CN105969469A - Moth-proof high-combustion efficiency biomass briquette fuel and production method thereof - Google Patents

Abstract

The invention discloses a moth-proof high-combustion efficiency biomass briquette fuel. According to the invention, the pretreated corn straws are taken as a raw material for anaerobic fermentation for 10-20 days, so that mechanical endurance of the briquette fuel is increased, finally, biogas residue is dried and crushed, and then is composited with an anti-slagging agent and an oxidant and other active ingredients for compression moulding under condition of 6MPa. The preparation method has the advantages of fast moulding and less required pressure, and is helpful for reducing equipment wearing. In the invention, magnesium carbonate is taken as the anti-slagging agent, during a combustion process, the Mg element and elements such as Si, K, and Na which are inherent in the corn straws and are capable of slagging are subjected to a reaction, a novel compound K2Mg(SO4)2 is generated and provides anti-slagging performance to the briquette fuel, potassium chlorate and manganese dioxide which are taken as an ignition-assisting agent are capable of increasing the combustion efficiency and heat energy of the fuel, and the produced briquette fuel has the advantages of good weather ability, moth resistance, and long-term storage, can replace the coal for generating and heating, and can realize low cost and high yield on the energy aspect.

Description

Biomass molding fuel that a kind of Anti-moth-eating efficiency of combustion is high and preparation method thereof

Technical field

The present invention relates to biomass fuel technical field, particularly relate to the biomass moulding that a kind of Anti-moth-eating efficiency of combustion is high Fuel and preparation method thereof.

Background technology

Biomass energy because it is renewable, aboundresources, environmental friendliness and become world's fourth largest energy, be also the most permissible Transport and the clean reproducible energy stored, mainly by the biomass energy technology modernized by agricultural wastes, felling Residue, feces of livestock and poultry, MSW, sanitary sewage become biological particles to fire with Raw material processings such as industrial organic waste waters The end products such as material, biodiesel, bio-fuel ethanol.Biomass fuel is discharged almost without SO2 during later-stage utilization, Decrease the acid rain caused by flue gas and the harm of greenhouse effect produced during it utilizes so that biomass energy has The most wide application prospect and development space, thus Developing Biomass fuel has become the mankind and has solved energy problem and improve ring One important means in border and developing direction.China is large agricultural country, and biomass resource enriches, the yield of annual agricultural crop straw More than 700,000,000 t, wherein amount usable is about 5.055 hundred million t, accounts for the 50%-60% of Chinese biological matter total resources, therefore, converts it Utilize significant.The raw materials such as agricultural crop straw exist loosely organized, density is little, distribution is not concentrated, the thermal efficiency is low, inconvenient Many defects such as transport and storage, are unfavorable for utilizing on a large scale, utilize mechanical force that compressed biomass or extruding are become density relatively Greatly, the thermal efficiency is high, it is simple to the solid fuel of transport storage is the most relatively advanced a kind of biomass economy mode.

It is tight to there is equipment attrition for straw compressing and forming in " molding fuel test is prepared in stalk anaerobic fermentation modification " literary composition The antibiont degraded barrier that weight and anaerobic fermentation face, it is proposed that the thinking of shaped fuel is prepared in a kind of stalk anaerobic fermentation modification And carried out experimental study.With corn straw as raw material in literary composition, the anaerobism that raw material carries out 10d and 20 d respectively by a definite date is sent out Ferment, the biogas residue after fermentation size-reduced and dried in 100 DEG C, be compressed into the granular fuel of diameter 10 mm under the conditions of 6 MPa. Result of the test shows: after stalk anaerobic fermentation, and the energy being retained in biogas residue is more than the energy transferred in biogas, straw biogas residue Energy value high, but after fermentation 20 d, straw content of ashes is 3 times of non-fermented stalk, and its clinkering property may be made to increase By force, the shaped fuel calorific value and prepared in literary composition only improves about 5.82% than raw material, it is impossible to meets blast furnace or has high heating value demand Place, and exist when small-sized cooking stove misfire, the problem such as the length duration of ignition and smoke pollution, efficiency of combustion is low, Need in addition modified to obtain high heating value, the novel biomass shaped fuel of resistive connection slag.

