atmosphere and the adhesion to the glass plate were poor.
[0065]
Comparative Example 2
An adhesive film and a laminate were obtained in the same manner as in Example 1, except that the corona discharge treatment condition on the surface of the adhesive film was 50 W · min / m ² , but the corona discharge treatment was not performed. The evaluation results are shown in Table 2, but the adhesion to the aluminum plate and the glass plate was poor.
[0066]
Comparative Example 3
Instead of 99.5% by weight of LDPE as an ethylene polymer and 0.5 part by weight of γ-glycidoxypropyltriethoxysilane as a silane coupling agent having an epoxy group and an alkoxy group, LDPE (Tosoh ( Product name: Petrocene 213) 95.0% by weight, as a silane coupling agent having an epoxy group and an alkoxy group, γ-glycidoxypropyltriethoxysilane (product name: Shin-Etsu Silicone, manufactured by Shin-Etsu Chemical Co., Ltd.) An attempt was made to form a film in the same manner as in Example 1 except that KBE403) was changed to 5.0% by weight. However, the resin slipped in the extruder and could not be formed into a film. The evaluation results are shown in Table 2.
[0067]
[Table 2]

【The invention's effect】
The present invention provides an adhesive film that does not require an adhesive and has excellent film appearance and cost performance.
[0068]
Further, the present invention provides a laminate having excellent adhesive strength by adhering an adherend made of resin, metal and / or silicon oxide or the like.

Claims

Ethylene polymer 98 having a melt mass flow rate of 0.1 to 50 g / 10 min measured according to JIS K 6922-1 (1998) and a density of 880 to 960 kg / m ³ measured according to JIS K 6922-1 (1998). A film made of an ethylene-based resin composition comprising 0.5 to 99.99% by weight and 0.01 to 1.5% by weight of a silane coupling agent having an epoxy group and an alkoxy group, and a film surface thereof An adhesive film, wherein at least one surface of the adhesive film is oxidized.

The adhesive film according to claim 1, wherein the oxidation treatment is at least one oxidation method selected from a corona discharge treatment, a flame treatment, and a plasma treatment.

(A) a film or sheet made of a thermoplastic resin,
(B) metal plate, metal foil or metal and / or metal oxide deposited film,
(C) glass plate, glass foil or silicon oxide deposited film,
(D) At least one or more substrates selected from the group consisting of paper are used as adherends, and at least one or more adherends and at least one or more of the adhesive films according to claim 1 or 2 are provided. Wherein the oxidized surface of the laminate is thermocompression-bonded.

The laminate according to claim 3, wherein the adherend is an aluminum plate and / or a glass plate.