CN106217877A - Use the emergent product that plastic part rapid manufacture special material is made - Google Patents
Use the emergent product that plastic part rapid manufacture special material is made Download PDFInfo
- Publication number
- CN106217877A CN106217877A CN201610637723.1A CN201610637723A CN106217877A CN 106217877 A CN106217877 A CN 106217877A CN 201610637723 A CN201610637723 A CN 201610637723A CN 106217877 A CN106217877 A CN 106217877A
- Authority
- CN
- China
- Prior art keywords
- matrix
- product
- plastic part
- special material
- rapid manufacture
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Use the emergent product made of plastic part rapid manufacture special material, meet an urgent need product main body including one, it is characterised in that described emergent product main body uses plastic part rapid manufacture special material to make;Plastic part rapid manufacture special material includes the matrix for generating product form, and described matrix includes that at least two film layer, two film interlayers are filled with uncured polymer matrix composites.Owing to curing rate can suitably control, therefore the product of needs can be made in the short period of time, and the matrix of same specification allows to make the emergent product such as different disaster relief articles for use, first-aid applicance, outdoor apparatus, emergent succedaneum, to make Emergency use.
Description
The filing date of the original application of this divisional application: on 04 27th, 2012, Application No.: 2012101273933, name
It is referred to as: plastic part rapid manufacture special material and use this material to carry out working of plastics to draw a design or the technique of production.
Technical field
The present invention relates to manufacturing industry, be specifically related to making material and the technique of working of plastics.
Background technology
In the design development of industry new product, in order to improve design, obtain client's accreditation, reality to be made
Object model, thus carry out product appearance accordingly and confirm and functional test etc..But make mock-up and often want die sinking, undoubtedly can
Increase development cost, simultaneously because mould development requires time for, the construction cycle will necessarily be extended.
In the manufacturing process carrying out be pilot (such as: souvenir, the product of limited edition, the articles made to order etc. of small lot)
In, as long as relating to die sinking, cost of manufacture will be of a relatively high.
Summary of the invention
The present invention also aims to provide a kind of emergent product using plastic part rapid manufacture special material to make, to solve
Certainly above-mentioned technical problem.
The present invention can realize by the following technical solutions:
Use the emergent product made of plastic part rapid manufacture special material, meet an urgent need product main body including one, it is characterised in that institute
Stating emergent product main body uses plastic part rapid manufacture special material to make;
Plastic part rapid manufacture special material includes the matrix for generating product form, and described matrix includes at least two
Film layer, two film interlayers are filled with uncured polymer matrix composites.The advantage of this proprietary material is: 1. for non-solid before solidification
State, it is allowed to deformation, can be by being solidified into solid-state after making product form, it is possible to quick Fabrication working of plastics.2. solidification speed
Spend the most controlled, it is allowed to Secondary Design in solidification process.3. store and transport can generate product form
Matrix rather than product, so matrix form motility is high, it is simple to transport and store.
Use plastic part rapid manufacture special material to carry out working of plastics to draw a design or the technique of production, it is characterised in that
Step one, makes the matrix for generating product form, and described matrix includes that at least two film layer, two film interlayers are filled with not
The polymer matrix composites of solidification;Step 2, utilizes matrix to make the product blank with product form;Step 3, by inciting somebody to action
Uncured polymer matrix composites solidification, makes product blank solidifying and setting become product.
During use, can by shearing, stretch, the means such as distortion, utilize matrix to make the product blank needed, then consolidate
Chemical conversion product.During whole, it is not necessary to mould, thus the cost of exploitation and small lot batch manufacture is greatly reduced.Due to
In the case of condition of cure reaches, curing rate is very fast, so invention is relative to the method using Mold Making, can effectively contract
The short construction cycle, obtain rapidly client's accreditation.
Polymer matrix composites are not solid-state before curing, as long as so matrix can generate the form of product i.e.
Can, it is not required that must be that the form of product maybe must possess a certain form.So the degree of freedom of matrix form is higher, permissible
According to transport, store and needing of using makes different forms.The matrix of the most same specification allows making different
Product, such product is provided with uniqueness, it is possible to embody the individual character of designer.And curing rate can suitably control, solid
During change, can give the chance of user secondary amendment, processing mortality is low.
As a kind of preferred version, two described film layers constitute an interlayer, are filled with uncured resin in described interlayer
Based composites.
The manufacture method of above-mentioned matrix:
Method one, the interlayer vacuum pumping of two described film interlayers, film layer and uncured polymer matrix composites are independent
Produce, independently sell, when needing to use, in interlayer, be filled with uncured polymer matrix composites make described matrix.Use
The method being filled with formula after this, user can independently selective membrane layer and the kind of uncured polymer matrix composites, specification
Deng, improve the motility of the initiative of user, making.
