DE102005048870A1 - Production of multicolored inscriptions or marks on label material e.g. for sign or label involves laser ablation downwards from top of material having substrate and 2 or more layers of different color, preferably plastics film laminate - Google Patents

Production of multicolored inscriptions or marks on label material e.g. for sign or label involves laser ablation downwards from top of material having substrate and 2 or more layers of different color, preferably plastics film laminate Download PDF

Info

Publication number
DE102005048870A1
DE102005048870A1 DE200510048870 DE102005048870A DE102005048870A1 DE 102005048870 A1 DE102005048870 A1 DE 102005048870A1 DE 200510048870 DE200510048870 DE 200510048870 DE 102005048870 A DE102005048870 A DE 102005048870A DE 102005048870 A1 DE102005048870 A1 DE 102005048870A1
Authority
DE
Germany
Prior art keywords
layer
color
layers
laser
film laminate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
DE200510048870
Other languages
German (de)
Inventor
Half Passoth
Uwe Ramin
Willibald Schmidt
Bernd Schneeweis
Norbert Wolf
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Mercedes Benz Group AG
Original Assignee
DaimlerChrysler AG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by DaimlerChrysler AG filed Critical DaimlerChrysler AG
Priority to DE200510048870 priority Critical patent/DE102005048870A1/en
Publication of DE102005048870A1 publication Critical patent/DE102005048870A1/en
Withdrawn legal-status Critical Current

Abstract

Production of colored inscriptions or marks on label materials, which have substrate layer(s) (1) and at least 2 colored layers (2, 2') of different color, the colored layers are ablated from above downwards and at least to the top colored layer (2) by laser radiation or laser gravure in the required areas (4, 5), so that the underlying colored layer (2', 2") or substrate (1) is exposed. An independent claim is also included for plastics film laminate with not less than 2 superimposed colored layers (2, 2') and a substrate layer (1) suitable for this purpose.

Description

Die Erfindung betrifft ein Verfahren zur Herstellung von farbigen Beschriftungen oder Markierungen auf Kunststofffolien, insbesondere mehrfarbigen Schildern oder Klebeetiketten mittels Laserbestrahlung oder Lasergravur und eine Kunststofffarbfolie oder Kunststofffarbetikette mit mehreren übereinander angeordneten Farbschichten und einer Trägerschicht, zur Herstellung von farbigen Beschriftungen oder Markierungen mittels Laserbestrahlung oder -gravur.The The invention relates to a method for the production of colored labels or markings on plastic films, in particular multi-colored signs or adhesive labels by means of laser irradiation or laser engraving and a plastic color foil or plastic color label with several superimposed arranged color layers and a carrier layer, for the production of colored labels or markings by means of laser irradiation or engraving.

Durch Lasergravur oder Laserbestrahlung gefertigte Schilder, Etiketten, Labels oder dergleichen (im folgenden zusammenfassend Etikettenmaterial) sind bereits weit verbreitet. Dabei besteht die Farbauswahl ganz überwiegend lediglich aus zwei Farben. In der Regel ist die Farbgebung auf Schwarz/Weiß beschränkt. Typischerweise wird dabei entweder eine schwarze Deckschicht im Schriftbereich weg gebrannt und eine weiße Grundschicht frei gelegt, so dass eine weiße Beschriftung erzeugt wird, oder in einer weißen Deckschicht wird durch Lasereinwirkung eine Schwärzung erzeugt, beziehungsweise eine Beschriftung eingebrannt, so dass schwarze Beschriftung auf weißem Grund zugänglich wird. Beim Verfahren zum Einbrennen von Beschriftungen kann durch lasersensitive Pigmente in der Deckschicht eine Verbesserung des Effekts erreicht werden.By Laser engraved or laser irradiated signs, labels, Labels or the like (in the following summary label material) are already widespread. The color selection is overwhelming only two colors. As a rule, the color scheme is limited to black and white. typically, is either a black cover layer in the writing area burned away and a white one Exposed base layer so that a white label is generated, or in a white one Cover layer is generated by laser action, a blackening, respectively a caption branded, leaving black caption on it white Reason accessible becomes. In the process of branding labels can by Laser-sensitive pigments in the topcoat improve the Effects are achieved.

In unterschiedlichsten Bereichen sind zweifarbige Schilder, Labels oder Klebeetiketten nicht mehr zeitgemäß. Mehrfarbige Beschriftungen sind in manchen Bereichen auch gesetzlich vorgeschrieben.In various areas are bicolor signs, labels or sticky labels out of date. Multi-colored labels are also required by law in some areas.

