CN108611924A - A kind of environment protection three-dimensional answers the production method of line wrapping paper - Google Patents
A kind of environment protection three-dimensional answers the production method of line wrapping paper Download PDFInfo
- Publication number
- CN108611924A CN108611924A CN201810318734.2A CN201810318734A CN108611924A CN 108611924 A CN108611924 A CN 108611924A CN 201810318734 A CN201810318734 A CN 201810318734A CN 108611924 A CN108611924 A CN 108611924A
- Authority
- CN
- China
- Prior art keywords
- parts
- paper
- mixture
- agent
- wrapping paper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses the production methods that a kind of environment protection three-dimensional answers line wrapping paper, specifically comprise the following steps：S1：5 10 parts of 100 150 parts of biodegradable bamboo fibre, 20 30 parts of starch, 5 10 parts of rosin size, 10 20 parts of talcum powder and titanium dioxide is taken to be put into mixing and blending machine and be stirred, time is 20 30 minutes, by the mixture after stirring by obtaining raw mixture after strainer filtering impurity；S2：Raw mixture is put into precipitation vessel and is precipitated, and 13 parts of 35 parts of wet strength agent, 35 parts of drying strengthening agent, 35 parts of retention agent, 13 parts of turpentine oil and paraffin is added, then the raw mixture in precipitation vessel is stirred using paddle stirrer, obtains pulp mixture.The present invention by turpentine oil and paraffin by being mixed in raw mixture, it is stirred using paddle stirrer, so that it is carried out hybrid reaction with the paper pulp raw material ingredient in raw mixture, effectively eliminates the foam in paper-making process, while improving the water resistant ability of finished product packing paper.
Description
Technical field
The present invention relates to gift wrap product technical field, more particularly to a kind of environment protection three-dimensional answers the producer of line wrapping paper
Method.
Background technology
Wrapping paper is a kind of common utilization packaging material, and wrapping paper generally all carries the decorative pattern of printing at present.But by
It is too simple single in the manufacture craft and making raw material of these wrapping papers, cause to use and feel cheap, texture is low, water resistant
Energy force difference, surface strength are low.
Therefore, it is necessary to solve the above problems to invent a kind of production method that environment protection three-dimensional answers line wrapping paper.
Invention content
The purpose of the present invention is to provide the production methods that a kind of environment protection three-dimensional answers line wrapping paper, by using polyethyleneimine
The mixture of amine and polypropylene amine is used as retention agent and adds a small amount of titanium dioxide cooperation talcum powder in paper pulp raw material serving as
Inorganic filler, which is used with to solve traditional wrapping paper, feels cheap, the low and ropy problem of texture.
To achieve the above object, the present invention provides the following technical solutions：A kind of environment protection three-dimensional answers the producer of line wrapping paper
Method specifically comprises the following steps：
S1：Take 100-150 parts of biodegradable bamboo fibre, 20-30 parts of starch, 5-10 parts of rosin size, talcum powder 10-20
5-10 parts of part and titanium dioxide, which are put into mixing and blending machine, to be stirred, and the time is 20-30 minutes, and the mixture after stirring is passed through
Raw mixture is obtained after strainer filtering impurity；
S2：Raw mixture is put into precipitation vessel and is precipitated, and be added 3-5 parts of wet strength agent, 3-5 parts of drying strengthening agent,
Then 1-3 parts of 3-5 parts of retention agent, 1-3 parts of turpentine oil and paraffin utilize paddle stirrer to the raw mixture in precipitation vessel
It is stirred, obtains pulp mixture；
S3：Pulp mixture is poured into head box, and it is diluted, the paper pulp after dilution is then passed through into pipe
Road is equably sprayed on forming net, will be put into room temperature for 25-30 DEG C topped with the forming net of paper pulp and is carried out in the environment of divulging information
Solarization is dried in the air, and online moisture to be formed obtains l Water Paper when dropping to 5-15wt%；
S4：L Water Paper on forming net is removed, it is squeezed using pressure roller, the l Water Paper after extruding is uniformly pasted
On the surface of drying cylinder, dried；
S5：Paper after drying is carried out to colouring and the compacting line in molding machine successively, is then rolled into big volume, and utilize
Paper cutter is sliced it to corresponding size, and finished product is obtained.
