DE202008012785U1 - Machinable A-Silicon Putty and its use - Google Patents
Machinable A-Silicon Putty and its use Download PDFInfo
- Publication number
- DE202008012785U1 DE202008012785U1 DE200820012785 DE202008012785U DE202008012785U1 DE 202008012785 U1 DE202008012785 U1 DE 202008012785U1 DE 200820012785 DE200820012785 DE 200820012785 DE 202008012785 U DE202008012785 U DE 202008012785U DE 202008012785 U1 DE202008012785 U1 DE 202008012785U1
- Authority
- DE
- Germany
- Prior art keywords
- mpas
- viscosity
- din
- impression
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Abstract
2-komponentiges
additionsvernetzendes Silicon-Putty-Material enthaltend
– 21–40
Gew.-% Organopolysiloxane mit mindestens zwei ungesättigten
Gruppen je Molekül, mit einer Viskosität von 500–50.000
mPas,
– 2–12 Gew.-% mindestens eines Organohydrogenpolysiloxans
mit mindestens 2 SiH-Gruppen im Molekül,
– 6–15
Gew.-% mindestens eines Paraffinöls der dynamischen Viskosität
bei 20°C von 50 bs 90 mPas (gemessen nach DIN 51562 T.1),
– 30–75
Gew.-% mindestens eines Füllstoffs,
– 0,00001–0,04
Gew.-% eines Pt-haltigen Hydrosilierungskatalysators, berechnet
als Pt,
– gegebenenfalls weitere Hilfsstoffe.Containing 2-component addition-curing silicone putty material
- 21-40 wt .-% organopolysiloxanes having at least two unsaturated groups per molecule, having a viscosity of 500-50,000 mPas,
2-12% by weight of at least one organohydrogenpolysiloxane having at least 2 SiH groups in the molecule,
6-15% by weight of at least one paraffin oil of the dynamic viscosity at 20 ° C. of 50 to 90 mPas (measured to DIN 51562 T.1),
30-75% by weight of at least one filler,
0.00001-0.04% by weight of a Pt-containing hydrosilation catalyst, calculated as Pt,
- optionally further excipients.
Description
Die Erfindung betrifft ein 2-komponentiges additionsvernetzendes Siliconmaterial mit Putty Konsistenz und dessen Verwendung.The The invention relates to a 2-component addition-crosslinking silicone material with putty consistency and its use.
Technischer HintergrundTechnical background
Wenn es darum geht, dass Abformungen von Gegenständen angefertigt werden, deren Dimensionen die ursprüngliche Situation möglichst exakt wiedergeben sollen, werden additionsvernetzende Silicone wegen ihrer besonderen Dimensionstreue bevorzugt angewandt. Mit diesen Materialien gelingt die Herstellung von passgenauen Restaurationen, zum Beispiel im Dental- oder otoplastischen Bereich. Gleichermaßen sind diese Abformmaterialien aufgrund ihrer Materialeigenschaften und der physiologischen Unbedenklichkeit gut geeignet zur Abformung in der Orthopädietechnik, zur Anfertigung von Epithesen, aber auch zur Anfertigung von genauen Formen in der technischen Modellherstellung sowie bei der Reproduktion von Oberflächen, unter anderem der Abformung von Kunstgegenständen. Solche additionsvernetzenden Silicone werden, insbesondere wenn sie bezüglich der Abbindecharakteristik schnell abbinden sollen (zum Beispiel bei der Abformung am Menschen), häufig als 2-Komponenten(2K)-Systeme angeboten, die vor der Anwendung gemischt werden müssen.If it is about making impressions of objects whose dimensions are the original situation as possible to reproduce exactly, are addition-curing silicones because of their particular dimension loyalty preferred. With these materials manages the production of tailor-made restorations, for example in the dental or otoplastic field. Equally are These impression materials due to their material properties and the physiological safety well suited for impression in orthopedic technology, for the preparation of epitheses, but also for the production of precise forms in the technical Modeling and reproduction of surfaces, among other things the impression of art objects. Such addition-curing silicones, especially when they are the setting characteristics quickly (for example in human impression), often as 2-component (2K) systems offered, which must be mixed before use.
Additionsvernetzende
Silicon-Abformmassen werden in verschiedenen Viskositäten
angeboten. Aus Gründen der besseren und einfacheren Applikation
sind insbesondere automatisch anmischbare 2K-Systeme bevorzugt.
