CN206451164U - A kind of array code magnetic signal positions induction installation - Google Patents
A kind of array code magnetic signal positions induction installation Download PDFInfo
- Publication number
- CN206451164U CN206451164U CN201720129294.7U CN201720129294U CN206451164U CN 206451164 U CN206451164 U CN 206451164U CN 201720129294 U CN201720129294 U CN 201720129294U CN 206451164 U CN206451164 U CN 206451164U
- Authority
- CN
- China
- Prior art keywords
- array
- magnetic
- induction coil
- magnetic signal
- alloy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Induction installation is positioned the utility model discloses a kind of array code magnetic signal, includes the control circuit of inductive component and connection inductive component, inductive component includes：Level code array and the vertically disposed vertical code array of level code array, level code array are constituted with vertical code array by magnetic signal induction coil assembly；Wherein, level code array is made up of more than one horizontal magnetic signal induction coil assembly；Vertical code array is made up of more than one perpendicular magnetic induction of signal coil unit；Wherein, horizontal magnetic signal induction coil assembly is in series by least two horizontal induction coils by differential lines；Perpendicular magnetic induction of signal coil unit is in series by least two horizontal induction coils by differential lines.The problem of the utility model solves the magnetic-inductive device detection time length of prior art, reaction speed is slow, device is complicated.
Description
Technical field
The utility model is related to magnetic induction field, more particularly to a kind of array code magnetic signal positioning induction installation.
Background technology
With the progress and development of electronic product and all kinds of Digit Control Machine Tools, the position sensing inductor adjusted the distance with two-dimensional surface
Application and demand it is more and more extensive.
Patent No. CN201320756682.X Chinese utility model patent " the individual layer wiring system of electromagnetic antenna " is public
Cloth is a kind of to set some independent electromagnetic induction channels coils to constitute magnetic signal positioning inductor in two-dimensional surface both direction, can
Position time writer to realize handwriting input contactor control device, this each channel position of magnetic signal positioning inductor for Scanning Detction
The independent electromagnetic induction passage coil of setting one, the such magnetic signal positioning inductor of sector scanning detection to need what is grown very much
Time, reflection speed is slow, and such magnetic signal positioning inductor is sufficiently complex, is not suitable for large scale magnetic signal positioning inductor
Design is used.
Utility model content
The utility model is intended at least solve one of technical problem in correlation technique to a certain extent.Therefore, this reality
It is to provide a kind of array code magnetic signal positioning induction installation with new main purpose, it is intended to solve the magnetic strength of prior art
Answer device detection time length, the problem of reaction speed is slow, device is complicated.
To achieve the above object, the utility model is provided
A kind of array code magnetic signal positions induction installation, including inductive component and the control electricity for connecting the inductive component
Road, it is characterised in that the inductive component includes：It is level code array, vertically disposed vertical with the level code array
Encoding array, the level code array is constituted with the vertical code array by magnetic signal induction coil assembly；
Wherein, the level code array is made up of more than one magnetic signal induction coil assembly；The vertical code
Array is made up of more than one magnetic signal induction coil assembly；
Wherein, the magnetic signal induction coil assembly is in series by least two magnetic induction coils by differential lines；
Wherein, the magnetic induction coil is made up of the continuous circular shape wire of 1 circle to 10 circles.
The differential lines of series connection magnetic induction coil are positioned in effective district in magnetic induction in the magnetic signal induction coil assembly, or
Outside magnetic induction positioning effective district.
The differential lines of series connection magnetic induction coil are outside magnetic induction positioning effective district in the magnetic signal induction coil assembly.
It is arranged on the magnetic signal induction coil in the level code array and the magnetic signal in the vertical code array
Induction coil intersect permutation and combination setting.
The control circuit includes multiselect an array switch, prime signal amplifier, controllable gain amplifier, band logical and amplified
Device, AC/DC convertor, integrating circuit, dc amplifier, charge and discharge switch and processor；
Wherein, described multiselect an array switch side respectively with the horizontal induction coil and the vertical line of magnetic induction
Circle connection, described multiselect an array switch opposite side is connected with the pre-amplifier, the pre-amplifier with it is described controllable
Gain amplifier is connected；
Lead to the processor for described controllable gain amplifier one end, and the controllable gain amplifier other end leads to described
Bandpass amplifier, the bandpass amplifier is connected by the AC/DC convertor with the integrating circuit；
The processor is led in described integrating circuit one end by dc amplifier, and the integrating circuit other end leads to institute
Charge and discharge switch is stated, the processor respectively leads to multiselect an array switch and the charge and discharge switch.
Permutation and combination is set to：Any magnetic signal induction coil assembly is taken up an official post in level code array and vertical code array
The row two-by-two of meaning magnetic signal induction coil and the magnetic induction coil on adjacent preceding or adjacent rear other magnetic signal induction coil assemblies
Row combination is not repeated with the permutation and combination two-by-two in other positions；
And the magnetic induction coil followed on the same magnetic signal induction coil assembly discontinuously goes out at an arbitrary position simultaneously
Now participate in permutation and combination two-by-two.
The row two-by-two of two adjacent magnetic induction coils of optional position in the level code array and vertical code array
Row combination is unique.
Have the beneficial effect that：
The magnetic signal coil unit of this magnetic signal positioning inductor is in series by multiple magnetic induction passage coils, each
Individual series connection magnetic signal induction coil assembly can detect the alternation magnetic signal source of multiple positions, such electromagnetic induction channel line simultaneously
The wiring of the lead-out wire of circle is with regard to simpler, Scanning Detction locking time of the magnetic signal positioning inductor to alternation magnetic signal source
Short, speed is fast.
Brief description of the drawings
, below will be to embodiment in order to illustrate more clearly of the utility model embodiment or technical scheme of the prior art
Or the accompanying drawing used required in description of the prior art is briefly described, it should be apparent that, drawings in the following description are only
It is some embodiments of the present utility model, for those of ordinary skill in the art, is not paying the premise of creative work
Under, other accompanying drawings can also be obtained according to the structure shown in these accompanying drawings.
Fig. 1 is the utility model overall structure diagram.
Fig. 2 is the magnetic induction cellular construction schematic diagram that the utility model differential lines are arranged in effective district.
Fig. 3 is the magnetic induction cellular construction schematic diagram that the utility model differential lines are arranged on outside effective district.
Fig. 4 is the horizontal array coding structure schematic diagram that the utility model differential lines are arranged in effective district.
Fig. 5 is the orthogonal array coding structure schematic diagram that the utility model differential lines are arranged in effective district.
Fig. 6 is the sensing element schematic diagram that the utility model differential lines are arranged in effective district.
Fig. 7 is the horizontal array coding structure schematic diagram that the utility model differential lines are arranged on outside effective district.
Fig. 8 is the orthogonal array coding structure schematic diagram that the utility model differential lines are arranged on outside effective district.
Fig. 9 is the sensing element schematic diagram that the utility model differential lines are arranged on outside effective district.
