CN110205020A - A kind of automobile chassis automatically cleaning protective agent and preparation method thereof - Google Patents
A kind of automobile chassis automatically cleaning protective agent and preparation method thereof Download PDFInfo
- Publication number
- CN110205020A CN110205020A CN201910458152.9A CN201910458152A CN110205020A CN 110205020 A CN110205020 A CN 110205020A CN 201910458152 A CN201910458152 A CN 201910458152A CN 110205020 A CN110205020 A CN 110205020A
- Authority
- CN
- China
- Prior art keywords
- parts
- silane
- automobile chassis
- added
- automatically cleaning
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to cleaning material technical fields, specially a kind of protectant preparation method of automobile chassis automatically cleaning, it is made of following substance according to mass fraction: 8 parts ~ 12 parts of trimethoxy silane, 1 part ~ 3 parts of methyltriethoxysilane, 3 parts ~ 5 parts of hexadecyl trimethoxy silane, 1 part ~ 3 parts of octadecyl methyl diethoxy silane, 10 parts ~ 20 parts of alkoxysilane polymer, 6 parts ~ 13 parts of silane compound, 8 parts ~ 20 parts of perfluorooctane sulfonate, 60 parts ~ 75 parts of D40 solvent, 5 parts ~ 10 parts of ethyl acetate, 5 parts ~ 10 parts of ethyl alcohol, 5 parts ~ 10 parts of tetrabutyl titanate ester, 1 part ~ 3 parts of triethanolamine, 0.2 part ~ 3 parts of organotin, above each material mixing reacts to obtain product.A kind of automobile chassis automatically cleaning protective agent provided by the invention and preparation method thereof, is sprayed on automobile chassis, water can not only be prevented to enter in chassis, prevent from corroding, moreover it is possible to prevent muddy water to be stained on chassis, bottom is kept to clean drying.
Description
Technical field
The invention belongs to cleaning material technical field, specially a kind of protectant preparation method of automobile chassis automatically cleaning.
Background technique
Automobile chassis generally all can anti-corrosion disposition, but this coating is also as just preventing corrosion function, once mud
Water is stained on chassis for a long time, and still gradually penetrating into chassis will cause corrosion, and influences automobile beauty.
Summary of the invention
In view of the above technical problems, the present invention provides a kind of automobile chassis automatically cleaning protective agent and preparation method thereof, not only
Have the function of anti-corrosion, can prevent muddy water from adsorbing with self-cleaning.
The specific technical proposal is:
A kind of automobile chassis automatically cleaning protective agent is made of following substance according to mass fraction: 8 parts ~ 12 parts of trimethoxy silane,
1 part ~ 3 parts of methyltriethoxysilane, 3 parts ~ 5 parts of hexadecyl trimethoxy silane, octadecyl methyl diethoxy silane 1
Part ~ 3 parts, 10 parts ~ 20 parts of alkoxysilane polymer, 6 parts ~ 13 parts of silane compound, 8 parts ~ 20 parts of perfluorooctane sulfonate, D40
60 parts ~ 75 parts of solvent, 5 parts ~ 10 parts of ethyl acetate, 5 parts ~ 10 parts of ethyl alcohol, 5 parts ~ 10 parts of tetrabutyl titanate ester, 1 part of triethanolamine ~
3 parts, 0.2 part ~ 3 parts of organotin.
Wherein, the organotin is one or two kinds of mixing in dibutyl tin dilaurate or isooctyl acid tin.
A kind of protectant preparation method of automobile chassis automatically cleaning, comprising the following steps:
(1) D40 solvent, ethyl acetate, ethyl alcohol is first added, is uniformly mixed, then sequentially adds trimethoxy silane, methyl three
Ethoxysilane stirs half an hour；
(2) hexadecyl trimethoxy silane, octadecyl methyl diethoxy silane, alkoxysilane polymer are added,
It stirs 45 minutes；
(3) silane compound, perfluorooctane sulfonate are added, half an hour is stirred；
(4) tetrabutyl titanate ester, triethanolamine are added, is stirred ten minutes；
(5) organotin is added, stirs 20 minutes, finally comes out of the stove.
A kind of automobile chassis automatically cleaning protective agent provided by the invention and preparation method thereof, is sprayed on automobile chassis, no
It is only capable of that water is prevented to enter in chassis, prevents from corroding, moreover it is possible to prevent muddy water to be stained on chassis, bottom is kept to clean drying.
Specific embodiment
It is described in conjunction with the embodiments the specific technical solution of the present invention.
Embodiment 1
A kind of automobile chassis automatically cleaning protective agent is made of following substance according to mass fraction: 10 parts of trimethoxy silane, methyl
2.3 parts of triethoxysilane, 4.7 parts of hexadecyl trimethoxy silane, 2.4 parts of octadecyl methyl diethoxy silane, alkane
14 parts of oxysilane polymer, 12 parts of silane compound, 10 parts of perfluorooctane sulfonate, 68 parts of D40 solvent, 9 parts of ethyl acetate, second
6 parts of alcohol, 10 parts of tetrabutyl titanate ester, 2 parts of triethanolamine, 2.5 parts of organotin, 68 parts of D40 solvent.
Wherein, the organotin is one or two kinds of mixing in dibutyl tin dilaurate or isooctyl acid tin.