Niedrigviskose Massen lassen sich dabei leicht in Statikmischern
anmischen, wenn die Materialien aus Kartuschen mittels einer Handpistole
ausgefördert werden. Für höherkonsistente
Materialien gibt es marktübliche Mischmaschinen (wie zum
Beispiel Dynamix®-(Heraeus Kulzer),
Mixstar®-(DMG) oder auch Pentamix®-(3M ESPE)Geräte), die
mittel- und hochviskose Pasten ausfördern und in einem
dynamischen Mischer mischen können. Naturgemäß sind
knetbare und unmittelbar nach dem Mischvorgang klebfreie Sili con"knet"massen
(Putties) besonders schwer ausförder- und mischbar (mögliche
Mischmaschinen sind unter anderem unter [0013] in
Diese „knetbaren"
Materialien, die in der
Dies
ist zum Beispiel in der zahnärztlichen Praxis bei der Abdrucknahme
mittels Sandwich- oder 2-phasiger Korrekturtechnik wichtig (aber
auch zum Beispiel in der Defektabformung in Orthopädie/Epithesenanfertigung
beziehungsweise nach Anpassung an die spezifischen Eigenschaften
auch in der Gehörgangabformung). Die Putty-Materialien
sind nach der Anmischung standfest (Konsistenz nach
Weitere
grundsätzliche Erfordernisse und Eigenschaften sind zum
Beispiel
Es hat nicht an Versuchen gefehlt, maschinenmischbare Putties bereitzustellen:It There has been no lack of attempts to provide machine-mixable putties:
Stand der TechnikState of the art
Wie
bereits erwähnt, sind bezüglich der Genauigkeit
und der physiologischen Unbedenklichkeit reine additionsvernetzende
maschinenmischbare Silicon-Putty-Materialien besonders erstrebenswert.
Diese werden in
- a) 1–35% Organopolysiloxanen mit 2 ungesättigten Gruppen im Molekül,
- b) 1–10% mindestens eines Organohydrogenpolysiloxan mit ≥ 2 SiH-Gruppen/Molekül,
- c) 0,00005–0,05% Pt-Katalysator (berechnet auf Pt),
- d) 4–10% Paraffinöl oder weißes Mineralöl oder Gemische und
- e) 50–90% mindestens eines Füllstoffes
besteht, wobei Merkmal a) aus
- – mindestens einem Organopolysiloxan mit einer Viskosität von 25–1.000 mPas und
- – mindestens einem Organopolysiloxan mit einer Viskosität von 60.000–500.000 mPas
besteht; fernerhin besitzt diese Zusammensetzung in mindestens einer der beiden Komponenten eine nach einem in der Schrift definierten Verfahren gemessenen Brookfield-Viskosität von 800–2.000 Pas und eine Konsistenz ≤ 35 mm nach
- a) 1-35% organopolysiloxanes having 2 unsaturated groups in the molecule,
- b) 1-10% of at least one organohydrogenpolysiloxane having ≥ 2 SiH groups / molecule,
- c) 0.00005-0.05% Pt catalyst (calculated on Pt),
- d) 4-10% paraffin oil or white mineral oil or mixtures and
- e) 50-90% of at least one filler
consists, wherein feature a) off
- At least one organopolysiloxane having a viscosity of 25-1,000 mPas and
- - At least one organopolysiloxane having a viscosity of 60,000-500,000 mPas
consists; Furthermore, this composition possesses in at least one of the two components a Brookfield viscosity of 800-2,000 Pas measured according to a method defined in the document and a consistency ≦ 35 mm after
Aus
der Offenbarung der
Wie
bereits erwähnt, benötigen solche Zusammensetzungen
trotzdem, um für das Automixsystem geeignet zu sein, spezielle
Anpassungen des Equipments. Es wäre daher wünschenswert,
ein leichter ausförderbares, einheitlich maschinengängiges
2K-A-Silicon-Putty vorliegen zu haben, das „echte" Putty-Eigenschaften aufweist
(Führung, kein Durchbeißen bei Anwendung, direkt
nach Mischvorgang klebfrei formbar/modellierbar, Konsistenz nach
Beschreibung der ErfindungDescription of the invention
Überraschenderweise wurde gefunden, dass es mit sehr niedrigviskosem Paraffinöl (Viskosität << 100 mPas) möglich ist, die genannten Anforderungen erfüllende A-Silicon-Putty-Materialien bereitzustellen. Insbesondere ist es überraschend, dass auch bei Verwendung eines im Vergleich zum Stand der Technik deutlich niedrigviskoseren Paraffinöls noch eine „Putty"-Konsistenz erzielbar ist.Surprisingly It was found to be very low viscosity paraffin oil (Viscosity << 100 mPas) possible is, the said requirements fulfilling A-silicone putty materials provide. In particular, it is surprising that even when using a significantly lower viscosity compared to the prior art Paraffin oil still a "Putty" consistency achievable is.