Method two, during producing, is filled with uncured resin base and is combined in the interlayer of two described film interlayers
Material, forms described matrix.Use this one-time formed method, relative to after be filled with the method for formula, matrix be readily transported and
Storage, user easily operates.
Method three, uses the manufacture method of Silicon moulds to make matrix.The method technical maturity, reliability is high.
As another kind of preferred version, two described film interlayers are provided with the chamber that at least two is surrounded, institute by part film layer
Uncured polymer matrix composites it are filled with in stating chamber.Each chamber can be connected, it is also possible to relatively independent.Chamber and chamber
The film floor of junction, room can be carried out bending and cutting by connector as the connector of matrix.Technique scheme is easy to
Make the product of same specification, it is adaptable to carrying out the production of be pilot, wherein connector can play assembling prompting, limit
The effect of product specification.
The manufacture method of above-mentioned matrix:
Method one, during producing, is filled with uncured resin base and is combined in the interlayer of two described film interlayers
Material, forms described matrix.Use this one-time formed method.
Method two, uses the manufacture method of Silicon moulds to make matrix.The method technical maturity, reliability is high.
Described matrix is preferably lamellar.Can carry out during use cutting, fold, the one bended etc. in operation or one with
The combination of upper operation, thus make product blank, then solidification obtains product.Described matrix can be provided with bindiny mechanism, matrix
Connected by bindiny mechanism.For complicated structure, respectively each simple parts can be solidified, after solidification, carry out group
Dress, it is also possible to be combined before curing, solidify after combining, in order to be firmly combined with.Can print on described film layer
Decorative pattern, connecting line, cutting wires and/or fold line etc..
Described matrix can also be a matrix with predetermined form, and matrix can directly be cured as product.Matrix can
Directly to exist with a predetermined form, it is also possible to be a predetermined form after reconstruction.Recovery can by inflation form,
The various ways such as the form that the elastic form of film layer, external force makes matrix restore are utilized to restore.
The application of the present invention:
Can apply to industry new product design development, it is possible to process in the short period of time with design consistent
Mock-up, designer can be carried out product appearance and confirm and functional test etc. according to mock-up, thus improve design side
Case, reduces development cost, shortens construction cycle, the purpose of acquisition client accreditation rapidly.
Can apply in article of everyday use, the DIY design of ornament or Character Design, owing to the manufacturing process of product is simple,
Manufacture method is easily mastered, and common consumer can make.
Can apply to the making of emergent product.Owing to curing rate can suitably control, therefore can be in the short period of time
Make the product of needs, and the matrix of same specification allows to make different disaster relief articles for use, first-aid applicance, outdoor apparatus, meet an urgent need
The emergent product such as succedaneum, to make Emergency use.
Can apply to the making of sculpture, can be by the way of the Gypsum Fibrosum that sprays paint outside the product that the present invention makes, sprays etc.
Hollow or the solid sculpture of quick Fabrication, which, during carrying out hollow sculpture making, can effectively save Production Time.
The present invention can also be utilized to make the mould of sculpture, then irrigate the materials such as lime white and carry out sculpture making.
Can also be used to make the protection device of fragile article, such as, make protection with packing, make neonychium, making corner protector
Deng.Particularly film layer uses elastomeric material when.And owing to before uncured, matrix is non-solid, can deform,
So being particularly well-suited to have in the protection of the fragile article of unconventional form, specific form.
Two film interlayers are also provided with at least two microcapsule, are filled with uncured resin in the microcapsule wall of described microcapsule
Based composites.Between described microcapsule and microcapsule be in close contact, the uncured polymer matrix composites in microcapsule after hardening,
The shape of microcapsule is fixed, and then makes matrix be fixed, and then makes product.
Uncured polymer matrix composites it are filled with in space between described microcapsule and microcapsule.When solidifying, fill out
Fill and solidify together with microcapsule at the uncured polymer matrix composites in space, solid further to the position between microcapsule and microcapsule
Fixed, strengthen mechanical strength.At interstitial uncured polymer matrix composites after hardening, can play to space fill and
Adhesive effect, thus it is greatly enhanced mechanical strength.
Described microcapsule can be dispersed in the space of two described film interlayers, is filled with in the space of two described film interlayers
Uncured polymer matrix composites.Relative movement can be allowed between microcapsule.
The spacing of two described film interlayers can be more than the twice of microcapsule average thickness, in order to microcapsule is overlapped mutually, and increases
Strong mechanical performance.
One film layer of described matrix is positioned at lower section, is fixedly arranged above one layer of auxiliary film, capsule is distributed in described auxiliary film
Bubble, using vesicle as described microcapsule wall, is filled with uncured polymer matrix composites in described vesicle.By microcapsule is arranged on
In auxiliary film, make auxiliary film that microcapsule to play certain fixation.And then make microcapsule arrangement will not excessively concentrate at one or
Person excessively disperses.
