CN106280520A - A kind of Wood-plastic material - Google Patents
A kind of Wood-plastic material Download PDFInfo
- Publication number
- CN106280520A CN106280520A CN201610702355.4A CN201610702355A CN106280520A CN 106280520 A CN106280520 A CN 106280520A CN 201610702355 A CN201610702355 A CN 201610702355A CN 106280520 A CN106280520 A CN 106280520A
- Authority
- CN
- China
- Prior art keywords
- agent
- parts
- wood
- prepares
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of Wood-plastic material, in units of weight portion, including following raw material: 42 78 parts of Eucalyptus powder, corn stalk powder 32 48 parts, 11 14 parts of papers for books and periodicals powder, plastic bag grain 9 13 parts, filler 68 parts, synthetics 46 parts, lubricant 12 parts, antimildew and antibacterial agent 12 parts, hygroscopic agent 12 parts, fire retardant 24 parts, smoke suppressant 24 parts, binding agent 6 10 parts, viscosifier 24 parts, softening agent 13 parts, UV absorbent 12 parts.The Wood-plastic material of the present invention can be widely applied to hotel, restaurant, building decoration and fitment, good flame retardation effect, it is impossible to burns and forms flame, stable and reliable for performance.
Description
[technical field]
The invention belongs to Wood-plastic material technology of preparing and field of Environment Protection, be specifically related to a kind of Wood-plastic material.
[background technology]
Wood plastic composite (WPC), is a kind of main by answering that material and plastics based on timber or cellulose are made
Condensation material, it is simply that a certain proportion of wood fiber (such as wood powder, powder of straw, cotton stalk powder, bamboo powder, shell powder etc.) is made through pretreatment
A kind of new material being combined into thermoplastic polymer resin or other materials;This new material not only environmental protection but also have
There is good mechanical stability, but the two big raw material wood fiber of composition wood plastic composite and polyolefin are all inflammability materials
Material, is also combustible material for this this composite, and giving the good fire resistance of wood plastic composite is the development of this materials application
Needs;Individually the fire-retardant research to timber and the wood fiber has a lot, typically has phosphorus-nitrogenated flame retardant;Boron flame retardant;Halogen
Fire retardant;Other inorganic salts etc.;But main based on phosphorus-nitrogenated flame retardant it is considered to be optimum wood fire retardant, phosphorus,
Two kinds of elements of nitrogen play synergism in wood fire retardant and improve flame retardant effect;But these fire retardants almost have one jointly
Feature, it is simply that reducing the thermal degradation temperature of the wood fiber significantly, this may result in the processing that cannot be carried out composite;Right
Also a lot of in the research of polyolefin flame-retardant, its flame resistant method is frequently with halogen containing flame-retardant and antimony oxide (Sb2O3) coordinate make
With;Metal hydroxides (Al (OH)3、Mg(OH)2) fire retardant;Expansibility flame-proof agent;Ammonium polyphosphate flame retardant etc.;Halogen-free flameproof
The focus of polyolefin flame-retardant research, expanding fire retardant polyolefin/Wood Fiber Composites is carried out dual fire-retardant be this be combined
The focus of the fire-retardant research of material;But the interpolation of fire retardant often deteriorates the mechanical property of composite, therefore to fire-retardant multiple
The research of the research flame-proof composite material of condensation material to study interface compatibility, heat stability and anti-flammability, to obtain reason simultaneously
The flame-proof composite material thought.
[summary of the invention]
The technical problem to be solved in the present invention is to provide a kind of Wood-plastic material, to solve the interpolation of fire retardant in prior art
The problems such as the mechanical property that can deteriorate Wood-plastic material.The Wood-plastic material of the present invention can be widely applied to hotel, restaurant, building decoration
Finishing, good flame retardation effect, it is impossible to burn and form flame, stable and reliable for performance.
