CN106187323B - A kind of Imitation Rock Porcelain Tiles and its production method with three-dimensional decorative effect - Google Patents
A kind of Imitation Rock Porcelain Tiles and its production method with three-dimensional decorative effect Download PDFInfo
- Publication number
- CN106187323B CN106187323B CN201510217605.0A CN201510217605A CN106187323B CN 106187323 B CN106187323 B CN 106187323B CN 201510217605 A CN201510217605 A CN 201510217605A CN 106187323 B CN106187323 B CN 106187323B
- Authority
- CN
- China
- Prior art keywords
- porcelain tiles
- imitation rock
- rock porcelain
- fabric
- starch adhesive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of Imitation Rock Porcelain Tiles and its production method with three-dimensional decorative effect, comprising the following steps: (1) prepare Imitation Rock Porcelain Tiles green body powder according to a conventional method；(2) Imitation Rock Porcelain Tiles fabric is prepared；(3) Imitation Rock Porcelain Tiles body preparation；(4) body drying；(5) starch adhesive A is drenched；(6) fabric B is printed；(7) it is dried after applying cloth fabric；(8) spray infiltration ink；(9) it is burnt into；(10) edging.The beneficial effects of the invention are as follows cost increases caused by solving starch adhesive in the prior art and assistant toner dosage greatly, pattern texture lacks the problem of solid grain expression, it solves the show-through inaesthetic technical problem of the deep processings such as existing ceramic brick with permeated pattern fluting, chamfering simultaneously, provides a kind of production method of the richer Imitation Rock Porcelain Tiles of more environmentally friendly economy, decorative effect.
Description
Technical field
The present invention relates to architectural pottery technical field, more particularly to a kind of Imitation Rock Porcelain Tiles with three-dimensional decorative effect and its
Production method.
Background technique
Currently, seeping flower porcelain brick product is to achieve the effect that imitation natural stone line or wood grain, " seeping flower " polishing skill is generallyd use
Art, and experienced in terms of seeping flower process from the infiltration that silk-screen printing includes soluble-salt and spend liquid to the upgrading of spray infiltration ink.In
State patent CN102795892B describes a kind of infiltration flower Imitation Rock Porcelain Tiles and its production method, throws face by drenching porcelain in green body layer surface
On the one hand the penetration depth for seeping flower salt can be down to 0.3 ~ 0.5mm from 2 ~ 3mm of traditional pattern permeating tile, expand and seeped flower salt by slurry
Using type, pattern is enriched；On the other hand the grinding thichness for reducing polishing process, reduces waste material yield.Assistant toner
The use of cooperation ink-jet infiltration ink has been obviously improved the color saturation and lightness of decorative pattern, and clean mark is fine and smooth.However,
Single use ink-jet realizes that imitation natural stone line or wood grain make the decoration of ceramic tile be only limited to planar scale, for stone pattern or wood
But it is short of the expression of stereoscopic level in the gully of hole and fluctuating in line.In addition, starch adhesive, which is all made of multiple tracks glaze pouring, applies cloth, face
It is larger to starch dosage, and the assistant toner of the higher cost accordingly introduced is also on the high side, causes production cost higher.
Summary of the invention
Present invention aim to address starch adhesive in the prior art and assistant toner dosage higher cost caused greatly, pattern textures
The problem of lacking solid grain expression, provide a kind of production method of the richer Imitation Rock Porcelain Tiles of more environmentally friendly economy, decorative effect.
It is a further object of the present invention to provide the Imitation Rock Porcelain Tiles with three-dimensional decorative effect with this method production.