Aus der DE 10 2004 053 376 A1 ist ein Verfahren zur Herstellung von farbigen Beschriftungen auf Kunststoffen bekannt. Dabei wird ein Folienlaminat mit zwei übereinander liegenden und mit einer Trägerfolie getrennten Schichten verwendet. Die erste Schicht enthält einen Energieabsorber und die zweite Schicht Farbmittel und eine Polymerkomponente. Bei der Lasergravur verschweißt die Polymerkomponente mit der Kunststoffoberfläche, wodurch die Beschriftungsfarbe auf den Kunststoff übertragen wird. Hierdurch können nur einfarbige Markierungen oder Beschriftungen hergestellt werden.From the DE 10 2004 053 376 A1 is a method for the production of colored labels on plastics known. In this case, a film laminate with two superposed and separated with a carrier film layers is used. The first layer contains an energy absorber and the second layer colorant and a polymer component. In laser engraving, the polymer component bonds to the plastic surface, which transfers the marking color to the plastic. As a result, only monochrome markings or labels can be produced.

Aus der DE 200 17 501 ist eine durch Laserstrahl beschriftbare Folie bekannt, mit der sich mehrfarbige Farbfolien herstellen lasen. Die beschriftbare Folie weist mindestens eine für einen Laserstrahl weitgehend durchlässige Schutzschicht (Deckschicht) auf, an deren Unterseite mindestens eine opake und durch den Laserstrahl ablatierbare Schicht und mindestens eine gegen Laserstrahlung weitgehend resistente und kontrastgebende Schicht angeordnet ist. Die Beschriftung erfolgt, indem die ablatierbare Schicht unter der Deckschicht abgetragen wird und die darunter liegenden Schichten freigelegt werden. Werden mehrere ablatierbare opake Schichten mit dazwischen liegenden transparenten und durchgefärbten Schichten angeordnet so sind auch verschiedenfarbige Beschriftungen möglich. Durch Abtragen einer oder mehrerer opaker ablatierbarer Schichten werden entsprechend mehrere Farbschichten frei gelegt, wobei sich die Farbe der Beschriftung dann additiv aus den Schichtfarben zusammensetzt.From the DE 200 17 501 is a laser-writable film known to make with the multicolor color films read. The inscribable film has at least one protective layer (cover layer) which is largely transparent to a laser beam, on the underside of which at least one opaque layer which can be ablated by the laser beam and at least one layer which is largely resistant and contrasting to laser radiation is arranged. The inscription takes place by ablating the ablatable layer under the cover layer and exposing the underlying layers. If several ablatable opaque layers are arranged with transparent and through-colored layers in between, then also differently colored inscriptions are possible. By removing one or more opaque layers which can be ablated, a plurality of color layers are accordingly exposed, the color of the lettering then being composed of the layer colors additively.

Nachteilig ist, dass die opake Schicht im inneren der Folie liegt. Dies bringt Nachteile beim Durchstrahlen der darüber liegenden Folienschichten, sowie beim Ablatieren, da das ablatierte Material im Folieninneren entsteht.adversely is that the opaque layer lies inside the film. This brings Disadvantages when irradiating the overlying film layers, and during ablation, as the ablated material inside the film arises.

Es ist Aufgabe der Erfindung, ein einfaches Laserbeschriftungs-Verfahren zur Herstellung von mehrfarbigem Etikettenmaterial aufzuzeigen und Kunststoffetiketten, beziehungsweise Kunststofffolienlaminate für eine Laserbeschriftung zur Herstellung von mehrfarbig beschriftetem Etikettenmaterial, beziehungsweise Kunststofffolienlaminate bereitzustellen.It The object of the invention is a simple laser marking method for the production of multicolored label material and plastic labels, or plastic film laminates for a laser marking the Production of multi-colored labeled label material, respectively To provide plastic film laminates.

Die Aufgabe wird erfindungsgemäß gelöst, durch ein Verfahren zur Herstellung von farbigen Beschriftungen oder Markierungen auf Etikettenmaterial, welches zumindest eine Trägerschicht und mindestens zwei Farbschichten unterschiedlicher Färbung aufweist, mit den Merkmalen des Anspruchs 1, sowie durch ein Kunststofffolienlaminat mit mindestens zwei übereinander angeordneten Farbschichten und einer Trägerschicht, zur Herstellung von farbigen Beschriftungen oder Markierungen, beziehungsweise Kunststofffarbetiketten mit den Merkmalen des Anspruchs 11.The The object is achieved by, by a method of producing colored labels or markings on label material, which at least one carrier layer and at least two Has color layers of different colors, with the features of claim 1, and by a plastic film laminate with at least two on top of each other arranged color layers and a carrier layer, for the production colored labels or markings, or plastic color labels with the features of claim 11.

Der Gegenstand der Erfindung wird anhand von schematischen Zeichnungen näher erläutert.Of the The invention is based on schematic drawings explained in more detail.