In order to solve above technical problem, the present invention by the following technical solutions:
A kind of Wood-plastic material, in units of weight portion, including following raw material: Eucalyptus powder 42-78 part, corn stalk powder 32-
48 parts, papers for books and periodicals powder 11-14 part, plastic bag grain 9-13 part, filler 6-8 part, synthetics 4-6 part, lubricant 1-2 part, mildew-resistant
Antibacterial 1-2 part, hygroscopic agent 1-2 part, fire retardant 2-4 part, smoke suppressant 2-4 part, binding agent 6-10 part, viscosifier 2-4 part, softness
Agent 1-3 part, UV absorbent 1-2 part;
Described filler is Kaolin;
Described synthetics is in units of weight portion, including following raw material: propellant 0.3-0.5 part, coupling agent 0.6-0.8
Part, compatilizer 0.4-0.6 part, antioxidant 0.3-0.5 part, regulator 0.3-0.6 part, hardening agent 0.3-0.5 part, flocculation agent
0.6-0.8 part, plasticizer 0.6-0.9 part, stabilizer 0.3-0.4 part, terminator 0.3-0.4 part;
Described hardening agent is in units of weight portion, including following raw material: styrene 0.08-0.12 part, methylcrotonic acid first
Ester 0.08-0.12 part, vinylacetate 0.06-0.1 part, cobalt naphthenate 0.04-0.08 part, zinc chloride 0.04-0.08 part;
Described stabilizer is organic tin stabilizer;
Described lubricant is maleic anhydride grafted polyethylene wax;
Described antimildew and antibacterial agent is antimildew and antibacterial agent AEM5700-B;
Described hygroscopic agent is silica gel;
Described fire retardant is in units of weight portion, including following raw material: antimony oxide 5-8 part, vinyl triethoxyl
Silane 3-5 part, triethyl phosphate 3-4 part, magnesium chloride 5-7 part, phenolic resin 2-4 part, bentonite 0.6-1 part;
Described smoke suppressant is in units of weight portion, including following raw material: zinc molybdate 8-14 part, aluminium hydroxide 6-10 part, stone
English powder 2-3 part, copper oxide 1-2 part;
Described binding agent, with tapioca as raw material, carries out cross-linked graft reaction by elder generation with triglyceride, percarbamide,
Then carry out cross-linking reaction with potassium hydroxide and epoxychloropropane, then carry out pre-gelatinized reaction, be finally dried, pulverize, sieve and
?;
Described viscosifier are glycidoxy-propyltrimethoxy silane;
Described softening agent is polyester fiber;
Described UV absorbent is oxybenzoic acid phenyl ester;
The preparation method of described Wood-plastic material, comprises the following steps:
S1: prepare synthetics, the preparation method of described synthetics, comprise the following steps:
S11: propellant, coupling agent, compatilizer, antioxidant mixing are warming up to 115-125 DEG C, are 100-at rotating speed
React 40-90min under 300r/min, prepare material A;
S12: be warming up to 145-155 after adding regulator, hardening agent, flocculation agent mixing in the material A that step S11 prepares
DEG C, under rotating speed is 300-400r/min, reacts 150-220min, prepares material B;
S13: be cooled to 115-120 after adding plasticizer, stabilizer, terminator mixing in the material B that step S12 prepares
DEG C, under rotating speed is 200-300r/min, reacts 60-100min, prepares synthetics;
S2: prepare binding agent, the preparation method of described binding agent, comprise the following steps:
S21: compound concentration is para arrowroot slurry A of 20-23Be ';
S22: it is 1.5%-1.8% triglyceride, percarbamide that para arrowroot slurry A in step S21 adds concentration, so
After be 26-34 DEG C in temperature, speed of agitator be carry out under 50-80r/min cross-linked graft reaction 0.6-1h, prepare slurry B;
S23: add potassium hydroxide and epoxychloropropane in the slurry B of step S22, be then 32-36 DEG C in temperature, stir
Mixing rotating speed is to carry out cross-linking reaction 0.2-0.5h under 60-100r/min, prepares slurry C;
S24: be delivered to the slurry C of step S23 in cylindrical drier carry out pre-gelatinized and be 140-145 DEG C in temperature
Lower dry, prepare the material D of water content≤6%;
S25: wind after the material D pulverizing of step S24, excessively 60-100 mesh sieve is delivered to whirlwind separator and is collected, system
Obtain binding agent;
S3: by step S1 prepare synthetics, step S2 prepare binding agent, Eucalyptus powder, corn stalk powder, papers for books and periodicals
Powder, plastic bag grain, filler, lubricant, antimildew and antibacterial agent, hygroscopic agent, fire retardant, smoke suppressant, viscosifier, softening agent, ultraviolet
Light absorbers is put in pressure cooker, HIGH PRESSURE TREATMENT 0.5-0.8h under pressure is 12-15MPa, prepares raw material A;
S4: the raw material A that step S3 prepares is put into freezing 2-4h at temperature≤-30 DEG C, prepares raw material B;
S5: by step S4 prepare raw material B put in dehydrator, dry at temperature is 78-80 DEG C to water content≤
5%, prepare raw material C;
S6: raw material C step S5 prepared puts in blender, stirs 6-9min under rotating speed is 300-500r/min,
Prepare particle;
S7: put in extruder by the particle that step S6 prepares, extrudes, through supercooling at temperature is 185-190 DEG C
Molding, prepares Wood-plastic material.
Further, propellant described in step S11 is aerogel generating agent.
Further, coupling agent described in step S11 is furfural.
Further, compatilizer described in step S11 is acrylic type compatilizer.
Further, antioxidant described in step S11 is WINGSTAYL.
Further, regulator described in step S12 is JINHASS.
Further, flocculation agent described in step S12 is aluminium polychlorid.
Further, plasticizer described in step S13 is citrate.
Further, terminator described in step S13 is styrene.
Further, the mixed liquor cooling down employing described in step S7 is to be by water, ethanol, the mass ratio of ethyl salicylate
95-100:4-6:2-3 makes.
The method have the advantages that
(1) Wood-plastic material of the present invention has high flame resistance and smoke suppressing effect, at high temperature will not discharge poisonous and harmful
Material, it is to avoid the secondary injury to human body;
(2) heat-proof quality of the Wood-plastic material of the present invention is the best, it is to avoid the scald to human body, and has well insulation
Property;
(3) the Wood-plastic material material of the present invention is fine and close, and mechanical property is good, extremely durable.
