CN106977903A - A kind of TPE intermingling materials and preparation method thereof - Google Patents
A kind of TPE intermingling materials and preparation method thereof Download PDFInfo
- Publication number
- CN106977903A CN106977903A CN201710212334.9A CN201710212334A CN106977903A CN 106977903 A CN106977903 A CN 106977903A CN 201710212334 A CN201710212334 A CN 201710212334A CN 106977903 A CN106977903 A CN 106977903A
- Authority
- CN
- China
- Prior art keywords
- parts
- tpe
- raw material
- materials
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of TPE intermingling materials and preparation method thereof, its raw material is as follows by weight：10 20 parts of styrene analog thermoplastic elastomer, 10 30 parts of white oil, 10 20 parts of polyolefin elastomer, 5 10 parts of compatilizer, 30 50 parts of TPUE, 0 20 parts of filler.A kind of TPE intermingling materials that the present invention is provided and preparation method thereof, each component raw material are weighed by weight ratio, melting extrusion granulation is heated by double screw extruder after the raw material high-speed stirred bucket weighed up is well mixed and obtains TPE intermingling materials, it can be used for the non-polar materials such as encapsulated PP and PE, encapsulated PC and ABS polar materials can be used for again simultaneously, solving traditional TPE material can not be while the problem of being used for encapsulated polar material and non-polar material, adds the use value of product and improves productivity effect.
Description
Technical field
The present invention relates to TPE material technical field, more particularly to a kind of TPE intermingling materials and preparation method thereof.
Background technology
Traditional TPE (thermoplastic elastomer (TPE)) otherwise intermingling material is only used for bag in the application of the encapsulated aspect of double-shot moulding
The non-polar materials such as glue PP and PE, or being only used for encapsulated PC and ABS polar materials, which limits answering for TPE material
With scope, the encapsulated products for making some companies have to be done different requirements using the TPE material of two kinds of specifications are returned in regrinding-material
Debit face must separate and handle, and so can not only increase workload, and can cause unnecessary waste.
The content of the invention
The invention aims to solve shortcoming present in prior art, and a kind of TPE intermingling materials for proposing and
Its preparation method.
To achieve these goals, present invention employs following technical scheme：
A kind of TPE intermingling materials, its raw material is as follows by weight：10-20 parts of styrene analog thermoplastic elastomer, white oil
10-30 parts, 10-20 parts of polyolefin elastomer, 5-10 parts of compatilizer, 30-50 parts of TPUE, filler 0-20
Part.
It is preferred that, the filler is mineral filler.
A kind of preparation method for TPE intermingling materials that the present invention is also provided, comprises the following steps：
S1：Get the raw materials ready, each component raw material are weighed by weight ratio, are weighed in strict accordance with ratio, material is put after weighing
Purchase use；
S2：First the styrene analog thermoplastic elastomer for weighing up weight is added in high-speed stirred bucket, white oil is then added,
Allow styrene analog thermoplastic elastomer and white oil to be stirred 10 minutes in high-speed stirred bucket, promote styrene analog thermoplastic elastomer
Absorption to white oil；
S3：The addition of clout, then remaining raw material is separately added into, it is sufficiently mixed 10 minutes, obtains in high-speed stirred bucket
To mixing material；
S4：Mixing material is added in the hopper of double screw extruder, melting extrusion is heated by double screw extruder
Granulation, each area's temperature of extruder is set as between 150-220 DEG C, and TPE pellets are obtained after cooling.
A kind of TPE intermingling materials that the present invention is provided and preparation method thereof, weigh each component raw material by weight ratio, will
The raw material high-speed stirred bucket weighed up heats melting extrusion granulation by double screw extruder after being well mixed and obtains TPE blendings
Material, can be used for the non-polar materials such as encapsulated PP and PE, while can be used for encapsulated PC and ABS polar materials again, solve
The problem of traditional TPE material can not be used for encapsulated polar material and non-polar material simultaneously, add the use value of product
With improve productivity effect.
Embodiment
In order to make the purpose , technical scheme and advantage of the present invention be clearer, below in conjunction with specific embodiment, to this
Invention is further elaborated.It should be appreciated that the specific embodiments described herein are merely illustrative of the present invention, not
For limiting the present invention.
Embodiment 1
A kind of TPE intermingling materials, its raw material is as follows by weight：10 parts of styrene analog thermoplastic elastomer, 10 parts of white oil,
10 parts of polyolefin elastomer, 5 parts of compatilizer, 30 parts of TPUE, 5 parts of filler.The filler is filled out for mineral matter
Material.
A kind of preparation method for TPE intermingling materials that the present invention is also provided, comprises the following steps：
S1：Get the raw materials ready, each component raw material are weighed by weight ratio, are weighed in strict accordance with ratio, material is put after weighing
Purchase use；
S2：First the styrene analog thermoplastic elastomer for weighing up weight is added in high-speed stirred bucket, white oil is then added,
Allow styrene analog thermoplastic elastomer and white oil to be stirred 10 minutes in high-speed stirred bucket, promote styrene analog thermoplastic elastomer
Absorption to white oil；
S3：The addition of clout, then remaining raw material is separately added into, it is sufficiently mixed 10 minutes, obtains in high-speed stirred bucket
To mixing material；
S4：Mixing material is added in the hopper of double screw extruder, melting extrusion is heated by double screw extruder
Granulation, each area's temperature of extruder is set as between 150-220 DEG C, and TPE pellets are obtained after cooling.
