CN106189071A - A kind of Abrasion Resistance Modified Nylon - Google Patents
A kind of Abrasion Resistance Modified Nylon Download PDFInfo
- Publication number
- CN106189071A CN106189071A CN201610736237.5A CN201610736237A CN106189071A CN 106189071 A CN106189071 A CN 106189071A CN 201610736237 A CN201610736237 A CN 201610736237A CN 106189071 A CN106189071 A CN 106189071A
- Authority
- CN
- China
- Prior art keywords
- parts
- abrasion resistance
- nylon
- resistance modified
- modified nylon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The open a kind of Abrasion Resistance Modified Nylon of the present invention, is made up of the raw material components of following number: 120 150 parts of pc, 100 150 parts of pbt plastics, 150 180 parts of ppsu, 80 100 parts of pvc, 60 80 parts of polyphenylene oxide, 150 200 parts of PPS, 120 150 parts of PSF, 160 200 parts of PEEK, 5 10 parts of Colophonium, 10 12 parts of glycerol, 8 10 parts of adipic acids, 20 28 parts of nitrile rubbers, 10 15 parts of glass dust, 8 10 parts of aminopropyl triethoxysilanes, 10 15 parts of acrylonitrile butadient styrenes, 12 15 parts of activated aluminas.This Abrasion Resistance Modified Nylon improves the rigidity of nylon, wearability;For the relation of balance wearability with fragility, add a certain amount of flexible elastomer and play toughness reinforcing and wear-resisting effect;Improve the wearability of nylon, surface lubrication and brightness effect.
Description
Technical field
The present invention relates to the technical field of a kind of macromolecular material, particularly relate to a kind of Abrasion Resistance Modified Nylon.
Background technology
Nylon has good self lubricity, wearability, oil resistivity and good comprehensive mechanical property, machinery, transmission,
Seal in uniform wearability requires higher field and be widely used.Have the wear-resisting PA66 skill of several types at present
Art, PA66 as the most modifies in caoutchouc elasticity, graphite modified PA66, molybdenum sulfide modified Pa 66 etc..In recent years, utilized
The modified abrasion resistant PA66 of PTFE micropowder anti-wear agent exploitation, obtains market and extensively favors, and wearability is superior, modified with molybdenum sulfide
PA66 compares, and can prepare white article, but both there is addition hour, and wearability is general;Addition is big, modified processing
The shortcomings such as difficulty, cost are high, product surface is the brightest.It is contemplated that by PA66 resin is modified so that it is possess
Preferably wearability, surface lubrication, brightness effect and preferable comprehensive mechanical property.
Summary of the invention
The invention aims to overcome the upper existing shortcoming stating prior art, it is provided that a kind of Abrasion Resistance Modified Nylon, should
Abrasion Resistance Modified Nylon improves the rigidity of nylon, wearability;For balance wearability and the relation of fragility, add a certain amount of flexibility
Elastomer plays toughness reinforcing and wear-resisting effect;Improve the wearability of nylon, surface lubrication and brightness effect.
The technical solution adopted for the present invention to solve the technical problems is: a kind of Abrasion Resistance Modified Nylon, by following number
Raw material components forms: 120-150 part pc, 100-150 part pbt plastics, 150-180 part ppsu, 80-100 part pvc, 60-80 part are gathered
Phenylate, 150-200 part PPS, 120-150 part PSF, 160-200 part PEEK, 5-10 part Colophonium, 10-12 part glycerol, 8-10 part oneself
Diacid, 20-28 part nitrile rubber, 10-15 part glass dust, 8-10 part aminopropyl triethoxysilane, 10-15 part acrylic nitrile-butadiene
Diene-styrene copolymer, 12-15 part activated alumina.
Further, the number of each raw material components is: 120 parts of pc, 100 parts of pbt plastics, 150 parts of ppsu, 80 parts of pvc, 60
Part polyphenylene oxide, 150 parts of PPS, 120 parts of PSF, 160 parts of PEEK, 5 parts of Colophonium, 10 parts of glycerol, 8 parts of adipic acids, 20 parts of nitrile rubbers,
10 parts of glass dust, 8 parts of aminopropyl triethoxysilanes, 10 parts of acrylonitrile-butadiene-styrene copolymers, 12 parts of active oxidations
Aluminum.
