DE4244664A1 - Transfer-printing sheet, and the use thereof in the production of decorative boards - Google Patents
Transfer-printing sheet, and the use thereof in the production of decorative boardsInfo
- Publication number
- DE4244664A1 DE4244664A1 DE4244664A DE4244664A DE4244664A1 DE 4244664 A1 DE4244664 A1 DE 4244664A1 DE 4244664 A DE4244664 A DE 4244664A DE 4244664 A DE4244664 A DE 4244664A DE 4244664 A1 DE4244664 A1 DE 4244664A1
- Authority
- DE
- Germany
- Prior art keywords
- resin
- layer
- pattern layer
- base paper
- transfer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
Die vorliegende Erfindung betrifft einen Umdruckbogen und seine Verwendung bei der Herstellung von Dekorplatten, die als Baumaterialien und als Inneneinrichtungsmaterialien verwendet werden, insbesondere bei der Herstellung von mit in Wärme ausgehärtetem Harz beschichteten Dekorplatten, wobei das in Wärme aushärtbare Harz ein Melaminharz umfaßt.The present invention relates to a transfer sheet and its use in the production of decorative panels, which as Building materials and as interior furnishing materials be used, especially in the Preparation of thermoset resin coated decorative panels, wherein the thermosetting resin comprises a melamine resin.
Von mit in Wärme ausgehärtetem Harz beschichtete Dekorplatten eignen sich zur Verwendung als Wandmaterialien, Boden materialien und Materialien für Haushaltsmöbel, Küchen einrichtungen und ähnliches, wobei für sämtliche Materialien hohe Festigkeit und Hitzebeständigkeit gefordert wird. Dekor platten dieses Typs werden im allgemeinen hergestellt, indem ein Muster auf einen porösen Rohpapierbogen mittels Tiefdruck, Offsetdruck oder ähnlichem aufgebracht wird, der Rohpapierbogen mit einem in Wärme härtbaren Harz imprägniert und der erhaltene Rohpapierbogen zur Aushärtung des in Wärme härtbaren Harzes heißgepreßt wird.Of decorative panels coated with thermosetting resin are suitable for use as wall materials, floor materials and materials for household furniture, kitchens facilities and the like, with all materials high strength and heat resistance is required. decor plates of this type are generally made by a pattern on a porous base sheet by means of Gravure printing, offset printing or the like is applied, the Base paper sheet impregnated with a thermosetting resin and the obtained raw paper sheet for curing the in heat curable resin is hot pressed.
Titan-enthaltendes Papier wurde als poröser Rohpapierbogen für die obigen üblichen Dekorplatten verwendet. Zur Gewährleistung eines vollständigen Eindringens eines Harzes in den Rohpapierbogen wird die Gasdurchlässigkeit des Rohpapierbogens niedrig gehalten und ein den Rohpapierbogen bildendes Zellstoffasergewirr rauh ausgebildet. Darüber hinaus wird eine große Menge von Titan-Weiß oder einem Farbpigment eingesetzt, wenn das Papier (Rohpapierbogen) hergestellt wird. Ein solcher poröser Rohpapierbogen ist jedoch minderwertig in seiner Druckeignung für ein Papier, wie ein beschichtetes oder ein Kunstdruckpapier. Ein Muster kann daher auf den Rohpapierbogen nicht mit ausreichend großer Reproduzierbarkeit gedruckt werden und zahlreiche kleine, unbedruckte Stellen entstehen in einem mit einem Muster bedruckten Bereich. Ferner kann die Druckerfarbe nicht stabil auf den Rohpapierbogen übertragen werden, so daß es schwierig ist, die Qualität des Produktes gleichmäßig zu kontrollieren. Druckverfahren des vorstehenden Typs werden in den japanischen Patentanmeldungen Nr. 4540/1951 und 7737/1959 beschrieben.Titanium-containing paper was used as a porous base paper sheet used for the above conventional decorative panels. to Ensuring complete penetration of a resin in the base paper sheet is the gas permeability of the Base paper sheets kept low and one the base paper sheet forming Zellstoffasergewirr rough. About that In addition, a large amount of titanium white or a Color pigment used when the paper (base sheet) will be produced. Such a porous base paper sheet is but inferior in its print suitability for a paper, like a coated or art paper. A pattern therefore can not be sufficient on the base paper sheet great reproducibility can be printed and numerous small, unprinted spots arise in one with a Pattern printed area. Furthermore, the printer color not stably transferred to the base paper sheet, so that it is difficult, the quality of the product evenly to control. Printing method of the above type are disclosed in Japanese Patent Application Nos. 4540/1951 and 7737/1959.