Eine
zweikomponentige maschinenanmischbare additionsvernetzende Silicon-Putty-Zusammensetzung
enthaltend die folgenden Bestandteile 1) bis 5) erfüllt
die oben genannten Eigenschaften (wie zum Beispiel Konsistenzen
nach
- 1) 21–40 Gew.-% eines oder mehrere Organopolysiloxane mit mindestens 2 ungesättigten Gruppen pro Molekül, wobei diese eine Viskosität zeigen von 500 mPas–50.000 mPas,
- 2) 2–12 Gew.-% mindestens eines Organohydropolysiloxans mit mindestens 2 SiH-Gruppen im Molekül,
- 3) 6–15 Gew.-% mindestens eines Paraffinöls
der dynamischen Viskosität bei 20°C von 50 bs
90 mPas (gemessen nach
DIN 51562 T.1 - 4) 30–75 Gew.-% mindestens eines Füllstoffs,
- 5) 0,00001–0,04 Gew.-% eines Pt-haltigen Hydrosilierungskatalysators, berechnet als Pt und
- 6) gegebenenfalls weitere übliche Hilfsstoffe, wie zum Beispiel Trocknungsmittel, Mittel zur Verminderung von Gasschäden, Farbmittel, Strukturmittel, Opaker, Mattierungsmittel, Verdünner, Vaselinen, Inhibitoren, Antioxidationsmittel, Geruchsstoffe.
- 1) 21-40% by weight of one or more organopolysiloxanes having at least 2 unsaturated groups per molecule, these having a viscosity of 500 mPas-50,000 mPas,
- 2) 2-12% by weight of at least one organohydropolysiloxane having at least 2 SiH groups in the molecule,
- 3) 6-15 wt .-% of at least one paraffin oil of the dynamic viscosity at 20 ° C of 50 bs 90 mPas (measured after
DIN 51562 T.1 - 4) 30-75% by weight of at least one filler,
- 5) 0.00001-0.04 wt% of a Pt-containing hydrosilation catalyst calculated as Pt and
- 6) optionally other conventional auxiliaries, such as drying agents, agents for reducing gas damage, colorants, structurants, opaques, matting agents, thinners, vaselines, inhibitors, antioxidants, odors.
Zu 1): To 1):
Organosiloxane
mit mindestens 2 ungesättigten Gruppen können
durch die allgemeine-Formel
R1 = Alkylengruppe, vorzugsweise
Vinyl
R2 = Alkylgruppe ohne Mehrfachbindung,
vorzugsweise Methyl
n > 1
m ≥ 0.Organosiloxanes having at least 2 unsaturated groups can be represented by the general formula
R 1 = alkylene group, preferably vinyl
R 2 = alkyl group without multiple bond, preferably methyl
n> 1
m ≥ 0.
Komponente 1) ist bevorzugt mindestens ein Diorganopolysiloxan mit terminalen Triorganosiloxygruppen, von denen mindestens eine Vinylgruppe ist.component 1) is preferably at least one diorganopolysiloxane with terminal Triorganosiloxy groups of which at least one is vinyl group.
Bevorzugte
Diorganopolysiloxane dieser Struktur haben die folgende Formel:
Die
Herstellung der Komponente 1) erfolgt nach üblichen Verfahren,
die beispielsweise in
Besonders bevorzugt sind lineare Polydimethylsiloxane obiger Struktur mit den angegebenen Viskositätsbereichen, bei denen die Endgruppen aus Dimethylvinylsiloxyeinheiten bestehen und die weiteren Substituenten R in der Kette aus Methylgruppen bestehen.Especially preferred are linear polydimethylsiloxanes of the above structure with the specified viscosity ranges at which the end groups consist of dimethylvinylsiloxy and the other substituents R in the chain consist of methyl groups.