The space of two described film interlayers can arrange two-layer or two-layer with upper strata auxiliary film.To meet mechanical performance
Demand.
Described auxiliary film is provided with upwards heaves downwardly open vesicle, there is spacing between vesicle and vesicle;In auxiliary film
Part between vesicle with vesicle is fixing with described film layer to be connected, so that vesicle is sealed by film layer, forms described microcapsule.Logical
Cross above-mentioned design, production technology can be greatly simplified.
Between vesicle and vesicle, fill uncured polymer matrix composites, and cover another layer of described film layer up.
Two film interlayers can also be provided with at least two granule, is filled with uncured tree described at least two between granule
Resin-based composite.Granule can be foam beads, bead, glass microballoon, metallic particles, building stones granule, plastic grain etc..
Preferably bead and glass microballoon.By arranging solid particle, reduce the consumption of polymer matrix composites, cost-effective, and
Physical property can be improved.
Two film interlayers can also be filled with the vesicle of gas in being provided with.Thus reduce weight.
Part microcapsule can not be full of by uncured polymer matrix composites, fill in remaining space solid particle or
Person's gas, with tuning performance.The solid particle filled can be foam, bead, metallic particles, building stones granule, plastic grain
Deng.
Two film layers of described matrix are respectively elastomeric material, in order to more random carrying out bend, stretch, manufacture recessed
Fall into or protruding, strengthen the randomness deposited and use.Described microcapsule wall is elastomeric material.So that more random carrying out is curved
Folding, strengthens the randomness deposited and use.
It is opaque for having one in two film layers of described matrix, in case penetrating whole base carrying out light irradiation time line
Body.
An inner side in two film layers of described matrix is reflective material, in order to reflect light back at microcapsule, promotees
Make to realize solidification as early as possible, and save light energy.
Described matrix connects one for supporting and limit the support member of product form.Before not solidifying, it is allowed to
Bending deformation, the distance between matrix and matrix can not get fixing, so the thickness of the resin base product of band support member is in solidification
Before can relatively thin, volume can be the least.And during solidification, it is possible to use the supporting role of shell is limited by support member
The form of matrix, plays the effect of sizing.
As a kind of preferred version, described matrix is provided with one by part of matrix or cavity that all matrix is formed, described
Support member is positioned at described cavity.Cavity can be close cavity, if matrix is the spherical shell shape of a closing, now matrix need to set into
QI KOU, support member is preferably the elastic supporting member for supporting optical member using elastomeric material to make.Can utilize support according to the characteristic of elastomeric material
Part helps matrix to be recovered to preformed shape.Cavity can also be semi-enclosed cavity, if matrix is a semi-enclosed brush holder type,
Support member can be both the elastic supporting member for supporting optical member using elastomeric material to make, and can be again to be filled with uncured light-cured resin base again
The body of condensation material, can make the resin base product molding of band support member by solidifying the form of shell after first solidification support member
For required product.
As another kind of preferred version, described matrix has two, and two matrixes be arranged in parallel, set between described matrix and matrix
There is support member.Described support member is flexible pipe body, is filled with uncured polymer matrix composites in flexible pipe body.Do not entering
Before row solidification, support member and two matrixes are flexibility, it is allowed to bending, and the distance between matrix and matrix can not get solid
It is fixed, so the thickness of micro-capsule photo-curing material before curing can be relatively thin.
Two matrixes can be with peripheral sealing and be provided with an air inlet.When depositing, the air between two matrixes is extracted out, make to prop up
Support member bends, and then makes two matrixes inwardly close up, thinning, it is simple to deposit.Before curing, by air inlet between two matrixes
Space in be filled with air, and then make two matrixes separate and spreadings, make support member stretching open, then carry out photocuring.Thus
Two matrixes and support member is made to solidify respectively, so that the resin base product of described band support member can possess necessarily after hardening
Thickness, and because for hollow structure, so lighter in weight.This is similar to that upper shell is provided with the structure of the cavity of closing,
But support member is preferably filled with the body of uncured light-cured resin based composites.Can also periphery blow-by, periphery
Packing less structure, the convenient matrix to breakage is repaired.
Described support member can be the elastic supporting member for supporting optical member using elastomeric material to make.Described support member can also be for being filled with
The body of uncured light-cured resin based composites, the tube wall of described support member uses elasticity or flexible material to make
Tube wall.
