DE102004023361A1

DE102004023361A1 - High strength yarn material, for use in protective gloves, is a core yarn with a metal core cladded with aramide fibers and an outer cladding of fibers for comfort against the skin

Info

Publication number: DE102004023361A1
Application number: DE200410023361
Authority: DE
Inventors: Hannes Junger
Original assignee: W & R GmbH; W+R GmbH
Current assignee: W & R GmbH; W+R GmbH
Priority date: 2004-05-12
Filing date: 2004-05-12
Publication date: 2005-12-08

Abstract

The high resistance yarn, for use in protective gloves, is a core yarn of metal twisted or cladded with para-aramide and/or aramide fibers. The core is wholly shrouded by the aramide fibers. The aramide fibers are spun in a stretch broken process. The core yarns have an outer shrouding of cotton fibers and the like, for a comfortable handle against the skin. The glove fabric is an interlock knit, a woven, knitted or nonwoven material.

Description

Die Erfindung betrifft ein Garn oder Gespinst, eine daraus hergestellte Strickware oder ein Gewebe, ein Gewirk oder ein Vlies, das mit dem Garn oder Gespinst hergestellt wurde. Darüber hinaus wird aus dem erfindungsgemäßen Material ein Handschuh oder Teile davon hergestellt, die besonders strapazierfähig sind.The The invention relates to a yarn or web, a product made therefrom Knitwear or a fabric, a knitted fabric or a nonwoven which is combined with the Yarn or web was made. In addition, from the material of the invention a glove or parts made of it, which are particularly hard-wearing.

Für besondere Einsatzzwecke, wie die Herstellung von Sicherheitshandschuhen für die Feuerwehr, die Polizei oder sonstige Personengruppen werden einerseits Garne benötigt, die besonders widerstandsfähig sind und sich zu einem Textil verarbeiten lassen, mit dem Körperteile eines Menschen unter schwierigen Einsatzbereichen dauerhaft geschützt werden können. Andererseits soll das Material oder Textil bevorzugt für die Handschuhherstellung geeignet sein, um bei Arbeiten unter extremen Bedingungen die Hände einer Person dauerhaft schützen zu können.For special Purposes, such as the production of safety gloves for the fire brigade, on the one hand, the police or other groups of people become yarns needed the most resistant are and can be processed into a textile, with the body parts of a person under difficult operational conditions permanently be protected can. On the other hand, the material or textile is preferably suitable for glove production be to work hands in extreme conditions Protect person permanently can.

Beispielsweise ist aus der EP 1 234 515 A2 bekannt, Schutzhandschuhe im Bereich der Innenhand mit temperaturbeständigen und schnittfesten Fasern zu versehen, sowie in diesen Bereichen hautfreundliche Fasern anzureichern.For example, is from the EP 1 234 515 A2 Known to provide protective gloves in the palm area with temperature-resistant and cut-resistant fibers, and to enrich skin-friendly fibers in these areas.

Aufgabe der Erfindung ist es, ein Garn oder Gespinst zu entwickeln, das einerseits in einem hohem Maße schnittfest und strapazierfähig ist, und sich andererseits zu Materialien weiterverarbeiten lässt, die einen angenehmen Tragekomfort auf der Haut oder am Körper eines Menschen ermöglichen.task The invention is to develop a yarn or web that on the one hand to a high degree cut resistant and durable on the other hand can be further processed into materials that a pleasant wearing comfort on the skin or on the body of a Enable people.

Gelöst wird diese Aufgabe erfindungsgemäß durch ein Garn oder Gespinst bestehend aus einem Core-Garn aus Metall, das mit oder von einer Para-Aramidfaser und/oder einer Aramidfaser verzwirnt oder umsponnen ist, die das Core-Garn offen oder in Abstufungen bis zu einer völlig abgedeckten Seele ummantelt.Is solved this task according to the invention by a yarn or web consisting of a core yarn of metal, that with or from a para-aramid fiber and / or an aramid fiber twisted or braided, the core yarn open or in increments up to a complete one Covered soul encased.