Preferably, the environment protection three-dimensional answers raw material and shared mass percent used in line wrapping paper and is：Biology can
It degrades 100-150 parts of bamboo fibre, 20-30 parts of starch, 5-10 parts of rosin size, 10-20 parts of talcum powder, 5-10 parts of titanium dioxide, wet
1-3 parts of strong 3-5 parts of agent, 3-5 parts of drying strengthening agent, 3-5 parts of retention agent, 1-3 parts of turpentine oil and paraffin.
Preferably, content of magnesia is 30wt% in the talcum powder, and particle mesh number is 1000-1200 mesh, silica
Content is 60wt%.
Preferably, the content of titanium dioxide is more than 97wt% in the titanium dioxide, and the biodegradable bamboo fibre is short
Fiber.
Preferably, the wet strength agent is phenolic resin, and the drying strengthening agent is polyacrylamide, and the retention agent is polyethylene
The mixture of imines and polypropylene amine.
Preferably, in the S1, the rotating speed of mixing and blending machine is 40-50 revs/min, and in the S2, paddle stirrer turns
Speed is 80-100 revs/min.
Preferably, in the S3, it is 8-12 hours to shine the time of drying in the air, pulp density 0.8.
The technique effect and advantage of the present invention：
1, coordinate talcum powder to serve as inorganic filler by adding a small amount of titanium dioxide in paper pulp raw material, improve packaging
The surface smoothness of paper makes paper internal voids become smaller and attenuates；
2, wet strength agent is used as using phenolic resin, the wet strength of wrapping paper is enhanced, using polyethyleneimine and polypropylene
The mixture of amine is used as retention agent, reduces the loss of filler and fiber fines in paper-making process, improves the quality of wrapping paper；
3, turpentine oil and paraffin are mixed in raw mixture, it is stirred using paddle stirrer, makes itself and original
Expect that the paper pulp raw material ingredient in mixture carries out hybrid reaction, has effectively eliminated the foam in paper-making process, improved simultaneously
The water resistant ability of finished product packing paper；
4, starch and rosin size are added in the feed and is used as sizing material, and to the raw materials such as itself and biodegradable bamboo fibre into
Row stirring, further enhances the water resistant ability of wrapping paper, and improve its surface strength and anti-friction ability, reduces paper
Hair loss phenomenon in forming process improves the aesthetics and texture of product；
5, present invention process is simple, and equipment requirement is low, and operability is strong, has good society generalization application.
Specific implementation mode
The technical scheme in the embodiments of the invention will be clearly and completely described below, it is clear that described implementation
Example is only a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, this field is common
The every other embodiment that technical staff is obtained without making creative work belongs to the model that the present invention protects
It encloses.
Embodiment 1：
A kind of environment protection three-dimensional answers the production method of line wrapping paper, specifically comprises the following steps：
S1：Take 5 parts of 100 parts of biodegradable bamboo fibre, 20 parts of starch, 5 parts of rosin size, 10 parts of talcum powder and titanium dioxide
It is put into mixing and blending machine and is stirred, rotating speed is 40 revs/min, and the time is 20 minutes, and the mixture after stirring is passed through strainer
Raw mixture is obtained after impurity screening；
S2：Raw mixture is put into precipitation vessel and is precipitated, and 3 parts of wet strength agent, 3 parts of drying strengthening agent, retention is added
1 part of 3 parts of agent, 1 part of turpentine oil and paraffin, are then stirred the raw mixture in precipitation vessel using paddle stirrer,
Rotating speed is 80 revs/min, obtains pulp mixture；
S3：Pulp mixture is poured into head box, and pulp density is diluted to 0.8, then by the paper after dilution
Slurry is equably sprayed on forming net by pipeline, will be put into room temperature for 25 DEG C and in the environment of divulging information topped with the forming net of paper pulp
Shine and dry in the air, it is 8 hours to shine the time of drying in the air, and online moisture to be formed obtains l Water Paper when dropping to 5wt%；
S4：L Water Paper on forming net is removed, it is squeezed using pressure roller, the l Water Paper after extruding is uniformly pasted
On the surface of drying cylinder, dried；
S5：Paper after drying is carried out to colouring and the compacting line in molding machine successively, is then rolled into big volume, and utilize
Paper cutter is sliced it to corresponding size, and finished product is obtained.