The technical scheme is that a kind of production method of the Imitation Rock Porcelain Tiles with three-dimensional decorative effect, including following step
It is rapid:
(1) Imitation Rock Porcelain Tiles green body powder is prepared according to a conventional method, it is spare；
(2) Imitation Rock Porcelain Tiles fabric is prepared, the Imitation Rock Porcelain Tiles fabric of use is divided into starch adhesive A and two kinds of fabric B, starch adhesive A and fabric B's
Siccative chemical composition is consistent, similar to green body powder in step (1), but wherein K2O+Na2O:6 ~ 8%, impurity≤4%(are weight
Percentage)；The siccative of starch adhesive A carries out ingredient using feldspar poor material and kaolin families plastic raw material, but the siccative of fabric B is complete
Portion carries out ingredient using aluminium oxide, quartz, feldspar non-plastic raw material；It is 325 mesh screen residues that the slurry of two kinds of fabrics, which controls fineness,
For amount within 0.5%, specific gravity is 1.60 ~ 1.90g/cm3, wherein the siccative of starch adhesive A and auxiliary additive wet ball grinding are drenched at satisfaction
The slurry of performance requirement is applied, the siccative and auxiliary additive wet ball grinding of fabric B is dried after meeting size performance requirement, made
At dry powder, and the printing fabric for meeting printing performance is mixed with stamp-pad ink, auxiliary additive, it is spare；
(3) Imitation Rock Porcelain Tiles body preparation: by Imitation Rock Porcelain Tiles green body powder obtained in step (1) according to designed pattern line
Reason carries out multitube cloth, cloth is then spread in brick machine die cavity, under the pressure of 20 ~ 50MPa, by Imitation Rock Porcelain Tiles green body powder pressure
Imitation Rock Porcelain Tiles green compact are made；
(4) body drying: Imitation Rock Porcelain Tiles green compact prepared by step (3) are dried at 150 ~ 300 DEG C in dry kiln；
(5) it drenches starch adhesive A: the Imitation Rock Porcelain Tiles starch adhesive A of step (2) preparation is applied into the Imitation Rock Porcelain Tiles life of cloth after the drying with glaze pouring
Base surface, the weight of the applied starch adhesive of unit area are 400 ~ 800g/m2；
(6) it prints fabric B: Imitation Rock Porcelain Tiles fabric B prepared by step (2) being applied into cloth with printing technology and was drenching starch adhesive A's
Billet surface；
(7) it is dried after applying cloth fabric: the Imitation Rock Porcelain Tiles green compact for applying fabric is dried at 150 ~ 300 DEG C in dry kiln again
It is dry；
(8) it spray infiltration ink: is sprayed on Imitation Rock Porcelain Tiles green body, is cooperated by designed pattern using Digital ink-jet printer
Blank pattern texture, so that brick body surface and green body have similar texture and quality；
(9) it is burnt into: the Imitation Rock Porcelain Tiles green compact that step (8) is jetted through infiltration ink being placed in roller kilns and are burnt using conventional Imitation Rock Porcelain Tiles
At temperature schedule, pressure regime and atmosphere system, once-firing, firing temperature is 1150 ~ 1250 DEG C, firing period is 40 ~
Imitation Rock Porcelain Tiles semi-finished product are made in 90min；
(10) edging: using conventional edging process equipment, double of finished bricks carries out edging processing, and being made has three-dimensional dress
Adorn the Imitation Rock Porcelain Tiles finished product of effect.
It is all not add special instruction in above step, all use conventional control means in the prior art.
To complete second goal of the invention, using the porcelain with three-dimensional decorative effect by above-mentioned steps production
Brick.
Contain kaolin families plastic raw material in the formula of the prior art, printing fabric is directly prepared into, easily because of plasticity
Raw material sticky net and influence printing performance, in step (2) of the present invention fabric B be all made of aluminium oxide, quartz, feldspar non-plastic raw material into
Row ingredient, preferably solves problems.
It include auxiliary colorant ZnO, TiO in the auxiliary additive of fabric B in step (2)2One of or a variety of, starch adhesive
ZnO, TiO are not included in the auxiliary additive of A2Etc. auxiliary colorants.
As further technical solution, the auxiliary additive additive amount of fabric B is calculated as in step (2) with fabric siccative
ZnO is 0.2 ~ 1%, TiO2It is 0.2 ~ 5%.