Im Falle, wo ein Muster nicht leicht auf einen Rohpapier bogen gedruckt werden kann, kann eine Drucktechnik verwendet werden. Gemäß dieser Technik wird eine Musterschicht mittels einer Klebeschicht auf einen Rohpapierbogen übertragen. Beispielsweise beschreiben die japanische Patentanmeldung Nr. 22732/1963 und die japanische Offenlegungsschrift Nr. 148662/1984 ein Verfahren zur Herstellung von Dekorplatten unter Verwendung der Umdrucktechnik. In diesem Verfahren wird ein Umdruckbogen, der eine gemaserte Musterschicht enthält, über einen vorher mit einem Harz imprägnierten Rohpapierbogen gelegt, der Umdruckbogen und der Rohpapierbogen dann heißgepreßt und der Umdruckbogen schließlich von dem Rohpapierbogen abgestreift, wodurch eine Dekorplatte mit einem Holz-gemaserten Muster erhalten wird.In the case where a pattern is not easy on a base paper Sheet can be printed, a printing technique be used. According to this technique, a Pattern layer by means of an adhesive layer on a Transfer raw paper sheet. For example, describe the Japanese Patent Application No. 22732/1963 and Japanese Laid-Open Publication No. 148662/1984 discloses a method for Production of decorative panels using the Umdrucktechnik. In this process, a transfer sheet, which contains a textured pattern layer over a previous one laid with a resin impregnated base paper sheet, the Transfer sheet and the base paper sheet then hot pressed and the Finally, the transfer sheet is stripped off the base paper sheet, making a decorative panel with a wood-grained pattern is obtained.
Dieses Herstellungsverfahren für Dekorplatten, bei dem die Umdrucktechnik verwendet wird, ist jedoch nicht fehlerfrei. Einmal kann die Musterschicht nicht fest auf den mit einem Harz imprägnierten Rohpapierbogen geklebt werden, wenn die Musterschicht (Holz-gemasertes Muster) auf den Rohpapierbogen übertragen wird. Im Falle, wo ein Rohpapierbogen verwendet wird, auf den die Musterschicht fest geklebt werden kann, kann das Harz nicht vollständig in den Rohpapierbogen eingedrungen sein. Im spezielleren wird in dem vorstehend beschriebenen üblichen Verfahren ein Umdruckbogen auf einen porösen Rohpapierbogen gelegt, nachdem letzterer mit einem Harz imprägniert worden ist. Der Umdruckbogen und der Rohpapierbogen werden dann heißgepreßt, so daß das im Rohpapierbogen enthaltene Harz in die Musterschicht eindringen kann. Der Rohpapierbogen und die Musterschicht werden somit über das Harz miteinander verbunden. Wir haben jedoch gefunden, daß, wenn eine dicke und dichte Klebeschicht verwendet wird, um die Musterschicht fest auf die Oberfläche des Rohpapierbogens zu kleben, das Harz nicht gleichmäßig in die Musterschicht bei dem vorstehend angegebenen Verbindungsverfahren eindringen kann. Als Ergebnis hiervon ist die Menge an erhaltenem Produkt sehr niedrig. Wird jedoch andererseits eine dünne und grobe Klebeschicht verwendet, um ein vollständiges Eindringen des Harzes in die Musterschicht zu gewährleisten, ist die Grenzflächenhaftung zwischen der Musterschicht und dem Rohpapierbogen vermindert. Dies führt auch zu einer verminderten Qualität der Dekorplatten.This manufacturing process for decorative panels, in which the Umdrucktechnik is used, but is not error-free. Once the pattern layer can not be fixed on the one with Resin impregnated base paper sheets are glued when the Pattern layer (wood-grained pattern) on the Base paper sheet is transferred. In the case where one Raw paper sheet is used, on which the pattern layer can be stuck firmly, the resin can not completely in have penetrated the base paper sheet. In the more specific will in the conventional method described above Transfer sheet laid on a porous base sheet, after the latter has been impregnated with a resin. The Transfer sheet and the base paper sheet are then hot-pressed, so that the resin contained in the raw paper sheet in the Pattern layer can penetrate. The base paper sheet and the Pattern layer thus become together over the resin connected. However, we found that if a thick and dense adhesive layer is used to make the pattern layer firmly stick to the surface of the base paper sheet, the Resin not evenly in the pattern layer at the penetrate the above-mentioned connection method. As a result, the amount of product obtained is very low. However, on the other hand becomes a thin and coarse Adhesive layer used to complete penetration of the To ensure resin in the pattern layer is the Interface adhesion between the pattern layer and the Base paper sheet reduced. This also leads to a reduced quality of decorative panels.
Ein weiteres Problem liegt darin, daß, nachdem die Muster schicht durch Heißpressen auf den Rohpapierbogen übertragen ist, ein Substrat des Umdruckbogens nicht immer fein von der Musterschicht getrennt wird. Dies liegt daran, daß das Substrat des Umdruckbogens und die Musterschicht durch das in die Musterschicht eingedrungene Harz dazu neigen, fest miteinander verklebt zu werden.Another problem is that, after the patterns transferred layer by hot pressing on the base paper sheet is a substrate of the transfer sheet not always fine from the Pattern layer is separated. This is because that Substrate of the transfer sheet and the pattern layer through the in the pattern layer penetrated resin tend to solid to be glued together.
