CN107177267A - A kind of peelable sealing wax - Google Patents
A kind of peelable sealing wax Download PDFInfo
- Publication number
- CN107177267A CN107177267A CN201710520839.1A CN201710520839A CN107177267A CN 107177267 A CN107177267 A CN 107177267A CN 201710520839 A CN201710520839 A CN 201710520839A CN 107177267 A CN107177267 A CN 107177267A
- Authority
- CN
- China
- Prior art keywords
- parts
- sealing wax
- peelable sealing
- tissuemat
- defoamer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of peelable sealing wax of the present invention, it is characterised in that include the raw material of following parts by weight：Fluorinated silicone modified acrylic resin：50 80 parts；Tissuemat E particulate：10 18 parts；Rosin：7 15 parts；Defoamer：0.1 3 parts；Wetting agent：16 parts；Swelling agent：0.1 5 parts；Thickener：0.5 5 parts；Cosolvent：3 10 parts；Water：8 18 parts.A kind of peelable sealing wax that the present invention is provided, containing fluorinated silicone modified acrylic resin and Tissuemat E particulate coordinative role, obtained coating environmental protection, cheap, ageing-resistant after coating film forming, easy peeling, good weatherability.
Description
Technical field
The present invention relates to a kind of peelable sealing wax.
Background technology
Stripable paint is commonly used to the provisional protection of historical relic, precision component, plant equipment and other items, can also apply
In the dirt strippable coating of the home appliances such as smoke exhaust ventilator, exhaust umbrella.Strippable protective coating must is fulfilled in all weather conditions
The lower requirement used, that is, must have excellent weatherability.It must is fulfilled for basic technical requirements：Water resistance, light shine
It is aging, high temperature resistant, low temperature resistant, removability is kept when weather changes repeatedly.Existing rippability coating is solvent-based system,
A large amount of to use organic solvent, one side volatile organic content is high to cause severe contamination, the opposing party to production and use environment
Face there is also production cost it is high the problem of.
The content of the invention
To solve above-mentioned problem, it is an object of the invention to provide a kind of peelable sealing wax.It is described to contain fluorine silicon
Acrylic resin modified and Tissuemat E particulate coordinative role, it is obtained coating environmental protection, cheap, it is resistance to after coating film forming
Aging, easy peeling, good weatherability.
To reach above-mentioned purpose, the technical scheme is that：
A kind of peelable sealing wax, includes the raw material of following parts by weight：Fluorinated silicone modified acrylic resin：50-80 parts；Tissuemat E
Particulate：10-18 parts；Rosin：7-15 parts；Defoamer：0.1-3 parts；Wetting agent：1-6 parts；Swelling agent：0.1-5 parts；Thickener：
0.5-5 parts；Cosolvent：3-10 parts；Water：8-18 parts.
Further, the raw material of following parts by weight is included：Fluorinated silicone modified acrylic resin：55-75 parts；Tissuemat E is micro-
Grain：13-18 parts；Rosin：7-12 parts；Defoamer：0.1-2 parts；Wetting agent：2-4 parts；Swelling agent：0.1-3 parts；Thickener：0.5-
3 parts；Cosolvent：3-6 parts；Water：8-15 parts.
Further, the raw material of following parts by weight is included：Fluorinated silicone modified acrylic resin：66 parts；Tissuemat E particulate：
15 parts；Rosin：7.5 part；Defoamer：0.8 part；Wetting agent：2.5 part；Swelling agent：2.2 part；Thickener：1.8 part；Cosolvent：4
Part；Water：12 parts.
Further, the particle diameter of the Tissuemat E particulate is 200 ~ 400nm.
Further, the defoamer is organosiloxane or polyethers or amide-type defoamer.
Further, the wetting agent is AEO.
Further, the water is deionized water.
The beneficial effects of the present invention are：
A kind of peelable sealing wax that the present invention is provided, containing fluorinated silicone modified acrylic resin and Tissuemat E particulate coordinative role,
It is obtained coating environmental protection, cheap, it is ageing-resistant after coating film forming, easily peel off, good weatherability.
Embodiment
In order to make the purpose , technical scheme and advantage of the present invention be clearer, it is further detailed with reference to embodiments
Describe in detail bright.
