CN106366891A - Anticorrosive nano polyurethane floor paint - Google Patents
Anticorrosive nano polyurethane floor paint Download PDFInfo
- Publication number
- CN106366891A CN106366891A CN201610937205.1A CN201610937205A CN106366891A CN 106366891 A CN106366891 A CN 106366891A CN 201610937205 A CN201610937205 A CN 201610937205A CN 106366891 A CN106366891 A CN 106366891A
- Authority
- CN
- China
- Prior art keywords
- parts
- floor paint
- nano
- anticorrosive
- resistance
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an anticorrosive nano polyurethane floor paint which comprises the following components in parts by weight: 65-80 parts of water-based polyurethane resin, 13-15 parts of diethylene glycol butyl ether acetate, 4-7 parts of tetrakis(methylethylketoximino)silane, 4-13 parts of nano silicon dioxide, 8-12 parts of ethanediol, 4-6 parts of actinolite powder, 8-10 parts of toluene diisocyanate, 8-12 parts of nano aluminum oxide, 3.5-7.5 parts of sodium diethylhexyl sulfosuccinate, 2.5-4.5 parts of ethoxylated alkylphenol ammonium sulfate, 20-30 parts of vinyl acetate-acrylic emulsion, 10-13 parts of polytetrafluoroethylene wax and 11-14 parts of hydroxyethyl cellulose. The anticorrosive nano polyurethane floor paint has favorable wear resistance and high-temperature resistance, enhances the bonding strength between the coating and floor, improves the curing speed at various temperatures, and has favorable water resistance and chemical corrosion resistance.
Description
Technical field
The present invention relates to a kind of floor paint, more particularly, to a kind of anticorrosive nano polyurethane floor paint.
Background technology
Anti-corrosion floor paint is mainly suitable for the terrace of preservative tank, heavy-duty machinery surface treatment and the perishable region of chemical enterprise,
The antiseptic project of petroleum industry and cesspool chemical bath etc..Permeability resistance is strong, resistance to strong acid, alkali, salt and various organic solvent, surface
Hardness is high, and compactness is good.Fork truck can be stood, truck rolls for a long time, make that ground severe is corrosion-resistant, strong acid-base resistance, chemically-resistant solvent,
Impact resistance, anti-polygon ground.The scope of application: the field such as Electroplate Factory, Battery Plant, chemical plant, electrolyzer, pharmaceutical factory, acid-base neutralization pond
Ground, metope and equipment surface.Wherein anticorrosive nano polyurethane floor paint has preferable mechanical performance, and general hardness is all
Relatively higher, but also there is the ability of wear and shock-resistant, chemical resistance is good, good weatherability.And terrace paint coating development
So far, because it has excellent physical and mechanical propertiess, electrical insulation capability, the performance such as resistance to chemical attack, national economy each
Field is widely applied, and its yield is continuously increased, and quality improves constantly, and new varieties continue to bring out.With market economy
Constantly develop, competition is also to grow in intensity, and that is accomplished by being developed in the technology and production capacity of enterprise, promotes coating more
New regenerate, and nano paint, raw materials used with existing floor paint compared with have unrivaled ultra-fine property and uniqueness, its product is comprehensive
Close performance and quality is significantly better than its like product, and cost is less than traditional product, has caused the great attention of countries in the world, and
Building coating industry new trend will be led, become the new fashion of decoration industry, nanometer terrace paint coating will have become terrace paint coating and sent out
The inexorable trend of exhibition.Accordingly, it would be desirable to develop a kind of water-repellent preservation nano-polyurethane floor paint that can overcome problem described above.
Content of the invention
It is an object of the invention to provide a kind of anticorrosive nano polyurethane floor paint.
To achieve these goals, the invention provides a kind of anticorrosive nano polyurethane floor paint, comprise following weight portion
Component: waterborne polyurethane resin 65-80 part, butyl acetate 13-15 part, four butanone oximino silane 4-7 parts, nanometer
Silicon dioxide 4-13 part, ethylene glycol 8-12 part, Actinolitum powder 4-6 part, toluene di-isocyanate(TDI) 8-10 part, nano aluminium oxide 8-12
Part, dioctyl sodium sulfosuccinate 3.5-7.5 part, ethoxylated alkylphenol ammonium sulfate 2.5-4.5 part, acrylate and vinyl acetate emulsion 20-30 part,
Polytetrafluoroethylwax wax 10-13 part, hydroxyethyl cellulose 11-14 part.