Zu 2): To 2):
Organohydrogenpolysiloxan
mit mindestens 2 SiH-Gruppen, dargestellt durch die allgemeine Formel:
R
= H oder R2
0 ≥ 1
p ≥ 0.Organohydrogenpolysiloxane having at least 2 SiH groups represented by the general formula:
R = H or R 2
0 ≥ 1
p ≥ 0.
Komponente 2) ist bevorzugt ein Organopolysiloxan mit mindestens 2 Si-gebundenen Wasserstoffatomen pro Molekül. Dieses Organopolysiloxan enthält bevorzugt 0,01 bis 2 Gew.-% silici umgebundenen Wasserstoff. Die Silikonvalenzen, die nicht mit Wasserstoff- oder Sauerstoffatomen abgesättigt sind, werden mit monovalenten Kohlenwasserstoffradikalen abgesättigt, die frei von aliphatischen Mehrfachbindungen sind. Die Kohlenwasserstoffradikale können substituiert oder unsubstituiert sein. Mindestens 50%, bevorzugt 100% der Kohlenwasserstoffradikale, die an Siliciumatomen gebunden sind, bestehen aus Methylradikalen. Die Herstellung auch derartiger Komponenten ist in den unter 1) genannten Literaturstellen hinsichtlich Struktur und Herstellung beschrieben.component 2) is preferably an organopolysiloxane having at least 2 Si-bonded Hydrogen atoms per molecule. This organopolysiloxane contains preferably 0.01 to 2 wt .-% silici bound Hydrogen. The silicone valencies that are not hydrogen or Oxygen atoms are saturated with monovalent Hydrocarbon radicals saturated, free of aliphatic Multiple bonds are. The hydrocarbon radicals can be substituted or unsubstituted. At least 50%, preferably 100% of the hydrocarbon radicals bonded to silicon atoms are, consist of methyl radicals. The production of such Components are in the references mentioned under 1) terms Structure and production described.
Die Mengenverhältnisse der Komponenten 1) und 2) sind bevorzugt derart gewählt, dass pro Mol an ungesättigter Doppelbindung der Komponente 1) 0,75 bis 5 Mol SiH-Einheiten aus der Komponente 2) vorliegen. Die Summe der Komponenten 1) und 2) liegen im Bereich von 10 bis 40 Gew.-%, bevorzugt von 15 bis 25 Gew.-%, bezogen auf das Gesamtgewicht aller Komponenten.The Ratios of components 1) and 2) are preferred chosen such that per mole of unsaturated Double bond of component 1) from 0.75 to 5 mol SiH units Component 2) are present. The sum of components 1) and 2) are in the range of 10 to 40 wt .-%, preferably from 15 to 25 Wt .-%, based on the total weight of all components.
Zu 3) Paraffinöl:To 3) paraffin oil:
Komponente
3) ist ein Paraffinöl oder weißes Mineralöl,
das ein bei Raumtemperatur flüssiges Gemisch von Alkanen
mit einer dynamischen Viskosität bei 20°C von
50 bs 90 mPas (gemessen nach
Zu 4) Füllstoff:To 4) filler:
Als Füllstoffe können sowohl verstärkende als auch nicht verstärkende Füllstoffe verwendet werden. Die verwendeten Füllstoffe können oberflächenbehandelt sein oder auch nicht.When Fillers can be both reinforcing used as well as non-reinforcing fillers become. The fillers used can be surface treated his or not.
Typische nicht verstärkende Füllstoffe sind Quarze, Cristobalite, Diatomeenerden, Kieselgure, Schichtsilikate (Bentonite), Calciumcarbonate, Talkum, Zeolithe, Montmorillonite, Natriumaluminiumsilikate, Metalloxide wie Aluminium- oder Zinkoxid bzw. deren Mischoxide, Glaspulver. Diese Füllstoffe können durch Oberflächenbehandlung hydrophobiert sein. Zusätzlich sind Kunststoff- oder Glashohlkugeln zu nennen. Es kommen auch faserförmige Füllstoffe in Frage. Die Füllstoffe können auch röntgenopak sein, wie z. B. Zirkonium- oder Bariumverbindungen.typical non-reinforcing fillers are quartz, cristobalites, Diatomaceous earth, diatomaceous earth, phyllosilicates (bentonites), calcium carbonates, Talc, zeolites, montmorillonites, sodium aluminum silicates, metal oxides such as aluminum or zinc oxide or their mixed oxides, glass powder. These fillers can be made by surface treatment be hydrophobic. In addition, plastic or glass bubbles to call. There are also fibrous fillers in question. The fillers can also be radiopaque be like For example, zirconium or barium compounds.