Weiterhin wird die Erfindung durch die Herstellung einer Interlock-Strickware, eines Gewebes, eines Gewirks oder eines Vlieses gelöst, die zur Herstellung des Textils das erfindungsgemäße Garn oder Gespinst verwendet. Ebenfalls wird die Erfindung durch die Herstellung eines Schutzhandschuhs bzw. Teile davon gelöst, indem aus dem erfindungsgemäßen Material diese Handschuhe oder Teile davon hergestellt werden.Farther the invention by the production of an interlock knit, a Fabric, a knitted fabric or a nonwoven fabric used to make the fabric Textile the yarn of the invention or Woven spun. Also, the invention by the production a protective glove or parts thereof dissolved by the material of the invention these gloves or parts thereof are manufactured.

Das erfindungsgemäße Garn oder Gespinst hat den wesentlichen Vorteil, dass es gegenüber bekannten Materialien eine noch größere Festigkeit aufweist und dies bei Garnfeinheiten von ca. NM 45 – 50. Die Para-Aramidfaser und/oder die Aramidfaser armieren mehr oder weniger stark eine Metallseele, die ohnehin schon sehr schnitt- und stichfest ist. Die Para-Aramidfaser und/oder die Aramidfaser sind zäh und reißfest und lassen sich in dieser Qualität als hochfeine Fasern herstellen. Über die Verzwirnung mit dem Core-Garn lässt sich ein Garn oder Gespinst herstellen, das weitaus widerstandsfähiger gegenüber äußeren Einflüssen ist, als z. B. bekannte Garne mit einer Glasseele oder DREF-Garne. Je nach Anteil der unterschiedlichen Fasern lässt sich das erfindungsgemäße Garn elastischer herstellen und es ist auch möglich, das Core-Garn unterschiedlich stark mit den Fasern zu überdecken. Insgesamt wird ein Garn oder Gespinst geschaffen, das Witterungsverhältnissen jedweder Art dauerhaft ausgesetzt werden kann, temperaturbeständig ist und sich als besonders beschädigungsresistent auszeichnet.The yarn according to the invention or Gespinst has the substantial advantage that it opposite known Materials has an even greater strength and this at yarn counts of about NM 45 - 50. The para-aramid fiber and / or the aramid fiber more or less strongly reinforce a metal core which already very cut and puncture proof anyway. The para-aramid fiber and / or the aramid fiber are tough and tearproof and let in this quality as a high-fine fibers produce. About the twist with the Leaves core yarn create a yarn or web that is far more resistant to external influences, as z. B. known yarns with a glass fiber or DREF yarns. Depending on the proportion of different fibers the yarn of the invention It is also possible to make the core yarn different to cover strongly with the fibers. Overall, a yarn or web is created, the weather conditions of any kind can be permanently exposed, is temperature resistant and especially damage resistant distinguished.

Wird aus dem erfindungsgemäßen Garn ein Textil oder Teile davon gefertigt, so lassen sich Kleidungsstücke daraus herstellen, die besonders strapazierfähig sind und dennoch einen angenehmen Tragekomfort ermöglichen. Darüber hinaus lässt sich das erfindungsgemäße Textil oder Teile davon mit bekannten Textilien kombinieren, die diese vor lokalen Beschädigungen schützen. Besonders geeignet ist das erfindungsgemäße Garn oder Gespinst für die Herstellung von Schutzhandschuhen, weil es besonders widerstandsfähig ist und gleichzeitig eine hohe Beweglichkeit der einzelnen Finger in einem solchen Handschuh zulässt.Becomes from the yarn of the invention a textile or parts made of it, so garments can be made out of it which are particularly hard-wearing and yet one allow comfortable wearing. About that lets out the textile of the invention or parts of it with familiar textiles that combine these against local damage protect. Particularly suitable is the yarn or web of the invention for the production of protective gloves, because it is particularly resistant and at the same time a high mobility of the individual fingers in allows such a glove.