It also comprises fatty alcohol-polyoxyethylene ether 3-7 part.
It also comprises Oleum Ricini 10-14 part.
It also comprises glass dust 10-16 part.
Beneficial effect: anticorrosive nano polyurethane floor paint of the present invention has good wearability and resistance to elevated temperatures, improves
Bond strength between coating and terrace, improves curing rate at various temperatures, and also has good resistance to water and resist
Chemical corrosivity.
Specific embodiment
Embodiment 1
The anticorrosive nano polyurethane floor paint of the present embodiment, comprises following parts by weight of component: 65 parts of waterborne polyurethane resin, diethyl
13 parts of glycol monobutyl ether acetate, 4 parts of four butanone oximino silane, 4 parts of nano silicon, 8 parts of ethylene glycol, 4 parts of Actinolitum powder, first
8 parts of phenylene diisocyanate, 8 parts of nano aluminium oxide, 3.5 parts of dioctyl sodium sulfosuccinate, ethoxylated alkylphenol ammonium sulfate 2.5
Part, 20 parts of acrylate and vinyl acetate emulsion, 10 parts of polytetrafluoroethylwax wax, 11 parts of hydroxyethyl cellulose.Above-mentioned material is put in agitator tank, stirring
Tank temperature is 50 DEG C, and stirring and evenly mixing can get after being cooled to room temperature after mixing.
Performance floor paint being obtained to the present embodiment measures, and the performance test data detecting is: paint film is smooth, light
Sliding, pencil hardness: 1h, adhesive force :≤1 grade, pliability :≤2mm, comprcssive strength: 85mpa, resistance to water, after soaking 7 days: no become
Change, bubble-free, wrinkle resistant, do not fall off；Acid resistance, 5% sulphuric acid, after soaking 7 days, bubble-free, flawless, do not peel off, there is no powder
Change, dissolution phenomenon；Alkali resistance, 5% sodium hydroxide, after soaking 7 days, bubble-free, flawless, do not peel off, do not have efflorescence, dissolution existing
As.
Embodiment 2
The anticorrosive nano polyurethane floor paint of the present embodiment, comprises following parts by weight of component: 80 parts of waterborne polyurethane resin, diethyl
15 parts of glycol monobutyl ether acetate, 7 parts of four butanone oximino silane, 13 parts of nano silicon, 12 parts of ethylene glycol, 6 parts of Actinolitum powder,
10 parts of toluene di-isocyanate(TDI), 12 parts of nano aluminium oxide, 7.5 parts of dioctyl sodium sulfosuccinate, ethoxylated alkylphenol sulphuric acid
4.5 parts of ammonium, 30 parts of acrylate and vinyl acetate emulsion, 13 parts of polytetrafluoroethylwax wax, 14 parts of hydroxyethyl cellulose, 7 parts of fatty alcohol-polyoxyethylene ether.Will
Above-mentioned material is put in agitator tank, and agitator tank temperature is 80 DEG C, and stirring and evenly mixing can get after being cooled to room temperature after mixing.
Performance floor paint being obtained to the present embodiment measures, and the performance test data detecting is: paint film is smooth, light
Sliding, pencil hardness: 1h, adhesive force :≤1 grade, pliability :≤2mm, comprcssive strength: 89mpa, resistance to water, after soaking 7 days: no become
Change, bubble-free, wrinkle resistant, do not fall off；Acid resistance, 5% sulphuric acid, after soaking 7 days, bubble-free, flawless, do not peel off, there is no powder
Change, dissolution phenomenon；Alkali resistance, 5% sodium hydroxide, after soaking 7 days, bubble-free, flawless, do not peel off, do not have efflorescence, dissolution existing
As.
Embodiment 3
The anticorrosive nano polyurethane floor paint of the present embodiment, comprises following parts by weight of component: 65 parts of waterborne polyurethane resin, diethyl
13 parts of glycol monobutyl ether acetate, 4 parts of four butanone oximino silane, 4 parts of nano silicon, 8 parts of ethylene glycol, 4 parts of Actinolitum powder, first
8 parts of phenylene diisocyanate, 8 parts of nano aluminium oxide, 3.5 parts of dioctyl sodium sulfosuccinate, ethoxylated alkylphenol ammonium sulfate 2.5
Part, 20 parts of acrylate and vinyl acetate emulsion, 10 parts of polytetrafluoroethylwax wax, 11 parts of hydroxyethyl cellulose, 3 parts of fatty alcohol-polyoxyethylene ether, Oleum Ricini
10 parts.Above-mentioned material is put in agitator tank, agitator tank temperature is 50 DEG C, and stirring and evenly mixing, after being cooled to room temperature after mixing
Obtain.
