CN1076161A - Imitative silicon rubber statue and manufacture method thereof - Google Patents
Imitative silicon rubber statue and manufacture method thereof Download PDFInfo
- Publication number
- CN1076161A CN1076161A CN 92113608 CN92113608A CN1076161A CN 1076161 A CN1076161 A CN 1076161A CN 92113608 CN92113608 CN 92113608 CN 92113608 A CN92113608 A CN 92113608A CN 1076161 A CN1076161 A CN 1076161A
- Authority
- CN
- China
- Prior art keywords
- silicon rubber
- statue
- gypsum
- composite bed
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention constitutes hollow artificial figure statue profile layer by silicon rubber, and bonding fiber cloth composite bed is arranged in the profile layer, and bonding fiberglass internal layer is arranged on the composite bed.Manufacture method is included in and turns over silicon rubber external mold that support is arranged of system on the clay figure; On external mold, turn over the system simulation waxen figure; On waxen imagen, cast gypsum mold; After the dewaxing gypsum mold being put into baking oven toasts; To mix up look, the silicon rubber that adds glue crosslinking agent is poured constantly rocking-turn in the gypsum mold into, up to curing; Binder fibre cloth composite bed in the silicon rubber statue; Bonding fiberglass internal layer on composite bed; Remove the gypsum shell after waiting to solidify, eyes are installed, insert hair, beauty is handled.
Description
The present invention is with relevant as the artificial figure carving handicraft product and the manufacture method thereof of main material with silicon rubber.
Traditional artificial figure statue all is to make with cured or animi resin material, although also all give sense true to nature in appearance, a lot of shortcomings is arranged also.The strict temperature environment of preservation that adds cured picture, otherwise easily cold cracking or thermal deformation; Intensity, the hardness of cured picture are very poor, very easily damage, and it is very inconvenient to transport, manage, and is of limited application.Traditional artificial figure statue does not have the emulation sense of touch.
The purpose of this invention is to provide a kind of applied range, combination property is strong, especially has the higher sense of reality, is convenient to the artificial figure statue that transports and safeguard.
Another object of the present invention provides the process that a kind of production has the artificial figure statue of These characteristics.
The present invention is achieved in that
The present invention constitutes hollow artificial figure statue profile layer by silicon rubber.The fiberglass internal layer that combines is arranged in the profile layer.
Silicon has bonding fiber cloth composite bed as interlayer in glue profile layer and the fiberglass.
Figure statue eye frame of the present invention is the cavity, and its edge has only silastic-layer, and artificial eye is bonded in the frame internally by silicon rubber.
Fiber cloth composite bed of the present invention can be cotton or the fiber crops or the glass fibre layer of cloth of silicon rubber bonding, and composite bed and fiberglass internal layer bonding place are exposed fiber cloth.
The present invention includes human head picture, body, four limbs and human body.
Manufacture method of the present invention comprises following processing step:
1. mould atrichous human head picture with mud or plasticine, body or four limbs are got to be compressed on behind the natural dermatoglyph by silicon rubber again and are made dermatoglyph on the statue.
2. silicon rubber mould of the system of on statue, turning over support outside gypsum or the fiberglass work.Promptly on statue, turn over the silicon rubber external mold of an integral body of system earlier, on the silicon rubber external mold, mould the plaster block mould as support.Get the plaster block mould during delivery earlier, cut at the unshowy place of silicon rubber external mold then, its taking-up.Silicon rubber external mold and plaster block mould are reconfigured.Because silicon rubber external mold score is very little, the cured picture that turns over system does not almost have vestige.
3. in silicon rubber mould, turn over cured picture of emulation of system.
4. on the cured picture of the emulation that trims, cast gypsum, make the back and place more than 24 hours again that row takes off cured.
5. dash to scald to take off with steam or boiling water and gypsum mold was put into baking oven roasting 2-6 hour after cured, temperature is 90-180 ℃.
6. transferred pigment such as oil colour or multiple pigment powder in silicon rubber.Make its tone that reaches the required colour of skin, leave standstill a few hours fully to eliminate bubble.
7. in mixing up the silicon rubber of look, add the tetraethoxysilance of its heavy 4-6%, be the dibutyl tin laurate of its weight 0.4-0.8%, pour in the gypsum mold constantly rocking-turn mould after mixing evenly immediately into, glue is evenly distributed, until not flowing.One time became uneven is even, teeming once more.For the intensity that increases the profile layer can add the silastic-layer that one or more layers accompanies fiber cloth, the statue gross thickness is advisable at 1-1.5cm.
8. several layers of resin of silicon rubber shell inner chamber brush and the glass fabric behind the glue connection made fiberglass and supported inner layer case.Treat to beat the gypsum shell behind the resin solidification.