Die einsetzbaren nicht-verstärkenden Füllstoffe sind bevorzugt solche mit einer BET-Oberfläche von bis zu 50 m2/g. Weiter Beispiele sind Calciumsilikat, Zirkoniumsilikat, Bariumsulfat, Gips, Kunststoffpulver. Besonders bevorzugt sind Quarz, Cristobalit und Natriumaluminiumsilikate, die oberflächenbehandelt sein können.The usable non-reinforcing fillers are preferably those having a BET surface area of up to 50 m 2 / g. Further examples are calcium silicate, zirconium silicate, barium sulfate, gypsum, plastic powder. Particularly preferred are quartz, cristobalite and sodium aluminum silicates, which may be surface-treated.
Verstärkende Füllstoffe können zum Beispiel Kieselgele, pyrogene oder Fällungskieselsäuren, Siliciumaluminiummischoxide sein.reinforcing Fillers can be, for example, silica gels, pyrogenic or precipitated silicas, silicoaluminum mixed oxides be.
Vorzugsweise werden Mischungen verschiedener Füllstoffe eingesetzt.Preferably Mixtures of different fillers are used.
Zu 5) Der Pt-haltige HydrosilierungskatalysatorTo 5) The Pt-containing hydrosilation catalyst
Dies
ist bevorzugt ein Platinkomplex, der z. B. aus Hexachloroplatinsäure
durch Reduktion mit Tetramethyldivinyldisiloxan hergestellt werden
kann. Geeignet sind aber auch andere Platinverbindungen, die die Additionsvernetzung
beschleunigen. Gut geeignet sind beispielsweise solche Platin-Siloxan-Komplexe,
wie sie in
Zu 6) Hilfsmittel bzw. HilfsstoffeTo 6) auxiliaries or auxiliaries
Hilfsstoffe können zum Beispiel Trocknungsmittel, Mittel zur Verminderung von Gasschäden, Farbmittel, Strukturmittel, Opaker, Mattierungsmittel, Verdünner, Vaselinen, Inhibitoren, Antioxidationsmittel, Geruchsstoffe sein. Es kommen auch Weichmacher oder Trennöle, wie Polydimethylsiloxan-Öle, ohne reaktive Alkenyl- oder SiH-Gruppen mit einer Viskosität von vorzugsweise 0,001–10 Pa·s bei 25°C in Frage. Darüber hinaus können zusätzliche Formtrennmittel wie Fettsäure- oder Fettalkoholderivate oder Extrusionshilfsmittel, wie PTFE-Pasten Verwendung finden. Die Stabilität nach Heißlufteinwirkung lässt sich beispielsweise mit bekannten Heißluftstabilisatoren, wie Fe-, Ti-, Ce-Verbindungen, organischer Salze davon oder ihrer organischen Komplexe erhöhen. Weiterhin können auch organische Farbstoffe, wie trübende oder nicht trübende Farbstoffe enthalten sein. Es kommen auch Zeolithe, Pd auf Trägermaterial, Farbpigmente, hydriertes Rhizinusölderivat als Strukturmittel, kurzkettige oder zyklische Siliconverbindung wie Vinyl-D4 oder Vinyl-M2 als Inhibitor, und Antioxidationsmittel in Betracht.Adjuvants may be, for example, desiccants, gas damage reducers, colorants, structurants, opaques, matting agents, thinners, vaselines, inhibitors, antioxidants, fragrances. Also suitable are plasticizers or release oils, such as polydimethylsiloxane oils, without reactive alkenyl or SiH groups having a viscosity of preferably 0.001-10 Pa · s at 25 ° C. In addition, additional mold release agents such as fatty acid or fatty alcohol derivatives or extrusion aids, such as PTFE pastes can be used. The stability after hot air exposure can be increased, for example, with known hot air stabilizers, such as Fe, Ti, Ce compounds, organic salts thereof or their organic complexes. Furthermore, organic dyes, such as opacifying or non-opacifying dyes may be included. Also suitable are zeolites, Pd on support material, color pigments, hydrogenated castor oil derivative as structurant, short-chain or cyclic silicone compound such as vinyl-D 4 or vinyl-M 2 as inhibitor, and antioxidants.
