CN1273402C - Layered decorative glass board and its manufacture - Google Patents
Layered decorative glass board and its manufacture Download PDFInfo
- Publication number
- CN1273402C CN1273402C CN 01131104 CN01131104A CN1273402C CN 1273402 C CN1273402 C CN 1273402C CN 01131104 CN01131104 CN 01131104 CN 01131104 A CN01131104 A CN 01131104A CN 1273402 C CN1273402 C CN 1273402C
- Authority
- CN
- China
- Prior art keywords
- glass
- stained glass
- jigsaw
- board
- stained
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention discloses a stacking decorative glass board and a manufacturing method thereof. The stacking decorative glass board is composed of a plurality of color glass pieces and a color glass splice board of which the edge is attached, one double-surface adhesive tape is attached to one side along the periphery of the color glass splice board, a transparent solid supporting board is attached to one side of the color glass pieces with the adhesive tape, and a small thin mid-hollow layer is formed in the middle; the mobile transparent resin adhesive is poured into the small thin mid-hollow layer from a gap of the adhesive tape, and the color glass splice board can be attached to a support board tightly after the resin adhesive is solidified. A second support board is attached to the other side of the color splice board in the same mode so as to be firm, and the stacking decorative glass board which is manufactured is firmer than a traditional decorative glass board.
Description
Technical field
The present invention relates to decorative glass board, refer in particular to a kind of layered decorative glass board and manufacture method thereof.
Background technology
The decorative glass board of commonly using mostly is welded by the stained glass sheet.Because the connection between the stained glass sheet is very fragile, thereby limited the size of decorative glass board.The ambetti window that one fan is big only can be made by the decorative glass board of filling fritter in a metal frame.The restriction that design in the decorative glass board seriously is subjected to single little stained glass sheet and separates thick of used metal frame.And,, make that decorative sheet still is easy to be broken by strong wind and slungshot because the weldering of the fragility between the stained glass sheet connects.And the decorative glass board outside these are exposed to also can be subjected to the influence of weather and environmental pollution and be destroyed.
The laminated glass plate also is the window manufacturing technology that is widely known by the people.Typical laminated glass plate is by the very thin Resin adhesive of one deck two blocks of solid glass plates to be bonded together to form.In any case concerning the application of weight sensitive, traditional laminated glass is still too heavy for those, the ship that for example cruises is just refused traditional laminated glass.
Yet, there is no layered decorative glass board in the former technology and be found.
Summary of the invention
Main purpose of the present invention is to provide a kind of layered decorative glass board and manufacture method thereof, makes layered decorative glass board more solid than traditional decorative glass board, with anti-broken;
Secondary objective of the present invention is to provide a kind of layered decorative glass board and manufacture method thereof, makes layered decorative glass board enough firm, can produce large size;
Another object of the present invention is to provide a kind of layered decorative glass board and manufacture method thereof, make layered decorative glass board can resist the infringement of weather and environmental pollution;
Another purpose of the present invention is to provide a kind of layered decorative glass board and manufacture method thereof, makes layered decorative glass board enough light, to be fit to the application of weight sensitive.
The present invention realizes above-mentioned purpose like this:
A kind of layered decorative glass board comprises stained glass sheet, tamanori, back up pad and tack coat;
The stained glass sheet is placed on the predefined pattern, and forms a gap between adjacent stained glass sheet;
Tamanori is positioned in the described gap, in order to described stained glass sheet cementation is become a stained glass jigsaw;
Transparent support plate is parallel to connect first that is fixed in described stained glass jigsaw, and constructs a hollow layer with it;
A transparent bonding layer is folded between described stained glass jigsaw and the described back up pad.
Wherein, above-mentioned tack coat comprises that a periphery double sticky tape and that is surrounded on described stained glass jigsaw is by the transparent resin adhesive that can insert described double sticky tape enclosed space.
Above-mentioned back up pad can be one in order to improve the sheet glass of rigidity, so that layered decorative glass board can be resisted the infringement of weather and environmental pollution; Also can be a plastic plate, make layered decorative glass board enough light, to be fit to the application of weight sensitive in order to weight reduction.