9. dig out the position of placing artificial eye at statue eyes place with scraper, it is fixing from the outside with gypsum that the back is laid, adjusted to artificial eye from inner chamber, and recycle silicon rubber is fixed from inner chamber.After removing gypsum, repair perfect with silicon rubber.
10. have the acupuncture of fork to plug in the instrument of sending out with the tip hair of choosing is inserted the position that statue becomes mildewed and sends out, needling direction should be the hair growth direction.The plug in instrument of sending out can insert little rod with tiny sewing-needle, cut off backshank from the through wires hole middle part, grinds to form.
Oil colour and cosmetic look are connect the color difference of each position skin of personage with soft fabric, and branch gently rubs on statue, makes it have color effect as the true personage, at last by the grease glazing, strengthens the skin moistened sense.
The present invention has overcome the traditional simulation figure statue shortcomings such as heat, easily cracked, yielding, no touch emulation sense of being afraid of cold.Shift portrait emulation sculpture level onto new height.The present invention has the touch sense of emulation, and lifelike image reaches the effect of mixing the spurious with the genuine.Higher intensity is arranged, be convenient to transportation and maintenance, can make an itinerant exhibition.Have wide range of applications, both can replace the cured picture of traditional emulation, can be used as the high fashion model again, movie prop, teaching mode, the setoff showpiece of tourist attractions etc.
Fig. 1 is a structural map of the present invention.
1-silicon rubber profile layer,
2-fiber cloth composite bed,
3-fiberglass internal layer,
The 4-artificial eye,
5-silicon rubber tack coat,
The 6-hair.
Claims (5)
1, imitative silicon rubber statue is characterized in that a silicon rubber and lining material make, and silicon rubber constitutes hollow figure statue profile layer, and the fiberglass internal layer that combines is arranged in the profile layer.
2, imitative silicon rubber statue according to claim 1 is characterized in that interlayer has bonding fiber cloth composite bed in silicon rubber profile layer and the fiberglass.
3, imitative silicon rubber statue according to claim 1 and 2 is characterized in that statue eye frame is the cavity, and its edge has only silastic-layer, and artificial eye is bonded in the frame internally by silicon rubber.
4, imitative silicon rubber statue according to claim 2 is characterized in that the fiber cloth composite bed can be cotton or the fiber crops or the glass fibre layer of cloth of silicon rubber bonding, and composite bed and fiberglass internal layer bonding place are exposed fiber cloth.
5, the manufacture method of the imitative silicon rubber statue in described according to claim 1 comprises following processing step:
1.. mould atrichous portrait with mud or plasticine, human body formula four limbs are got to be compressed on behind the natural dermatoglyph by silicon rubber again and are made dermatoglyph on the statue.
2.. silicon rubber mould of the system of on statue, turning over support outside gypsum or the fiberglass work.
3.. in silicon rubber mould, turn over cured picture of emulation of system.
4.. on the cured picture of the emulation that trims, cast plaster shell, make the back place take off again more than 24 hours cured,
5.. dash to scald to take off with steam or boiling water and plaster mold was put into baking oven roasting 2-6 hour after cured, temperature is 90 °-180 ℃.
6.. transferred pigment makes its tone that reaches the required colour of skin in silicon rubber, leave standstill a few hours fully to eliminate bubble,
7.. the positive silicic acid second that adds its weight 4-6% at the silicon rubber that mixes up look cured, the dibutyl tin laurate of 0.4-0.8%, pour continuous rocking-turn mould in the gypsum mold after mixing evenly immediately into, glue is evenly distributed, until not flowing, can add the silicon rubber composite bed that one or more layers accompanies fiber cloth for gaining in strength
8.. silicon rubber shell inner chamber brushing number layer resin and glass fabric behind the glue connection, make the fiberglass support shell.Can beat the gypsum shell behind the resin solidification,
9.. dig out the position of placing artificial eye at statue eyes place with scraper, artificial eye is laid from inner chamber, adjusts the back and is fixed from the outside with gypsum, and recycle silicon rubber is fixed from inner chamber, remove gypsum after, repair perfect with silicon rubber.
10.. have the acupuncture of fork to plug in the instrument of sending out with the tip hair of choosing is thrust the position that statue becomes mildewed and sends out, being needled into direction should be the hair growth direction.
(11). with the heterochromia of soft fabric by each position skin of personage, branch gently rubs on statue with oil colour and cosmetic look, makes it have color effect as the true personage, at last by the grease glazing, strengthens the skin moistened sense.
(12). the body of giving sb. a hard time can be by the human head picture of making respectively, body, four limbs in conjunction with or be bonded.