CN106638122A - Macromolecular antibacterial raw paper material for packaging cartons and preparation method thereof - Google Patents
Macromolecular antibacterial raw paper material for packaging cartons and preparation method thereof Download PDFInfo
- Publication number
- CN106638122A CN106638122A CN201611181040.6A CN201611181040A CN106638122A CN 106638122 A CN106638122 A CN 106638122A CN 201611181040 A CN201611181040 A CN 201611181040A CN 106638122 A CN106638122 A CN 106638122A
- Authority
- CN
- China
- Prior art keywords
- parts
- mentioned
- stirred
- dispersion liquid
- added
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a macromolecular antibacterial raw paper material for packaging cartons and a preparation method thereof. The material is prepared from, by weight, 0.8-2 parts of alkenyl succinic anhydride, 0.5-1 part of hexamethyl phosphoryl triamide, 1-2 parts of sodium fluoroborate, 3-4 parts of palm wax, 0.8-2 parts of alkylolamides, 1-2 parts of sodium benzoate, 0.4-1 part of ammonium molybdate, 0.8-1 part of 2-bromo-4-methylphenol, 2-3 parts of polyacrylamide, 0.3-1 part of fatty acid polyglycol ester, 1.5-2 parts of calcium linoleate, 2.6-3 parts of benzyl triphenyl phosphonium chloride, 17-20 parts of styrene, 0.5-1 part of dodecyl trimethyl ammonium chloride, 2-3 parts of calcium propionate, 90-100 parts of bamboo pulp, 10-14 parts of mineral wool fibers, 30-40 parts of jute pulp, 0.4-1 part of a silane coupling agent kh5600, 3-5 parts of artemisia seed glue and 0.1-0.2 part of ammonium persulfate. High dimensional stability, great antibacterial performance, excellent comprehensive performance and long service life of finished products are realized.
Description
Technical field
The present invention relates to Packaging Box field of material technology, more particularly to a kind of Packaging Box antibacterial body paper material of macromolecule
Material and preparation method thereof.
Background technology
In recent years, with the continuous improvement of people's living standard, the use range of Packaging Box is also increasingly wider, not only wraps
Traditional household items are included, also including various aquatic products, fresh, chemical drugss etc., it is more preferable that this requires that Packaging Box has
The materials such as protective value, the employing velveteen that traditional Packaging Box has, paper pulp fiber length is longer made by these, and fiber is very curved
Song, poor dimensional stability, and with very strong water absorption, the environment for running into humidity is easy for damage, meanwhile, paper material conduct
One of common used material, is the field closely related with people's life, and in people's life Packaging Box is all likely to be exposed everywhere.Cause
This, in order to prevent Packaging Box use during noxious bacteria propagation caused by various diseases, protect human body health,
Health is ground, Packaging Box of the research and development with anti-microbial property is also necessary, therefore we are accomplished by constantly raising
The combination property of Packaging Box, meets its use in each packaging field, improves the use environment of safety and environmental protection.
The content of the invention
The object of the invention is exactly to make up the defect of prior art, there is provided a kind of Packaging Box antibacterial body paper of macromolecule
Material and preparation method thereof.
The present invention is achieved by the following technical solutions.
A kind of Packaging Box antibacterial body paper material of macromolecule, it is by made by the raw material of following weight parts:
Alkenyl succinic anhydride 0.8-2, HMPA 0.5-1, Sodium fluoroborate 1-2, palm wax 3-4, alkylolamideses
0.8-2, sodium benzoate 1-2, ammonium molybdate 0.4-1,2- bromo-4-methylphenol 0.8-1, polyacrylamide 2-3, fatty acid polyglycol second two
Alcohol ester 0.3-1, linoleic acid calcium soap 1.5-2, benzyl triphenyl phosphonium chloride phosphine 2.6-3, styrene 17-20, trimethyl chlorine
Change ammonium 0.5-1, calcium propionate 2-3, bamboo pulp 90-100, mineral wool fiber 10-14, jute pulp 30-40, silane coupler kh560 0.4-1,
Artemisia glue 3-5, Ammonium persulfate. 0.1-0.2.
