CN107601963A - Light glazed tile - Google Patents
Light glazed tile Download PDFInfo
- Publication number
- CN107601963A CN107601963A CN201710890837.1A CN201710890837A CN107601963A CN 107601963 A CN107601963 A CN 107601963A CN 201710890837 A CN201710890837 A CN 201710890837A CN 107601963 A CN107601963 A CN 107601963A
- Authority
- CN
- China
- Prior art keywords
- resin
- colorant
- triethanolamine
- glazed tile
- magnesium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of light glazed tile, glazed tiles are in the form of sheets, it is made up of some crests being sequentially connected or trough, glazed tiles are made up of top layer and bottom, top layer is made up of modified resin and the hydrophobic layer being positioned above, bottom is made up of magnesium chloride, magnesium silicate, resin, ammonium chloride, triethanolamine and colorant, and magnesium chloride, magnesium silicate, resin, ammonium chloride, the mass ratio of triethanolamine and colorant are 45 65:25‑35:20‑40:10‑20:1‑10:6‑15.Smooth clean and tidy, bright in colour beautiful, the light weight in light glazed tile surface of the present invention, waterproof, cost are low.
Description
Technical field
The present invention relates to colored glaze product field for building, more particularly to a kind of light glazed tile.
Background technology
The modeling of glazed tiles tonerde is burnt till after type is made, and generally imposes the colored lead glaze such as golden yellow, emerald green, dark blue,
It is splendid, it is durable in use.But traditional glazed tiles complex manufacturing technology, production cycle length are fluffy with China's construction modelled after an antique
The exhibition of breaking out, the growing demand of building trade can not have been met by being increasingly used widely in modern architecture.
Existing glazed tiles are formed using a variety of pug mixed sinterings, and its glaze layer is general thicker and produces and answers
Power, quality weight, it is easily caused product glaze paint and cracking occurs, collapse the defects of stripping.Existing glazed tiles are in climate variability area or long
Easily faded under the sunlight of time, although the lead glaze on its surface can play certain water proofing property, its water resistance also has
Treat further to improve.
The content of the invention
In order to solve the above technical problems, it is an object of the invention to provide a kind of light glazed tile, lightweight coloured glaze of the invention
Smooth clean and tidy, bright in colour beautiful, the light weight in watt surface, waterproof, cost are low.
A kind of light glazed tile of the present invention, glazed tiles in the form of sheets, are made up of, coloured glaze some crests being sequentially connected or trough
Glass watt is made up of top layer and bottom, and top layer is made up of modified resin and the hydrophobic layer being positioned above, and bottom is by magnesium chloride, silicon
Sour magnesium, resin, ammonium chloride, triethanolamine and colorant are made, magnesium chloride, magnesium silicate, resin, ammonium chloride, triethanolamine and colorant
Mass ratio be 45-65:25-35:20-40:10-20:1-10:6-15.
Further, the preparation method of bottom comprises the following steps：
Magnesium chloride, magnesium silicate, resin, ammonium chloride, triethanolamine and colorant are mixed in water, are then poured in mould,
Natural cooling solidify afterwards after heating at 60-80 DEG C.
Further, modified resin is Corvic or ABS resin.
Further, resin is Lauxite or phenolic resin.
Further, colorant is the one or more in cobalt oxide, iron oxide, cadmium sulfide and aluminium chloride.
Further, pouring into also includes upper and lower the step of shaking 20-30min after mould.
Further, the quality of water is magnesium chloride, magnesium silicate, resin, ammonium chloride, triethanolamine and colorant gross mass
30%-50%.
Further, the inner surface of mould is coated with a strata tetrafluoroethene.
By such scheme, the present invention at least has advantages below：
Modified resin can provide smooth surface for glazed tiles, and hydrophobic layer can improve the water resistance of glazed tiles, and assign
Its self-cleaning function is given, makes its color more bright-coloured；Contain resin in the material of bottom, alleviate the weight of glazed tiles, bottom
Formula for optimize proportioning.The preparation method of bottom is simple, it is therefore prevented that the generation of bubble so that glazed tiles internal structure is more
Step up close, improve its impact resistance.
Described above is only the general introduction of technical solution of the present invention, in order to better understand the technological means of the present invention,
And can be practiced according to the content of specification, below with presently preferred embodiments of the present invention and coordinate detailed description as after.
Embodiment
With reference to embodiment, the embodiment of the present invention is described in further detail.Following examples are used for
Illustrate the present invention, but be not limited to the scope of the present invention.
Embodiment 1
A kind of light glazed tile of the present invention, glazed tiles in the form of sheets, are made up of, coloured glaze some crests being sequentially connected or trough
Glass watt is made up of top layer and bottom, and top layer is made up of modified resin and the hydrophobic layer being positioned above.Specifically, modified resin
For Corvic.Bottom is made up of magnesium chloride, magnesium silicate, resin, ammonium chloride, triethanolamine and colorant, magnesium chloride, silicic acid
Magnesium, resin, ammonium chloride, the mass ratio of triethanolamine and colorant are 45:35:40:10:10:6.Specifically, resin is ureaformaldehyde tree
Fat, colorant are cobalt oxide and iron oxide (mass ratio 3:1).
The preparation method of bottom comprises the following steps：
Magnesium chloride, magnesium silicate, resin, ammonium chloride, triethanolamine and colorant are mixed in water, the quality of water is chlorination
Magnesium, magnesium silicate, resin, ammonium chloride, the 30% of triethanolamine and colorant gross mass.Then it is poured in mould, the inner surface of mould
Coated with a strata tetrafluoroethene.Concussion 20min up and down, then heats 5h, natural cooling solidify afterwards at 60 DEG C.