(4) Wood-plastic material of the present invention can be widely applied to hotel, restaurant, building decoration and fitment, good flame retardation effect, it is impossible to
Burning and formation flame, stable and reliable for performance.
[detailed description of the invention]
For ease of being more fully understood that the present invention, being illustrated by following example, these embodiments belong to the present invention's
Protection domain, but it is not intended to protection scope of the present invention.
In an embodiment, described Wood-plastic material, in units of weight portion, including following raw material: Eucalyptus powder 42-78 part, jade
Rice powder of straw 32-48 part, papers for books and periodicals powder 11-14 part, plastic bag grain 9-13 part, filler 6-8 part, synthetics 4-6 part, lubricant
1-2 part, antimildew and antibacterial agent 1-2 part, hygroscopic agent 1-2 part, fire retardant 2-4 part, smoke suppressant 2-4 part, binding agent 6-10 part, viscosifier
2-4 part, softening agent 1-3 part, UV absorbent 1-2 part;
Described filler is Kaolin;
Described synthetics is in units of weight portion, including following raw material: propellant 0.3-0.5 part, coupling agent 0.6-0.8
Part, compatilizer 0.4-0.6 part, antioxidant 0.3-0.5 part, regulator 0.3-0.6 part, hardening agent 0.3-0.5 part, flocculation agent
0.6-0.8 part, plasticizer 0.6-0.9 part, stabilizer 0.3-0.4 part, terminator 0.3-0.4 part;
Described propellant is aerogel generating agent;
Described coupling agent is furfural;
Described compatilizer is acrylic type compatilizer;
Described antioxidant is WINGSTAYL;
Described regulator is JINHASS;
Described hardening agent is in units of weight portion, including following raw material: styrene 0.08-0.12 part, methylcrotonic acid first
Ester 0.08-0.12 part, vinylacetate 0.06-0.1 part, cobalt naphthenate 0.04-0.08 part, zinc chloride 0.04-0.08 part;
Described flocculation agent is aluminium polychlorid;
Described plasticizer is citrate;
Described stabilizer is organic tin stabilizer;
Described terminator is styrene;
Described lubricant is maleic anhydride grafted polyethylene wax;
Described antimildew and antibacterial agent is antimildew and antibacterial agent AEM5700-B;
Described hygroscopic agent is silica gel;
Described fire retardant is in units of weight portion, including following raw material: antimony oxide 5-8 part, vinyl triethoxyl
Silane 3-5 part, triethyl phosphate 3-4 part, magnesium chloride 5-7 part, phenolic resin 2-4 part, bentonite 0.6-1 part;
Described smoke suppressant is in units of weight portion, including following raw material: zinc molybdate 8-14 part, aluminium hydroxide 6-10 part, stone
English powder 2-3 part, copper oxide 1-2 part;
Described binding agent, with tapioca as raw material, carries out cross-linked graft reaction by elder generation with triglyceride, percarbamide,
Then carry out cross-linking reaction with potassium hydroxide and epoxychloropropane, then carry out pre-gelatinized reaction, be finally dried, pulverize, sieve and
?;
Described viscosifier are glycidoxy-propyltrimethoxy silane;
Described softening agent is polyester fiber;
Described UV absorbent is oxybenzoic acid phenyl ester;
The preparation method of described Wood-plastic material, comprises the following steps:
S1: prepare synthetics, the preparation method of described synthetics, comprise the following steps:
S11: propellant, coupling agent, compatilizer, antioxidant mixing are warming up to 115-125 DEG C, are 100-at rotating speed
React 40-90min under 300r/min, prepare material A;
S12: be warming up to 145-155 after adding regulator, hardening agent, flocculation agent mixing in the material A that step S11 prepares
DEG C, under rotating speed is 300-400r/min, reacts 150-220min, prepares material B;
S13: be cooled to 115-120 after adding plasticizer, stabilizer, terminator mixing in the material B that step S12 prepares
DEG C, under rotating speed is 200-300r/min, reacts 60-100min, prepares synthetics;
S2: prepare binding agent, the preparation method of described binding agent, comprise the following steps:
S21: compound concentration is para arrowroot slurry A of 20-23Be ';
S22: it is 1.5%-1.8% triglyceride, percarbamide that para arrowroot slurry A in step S21 adds concentration, so
After be 26-34 DEG C in temperature, speed of agitator be carry out under 50-80r/min cross-linked graft reaction 0.6-1h, prepare slurry B;
S23: add potassium hydroxide and epoxychloropropane in the slurry B of step S22, be then 32-36 DEG C in temperature, stir
Mixing rotating speed is to carry out cross-linking reaction 0.2-0.5h under 60-100r/min, prepares slurry C;
S24: be delivered to the slurry C of step S23 in cylindrical drier carry out pre-gelatinized and be 140-145 DEG C in temperature
Lower dry, prepare the material D of water content≤6%;
S25: wind after the material D pulverizing of step S24, excessively 60-100 mesh sieve is delivered to whirlwind separator and is collected, system
Obtain binding agent;
S3: by step S1 prepare synthetics, step S2 prepare binding agent, Eucalyptus powder, corn stalk powder, papers for books and periodicals
Powder, plastic bag grain, filler, lubricant, antimildew and antibacterial agent, hygroscopic agent, fire retardant, smoke suppressant, viscosifier, softening agent, ultraviolet
Light absorbers is put in pressure cooker, HIGH PRESSURE TREATMENT 0.5-0.8h under pressure is 12-15MPa, prepares raw material A;
S4: the raw material A that step S3 prepares is put into freezing 2-4h at temperature≤-30 DEG C, prepares raw material B;
S5: by step S4 prepare raw material B put in dehydrator, dry at temperature is 78-80 DEG C to water content≤
5%, prepare raw material C;
S6: raw material C step S5 prepared puts in blender, stirs 6-9min under rotating speed is 300-500r/min,
Prepare particle;
S7: put in extruder by the particle that step S6 prepares, extrudes at temperature is 185-190 DEG C, through mixing
Liquid cooling molding, prepares Wood-plastic material, and described mixed liquor is to be 95-100:4-6 by water, ethanol, the mass ratio of ethyl salicylate:
2-3 makes.