Embodiment
Below in conjunction with the accompanying drawing in the utility model embodiment, the technical scheme in the utility model embodiment is carried out
Clearly and completely describe, it is clear that described embodiment is only a part of embodiment of the present utility model, rather than all
Embodiment.
Based on the embodiment in the utility model, those of ordinary skill in the art are not under the premise of creative work is made
The every other embodiment obtained, belongs to the scope of the utility model protection.
It is to be appreciated that institute is directional in the utility model embodiment indicates (such as up, down, left, right, before and after ...)
Relative position relation, motion conditions for being only used for explaining under a certain particular pose (as shown in drawings) between each part etc., such as
When really the particular pose changes, then directionality indicates also correspondingly therewith to change.
In the utility model such as relating to the description of " first ", " second " etc. be only used for describe purpose, and it is not intended that
Indicate or imply its relative importance or the implicit quantity for indicating indicated technical characteristic.Thus, define " first ",
At least one this feature can be expressed or be implicitly included to the feature of " second ".
In description of the present utility model, " multiple " are meant that at least two, such as two, three etc., unless otherwise
It is clearly specific to limit.
In the utility model, unless otherwise clearly defined and limited, term " connection ", " fixation " etc. should do broad sense reason
Solution, for example, " fixation " can be fixedly connected or be detachably connected, or integrally；Can mechanically connect, also may be used
Be electrical connection；Can be joined directly together, can also be indirectly connected to by intermediary, can be the connection of two element internals
Or the interaction relationship of two elements, unless otherwise clear and definite restriction.For the ordinary skill in the art, can be with
Concrete meaning of the above-mentioned term in the utility model is understood as the case may be.
In addition, the technical scheme between each embodiment of the utility model can be combined with each other, but must be with ability
Domain those of ordinary skill can be implemented as basis, will be understood that when the combination appearance of technical scheme is conflicting or can not realize
The combination of this technical scheme is not present, also not within the protection domain of the utility model requirement.
A kind of array code magnetic signal positions induction installation, including inductive component and the control electricity for connecting the inductive component
Road, it is characterised in that the inductive component includes：It is level code array, vertically disposed vertical with the level code array
Encoding array, the level code array is constituted with the vertical code array by magnetic signal induction coil assembly；
Wherein, the level code array is made up of more than one magnetic signal induction coil assembly；The vertical code
Array is made up of more than one magnetic signal induction coil assembly；
Wherein, the magnetic signal induction coil assembly is in series by least two magnetic induction coils by differential lines；
Wherein, the magnetic induction coil is made up of the continuous circular shape wire of 1 circle to 10 circles.
The differential lines of series connection magnetic induction coil are positioned in effective district in magnetic induction in the magnetic signal induction coil assembly, or
Outside magnetic induction positioning effective district.
The differential lines of series connection magnetic induction coil are outside magnetic induction positioning effective district in the magnetic signal induction coil assembly.
It is arranged on the magnetic signal induction coil in the level code array and the magnetic signal in the vertical code array
Induction coil intersect permutation and combination setting.
The control circuit includes multiselect an array switch, prime signal amplifier, controllable gain amplifier, band logical and amplified
Device, AC/DC convertor, integrating circuit, dc amplifier, charge and discharge switch and processor；
Wherein, described multiselect an array switch side respectively with the horizontal induction coil and the vertical line of magnetic induction
Circle connection, described multiselect an array switch opposite side is connected with the pre-amplifier, the pre-amplifier with it is described controllable
Gain amplifier is connected；
Lead to the processor for described controllable gain amplifier one end, and the controllable gain amplifier other end leads to described
Bandpass amplifier, the bandpass amplifier is connected by the AC/DC convertor with the integrating circuit；
The processor is led in described integrating circuit one end by dc amplifier, and the integrating circuit other end leads to institute
Charge and discharge switch is stated, the processor respectively leads to multiselect an array switch and the charge and discharge switch.
Permutation and combination is set to：Any magnetic signal induction coil assembly is taken up an official post in level code array and vertical code array
The row two-by-two of meaning magnetic signal induction coil and the magnetic induction coil on adjacent preceding or adjacent rear other magnetic signal induction coil assemblies
Row combination is not repeated with the permutation and combination two-by-two in other positions；
And the magnetic induction coil followed on the same magnetic signal induction coil assembly discontinuously goes out at an arbitrary position simultaneously
Now participate in permutation and combination two-by-two.
The row two-by-two of two adjacent magnetic induction coils of optional position in the level code array and vertical code array
Row combination is unique.
The material of the magnetic induction coil is alloy material, and the alloy material is made up of the alloy of following quality proportioning：
(FexCo1-x)a(Ni1-y-zAlyCez)bCucBdSieCrf, wherein a=30-60, b=30-55, c=1-5, d=1-8, e=1-5,
F=1-5, x=0.1-0.8, y=0.1-0.5, z=0.01-0.08；The preparation method of the alloy comprises the following steps：
Step one, the preparation of nano-alloy powder：Using powder based on iron powder, nickel powder, chromium powder and copper powder；Used
Iron powder 60~100 μm of granularity, purity >=99%；The granularity of nickel powder is 3~6 μm, purity>99%；The particle of chromium powder
80~120 μm of degree, purity >=99.9%；The granularity of copper powder is 50~130 μm, purity >=99.9%；
The iron powder, nickel powder, the mass ratio of chromium powder and copper powder are 20-40:15-30:1-6:1-5, is configured to mixed-powder,
Add absolute ethyl alcohol and stirring uniform, be put into after hermetically sealed can, in entering planetary type ball-milling under normal temperature on planetary ball mill, during ball milling
Between be 100-190h, obtain particle size be 1-10nm Fe-Ni-Cu-Cr alloy nano-powders, the basic powder with it is anhydrous
The mass ratio of ethanol is 1-2:0.5-3；
Step 2, the preparation of alloy powder matrix：
Quality proportioning according to alloy added after the nano-alloy powder obtained by step one is dried powder Si,
Al, Co, Ce and B, above-mentioned raw materials are put into vaccum sensitive stove, carry out melting at 1000-1500 DEG C, melt back 2-4 times,
Each melting 30-120min, after melting is finished, alloy cast ingot is obtained after carrying out strand, cooling under the protection of helium, will be cooled down
Alloy cast ingot afterwards, is put into after hermetically sealed can, and in entering planetary type ball-milling under normal temperature on planetary ball mill, the time of ball milling is
50-200h, it is the alloy powder matrix less than 15nm that ball milling, which obtains granularity,；The Si, Al, Co, Ce and B purity reach
More than 99.8%, Si particle diameter are that particle diameter is 10-100 μm, and Al particle diameter is 10-80 μm, and Co particle diameter is 10-120 μm, Ce grain
Footpath is 10-90 μm, and B particle diameter is 10-110 μm；
Step 3, sintering：
By the alloy powder matrix obtained by step 2 in argon gas atmosphere sintering furnace sinter molding, it is first in sintering process
First then existed with 10-15 DEG C/min heating rate in 400-500 DEG C of pre-burning 1-3h with 30-40 DEG C/min heating rate
1250-1350 DEG C of sintering 5-8h obtains base alloy；
Step 4, quenching：
The base alloy that step 3 is sintered, which is placed in glowing furnace, carries out Quenching Treatment, is 1100- first in hardening heat
1200 DEG C of soaking time 15-25min, are cooled to 50-80 DEG C of soaking time 30-40min in 5-10min afterwards；
Step 5, annealing：
Step 4 is quenched to obtained base alloy to be placed in the annealing furnace of argon gas atmosphere, 450-455 DEG C is first heated to,
1-2h is incubated, 525-535 DEG C is again heated to, 2-3h is incubated, 720 DEG C are then heated to, 3-4h is incubated, stops heating, in 30-
150-170 DEG C is cooled the temperature in 40min, room temperature is then naturally cooled to and obtains alloy；
Step 6, processing：
Alloy obtained by step 5 is carried out to the coil of shape needed for cutting processing is made.