A kind of described Packaging Box preparation method of the antibacterial body paper material of macromolecule, comprises the following steps:
(1)Above-mentioned alkenyl succinic anhydride is added in the deionized water of its weight 27-30 times, is stirred, rising high-temperature is
50-60 DEG C, insulated and stirred 3-5 minute, obtain anhydride aqueous solution;
(2)By above-mentioned sodium benzoate, ammonium molybdate, calcium propionate mixing, in being added to the deionized water of compound weight 30-40 times,
Stir, add abovementioned alkyl alkylolamides, stir, obtain antibacterial dispersion liquid;
(3)Above-mentioned 2- bromo-4-methylphenols are added in the dehydrated alcohol of its weight 67-70 times, are stirred, rise high-temperature
For 60-65 DEG C, above-mentioned benzyl triphenyl phosphonium chloride phosphine, palm wax, linoleic acid calcium soap, insulated and stirred 20-30 minute, in addition are added
Fatty acid polyethylene glycol ester is stated, is stirred to room temperature, obtain anti-corrosion alcohol dispersion liquid;
(4)Above-mentioned Dodecyl trimethyl ammonium chloride is added in jute pulp, is stirred, add above-mentioned hexamethyl phosphinylidyne three
Amine, stirs, and obtains jute pulp dispersion liquid;
(5)Above-mentioned styrene is added in anti-corrosion alcohol dispersion liquid, is stirred, be passed through nitrogen, add above-mentioned anhydride aqueous solution,
It is 70-74 DEG C to rise high-temperature, adds above-mentioned Ammonium persulfate., insulation reaction 3-4 hour, add above-mentioned jute pulp dispersion liquid, antibacterial point
Dispersion liquid, ultrasonic agitation 4-7 minute, adds above-mentioned artemisia glue, stirs, and obtains graft polymers mucus;
(6)Above-mentioned mineral wool fiber is added in its weight 10-12 times, 70-75% ethanol solution, adds above-mentioned grafting to gather
Compound mucus, silane coupler kh560, it is 51-60 DEG C to rise high-temperature, and insulated and stirred 1-2 hour obtains silanol dispersion liquid;
(7)Above-mentioned silanol dispersion liquid is mixed with remaining each raw material, is stirred, in being added to beater, beating, in 60-
20-30 minutes are incubated at 70 DEG C, Jing is discongested, defibrination, add water to solid content for 4-6%, manufactured paper with pulp molding by paper machine, dehydration is dried
It is dry, obtain body paper material.
It is an advantage of the invention that:
The present invention adopt styrene for monomer, and Ammonium persulfate. is initiator, and calcium propionate, sodium benzoate etc. are antibacterial auxiliary agent, is gathering
The polymer mucus with high-efficiency antimicrobial performance is obtained during conjunction, has then been surface-treated by silane coupler, carried
The high compatibility between polymer mucus and fibrous raw material, improves the dimensional stability of product, and the finished product of the present invention has very
Dimensional stability well and bacteriostasis property, combination property is superior, long perfomance life.
Specific embodiment
The following is embodiments of the invention one.
A kind of Packaging Box antibacterial body paper material of macromolecule, it is by made by the raw material of following weight parts:
Alkenyl succinic anhydride 0.8, HMPA 0.5, Sodium fluoroborate 1, palm wax 3, alkylolamideses 0.8, benzoic acid
Sodium 1, ammonium molybdate 0.4,2- bromo-4-methylphenols 0.8, polyacrylamide 2, fatty acid polyethylene glycol ester 0.3, linoleic acid calcium soap
1.5th, benzyl triphenyl phosphonium chloride phosphine 2.6, styrene 17, Dodecyl trimethyl ammonium chloride 0.5, calcium propionate 2, bamboo pulp 90, mineral wool
Fiber 10, jute pulp 30, silane coupler kh560 0.4, artemisia glue 3, Ammonium persulfate. 0.1.