Below by more specifically embodiment, the present invention will be described.
Embodiment 1
A kind of Wood-plastic material, in units of weight portion, including following raw material: 60 parts of Eucalyptus powder, corn stalk powder 40 parts, book
Periodical 13 parts of paper powder, plastic bag grain 11 parts, filler 7 parts, synthetics 5 parts, lubricant 1.5 parts, antimildew and antibacterial agent 1.5 parts, moisture absorption
Agent 1.5 parts, fire retardant 3 parts, smoke suppressant 3 parts, binding agent 8 parts, viscosifier 3 parts, softening agent 2 parts, UV absorbent 1.5 parts;
Described filler is Kaolin;
Described synthetics is in units of weight portion, including following raw material: propellant 0.4 part, coupling agent 0.7 part, compatilizer
0.5 part, antioxidant 0.4 part, regulator 0.5 part, hardening agent 0.4 part, flocculation agent 0.7 part, plasticizer 0.7 part, stabilizer 0.4
Part, terminator 0.3 part;
Described propellant is aerogel generating agent;
Described coupling agent is furfural;
Described compatilizer is acrylic type compatilizer;
Described antioxidant is WINGSTAYL;
Described regulator is JINHASS;
Described hardening agent is in units of weight portion, including following raw material: styrene 0.1 part, methylcrotonic acid methyl ester 0.1
Part, vinylacetate 0.08 part, cobalt naphthenate 0.06 part, zinc chloride 0.06 part;
Described flocculation agent is aluminium polychlorid;
Described plasticizer is citrate;
Described stabilizer is organic tin stabilizer;
Described terminator is styrene;
Described lubricant is maleic anhydride grafted polyethylene wax;
Described antimildew and antibacterial agent is antimildew and antibacterial agent AEM5700-B;
Described hygroscopic agent is silica gel;
Described fire retardant is in units of weight portion, including following raw material: antimony oxide 7 parts, vinyl triethoxyl silicon
4 parts of alkane, triethyl phosphate 3.5 parts, 6 parts of magnesium chloride, 3 parts of phenolic resin, bentonite 0.8 part;
Described smoke suppressant is in units of weight portion, including following raw material: zinc molybdate 11 parts, aluminium hydroxide 8 parts, silica flour
2.5 parts, copper oxide 1.5 parts;
Described binding agent, with tapioca as raw material, carries out cross-linked graft reaction by elder generation with triglyceride, percarbamide,
Then carry out cross-linking reaction with potassium hydroxide and epoxychloropropane, then carry out pre-gelatinized reaction, be finally dried, pulverize, sieve and
?;
Described viscosifier are glycidoxy-propyltrimethoxy silane;
Described softening agent is polyester fiber;
Described UV absorbent is oxybenzoic acid phenyl ester;
The preparation method of described Wood-plastic material, comprises the following steps:
S1: prepare synthetics, the preparation method of described synthetics, comprise the following steps:
S11: propellant, coupling agent, compatilizer, antioxidant mixing are warming up to 120 DEG C, under rotating speed is 200r/min
Reaction 65min, prepares material A;
S12: be warming up to 150 DEG C after adding regulator, hardening agent, flocculation agent mixing in the material A that step S11 prepares,
Under rotating speed is 400r/min, reacts 190min, prepares material B;
S13: be cooled to 118 DEG C after adding plasticizer, stabilizer, terminator mixing in the material B that step S12 prepares,
Under rotating speed is 300r/min, reacts 80min, prepares synthetics;
S2: prepare binding agent, the preparation method of described binding agent, comprise the following steps:
S21: compound concentration is para arrowroot slurry A of 22Be ';
S22: it is 1.7% triglyceride, percarbamide that para arrowroot slurry A in step S21 adds concentration, then in temperature
Degree is 30 DEG C, and speed of agitator is to carry out cross-linked graft reaction 0.8h under 70r/min, prepares slurry B;
S23: add potassium hydroxide and epoxychloropropane in the slurry B of step S22, is then 34 DEG C in temperature, stirring
Rotating speed is to carry out cross-linking reaction 0.3h under 80r/min, prepares slurry C;
S24: be delivered to the slurry C of step S23 in cylindrical drier carry out pre-gelatinized and do at temperature is 143 DEG C
Dry, prepared water content is the material D of 6%;
S25: wind after the material D pulverizing of step S24, excessively 80 mesh sieves is delivered to whirlwind separator and is collected, prepare viscous
Mixture;
S3: by step S1 prepare synthetics, step S2 prepare binding agent, Eucalyptus powder, corn stalk powder, papers for books and periodicals
Powder, plastic bag grain, filler, lubricant, antimildew and antibacterial agent, hygroscopic agent, fire retardant, smoke suppressant, viscosifier, softening agent, ultraviolet
Light absorbers is put in pressure cooker, HIGH PRESSURE TREATMENT 0.6h under pressure is 14MPa, prepares raw material A;
S4: the raw material A that step S3 prepares is put into freezing 4h at temperature is-30 DEG C, prepares raw material B;
S5: by step S4 prepare raw material B put in dehydrator, dry at temperature is 80 DEG C to water content be 5%,
Prepare raw material C;
S6: raw material C step S5 prepared puts in blender, stirs 8min under rotating speed is 400r/min, prepares broken
Grain;
S7: put in extruder by the particle that step S6 prepares, extrudes at temperature is 188 DEG C, cold through mixed liquor
But molding, prepares Wood-plastic material, and described mixed liquor is to be that 96:5:3 makes by water, ethanol, the mass ratio of ethyl salicylate.