Described support member one end is fixed on the matrix of side, forms a summit, is at least further fixed on separately at described apex
One end of one support member, i.e. one apex is fixed with at least two support members;Side matrix is total to the support member on summit,
Summit no longer it is total on opposite side matrix.Therefore two can constitute a triangular shape structure between support member and matrix, because triangular shape knot
Structure has stable feature, can be with the stability of reinforcing material.
One apex can draw two, three or four support members, it is also possible to draws more.But preferably draw three
Root, the structure of four support members.
Each apex all draws two, three or four support members, so that stabilized structure.
In two described film layers at least one layer be rupture pressure disc, strengthen fastness.It can also be provided that shellproof film.
In two described film layers wherein one layer be anti-ultraviolet film.Place photocuring middle-ultraviolet lamp to leak outside, and after hardening
Also function to completely cut off the effect of ultraviolet.
Two described film layers use flexibility or elastomeric material to make.So that making total present flexibility, allow for
Bending is deposited.Described granule is flexible, in order to makes total present flexibility, allows for bending and deposit.Preferred foams
Grain, flexiplast granule etc..Described microcapsule wall is flexible.So that making total present flexibility, allowing for bending and depositing.
The firming agent of described uncured polymer matrix composites is light curing agent and/or thermal curing agents.Use photocuring
During agent, in two described film layers, at least one film layer is light transmissive material.And described microcapsule wall is light transmissive material.Use heat cure
During agent, the expanded material that can also be mixed into the most foamed in uncured polymer matrix composites, to alleviate the weight of matrix.
Thermal curing agents can use normal temperature cure agent or the agent that is heating and curing.The agent that is heating and curing can be intermediate temperature setting agent or hot setting
Agent.
Described matrix can also be prop up after there is the matrix of form of setting, or be the combination of multiple parts.Make
Used time, after taking-up material is propped up, carry out solidifying the parts that i.e. can obtain needing.Described props up operation, can be by a portion
Part is individually propped up, or by realizing propping up operation after several unit constructions, constitutes the article needed.There is after propping up the shape of setting
The matrix of state.
For with the large components such as ship, house, device housings, the present invention includes two matrixes, and two matrixes be arranged in parallel,
Being provided with support member between described matrix and matrix, described support member is flexible pipe body, is filled with uncured resin in flexible pipe body
Based composites.So that shrinking the mechanical strength after depositing and strengthen solidification.
In advance the base shape after inflation is set to the shape of required parts, when needs use, gas is filled with
The shape of parts can be presented, i.e. can be obtained the parts needed by solidification.
Being provided with fibre reinforced materials in uncured polymer matrix composites, fibre reinforced materials can use glass fibers
One or several in the reinforcing fibers such as dimension, Plant fiber, carbon fiber.
It is mixed with pigment in uncured polymer matrix composites, colours.To adapt to color or patterning requirement.
It is mixed with pigment in uncured polymer matrix composites, colours, to adapt to color or patterning requirement.
It is mixed with pigment in uncured polymer matrix composites and is mixed with electroluminescent powder, and be embedded with wire.So that it is real
Existing electroluminescent, thus realize illumination or beautify.
Also including a light-shielding container, described micro-capsule photo-curing material leaves in described light-shielding container after folding, in order to
In longer-term storage.
Accompanying drawing explanation
Fig. 1 is the plastic part rapid manufacture special material a kind of structural representation when being lamellar;
Fig. 2 is a kind of structural representation of the plastic part rapid manufacture special material being provided with two matrixes;
Fig. 3 is a kind of structural representation that matrix has the plastic part rapid manufacture special material of predetermined form;
Fig. 4 be matrix be a kind of structural representation of the plastic part rapid manufacture special material of the spherical shell shape of a closing;
Fig. 5 is to use plastic part rapid manufacture special material to carry out working of plastics to draw a design or the process chart of production.
Detailed description of the invention
For the technological means making the present invention realize, creation characteristic, reach purpose and be easy to understand with effect, below knot
Conjunction is specifically illustrating, and the present invention is expanded on further.
With reference to Fig. 1, Fig. 2, Fig. 3 or Fig. 4, use the emergent product that plastic part rapid manufacture special material is made, should including one
Anxious product main body, described emergent product main body uses plastic part rapid manufacture special material to make;
Including the matrix for generating product form, described matrix includes at least two film layer 11, fills out between two film layers 11
It is filled with uncured polymer matrix composites.Polymer matrix composites are not solid-state before curing, if so matrix
The form of product can be generated, it is not required that must be that the form of product maybe must possess a certain form.So matrix
The degree of freedom of form is higher, can according to transport, store and needing of using makes different forms.The most same rule
The matrix of lattice allows to make different products, and such product is provided with uniqueness, it is possible to embody the individual character of designer.And solidify
Speed can suitably control, and in the curing process, can give the chance of user secondary amendment, and processing mortality is low.