The protectant preparation method of automobile chassis automatically cleaning, comprising the following steps:
(1) D40 solvent, ethyl acetate, ethyl alcohol is first added, is uniformly mixed, then sequentially adds trimethoxy silane, methyl three
Ethoxysilane stirs half an hour；
(2) hexadecyl trimethoxy silane, octadecyl methyl diethoxy silane, alkoxysilane polymer are added,
It stirs 45 minutes；
(3) silane compound, perfluorooctane sulfonate are added, half an hour is stirred；
(4) tetrabutyl titanate ester, triethanolamine are added, is stirred ten minutes；
(5) organotin is added, stirs 20 minutes, finally comes out of the stove.
Embodiment 2
A kind of automobile chassis automatically cleaning protective agent is made of following substance according to mass fraction: 8 parts ~ 12 parts of trimethoxy silane,
3 parts of methyltriethoxysilane, 3.5 parts of hexadecyl trimethoxy silane, 1.7 parts of octadecyl methyl diethoxy silane,
12 parts of alkoxysilane polymer, 11 parts of silane compound, 10 parts of perfluorooctane sulfonate, 75 parts of D40 solvent, 8 parts of ethyl acetate,
6 parts of ethyl alcohol, 9 parts of tetrabutyl titanate ester, 2 parts of triethanolamine, 2 parts of organotin.
Wherein, the organotin is isooctyl acid tin.
The protectant preparation method of automobile chassis automatically cleaning, comprising the following steps:
(1) D40 solvent, ethyl acetate, ethyl alcohol is first added, is uniformly mixed, then sequentially adds trimethoxy silane, methyl three
Ethoxysilane stirs half an hour；
(2) hexadecyl trimethoxy silane, octadecyl methyl diethoxy silane, alkoxysilane polymer are added,
It stirs 45 minutes；
(3) silane compound, perfluorooctane sulfonate are added, half an hour is stirred；
(4) tetrabutyl titanate ester, triethanolamine are added, is stirred ten minutes；
(5) organotin is added, stirs 20 minutes, finally comes out of the stove.
Embodiment 3
A kind of automobile chassis automatically cleaning protective agent is made of following substance according to mass fraction: 12 parts of trimethoxy silane, methyl
1 part of triethoxysilane, 4 parts of hexadecyl trimethoxy silane, 1.7 parts of octadecyl methyl diethoxy silane, alkoxy
15 parts of silane polymer, 7 parts of silane compound, 15 parts of perfluorooctane sulfonate, 65 parts of D40 solvent, 7 parts of ethyl acetate, ethyl alcohol 8
Part, 9 parts of tetrabutyl titanate ester, 2 parts of triethanolamine, 3 parts of organotin.
Wherein, the organotin is dibutyl tin dilaurate, isooctyl acid tin, respectively accounts for half.
The protectant preparation method of automobile chassis automatically cleaning, comprising the following steps:
(1) D40 solvent, ethyl acetate, ethyl alcohol is first added, is uniformly mixed, then sequentially adds trimethoxy silane, methyl three
Ethoxysilane stirs half an hour；
(2) hexadecyl trimethoxy silane, octadecyl methyl diethoxy silane, alkoxysilane polymer are added,
It stirs 45 minutes；
(3) silane compound, perfluorooctane sulfonate are added, half an hour is stirred；
(4) tetrabutyl titanate ester, triethanolamine are added, is stirred ten minutes；
(5) organotin is added, stirs 20 minutes, finally comes out of the stove.
Claims (3)
1. a kind of automobile chassis automatically cleaning protective agent, which is characterized in that be made of following substance according to mass fraction: trimethoxy
8 parts ~ 12 parts of silane, 1 part ~ 3 parts of methyltriethoxysilane, 3 parts ~ 5 parts of hexadecyl trimethoxy silane, octadecyl methyl
1 part ~ 3 parts of diethoxy silane, 10 parts ~ 20 parts of alkoxysilane polymer, 6 parts ~ 13 parts of silane compound, perfluorooctane sulfonate
8 parts ~ 20 parts, 60 parts ~ 75 parts of D40 solvent, 5 parts ~ 10 parts of ethyl acetate, 5 parts ~ 10 parts of ethyl alcohol, 5 parts ~ 10 parts of tetrabutyl titanate ester,
1 part ~ 3 parts of triethanolamine, 0.2 part ~ 3 parts of organotin.
2. a kind of automobile chassis automatically cleaning protective agent according to claim 1, which is characterized in that the organotin is two
One or two kinds of mixing in dibutyl tin laurate or isooctyl acid tin.
3. a kind of protectant preparation method of automobile chassis automatically cleaning according to claim 1 or 2, which is characterized in that packet
Include following steps:
(1) D40 solvent, ethyl acetate, ethyl alcohol is first added, is uniformly mixed, then sequentially adds trimethoxy silane, methyl three
Ethoxysilane stirs half an hour；
(2) hexadecyl trimethoxy silane, octadecyl methyl diethoxy silane, alkoxysilane polymer are added,
It stirs 45 minutes；
(3) silane compound, perfluorooctane sulfonate are added, half an hour is stirred；
(4) tetrabutyl titanate ester, triethanolamine are added, is stirred ten minutes；
(5) organotin is added, stirs 20 minutes, finally comes out of the stove.