Or, the number of each raw material components is: 150 parts of pc, 150 parts of pbt plastics, 180 parts of ppsu, 100 parts of pvc, 80
Part polyphenylene oxide, 200 parts of PPS, 150 parts of PSF, 200 parts of PEEK, 10 parts of Colophonium, 12 parts of glycerol, 10 parts of adipic acids, 28 parts of butyronitrile rubbers
Glue, 15 parts of glass dust, 10 parts of aminopropyl triethoxysilanes, 15 parts of acrylonitrile-butadiene-styrene copolymers, 15 parts of activity
Aluminium oxide.
In sum, the Abrasion Resistance Modified Nylon of the present invention improves the rigidity of nylon, wearability;For balance wearability with crisp
Property relation, add a certain amount of flexible elastomer and play toughness reinforcing with wear-resisting effect;Improve the wearability of nylon, surface lubrication with
Brightness effect.
Detailed description of the invention
Embodiment 1
A kind of Abrasion Resistance Modified Nylon described by the present embodiment 1, is made up of the raw material components of following number: 120 parts of pc, 100 parts
Pbt plastics, 150 parts of ppsu, 80 parts of pvc, 60 parts of polyphenylene oxide, 150 parts of PPS, 120 parts of PSF, 160 parts of PEEK, 5 parts of Colophonium, 10 parts
Glycerol, 8 parts of adipic acids, 20 parts of nitrile rubbers, 10 parts of glass dust, 8 parts of aminopropyl triethoxysilanes, 10 parts of acrylic nitrile-butadienes two
Alkene-styrol copolymer, 12 parts of activated aluminas.
Embodiment 2
A kind of Abrasion Resistance Modified Nylon described by the present embodiment 2, is made up of the raw material components of following number: 150 parts of pc, 150 parts
Pbt plastics, 180 parts of ppsu, 100 parts of pvc, 80 parts of polyphenylene oxide, 200 parts of PPS, 150 parts of PSF, 200 parts of PEEK, 10 parts of Colophonium, 12
Part glycerol, 10 parts of adipic acids, 28 parts of nitrile rubbers, 15 parts of glass dust, 10 parts of aminopropyl triethoxysilanes, 15 parts of acrylonitrile-
BS, 15 parts of activated aluminas.
The above, be only presently preferred embodiments of the present invention, and technical scheme is not made any form
On restriction.Any simple modification that above example is made by every technical spirit according to the present invention, equivalent variations with repair
Decorations, all still fall within the range of technical scheme.
Claims (3)
1. an Abrasion Resistance Modified Nylon, it is characterised in that be made up of the raw material components of following number: 120-150 part pc, 100-
150 parts of pbt plastics, 150-180 part ppsu, 80-100 part pvc, 60-80 part polyphenylene oxide, 150-200 part PPS, 120-150 parts
PSF, 160-200 part PEEK, 5-10 part Colophonium, 10-12 part glycerol, 8-10 part adipic acid, 20-28 part nitrile rubber, 10-15 part
Glass dust, 8-10 part aminopropyl triethoxysilane, 10-15 part acrylonitrile-butadiene-styrene copolymer, 12-15 part activity
Aluminium oxide.
A kind of Abrasion Resistance Modified Nylon the most according to claim 1, it is characterised in that the number of each raw material components is: 120 parts
Pc, 100 parts of pbt plastics, 150 parts of ppsu, 80 parts of pvc, 60 parts of polyphenylene oxide, 150 parts of PPS, 120 parts of PSF, 160 parts of PEEK, 5 parts
Colophonium, 10 parts of glycerol, 8 parts of adipic acids, 20 parts of nitrile rubbers, 10 parts of glass dust, 8 parts of aminopropyl triethoxysilanes, 10 part third
Alkene nitrile-BS, 12 parts of activated aluminas.
A kind of Abrasion Resistance Modified Nylon the most according to claim 1, it is characterised in that the number of each raw material components is: 150
Part pc, 150 parts of pbt plastics, 180 parts of ppsu, 100 parts of pvc, 80 parts of polyphenylene oxide, 200 parts of PPS, 150 parts of PSF, 200 parts of PEEK,
10 parts of Colophonium, 12 parts of glycerol, 10 parts of adipic acids, 28 parts of nitrile rubbers, 15 parts of glass dust, 10 parts of aminopropyl triethoxysilanes,
15 parts of acrylonitrile-butadiene-styrene copolymers, 15 parts of activated aluminas.