Summary of the invention

The object of the invention is contemplated to make up the defect of prior art, it is provided that the biomass that a kind of Anti-moth-eating efficiency of combustion is high Shaped fuel and preparation method thereof.

The present invention is achieved by the following technical solutions:

The biomass molding fuel that a kind of Anti-moth-eating efficiency of combustion is high, is prepared by the raw materials in: corn straw 100, Pinus massoniana Lamb wood flour 15-17, rice husk 20-22, magnesium carbonate 3-4, calcium oxide 6-8, magnesium powder 0.5-0.7, monosodium glutamate waste liquid 6-7, potassium chlorate 7-8, manganese dioxide 1-2, boron-moisten soil 5-6, Kaolin 19-21, suitable quantity of water.

The manufacture method of the biomass molding fuel that described a kind of Anti-moth-eating efficiency of combustion is high, comprises the following steps:

(1) by potassium chlorate, manganese dioxide mixed grinding 20-30 minute, put in 60-80 DEG C of water-bath, add boron-moisten soil constant temperature 2-3 Hour, it is evaporated, adds monosodium glutamate waste liquid ultrasonic grinding 10-15 minute, be spray-dried and prepare combustion adjuvant；

(2) Kaolin 5-10wt% hydrochloric acid solution is soaked 1-2 hour, with hot wash to without chloride ion, add water in 80-100 DEG C Lower ultrasonic Treatment 8-10 minute, dries, and adds calcium oxide roasting 2-4 hour at 670-770 DEG C, is cooled to grinding at room temperature system Obtain modified kaolin；

(3) by corn straw, rice husk with hot-water soak 10-12 hour of 60-70 DEG C, filter and put in fermentation vat, control fermentation Pond temperature is at 30-50 DEG C, and humidity is 50-60%, and anaerobic fermentation processes 20-30 hour, adds modified kaolin, Pinus massoniana Lamb wood flour The isolation air that stirs continues fermentation 10-20 days, filtering drying, puts into and is crushed to 60-80 mesh in pulverizer；

(4) in step (3) material, add combustion adjuvant, water and the mixing of other residual components, send into single lead screw ex truding briquetting machine, with 6MPa's Briquetting pressure is squeezed into a diameter of 5-8mm, the cylindrical particle of a length of 3-8cm, is dried, discharging.

The invention have the advantage that the anaerobism that the present invention carries out 10-20d by a definite date with pretreated corn straw for raw material is sent out After ferment, the relative amount of stalk hemicellulose and cellulose reduces, and lignin relative amount increases, and volatile matter content reduces, benzene alcohol Extract declines can improve the mechanical endurance of shaped fuel, compound resistive connection slag agent and combustion-supporting after finally biogas residue drying being pulverized Agent and the compression forming under the conditions of 6MPa of other effective ingredient, fast desirable pressure of preparation process molding is little contributes to reduction equipment for this Abrasion；The present invention using magnesium carbonate as resistive connection slag agent, in combustion Mg element intrinsic with corn straw, knot can be caused The elements such as Si, K, Na of slag there occurs reaction, generates new compound K₂Mg(SO₄)₂And make it have anti-slagging properties, with Potassium chlorate, manganese dioxide etc. improve efficiency of combustion and the heat energy of fuel as combustion adjuvant, and the shaped fuel weatherability of preparation is good Anti-moth-eating can long-term storage, alternative coal is as generating, the fuel of heating, it is possible to realize the low cost in terms of the energy, high receives Benefit.

Detailed description of the invention

The biomass molding fuel that a kind of Anti-moth-eating efficiency of combustion is high, is prepared by the raw materials in: corn straw 100, Pinus massoniana Lamb wood flour 15, rice husk 20, magnesium carbonate 3, calcium oxide 6, magnesium powder 0.5, monosodium glutamate waste liquid 6, potassium chlorate 7, manganese dioxide 1, Boron-moisten soil 5, Kaolin 19, suitable quantity of water.