As further technical solution, silk-screen printing or glue roller printing is can be used in the printing surface sizing process in step (6).
As further technical solution, ink-jet surface thickness is 0.3 ~ 1.0mm in step (8).
Polishing or soft throwing process can be used after the processing of step (10) edging as further technical solution.If right
Imitation Rock Porcelain Tiles surface prepared by the present invention is processed by shot blasting, can be obtained a kind of with the ceramic polished of three-dimensional decorative effect
Brick.It is handled according to soft throwing, that is, obtains a kind of porcelain matt brick with three-dimensional decorative effect.
Compared with the prior art of the reports such as patent document CN102795892B, the present invention has following several respects advantage:
1, material is saved
The prior art is to reach suitable surface thickness, the technique for mostly using the identical starch adhesive of leaching twice in actual operation,
And a certain proportion of auxiliary colorant is introduced in starch adhesive, to cooperate subsequent ink-jetting pattern, enhance the hair color effect of ink.
Different, the present invention applies in first of starch adhesive A of cloth and does not add ZnO, TiO2Etc. auxiliary colorants, with prior art phase
Than reducing the dosage of auxiliary colorant, reducing production cost.The second fabric that the present invention applies cloth does not use leaching starch adhesive then
Technique, but dried after the siccative of fabric B and auxiliary additive wet ball grinding are met size performance requirement, dry powder is made, and
It is mixed with the printing fabric for meeting printing performance with stamp-pad ink, auxiliary additive, is printed onto fabric B by the way of printing
The billet surface of starch adhesive A was drenched, precoat can be greatly reduced using printing technology in leaching starch adhesive compared with prior art, fabric B
Thickness saves the dosage of starch adhesive.
2, loss is reduced
The leaching starch adhesive process of the prior art, starch adhesive Chang Yin are trapped in recovering tray or are adhered in conveyor belt and cause to waste
And loss, waste are about 20% or so of starch adhesive total amount, and the present invention when applying cloth second fabric using printer
Skill, then can substantially reduce the waste of fabric, and fabric utilization rate is up to 95% or more.
3, texture-rich
Existing ink-jet seeps flower Imitation Rock Porcelain Tiles and generally uses pure color green body, and texture is only limitted to the ink-jetting pattern of billet surface, decoration
Effect is dull, and the present invention forms certain decoration line by the way that green body powder is carried out multitube cloth by designed pattern texture
Road, and digital ink-jet infiltration technology is combined, so that incrustation and green body texture organically combine, greatly enrich conventional ink-jet infiltration
The decorative effect of flower Imitation Rock Porcelain Tiles.
Existing ink-jet seeps flower Imitation Rock Porcelain Tiles using leaching twice starch adhesive technique, and starch adhesive all covers billet surface, can only be simple
Supporting body of the ground as subsequent i alphakjet pattern, starch adhesive layer are confined to two-dimension plane structure, it is difficult to realize the decoration effect of stereo concave-convex
Fruit.And the present invention can realize different lines textures using printing web process as needed, really realize that point-line-face is more
Kind the texture even combination of Z-Correct bump mapping Z-correct.
In addition, the present invention prints web process can print using part is uneven.Due to common printed glaze fire degree is lower,
The lines of printing easily melt, and have Self-leveling effect, and filament texture is easily filled and led up because glaze melts, so that printing lines are confined to
Thick line texture, decoration texture are not fine and smooth enough.Compared with common printed glaze, the fiery degree of fabric of the present invention is high, glass phase is few, does not have
Have a temperature flowing of common glaze, thus a printable stria, stria since fiery degree height will not soften collapsing in firing,
And remain to after firing processing, therefore decoration texture is finer and smoother, and the ditch of stereoscopic three-dimensional level can be formed after firing processing
The hole of gully and a small amount of uneven distribution, to more realistically reproduce the crackle of lithotome and the sagging line of stomata or wood grain
Road and hole etc..