Von mit in Wärme härtbarem Harz beschichtete Dekorplatten erfordern, daß die den Rohpapierbogen bildende Faser, die Klebeschicht und die Musterschicht fest miteinander verklebt und durch ein Imprägnierungsharz verbunden werden. Wenn nicht, treten Blasen auf oder, es wird eine Trennung zwischen den Schichten verursacht, wenn Hitze an die Dekorplatten gebracht wird, beispielsweise, wenn ein ein heißes Wasser enthaltender Tiegel, Topf oder ähnliches auf die Dekorplatten gestellt wird. Blasen werden ebenfalls auf solchen Dekorplatten ausgebildet, wenn sie einer Nachformung unterzogen werden, bei der sie durch Hitzeanwendung gebogen werden.Of decorative panels coated with thermosetting resin require that the base sheet forming fiber, the Adhesive layer and the pattern layer firmly glued together and connected by an impregnating resin. If not, bubbles or, it will be a separation between the layers when heat is applied to the Decorative panels are brought, for example, if a one hot water containing crucible, pot or the like the decorative panels is placed. Bubbles are also on formed such decorative panels when they undergo a reshaping subjected to bending by heat application become.
Der vorliegenden Erfindung liegt somit die Aufgabe zugrunde, einen Umdruckbogen bereitzustellen, der bei der Herstellung von Dekorplatten hoher Qualität verwendet werden kann.The present invention is therefore based on the object to provide a transfer sheet used in the manufacture of decorative panels high quality can be used.
Erfindungsgemäß wird somit ein Umdruckbogen bereitgestellt, wie er in den Patentansprüchen definiert ist.According to the invention thus providing a transfer sheet, such as he is defined in the claims.
In der vorliegenden Erfindung wird eine Musterschicht auf einem Rohpapierbogen mittels eines Heißpreß-Umdruckver fahrens unter Verwendung eines erfindungsgemäßen Umdruckbogens ausgebildet. In the present invention, a pattern layer is formed a base paper sheet by means of a Heißpreß Umdruckver driving using an inventive Transfer sheet formed.
Der erfindungsgemäße Umdruckbogen kann unter Verwendung folgender Materialien hergestellt werden.The transfer printing sheet according to the invention can be made using the following materials become.
Ein synthetischer Harzfilm, wie Polyester, Polyolefin, ein Vinylharz, Polycarbonat, Polyamid, Polystyrol, ein Ethylen vinylacetat-Copolymer oder ähnliches kann als Substratfilm für den Umdruckbogen verwendet werden.A synthetic resin film such as polyester, polyolefin, a Vinyl resin, polycarbonate, polyamide, polystyrene, an ethylene vinyl acetate copolymer or the like can be used as a substrate film be used for the transfer sheet.
Unter den aufgezählten synthetischen Harzfilmen sind ein Polyethylenterephthalat-Film, ein Polyethylennaphthalat-Film und ein Polybutylenterephthalat-Film als Polyester-Filme und ein Polyethylen-Film, ein Polypropylen-Film und ein Polymethylpenten-Film als Polyolefin-Filme bevorzugt. Ferner kann erfindungsgemäß ein Hochqualitätspapier oder ähnliches, auf dem eine Polyolefin-Schicht durch Schmelz-Extrusions- Beschichtung ausgebildet wird, auch als Substratfilm verwendet werden. Die Polyolefin-Schicht kann als Ablöseschicht dienen.Among the listed synthetic resin films are a Polyethylene terephthalate film, a polyethylene naphthalate film and a polybutylene terephthalate film as polyester films and a polyethylene film, a polypropylene film and a Polymethylpentene film is preferred as polyolefin films. Further can according to the invention a high quality paper or the like, on a polyolefin layer by melt extrusion Coating is formed, also as a substrate film be used. The polyolefin layer can be used as Serve as a release layer.
Wird eine Ablöseschicht, die nachstehend beschrieben wird, ferner auf dem Substratfilm bereitgestellt, kann der Substratfilm fließend von dem Umdruckbogen getrennt werden, nachdem die Musterschicht auf den Rohpapierbogen übertragen worden ist (nämlich nach dem Heißpreßschritt).When a peel layer, which will be described below, further provided on the substrate film, the Substrate film are separated fluently from the transfer sheet, after transferring the pattern layer to the base paper sheet (after the hot pressing step).
In dem erfindungsgemäßen Umdruckbogen wird eine Ablöseschicht, wenn nötig, auf dem Substratfilm bereitgestellt, um die Ablösefähigkeit des Substrat films von der Musterschicht zu verbessern. Die Ablöse schicht wird unter Verwendung eines Gemischs, umfassend ein Acrylsäureharz und ein Melaminharz hergestellt, das fest an den Substratfilm, jedoch nur in einem solchen Ausmaß an der Musterschicht kleben kann, daß die Ablöseschicht die Musterschicht nicht abziehen kann, bevor die Musterschicht auf den Rohpapierbogen übertragen ist und leicht von der Musterschicht an der Grenzfläche zwischen der Musterschicht und der Ablöseschicht getrennt werden kann, nachdem die Musterschicht übertragen ist.In the transfer printing sheet according to the invention is a Release layer, if necessary, on the substrate film provided to the peelability of the substrate film from the pattern layer to improve. The transfer layer is produced using a mixture comprising an acrylic acid resin and a melamine resin, firmly attached to the substrate film, but only in one can stick to the pattern layer to such an extent that the Peel layer can not peel the pattern layer before the pattern layer is transferred to the base paper sheet and slightly from the pattern layer at the interface between the Pattern layer and the release layer can be separated after the pattern layer has been transferred.