Performance floor paint being obtained to the present embodiment measures, and the performance test data detecting is: paint film is smooth, light
Sliding, pencil hardness: 1h, adhesive force :≤1 grade, pliability :≤2mm, comprcssive strength: 95mpa, resistance to water, after soaking 7 days: no become
Change, bubble-free, wrinkle resistant, do not fall off；Acid resistance, 5% sulphuric acid, after soaking 7 days, bubble-free, flawless, do not peel off, there is no powder
Change, dissolution phenomenon；Alkali resistance, 5% sodium hydroxide, after soaking 7 days, bubble-free, flawless, do not peel off, do not have efflorescence, dissolution existing
As.
Embodiment 4
The anticorrosive nano polyurethane floor paint of the present embodiment, comprises following parts by weight of component: 80 parts of waterborne polyurethane resin, diethyl
15 parts of glycol monobutyl ether acetate, 7 parts of four butanone oximino silane, 13 parts of nano silicon, 12 parts of ethylene glycol, 6 parts of Actinolitum powder,
10 parts of toluene di-isocyanate(TDI), 12 parts of nano aluminium oxide, 7.5 parts of dioctyl sodium sulfosuccinate, ethoxylated alkylphenol sulphuric acid
4.5 parts of ammonium, 30 parts of acrylate and vinyl acetate emulsion, 13 parts of polytetrafluoroethylwax wax, 14 parts of hydroxyethyl cellulose, 7 parts of fatty alcohol-polyoxyethylene ether, castor
14 parts of Oleum Sesami, 16 parts of glass dust.Above-mentioned material is put in agitator tank, agitator tank temperature is 80 DEG C, stirring and evenly mixing is cold after mixing
But can get to room temperature.
Performance floor paint being obtained to the present embodiment measures, and the performance test data detecting is: paint film is smooth, light
Sliding, pencil hardness: 1h, adhesive force :≤1 grade, pliability :≤2mm, comprcssive strength: 98mpa, resistance to water, after soaking 7 days: no become
Change, bubble-free, wrinkle resistant, do not fall off；Acid resistance, 5% sulphuric acid, after soaking 7 days, bubble-free, flawless, do not peel off, there is no powder
Change, dissolution phenomenon；Alkali resistance, 5% sodium hydroxide, after soaking 7 days, bubble-free, flawless, do not peel off, do not have efflorescence, dissolution existing
As.
The above, be only presently preferred embodiments of the present invention, not the present invention is made with any pro forma restriction, though
So the present invention is disclosed above with preferred embodiment, but is not limited to the present invention, any is familiar with this professional technology people
Member, in the range of without departing from technical solution of the present invention, when the technology contents of available the disclosure above make a little change or modification
For the Equivalent embodiments of equivalent variations, as long as being the content without departing from technical solution of the present invention, the technical spirit of the foundation present invention
Any simple modification, equivalent variations and the modification that above example is made, all still falls within the scope of technical solution of the present invention
Interior.
Claims (4)
1. a kind of anticorrosive nano polyurethane floor paint is it is characterised in that comprise following parts by weight of component: waterborne polyurethane resin 65-
80 parts, butyl acetate 13-15 part, four butanone oximino silane 4-7 parts, nano silicon 4-13 part, ethylene glycol
8-12 part, Actinolitum powder 4-6 part, toluene di-isocyanate(TDI) 8-10 part, nano aluminium oxide 8-12 part, dioctyl sodium sulfosuccinate
3.5-7.5 part, ethoxylated alkylphenol ammonium sulfate 2.5-4.5 part, acrylate and vinyl acetate emulsion 20-30 part, polytetrafluoroethylwax wax 10-13 part,
Hydroxyethyl cellulose 11-14 part.
2. the anticorrosive nano polyurethane floor paint according to claim 1 it is characterised in that: it also comprises fatty alcohol polyoxy
Vinyl Ether 3-7 part.
3. the anticorrosive nano polyurethane floor paint according to claim 2 it is characterised in that: it also comprises Oleum Ricini 10-
14 parts.
4. anticorrosive nano polyurethane floor paint according to claim 3 it is characterised in that: it also comprises glass dust 10-16
Part.