The manufacture method of the biomass molding fuel that described a kind of Anti-moth-eating efficiency of combustion is high, comprises the following steps:

(1) by potassium chlorate, manganese dioxide mixed grinding 20-30 minute, put in 60-80 DEG C of water-bath, add boron-moisten soil constant temperature 2-3 Hour, it is evaporated, adds monosodium glutamate waste liquid ultrasonic grinding 10-15 minute, be spray-dried and prepare combustion adjuvant；

(2) Kaolin 5-10wt% hydrochloric acid solution is soaked 1-2 hour, with hot wash to without chloride ion, add water in 80-100 DEG C Lower ultrasonic Treatment 8-10 minute, dries, and adds calcium oxide roasting 2-4 hour at 670-770 DEG C, is cooled to grinding at room temperature system Obtain modified kaolin；

(3) by corn straw, rice husk with hot-water soak 10-12 hour of 60-70 DEG C, filter and put in fermentation vat, control fermentation Pond temperature is at 30-50 DEG C, and humidity is 50-60%, and anaerobic fermentation processes 20-30 hour, adds modified kaolin, Pinus massoniana Lamb wood flour The isolation air that stirs continues fermentation 10-20 days, filtering drying, puts into and is crushed to 60-80 mesh in pulverizer；

(4) in step (3) material, add combustion adjuvant, water and the mixing of other residual components, send into single lead screw ex truding briquetting machine, with 6MPa's Briquetting pressure is squeezed into a diameter of 5-8mm, the cylindrical particle of a length of 3-8cm, is dried, discharging.

The technical parameter index using the biomass molding fuel of present invention production is as follows:

(1) relaxed density is 1.182g/cm³；

(2) biogas residue lignin quality mark adds 36.6%；

(3) ash: 6.98%；

(4) calorific value: 25.92MJ/kg.

Claims (2)

1. the biomass molding fuel that an Anti-moth-eating efficiency of combustion is high, it is characterised in that be prepared by the raw materials in: Corn straw 100, Pinus massoniana Lamb wood flour 15-17, rice husk 20-22, magnesium carbonate 3-4, calcium oxide 6-8, magnesium powder 0.5-0.7, monosodium glutamate are useless Liquid 6-7, potassium chlorate 7-8, manganese dioxide 1-2, boron-moisten soil 5-6, Kaolin 19-21, suitable quantity of water.

The manufacture method of the biomass molding fuel that a kind of Anti-moth-eating efficiency of combustion the most according to claim 1 is high, it is special Levy and be to comprise the following steps:

(1) by potassium chlorate, manganese dioxide mixed grinding 20-30 minute, put in 60-80 DEG C of water-bath, add boron-moisten soil constant temperature 2-3 Hour, it is evaporated, adds monosodium glutamate waste liquid ultrasonic grinding 10-15 minute, be spray-dried and prepare combustion adjuvant；

(2) Kaolin 5-10wt% hydrochloric acid solution is soaked 1-2 hour, with hot wash to without chloride ion, add water in 80-100 DEG C Lower ultrasonic Treatment 8-10 minute, dries, and adds calcium oxide roasting 2-4 hour at 670-770 DEG C, is cooled to grinding at room temperature system Obtain modified kaolin；

(3) by corn straw, rice husk with hot-water soak 10-12 hour of 60-70 DEG C, filter and put in fermentation vat, control fermentation Pond temperature is at 30-50 DEG C, and humidity is 50-60%, and anaerobic fermentation processes 20-30 hour, adds modified kaolin, Pinus massoniana Lamb wood flour The isolation air that stirs continues fermentation 10-20 days, filtering drying, puts into and is crushed to 60-80 mesh in pulverizer；

(4) in step (3) material, add combustion adjuvant, water and the mixing of other residual components, send into single lead screw ex truding briquetting machine, with 6MPa's Briquetting pressure is squeezed into a diameter of 5-8mm, the cylindrical particle of a length of 3-8cm, is dried, discharging.