Embodiment 2
A kind of Wood-plastic material, in units of weight portion, including following raw material: 42 parts of Eucalyptus powder, corn stalk powder 32 parts, book
Periodical 11 parts of paper powder, plastic bag grain 9 parts, filler 6 parts, synthetics 4 parts, lubricant 1 part, antimildew and antibacterial agent 1 part, hygroscopic agent 1 part,
Fire retardant 2 parts, smoke suppressant 2 parts, binding agent 6 parts, viscosifier 2 parts, softening agent 1 part, UV absorbent 1 part;
Described filler is Kaolin;
Described synthetics is in units of weight portion, including following raw material: propellant 0.3 part, coupling agent 0.6 part, compatilizer
0.4 part, antioxidant 0.3 part, regulator 0.3 part, hardening agent 0.3 part, flocculation agent 0.6 part, plasticizer 0.6 part, stabilizer 0.3
Part, terminator 0.3 part;
Described propellant is aerogel generating agent;
Described coupling agent is furfural;
Described compatilizer is acrylic type compatilizer;
Described antioxidant is WINGSTAYL;
Described regulator is JINHASS;
Described hardening agent is in units of weight portion, including following raw material: styrene 0.08 part, methylcrotonic acid methyl ester 0.08
Part, vinylacetate 0.06 part, cobalt naphthenate 0.04 part, zinc chloride 0.04 part;
Described flocculation agent is aluminium polychlorid;
Described plasticizer is citrate;
Described stabilizer is organic tin stabilizer;
Described terminator is styrene;
Described lubricant is maleic anhydride grafted polyethylene wax;
Described antimildew and antibacterial agent is antimildew and antibacterial agent AEM5700-B;
Described hygroscopic agent is silica gel;
Described fire retardant is in units of weight portion, including following raw material: antimony oxide 5 parts, vinyl triethoxyl silicon
3 parts of alkane, triethyl phosphate 3 parts, 5 parts of magnesium chloride, 2 parts of phenolic resin, bentonite 0.6 part;
Described smoke suppressant is in units of weight portion, including following raw material: zinc molybdate 8 parts, aluminium hydroxide 6 parts, silica flour 2
Part, copper oxide 1 part;
Described binding agent, with tapioca as raw material, carries out cross-linked graft reaction by elder generation with triglyceride, percarbamide,
Then carry out cross-linking reaction with potassium hydroxide and epoxychloropropane, then carry out pre-gelatinized reaction, be finally dried, pulverize, sieve and
?;
Described viscosifier are glycidoxy-propyltrimethoxy silane;
Described softening agent is polyester fiber;
Described UV absorbent is oxybenzoic acid phenyl ester;
The preparation method of described Wood-plastic material, comprises the following steps:
S1: prepare synthetics, the preparation method of described synthetics, comprise the following steps:
S11: propellant, coupling agent, compatilizer, antioxidant mixing are warming up to 115 DEG C, under rotating speed is 100r/min
Reaction 90min, prepares material A;
S12: be warming up to 145 DEG C after adding regulator, hardening agent, flocculation agent mixing in the material A that step S11 prepares,
Under rotating speed is 300r/min, reacts 220min, prepares material B;
S13: be cooled to 115 DEG C after adding plasticizer, stabilizer, terminator mixing in the material B that step S12 prepares,
Under rotating speed is 200r/min, reacts 100min, prepares synthetics;
S2: prepare binding agent, the preparation method of described binding agent, comprise the following steps:
S21: compound concentration is para arrowroot slurry A of 20Be ';
S22: it is 1.5% triglyceride, percarbamide that para arrowroot slurry A in step S21 adds concentration, then in temperature
Degree is 26 DEG C, and speed of agitator is to carry out cross-linked graft reaction 1h under 50r/min, prepares slurry B;
S23: add potassium hydroxide and epoxychloropropane in the slurry B of step S22, is then 32 DEG C in temperature, stirring
Rotating speed is to carry out cross-linking reaction 0.5h under 60r/min, prepares slurry C;
S24: be delivered to the slurry C of step S23 in cylindrical drier carry out pre-gelatinized and do at temperature is 140 DEG C
Dry, prepared water content is the material D of 5%;
S25: wind after the material D pulverizing of step S24, excessively 60 mesh sieves is delivered to whirlwind separator and is collected, prepare viscous
Mixture;