Compared with prior art, present invention beneficial effect obtained is that solve starch adhesive in the prior art and assistant toner use
The problem of higher cost caused by amount is big, pattern texture lacks solid grain expression, while solving existing ceramic brick with permeated pattern and opening
The show-through inaesthetic technical problem of the deep processings such as slot, chamfering.Printing fabric mode has not only significantly saved the consume of fabric dosage, drop
Low production cost, while the high fire degree property of fabric still to be able to maintain original lines texture after burning, realization 3 D stereo level
Decorative effect, matched with green body entire body cloth texture, realize the reproduction true to nature of stone pattern or wood texture.
Specific embodiment
Embodiment 1
(1) Imitation Rock Porcelain Tiles green body powder is prepared according to a conventional method, and it is spare to deploy 3 kinds of color powders；
(2) Imitation Rock Porcelain Tiles fabric is prepared, fabric A carries out ingredient, face using feldspar poor material and kaolin families plastic raw material
The siccative of material B all uses aluminium oxide, quartz, feldspar non-plastic raw material to carry out ingredient, and the slurry of wet ball grinding, two kinds of fabrics is equal
Controlling fineness is 325 mesh sieve margins within 0.5%, specific gravity 1.78g/cm3, wherein the siccative of starch adhesive A and auxiliary additive are wet
Method ball milling applies the slurry of performance requirement at leaching is met, and the siccative and auxiliary additive wet ball grinding of fabric B meets slurry properties
It is dried after capable of requiring, dry powder is made, and be mixed with the printing fabric for meeting printing performance with stamp-pad ink, auxiliary additive, it is spare.
The chemical composition range of two kinds of fabrics is (parts by weight): SiO2: 66%, Al2O3: 17%, MgO+CaO:2.0%, K2O+Na2O:5%, it is remaining
Amount is impurity, also needs additional ZnO 0.2%, TiO in fabric B2 1%。
(3) Imitation Rock Porcelain Tiles body preparation: by Imitation Rock Porcelain Tiles green body powder obtained in step (1) according to designed pattern line
Reason, carry out multitube cloth, then spread cloth in brick machine die cavity, under the pressure of 30MPa, by Imitation Rock Porcelain Tiles green body powder pressing at
Imitation Rock Porcelain Tiles green compact；
(4) Imitation Rock Porcelain Tiles green compact prepared by step (3) are dried at 150 DEG C in dry kiln；
(5) it drenches starch adhesive A: the Imitation Rock Porcelain Tiles starch adhesive A of step (2) preparation is applied into the Imitation Rock Porcelain Tiles life of cloth after the drying with glaze pouring
Base surface, the weight of the applied starch adhesive of unit area are 800g/m2；
(6) it prints fabric B: Imitation Rock Porcelain Tiles fabric B prepared by step (2) being applied into cloth with silk-screen printing technique and was drenching starch adhesive
The billet surface of A；
(7) it is dried after applying cloth fabric: the Imitation Rock Porcelain Tiles green compact for applying fabric is dried at 200 DEG C in dry kiln again；
(8) it spray infiltration ink: is sprayed on Imitation Rock Porcelain Tiles green body, is cooperated by designed pattern using Digital ink-jet printer
Blank pattern texture, so that brick body surface and green body have similar texture and quality, ink jet layer is with a thickness of 0.3mm；
(9) it is burnt into: the Imitation Rock Porcelain Tiles green compact that step (8) is jetted through infiltration ink being placed in roller kilns and are burnt using conventional Imitation Rock Porcelain Tiles
At temperature schedule, pressure regime and atmosphere system, once-firing, firing temperature is 1160 DEG C, firing period 85min, is made
Imitation Rock Porcelain Tiles semi-finished product；
(10) edging: using conventional edging process equipment, double of finished bricks carries out edging processing, that is, obtaining one kind has
The Imitation Rock Porcelain Tiles finished product of the natural surface of three-dimensional decorative effect.