With reference to Fig. 5, use plastic part rapid manufacture special material to carry out working of plastics and draw a design or the technique of production, step
One, make the matrix for generating product form, described matrix includes at least two film layer 11, is filled with not between two film layers 11
The polymer matrix composites of solidification;Step 2, utilizes matrix to make the product blank with product form;Step 3, by inciting somebody to action
Uncured polymer matrix composites solidification, makes product blank solidifying and setting become product.During use, can be by shearing, drawing
Stretch, the means such as distortion, utilize matrix to make the product blank needed, be then solidified into product.During whole, it is not necessary to mould
Tool, thus the cost of exploitation and small lot batch manufacture is greatly reduced.In the case of reaching at condition of cure, curing rate
Comparatively fast, so invention is relative to the method using Mold Making, can effectively shorten the construction cycle, obtain rapidly client's accreditation.
As a kind of preferred version, two described film layers 11 constitute an interlayer, are filled with uncured tree in described interlayer
Resin-based composite.
The manufacture method of above-mentioned matrix:
Method one, the interlayer vacuum pumping between two described film layers 11, film layer 11 and uncured polymer matrix composites
Individually produce, independently sell, when needing to use, in interlayer, be filled with uncured polymer matrix composites make described matrix.
Use this after be filled with the method for formula, user can independently selective membrane layer 11 and the kind of uncured polymer matrix composites
Class, specification etc., improve the motility of the initiative of user, making.
Method two, during producing, is filled with uncured resin base multiple in the interlayer between two described film layers 11
Condensation material, forms described matrix.Use this one-time formed method, relative to after be filled with the method for formula, matrix is readily transported
And storage, user easily operates.
Method three, uses the manufacture method of Silicon moulds to make matrix.The method technical maturity, reliability is high.
As another kind of preferred version, it is provided with, between two described film layers 11, the chamber that at least two is surrounded by part film layer 11
Room, is filled with uncured polymer matrix composites in described chamber.Each chamber can be connected, it is also possible to relatively independent.Chamber
Room can be carried out bending and cutting by connector as the connector of matrix with the film floor 11 of chamber junction.Above-mentioned technology
Scheme is easy to make the product of same specification, it is adaptable to carrying out the production of be pilot, wherein connector can play assembling
Prompting, the effect of restriction product specification.
The manufacture method of above-mentioned matrix:
Method one, during producing, is filled with uncured resin base multiple in the interlayer between two described film layers 11
Condensation material, forms described matrix.Use this one-time formed method.
Method two, uses the manufacture method of Silicon moulds to make matrix.The method technical maturity, reliability is high.
As another kind of preferred version, described matrix can also be a matrix with predetermined form, and matrix can be straight
Connect and be cured as product.Matrix can directly exist with a predetermined form, it is also possible to is a predetermined form after reconstruction.Restore
Can by the form of inflation, utilize the various ways such as the form that the form of film layer 11 elasticity, external force makes matrix restore to carry out answering
Former.
Described matrix is preferably lamellar.Can carry out during use cutting, fold, the one bended etc. in operation or one with
The combination of upper operation, thus make product blank, then solidification obtains product.Described matrix can be provided with bindiny mechanism, matrix
Connected by bindiny mechanism.For complicated structure, respectively each simple parts can be solidified, after solidification, carry out group
Dress, it is also possible to be combined before curing, solidify after combining, in order to be firmly combined with.Can print on described film layer 11
Decorative pattern processed, connecting line, cutting wires and/or fold line etc..
Implant between film layer 11:
With reference to Fig. 1, Fig. 2 or Fig. 3, between two film layers 11, it is also provided with at least two microcapsule 12, described microcapsule 12 micro-
Uncured polymer matrix composites it are filled with in cyst wall.It is in close contact between described microcapsule 12 and microcapsule 12, in microcapsule 12
Uncured polymer matrix composites after hardening, fixed by the shape of microcapsule 12, and then makes matrix be fixed, and then system
Become product.
It is filled with uncured polymer matrix composites in space between described microcapsule 12 and microcapsule 12.Solidifying
Time, the uncured polymer matrix composites being filled in space solidify together with microcapsule 12, between microcapsule 12 and microcapsule 12
Position is fixed further, strengthens mechanical strength.At interstitial uncured polymer matrix composites after hardening, can play
Space is filled and adhesive effect, thus is greatly enhanced mechanical strength.
Described microcapsule 12 can be dispersed in the space between two described film layers 11, in the space between two described film layers 11
It is filled with uncured polymer matrix composites.Relative movement can be allowed between microcapsule 12.
Spacing between two described film layers 11 can be more than the twice of microcapsule 12 average thickness, in order to microcapsule 12 is the most folded
Add, strengthen mechanical performance.