Bevorzugte Ausführungsformen der Erfindung sind Zusammensetzungen enthaltend
- 1) 25–35 Gew.-% eines oder mehrerer Organopolysiloxane mit mindestens 2 ungesättigten Gruppen pro Molekül, wobei diese eine Viskosität zeigen von 500 mPas–50.000 mPas,
- 2) 3–8 Gew.-% Organohydrogenpolysiloxan mit mindestens 2 SiH-Gruppen im Molekül,
- 3) 7–11 Gew.-% mindestens eines Paraffinöls
der dynamischen Viskosität bei 20°C von 50 bs
90 mPas (gemessen nach
DIN 51562 T.1 - 4) 50–70 Gew.-% Füllstoffe,
- 5) 0,001–0,01 Gew.-% eines Pt-haltigen Hydrosilierungskatalysators, berechnet als Pt.
- 1) 25-35% by weight of one or more organopolysiloxanes having at least 2 unsaturated groups per molecule, these having a viscosity of 500 mPas-50,000 mPas,
- 2) 3-8% by weight of organohydrogenpolysiloxane having at least 2 SiH groups in the molecule,
- 3) 7-11 wt .-% of at least one paraffin oil of the dynamic viscosity at 20 ° C of 50 bs 90 mPas (measured after
DIN 51562 T.1 - 4) 50-70% by weight of fillers,
- 5) 0.001-0.01 wt% of a Pt-containing hydrosilation catalyst calculated as Pt.
Zusätzlich können Hilfsstoffe aus der Gruppe der Zeolithe, Pd auf Trägermaterial, Röntgenopaker, Farbpigmente, hydriertes Rhizinusölderivat als Strukturmittel, kurzkettige oder zyklische Siliconverbindung wie Vinyl-D4 oder Vinyl-M2 als Inhibitor, Geruchsstoff, Antioxidationsmittel anwesend sein.In addition, auxiliaries from the group of zeolites, Pd on support material, radiopaque, color pigments, hydrogenated castor oil derivative as structurant, short-chain or cyclic silicone compound such as vinyl-D 4 or vinyl-M 2 as inhibitor, odorant, antioxidant may be present.
Die Zusammensetzungen haben vorzugsweise die Form von zwei Pasten und beginnen die Abbindereaktion durch Vermischen.The Compositions are preferably in the form of two pastes and begin the setting reaction by mixing.
Um die Materialien lagerstabil zu halten, werden die Komponenten 1), 2) und 5) zweckmäßigerweise nicht zusammen in derselben Paste aufbewahrt, da dies zu einer vorzeitigen Aushärtung führen kann.Around keeping the materials storage stable, the components 1), 2) and 5) expediently not together in the same paste, as this leads to premature curing can lead.
In
einer bevorzugten Ausführungsform werden die 2-komponentigen
Formulierungen hinsichtlich der Einsatzstoffe so aufgeteilt, dass
Paste
A Bestandteile gemäß 1), 2), 3), 4) und 6) enthält
sowie
Paste B Bestandteile gemäß 1), 3),
4), 5) und 6).In a preferred embodiment, the 2-component formulations are divided with respect to the starting materials so that
Paste A contains components according to 1), 2), 3), 4) and 6) and
Paste B ingredients according to 1), 3), 4), 5) and 6).
Grundsätzlich sind sämtliche Mischungsverhältnisse zwischen A und B als geeignet zu betrachten, bevorzugt 1–10 Volumenteil A mit 1–10 Volumenteil B. In der Praxis orientiert sich an den üblichen, zum Teil zuvor genannten, etablierten Mischsystemen (Mischmaschine und den dafür konzipierten dynamischen Mischern). Als Primärpackmittel sind alle Packmittel, in denen die Einzelpasten lagerstabil sind, denkbar. In der Praxis haben sich (5:1)-Hartkartuschen (circa 380 ml) beziehungsweise (5:1)-Schlauchbeutelsysteme (circa 360 ml) bewährt.in principle are all mixing ratios between A and B considered suitable, preferably 1-10 parts by volume A with 1-10 parts by volume B. In practice oriented at the usual, partly before mentioned, established Mixing systems (mixing machine and the designed for it dynamic mixers). As primary packaging, all packaging, in which the individual pastes are stable in storage conceivable. In practice have (5: 1) -hart cartridges (about 380 ml) or (5: 1) -Buch bag systems (about 360 ml) proven.