Embodiment 2
(1) Imitation Rock Porcelain Tiles green body powder is prepared according to a conventional method, and it is spare to deploy 5 kinds of color powders；
(2) Imitation Rock Porcelain Tiles fabric is prepared, fabric A carries out ingredient, face using feldspar poor material and kaolin families plastic raw material
The siccative of material B all uses aluminium oxide, quartz, feldspar non-plastic raw material to carry out ingredient, and the slurry of wet ball grinding, two kinds of fabrics is equal
Controlling fineness is 325 mesh sieve margins within 0.5%, specific gravity 1.80g/cm3, wherein the siccative of starch adhesive A and auxiliary additive are wet
Method ball milling applies the slurry of performance requirement at leaching is met, and the siccative and auxiliary additive wet ball grinding of fabric B meets slurry properties
It is dried after capable of requiring, dry powder is made, and be mixed with the printing fabric for meeting printing performance with stamp-pad ink, auxiliary additive, it is spare.
The chemical composition range of two kinds of fabrics is (parts by weight): SiO2: 62%, Al2O3: 19%, MgO+CaO:2.0%, K2O+Na2O:7%, it is remaining
Amount is impurity, also needs additional ZnO 0.5%, TiO in fabric B2 4%。
(3) Imitation Rock Porcelain Tiles body preparation: by Imitation Rock Porcelain Tiles green body powder obtained in step (1) according to designed pattern line
Reason, carry out multitube cloth, then spread cloth in brick machine die cavity, under the pressure of 40MPa, by Imitation Rock Porcelain Tiles green body powder pressing at
Imitation Rock Porcelain Tiles green compact；
(4) Imitation Rock Porcelain Tiles green compact prepared by step (3) are dried at 200 DEG C in dry kiln；
(5) it drenches starch adhesive A: the Imitation Rock Porcelain Tiles starch adhesive A of step (2) preparation is applied into the Imitation Rock Porcelain Tiles life of cloth after the drying with glaze pouring
Base surface, the weight of the applied starch adhesive of unit area are 600g/m2；
(6) it prints fabric B: Imitation Rock Porcelain Tiles fabric B prepared by step (2) being applied into cloth with silk-screen printing technique and was drenching starch adhesive
The billet surface of A；
(7) it is dried after applying cloth fabric: the Imitation Rock Porcelain Tiles green compact for applying fabric is dried at 180 DEG C in dry kiln again；
(8) it spray infiltration ink: is sprayed on Imitation Rock Porcelain Tiles green body, is cooperated by designed pattern using Digital ink-jet printer
Blank pattern texture, so that brick body surface and green body have similar texture and quality, ink jet layer is with a thickness of 0.8mm；
(9) it is burnt into: the Imitation Rock Porcelain Tiles green compact that step (8) is jetted through infiltration ink being placed in roller kilns and are burnt using conventional Imitation Rock Porcelain Tiles
At temperature schedule, pressure regime and atmosphere system, once-firing, firing temperature is 1200 DEG C, firing period 60min, is made
Imitation Rock Porcelain Tiles semi-finished product；
(10) edging and polishing: using conventional edging process equipment, double of finished bricks carries out edging processing, then to porcelain
Brick surface is processed by shot blasting, that is, obtains a kind of polished brick in porcelain character finished product with three-dimensional decorative effect.
Embodiment 3
(1) Imitation Rock Porcelain Tiles green body powder is prepared according to a conventional method, and it is spare to deploy 4 kinds of color powders；
(2) Imitation Rock Porcelain Tiles fabric is prepared, fabric A carries out ingredient, face using feldspar poor material and kaolin families plastic raw material
The siccative of material B all uses aluminium oxide, quartz, feldspar non-plastic raw material to carry out ingredient, and the slurry of wet ball grinding, two kinds of fabrics is equal
Controlling fineness is 325 mesh sieve margins within 0.5%, specific gravity 1.86g/cm3, wherein the siccative of starch adhesive A and auxiliary additive are wet
Method ball milling applies the slurry of performance requirement at leaching is met, and the siccative and auxiliary additive wet ball grinding of fabric B meets slurry properties
It is dried after capable of requiring, dry powder is made, and be mixed with the printing fabric for meeting printing performance with stamp-pad ink, auxiliary additive, it is spare.