With reference to Fig. 2, a film layer 11 of described matrix is positioned at lower section, is fixedly arranged above one layer of auxiliary 13, described auxiliary film
Vesicle is distributed on 13, using vesicle as described microcapsule wall, in described vesicle, is filled with uncured polymer matrix composites.Pass through
Microcapsule 12 is arranged in auxiliary film 13, makes auxiliary film 13 that microcapsule 12 is played certain fixation.And then make microcapsule 12 row
Cloth will not excessively concentrate at one or excessively disperse.
Space between two described film layers 11 can arrange two-layer or two-layer with upper strata auxiliary film 13.To meet machinery
Performance requirement.
Described auxiliary film 13 is provided with upwards heaves downwardly open vesicle, there is spacing between vesicle and vesicle;Auxiliary film
Upper vesicle is fixing with described film layer 11 with the part between vesicle to be connected, so that vesicle is sealed by film layer 11, is formed described
Microcapsule 12.By above-mentioned design, production technology can be greatly simplified.
Between vesicle and vesicle, fill uncured polymer matrix composites, and cover another layer of described film layer up
11。
With reference to Fig. 3, at least two granule 15 can also be provided with between two film layers 11, fill out between granule 15 described at least two
It is filled with uncured polymer matrix composites.Granule 15 can be foam beads, bead, glass microballoon, metallic particles, building stones
Granule, plastic grain etc..Preferably bead and glass microballoon.By arranging solid particle, reduce the use of polymer matrix composites
Amount, cost-effective, and physical property can be improved.
The vesicle of gas it is filled with in being also provided with between two film layers 11.Thus reduce weight.
Part microcapsule 12 can not be full of by uncured polymer matrix composites, in remaining space, fill solid particle
Or gas, with tuning performance.The solid particle filled can be foam, bead, metallic particles, building stones granule, plastics
Grain etc..
It is provided with matrix and the structure thereof of support member:
With reference to Fig. 2, Fig. 3 and Fig. 4, described matrix connects one for supporting and limit the support member 14 of product form.Do not having
Having before solidifying, it is allowed to bending deformation, the distance between matrix and matrix can not get fixing, so the resin of band support member 14
The thickness of base product before curing can relatively thin, volume can be the least.And during solidification, it is possible to use support member 14
Supporting role to shell limits the form of matrix, plays the effect of sizing.
As a kind of preferred version, described matrix is provided with one by part of matrix or cavity that all matrix is formed, described
Support member is positioned at described cavity.Cavity can be the cavity closed, and such as Fig. 4, matrix is the spherical shell shape of a closing, and now matrix needs
If air inlet 2, support member 14 is preferably the elastic supporting member for supporting optical member using elastomeric material to make.Can according to the characteristic of elastomeric material,
Support member 14 is utilized to help matrix to be recovered to preformed shape.Cavity can also be semi-enclosed cavity, if matrix is one semiclosed
Brush holder type, support member 14 both can be to use the elastic supporting member for supporting optical member made of elastomeric material, can be again be filled with uncured
The body of light-cured resin based composites, can make band support member by solidifying the form of shell after first solidification support member
Resin base product is shaped to required product.
As another kind of preferred version, with reference to Fig. 2, described matrix has two, and two matrixes be arranged in parallel, described matrix with
Support member 14 it is provided with between matrix.Described support member 14 is flexible pipe body, is filled with uncured resin base and is combined in flexible pipe body
Material.Before not solidifying, support member 14 and two matrixes are flexibility, it is allowed to bending, and matrix and matrix
Between distance can not get fixing, so the thickness of micro-capsule photo-curing material before curing can be relatively thin.
Two matrixes can be with peripheral sealing and be provided with an air inlet 2.When depositing, the air between two matrixes is extracted out, makes
Support member 14 bends, and then makes two matrixes inwardly close up, thinning, it is simple to deposit.Before curing, by air inlet 2 to two
It is filled with air in space between matrix, and then makes two matrixes separate and spreading, make support member 14 stretching open, then carry out light solid
Change.So that two matrixes and support member 14 solidify respectively, thus can possess certain thickness after hardening, and because for hollow
Structure, so lighter in weight.This is similar to that matrix above is provided with the structure of the cavity of closing, but support member 14 is preferably filled out
It is filled with the body of uncured light-cured resin based composites.Can also periphery blow-by, the packing less structure of periphery, convenient
Damaged matrix is repaired.
Described support member 14 can be the elastic supporting member for supporting optical member using elastomeric material to make.Described support member 14 can also be for filling out
Being filled with the body of uncured light-cured resin based composites, the tube wall of described support member 14 is to use elastic or flexible material
The tube wall made.