In weiterer vorteilhafter Ausgestaltung der Erfindung ist die Para-Aramidfaser und/oder die Aramidfaser im „stretch broken"-Spinnverfahren ersponnen. Dies hat den Vorteil, dass mit derartigen Fasern hochfeine erfindungsgemäße Garne oder Gespinste hergestellt werden können und die Intensität der Umwindung, d. h. der Grad einer Abdeckung des Core-Garnes, sich einfachst einstellen lässt. Die im „stretch broken"-Verfahren hergestellten und/oder verarbeiteten Fasern ermöglichen als Garn einen besseren Faserverbund, wodurch die Reiß- und Schnittfestigkeit erhöht wird. Längere Dehnungen, Belastungen dieser Garne sind möglich und eine gute Abdeckung der Metallseele ist gewährleistet.In Another advantageous embodiment of the invention is the para-aramid fiber and / or the aramid fiber in the "stretch broken "-Spinnverfahren spun. This has the advantage that with such fibers extremely fine Yarns according to the invention or webs can be made and the intensity of the wrap, d. H. the degree of coverage of the core yarn, adjust easily leaves. The in the "stretch broken "process produced and / or processed fibers allow a better than yarn Fiber composite, reducing the tear and cut resistance elevated becomes. longer Strains, loads of these yarns are possible and good coverage the metal core is guaranteed.

In einer bevorzugten Ausgestaltung der Erfindung ist das Core-Garn als Edelstahlseele ausgebildet. Dies hat den Vorteil, dass auch unter erhöhten Feuchtigkeitseinflüssen das erfindungsgemäße Garn oder Gespinst nicht korrodieren kann.In A preferred embodiment of the invention is the core yarn designed as a stainless steel soul. This has the advantage of that too under increased humidity influences the yarn according to the invention or Spun can not corrode.

Mit dem erfindungsgemäßen Garn oder Gespinst lassen sich Gewebe, Gewirke oder Vliese herstellen, die sich ohne erhöhten Aufwand zu Kleidungsstücken oder Teilen davon weiterverarbeiten lassen oder es lässt sich eine Interlock-Strickware auf einer speziellen Rundstrickmaschine herstellen und dies ohne die übliche Zugabe von Garn-Avivagen.With the yarn or web of the invention can be fabric, knitted or non-wovens produce that further processed without increased effort to garments or parts thereof or you can make an interlock knitwear on a special circular knitting machine without the usual addition of yarn avivage.

In weiterer Ausgestaltung der Erfindung wird das Garn oder das Gespinst als Doubleface-Strickware eingesetzt. Das Garn oder das Gespinst weist zusätzlich eine hautfreundliche PETP-Faser auf, die in einer weiteren Ausgestaltung der Erfindung noch mit einem Baumwollfaden ummantelt sein kann, der Silberanteile aufweist.In Another embodiment of the invention is the yarn or the web used as a double-face knitwear. The yarn or the web indicates additionally a skin-friendly PETP fiber, which in a further embodiment the invention can still be covered with a cotton thread, the silver shares.

Dies hat den Vorteil, dass mit einem sehr feingliedrigen Polyesterfaden aus PETP eine an die Faser angrenzende Feuchtigkeit sehr gut abgeleitet werden kann. Mit den Silberanteilen im Baumwollfaden ist eine antibakterielle Wirkung des erfindungsgemäßen Textils gewährleistet. Bevorzugt sind die Baumwollfäden mit Silberanteilen so um das Garn oder das Gespinst angeordnet, dass die Silberanteile in direktem Hautkontakt mit einem menschlichen Körper stehen können.This has the advantage that with a very delicate polyester thread From PETP a moisture adjacent to the fiber can be very well dissipated can. With the silver parts in the cotton thread is an antibacterial Effect of the textile according to the invention guaranteed. The cotton threads are preferred arranged with silver parts around the yarn or the web, that the silver portions are in direct skin contact with a human body can.