The environment protection three-dimensional answers raw material and shared mass percent used in line wrapping paper：Biodegradable bamboo is fine
100 parts of dimension, 20 parts of starch, 5 parts of rosin size, 10 parts of talcum powder, 5 parts of titanium dioxide, 3 parts of wet strength agent, 3 parts of drying strengthening agent, retention agent 3
1 part of part, 1 part of turpentine oil and paraffin.
In the talcum powder content of magnesia be 30wt%, particle mesh number be 1000 mesh, dioxide-containing silica 60wt%,
The content of titanium dioxide is more than 97wt% in the titanium dioxide, and the biodegradable bamboo fibre is staple fiber, the wet strength agent
For phenolic resin, the drying strengthening agent is polyacrylamide, and the retention agent is the mixture of polyethyleneimine and polypropylene amine.
Subordinate list 1
Embodiment 2：
A kind of environment protection three-dimensional answers the production method of line wrapping paper, specifically comprises the following steps：
S1：Take 150 parts of biodegradable bamboo fibre, 30 parts of starch, 10 parts of rosin size, 20 parts of talcum powder and titanium dioxide 10
Part, which is put into mixing and blending machine, to be stirred, and rotating speed is 50 revs/min, and the time is 30 minutes, and the mixture after stirring is passed through filter
Raw mixture is obtained after net filtration impurity；
S2：Raw mixture is put into precipitation vessel and is precipitated, and 5 parts of wet strength agent, 5 parts of drying strengthening agent, retention is added
3 parts of 5 parts of agent, 3 parts of turpentine oil and paraffin, are then stirred the raw mixture in precipitation vessel using paddle stirrer,
Rotating speed is 100 revs/min, obtains pulp mixture；
S3：Pulp mixture is poured into head box, and pulp density is diluted to 0.8, then by the paper after dilution
Slurry is equably sprayed on forming net by pipeline, will be put into room temperature for 30 DEG C and in the environment of divulging information topped with the forming net of paper pulp
Shine and dry in the air, it is 12 hours to shine the time of drying in the air, and online moisture to be formed obtains l Water Paper when dropping to 15wt%；
S4：L Water Paper on forming net is removed, it is squeezed using pressure roller, the l Water Paper after extruding is uniformly pasted
On the surface of drying cylinder, dried；
S5：Paper after drying is carried out to colouring and the compacting line in molding machine successively, is then rolled into big volume, and utilize
Paper cutter is sliced it to corresponding size, and finished product is obtained.
The environment protection three-dimensional answers raw material and shared mass percent used in line wrapping paper：Biodegradable bamboo is fine
150 parts of dimension, 30 parts of starch, 10 parts of rosin size, 20 parts of talcum powder, 10 parts of titanium dioxide, 5 parts of wet strength agent, 5 parts of drying strengthening agent, retention
3 parts of 5 parts of agent, 3 parts of turpentine oil and paraffin.
In the talcum powder content of magnesia be 30wt%, particle mesh number be 1200 mesh, dioxide-containing silica 60wt%,
The content of titanium dioxide is more than 97wt% in the titanium dioxide, and the biodegradable bamboo fibre is staple fiber, the wet strength agent
For phenolic resin, the drying strengthening agent is polyacrylamide, and the retention agent is the mixture of polyethyleneimine and polypropylene amine.