Die Musterschicht kann in bekannter Druckweise unter Verwendung üblicher Druckerfarbe ausgebildet werden. Bevorzugt ist jedoch, daß ein Bindemittel oder ein Träger eines zur Ausbildung der Musterschicht zu verwendenden Druckerfarbenmittels ein Gemisch aus einem Butylaldehydharz und einem Melaminharz ist.The pattern layer can under known pressure under Use of conventional printer ink are formed. However, it is preferred that a binder or a carrier one to be used for forming the pattern layer Ink by means of a mixture of a butylaldehyde resin and a melamine resin.
Zelluloseharze, wie Nitrozellulose, Zelluloseacetat und Zelluloseacetatpropionat, Acrylsäureharze, wie Polymethyl methacrylat, Butylaldehydharze und Gemische davon können ebenfalls als Träger der Druckerfarbe verwendet werden. Insbesondere ist ein Zellulosegemisch oder ein Gemisch aus einem Melaminharz und einem Butylaldehydharz bevorzugt, da es die Permeabilität einer Melaminharz-Lösung verbessert, die als Imprägnierungsharz in dem späteren Verfahren eingesetzt wird. Obige Harze können in einer Lösungsmittel löslichen Druckerfarbe und in einer wäßrigen Druckerfarbe (wasserlösliche Druckerfarbe) verwendet werden. Ein Pigment, ein Farbstoff oder ähnliches kann dem Harz gemäß üblicher Verfahren zugegeben werden, wodurch eine gewünschte Drucker farbe erhalten wird.Cellulose resins, such as nitrocellulose, cellulose acetate and Cellulose acetate propionate, acrylic resins such as polymethyl methacrylate, butylaldehyde resins and mixtures thereof also be used as a carrier of the printing ink. In particular, a cellulose mixture or a mixture of a melamine resin and a butyl aldehyde resin, since it improves the permeability of a melamine resin solution, as the impregnating resin in the later process is used. The above resins can be in a solvent soluble ink and in an aqueous ink (water-soluble ink) can be used. A pigment, a dye or the like may be more usual in the resin Procedures are added, creating a desired printer color is obtained.
Eine Klebeschicht spielt eine besondere Rolle in der vorliegenden Erfindung. Ein Harz, das mit einem in Wärme aushärtbaren Harz verträglich ist, mit dem der Rohpapierbogen imprägniert wird, wird zur Ausbildung der Klebeschicht vorzugsweise verwendet. An adhesive layer plays a special role in the present invention. A resin that is in heat thermosetting resin is compatible with the Base paper sheet is impregnated, is used to form the Adhesive layer preferably used.
Nach Wahl des Harzes sollt die Verwendbarkeit und Verträglichkeit zwischen dem Harz und einem zur Imprägnierung zu verwendenden in Wärme aushärtbaren Harz und die Permeabilität und die Klebeeigenschaften des Harzes sorgfältig geprüft werden. Mit anderen Worten, ist es notwendig, das Harz so auszuwählen, daß die auf den Rohpapierbogen übertragene Klebeschicht das Eindringen des in Wärme aushärtbaren Harzes in den Umdruckbogen nicht stört und daß die Klebeschicht und das in Wärme aushärtbare Harz fest verklebt werden können, nachdem das in Wärme aushärtbare Harz ausgehärtet ist. Speziell eignet sich ein Gemisch aus einem Melamin- und einem Butylaldehydharz, insbesondere das Gemisch mit einem Mischungsverhältnis von 4 : 1 bis 1 : 1 (Gewichtsbasis) als Klebemittel. Die Klebeschicht kann ausgebildet werden, indem das Klebemittel durch ein bekanntes Verfahren, wie ein Beschichtungs verfahren, verwendet wird. Als Lösungsmittel für das Klebemittel kann sowohl ein organisches Lösungsmittel als auch Wasser verwendet werden.At the choice of the resin, the usability and compatibility between the resin and a to Impregnation to be used in thermosetting resin and the permeability and the adhesive properties of the resin be checked carefully. In other words, it is necessary to select the resin so that the on the Base paper sheet transferred adhesive layer the penetration of the in thermosetting resin in the transfer sheet does not bother and that the adhesive layer and the thermosetting resin can be firmly glued after that in heat hardenable resin is cured. Specially suitable Mixture of a melamine and a butylaldehyde resin, in particular the mixture with a mixing ratio of 4: 1 to 1: 1 (weight basis) as an adhesive. The Adhesive layer can be formed by the adhesive by a known method, such as a coating procedure, is used. As a solvent for the Adhesive can be both an organic solvent as also be used water.
Eine Ablöseschicht wird oft auf der Oberfläche üblicher Umdruckbögen zum Schutz einer Musterschicht angebracht. In der vorliegenden Erfindung ist es jedoch nicht notwendig, eine solche Ablöseschicht bereitzustellen. Dies liegt daran, daß die Ablöseschicht dazu neigt, das Eindringen des Harzes in den Rohpapierbogen zu stören und auch den Oberflächenglanz zu schwächen.A release layer often becomes more common on the surface Transfer sheets attached to protect a pattern layer. In However, it is not necessary for the present invention to to provide such a release layer. This is because that the release layer tends to prevent the penetration of the resin in the raw paper sheet to disturb and also the Weaken surface gloss.