The proportioning of the preferred alloy of the embodiment is：
(Fe0.6Co0.4)50(Ni0.65Al0.3Ce0.05)35Cu3B6Si3Cr3；
The structure of the more preferred alloy is：The alloy forms α-Fe phases, the α-Fe phases for the Co that adulterates and amorphous phase composition,
Wherein α-Fe phases and doping Co α-Fe the first phases of phase composition, the particle size of α-Fe phases and doping Co α-Fe phases in the first phase
Between 1-15nm, first mutually with foring an interface phase between amorphous phase, wherein the saturation magnetization of the first phase is about
1.52T, boundary is the interface that a thickness is 1-1.5nm, and the contents of wherein Ni in the first phase are containing in amorphous phase
1.5 times of amount.
In step one, Ball-milling Time preferably is 152h.
In step 5 more preferably, step 4 is quenched to obtained base alloy to be placed in the annealing furnace of argon gas atmosphere, it is first
455 DEG C are first heated to, 1.5h is incubated, 530 DEG C are again heated to afterwards, 2.5h is incubated, 720 DEG C are then heated to, 3.5h is incubated,
Stop heating, 150-170 DEG C is cooled the temperature in 30-40min, room temperature is then naturally cooled to and obtains alloy.
Embodiment 1
As shown in Figure 1, Figure 2 with shown in Fig. 4~Fig. 6, a kind of array code magnetic signal positions induction installation, including inductive component
100 pass through connector grafting or direct thermal compression welding to detection control circuit, sense with detection control circuit 10, sensing element 100
Element 100 is answered to include：Level code array 1010 and the vertically disposed vertical code array 1011 of level code array 1010, water
Flat encoding array 1010 is constituted with vertical code array 1011 by magnetic signal induction coil assembly；
Wherein, level code array 1010 is made up of more than one magnetic signal induction coil assembly；Vertical code array
1011 are made up of more than one magnetic signal induction coil assembly；
Wherein, magnetic signal induction coil assembly is in series by least two magnetic induction coils 101 by differential lines 102.
Wherein, magnetic induction coil is made up of the continuous circular shape wire of 1 circle to 10 circles.
Differential lines 102 are arranged in magnetic signal positioning effective district 118, and magnetic induction coil is electrically conducting transparent material or non-
Bright conductive material, vertical code array 1011 is arranged in same device with level code array 1010.
Preferably, magnetic signal induction coil 101 and vertical code array 1011 in level code array 1010 are arranged on
In magnetic signal induction coil 101 intersect permutation and combination setting.
Preferably, detection control circuit 10 includes multiselect an array switch 103, prime signal amplifier 104, controllable gain
Amplifier 105, bandpass amplifier 106, AC/DC convertor 107, integrating circuit 108, dc amplifier 109, charge and discharge switch
112 and processor 110；
Wherein, multiselect an array switch 103 sides respectively with level code array 1010 and vertical code array 1011
Magnetic induction coil 101 is connected, multiselect an array switch 103 opposite sides be connected with pre-amplifier 104, pre-amplifier 104 and
Controllable gain amplifier 105 is connected；
Lead to the one end of controllable gain amplifier 105 processor 110, and the other end of controllable gain amplifier 105, which leads to band logical, to be put
Big device 106, bandpass amplifier 106 is connected by AC/DC convertor 107 with integrating circuit 108；
Processor 110 is led in the one end of integrating circuit 108 by dc amplifier 109, and the other end of integrating circuit 108, which leads to, to be filled
Discharge switch 112, processor 110 leads to multiselect an array switch 103 by scanning bus 114, and the opposite side of processor 110 leads to
Charge and discharge switch 112.
Preferably, permutation and combination is set to：Any magnetic signal in level code array 1010 and vertical code array 1011
On induction coil assembly on any magnetic signal induction coil 101 and adjacent preceding or adjacent rear other magnetic signal induction coil assemblies
The permutation and combination two-by-two of magnetic induction coil 101 is not repeated with the permutation and combination two-by-two in other positions；
And the appearance discontinuous at an arbitrary position of the magnetic induction coil 101 on same magnetic signal induction coil assembly is followed simultaneously
Participate in permutation and combination two-by-two；
Preferably, two line of magnetic inductions adjacent with optional position in vertical code array 1011 of level code array 1010
The permutation and combination two-by-two of circle 101 is unique；
Differential lines 102 are arranged in magnetic signal positioning effective district 118.
The material of the magnetic induction coil is alloy material, and the alloy material is made up of the alloy of following quality proportioning：
(FexCo1-x)a(Ni1-y-zAlyCez)bCucBdSieCrf, wherein a=30-60, b=30-55, c=1-5, d=1-8, e=1-5, f
=1-5, x=0.1-0.8, y=0.1-0.5, z=0.01-0.08；The preparation method of the alloy comprises the following steps：
Step one, the preparation of nano-alloy powder：Using powder based on iron powder, nickel powder, chromium powder and copper powder；Used
Iron powder 60~100 μm of granularity, purity >=99%；The granularity of nickel powder is 3~6 μm, purity>99%；The particle of chromium powder
80~120 μm of degree, purity >=99.9%；The granularity of copper powder is 50~130 μm, purity >=99.9%；
The iron powder, nickel powder, the mass ratio of chromium powder and copper powder are 20-40:15-30:1-6:1-5, is configured to mixed-powder,
Add absolute ethyl alcohol and stirring uniform, be put into after hermetically sealed can, in entering planetary type ball-milling under normal temperature on planetary ball mill, during ball milling
Between be 100-190h, obtain particle size be 1-10nm Fe-Ni-Cu-Cr alloy nano-powders, the basic powder with it is anhydrous
The mass ratio of ethanol is 1-2:0.5-3；
Step 2, the preparation of alloy powder matrix：
Quality proportioning according to alloy added after the nano-alloy powder obtained by step one is dried powder Si,
Al, Co, Ce and B, above-mentioned raw materials are put into vaccum sensitive stove, carry out melting at 1000-1500 DEG C, melt back 2-4 times,
Each melting 30-120min, after melting is finished, alloy cast ingot is obtained after carrying out strand, cooling under the protection of helium, will be cooled down
Alloy cast ingot afterwards, is put into after hermetically sealed can, and in entering planetary type ball-milling under normal temperature on planetary ball mill, the time of ball milling is
50-200h, it is the alloy powder matrix less than 15nm that ball milling, which obtains granularity,；The Si, Al, Co, Ce and B purity reach
More than 99.8%, Si particle diameter are that particle diameter is 10-100 μm, and Al particle diameter is 10-80 μm, and Co particle diameter is 10-120 μm, Ce grain
Footpath is 10-90 μm, and B particle diameter is 10-110 μm；
Step 3, sintering：
By the alloy powder matrix obtained by step 2 in argon gas atmosphere sintering furnace sinter molding, it is first in sintering process
First then existed with 10-15 DEG C/min heating rate in 400-500 DEG C of pre-burning 1-3h with 30-40 DEG C/min heating rate
1250-1350 DEG C of sintering 5-8h obtains base alloy；
Step 4, quenching：
The base alloy that step 3 is sintered, which is placed in glowing furnace, carries out Quenching Treatment, is 1100- first in hardening heat
1200 DEG C of soaking time 15-25min, are cooled to 50-80 DEG C of soaking time 30-40min in 5-10min afterwards；
Step 5, annealing：
Step 4 is quenched to obtained base alloy to be placed in the annealing furnace of argon gas atmosphere, 450-455 DEG C is first heated to,
1-2h is incubated, 525-535 DEG C is again heated to, 2-3h is incubated, 720 DEG C are then heated to, 3-4h is incubated, stops heating, in 30-
150-170 DEG C is cooled the temperature in 40min, room temperature is then naturally cooled to and obtains alloy；
Step 6, processing：
Alloy obtained by step 5 is carried out to the coil of shape needed for cutting processing is made.