The chemical composition range of two kinds of fabrics is (parts by weight): SiO2: 65%, Al2O3: 17%, MgO+CaO:2.0%, K2O+Na2O:8%, it is remaining
Amount is impurity, also needs additional ZnO 0.8%, TiO in fabric B2 3%。
(3) Imitation Rock Porcelain Tiles body preparation: by Imitation Rock Porcelain Tiles green body powder obtained in step (1) according to designed pattern line
Reason, carry out multitube cloth, then spread cloth in brick machine die cavity, under the pressure of 50MPa, by Imitation Rock Porcelain Tiles green body powder pressing at
Imitation Rock Porcelain Tiles green compact；
(4) Imitation Rock Porcelain Tiles green compact prepared by step (3) are dried at 270 DEG C in dry kiln；
(5) it drenches starch adhesive A: the Imitation Rock Porcelain Tiles starch adhesive A of step (2) preparation is applied into the Imitation Rock Porcelain Tiles life of cloth after the drying with glaze pouring
Base surface, the weight of the applied starch adhesive of unit area are 400g/m2；
(6) it prints fabric B: Imitation Rock Porcelain Tiles fabric B prepared by step (2) being applied into cloth with roller printing technique and was drenching starch adhesive
The billet surface of A；
(7) it is dried after applying cloth fabric: the Imitation Rock Porcelain Tiles green compact for applying fabric is dried at 250 DEG C in dry kiln again；
(8) it spray infiltration ink: is sprayed on Imitation Rock Porcelain Tiles green body, is cooperated by designed pattern using Digital ink-jet printer
Blank pattern texture, so that brick body surface and green body have similar texture and quality, ink-jet surface thickness is 0.5mm；
(9) it is burnt into: the Imitation Rock Porcelain Tiles green compact that step (8) is jetted through infiltration ink being placed in roller kilns and are burnt using conventional Imitation Rock Porcelain Tiles
At temperature schedule, pressure regime and atmosphere system, once-firing, firing temperature is 1230 DEG C, firing period 50min, is made
Imitation Rock Porcelain Tiles semi-finished product；
(10) edging and soft throwing: using conventional edging process equipment, double of finished bricks carries out edging processing, then to porcelain
Brick surface carries out soft throwing processing, that is, obtains a kind of porcelain matt brick finished product with three-dimensional decorative effect.
The above embodiments are merely illustrative of the technical scheme of the present invention and are not intended to be limiting thereof, although referring to preferred embodiment pair
The present invention is described in detail, those of ordinary skills in the art should understand that.It still can be to the specific reality of invention
The mode of applying is modified or some technical features can be equivalently replaced, without departing from the spirit of the technical scheme of the invention,
It should all cover within the scope of the technical scheme claimed by the invention.