Erfindungsgemäß kann ferner eine Beschichtungslage zwischen der Musterschicht und der Klebeschicht bereitgestellt werden. Der Substratfilm wird direkt mit der Klebeschicht in einem nicht-bedruckten Bereich der Musterschicht in Kontakt gebracht. Daher kann der Substratfilm nicht vollständig von der Musterschicht getrennt werden, nachdem die Musterschicht auf den Rohpapierbogen übertragen worden ist und das Muster neigt dazu teilweise an dem Substratfilm haften zu bleiben. Die zwischen der Musterschicht und der Klebeschicht angebrachte Beschichtungslage kann als Sperrschicht dienen und wirksam die mangelhafte Trennung verhindern.According to the invention, a coating layer may further be provided between the pattern layer and the adhesive layer provided become. The substrate film is directly in with the adhesive layer a non-printed area of the pattern layer in contact brought. Therefore, the substrate film can not be completely removed from the pattern layer are separated after the pattern layer has been transferred to the base paper sheet and the pattern tends to stick partially to the substrate film. The between the pattern layer and the adhesive layer attached coating layer can serve as a barrier layer and effectively prevent the defective separation.
Die Beschichtungslage kann unter Verwendung eines Beschichtungsmittels ausgebildet werden, das durch Lösung eines Harzes in einem Lösungsmittel ohne Einbringung eines Pigments hergestellt wird, wobei das Harz das gleiche wie das Bindemittelharz des zur Bildung der Musterschicht verwendeten Druckerfarbenmittels ist, oder vorzugsweise dadurch hergestellt wird, daß ein Streckmittel-Pigment, wie Calciumcarbonat, Bariumcarbonat, Aluminiumoxid oder Silicium dioxid obigem Harz zugegeben wird und das erhaltene Gemisch durch ein Lösungsmittel verdünnt wird. Das Beschichtungs mittel wird auf die Gesamtoberfläche der Klebeschicht zur Ausbildung der Beschichtungslage aufgetragen. Wird eine Beschichtungslage unter Verwendung eines Beschichtungs mittels gebildet, das ein Streckmittel-Pigment zwischen dem Substratfilm und der Musterschicht enthält, so bedeckt sie die Musterschicht, nachdem die Musterschicht auf den Rohpapierbogen übertragen ist, wodurch eine matte Schicht ausgebildet wird. Als Folge hiervon ist der Glanz der Muster oberfläche stark geschwächt oder die Farbenintensität infolge einer Rötung vermindert. Daher ist es bevorzugt, die Beschichtungslage zwischen der Musterschicht und der Klebeschicht anzubringen.The coating layer can be prepared using a Be formed coating agent by solution a resin in a solvent without introduction of a Pigments is made, wherein the resin is the same as the binder resin of the formation of the pattern layer used ink medium, or preferably is prepared by a diluent pigment, such as Calcium carbonate, barium carbonate, alumina or silicon the above resin is added and the resulting mixture is diluted by a solvent. The coating Medium is applied to the total surface of the adhesive layer Forming the coating layer applied. Will one Coating layer using a coating formed by means of an extender pigment between the Substrate film and the pattern layer so it covers the pattern layer after the pattern layer on the Raw paper sheet is transferred, creating a matte layer is trained. As a result, the luster of the patterns surface greatly weakened or the color intensity reduced as a result of redness. Therefore, it is preferred that Coating layer between the pattern layer and the Adhesive layer to install.
Jeglicher für die üblichen Dekorplatten verwendete Rohpapierbogen kann als Rohpapierbogen verwendet werden. Spezielle Beispiele des Rohpapierbogens umfassen Titan-enthaltendes Papier, Kunstpapier, Kohlepapier, Baumwollstoff, Web- bzw. Nicht-Webstoff aus Glasfaser oder synthetischer Harzfaser. Anything used for the usual decorative panels Raw paper sheets can be used as raw paper sheets be used. Specific examples of Raw paper sheets include titanium-containing paper, Art paper, carbon paper, cotton fabric, woven or Nonwoven fabric of glass fiber or synthetic resin fiber.
Von diesen Papierbögen ist Titan-enthaltendes Papier mit einem Flächengewicht von 35 g/m2 bis 140 g/m2, insbesondere 55 g/m2 bis 100 g/m2 bevorzugt. Dies liegt daran, daß obiges Papier vollständig mit einem Harz imprägniert werden kann und ein ausgezeichnetes Bild sofort zum Ausdruck gebracht wird, wenn das Papier als Rohpapierbogen verwendet wird.Of these paper sheets, titanium-containing paper having a basis weight of 35 g / m 2 to 140 g / m 2 , in particular 55 g / m 2 to 100 g / m 2 is preferred. This is because the above paper can be completely impregnated with a resin and an excellent image is immediately expressed when the paper is used as a base paper sheet.
Ein in Wärme aushärtbares Harz, mit dem der Rohpapierbogen imprägniert wird, kann aus den Harzen ausgewählt werden, die zur Herstellung üblicher Dekorplatten verwendet werden und ein Melaminharz umfassen. Ein Härtungsmittel kann bei Bedarf zusammen mit dem in Wärme aushärtbaren Harz verwendet werden.A thermosetting resin, with the raw paper sheet can be selected from the resins that are impregnated used for the production of conventional decorative panels and comprise a melamine resin. A curing agent can be used together with the heat when needed hardenable resin can be used.