Dabei zeigen:there demonstrate:

1 Ein Kunststofffolienlaminat ohne Beschriftung mit einer Trägerschicht (1), und zwei Farbschichten (2) und (2'), sowie eine Schicht aus Klebemittel (6), sowie beschrifteten Bereichen (4, 5) 1 A plastic film laminate without inscription with a carrier layer ( 1 ), and two color layers ( 2 ) and ( 2 ' ), as well as a layer of adhesive ( 6 ), as well as labeled areas ( 4 . 5 )

2 Ein beschriftetes Kunststofffolienlaminat mit einer Trägerschicht (1), und vier Farbschichten (2), (2'), (2''), (2'''), dazwischen liegenden Pufferschichten (3), einer Klebemittelschicht (6), sowie beschrifteten Bereichen (7, 8, 9) Der erste Aspekt der Erfindung betrifft ein Verfahren zur Herstellung von farbigen Beschriftungen oder Markierungen auf Etikettenmaterial, welches zumindest eine Trägerschicht und mindestens zwei Farbschichten unterschiedlicher Färbung aufweist, wobei die Farbschichten durch Laserbestrahlung oder Lasergravur von oben nach unten in den zu beschriftenden oder zu markierenden Bereichen ablatiert werden, so dass jeweils darunter angeordnete Farbschichten freigelegt werden. 2 A labeled plastic film laminate with a carrier layer ( 1 ), and four color layers ( 2 ) 2 ' ) 2 '' ) 2 ''' ), intermediate buffer layers ( 3 ), an adhesive layer ( 6 ), as well as be written areas ( 7 . 8th . 9 The first aspect of the invention relates to a method for producing colored labels or markings on label material, which has at least one carrier layer and at least two color layers of different colors, wherein the color layers by laser irradiation or laser engraving from top to bottom in the areas to be labeled or to be marked ablated, so that each underlying color layers are exposed.

Das erfindungsgemäße Verfahren wird anhand 1 schematisch erläutert. Erfindungsgemäß erfolgt die mindestens zweifarbige Beschriftung des Etikettenmaterials dadurch, dass zumindest die oberste Farbschicht (2) durch Laserablation unter Bildung eines beschrifteten Bereichs (5) abgetragen wird und hierdurch die darunter angeordnete Farbschicht (2') einen neuen Farbeindruck erzeugt. Der Schritt der Laserablation kann je nach gewünschter Färbung in die Tiefe fortgesetzt werden. Durch Entfernung der Farbschichten (2) und (2') wird ein beschrifteter Bereich (4) gebildet, der die Trägerschicht (1) frei legt. Die Farbschichten, sowie die Trägerschicht unterscheiden sich farblich voneinander. Obwohl die Trägerschicht lediglich so ausgebildet ist dass Sie dem Etikettenmaterial mechanische Stabilität gibt, ist es zweckmäßig die Trägerschicht ebenfalls farbig auszugestalten.The inventive method is based on 1 schematically explained. According to the invention, the at least two-colored inscription of the label material takes place in that at least the uppermost color layer ( 2 ) by laser ablation to form a labeled area ( 5 ) and thereby the underlying color layer ( 2 ' ) creates a new color impression. The laser ablation step can be continued to depth depending on the desired coloration. By removing the color layers ( 2 ) and ( 2 ' ) becomes a labeled area ( 4 ), which forms the carrier layer ( 1 ) releases. The color layers, as well as the carrier layer differ in color from each other. Although the carrier layer is only designed so that it gives the label material mechanical stability, it is expedient to design the carrier layer also colored.

Sollen mehrere Farbschichten (2, 2') durch Laserablation (Lasergravur) abgetragen werden, so werden diese in einer ersten Ausgestaltung der Erfindung sequentiell ablatiert.Should several layers of paint ( 2 . 2 ' ) are ablated by laser ablation (laser engraving), they are ablated sequentially in a first embodiment of the invention.

Hierzu wird der Laserstrahl mehrfach über das Etikettenmaterial bewegt und pro Laserdurchgang nur die jeweils unter der oben liegenden Farbschicht angeordnete Farbschicht freigelegt.For this the laser beam is repeated over the Label material moves and per laser passage only the respectively exposed under the overhead color layer arranged color layer.

In einer weiteren Ausgestaltung erfolgt ein paralleler Abtrag von mehrere Farbschichten (2, 2') auf einmal. Pro Laserdurchgang werden die oben liegende und mindestens die unmittelbar darunter liegende Farbschicht ablatiert. Dies kann in einfacher weise durch die Schreibgeschwindigkeit des Laserstrahls oder Variation der Strahlleistung erreicht werden.In a further embodiment, a parallel removal of several color layers ( 2 . 2 ' ) at once. For each laser pass, the overlying and at least the immediately underlying color layer are ablated. This can be achieved in a simple manner by the writing speed of the laser beam or variation of the beam power.