The proportioning of the preferred alloy of the embodiment is：
(Fe0.6Co0.4)50(Ni0.65Al0.3Ce0.05)35Cu3B6Si3Cr3；
The structure of the more preferred alloy is：The alloy forms α-Fe phases, the α-Fe phases for the Co that adulterates and amorphous phase composition,
Wherein α-Fe phases and doping Co α-Fe the first phases of phase composition, the particle chi of α-Fe phases and doping Co α-Fe phases in the first phase
It is very little between 1-15nm, first mutually with foring an interface phase between amorphous phase, wherein the saturation magnetization of the first phase is about
For 1.52T, boundary is the interface that a thickness is 1-1.5nm, and the contents of wherein Ni in the first phase are in amorphous phase
1.5 times of content.
In step one, Ball-milling Time preferably is 152h.
In step 5 more preferably, step 4 is quenched to obtained base alloy to be placed in the annealing furnace of argon gas atmosphere, it is first
455 DEG C are first heated to, 1.5h is incubated, 530 DEG C are again heated to afterwards, 2.5h is incubated, 720 DEG C are then heated to, 3.5h is incubated,
Stop heating, 150-170 DEG C is cooled the temperature in 30-40min, room temperature is then naturally cooled to and obtains alloy.
【Performance test】
(1) nano-alloy powder obtained by step one：
Sample is measured using Japanese Riken Denshi companies Mode IBHV-525 types vibrating specimen magnetometers (VSM)
Magnetic property.
1st, find that Ni, Cr and Cu diffraction maximum will go out after a period of time is milled to by studying the XRD spectral lines after ball milling
The situation now disappeared substantially, this is due to the increase with Ball-milling Time, Fe formation supersaturated solid solutions, perfection of crystal by
To destruction so that the crystal grain for participating in diffraction is reduced and causes peak height gradually to reduce, and Ni, Cr and Cu diffraction maximum are decreased up to substantially
Disappear, illustrate that Ni, Cr and Cu are solid-solution in Fe, form Fe supersaturated solid solution, research it has also been found that the appearance of this situation, right
It is inversely proportional in Cr contents and Ball-milling Time；But the particle in ball milling later stage is hardened, internal stress increase, when reaching elastic limit
When, particle starts fragmentation, while powder is constantly refined, and along with the generation of powder agglomeration, this is due to ball milling mistake
Cheng Zhong, forms many nanometer grade powders, and size reaches that the surface of nano level powder can increase with energy of adsorption, so as to cause
Agglomeration, therefore Ball-milling Time that should be optimal under the proportioning is 152h；
2nd, under after first rising with the saturation magnetization of the rising Fe-Ni-Cu-Cr of Cr contents alloy as described in Table 1
Drop, reaches maximum when Cr contents are 3-6%, (the σ of maximum 172 is reached when 5%s/A·m2·kg-1)；Because, when
The increase of Cr contents, can cause long-range order ferromagnetism in alloy mutually to increase, but Cr elements do not have magnetic moment, so than saturation magnetic
Change intensity as the increase of Cr contents first rises the situation declined afterwards；With the magnetic conductivity variable quantity of the rising of the Cr contents alloy
Downward trend after first rising is realized, obtains when content is 5% being saturation magnetization and the optimal proportioning of magnetic conductivity.
The performance test of the nano-alloy powder of table 1：
| Cr contents | Saturation magnetization (σs/A·m2·kg-1) | Magnetic conductivity increment |
| 0% | 124 | 0% |
| 1% | 147 | 1% |
| 3% | 151 | 2% |
| 5% | 172 | 3% |
| 7% | 150 | 1.5% |
| 9% | 131 | - 1% |
(2)
(1) add cerium in preparation process so that Ni is adulterated containing Ce elements in alloy, research find due to
Simultaneously containing thick atoms such as Cr, Ni in alloy, when thick atom combines to form alloy with small atom, then a kind of gold can be generated
Compound L aves phases between category, its different size atoms are stacked in structure cell in most fine and close mode, and its hardness is higher, there is aobvious
The invigoration effect of work, with the increase of Ce elements, hard phase increases in alloy, promotes the solid solution even tissue in alloy thin
Change, cause alloy to be not easily broken and peel off in the presence of external force, research finds the alloy table after friction of the alloy containing Ce
Face seems smooth, illustrates that support protective effect of the fibrous base to hard phase is increased, is mutually not easily stripped and comes off firmly, thus
Wear-resistant ability is improved, wear extent is reduced, wearability increases than not adding Ce alloy to improve more than 20%~30%
Ce content causes the austenite content in alloy body to reduce, and can be effectively improved the microstructure of alloy surface, so as to improve
The decay resistance of alloy；It has further been found that with after the increasing to a certain degree of Ce contents, crocking resistance in alloy and
Decay resistance strengthens, but downward trend is presented in magnetic conductivity, and this is due to for alloy after Ce increases to a certain extent
The refining effect of grain size, which reduces, reaches bottleneck, therefore slows down as the increase of Ce contents increases for crocking resistance, such as
When Ce contents are 1.75% it is optimum proportioning described in table 2, wherein the proportioning of alloy is (Fe0.6Co0.4)50
(Ni0.65Al0.3Ce0.05)35Cu3B6Si3Cr3。
Wear test：Carried out on RRT2III type reciprocating friction abrasion machines, the mating plate of wear test sample is 70mm
× 1317mm × 10mm white fused alumina emery sticks, granularity is 200 mesh, and specimen surface roughness is between 018~014 μm.Test speed
150r/s, test pressure 28MPa, testing time 10min, each sample testing number of times 1600-1800 times test stroke 75m, room
Warm 20-25 DEG C, humidity 23-26%, unlubricated dry wear test, wear extent is tested with universal electronic assay balance.It is not added with Ce
Alloy wear extent be 0.019/mg；
Corrosion test：Corrosive medium chooses H2SO4(5%), HCl (5%) and NaOH (5%), sample is under slight boiling condition
Corrode 24h, corrosion test is carried out using weight-loss method, sample first wants sanding and polishing, front and rear acetone soak, alcohol are clear corroding
Wash, hair-dryer drying after with a ten thousandth balance claim corrosion before and after weight, rate of corrosion.