Heißpressen, das durchgeführt wird, um das Eindringen des in Wärme aushärtbaren Harzes in den Rohpapierbogen zur Bildung eines Papierbogens und zur Aushärtung des Harzes zu veranlassen, kann gemäß bekannter, auf die Herstellung üblicher Dekorplatten ausgerichteter Verfahren, erfolgen. Speziell wird bei Verwendung eines Melaminharzes als in Wärme aushärtbares Harz ein Rohpapierbogen in eine Lösungsmittellösung des Harzes eingetaucht und dann herausgezogen. Nachdem das Lösungsmittel abgedampft ist, wird der Rohpapierbogen mittels einer Metallgußform heißgepreßt.Hot pressing, which is carried out to prevent the penetration of the Heat curable resin in the base paper sheet to form a paper sheet and to cure the resin may, according to known, on the manufacture conventional decorative panels aligned procedures done. Specifically, when using a melamine resin as a thermosetting resin Raw paper sheet in a solvent solution of the resin dipped in and then pulled out. After that Solvent is evaporated, the base paper sheet Hot-pressed by means of a metal mold.
Auf dem so mit Harz imprägnierten Rohpapierbogen wird ein Sauerstoff-Sperrfilm, wie aus Vinylon- oder Polyethylenterephthalat, gebildet und ausgehärtet.On the so impregnated with resin Raw paper sheet will look like an oxygen-blocking film Vinylone or polyethylene terephthalate, formed and hardened.
Der erfindungsgemäße Umdruckbogen eignet sich in einem Verfahren zur Herstellung von mit in Wärme aushärtbarem Harz beschichteten Dekorplatten, wobei eine Musterschicht auf einen Rohpapierbogen mittels eines Umdruckverfahrens anstelle eines Druckverfahrens aufgebracht wird. Da ein synthetischer Harzfilm mit hoher Ablösefähigkeit als Substratfilm für den Umdruckbogen verwendet wird, können Dekorplatten hergestellt werden, die frei von nicht-bedruckten Stellen in einem mit Muster bedruckten Bereich sind und ein schönes Aussehen haben.The transfer sheet according to the invention is suitable in a process for the preparation of in Heat curable resin coated decorative panels, being a pattern layer on one Raw paper sheet by means of a transfer printing process instead a printing process is applied. As a synthetic Resin film with high peelability as a substrate film for the Transfer sheet is used, decorative panels can be made Be free of non-printed spots in one with Pattern printed area are and have a nice look to have.
Ferner wird erfindungsgemäß die Klebeschicht unter Verwendung eines Harzes oder eines das Harz enthaltenden Mittels gebildet, das mit einem in Wärme aushärtbaren Harz zur Imprägnierung sehr verträglich ist. Deshalb ist die Haftung zwischen dem Umdruckbogen und dem Rohpapierbogen verstärkt und vollkommenes Eindringen des in Wärme aushärtbaren Harzes in den Umdruckbogen gewährleistet. Zusätzlich ist das Imprägnierungsharz mit der Klebeschicht und der Musterschicht verträglich, so daß es vollständig in die Schichten eindringen und sie fest miteinander verbinden kann. Deshalb kann eine Dekorplatte erhalten werden, die kaum Blasen produziert, wenn sie Hitze ausgesetzt ist.Furthermore, according to the invention, the adhesive layer under Use of a resin or a resin containing Means formed with a thermosetting resin is very compatible for impregnation. That is why the Adhesion between the transfer sheet and the base paper sheet amplified and perfect penetration of heat hardenable resin ensured in the transfer sheet. In addition, the impregnation resin with the adhesive layer and the pattern layer so that it is completely in penetrate the layers and connect them firmly together can. Therefore, a decorative plate can be obtained which Barely bubbles when exposed to heat.
Wird eine Ablöseschicht unter Verwendung eines Gemisches aus einem Melaminharz und einem Acrylsäureharz bereitgestellt, kann ein Umdruckbogen erhalten werden, der eine glatte Trennung zwischen dem Substratfilm und der Musterschicht gewährleistet. Wird ferner eine Klebeschicht unter Verwendung eines Gemisches aus einem Butylaldehydharz und einem Melaminharz gebildet und gleichzeitig ein Melaminharz als in Wärme aushärtbares Harz zur Imprägnierung eingesetzt, stört die Klebeschicht das Eindringen des Melaminharzes in den Rohpapierbogen nicht. Eine Dekorplatte hoher Qualität kann somit erhalten werden.When a peel layer is made using a mixture a melamine resin and an acrylic resin, can be obtained a transfer sheet, which is a smooth Separation between the substrate film and the pattern layer guaranteed. Further, an adhesive layer is under Use of a mixture of a butylaldehyde resin and a melamine resin and at the same time a melamine resin used as a thermosetting resin for impregnation, the adhesive layer disturbs the penetration of the melamine resin into not the base paper sheet. A decorative plate of high quality can thus be obtained.