Beide Verfahren können auch in zweckmäßiger Weise kombiniert werden.Both Procedures can also in an appropriate manner be combined.

Durch das vorgestellte Verfahren lassen sich in sehr einfacher und direkter Weise mehrfarbige Farbetiketten erzeugen. Durch das Laserablationsverfahren, bzw. Lasergravur ist eine sehr hohe Individualisierung der einzelnen Etiketten möglich.By The presented method can be very simple and direct Create multi-colored color labels. Through the laser ablation process, or laser engraving is a very high individualization of the individual Labels possible.

In einer weiteren Ausgestaltung der Erfindung werden als Etikettenmaterial Folienlaminate verwendet die zwischen den Farbschichten Pufferschichten (3) aufweisen (vergl. 2). Je nach beabsichtigter Verfahrensweise können die Pufferschichten aus transparentem oder opakem Material bestehen.In a further embodiment of the invention, film laminates are used as the label material, and the buffer layers between the color layers (FIG. 3 ) have (see. 2 ). Depending on the intended procedure, the buffer layers may consist of transparent or opaque material.

In einer ersten Variante, gemäß beschriftetem Bereich (7), wird beim Abtrag der Farbschichten (2, 2') die darunter liegende Pufferschicht (3) nicht abgetragen. Hierbei ist die Pufferschicht (3) transparent ausgestaltet, so dass die hierunter angeordnete Farbschicht (2'') farbgebend wird.In a first variant, according to the labeled area ( 7 ), when removing the color layers ( 2 . 2 ' ) the underlying buffer layer ( 3 ) not removed. Here, the buffer layer ( 3 ) so that the color layer ( 2 '' ) becomes coloring.

Diese Verfahrensvariante hat den Vorteil, dass die zuoberst liegende Farbschicht durch eine Schutzschicht abgedeckt bleibt.These Process variant has the advantage that the uppermost color layer covered by a protective layer remains.

In einer zweiten Variante, gemäß beschriftetem Bereich (8), wird beim Abtrag der Farbschichten (2, 2') die darunter liegende Pufferschicht (3) mit abgetragen. Hierbei kann die Pufferschicht (3) sowohl transparent als auch opak ausgestaltet sein.In a second variant, according to labeled area ( 8th ), when removing the color layers ( 2 . 2 ' ) the underlying buffer layer ( 3 ) with removed. In this case, the buffer layer ( 3 ) be both transparent and opaque designed.

In einer dritten Variante, gemäß beschriftetem Bereich (9), wird beim Abtrag der Farbschichten (2, 2') die darunter liegende Pufferschicht (3) nur teilweise mit abgetragen. Hierbei ist die Pufferschicht (3) wiederum transparent ausgestaltet, so dass die hierunter angeordnete Farbschicht (2'') farbgebend wird. Diese Verfahrensvariante ist besonders bevorzugt. Die Pufferschicht kann hierbei verfahrenbedingte und nicht erwünschte Schwankungen der Ablationstiefe aufnehmen beziehungsweise ausgleichen. Wird die Ablationstiefe in etwa auf die Mitte der Pufferschicht eingestellt, so ist auch bei prozessbedingten Schwankungen der Tiefe noch sicher gestellt, dass die obere Farbschicht vollständig abgetragen und die untere noch nicht geschädigt bzw. abgetragen wird. Eine unsaubere Entfernung der oberen Farbschicht, sowie ein teilweises Abtragen der darunter liegenden Farbschicht könnte zu einer merklichen Verfälschung des Farbeindrucks führen.In a third variant, according to the labeled area ( 9 ), when removing the color layers ( 2 . 2 ' ) the underlying buffer layer ( 3 ) only partially with removed. Here, the buffer layer ( 3 ) in turn made transparent, so that the below arranged color layer ( 2 '' ) becomes coloring. This process variant is particularly preferred. The buffer layer can absorb or compensate for process-related and undesired fluctuations in the ablation depth. If the ablation depth is set approximately to the middle of the buffer layer, it is ensured even in the case of process-related fluctuations of the depth that the upper color layer is completely removed and the lower one is not yet damaged or removed. An unclean removal of the upper color layer, as well as a partial removal of the underlying color layer could lead to a noticeable falsification of the color impression.