Geeignete
Kartuschen- und Schlauchbeutelsysteme sind in
Anwendungsbereiche:Applications:
Die Zusammensetzung der Erfindung kann wie folgt Verwendung finden:
- 1. Vor allem als Putty in der zahnärztlichen Praxis als Abformmaterial (Vorteil: komfortables Mischen, keine Kontamination zwischen Base und Cat. wie beim manuellen Mischen, keine Materialvergeudung (nur soviel wird gefördert wie notwendig), homogene, blasen- und streifenfreie Mischung, keine Inhibition durch unter Umständen ungeeignete Handschuhe) in allen dortigen Putty-Indikationen. Die Kombination auch mit niedrigviskosen Korrekturmaterialienis ist problemlos möglich.
- 2. Verwendung im Dentallabor („Lab Putty", zum Beispiel zum Ausblocken, zur Herstellung von Vorwällen etc.).
- 3. Bei der Abformung von Defekten am Gesichtsschädel, an Gliedmaßen, am Rumpf von Menschen zur Anfertigung von individuellen Körperersatzteilen oder Hilfsmitteln (wie orthopädischen Einlagen).
- 4. Bei der Abformung von Oberflächen/Gegenständen, gegebenenfalls in Kombination mit Korrekturmaterialien.
- 5. Bei der Abformung von biologischem Substrat, zum Beispiel in der Tierheilkunde.
- 6. Das Material lässt sich gegebenenfalls in weicherer Einstellung (zum Beispiel durch Zusatz von Vaseline) auch direkt aus einer Spritze fördern und ist aus dieser heraus auch als Abformmaterial, zum Beispiel für Ohrabformungen, geeignet.
- 7. Die aus der Maschine geförderten Materialien sind analog den bekannten handangemischten A-Silicon-Putty-Materialien anwendbar, das heißt, sie können normal beschnitten, desinfiziert, gereinigt, gelagert, mit Modellmaterial ausgegossen beziehungsweise auch mit Korrekturmaterial verwendet werden.
- 1. Above all as a putty in the dental practice as an impression material (advantage: comfortable mixing, no contamination between base and cat as with manual mixing, no waste of material (only as much is encouraged as necessary), homogeneous, bubble and streak-free mixture, none Inhibition by possibly unsuitable gloves) in all local putty indications. The combination with low-viscosity correction materials is possible without problems.
- 2. Use in the dental laboratory ("Lab Putty", for example for blocking out, for the production of lintels, etc.).
- 3. In the imaging of defects on the facial skeleton, on the limbs, on the trunk of people to make individual body parts or aids (such as orthopedic insoles).
- 4. In the impression of surfaces / objects, if necessary in combination with correction materials.
- 5. In the impression of biological substrate, for example in veterinary medicine.
- 6. If necessary, the material can also be conveyed directly from a syringe in a softer setting (for example by adding petroleum jelly) and is also suitable for this purpose as an impression material, for example for ear impressions.
- 7. The materials conveyed from the machine are analogous to the known hand-mixed A-silicone putty materials applicable, that is, they can be normal pruned, disinfected, cleaned, stored, poured with model material or even be used with correction material.
Die
Eignung als maschinenanmischbares A-Silicon-Putty von Variante 1
unter Verwendung einer sehr niedrigviskosen Paraffinölqualität
ist insofern überraschend, da das Paraffinöl prak tisch
als Verdünner oder Trennmittel wirkt und in höheren
Anteilen enthalten ist. Dennoch ist das Material, abgefüllt
in eine übliche 5:1-Kunststoffkartusche, mit einem handelsüblichen
Anmischgerat mischbar und erfüllt nicht nur die Konsistenzbedingungen
nach
Beispiele:Examples:
Die folgenden Beispiele sollen die Erfindung verdeutlichen, ohne diese einzuschränken. Teil- und Prozentangaben beziehen sich wie in der übrigen Beschreibung auf das Gewicht, sofern nicht anders angegeben.The The following examples illustrate the invention, without this limit. Parts and percentages refer as in the rest of the description on the weight, provided not stated otherwise.