Wie vorstehend beschrieben, kann mit Hilfe des erfindungsgemäßem Umdruckbogens eine Dekorplatte erhalten werden, in der eine Musterschicht, eine Klebeschicht und ein Rohpapierbogen fest durch ein in sie gleichmäßig eingedrungenes in Wärme aushärtbares Harz verbunden werden. Die Dekorplatte zeichnet sich darin aus, daß Blasen kaum gebildet werden, selbst wenn die Platte teilweise erhitzt wird.As described above, with the help of the inventive transfer sheet a Decorative plate to be obtained in a pattern layer, a Adhesive layer and a base paper sheet stuck by one in it evenly penetrated thermosetting resin get connected. The decor panel is characterized by that bubbles are hardly formed, even if the plate partially heated.
Die unter Verwendung des erfindungsgemäßen Umdruckbogens erhaltenen Dekorplatten eignen sich für Inneneinrichtungsmaterialien, wie Wandmaterialien und Bodenmaterialien, und auch für Dekormaterialien, die für Haushaltsmöbel und Küchen einrichtungen verwendet werden.The obtained using the transfer printing sheet according to the invention Decorative panels are suitable for interior furnishing materials, like wall materials and floor materials, and also for Decoration materials for household furniture and kitchens facilities are used.
Die vorliegende Erfindung wird durch die Beispiele näher erläutert. Diese sind jedoch nicht als beschränkend zu verstehen.The present invention will be more apparent from the examples explained. These are not, however, to be limiting understand.
Eine Druckerfarbe und ein Klebemittel wurden mit den
folgenden Formulierungen hergestellt. Es wird darauf
hingewiesen, daß ein 50 : 30 : 20 (Gewichtsbasis) gemischtes
Lösungsmittels aus Toluol, Isopropylalkohol und Ethylacetat
als Lösungsmittel der Druckerfarbe und des Klebemittels
verwendet wurde.
Druckerfarbe:An ink and an adhesive were made with the following formulations. It should be noted that a 50:30:20 (weight basis) mixed solvent of toluene, isopropyl alcohol and ethyl acetate was used as the solvent of the ink and the adhesive.
Printer Color:
Klebemittel:Adhesive:
Ein Ablösemittel, ein 1 : 1 (Gewichtsbasis) Gemisch aus einem Melaminharz und einem Acrylsäureharz, wurde auf einen Substratfilm einer Dicke von 25 µm, ein durch Toray Industries, Inc., hergestellter Polyethylenterephthalatfilm vom "S-Typ" (Warenzeichen), aufgebracht und auf eine Temperatur von 180°C erhitzt. Das Ablösemittel wurde somit ausgehärtet, wodurch eine Ablöseschicht erhalten wurde.A release agent, a 1: 1 (weight basis) mixture of a Melamine resin and an acrylic resin, was applied to a Substrate film of 25 μm thickness, one by Toray Industries, Inc., produced polyethylene terephthalate film of the "S-type" (trademark), applied and on a Temperature of 180 ° C heated. The release agent thus became hardened, whereby a release layer was obtained.
Auf der auf dem Substratfilm gebildeten Ablöseschicht wurde ein gemasertes Muster durch Tiefdruck unter Verwendung der vorstehend beschriebenen Druckerfarbe aufgebracht. Das vorstehend beschriebene Klebemittel wurde dann auf die gedruckte Oberfläche mittels einer Druckwalze aufgebracht, wodurch ein Umkehrbogen erhalten wurde.On the release layer formed on the substrate film was a grained pattern by gravure printing using the applied above described ink. The The adhesive described above was then applied to the printed surface applied by means of a pressure roller, whereby a reverse bow was obtained.
Als Rohpapierbogen wurde das von Kohjin Co., Ltd., hergestellte Rohpapier für Dekorplatten "KW-80" (Warenzeichen) verwendet, das ein Flächengewicht von 80 g/m2 hat. Der Umdruckbogen wurde auf das Rohpapier gelegt und dann wurden beide mittels einer auf eine Temperatur von 150°C erwärmten Metall-Druckerwalze gepreßt. Das auf dem Umdruckbogen gedruckte Muster wurde somit auf das Rohpapier übertragen.As the base paper sheet, the decorative paper "KW-80" (trademark) manufactured by Kohjin Co., Ltd., having a basis weight of 80 g / m 2 , was used. The transfer sheet was placed on the base paper and then both were pressed by means of a heated to a temperature of 150 ° C metal printing roller. The printed on the transfer sheet pattern was thus transferred to the base paper.
Das Muster-tragende Rohpapier wurde mit einer Lösungsmittel lösung eines Melaminharzes imprägniert. Nachdem das Lösungsmittel verdampft war, wurde das Rohpapier heißge preßt, wodurch eine Dekorplatte erhalten wurde. Die so erhaltene Dekorplatte zeigte eine hohe Qualität, nämlich das Melaminharz war gleichmäßig in die Platte eingedrungen und alle darin vorliegenden Schichten waren fest miteinander verbunden.The pattern-bearing base paper was treated with a solvent solution of a melamine resin impregnated. After that Solvent was evaporated, the raw paper was hot presses, whereby a decorative plate was obtained. The way obtained decorative panel showed a high quality, namely the Melamine resin had penetrated evenly into the plate and all the layers in it were solid connected.