Subordinate list 2
Embodiment 3：
A kind of environment protection three-dimensional answers the production method of line wrapping paper, specifically comprises the following steps：
S1：Take 8 parts of 130 parts of biodegradable bamboo fibre, 25 parts of starch, 8 parts of rosin size, 15 parts of talcum powder and titanium dioxide
It is put into mixing and blending machine and is stirred, rotating speed is 45 revs/min, and the time is 25 minutes, and the mixture after stirring is passed through strainer
Raw mixture is obtained after impurity screening；
S2：Raw mixture is put into precipitation vessel and is precipitated, and 4 parts of wet strength agent, 4 parts of drying strengthening agent, retention is added
2 parts of 4 parts of agent, 2 parts of turpentine oil and paraffin, are then stirred the raw mixture in precipitation vessel using paddle stirrer,
Rotating speed is 90 revs/min, obtains pulp mixture；
S3：Pulp mixture is poured into head box, and pulp density is diluted to 0.8, then by the paper after dilution
Slurry is equably sprayed on forming net by pipeline, will be put into room temperature for 28 DEG C and in the environment of divulging information topped with the forming net of paper pulp
Shine and dry in the air, it is 10 hours to shine the time of drying in the air, and online moisture to be formed obtains l Water Paper when dropping to 10wt%；
S4：L Water Paper on forming net is removed, it is squeezed using pressure roller, the l Water Paper after extruding is uniformly pasted
On the surface of drying cylinder, dried；
S5：Paper after drying is carried out to colouring and the compacting line in molding machine successively, is then rolled into big volume, and utilize
Paper cutter is sliced it to corresponding size, and finished product is obtained.
The environment protection three-dimensional answers raw material and shared mass percent used in line wrapping paper：Biodegradable bamboo is fine
130 parts of dimension, 25 parts of starch, 8 parts of rosin size, 15 parts of talcum powder, 8 parts of titanium dioxide, 4 parts of wet strength agent, 4 parts of drying strengthening agent, retention agent 4
2 parts of part, 2 parts of turpentine oil and paraffin.
In the talcum powder content of magnesia be 30wt%, particle mesh number be 1100 mesh, dioxide-containing silica 60wt%,
The content of titanium dioxide is more than 97wt% in the titanium dioxide, and the biodegradable bamboo fibre is staple fiber, the wet strength agent
For phenolic resin, the drying strengthening agent is polyacrylamide, and the retention agent is the mixture of polyethyleneimine and polypropylene amine.
Subordinate list 3
It can be obtained according to embodiment 1-3
Subordinate list 4
Three kinds of environment protection three-dimensionals can be obtained by above three groups of embodiments and answer line wrapping paper, these three environment protection three-dimensionals are answered into line
Wrapping paper is tested for the property respectively, then carries out soak test with the wrapping paper Jing Guo common process, as a result obtains three groups of implementations
Environment protection three-dimensional in example, which answers line wrapping paper, different promotions, and the effect that ability is impregnated wherein in embodiment 2 is best, and value is most
Height, the present invention coordinate talcum powder to serve as inorganic filler, improve packaging by adding a small amount of titanium dioxide in paper pulp raw material
The surface smoothness of paper makes paper internal voids become smaller and attenuates, and is used as wet strength agent using phenolic resin, enhances the wet of wrapping paper
Intensity is used as retention agent using the mixture of polyethyleneimine and polypropylene amine, reduces filler and fiber fines in paper-making process
Loss, improve the quality of wrapping paper, turpentine oil and paraffin be mixed in raw mixture, using paddle stirrer to its into
Row stirring, makes it carry out hybrid reaction with the paper pulp raw material ingredient in raw mixture, has effectively eliminated in paper-making process
Foam, while the water resistant ability of finished product packing paper is improved, starch is added in the feed and rosin size is used as sizing material, and to it
It is stirred with raw materials such as biodegradable bamboo fibres, further enhances the water resistant ability of wrapping paper, and improve its surface
Intensity and anti-friction ability reduce hair loss phenomenon of the paper in forming process.