Embodiment 1
A kind of peelable sealing wax, includes the raw material of following parts by weight：Fluorinated silicone modified acrylic resin：50 parts；Tissuemat E is micro-
Grain：12 parts；Rosin：11 parts；Defoamer：3 parts；Wetting agent：2 parts；Swelling agent：5 parts；Thickener：0.5 part；Cosolvent：8 parts；
Water：12 parts.
Embodiment 2
A kind of peelable sealing wax, includes the raw material of following parts by weight：Fluorinated silicone modified acrylic resin：58 parts；Tissuemat E is micro-
Grain：10 parts；Rosin：13 parts；Defoamer：1 part；Wetting agent：1 part；Swelling agent：0.1 part；Thickener：2 parts；Cosolvent：10 parts；
Water：8 parts.
Embodiment 3
A kind of peelable sealing wax, includes the raw material of following parts by weight：Fluorinated silicone modified acrylic resin：66 parts；Tissuemat E is micro-
Grain：15 parts；Rosin：7.5 part；Defoamer：0.8 part；Wetting agent：2.5 part；Swelling agent：2.2 part；Thickener：1.8 part；Hydrotropy
Agent：4 parts；Water：12 parts.
Embodiment 4
A kind of peelable sealing wax, includes the raw material of following parts by weight：Fluorinated silicone modified acrylic resin：73 parts；Tissuemat E is micro-
Grain：13 parts；Rosin：7 parts；Defoamer：0.1 part；Wetting agent：6 parts；Swelling agent：4 parts；Thickener：3 parts；Cosolvent：3 parts；Water：
18 parts.
Embodiment 5
A kind of peelable sealing wax, includes the raw material of following parts by weight：Fluorinated silicone modified acrylic resin：80 parts；Tissuemat E is micro-
Grain：18 parts；Rosin：15 parts；Defoamer：0.4 part；Wetting agent：4.5 part；Swelling agent：3 parts；Thickener：5 parts；Cosolvent：6 parts；
Water：13 parts.
A kind of peelable sealing wax that the present invention is provided, coordinates to make containing fluorinated silicone modified acrylic resin and Tissuemat E particulate
It is ageing-resistant after coating film forming with, obtained coating environmental protection, cheap, easily peel off, good weatherability.
It should be noted that the above embodiments are merely illustrative of the technical solutions of the present invention and it is unrestricted.Although with reference to compared with
The present invention is described in detail good embodiment, it will be understood by those within the art that, can be to the technology of invention
Scheme is modified or equivalent substitution, and without departing from the scope of technical solution of the present invention, it all should cover the power in the present invention
In sharp claimed range.
Claims (7)
1. a kind of peelable sealing wax, it is characterised in that include the raw material of following parts by weight：Fluorinated silicone modified acrylic resin：50-
80 parts；Tissuemat E particulate：10-18 parts；Rosin：7-15 parts；Defoamer：0.1-3 parts；Wetting agent：1-6 parts；Swelling agent：0.1-
5 parts；Thickener：0.5-5 parts；Cosolvent：3-10 parts；Water：8-18 parts.
2. a kind of peelable sealing wax according to claim 1, it is characterised in that include the raw material of following parts by weight：Fluorine
Fluorine-silicon modified acrylic resin：55-75 parts；Tissuemat E particulate：13-18 parts；Rosin：7-12 parts；Defoamer：0.1-2 parts；Wetting
Agent：2-4 parts；Swelling agent：0.1-3 parts；Thickener：0.5-3 parts；Cosolvent：3-6 parts；Water：8-15 parts.
3. a kind of peelable sealing wax according to claim 1, it is characterised in that include the raw material of following parts by weight：Fluorine
Fluorine-silicon modified acrylic resin：66 parts；Tissuemat E particulate：15 parts；Rosin：7.5 part；Defoamer：0.8 part；Wetting agent：2.5 part；
Swelling agent：2.2 part；Thickener：1.8 part；Cosolvent：4 parts；Water：12 parts.
4. a kind of peelable sealing wax according to claim 1, it is characterised in that the particle diameter of the Tissuemat E particulate is
200~400nm。
5. a kind of peelable sealing wax according to claim 1, it is characterised in that the defoamer is organosiloxane or poly-
Ether or amide-type defoamer.
6. a kind of peelable sealing wax according to claim 1, it is characterised in that the wetting agent is aliphatic alcohol polyethenoxy
Ether.
7. a kind of peelable sealing wax according to claim 1, it is characterised in that the water is deionized water.