The following is embodiments of the invention two.
A kind of Packaging Box antibacterial body paper material of macromolecule, it is by made by the raw material of following weight parts:
Alkenyl succinic anhydride 1.5, HMPA 0.7, Sodium fluoroborate 1.5, palm wax 3.5, alkylolamideses 1.5, benzene
Sodium formate 1.4, ammonium molybdate 0.6,2- bromo-4-methylphenols 0.9, polyacrylamide 2.4, fatty acid polyethylene glycol ester 0.7, sub- oil
Sour calcium soap 1.6, benzyl triphenyl phosphonium chloride phosphine 2.8, styrene 19, Dodecyl trimethyl ammonium chloride 0.7, calcium propionate 2.5, bamboo pulp
95th, mineral wool fiber 12, jute pulp 34, silane coupler kh560 0.8, artemisia glue 4, Ammonium persulfate. 0.1.
The following is embodiments of the invention three.
A kind of Packaging Box antibacterial body paper material of macromolecule, it is by made by the raw material of following weight parts:
Alkenyl succinic anhydride 2, HMPA 1, Sodium fluoroborate 2, palm wax 4, alkylolamideses 2, sodium benzoate 2, molybdenum
Sour ammonium 1,2- bromo-4-methylphenols 1, polyacrylamide 3, fatty acid polyethylene glycol ester 1, linoleic acid calcium soap 2, benzyltriphenyl phosphonium chlorine
Change phosphine 3, styrene 20, Dodecyl trimethyl ammonium chloride 1, calcium propionate 3, bamboo pulp 100, mineral wool fiber 14, jute pulp 40, silane idol
Connection agent kh560 1, artemisia glue 5, Ammonium persulfate. 0.2.
A kind of described Packaging Box preparation method of the antibacterial body paper material of macromolecule, comprises the following steps:
(1)Above-mentioned alkenyl succinic anhydride is added in the deionized water of 27 times of its weight, is stirred, it is 50 to rise high-temperature
DEG C, insulated and stirred 3 minutes obtains anhydride aqueous solution;
(2)By above-mentioned sodium benzoate, ammonium molybdate, calcium propionate mixing, in being added to the deionized water of 30 times of compound weight, stirring
Uniformly, abovementioned alkyl alkylolamides is added, is stirred, obtain antibacterial dispersion liquid;
(3)Above-mentioned 2 bromomethyl phenol is added in the dehydrated alcohol of 67 times of its weight, is stirred, it is 60 DEG C to rise high-temperature,
Above-mentioned benzyl triphenyl phosphonium chloride phosphine, palm wax, linoleic acid calcium soap, insulated and stirred 20 minutes is added to add above-mentioned fatty acid polyglycol second
Diol ester, stirs to room temperature, obtains anti-corrosion alcohol dispersion liquid;
(4)Above-mentioned Dodecyl trimethyl ammonium chloride is added in jute pulp, is stirred, add above-mentioned hexamethyl phosphinylidyne three
Amine, stirs, and obtains jute pulp dispersion liquid;
(5)Above-mentioned styrene is added in anti-corrosion alcohol dispersion liquid, is stirred, be passed through nitrogen, add above-mentioned anhydride aqueous solution,
It is 70 DEG C to rise high-temperature, adds above-mentioned Ammonium persulfate., insulation reaction 3 hours to add above-mentioned jute pulp dispersion liquid, antibacterial dispersion liquid,
Ultrasonic agitation 4 minutes, adds above-mentioned artemisia glue, stirs, and obtains graft polymers mucus;
(6)Above-mentioned mineral wool fiber is added in 10 times of its weight, 70% ethanol solution, adds above-mentioned graft polymers to stick
Liquid, silane coupler kh560, it is 51 DEG C to rise high-temperature, and insulated and stirred 1 hour obtains silanol dispersion liquid;
(7)Above-mentioned silanol dispersion liquid is mixed with remaining each raw material, is stirred, in being added to beater, beating, at 60 DEG C
Lower insulation 20 minutes, Jing is discongested, defibrination, adds water to solid content for 4%, is manufactured paper with pulp molding by paper machine, and dehydration, drying obtains body paper material
Material.