Embodiment 2
A kind of TPE intermingling materials, its raw material is as follows by weight：15 parts of styrene analog thermoplastic elastomer, 15 parts of white oil,
15 parts of polyolefin elastomer, 8 parts of compatilizer, 40 parts of TPUE, 15 parts of filler.The filler is filled out for mineral matter
Material.
A kind of preparation method for TPE intermingling materials that the present invention is also provided, comprises the following steps：
S1：Get the raw materials ready, each component raw material are weighed by weight ratio, are weighed in strict accordance with ratio, material is put after weighing
Purchase use；
S2：First the styrene analog thermoplastic elastomer for weighing up weight is added in high-speed stirred bucket, white oil is then added,
Allow styrene analog thermoplastic elastomer and white oil to be stirred 10 minutes in high-speed stirred bucket, promote styrene analog thermoplastic elastomer
Absorption to white oil；
S3：The addition of clout, then remaining raw material is separately added into, it is sufficiently mixed 10 minutes, obtains in high-speed stirred bucket
To mixing material；
S4：Mixing material is added in the hopper of double screw extruder, melting extrusion is heated by double screw extruder
Granulation, each area's temperature of extruder is set as between 150-220 DEG C, and TPE pellets are obtained after cooling.
Embodiment 3
A kind of TPE intermingling materials, its raw material is as follows by weight：18 parts of styrene analog thermoplastic elastomer, 25 parts of white oil,
18 parts of polyolefin elastomer, 9 parts of compatilizer, 45 parts of TPUE, 18 parts of filler.The filler is filled out for mineral matter
Material.
A kind of preparation method for TPE intermingling materials that the present invention is also provided, comprises the following steps：
S1：Get the raw materials ready, each component raw material are weighed by weight ratio, are weighed in strict accordance with ratio, material is put after weighing
Purchase use；
S2：First the styrene analog thermoplastic elastomer for weighing up weight is added in high-speed stirred bucket, white oil is then added,
Allow styrene analog thermoplastic elastomer and white oil to be stirred 10 minutes in high-speed stirred bucket, promote styrene analog thermoplastic elastomer
Absorption to white oil；
S3：The addition of clout, then remaining raw material is separately added into, it is sufficiently mixed 10 minutes, obtains in high-speed stirred bucket
To mixing material；
S4：Mixing material is added in the hopper of double screw extruder, melting extrusion is heated by double screw extruder
Granulation, each area's temperature of extruder is set as between 150-220 DEG C, and TPE pellets are obtained after cooling.
The difference of various raw material proportionings can obtain the material of different performance, different ratio combination be tested, obtaining property
Energy table is as follows：
A kind of TPE intermingling materials that the present invention is provided and preparation method thereof, weigh each component raw material by weight ratio, will
The raw material high-speed stirred bucket weighed up heats melting extrusion granulation by double screw extruder after being well mixed and obtains TPE blendings
Material, can be used for the non-polar materials such as encapsulated PP and PE, while can be used for encapsulated PC and ABS polar materials again, solve
The problem of traditional TPE material can not be used for encapsulated polar material and non-polar material simultaneously, add the use value of product
With improve productivity effect.
The foregoing is only a preferred embodiment of the present invention, but protection scope of the present invention be not limited thereto,
Any one skilled in the art the invention discloses technical scope in, technique according to the invention scheme and its
Inventive concept is subject to equivalent substitution or change, should all be included within the scope of the present invention.
Claims (3)
1. a kind of TPE intermingling materials and preparation method thereof, it is characterised in that：Its raw material is as follows by weight：Phenylethylene thermoplastic
Property 10-20 parts of elastomer, 10-30 parts of white oil, 10-20 parts of polyolefin elastomer, 5-10 parts of compatilizer, thermoplastic polyurethane elastic
30-50 parts of body, 0-20 parts of filler.
2. a kind of TPE intermingling materials according to claim 1, it is characterised in that：The filler is mineral filler.
3. a kind of preparation method of the TPE intermingling materials described in claim 1, it is characterised in that：Comprise the following steps：
S1：Get the raw materials ready, each component raw material are weighed by weight ratio, are weighed in strict accordance with ratio, material places standby after weighing
With；
S2：First the styrene analog thermoplastic elastomer for weighing up weight is added in high-speed stirred bucket, white oil is then added, allows benzene
Ethene analog thermoplastic elastomer and white oil are stirred 10 minutes in high-speed stirred bucket, promote styrene analog thermoplastic elastomer dialogue
The absorption of oil；
S3：The addition of clout, then remaining raw material is separately added into, it is sufficiently mixed 10 minutes, is mixed in high-speed stirred bucket
Condensation material；
S4：Mixing material is added in the hopper of double screw extruder, heating melting extrusion by double screw extruder granulates,
Each area's temperature of extruder is set as between 150-220 DEG C, and TPE pellets are obtained after cooling.