Finally it should be noted that：The foregoing is only a preferred embodiment of the present invention, is not intended to restrict the invention,
Although the present invention is described in detail referring to the foregoing embodiments, for those skilled in the art, still may be used
With technical scheme described in the above embodiments is modified or equivalent replacement of some of the technical features,
All within the spirits and principles of the present invention, any modification, equivalent replacement, improvement and so on should be included in the present invention's
Within protection domain.
Claims (7)
1. a kind of environment protection three-dimensional answers the production method of line wrapping paper, which is characterized in that specifically comprise the following steps：
S1：Take 100-150 parts of biodegradable bamboo fibre, 20-30 parts of starch, 5-10 parts of rosin size, 10-20 parts of talcum powder and
5-10 parts of titanium dioxide, which is put into mixing and blending machine, to be stirred, and the time is 20-30 minutes, and the mixture after stirring is passed through strainer
Raw mixture is obtained after impurity screening；
S2：Raw mixture is put into precipitation vessel and is precipitated, and 3-5 parts of wet strength agent, 3-5 parts of drying strengthening agent, retention is added
Then 1-3 parts of 3-5 parts of agent, 1-3 parts of turpentine oil and paraffin carry out the raw mixture in precipitation vessel using paddle stirrer
Stirring, obtains pulp mixture；
S3：Pulp mixture is poured into head box, and it is diluted, it is then that the paper pulp after dilution is equal by pipeline
It is sprayed on forming net, dries in the air being put into room temperature for 25-30 DEG C topped with the forming net of paper pulp and in the environment of divulging information shine evenly,
Online moisture to be formed obtains l Water Paper when dropping to 5-15wt%；
S4：L Water Paper on forming net is removed, it is squeezed using pressure roller, the l Water Paper after extruding is uniformly attached to baking
The surface of cylinder, is dried；
S5：Paper after drying is carried out to colouring and the compacting line in molding machine successively, is then rolled into big volume, and utilize cut paper
Machine is sliced it to corresponding size, and finished product is obtained.
2. a kind of environment protection three-dimensional according to claim 1 answers the production method of line wrapping paper, it is characterised in that：The environmental protection
Raw material and shared mass percent used in the multiple line wrapping paper of solid are：100-150 parts of biodegradable bamboo fibre, starch
20-30 parts, 5-10 parts of rosin size, 10-20 parts of talcum powder, 5-10 parts of titanium dioxide, 3-5 parts of wet strength agent, 3-5 parts of drying strengthening agent, help
Stay 1-3 parts of 3-5 parts of agent, 1-3 parts of turpentine oil and paraffin.
3. a kind of environment protection three-dimensional according to claim 1 answers the production method of line wrapping paper, it is characterised in that：The talcum
Content of magnesia is 30wt% in powder, and particle mesh number is 1000-1200 mesh, dioxide-containing silica 60wt%.
4. a kind of environment protection three-dimensional according to claim 1 answers the production method of line wrapping paper, it is characterised in that：The titanium white
The content of titanium dioxide is more than 97wt% in powder, and the biodegradable bamboo fibre is staple fiber.
5. a kind of environment protection three-dimensional according to claim 1 answers the production method of line wrapping paper, it is characterised in that：It is described wet strong
Agent is phenolic resin, and the drying strengthening agent is polyacrylamide, and the retention agent is the mixture of polyethyleneimine and polypropylene amine.
6. a kind of environment protection three-dimensional according to claim 5 answers the production method of line wrapping paper, it is characterised in that：The S1
In, the rotating speed of mixing and blending machine is 40-50 revs/min, and in the S2, the rotating speed of paddle stirrer is 80-100 revs/min.
7. a kind of environment protection three-dimensional according to claim 5 answers the production method of line wrapping paper, it is characterised in that：The S3
In, it is 8-12 hours to shine the time of drying in the air, pulp density 0.8.