With reference to Fig. 2, described support member 14 one end is fixed on the matrix of side, forms a summit, at described apex at least
Being further fixed on one end of another support member 14, i.e. one apex is fixed with at least two support members 14;On the matrix of side altogether
The support member 14 on summit, is no longer total to summit on opposite side matrix.Therefore a triangle can be constituted between two support members 14 and matrix
Shape structure, because triangular shape structure has stable feature, can be with the stability of reinforcing material.
One apex can draw two, three or four support members 14, it is also possible to draws more.But preferably draw
The structure of three, four support members.
Each apex all draws two, three or four support members 14, so that stabilized structure.
In two described film layers 11 at least one layer be rupture pressure disc, strengthen fastness.It can also be provided that shellproof film.
In two described film layers 11 wherein one layer be anti-ultraviolet film.Place photocuring middle-ultraviolet lamp to leak outside, and in solidification
After also function to completely cut off ultraviolet effect.
The material of film layer 11:
Described film layer 11 uses flexibility or elastomeric material to make.So that making total present flexibility, allow for curved
Folding is deposited.So that more random carrying out bends, stretches, manufactures depression or projection, strengthen the randomness deposited and use.
Described granule is flexible, in order to makes total present flexibility, allows for bending and deposit.Preferred foams granule, flexibility are moulded
Material granule etc..Described microcapsule wall is flexible.So that making total present flexibility, allowing for bending and depositing.Described microcapsule
Wall is elastomeric material.So that more random carrying out bends, strengthen the randomness deposited and use.
It is opaque for having one in two film layers 11 of described matrix, in case penetrating whole base carrying out light irradiation time line
Body.An inner side in two film layers 11 of described matrix is reflective material, in order to reflect light back at microcapsule, promotes to the greatest extent
Realize solidification soon, and save light energy.
The kind of firming agent:
The firming agent of described uncured polymer matrix composites is light curing agent and/or thermal curing agents.Use photocuring
During agent, in two described film layers 11, at least one film layer 11 is light transmissive material.And described microcapsule wall is light transmissive material.Use heat
During firming agent, the expanded material that can also be mixed into the most foamed in uncured polymer matrix composites, to alleviate matrix
Weight.Thermal curing agents can use normal temperature cure agent or the agent that is heating and curing.The agent that is heating and curing can be intermediate temperature setting agent or high temperature
Firming agent.
Described matrix can also be prop up after there is the matrix of form of setting, or be the combination of multiple parts.Make
Used time, after taking-up material is propped up, carry out solidifying the parts that i.e. can obtain needing.Described props up operation, can be by a portion
Part is individually propped up, or by realizing propping up operation after several unit constructions, constitutes the article needed.There is after propping up the shape of setting
The matrix of state.
For with the large components such as ship, house, device housings, the present invention includes two matrixes, and two matrixes be arranged in parallel,
Being provided with support member between described matrix and matrix, described support member is flexible pipe body, is filled with uncured resin in flexible pipe body
Based composites.So that shrinking the mechanical strength after depositing and strengthen solidification.
In advance the base shape after inflation is set to the shape of required parts, when needs use, gas is filled with
The shape of parts can be presented, i.e. can be obtained the parts needed by solidification.
Being provided with fibre reinforced materials in uncured polymer matrix composites, fibre reinforced materials can use glass fibers
One or several in the reinforcing fibers such as dimension, Plant fiber, carbon fiber.
It is mixed with pigment in uncured polymer matrix composites, colours.To adapt to color or patterning requirement.
It is mixed with pigment in uncured polymer matrix composites, colours, to adapt to color or patterning requirement.
It is mixed with pigment in uncured polymer matrix composites and is mixed with electroluminescent powder, and be embedded with wire.So that it is real
Existing electroluminescent, thus realize illumination or beautify.
Also including a light-shielding container, described micro-capsule photo-curing material leaves in described light-shielding container after folding, in order to
In longer-term storage.
The application of the present invention:
Can apply to industry new product design development, it is possible to process in the short period of time with design consistent
Mock-up, designer can be carried out product appearance and confirm and functional test etc. according to mock-up, thus improve design side
Case, reduces development cost, shortens construction cycle, the purpose of acquisition client accreditation rapidly.
Can apply in article of everyday use, the DIY design of ornament or Character Design, owing to the manufacturing process of product is simple,
Manufacture method is easily mastered, and common consumer can make.
Can apply to the making of emergent product.Owing to curing rate can suitably control, therefore can be in the short period of time
Make the product of needs, and the matrix of same specification allows to make different disaster relief articles for use, first-aid applicance, outdoor apparatus, meet an urgent need
The emergent product such as succedaneum, to make Emergency use.