Eine Druckerfarbe, ein Beschichtungsmittel und ein Klebemittel wurden mit den folgenden Formulierungen hergestellt. Es wird darauf hingewiesen, daß ein 50 : 30 : 20 (Gewichtsbasis) gemischtes Lösungsmittel aus Toluol, Isopropylalkohol und Ethylacetat als Lösungsmittel für die Druckerfarbe, das Beschichtungsmittel und das Klebemittel verwendet wurde.A printing ink, a coating agent and a Adhesives were made with the following formulations manufactured. It should be noted that a 50: 30: 20 (Weight basis) mixed solvent of toluene, Isopropyl alcohol and ethyl acetate as a solvent for the Printing ink, the coating agent and the adhesive was used.
Druckerfarbe:Printer Color:
Beschichtungsmittel:Coating agent:
Klebemittel:Adhesive:
Ein Ablösemittel, 1 : 1 (Gewichtsbasis) Gemisch aus einem Melaminharz und einem Acrylsäureharz, wurde auf einen Substratfilm einer Dicke von 25 µm, ein durch Toray Industries, Inc., hergestellter Polyethylenterephthalat film vom "S Typ" (Warenzeichen) in einer Menge von 2 g/m2 auf Trockenbasis mittels Tiefdruck aufgebracht und auf eine Temperatur von 180°C erhitzt. Somit wurde das Ablösemittel ausgehärtet, wodurch eine Ablöseschicht erhalten wurde.A releasing agent, 1: 1 (weight basis) mixture of a melamine resin and an acrylic acid resin, was coated on a substrate film of 25 μm in thickness, an "S" type polyethylene terephthalate film (trademark) manufactured by Toray Industries, Inc. in an amount of 2 g / m 2 applied on dry basis by gravure and heated to a temperature of 180 ° C. Thus, the release agent was cured, whereby a release layer was obtained.
Auf der auf dem Substratfilm gebildeten Ablöseschicht wurde ein gemasertes Muster durch Tiefdruck unter Verwendung der vorstehend beschriebenen Druckerfarbe aufgebracht. Das vorstehend beschriebene Beschichtungsmittel wurde dann auf die gedruckte Oberfläche in einer Menge von 2 g/m2 auf Trockenbasis mittels Tiefdruck aufgebracht und das Klebemittel wurde darauf in einer Menge von 2 g/m2 auf Trockenbasis mittels einer Tiefdruck-Druckerwalze aufgebracht. Somit wurde ein Umdruckbogen erhalten.On the release layer formed on the substrate film, a grained pattern was gravure-printed using the above-described ink. The above-described coating agent was then gravure-coated on the printed surface in an amount of 2 g / m 2 on a dry basis, and the adhesive was applied thereon in an amount of 2 g / m 2 on a dry basis by means of a gravure printing roller. Thus, a transfer sheet was obtained.
Als Rohpapierbogen wurden das durch Kohjin Co., Ltd. hergestellte Rohpapier für Dekorplatten "KW-80" (Warenzeichen) verwendet, das ein Flächengewicht von 80 g/m2 hat. Der Umdruckbogen wurde auf das Rohpapier gelegt und dann wurden beide mittels einer auf die Temperatur von 150°C erwärmten Metall-Druckerwalze gepreßt. Das auf den Umdruckbogen gepreßte Muster wurde somit auf das Rohpapier übertragen.As a base paper sheet, by Kohjin Co., Ltd. prepared base paper for decorative panels "KW-80" (trademark) used, which has a basis weight of 80 g / m 2 . The transfer sheet was placed on the base paper and then both were pressed by means of a heated to the temperature of 150 ° C metal printing roller. The pattern pressed onto the transfer sheet was thus transferred to the base paper.
Das Muster-tragende Rohpapier wurde dann mit einer Lösungs mittellösung eines Melaminharzes imprägniert. Nachdem das Lösungsmittel abgedampft war, wurde das Rohpapier heiß gepreßt, wodurch eine Dekorplatte erhalten wurde. Die so erhaltene Dekorplatte wies eine hohe Qualität auf, so war das Melaminharz gleichmäßig in die Platte eingedrungen und alle darin enthaltenen Schichten fest miteinander verbunden.The pattern-bearing base paper was then treated with a solution medium solution of a melamine resin impregnated. After that Solvent was evaporated, the raw paper was hot pressed, whereby a decorative plate was obtained. The way obtained decorative panel had a high quality, so was the melamine resin penetrated evenly into the plate and all the layers contained in it are firmly connected.
Claims (4)
einen aus einem synthetischen Harz gebildeten Substratfilm,
eine ggf. auf dem Substratfilm gebildete Ablöseschicht, wobei ein Gemisch aus einem Acrylsäureharz und einem Melaminharz verwendet wird,
eine auf der Ablöseschicht gebildete Musterschicht, und eine auf der Musterschicht gebildete Klebeschicht, wobei ein Gemisch aus einem Butylaldehydharz und einem Melaminharz verwendet wird.1. Transfer sheet containing:
a substrate film formed of a synthetic resin,
a release layer optionally formed on the substrate film, using a mixture of an acrylic acid resin and a melamine resin,
a pattern layer formed on the release layer, and an adhesive layer formed on the pattern layer using a mixture of a butyl aldehyde resin and a melamine resin.