The 2-in-1 golden performance test of table：
(3)
It is sintered in step 3 by reheating processing, heating is formally sintered after being preheated first.Through
Cross research and find that the initial permeability after than one time the pre-heat treatment of initial permeability after reheating processing is good, its magnetic conductance
Rate is higher than the alloy 5-10% of single heating, with the rise of temperature, alloy recurring structure relaxation, to stable low interior energy shape
State changes.And the rate of heat addition of reheating technique is also required to the rate of heat addition of significantly larger than first time pre-heating technique：" first
With 10-15 DEG C/min heating rate in 400-500 DEG C of pre-burning 1-3h, then with 30-40 DEG C/min heating rate in 1250-
1350 DEG C of sintering 5-8h " are preferably " first with 12 DEG C/min heating rate in 400-500 DEG C of pre-burning 2h, then with 35 DEG C/min
Heating rate sinter 7h " at 1250-1350 DEG C, second of rate of heat addition be almost three times in the rate of heat addition of first time, pass through
Research is found because preheating before has caused alloy body to have certain adaptability, by being rapidly heated so that material
Alloy it is rapid and crystallize more abundant, intercrystalline coupling is stronger, so that the effective anisotropy constant of material is lower,
Initial permeability is higher.Learnt by experiment, the alloy initial permeability handled using reheating after being sintered is higher than
Single heats the alloy initial permeability 3-7% after being sintered, and first time is three times in using second of rate of heat addition
The initial permeability of the alloy obtained after the rate of heat addition handles the initial magnetic of alloy after being sintered compared to common reheating
Conductance improves 4-8%；
(4) second stage in the quenching Step in the utility model employs quick quenching Step, is sent out by studying
It is existing, the performance more high-quality that quick quenching Step enables to alloy is employed, the notched bar impact strength of alloy can be improved and hard
Angle value, and influence is had no for magnetic property, the alloy is in quenching process, and the internal structure of its material undergoes phase transition toughness reinforcing, Ce
Element can partly melt so that the Ce in Binder Phase has little time to separate out in the case of chilling, serve the work for melting reinforcing admittedly
With the impact flexibility and hardness number of the alloy can be greatly improved.Impact flexibility can reach 0.72-0.89MJ/m2, wherein
It is by the proportioning considered when alloy material：Wherein the proportioning of alloy is (Fe0.6Co0.4)50(Ni0.65Al0.3Ce0.05)35Cu3B6Si3Cr3, when impact flexibility and properties of the Ce contents when being about 1.75% reach that most preferably, impact flexibility is
0.85MJ/m2, Rockwell hardness number is 38HRC.
(5) alloy forms α-Fe phases, the α-Fe phases for the Co that adulterates and amorphous phase composition after annealing steps, wherein
The particle size of α-Fe phases and doping Co α-Fe phases is in 1- in α-Fe the first phases of phase composition of α-Fe phases and doping Co, the first phase
Between 15nm, first mutually with foring an interface phase between amorphous phase, wherein the saturation magnetization of the first phase is about
1.52T, boundary is the interface that a thickness is 1-1.5nm, and the contents of wherein Ni in the first phase are containing in amorphous phase
1.5 times of amount；
The utility model it is creative prepare nano-alloy powder first, metal is added afterwards and carries out melting, so that
Ni can be entered in the first phase of α-Fe phases and doping Co α-Fe phase compositions, find to work as Ni in the first phase by research
Content for 1.5 times of content in amorphous phase when the alloy saturation magnetization it is maximum, the saturated magnetization of its alloy is strong
Degree is about 1.57T.
(1) annealing temperature in step 5 has certain influence for the crystal grain diameter of alloy.In alloy heating process, by
In there are different metallic elements, 455 DEG C are first heated to by studying discovery, 1.5h is incubated, first cause the member in the first phase
Plain Preferential Nucleation, is again heated to 530 DEG C afterwards, is incubated 2.5h, is then heated to 720 DEG C, is incubated 3.5h so that amorphous phase this
When can obtain uniform tiny nanostructured.If finding that crystallite dimension is drastically when temperature is increased to 750 DEG C after heating up again
Grow up, it increases magnetic anisotropy, while big crystal grain plays inhibition to the displacement of domain wall, magnetic moments rotations.Therefore this practicality
It is new use optimal annealing temperature for " be first heated to 455 DEG C, be incubated 1.5h, first cause the element in the first phase preferential into
Core, is again heated to 530 DEG C afterwards, is incubated 2.5h, is then heated to 720 DEG C, is incubated 3.5h ".
(2) research finds to need progress insulation program during being annealed, but the time of insulation and this practicality
The magnetic property of novel alloy has very big relation, and with the extension of soaking time, magnetic property declines.Due in the inside of alloy
In the presence of very big internal stress, and different parts solidification propulsion mode is different and forming region stress field, after 720 DEG C are incubated 3-4h
(optimal soaking time is 3.5h), the internal stress of alloy can be reached in sufficient release, each different performance reduction of magnetocrystalline, alloy
The meta-stable structure in portion tends towards stability, and alloy is shown excellent soft magnet performance.But after 720 DEG C of insulations are more than 4h, by
In the precipitated phase for occurring in that deterioration magnetic property, alloy magnetic property is caused to decline.
Embodiment 2
Reference picture 1, Fig. 3 and Fig. 7~Fig. 9, are with the difference of embodiment, and differential lines 102 are arranged on magnetic signal and determined
Outside the effective district 118 of position, magnetic induction coil 101 is opaque conductive material, vertical code array 1011 and level code array
1010 are arranged in same device, and the material of magnetic induction coil is consistent with embodiment 1.
Operation principle is as follows：
In reference picture 6 and Fig. 9, the close level code array 1010 in alternation magnetic signal source 117, level code array 1010
Several adjacent level line of magnetic induction coil units (Fig. 3) close to alternation magnetic signal source 117, for example：X1, x5, x7 and alternation magnetic are believed
The mutual inductance of number source 117 produces magnetic mutual inductance signal.