Above-mentioned layered decorative glass board also comprises an additional transparent back up pad, is adhered to second of described stained glass jigsaw by second tack coat, in order to gain in strength.
Above-mentioned interim stayed surface has a surface that has stickiness, in order to prevent described stained glass sheet relatively sliding.
Above-mentioned adhesive tape is a zona pellucida.
Above-mentioned layered decorative glass board is transparently also offered an otch in around sheet glass at one, and described stained glass sheet is put into described otch, in order to constituting described stained glass jigsaw so that described stained glass sheet by described transparent around sheet glass institute around.
A kind of method of making above-mentioned layered decorative glass board comprises that step is as follows:
Process unicolor stained glass sheet according to predetermined sliceable shape together;
The described stained glass sheet of arranging on an interim stayed surface keeps a gap between described stained glass sheet;
Filling adhesive between the parallel clearance that constitutes between described stained glass sheet is in order to constitute a stained glass jigsaw;
Described stained glass jigsaw and a roughly the same transparent support plate are bonded together.
Wherein, above-mentioned stained glass jigsaw and transparent support plate step for adhering are as follows:
Adopt a double sticky tape along first periphery of described stained glass jigsaw around laying, and leave one and fill the gap;
Place a transparent support plate on the described adhesive tape to constitute the hollow layer between a described back up pad that is bonded by adhesive tape and described stained glass jigsaw;
Tilt described stained glass jigsaw and back up pad make described filling gap up;
Transparent glue is poured into described hollow layer between described stained glass jigsaw and described back up pad;
With described decorative glass board horizontal positioned, so that described glue is outwards towards described filling Clearance Flow;
After described glue is full of filling gap in the described adhesive tape, seal described gap.
Like this, more solid, firm according to the layered decorative glass board that described structure and method are made than traditional decorative glass board, more fragmentation can be resisted, and large size can be produced.
Description of drawings
Fig. 1 is the sectional view of first embodiment of the invention;
Fig. 2 is the sectional view of second embodiment of the invention;
Fig. 3 is the skeleton view of stained glass sheet splicing;
Fig. 4 is the skeleton view of the stained glass jigsaw that is bonded by the stained glass sheet;
Fig. 5 is the synoptic diagram that double sticky tape is applied to stained glass jigsaw periphery;
Fig. 6 is back up pad and stained glass jigsaw bonded synoptic diagram;
Fig. 7 pours into stained glass jigsaw and back up pad intermediary hollow layer synoptic diagram with Resin adhesive;
Fig. 8 is the synoptic diagram that Resin adhesive extends and be full of hollow layer;
Fig. 9 is the exploded view of third embodiment of the invention.
Specific embodiment
Below in conjunction with drawings and Examples, the present invention is further described.
As shown in Figure 1, the first embodiment of the present invention comprise stained glass sheet 10-14 along its edge by the tamanori 15 bonding stained glass jigsaw 16 that form.Described stained glass sheet 10-14 can be arbitrary suitable thickness, and can be translucent or opaque.Stained glass jigsaw 16 can comprise the stained glass sheet of arbitrary number, wherein is also included within the transparent sheet glass of embedding in numerous stained glass sheets.Transparent solid support plate 17 is adhered on first of stained glass jigsaw 16 by adding therein tack coat 18.Be to increase rigidity, transparent support plate 17 can be selected glass for use, and for weight reduction, then plastics is more suitable.Even from the weight consideration, the stained glass sheet also can be plastics.The plastics that are suitable for are not limited to polycarbonate, vinylformic acid and polyester.Plastic support board should be enough light so that can be applicable to those application, adopt the ship that cruises of traditional glass such as refusal to weight sensitive.