S3: by step S1 prepare synthetics, step S2 prepare binding agent, Eucalyptus powder, corn stalk powder, papers for books and periodicals
Powder, plastic bag grain, filler, lubricant, antimildew and antibacterial agent, hygroscopic agent, fire retardant, smoke suppressant, viscosifier, softening agent, ultraviolet
Light absorbers is put in pressure cooker, HIGH PRESSURE TREATMENT 0.8h under pressure is 12MPa, prepares raw material A;
S4: the raw material A that step S3 prepares is put into freezing 3h at temperature is-40 DEG C, prepares raw material B;
S5: by step S4 prepare raw material B put in dehydrator, dry at temperature is 78 DEG C to water content be 4%,
Prepare raw material C;
S6: raw material C step S5 prepared puts in blender, stirs 9min under rotating speed is 300r/min, prepares broken
Grain;
S7: put in extruder by the particle that step S6 prepares, extrudes at temperature is 185 DEG C, cold through mixed liquor
But molding, prepares Wood-plastic material, and described mixed liquor is to be that 95:4:2 makes by water, ethanol, the mass ratio of ethyl salicylate.
Embodiment 3
A kind of Wood-plastic material, in units of weight portion, including following raw material: 78 parts of Eucalyptus powder, corn stalk powder 48 parts, book
Periodical 14 parts of paper powder, plastic bag grain 13 parts, filler 8 parts, synthetics 6 parts, lubricant 2 parts, antimildew and antibacterial agent 2 parts, hygroscopic agent 2
Part, fire retardant 4 parts, smoke suppressant 4 parts, binding agent 10 parts, viscosifier 4 parts, softening agent 3 parts, UV absorbent 2 parts;
Described filler is Kaolin;
Described synthetics is in units of weight portion, including following raw material: propellant 0.5 part, coupling agent 0.8 part, compatilizer
0.6 part, antioxidant 0.5 part, regulator 0.6 part, hardening agent 0.5 part, flocculation agent 0.8 part, plasticizer 0.9 part, stabilizer 0.4
Part, terminator 0.4 part;
Described propellant is aerogel generating agent;
Described coupling agent is furfural;
Described compatilizer is acrylic type compatilizer;
Described antioxidant is WINGSTAYL;
Described regulator is JINHASS;
Described hardening agent is in units of weight portion, including following raw material: styrene 0.12 part, methylcrotonic acid methyl ester 0.12
Part, vinylacetate 0.1 part, cobalt naphthenate 0.08 part, zinc chloride 0.08 part;
Described flocculation agent is aluminium polychlorid;
Described plasticizer is citrate;
Described stabilizer is organic tin stabilizer;
Described terminator is styrene;
Described lubricant is maleic anhydride grafted polyethylene wax;
Described antimildew and antibacterial agent is antimildew and antibacterial agent AEM5700-B;
Described hygroscopic agent is silica gel;
Described fire retardant is in units of weight portion, including following raw material: antimony oxide 8 parts, vinyl triethoxyl silicon
5 parts of alkane, triethyl phosphate 4 parts, 7 parts of magnesium chloride, 4 parts of phenolic resin, bentonite 1 part;
Described smoke suppressant is in units of weight portion, including following raw material: zinc molybdate 14 parts, aluminium hydroxide 10 parts, silica flour 3
Part, copper oxide 2 parts;
Described binding agent, with tapioca as raw material, carries out cross-linked graft reaction by elder generation with triglyceride, percarbamide,
Then carry out cross-linking reaction with potassium hydroxide and epoxychloropropane, then carry out pre-gelatinized reaction, be finally dried, pulverize, sieve and
?;
Described viscosifier are glycidoxy-propyltrimethoxy silane;
Described softening agent is polyester fiber;
Described UV absorbent is oxybenzoic acid phenyl ester;
The preparation method of described Wood-plastic material, comprises the following steps:
S1: prepare synthetics, the preparation method of described synthetics, comprise the following steps:
S11: propellant, coupling agent, compatilizer, antioxidant mixing are warming up to 125 DEG C, under rotating speed is 300r/min
Reaction 40min, prepares material A;
S12: be warming up to 155 DEG C after adding regulator, hardening agent, flocculation agent mixing in the material A that step S11 prepares,
Under rotating speed is 400r/min, reacts 150min, prepares material B;
S13: be cooled to 120 DEG C after adding plasticizer, stabilizer, terminator mixing in the material B that step S12 prepares,
Under rotating speed is 300r/min, reacts 60min, prepares synthetics;