Als Laserlicht wird bevorzugt sichtbares oder ultraviolettes Licht gewählt, wobei als Laserlichtquelle bevorzugt ein CO2-Laser oder ein Excimer Laser gewählt wird. Im Prinzip sind aber auch andere Laserlichtquellen geeignet, sofern Sie gut regelbar sind und hohe Leistungsdichten ermöglichen. Für eine effiziente Ablation des Schicht-Materials ist dabei kurzwelliges Licht ist dabei zu bevorzugen.Visible or ultraviolet light is preferably selected as the laser light, wherein a CO 2 laser or an excimer laser is preferably selected as the laser light source. In principle, however, other laser light sources are also suitable, as long as they are easy to control and allow high power densities. For an efficient ablation of the layer material, short-wave light is to be preferred.

Ein weiterer Aspekt der Erfindung betrifft Kunststofffolienlaminat, wie es für die Anwendung des erfindungsgemäßen Verfahrens besonders geeignet ist. Erfindungsgemäß ist ein Kunststofffolienlaminat mit mindestens zwei übereinander angeordneten Farbschichten (2, 2') und einer Trägerschicht (1) vorgesehen, wobei das Material der Farbschichten aus Trägerpolymer, Farbpigmenten und Hilfsstoffen aufgebaut ist und durch Laserbestrahlung rückstandsfrei entfernbar ist.Another aspect of the invention relates to plastic film laminate, as it is particularly suitable for the application of the method according to the invention. According to the invention, a plastic film laminate having at least two color layers ( 2 . 2 ' ) and a carrier layer ( 1 ), wherein the material of the color layers composed of carrier polymer, color pigments and auxiliaries and can be removed without residue by laser irradiation.

Dabei ist es von besonderer Bedeutung, dass die Farbschichten durch eine Lasergravur oder eine Laserablation rückstandsfrei entfernbar sind und nicht wie bei gängigen Farbfolien üblich durch Lasereinwirkung geschwärzt werden. Im Kunststofflaminat mit der erfindungsgemäßen Anordnung der Farbschichten erfolgen somit bei der Laserbestrahlung eine Zersetzung und eine Verdampfung von Trägerpolymer, Hilfsstoffen und Farbpigment ohne Bildung nichtflüchtiger Zersetzungsprodukte, welche in dem zu markierenden Bereich verbleiben.there it is of particular importance that the color layers by a Laser engraving or laser ablation are removed without residue and not as usual Color foils usual blackened by laser action become. In the plastic laminate with the inventive arrangement The color layers are thus decomposed during laser irradiation and evaporation of carrier polymer, Excipients and color pigment without education non-volatile Decomposition products which remain in the area to be marked.

Die Dicke der einzelnen Farbschichten richtet sich unter anderem nach Pigmentgehalt und/oder Laserverfahren, bzw. Laserlichtquelle. Sie kann für die verschiedenen Farbschichten je nach Bedarf auch unterschiedlich gewählt werden.The Thickness of the individual layers of paint depends, among other things Pigment content and / or laser process, or laser light source. she can for the different color layers as needed also different chosen become.

Bevorzugt wird eine Dicke im Bereich von 10 bis 100 μm gewählt. Gegebenenfalls können auch dünnere Schichten im Bereich von 1 bis 10 μm zweckmäßig sein.Prefers a thickness in the range of 10 to 100 microns is selected. Optionally, even thinner layers can be useful in the range of 1 to 10 microns.

Bei der Zusammensetzung der Farbschichten kann hinsichtlich der Pigmente und der Hilfsstoffe im Wesentlichen auf die für Farbfolien üblichen Materialien zurückgegriffen werden. Dabei sind unter Hilfsstoffen insbesondere Weichmacher, oder Stabilisatoren zu verstehen. Darüber hinaus können bei den Hilfsstoffen ebenfalls Materialien enthalten sein, welche die Laserablation unterstützen.at the composition of the color layers may be in terms of pigments and the auxiliaries substantially to those customary for color films Materials used become. In particular, auxiliary substances include plasticizers, or stabilizers. In addition, at the Auxiliary materials may also be included, which includes laser ablation support.