Embodiment 2
A kind of light glazed tile of the present invention, glazed tiles in the form of sheets, are made up of, coloured glaze some crests being sequentially connected or trough
Glass watt is made up of top layer and bottom, and top layer is made up of modified resin and the hydrophobic layer being positioned above.Specifically, modified resin
For ABS resin.Bottom is made up of magnesium chloride, magnesium silicate, resin, ammonium chloride, triethanolamine and colorant, magnesium chloride, magnesium silicate, tree
Fat, ammonium chloride, the mass ratio of triethanolamine and colorant are 65:25:20:20:1:15.Specifically, resin is phenolic resin, colorant
For cadmium sulfide and aluminium chloride (mass ratio 1:1).
The preparation method of bottom comprises the following steps：
Magnesium chloride, magnesium silicate, resin, ammonium chloride, triethanolamine and colorant are mixed in water, the quality of water is chlorination
Magnesium, magnesium silicate, resin, ammonium chloride, the 50% of triethanolamine and colorant gross mass.Then it is poured in mould, the inner surface of mould
Coated with a strata tetrafluoroethene.Concussion 30min up and down, then heats 5h, natural cooling solidify afterwards at 80 DEG C.
Embodiment 3
A kind of light glazed tile of the present invention, glazed tiles in the form of sheets, are made up of, coloured glaze some crests being sequentially connected or trough
Glass watt is made up of top layer and bottom, and top layer is made up of modified resin and the hydrophobic layer being positioned above.Specifically, modified resin
For ABS resin.Bottom is made up of magnesium chloride, magnesium silicate, resin, ammonium chloride, triethanolamine and colorant, magnesium chloride, magnesium silicate, tree
Fat, ammonium chloride, the mass ratio of triethanolamine and colorant are 55:30:30:15:5:15.Specifically, resin is phenolic resin, colorant
For iron oxide, cadmium sulfide and aluminium chloride (mass ratio 1:1:2).
The preparation method of bottom comprises the following steps：
Magnesium chloride, magnesium silicate, resin, ammonium chloride, triethanolamine and colorant are mixed in water, the quality of water is chlorination
Magnesium, magnesium silicate, resin, ammonium chloride, the 40% of triethanolamine and colorant gross mass.Then it is poured in mould, the inner surface of mould
Coated with a strata tetrafluoroethene.Concussion 30min up and down, then heats 5h, natural cooling solidify afterwards at 70 DEG C.
Embodiment 4
A kind of light glazed tile of the present invention, glazed tiles in the form of sheets, are made up of, coloured glaze some crests being sequentially connected or trough
Glass watt is made up of top layer and bottom, and top layer is made up of modified resin and the hydrophobic layer being positioned above.Specifically, modified resin
For ABS resin.Bottom is made up of magnesium chloride, magnesium silicate, resin, ammonium chloride, triethanolamine and colorant, magnesium chloride, magnesium silicate, tree
Fat, ammonium chloride, the mass ratio of triethanolamine and colorant are 55:30:35:15:8:8.Specifically, resin is phenolic resin, colorant
For aluminium chloride.
The preparation method of bottom comprises the following steps：
Magnesium chloride, magnesium silicate, resin, ammonium chloride, triethanolamine and colorant are mixed in water, the quality of water is chlorination
Magnesium, magnesium silicate, resin, ammonium chloride, the 45% of triethanolamine and colorant gross mass.Then it is poured in mould, the inner surface of mould
Coated with a strata tetrafluoroethene.Concussion 25min up and down, then heats 5h, natural cooling solidify afterwards at 75 DEG C.
Described above is only the preferred embodiment of the present invention, is not intended to limit the invention, it is noted that for this skill
For the those of ordinary skill in art field, without departing from the technical principles of the invention, can also make it is some improvement and
Modification, these improvement and modification also should be regarded as protection scope of the present invention.
Claims (8)
- A kind of 1. light glazed tile, it is characterised in that：The glazed tiles in the form of sheets, by some crests being sequentially connected or trough structure Into the glazed tiles are made up of top layer and bottom, and the top layer is made up of modified resin and the hydrophobic layer being positioned above, institute Bottom is stated to be made up of magnesium chloride, magnesium silicate, resin, ammonium chloride, triethanolamine and colorant, the magnesium chloride, magnesium silicate, resin, The mass ratio of ammonium chloride, triethanolamine and colorant is 45-65:25-35:20-40:10-20:1-10:6-15.
- 2. light glazed tile according to claim 1, it is characterised in that the preparation method of the bottom includes following step Suddenly：The magnesium chloride, magnesium silicate, resin, ammonium chloride, triethanolamine and colorant are mixed in water, are then poured in mould, Natural cooling solidify afterwards after heating at 60-80 DEG C.
- 3. light glazed tile according to claim 1 or 2, it is characterised in that：The modified resin is Corvic Or ABS resin.
- 4. light glazed tile according to claim 1 or 2, it is characterised in that：The resin is Lauxite or phenolic aldehyde tree Fat.
- 5. light glazed tile according to claim 1 or 2, it is characterised in that：The colorant is cobalt oxide, iron oxide, sulphur One or more in cadmium and aluminium chloride.
- 6. light glazed tile according to claim 2, it is characterised in that：Pouring into also includes concussion 20- up and down after mould The step of 30min.
- 7. light glazed tile according to claim 2, it is characterised in that：The quality of water be magnesium chloride, magnesium silicate, resin, The 30%-50% of ammonium chloride, triethanolamine and colorant gross mass.
- 8. light glazed tile according to claim 2, it is characterised in that：The inner surface of the mould is coated with a strata four PVF.