Several adjacent level magnetic induction coils 101 of this magnetic mutual inductance signal are produced, such as x1, x5, x7 assembly coding are
X5x1, x5x7, x7x5, x1x5x7 or x7x5x1, the assembly coding are current alternation magnetic signal source 117 in level code array
Horizontal coordinate coding in 1010 nuclear magnetic signals positioning effective district 118, produces the stronger magnetic induction coil 101 of magnetic mutual inductance signal and sentences
Determine closer to alternation magnetic signal source 117.
Similarly, alternation magnetic signal source 117 is close in vertical code array 1011, perpendicular encoding array 1011 hands over
Become several adjacent line of magnetic induction coil units (Fig. 3) in magnetic signal source 117, such as y6, y2, y4 and alternation magnetic signal source 117 are mutual
Sense produces magnetic mutual inductance signal.
The assembly coding for producing several adjacent magnetic induction coils 101 such as y6, y2, y4 of this magnetic mutual inductance signal is y6y2,
Y2y6, y2y4, y4y2, y6y2y4 or y4y2y6, the assembly coding are current alternation magnetic signal source 117 in vertical code array
1011 and magnetic signal positioning effective district 118 in vertical coordinate coding, produce the stronger magnetic induction coil 101 of magnetic mutual inductance signal and sentence
Determine closer to alternation magnetic signal source 117.
Close to x1, x5, x7 or y6, y2, y4 of several adjacent magnetic induction coils 101 in alternation magnetic signal source 117 combination
Encode x1x5, x5x1, x5x7, x7x5, x1x5x7 or x7x5x1 and y6y2, y2y6, y2y4, y4y2, y6y2y4 or y4y2y6, generation
Detection magnetic signal framing effective district 118 horizontally and vertically big of the table alternation magnetic signal source 117 in sensing element 100
Cause absolute coordinate position.
Alternation magnetic signal source 117 judges that most strong magnetic induction coil of magnetic mutual inductance signal at substantially absolute coordinate position
101, such as x1x5x7 x5 and y6y2y4 y2 positions, further according to the sensing magnetic of the magnetic induction coil of most strong magnetic induction coil both sides
The ratio of mutual inductance signal intensity judges that alternation magnetic signal source 117 leads in most strong magnetic induction coil x1x5x7 x5 and y6y2y4 y2
The fine relative position of opposite sides magnetic induction coil 2 in road region.
Most strong magnetic induction coil x5 and magnetic induction coil x1, x7 and the y6 of y2 both sides, the ratio of y4 magnetic mutual inductance signal intensity
For 1:1 represents alternation magnetic signal source 117 in most strong magnetic induction coil x5 and y2 passages center, more than 1:1 judges to hand over
Become magnetic signal source 117 in most strong magnetic induction coil x5 and y2 passages region and amesiality time strong magnetic induction coil,
The distance of skew is directly proportional with this ratio, less than 1:1 judges alternation magnetic signal source 117 in most strong magnetic induction coil x5 and y2
In passage region and time strong line of magnetic induction coil unit of opposite side is inclined to, the distance of skew is inversely proportional with this ratio.
The material of the magnetic induction coil is alloy material, and the alloy material is made up of the alloy of following quality proportioning：
(FexCo1-x)a(Ni1-y-zAlyCez)bCucBdSieCrf, wherein a=30-60, b=30-55, c=1-5, d=1-8, e=1-5,
F=1-5, x=0.1-0.8, y=0.1-0.5, z=0.01-0.08；The preparation method of the alloy comprises the following steps：
Step one, the preparation of nano-alloy powder：Using powder based on iron powder, nickel powder, chromium powder and copper powder；Used
Iron powder 60~100 μm of granularity, purity >=99%；The granularity of nickel powder is 3~6 μm, purity>99%；The particle of chromium powder
80~120 μm of degree, purity >=99.9%；The granularity of copper powder is 50~130 μm, purity >=99.9%；
The iron powder, nickel powder, the mass ratio of chromium powder and copper powder are 20-40:15-30:1-6:1-5, is configured to mixed-powder,
Add absolute ethyl alcohol and stirring uniform, be put into after hermetically sealed can, in entering planetary type ball-milling under normal temperature on planetary ball mill, during ball milling
Between be 100-190h, obtain particle size be 1-10nm Fe-Ni-Cu-Cr alloy nano-powders, the basic powder with it is anhydrous
The mass ratio of ethanol is 1-2:0.5-3；
Step 2, the preparation of alloy powder matrix：
Quality proportioning according to alloy added after the nano-alloy powder obtained by step one is dried powder Si,
Al, Co, Ce and B, above-mentioned raw materials are put into vaccum sensitive stove, carry out melting at 1000-1500 DEG C, melt back 2-4 times,
Each melting 30-120min, after melting is finished, alloy cast ingot is obtained after carrying out strand, cooling under the protection of helium, will be cooled down
Alloy cast ingot afterwards, is put into after hermetically sealed can, and in entering planetary type ball-milling under normal temperature on planetary ball mill, the time of ball milling is
50-200h, it is the alloy powder matrix less than 15nm that ball milling, which obtains granularity,；The Si, Al, Co, Ce and B purity reach
More than 99.8%, Si particle diameter are that particle diameter is 10-100 μm, and Al particle diameter is 10-80 μm, and Co particle diameter is 10-120 μm, Ce's
Particle diameter is 10-90 μm, and B particle diameter is 10-110 μm；
Step 3, sintering：
By the alloy powder matrix obtained by step 2 in argon gas atmosphere sintering furnace sinter molding, it is first in sintering process
First then existed with 10-15 DEG C/min heating rate in 400-500 DEG C of pre-burning 1-3h with 30-40 DEG C/min heating rate
1250-1350 DEG C of sintering 5-8h obtains base alloy；
Step 4, quenching：
The base alloy that step 3 is sintered, which is placed in glowing furnace, carries out Quenching Treatment, is 1100- first in hardening heat
1200 DEG C of soaking time 15-25min, are cooled to 50-80 DEG C of soaking time 30-40min in 5-10min afterwards；
Step 5, annealing：
Step 4 is quenched to obtained base alloy to be placed in the annealing furnace of argon gas atmosphere, 450-455 DEG C is first heated to,
1-2h is incubated, 525-535 DEG C is again heated to, 2-3h is incubated, 720 DEG C are then heated to, 3-4h is incubated, stops heating, in 30-
150-170 DEG C is cooled the temperature in 40min, room temperature is then naturally cooled to and obtains alloy；
Step 6, processing：
Alloy obtained by step 5 is carried out to the coil of shape needed for cutting processing is made.
The proportioning of the preferred alloy of the embodiment is：
(Fe0.6Co0.4)50(Ni0.65Al0.3Ce0.05)35Cu3B6Si3Cr3；
The structure of the more preferred alloy is：The alloy forms α-Fe phases, the α-Fe phases for the Co that adulterates and amorphous phase composition,
Wherein α-Fe phases and doping Co α-Fe the first phases of phase composition, the particle size of α-Fe phases and doping Co α-Fe phases in the first phase
Between 1-15nm, first mutually with foring an interface phase between amorphous phase, wherein the saturation magnetization of the first phase is about
1.52T, boundary is the interface that a thickness is 1-1.5nm, and the contents of wherein Ni in the first phase are containing in amorphous phase
1.5 times of amount.