Besonders vorteilhaft ist es, wenn Materialien aus dem erfindungsgemäßen Garn oder Gespinst zu Handschuhen, insbesondere Schutzhandschuhen, weiterverarbeitet werden. Es ist wichtig, dass zumindest die Innenhandfläche des Handschuhs oder des Innenfutters des Handschuhs oder der gesamte Handschuh aus diesem Material hergestellt ist. Sind Sicherheitshandschuhe aus diesem Material oder Teile davon daraus gefertigt, so sind solche Handschuhe auch unter extremen Einsatzbedingungen besonders sicher und schützen die Hände von Personen vor Verletzungen.Especially It is advantageous if materials from the yarn according to the invention or webbing for gloves, in particular protective gloves, further processed become. It is important that at least the palm of the hand Glove or glove or the entire lining of the glove Glove made of this material. Are safety gloves made of this material or parts thereof, such are Gloves particularly safe under extreme conditions of use and protect the hands of Persons from injuries.

In weiterer Ausgestaltung der Erfindung kann der Handschuh als Innenhandschuh hergestellt sein, der in einen atmungsaktiven und bevorzugt Wasser abweisenden Außenhandschuh eingefügt ist. Über eine derartige Kombination lassen sich Vorteile verschiedenster Textilien miteinander kombinieren und so kann das erfindungsgemäße Garn oder Gespinst dauerhaft vor Wasser geschützt werden.In Further embodiment of the invention, the glove as an inner glove be prepared in a breathable and preferably water repellent outer glove is inserted. Over a Such combination can be advantages of various textiles combine together and so can the yarn of the invention or sponges are permanently protected from water.

Zusätzlich ist es möglich, die erfindungsgemäßen Handschuhe mit Protektoren im Knöchelbereich einer in den Handschuh eingesteckten Hand auszubilden. Dies erhöht noch zusätzlich die Sicherheit derartiger Handschuhe und schützt die einzelnen Finger vor Verletzungen.In addition is it is possible the gloves according to the invention with protectors in the ankle area form a hand inserted in the glove. This is still increasing additionally the safety of such gloves and protects the individual fingers Injury.

Es wird ein Garn oder Gespinst aus einem Core-Garn aus Metall vorgestellt, das mit oder von einer Para-Aramidfaser und/oder einer Aramidfaser verzwirnt oder umsponnen ist. Das Core-Garn kann unterschiedlich stark von den Para-Aramidfasern und/oder der Aramidfaser abgedeckt sein und in einer Ausführungsform ist das Garn oder Gespinst vollständig ohne Lücke von den Para-Aramidfasern und/oder Aramidfasern ummantelt. Aus dem Garn oder Gespinst lassen sich Kleidungsstücke, insbesondere Schutzhandschuhe, herstellen.It a yarn or web is presented from a metal core yarn, which is twisted with or from a para-aramid fiber and / or an aramid fiber or wound around. The core yarn can vary greatly from be covered by the para-aramid fibers and / or the aramid fiber and in one embodiment the yarn or web is completely without gap from the para-aramid fibers and / or Aramid fibers sheathed. From the yarn or webbing can be garments, in particular Protective gloves.

Claims

Yarn or web consisting of a core yarn (Soul thread) made of metal, with or by a para-aramid fiber and / or an aramid fiber is twisted or wound, the Core yarn open or in increments up to a fully covered Soul sheathed.

Yarn or web as claimed in claim 1, characterized in that that the para-aramid fiber and / or the aramid fiber in the "stretch broken "-Spinnverfahren spun.

Yarn or web according to claim 1 or 2, characterized characterized in that the core yarn is formed as a stainless steel core is.

Use of the yarn or webbing after one of claims 1 to 3, characterized in that the yarn or webbing for Production of an interlock knitted fabric, a fabric, a knitted fabric or a fleece is used.

Use of the yarn or webbing after one of claims 1 to 3, characterized in that the preparation without the addition a yarn-avivage takes place.

Use of the yarn or webbing after one of claims 1 to 3 as a double-face knitwear, with the yarn or webbing with a skin-friendly PETP fiber, preferably with four surface channels, and / or with a silver thread containing cotton thread, sheathed is.

Production of a glove using a Textile according to one of the claims 4 to 6, characterized in that at least the palm of the hand Glove or the inner lining of the glove or the entire Glove made of this material.

Production of a glove according to claim 7, characterized characterized in that the glove is made as an inner glove which is in a breathable and preferably water-repellent outer glove added is.

Production of a glove according to claim 7 or 8, characterized in that the glove protectors in the ankle area having a hand inserted into the glove.