Der überwiegende Bestandteil der Farbfolie wird durch das Trägerpolymer gebildet. Daher ist hier ein Polymer zu verwenden, das sich möglichst einfach rückstandsfrei zersetzen bzw. durch Laserablation abtragen lässt. Polymere ohne aromatische Gruppen sind in allgemeinen schlechte Absorber für Licht und daher nur schwierig durch Laserablation/gravur abzutragen. Polymere mit aromatischen Gruppen und Polymere mit chromophoren Gruppen sind für die Farbschicht zu bevorzugen. Bevorzugt ist das Trägerpolymer der Farbschichten überwiegend aus Polyaromaten aufgebaut und/oder enthält lasersensitive Pigmente, beziehungsweise Chromophore. Besonders geeignete Polyaromaten sind Polyimide und/oder Polyamide, bevorzugt als Polymerblends mit weiteren Kunststoffen. Unter den chromophoren Gruppen sind Triazine (-N=N-N<) besonders geeignet. Es ist zweckmäßig, als eine Komponente der Hilfsstoffe lasersensitive Pigmente, insbesondere mit chromophoren Gruppen aus Triazinen zu verwenden.The predominant Component of the color film is formed by the carrier polymer. Therefore Here is a polymer to use, the most easily residue-free decompose or ablate by laser ablation. Polymers without aromatic groups are generally poor absorbers of light and therefore difficult ablate by laser ablation / engraving. Polymers with aromatic groups and polymers with chromophoric groups are preferable for the color layer. The carrier polymer is preferred the color layers predominantly Built up polyaromatics and / or contains laser-sensitive pigments, or chromophores. Particularly suitable polyaromatics are Polyimides and / or polyamides, preferably as polymer blends with further Plastics. Among the chromophoric groups, triazines (-N = N-N <) are particularly suitable. It is appropriate as a component of the excipients laser-sensitive pigments, in particular to use with chromophoric groups of triazines.

In einer weiteren erfindungsgemäßen Ausgestaltung des Kunststofffolienlaminats, gemäß 2, sind zwischen den Farbschichten weitere Schichten als Pufferschichten vorgesehen, wobei zumindest zwei der Farbschichten (2, 2') durch eine transparente Pufferschicht (3) getrennt werden. Pufferschichten können dabei zusätzlich auch als Deckschicht, d. h. über der obersten Farbschicht (2) oder unterhalb der untersten Farbschicht (2''') angeordnet sein. Die Pufferschichten haben dabei zum einen die Wirkung als Schutzschicht für die Oberfläche der Farbschichten. Zum anderen dienen sie aber auch als Ausgleich für eine schwankende Eindringtiefe des Lasers bei der Lasergravur. Die Dicke der Pufferschichten liegt im gleichen Bereich wie die Dicke der Farbschichten, insbesondere im Bereich von 10 bis 100 μm. Die Dicke der einzelnen Pufferschichten kann dabei unterschiedlich sein.In a further inventive embodiment of the plastic film laminate, according to 2 , further layers are provided as buffer layers between the color layers, with at least two of the color layers ( 2 . 2 ' ) through a transparent buffer layer ( 3 ) are separated. In addition, buffer layers can also be used as cover layer, ie above the uppermost ink layer ( 2 ) or below the lowest color layer ( 2 ''' ) can be arranged. On the one hand, the buffer layers have the effect of protecting the surface of the color layers. On the other hand, they also serve as compensation for a fluctuating penetration depth of the laser during laser engraving. The thickness of the buffer layers is in the same range as the thickness of the color layers, in particular in the range of 10 to 100 microns. The thickness of the individual buffer layers can be different.

In bevorzugter Ausgestaltung weisen die Pufferschichten mindestens die 2-fache Dicke der jeweils darüber liegenden Farbschicht auf.In preferred embodiment, the buffer layers at least 2 times the thickness of the overlying color layer.

Die Pufferschichten sind dabei ebenso wie die Farbschichten aus einem Material aufgebaut, dass sich durch die Laserablation/gravur rückstandsfrei zersetzen bzw. entfernen lässt. Bevorzugt sind die Pufferschichten aus einem der Trägerpolymere, gegebenenfalls mit Hilfsstoffen, der Farbschichten aufgebaut.The Buffer layers are just like the color layers of one Material constructed so that the laser ablation / engraving leaves no residue decompose or remove. Preferably, the buffer layers of one of the carrier polymers, optionally with auxiliaries, built up of color layers.

Je nach Verfahrensvariante können die Pufferschichten unterschiedliche optische Eigenschaften aufweisen. Die Pufferschichten können insbesondere transparent, opak oder vollständig Licht-undurchlässig sein. Die Opazität kann durch übliche Zusatzstoffe eingestellt werden. Eine transparente Pufferschicht kann ebenso als Schutzschicht auf der Oberfläche des Kunststofffolienlaminats angeordnet sein.ever according to process variant can the buffer layers have different optical properties. The buffer layers can especially transparent, opaque or completely opaque to light. The opacity can by usual Additives can be adjusted. A transparent buffer layer can also act as a protective layer on the surface of the plastic film laminate be arranged.

Für die Trägerschicht können die bei der Herstellung von Etikettenmaterial üblichen Werkstoffe verwendet werden. Es ist dabei zweckmäßig die Trägerschicht (1) selbst mit Farbpigment auszustatten. Die Dicke und weitere Ausgestaltung der Trägerschicht (1) richtet sich im Wesentlichen nach dem beabsichtigten Einsatzgebiet des Etikettenmaterials.For the carrier layer, the usual materials used in the production of label material can be used. It is expedient the carrier layer ( 1 ) equip itself with color pigment. The thickness and further configuration of the carrier layer ( 1 ) depends essentially on the intended field of application of the label material.