Claims (7)
1. a kind of production method of the Imitation Rock Porcelain Tiles with three-dimensional decorative effect, it is characterised in that it the following steps are included:
(1) Imitation Rock Porcelain Tiles green body powder is prepared according to a conventional method, it is spare；
(2) Imitation Rock Porcelain Tiles fabric is prepared, the Imitation Rock Porcelain Tiles fabric of use is divided into starch adhesive A and two kinds of fabric B, the siccative of starch adhesive A and fabric B
Chemical composition is consistent, similar to green body powder in step (1), but wherein K by weight percentage2O+Na2O:6~8%, impurity≤
4%；The siccative of starch adhesive A carries out ingredient using feldspar poor material and kaolin families plastic raw material, but the siccative of fabric B is all adopted
Ingredient is carried out with aluminium oxide, quartz, feldspar non-plastic raw material；Starch adhesive A, fabric B slurry control fineness be 325 mesh sieve margins
Within 0.5%, specific gravity is 1.60~1.90, and wherein the siccative of starch adhesive A and auxiliary additive wet ball grinding apply performance at leaching is met
It is required that slurry, auxiliary colorant ZnO, TiO is not included in the auxiliary additive of starch adhesive A2, the siccative and auxiliary of fabric B
Additive wet ball grinding is dried after meeting size performance requirement, in the auxiliary additive of fabric B comprising auxiliary colorant ZnO,
TiO2One of or it is a variety of, dry powder is made, and the printing surface for meeting printing performance is mixed with stamp-pad ink, auxiliary additive
Material, it is spare；
(3) Imitation Rock Porcelain Tiles body preparation: by Imitation Rock Porcelain Tiles green body powder obtained in step (1) according to designed pattern texture, into
Row multitube cloth, then spread cloth in brick machine die cavity, under the pressure of 20~50MPa, by Imitation Rock Porcelain Tiles green body powder pressing at
Imitation Rock Porcelain Tiles green compact；
(4) body drying: Imitation Rock Porcelain Tiles green compact prepared by step (3) are dried at 150~300 DEG C in dry kiln；
(5) it drenches starch adhesive A: starch adhesive A prepared by step (2) is applied into the Imitation Rock Porcelain Tiles green surface of cloth after the drying with glaze pouring, it is single
The weight of the applied starch adhesive of plane product is 400~800g/m2；
(6) it prints fabric B: fabric B prepared by step (2) is applied into cloth in the billet surface for having drenched starch adhesive A with printing technology；
(7) it is dried after applying cloth fabric: the Imitation Rock Porcelain Tiles green compact for applying fabric is dried at 150~300 DEG C in dry kiln again；
(8) it spray infiltration ink: is sprayed on Imitation Rock Porcelain Tiles green body using Digital ink-jet printer by designed pattern, cooperates green body
Pattern texture, so that brick body surface and green body have similar texture and quality；
(9) it is burnt into: the Imitation Rock Porcelain Tiles green compact that step (8) is jetted through infiltration ink being placed in roller kilns and are burnt into temperature using conventional Imitation Rock Porcelain Tiles
Degree system, pressure regime and atmosphere system, once-firing, firing temperature be 1150~1250 DEG C, firing period be 40~
Imitation Rock Porcelain Tiles semi-finished product are made in 90min；
(10) edging: using conventional edging process equipment, double of finished bricks carries out edging processing, and being made has stereo decoration effect
The Imitation Rock Porcelain Tiles finished product of fruit.
2. the production method of the Imitation Rock Porcelain Tiles with three-dimensional decorative effect as described in claim 1, it is characterised in that: the auxiliary
Additive additive amount is calculated as ZnO with fabric siccative as 0.2~1%, TiO2It is 0.2~5%.
3. the production method of the Imitation Rock Porcelain Tiles with three-dimensional decorative effect as described in claim 1, it is characterised in that: step (6)
In printing web process use silk-screen printing or glue roller printing.
4. the production method of the Imitation Rock Porcelain Tiles with three-dimensional decorative effect as described in claim 1, it is characterised in that: step (6)
It is middle to be printed using part is uneven, so that stereo decoration texture is more life-like.
5. the production method of the Imitation Rock Porcelain Tiles with three-dimensional decorative effect as described in claim 1, it is characterised in that: step (8)
Ink-jet surface thickness is 0.3~1.0mm.
6. the production method of the Imitation Rock Porcelain Tiles with three-dimensional decorative effect as described in claim 1, it is characterised in that: step (10)
After edging processing, handled using polishing process.
7. having solid as prepared by the production method of any Imitation Rock Porcelain Tiles with three-dimensional decorative effect of claim 1~6
The Imitation Rock Porcelain Tiles of decorative effect.