In step one, Ball-milling Time preferably is 152h.
In step 5 more preferably, step 4 is quenched to obtained base alloy to be placed in the annealing furnace of argon gas atmosphere, it is first
455 DEG C are first heated to, 1.5h is incubated, 530 DEG C are again heated to afterwards, 2.5h is incubated, 720 DEG C are then heated to, 3.5h is incubated,
Stop heating, 150-170 DEG C is cooled the temperature in 30-40min, room temperature is then naturally cooled to and obtains alloy.
【Performance test】
(1) nano-alloy powder obtained by step one：
Sample is measured using Japanese Riken Denshi companies Mode IBHV-525 types vibrating specimen magnetometers (VSM)
Magnetic property.
1st, find that Ni, Cr and Cu diffraction maximum will go out after a period of time is milled to by studying the XRD spectral lines after ball milling
The situation now disappeared substantially, this is due to the increase with Ball-milling Time, Fe formation supersaturated solid solutions, perfection of crystal by
To destruction so that the crystal grain for participating in diffraction is reduced and causes peak height gradually to reduce, and Ni, Cr and Cu diffraction maximum are decreased up to substantially
Disappear, illustrate that Ni, Cr and Cu are solid-solution in Fe, form Fe supersaturated solid solution, research it has also been found that the appearance of this situation, right
It is inversely proportional in Cr contents and Ball-milling Time；But the particle in ball milling later stage is hardened, internal stress increase, when reaching elastic limit
When, particle starts fragmentation, while powder is constantly refined, and along with the generation of powder agglomeration, this is due to ball milling mistake
Cheng Zhong, forms many nanometer grade powders, and size reaches that the surface of nano level powder can increase with energy of adsorption, so as to cause
Agglomeration, therefore Ball-milling Time that should be optimal under the proportioning is 152h；
2nd, under after first rising with the saturation magnetization of the rising Fe-Ni-Cu-Cr of Cr contents alloy as described in Table 1
Drop, reaches maximum when Cr contents are 3-6%, (the σ of maximum 172 is reached when 5%s/A·m2·kg-1)；Because, when
The increase of Cr contents, can cause long-range order ferromagnetism in alloy mutually to increase, but Cr elements do not have magnetic moment, so comparing saturation
The intensity of magnetization first rises the situation declined afterwards with the increase of Cr contents；With the magnetic conductivity change of the rising of the Cr contents alloy
Amount realizes downward trend after first rising, obtains when content is 5% being saturation magnetization and the optimal proportioning of magnetic conductivity.
The performance test of the nano-alloy powder of table 1：
| Cr contents | Saturation magnetization (σs/A·m2·kg-1) | Magnetic conductivity increment |
| 0% | 124 | 0% |
| 1% | 147 | 1% |
| 3% | 151 | 2% |
| 5% | 172 | 3% |
| 7% | 150 | 1.5% |
| 9% | 131 | - 1% |
(2)
(1) add cerium in preparation process so that Ni is adulterated containing Ce elements in alloy, research find due to
Simultaneously containing thick atoms such as Cr, Ni in alloy, when thick atom combines to form alloy with small atom, then a kind of gold can be generated
Compound L aves phases between category, its different size atoms are stacked in structure cell in most fine and close mode, and its hardness is higher, there is aobvious
The invigoration effect of work, with the increase of Ce elements, hard phase increases in alloy, promotes the solid solution even tissue in alloy thin
Change, cause alloy to be not easily broken and peel off in the presence of external force, research finds the alloy table after friction of the alloy containing Ce
Face seems smooth, illustrates that support protective effect of the fibrous base to hard phase is increased, is mutually not easily stripped and comes off firmly, thus
Wear-resistant ability is improved, wear extent is reduced, wearability increases than not adding Ce alloy to improve more than 20%~30%
Ce content causes the austenite content in alloy body to reduce, and can be effectively improved the microstructure of alloy surface, so as to improve
The decay resistance of alloy；It has further been found that with after the increasing to a certain degree of Ce contents, crocking resistance in alloy and
Decay resistance strengthens, but downward trend is presented in magnetic conductivity, and this is due to for alloy after Ce increases to a certain extent
The refining effect of grain size, which reduces, reaches bottleneck, therefore slows down as the increase of Ce contents increases for crocking resistance, such as
When Ce contents are 1.75% it is optimum proportioning described in table 2, wherein the proportioning of alloy is (Fe0.6Co0.4)50
(Ni0.65Al0.3Ce0.05)35Cu3B6Si3Cr3。
Wear test：Carried out on RRT2III type reciprocating friction abrasion machines, the mating plate of wear test sample is 70mm
× 1317mm × 10mm white fused alumina emery sticks, granularity is 200 mesh, and specimen surface roughness is between 018~014 μm.Test speed
150r/s, test pressure 28MPa, testing time 10min, each sample testing number of times 1600-1800 times test stroke 75m, room
Warm 20-25 DEG C, humidity 23-26%, unlubricated dry wear test, wear extent is tested with universal electronic assay balance.It is not added with Ce
Alloy wear extent be 0.019/mg；
Corrosion test：Corrosive medium chooses H2SO4(5%), HCl (5%) and NaOH (5%), sample is under slight boiling condition
Corrode 24h, corrosion test is carried out using weight-loss method, sample first wants sanding and polishing, front and rear acetone soak, alcohol are clear corroding
Wash, hair-dryer drying after with a ten thousandth balance claim corrosion before and after weight, rate of corrosion.
The 2-in-1 golden performance test of table：
(3)
It is sintered in step 3 by reheating processing, heating is formally sintered after being preheated first.Through
Cross research and find that the initial permeability after than one time the pre-heat treatment of initial permeability after reheating processing is good, its magnetic conductance
Rate is higher than the alloy 5-10% of single heating, with the rise of temperature, alloy recurring structure relaxation, to stable low interior energy state
Transformation.And the rate of heat addition of reheating technique is also required to the rate of heat addition of significantly larger than first time pre-heating technique：" first with
10-15 DEG C/min heating rate is in 400-500 DEG C of pre-burning 1-3h, then with 30-40 DEG C/min heating rate in 1250-
1350 DEG C of sintering 5-8h " are preferably " first with 12 DEG C/min heating rate in 400-500 DEG C of pre-burning 2h, then with 35 DEG C/min
Heating rate sinter 7h " at 1250-1350 DEG C, second of rate of heat addition be almost three times in the rate of heat addition of first time, pass through
Research is found because preheating before has caused alloy body to have certain adaptability, by being rapidly heated so that material
Alloy it is rapid and crystallize more abundant, intercrystalline coupling is stronger, so that the effective anisotropy constant of material is lower,
Initial permeability is higher.Learnt by experiment, the alloy initial permeability handled using reheating after being sintered is higher than
Single heats the alloy initial permeability 3-7% after being sintered, and first time is three times in using second of rate of heat addition
The initial permeability of the alloy obtained after the rate of heat addition handles the initial magnetic of alloy after being sintered compared to common reheating
Conductance improves 4-8%；
(4) second stage in the quenching Step in the utility model employs quick quenching Step, is sent out by studying
It is existing, the performance more high-quality that quick quenching Step enables to alloy is employed, the notched bar impact strength of alloy can be improved and hard
Angle value, and influence is had no for magnetic property, the alloy is in quenching process, and the internal structure of its material undergoes phase transition toughness reinforcing, Ce
Element can partly melt so that the Ce in Binder Phase has little time to separate out in the case of chilling, serve the work for melting reinforcing admittedly
With the impact flexibility and hardness number of the alloy can be greatly improved.Impact flexibility can reach 0.72-0.89MJ/m2, wherein
It is by the proportioning considered when alloy material：Wherein the proportioning of alloy is (Fe0.6Co0.4)50(Ni0.65Al0.3Ce0.05)35Cu3B6Si3Cr3, when impact flexibility and properties of the Ce contents when being about 1.75% reach that most preferably, impact flexibility is
0.85MJ/m2, Rockwell hardness number is 38HRC.