Aus
Tabelle 1 ist zu erkennen, daß auch bei der Verwendung
der niedrigviskoseren Paraffinölqualität die Variante
1 mit einer Vinylsiliconölviskosität von 20.000
mPas überraschenderweise geeignet, eine putty-ähnliche,
maschinenanmischbare Qualität zu erzeugen (während
die aus Vergleichsgründen ebenfalls gefertigte Variante
2 eine bezüglich
Die
verwendete Paraffinqualität ist wie folgt charakterisiert:
Das in der Tabelle dargestellte Paraffinöl hat eine dynamische Viskosität deutlich unter 100 mPas (bei 20°C), besonders bevorzugt < 80 mPas (bei 20°C). Es kann ein Paraffinöl oder ein entsprechendes Gemisch darstellen.The paraffin oil shown in the table has a dynamic Viscosity significantly below 100 mPas (at 20 ° C), more preferably <80 mPas (at 20 ° C). It can be a paraffin oil or a represent appropriate mixture.
ZITATE ENTHALTEN IN DER BESCHREIBUNGQUOTES INCLUDE IN THE DESCRIPTION
Diese Liste der vom Anmelder aufgeführten Dokumente wurde automatisiert erzeugt und ist ausschließlich zur besseren Information des Lesers aufgenommen. Die Liste ist nicht Bestandteil der deutschen Patent- bzw. Gebrauchsmusteranmeldung. Das DPMA übernimmt keinerlei Haftung für etwaige Fehler oder Auslassungen.This list The documents listed by the applicant have been automated generated and is solely for better information recorded by the reader. The list is not part of the German Patent or utility model application. The DPMA takes over no liability for any errors or omissions.
Zitierte PatentliteraturCited patent literature
- - EP 1502572 A1 [0003, 0006, 0008, 0009, 0010] - EP 1502572 A1 [0003, 0006, 0008, 0009, 0010]
- - EP 1372575 B1 [0006, 0009, 0010, 0010, 0011] - EP 1372575 B1 [0006, 0009, 0010, 0010, 0011]
- - WO 02/058641 [0006, 0008] WO 02/058641 [0006, 0008]
- - DE 10116223 [0010] - DE 10116223 [0010]
- - US 4035453 [0017] - US 4035453 [0017]
- - US 3715334 [0029] US 3715334 [0029]
- - US 3775352 [0029] US 3775352 [0029]
- - US 3814730 [0029] US 3814730 [0029]
- - EP 0787655 [0037, 0037] EP 0787655 [0037, 0037]
- - EP 1121195 [0037] - EP 1121195 [0037]
- - EP 1227049 [0037] - EP 1227049 [0037]
- - DE 202005000929 U1 [0037] - DE 202005000929 U1 [0037]
- - DE 102005061921 A1 [0037] DE 102005061921 A1 [0037]
- - DE 102005007055 A1 [0037] - DE 102005007055 A1 [0037]
- - E 102005002850 A1 [0037] - E 102005002850 A1 [0037]
- - DE 000029822967 U1 [0037] - DE 000029822967 U1 [0037]
- - DE 000029724380 U1 [0037] - DE 000029724380 U1 [0037]
- - DE 000029602111 U1 [0037] - DE 000029602111 U1 [0037]
- - DE 000010021467 A1 [0037] DE 000010021467 A1 [0037]
Zitierte Nicht-PatentliteraturCited non-patent literature
- - DIN EN ISO 4823 [0004] - DIN EN ISO 4823 [0004]
- - DIN EN ISO 4823:2000 [0005] - DIN EN ISO 4823: 2000 [0005]
- - ISO 4823 [0010] - ISO 4823 [0010]
- - DIN EN ISO 4823:2000 [0012] - DIN EN ISO 4823: 2000 [0012]
- - DIN EN ISO 4823:2000 [0014] - DIN EN ISO 4823: 2000 [0014]
- - DIN 51562 T.1 [0014] - DIN 51562 T.1 [0014]
- - W. Noll, "Chemie und Technologie der Silikone", Verlag Chemie Weinheim, 2. Auflage 1964, Seite 162–206 [0018] - W. Noll, "Chemistry and Technology of Silicones", Verlag Chemie Weinheim, 2nd edition 1964, pages 162-206 [0018]
- - DIN 51562 T.1 [0023] - DIN 51562 T.1 [0023]
- - DIN 51562 T.1 [0031] - DIN 51562 T.1 [0031]
- - ISO 4823 [0039] - ISO 4823 [0039]
- - ISO 4823 [0041] - ISO 4823 [0041]
Claims (4)