Can also be used to make the protection device of fragile article, such as, make protection with packing, make neonychium, making corner protector
Deng.Particularly film layer 11 uses elastomeric material when.And owing to before uncured, matrix is non-solid, can become
Shape, so being particularly well-suited to have in the protection of the fragile article of unconventional form, specific form.And body portion can be controlled
Solidification, the part of solidification plays the effect of defined position, and uncured part plays buffering ambient pressure, the effect of impulsive force.
This is matrix at least two, and two matrix surroundings seal, and can be filled with buffering object, such as gas, foam etc. between matrix.Can
To be initially charged with buffering object, then seal.
Can apply to the making of sculpture, can by spraying paint outside the product that the present invention makes, the side of brush lime white etc.
Hollow or the solid sculpture of formula quick Fabrication, which is during carrying out hollow sculpture making, when effectively can save making
Between.The present invention can also be utilized to make the mould of sculpture, then irrigate the materials such as lime white and carry out sculpture making.
Utilize plastic part rapid manufacture special material to make the technique of sculpture, step one, make and be used for generating product form
Matrix, described matrix includes at least two film layer 11, is filled with uncured polymer matrix composites between two film layers 11;Step
Rapid two, utilize matrix to build the profile of sculpture;Step 3, by uncured polymer matrix composites solidification, makes matrix solidification fixed
Type;Step 4, sprays paint to the theca externa 11 of matrix and/or brush Gypsum Fibrosum, brush lime white, makes sculpture.
Following technology utilization plastic part rapid manufacture special material can also be used to make sculpture, and step one, making is used for
Generating the matrix of product form, described matrix includes at least two film layer 11, is filled with uncured resin between two film layers 11
Based composites;Step 2, utilizes matrix to build the outline of sculpture, described outline leaves for injecting opening of lime white
Mouthful;Step 3, by uncured polymer matrix composites solidification, makes matrix solidifying and setting, constitutes the shell of sculpture;Step 4,
By injecting Gypsum Fibrosum and/or Calx in outward opening shell, sculpture is made in Gypsum Fibrosum and/or Calx hardening.That injects in step 4 can
To be Gypsum Fibrosum and/or Calx slurry, it is also possible to be Gypsum Fibrosum and/or pulverized limestone.Inject in step 4 can be Gypsum Fibrosum and/or stone
During ashes, Gypsum Fibrosum and/or the liquid of pulverized limestone hardening can be made by addition so that it is hardening.And pulverized limestone meeting when ripening
Release substantial amounts of heat, it is possible to further enhance the state of cure of the polymer matrix composites containing thermal curing agents.After step 4, also
The shell being made up of matrix can be removed.Shell can be as the external protection of sculpture, during preventing carrying and moving,
Damage is caused in inside.
The ultimate principle of the present invention and principal character and advantages of the present invention have more than been shown and described.The technology of the industry
Personnel, it should be appreciated that the present invention is not restricted to the described embodiments, simply illustrating this described in above-described embodiment and description
The principle of invention, without departing from the spirit and scope of the present invention, the present invention also has various changes and modifications, and these become
Change and improvement both falls within scope of the claimed invention.Claimed scope by appending claims and
Equivalent defines.
Claims (7)
1. use the emergent product made of plastic part rapid manufacture special material, meet an urgent need product main body including one, it is characterised in that described
Emergent product main body uses plastic part rapid manufacture special material to make;
Plastic part rapid manufacture special material includes the matrix for generating product form, and described matrix includes at least two film
Layer, two film interlayers are filled with uncured polymer matrix composites.
The emergent product that employing plastic part rapid manufacture special material the most according to claim 1 is made, it is characterised in that: two
Individual described film layer constitutes an interlayer, is filled with uncured polymer matrix composites in described interlayer.
The emergent product that employing plastic part rapid manufacture special material the most according to claim 2 is made, it is characterised in that: two
The interlayer vacuum pumping of individual described film interlayer, when needing to use, is filled with uncured polymer matrix composites in interlayer and makes
Described matrix.
The emergent product that employing plastic part rapid manufacture special material the most according to claim 1 is made, it is characterised in that: two
Individual described film interlayer is provided with the chamber that at least two is surrounded by part film layer, is filled with uncured resin base multiple in described chamber
Condensation material.
The emergent product that employing plastic part rapid manufacture special material the most according to claim 4 is made, it is characterised in that: chamber
The film floor of room and chamber junction as the connector of matrix, carries out bending by connector, cutting.
6. the emergent product made according to the employing plastic part rapid manufacture special material described in claim 1,2,3,4 or 5, it is special
Levy and be: printing pattern, connecting line, cutting wires and/or fold line on described film layer.
7. the emergent product made according to the employing plastic part rapid manufacture special material described in claim 1,2,3,4 or 5, it is special
Levy and be: described matrix is a matrix with predetermined form.