S2: prepare binding agent, the preparation method of described binding agent, comprise the following steps:
S21: compound concentration is para arrowroot slurry A of 23Be ';
S22: it is 1.8% triglyceride, percarbamide that para arrowroot slurry A in step S21 adds concentration, then in temperature
Degree is 34 DEG C, and speed of agitator is to carry out cross-linked graft reaction 0.6h under 80r/min, prepares slurry B;
S23: add potassium hydroxide and epoxychloropropane in the slurry B of step S22, is then 36 DEG C in temperature, stirring
Rotating speed is to carry out cross-linking reaction 0.2h under 100r/min, prepares slurry C;
S24: be delivered to the slurry C of step S23 in cylindrical drier carry out pre-gelatinized and do at temperature is 145 DEG C
Dry, prepared water content is the material D of 4%;
S25: wind after the material D pulverizing of step S24, excessively 100 mesh sieves is delivered to whirlwind separator and is collected, prepare viscous
Mixture;
S3: by step S1 prepare synthetics, step S2 prepare binding agent, Eucalyptus powder, corn stalk powder, papers for books and periodicals
Powder, plastic bag grain, filler, lubricant, antimildew and antibacterial agent, hygroscopic agent, fire retardant, smoke suppressant, viscosifier, softening agent, ultraviolet
Light absorbers is put in pressure cooker, HIGH PRESSURE TREATMENT 0.5h under pressure is 15MPa, prepares raw material A;
S4: the raw material A that step S3 prepares is put into freezing 2h at temperature is-50 DEG C, prepares raw material B;
S5: by step S4 prepare raw material B put in dehydrator, dry at temperature is 80 DEG C to water content be 3%,
Prepare raw material C;
S6: raw material C step S5 prepared puts in blender, stirs 6min under rotating speed is 500r/min, prepares broken
Grain;
S7: put in extruder by the particle that step S6 prepares, extrudes at temperature is 190 DEG C, cold through mixed liquor
But molding, prepares Wood-plastic material, and described mixed liquor is to be that 100:6:3 makes by water, ethanol, the mass ratio of ethyl salicylate.
The composite can be widely applied to hotel, restaurant, building decoration and fitment, good flame retardation effect, it is impossible to burn and form fire
Flame, stable and reliable for performance, its performance indications are tested by following fire resistance test experiments and Mechanics Performance Testing and are given:
(1) fire resistance test experiments
Sample prepared by above-described embodiment 1-3 is tailored into the platelet of standard, then uses oxygen index measurer HC-2 (south
Jing Shi Jiangning District analytical tool factory) and horizontal vertical burning analyzer CZF-3 (analytical tool factory of Jiangning county) the most right
Wood-plastic material carries out oxygen index (OI) and combustibility measures, oxygen index (OI) 38%-40%, and horizontal vertical combustibility is without catching fire, and cigarette is light,
Flame retardant effect is good.
(2) Mechanics Performance Testing experiment
Sample prepared by above-described embodiment 1-3 tailors growth 115mm, wide 10mm, the standard platelet of thick 2.5mm, then
Tester for elongation 5585 (American I NSTRON) and impact specimen machine ZBC1251-B (Mei Tesi industrial system company) is used to distinguish
Stretching Wood-plastic material and impact test, tensile figure (maximum pull, unit: N) 324.5-358.9, Impact Index is (tough
Property, non-notch), unit: ki/m2, 4.545-5.687, note: draw speed is 2mm/min.
In sum, the Wood-plastic material good flame retardation effect of the present invention, strong shock resistance, toughness is strong, has both obtained excellent
Fire resistance maintain again the preferable mechanical property of Wood-plastic material, be the excellent Wood-plastic material of a kind of performance, can be applicable, have
Significantly economic and social benefit.
Above content it cannot be assumed that the present invention be embodied as be confined to these explanation, technology belonging to the present invention is led
For the those of ordinary skill in territory, without departing from the inventive concept of the premise, it is also possible to make some simple deduction or replace,
All should be considered as belonging to the scope of patent protection that the present invention is determined by the claims submitted to.