Claims (2)
1. a kind of Packaging Box antibacterial body paper material of macromolecule, it is characterised in that it is made up of the raw material of following weight parts
's:
Alkenyl succinic anhydride 0.8-2, HMPA 0.5-1, Sodium fluoroborate 1-2, palm wax 3-4, alkylolamideses
0.8-2, sodium benzoate 1-2, ammonium molybdate 0.4-1,2- bromo-4-methylphenol 0.8-1, polyacrylamide 2-3, fatty acid polyglycol second two
Alcohol ester 0.3-1, linoleic acid calcium soap 1.5-2, benzyl triphenyl phosphonium chloride phosphine 2.6-3, styrene 17-20, trimethyl chlorine
Change ammonium 0.5-1, calcium propionate 2-3, bamboo pulp 90-100, mineral wool fiber 10-14, jute pulp 30-40, silane coupler kh560 0.4-1,
Artemisia glue 3-5, Ammonium persulfate. 0.1-0.2.
2. a kind of Packaging Box as claimed in claim 1 preparation method of the antibacterial body paper material of macromolecule, it is characterised in that
Comprise the following steps:
(1)Above-mentioned alkenyl succinic anhydride is added in the deionized water of its weight 27-30 times, is stirred, rising high-temperature is
50-60 DEG C, insulated and stirred 3-5 minute, obtain anhydride aqueous solution;
(2)By above-mentioned sodium benzoate, ammonium molybdate, calcium propionate mixing, in being added to the deionized water of compound weight 30-40 times,
Stir, add abovementioned alkyl alkylolamides, stir, obtain antibacterial dispersion liquid;
(3)Above-mentioned 2- bromo-4-methylphenols are added in the dehydrated alcohol of its weight 67-70 times, are stirred, rise high-temperature
For 60-65 DEG C, above-mentioned benzyl triphenyl phosphonium chloride phosphine, palm wax, linoleic acid calcium soap, insulated and stirred 20-30 minute, in addition are added
Fatty acid polyethylene glycol ester is stated, is stirred to room temperature, obtain anti-corrosion alcohol dispersion liquid;
(4)Above-mentioned Dodecyl trimethyl ammonium chloride is added in jute pulp, is stirred, add above-mentioned hexamethyl phosphinylidyne three
Amine, stirs, and obtains jute pulp dispersion liquid;
(5)Above-mentioned styrene is added in anti-corrosion alcohol dispersion liquid, is stirred, be passed through nitrogen, add above-mentioned anhydride aqueous solution,
It is 70-74 DEG C to rise high-temperature, adds above-mentioned Ammonium persulfate., insulation reaction 3-4 hour, add above-mentioned jute pulp dispersion liquid, antibacterial point
Dispersion liquid, ultrasonic agitation 4-7 minute, adds above-mentioned artemisia glue, stirs, and obtains graft polymers mucus;
(6)Above-mentioned mineral wool fiber is added in its weight 10-12 times, 70-75% ethanol solution, adds above-mentioned grafting to gather
Compound mucus, silane coupler kh560, it is 51-60 DEG C to rise high-temperature, and insulated and stirred 1-2 hour obtains silanol dispersion liquid;
(7)Above-mentioned silanol dispersion liquid is mixed with remaining each raw material, is stirred, in being added to beater, beating, in 60-
20-30 minutes are incubated at 70 DEG C, Jing is discongested, defibrination, add water to solid content for 4-6%, manufactured paper with pulp molding by paper machine, dehydration is dried
It is dry, obtain body paper material.