Unter der Trägerschicht kann Klebemittel (6), beispielsweise in der Form von Klebe- und Abdeckfolie angeordnet sein.Under the backing layer, adhesive ( 6 ), for example be arranged in the form of adhesive and cover film.

Claims (20)

Verfahren zur Herstellung von farbigen Beschriftungen oder Markierungen auf Etikettenmaterial, welches zumindest eine Trägerschicht (1) und mindestens zwei Farbschichten (2, 2') unterschiedlicher Färbung aufweist dadurch gekennzeichnet, dass die Farbschichten (2, 2') durch Laserbestrahlung oder Lasergravur von oben nach unten in den zu beschriftenden oder zu markierenden Bereichen (4, 5) ablatiert werden, so dass jeweils darunter angeordnete Farbschichten (2', 2'') oder die Trägerschicht (1) freigelegt werden, wobei sich das Ablatieren zumindest auf die oberste Farbschicht (2) erstreckt.Method for producing colored inscriptions or markings on label material, which comprises at least one carrier layer ( 1 ) and at least two color layers ( 2 . 2 ' ) of different colors, characterized in that the color layers ( 2 . 2 ' ) by laser irradiation or laser engraving from top to bottom in the zu labeling or marking areas ( 4 . 5 ) are ablated, so that each underlying color layers ( 2 ' . 2 '' ) or the carrier layer ( 1 ) are exposed, wherein the Ablatieren at least on the uppermost color layer ( 2 ). Verfahren nach Anspruch 1 dadurch gekennzeichnet, dass mehrere Farbschichten (2, 2') sequentiell ablatiert werden, so dass pro Laserdurchgang die jeweils unter der oben liegenden Farbschicht angeordnete Farbschicht freigelegt wird.A method according to claim 1, characterized in that several color layers ( 2 . 2 ' ) are ablated sequentially, so that the color layer arranged below the upper layer of paint is exposed per laser pass. Verfahren nach Anspruch 1 dadurch gekennzeichnet, dass mehrere Farbschichten (2, 2') parallel ablatiert werden, so dass pro Laserdurchgang die oben liegende und mindestens die unmittelbar darunter liegende Farbschicht ablatiert werden.A method according to claim 1, characterized in that several color layers ( 2 . 2 ' ) are ablated in parallel, so that the aboveground and at least the directly underlying color layer are ablated per laser pass. Verfahren nach einem der vorangegangenen Ansprüche, dadurch gekennzeichnet, dass Bereiche (4) gebildet werden in denen mindestens zwei Farbschichten (2, 2') abgetragen wurden.Method according to one of the preceding claims, characterized in that regions ( 4 ) are formed in which at least two color layers ( 2 . 2 ' ) were removed. Verfahren nach einem der vorangegangenen Ansprüche, dadurch gekennzeichnet, dass Bereiche gebildet werden in denen alle Farbschichten (2, 2', 2'', 2''') bis auf die Trägerschicht (1) ablatiert werden.Method according to one of the preceding claims, characterized in that areas are formed in which all color layers ( 2 . 2 ' . 2 '' . 2 ''' ) except for the carrier layer ( 1 ) are ablated. Verfahren nach einem der vorangegangenen Ansprüche dadurch gekennzeichnet, dass die Trägerschicht (1) durch eine Farbschicht gebildet wird.Method according to one of the preceding claims, characterized in that the carrier layer ( 1 ) is formed by a color layer. Verfahren nach einem der vorangegangenen Ansprüche dadurch gekennzeichnet, dass zwischen den Farbschichten Pufferschichten (3) aus transparentem Material angeordnet sind, wobei die Pufferschicht (3) beim Ablatieren der jeweils unmittelbar darunter liegenden Farbschicht vollständig abgetragen wird.Method according to one of the preceding claims, characterized in that between the color layers buffer layers ( 3 ) are arranged from transparent material, wherein the buffer layer ( 3 ) is completely ablated when ablating the immediately underlying color layer. Verfahren nach einem der vorangegangenen Ansprüche dadurch gekennzeichnet, dass zwischen den Farbschichten Pufferschichten (3) aus transparentem Material angeordnet sind, wobei beim Abtragen einer Farbschicht die jeweils darunter liegende Pufferschicht zumindest teilweise mit abgetragen wird.Method according to one of the preceding claims, characterized in that between the color layers buffer layers ( 3 ) are arranged made of transparent material, wherein the removal of a color layer, the respectively underlying buffer layer is at least partially removed with. Verfahren nach einem der vorangegangenen Ansprüche, dadurch gekennzeichnet, dass als Laserlicht sichtbares oder ultraviolettes Licht gewählt wird.Method according to one of the preceding claims, characterized characterized