(5) alloy forms α-Fe phases, the α-Fe phases for the Co that adulterates and amorphous phase composition after annealing steps, wherein
The particle size of α-Fe phases and doping Co α-Fe phases is in 1- in α-Fe the first phases of phase composition of α-Fe phases and doping Co, the first phase
Between 15nm, first mutually with foring an interface phase between amorphous phase, wherein the saturation magnetization of the first phase is about
1.52T, boundary is the interface that a thickness is 1-1.5nm, and the contents of wherein Ni in the first phase are containing in amorphous phase
1.5 times of amount；
The utility model it is creative prepare nano-alloy powder first, metal is added afterwards and carries out melting, so that
Ni can be entered in the first phase of α-Fe phases and doping Co α-Fe phase compositions, find to work as Ni in the first phase by research
Content for 1.5 times of content in amorphous phase when the alloy saturation magnetization it is maximum, the saturated magnetization of its alloy is strong
Degree is about 1.57T.
(1) annealing temperature in step 5 has certain influence for the crystal grain diameter of alloy.In alloy heating process, by
In there are different metallic elements, 455 DEG C are first heated to by studying discovery, 1.5h is incubated, first cause the member in the first phase
Plain Preferential Nucleation, is again heated to 530 DEG C afterwards, is incubated 2.5h, is then heated to 720 DEG C, is incubated 3.5h so that amorphous phase this
When can obtain uniform tiny nanostructured.If finding that crystallite dimension is drastically when temperature is increased to 750 DEG C after heating up again
Grow up, it increases magnetic anisotropy, while big crystal grain plays inhibition to the displacement of domain wall, magnetic moments rotations.Therefore this practicality
It is new use optimal annealing temperature for " be first heated to 455 DEG C, be incubated 1.5h, first cause the element in the first phase preferential into
Core, is again heated to 530 DEG C afterwards, is incubated 2.5h, is then heated to 720 DEG C, is incubated 3.5h ".
(2) research finds to need progress insulation program during being annealed, but the time of insulation and this practicality
The magnetic property of novel alloy has very big relation, and with the extension of soaking time, magnetic property declines.Due in the inside of alloy
In the presence of very big internal stress, and different parts solidification propulsion mode is different and forming region stress field, after 720 DEG C are incubated 3-4h
(optimal soaking time is 3.5h), the internal stress of alloy can be reached in sufficient release, each different performance reduction of magnetocrystalline, alloy
The meta-stable structure in portion tends towards stability, and alloy is shown excellent soft magnet performance.But after 720 DEG C of insulations are more than 4h, by
In the precipitated phase for occurring in that deterioration magnetic property, alloy magnetic property is caused to decline.
Preferred embodiment of the present utility model is the foregoing is only, the scope of the claims of the present utility model is not thereby limited,
It is every utility model of the present utility model design under, the equivalent structure made using the utility model specification and accompanying drawing content
Conversion, or directly/be used in other related technical fields indirectly and be included in scope of patent protection of the present utility model.
Claims (7)
1. a kind of array code magnetic signal positions induction installation, including inductive component and the control electricity for connecting the inductive component
Road, it is characterised in that the inductive component includes：It is level code array, vertically disposed vertical with the level code array
Encoding array, the level code array is constituted with the vertical code array by magnetic signal induction coil assembly；
Wherein, the level code array is made up of more than one magnetic signal induction coil assembly；The vertical code array
It is made up of more than one magnetic signal induction coil assembly；
Wherein, the magnetic signal induction coil assembly is in series by least two magnetic induction coils by differential lines；
Wherein, the magnetic induction coil is made up of the continuous circular shape wire of 1 circle to 10 circles.
2. a kind of array code magnetic signal positioning induction installation according to claim 1, it is characterised in that the magnetic signal
The differential lines of series connection magnetic induction coil position effective district in magnetic induction positioning effective district, or in magnetic induction in induction coil assembly
Outside.
3. a kind of array code magnetic signal positioning induction installation according to claim 1, it is characterised in that the magnetic signal
The differential lines of series connection magnetic induction coil are outside magnetic induction positioning effective district in induction coil assembly.
4. array code magnetic signal according to claim 1 positions induction installation, it is characterised in that be arranged on the level
Magnetic signal induction coil in encoding array and the magnetic signal induction coil in the vertical code array intersect arrangement group
Close and set.
5. array code magnetic signal according to claim 1 positions induction installation, it is characterised in that the control circuit bag
Include multiselect an array switch, prime signal amplifier, controllable gain amplifier, bandpass amplifier, AC/DC convertor, integration electricity
Road, dc amplifier, charge and discharge switch and processor；
Wherein, multiselect an array switch side connects with the horizontal induction coil and the vertical magnetic induction coil respectively
Connect, multiselect an array switch opposite side is connected with the pre-amplifier, the pre-amplifier and the controllable gain
Amplifier is connected；
Lead to the processor for described controllable gain amplifier one end, and the controllable gain amplifier other end leads to the band logical
Amplifier, the bandpass amplifier is connected by the AC/DC convertor with the integrating circuit；
The processor is led in described integrating circuit one end by dc amplifier, and the integrating circuit other end leads to described
Charge and discharge switch, the processor respectively leads to multiselect an array switch and the charge and discharge switch.
6. array code magnetic signal according to claim 2 positions induction installation, it is characterised in that permutation and combination is set
For：In level code array and vertical code array on any magnetic signal induction coil assembly any magnetic signal induction coil with it is adjacent
The permutation and combination two-by-two of magnetic induction coil after preceding or adjacent on other magnetic signal induction coil assemblies not with other positions
Permutation and combination two-by-two repeat；
And the magnetic induction coil followed on the same magnetic signal induction coil assembly is discontinuously joined at an arbitrary position simultaneously
With permutation and combination two-by-two.
7. array code magnetic signal according to claim 1 positions induction installation, it is characterised in that the level code battle array
The permutation and combination two-by-two of row two magnetic induction coils adjacent with optional position in vertical code array is unique.