Back up pad 17 can be fully transparent, translucent or semi-transparent, and is colourless or light color.Tack coat 18 preferably is made up of double sticky tape 19 and transparent Resin adhesive 20, but also can be made up of other suitable transparent bonding material forms.Double sticky tape 19 is preferably transparent, if but it be hidden in also can select for use under the framework opaque.Tack coat 18 can be any thickness, but preferably thin as much as possible, such as 1 millimeter.The power that the optimum thickness of back up pad 17 should be able to be resisted is that all are considered in advance, affact decorative glass board is as high wind and slungshot.
When the external unit that is used as a buildings, as window, door, wall etc., the outside surface that decorative glass board is preferably in the stained glass jigsaw is equipped with back up pad 17 to resist weather and environmental pollution.The non-stacked inner face of decorative glass board allows directly to see or touch stained glass jigsaw 16.Described back up pad 17 can be attached on the front or the reverse side of stained glass jigsaw 16.Because back up pad 17 has increased intensity, decorative glass board can be used as the place except the buildings external unit, as interior wall, dividing plate, partition, desktop, counter top etc.
As shown in Figure 2, the second embodiment of the present invention is to add a transparent solid back up pad 21 by other to bond to second of stained glass jigsaw 16 by second tack coat 22, and described second tack coat 22 is made up of a two-sided adhesive tape 23 and transparent resin adhesive 24.Back up pad 21 can be glass or plastics.This second back up pad 21 provides the bigger intensity and the ability of anti-weather.
Fig. 3 is to Figure 8 shows that the method for making layered decorative glass board.In Fig. 3, the stained glass sheet of any amount as sheet glass 25-28, is processed to desirable shape and they are arranged in together on interim bearing surface (in the drawings expression) and keep certain clearance to constitute desirable figure.Described interim bearing surface preferably is a bit sticky to prevent relatively sliding between sheet glass.For example, a list that has stickiness is layered on the inflexible platform, and sheet glass is arranged on the list that has stickiness.In Fig. 4, the gap between sheet glass 25-28 is all filled up with glass cement (as silica gel, Resins, epoxy etc.).Wipe out any glue that overflows from sheet glass 25-28.When glue air-dry or solidify after, sheet glass 25-28 has just connected into a stained glass jigsaw 30.
In Fig. 5, double faced adhesive tape 31 is used in first or top periphery of stained glass jigsaw 30, and leaves little airspace respectively and leave a bigger filling gap at the middle part on one side two corners.Double faced adhesive tape 31 is preferably transparent.In Fig. 6, one with the stained glass jigsaw at least quite the transparent solid support plate 32 of size be placed thereon double faced adhesive tape 31 tops.Described back up pad 32 can be glass or plastics.Simultaneously formed one by double faced adhesive tape 31 bonding very thin hollow layers that produce at stained glass jigsaw 30 and 32 of back up pads.
If back up pad 32 is the front of decorative glass board, stained glass jigsaw 30 is with its combination that faces up.If back up pad 32 is the reverse side of decorative glass board, and stained glass jigsaw 30 is with its combination that faces up, and stained glass jigsaw 30 should turn before back up pad 32 is installed.Place that second interim back up pad clamped stained glass jigsaw 30 on the top of stained glass jigsaw with two interim back up pads and upset just can be finished.
In Fig. 7, when the support that relies on interim back up pad (among the figure mark), stained glass jigsaw 30 and back up pad 32 are tilted in an angle between vertical and level.A funnel 33 that has suitable narrow outlet is put into the filling gap that is stayed by double faced adhesive tape 31.Transparent Resin adhesive 34 is poured into the hollow layer of 32 of stained glass jigsaw 30 and back up pads.Resin adhesive 34 should have good mobility so that be easy to flow into little space.Pour filling glue quantity through accurate calculation into to avoid waste and to overflow.Because the pressure stained glass jigsaw 30 of Resin adhesive 34 and back up pad 32 have outside protuberance slightly, so should not be poured into the upper edge of hollow layer when pouring into all glue.If stained glass jigsaw 30 and back up pad 32 are in vertical position, protuberance will be bigger, so their best positions should be about 45 °.In Fig. 8, decorative glass board outwards flowed out by to be allowed glue 34 by horizontal positioned.When glue 34 has been full of whole spaces, the gap of adhesive tape 31 should be sealed, and preferably uses silica gel.Glue 34 will solidify.