Claims (10)
1. a Wood-plastic material, it is characterised in that in units of weight portion, including following raw material: Eucalyptus powder 42-78 part, Semen Maydis
Powder of straw 32-48 part, papers for books and periodicals powder 11-14 part, plastic bag grain 9-13 part, filler 6-8 part, synthetics 4-6 part, lubricant 1-
2 parts, antimildew and antibacterial agent 1-2 part, hygroscopic agent 1-2 part, fire retardant 2-4 part, smoke suppressant 2-4 part, binding agent 6-10 part, viscosifier 2-
4 parts, softening agent 1-3 part, UV absorbent 1-2 part;
Described filler is Kaolin;
Described synthetics is in units of weight portion, including following raw material: propellant 0.3-0.5 part, coupling agent 0.6-0.8 part, phase
Hold agent 0.4-0.6 part, antioxidant 0.3-0.5 part, regulator 0.3-0.6 part, hardening agent 0.3-0.5 part, flocculation agent 0.6-0.8
Part, plasticizer 0.6-0.9 part, stabilizer 0.3-0.4 part, terminator 0.3-0.4 part;
Described hardening agent is in units of weight portion, including following raw material: styrene 0.08-0.12 part, methylcrotonic acid methyl ester
0.08-0.12 part, vinylacetate 0.06-0.1 part, cobalt naphthenate 0.04-0.08 part, zinc chloride 0.04-0.08 part;
Described stabilizer is organic tin stabilizer;
Described lubricant is maleic anhydride grafted polyethylene wax;
Described antimildew and antibacterial agent is antimildew and antibacterial agent AEM5700-B;
Described hygroscopic agent is silica gel;
Described fire retardant is in units of weight portion, including following raw material: antimony oxide 5-8 part, VTES
3-5 part, triethyl phosphate 3-4 part, magnesium chloride 5-7 part, phenolic resin 2-4 part, bentonite 0.6-1 part;
Described smoke suppressant is in units of weight portion, including following raw material: zinc molybdate 8-14 part, aluminium hydroxide 6-10 part, silica flour
2-3 part, copper oxide 1-2 part;
Described binding agent, with tapioca as raw material, carries out cross-linked graft reaction, then by elder generation with triglyceride, percarbamide
Carry out cross-linking reaction with potassium hydroxide and epoxychloropropane, then carry out pre-gelatinized reaction, be finally dried, pulverize, sieve and obtain;
Described viscosifier are glycidoxy-propyltrimethoxy silane;
Described softening agent is polyester fiber;
Described UV absorbent is oxybenzoic acid phenyl ester;
The preparation method of described Wood-plastic material, comprises the following steps:
S1: prepare synthetics, the preparation method of described synthetics, comprise the following steps:
S11: propellant, coupling agent, compatilizer, antioxidant mixing are warming up to 115-125 DEG C, are 100-300r/ at rotating speed
React 40-90min under min, prepare material A;
S12: be warming up to 145-155 DEG C after adding regulator, hardening agent, flocculation agent mixing in the material A that step S11 prepares,
Under rotating speed is 300-400r/min, reacts 150-220min, prepares material B;
S13: be cooled to 115-120 DEG C after adding plasticizer, stabilizer, terminator mixing in the material B that step S12 prepares,
Under rotating speed is 200-300r/min, reacts 60-100min, prepares synthetics;
S2: prepare binding agent, the preparation method of described binding agent, comprise the following steps:
S21: compound concentration is para arrowroot slurry A of 20-23Be ';
S22: it is 1.5%-1.8% triglyceride, percarbamide that para arrowroot slurry A in step S21 adds concentration, then exists
Temperature is 26-34 DEG C, and speed of agitator is to carry out cross-linked graft reaction 0.6-1h under 50-80r/min, prepares slurry B;
S23: adding potassium hydroxide and epoxychloropropane in the slurry B of step S22, be then 32-36 DEG C in temperature, stirring turns
Speed, for carrying out cross-linking reaction 0.2-0.5h under 60-100r/min, prepares slurry C;
S24: be delivered to the slurry C of step S23 in cylindrical drier carry out pre-gelatinized and do at temperature is 140-145 DEG C
Dry, prepare the material D of water content≤6%;
S25: wind after the material D pulverizing of step S24, excessively 60-100 mesh sieve is delivered to whirlwind separator and is collected, prepare viscous
Mixture;
S3: by step S1 prepare synthetics, step S2 prepare binding agent, Eucalyptus powder, corn stalk powder, papers for books and periodicals powder, mould
Pocket grain, filler, lubricant, antimildew and antibacterial agent, hygroscopic agent, fire retardant, smoke suppressant, viscosifier, softening agent, ultra-violet absorption
Agent is put in pressure cooker, HIGH PRESSURE TREATMENT 0.5-0.8h under pressure is 12-15MPa, prepares raw material A;
S4: the raw material A that step S3 prepares is put into freezing 2-4h at temperature≤-30 DEG C, prepares raw material B;
S5: the raw material B that step S4 prepares is put in dehydrator, dries to water content≤5% at temperature is 78-80 DEG C,
Prepare raw material C;
S6: raw material C step S5 prepared puts in blender, stirs 6-9min under rotating speed is 300-500r/min, prepares
Particle;
S7: put in extruder by the particle that step S6 prepares, extrudes at temperature is 185-190 DEG C, through cooling molding,
Prepare Wood-plastic material.
Wood-plastic material the most according to claim 1, it is characterised in that propellant described in step S11 is that aerosol occurs
Agent.
Wood-plastic material the most according to claim 1, it is characterised in that coupling agent described in step S11 is furfural.
Wood-plastic material the most according to claim 1, it is characterised in that compatilizer described in step S11 is acrylic type phase
Hold agent.
Wood-plastic material the most according to claim 1, it is characterised in that antioxidant described in step S11 is
WINGSTAYL。
Wood-plastic material the most according to claim 1, it is characterised in that regulator described in step S12 is JINHASS.
Wood-plastic material the most according to claim 1, it is characterised in that flocculation agent described in step S12 is aluminium polychlorid.
Wood-plastic material the most according to claim 1, it is characterised in that plasticizer described in step S13 is citrate.
Wood-plastic material the most according to claim 1, it is characterised in that terminator described in step S13 is styrene.
Wood-plastic material the most according to claim 1, it is characterised in that the mixed liquor cooling down employing described in step S7 is
It is that 95-100:4-6:2-3 makes by water, ethanol, the mass ratio of ethyl salicylate.