in that as laser light visible or ultraviolet Light selected becomes. Verfahren nach einem der vorangegangenen Ansprüche, dadurch gekennzeichnet, dass als Laserquelle ein CO2-Laser oder ein Excimer Laser gewählt wird.Method according to one of the preceding claims, characterized in that a CO 2 laser or an excimer laser is selected as the laser source. Kunststofffolienlaminat mit mindestens zwei übereinander angeordneten Farbschichten (2, 2') und einer Trägerschicht (1), geeignet für die Herstellung von farbigen Beschriftungen oder Markierungen gemäß einem Verfahren der vorangegangenen Ansprüche, dadurch gekennzeichnet, dass die Farbschichten aus Trägerpolymer, Farbpigmenten und Hilfsstoffen aufgebaut sind, welche durch Laserbestrahlung rückstandsfrei entfernbar ist.Plastic film laminate with at least two color layers ( 2 . 2 ' ) and a carrier layer ( 1 ), suitable for the production of colored lettering or markings according to a method of the preceding claims, characterized in that the color layers of carrier polymer, color pigments and excipients are constructed, which is removed without residue by laser irradiation. Kunststofffolienlaminat nach Anspruch 11, dadurch gekennzeichnet, dass die Farbschichten eine Dicke im Bereich von 10 bis 100 μm aufweisen.Plastic film laminate according to claim 11, characterized characterized in that the color layers have a thickness in the range of 10 to 100 μm exhibit. Kunststofffolienlaminat nach Anspruch 11, dadurch gekennzeichnet, dass das Trägerpolymer der Farbschichten überwiegend aus Polyaromaten aufgebaut ist und/oder lasersensitive Pigmente oder Chromophore enthält.Plastic film laminate according to claim 11, characterized in that the carrier polymer is the Coatings predominantly is constructed of polyaromatics and / or laser-sensitive pigments or chromophores. Kunststofffolienlaminat nach Anspruch 13, dadurch gekennzeichnet, dass die Polyaromaten durch Polyamide und/oder Polyamide gebildet sind.Plastic film laminate according to claim 13, characterized characterized in that the polyaromatics by polyamides and / or polyamides are formed. Kunststofffolienlaminat nach einem der Ansprüche 11 bis 14, dadurch gekennzeichnet, dass die Trägerpolymere und/oder lasersensitiven Pigmente chromophore Gruppen aus Triazinen enthalten.Plastic film laminate according to one of claims 11 to 14, characterized in that the carrier polymers and / or laser-sensitive Pigments contain chromophoric groups from triazines. Kunststofffolienlaminat nach einem der Ansprüche 11 bis 15, dadurch gekennzeichnet, dass zumindest zwei der Farbschichten (2, 2') durch eine transparente Pufferschicht (3) getrennt werden.Plastic film laminate according to one of claims 11 to 15, characterized in that at least two of the color layers ( 2 . 2 ' ) through a transparent buffer layer ( 3 ) are separated. Kunststofffolienlaminat nach Anspruch 16, dadurch gekennzeichnet, dass die Pufferschichten (3) eine Dicke im Bereich von 10 bis 100 μm aufweisen.Plastic film laminate according to claim 16, characterized in that the buffer layers ( 3 ) have a thickness in the range of 10 to 100 microns. Kunststofffolienlaminat nach Anspruch 16 oder 17, dadurch gekennzeichnet, dass die Pufferschichten mindestens die 2-fache Dicke der jeweils darüber liegenden Farbschicht aufweisen.Plastic film laminate according to claim 16 or 17, characterized in that the buffer layers at least the 2 times the thickness of each above having lying color layer. Kunststofffolienlaminat nach einem der Ansprüche 16 bis 18, dadurch gekennzeichnet, dass die Pufferschichten aus dem Trägerpolymer einer der Farbschichten aufgebaut ist.Plastic film laminate according to one of claims 16 to 18, characterized in that the buffer layers of the carrier polymer one of the color layers is constructed. Kunststofffolienlaminat nach einem der Ansprüche 16 bis 19, dadurch gekennzeichnet, dass als Deckschicht eine Pufferschicht als Schutzschicht angeordnet ist und/oder unter der Trägerschicht Klebemittel (6) angeordnet sind.Plastic film laminate according to one of claims 16 to 19, characterized in that a buffer layer is arranged as a protective layer as a protective layer and / or adhesive under the support layer ( 6 ) are arranged.
DE200510048870 2005-10-12 2005-10-12 Production of multicolored inscriptions or marks on label material e.g. for sign or label involves laser ablation downwards from top of material having substrate and 2 or more layers of different color, preferably plastics film laminate Withdrawn DE102005048870A1 (en)