The stained glass jigsaw needn't cover whole decorative glass board.For example, a corporate logo in the stained glass only accounts for the whole very little part of surface glass curtain wall.Shown in Fig. 9 exploded view, such one by stained glass jigsaw 35 and around it and be in the conplane decorative sheet of being formed around plate 36, described around plate 36 promptly can be glass also can be plastics.Should on size and dimension, be fit to put into stained glass jigsaw 35 by the otch 37 that is provided around plate 36.Being not only one around plate 36, perhaps is polylith, so otch 37 may be one or more otch around plate.Stained glass jigsaw 35 and around plate 36 by one or more transparent support plate 38 and 39 (required tack coat is not illustrated in the drawings) stacked together.
In a word, although above description is very concrete, it should not be a foundation of considering the scope of the invention, and only is an example optimizing embodiment.Many kinds variations all are possible under guidance of the present invention.For example, the different combining method that can adopt, mounting block, material, size etc., unless otherwise specified.Interelement relative position is variable, and its shape is also variable.
Claims (10)
1, a kind of layered decorative glass board is characterized in that:
Comprise stained glass sheet, tamanori, back up pad and tack coat;
The stained glass sheet is placed on the predefined pattern, and forms a gap between adjacent stained glass sheet;
Tamanori is positioned in the described gap, in order to described stained glass sheet cementation is become a stained glass jigsaw;
Transparent support plate is parallel to connect first that is fixed in described stained glass jigsaw, and constructs a hollow layer with it;
A transparent bonding layer is folded between described stained glass jigsaw and the described back up pad.
2, the layered decorative glass board described in claim 1 is characterized in that: tack coat is made of the transparent resin adhesive that can insert described double sticky tape enclosed space a periphery double sticky tape and that is surrounded on described stained glass jigsaw.
3, the layered decorative glass board described in claim 1 is characterized in that: back up pad is a sheet glass in order to raising rigidity.
4, the layered decorative glass board described in claim 1 is characterized in that: back up pad is a plastic plate in order to weight reduction.
5, the layered decorative glass board described in claim 1 is characterized in that: also comprise an additional transparent back up pad, be adhered to second of described stained glass jigsaw by second tack coat.
6, the layered decorative glass board described in claim 2 is characterized in that: double sticky tape is a zona pellucida.
7, the layered decorative glass board described in claim 1, it is characterized in that: transparently offer an otch in around sheet glass at one, and described stained glass sheet put into described otch, constitute described stained glass jigsaw so that described stained glass sheet by described transparent around sheet glass institute around.
8, a kind of method of making layered decorative glass board comprises that step is as follows:
Process unicolor stained glass sheet according to predetermined sliceable shape together;
The described stained glass sheet of arranging on an interim stayed surface keeps a gap between described stained glass sheet;
Filling adhesive between the gap that constitutes between described stained glass sheet is in order to constitute a stained glass jigsaw;
Described stained glass jigsaw and a roughly the same transparent support plate are bonded together.
9, a kind of method of making layered decorative glass board described in claim 8 is characterized in that: interim stayed surface has a surface that has stickiness.
10, a kind of method of making layered decorative glass board described in claim 8, it is characterized in that: stained glass jigsaw and transparent support plate step for adhering are as follows:
Adopt a double sticky tape along first periphery of described stained glass jigsaw around laying, and leave one and fill the gap;
Place a transparent support plate on the described adhesive tape to constitute the hollow layer between a described back up pad that is bonded by adhesive tape and described stained glass jigsaw;
Tilt described stained glass jigsaw and back up pad make described filling gap up;
Transparent glue is poured into described hollow layer between described stained glass jigsaw and described back up pad;
With described decorative glass board horizontal positioned, so that described glue is outwards towards described filling Clearance Flow;
After described glue is full of filling gap in the described adhesive tape, seal described gap.